KR100303128B1 - 금속의다이캐스팅용윤활제조성물및다이캐스팅방법 - Google Patents

금속의다이캐스팅용윤활제조성물및다이캐스팅방법 Download PDF

Info

Publication number
KR100303128B1
KR100303128B1 KR1019930016415A KR930016415A KR100303128B1 KR 100303128 B1 KR100303128 B1 KR 100303128B1 KR 1019930016415 A KR1019930016415 A KR 1019930016415A KR 930016415 A KR930016415 A KR 930016415A KR 100303128 B1 KR100303128 B1 KR 100303128B1
Authority
KR
South Korea
Prior art keywords
weight
present
composition
component
amount
Prior art date
Application number
KR1019930016415A
Other languages
English (en)
Inventor
안토니피.윌로우비
Original Assignee
애치슨인더스트리이즈인코포레이팃드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 애치슨인더스트리이즈인코포레이팃드 filed Critical 애치슨인더스트리이즈인코포레이팃드
Application granted granted Critical
Publication of KR100303128B1 publication Critical patent/KR100303128B1/ko

Abstract

본 발명은 액체 담체에, 예를 들어 수성 에멀젼에 미세하게 분산된 폴리프로필렌을 함유하는 금속의 다이캐스팅용 윤활제/이형제 조성물과 이 조성물을 사용하여 금속부품을 다이캐스팅 하는 방법을 제공한다. 본 조성물은 자동차 엔진 부품과 같은 다이캐스트 부품 제조시에 사용하기에 적합하다.

Description

[발명의 명칭]
금속의 다이캐스팅용 윤활제 조성물 및 다이캐스팅방법
[발명의 상세한 설명]
본 출원은 1992년 8월 27일자 출원된 미합중국 특허출원 07/936,581호의 CIP 출원이다.
본 발명은 금속의 다이캐스팅(diecasting)에 사용되는 윤활제 조성물로서, 향상된 윤활성 및 이형성을 갖는 조성물에 관한 것이다.
가압 다이캐스팅 및 스퀴즈 캐스팅에 이용되는 다이캐스팅 머신은 고압 및 고온하에 가동된다. 이러한 장치에 사용되는 다이의 표면은 윤활성을 지니고 밀폐가 되어 있어야 금속주물이 효율적으로 유동할수 있고, 완전하게 이형될 수 있다. 이 밖에도, 각종 가동부품들이 윤활성을 지녀야 한다. 다이캐스팅을 위한 윤활제 조성물의 기본요건은 다음과 같다 :
(1) 이형능(parting ability) : 주물이 다이 표면으로부터 변형이나 과도한 응력을 받지 않고 이탈할 수 있어야 한다.
(2) 장벽형성 : 윤활제가 다이 표면에 대한 주물 금속의 접착성을 감소시키기 위해 주물 금속과 다이 표면 사이에 물리적 장벽을 형성해야 한다(주형할 금속에 따라 "솔더링(Soldering)" 또는 "갈바나이징(Galvanizing)"으로 언급됨).
(3) 표면 가공의 조절 : 윤활제 조성물은 강철을 부식하거나 주물의 표면을 손상시키거나, 또는 후속 마무리 작업을 방해하거나 방지할 가능성이 있는, 바람직하지 못한 잔류물을 다이 표면상에 남기지 않아야 한다.
(4) 주조시의 안정성 : 윤활제 조성물은 주물 표면에 기공을 유발하고, 주조시의 압력 내밀성을 손상시킬 수 있는 가스를 과량으로 배출하지 않아야 한다.
(5) 위생 및 안전성 : 윤활제 조성물은, 독성 성분 또는 이들이 반응하여 원치 않는 부산물을 형성할 수 있는 성분들을 함유하지 않아야 한다.
초기의 다이캐스팅에 있어서는 각종 페이스트, 오일, 그리이스 및 왁스를 사용하여 이들을 부러싱을 비롯하여 다양한 수단으로 다이상에 처리하였다. 이들 물질들은, 종종 용매 및 오일이 뜨거워진 다이 표면에서 증발하거나 연소하기 때문에, 심하게 발연하는 문제를 야기시킨다. 알루미늄 페이스트 및 미세하게 분쇄된 흑연과 같은 첨가제가 사용되어 왔으나, 이들 첨가제는 많은 적용분야에서 바람직하지 않은 것으로 여겨지는, 표면 변색(흑연 착색)을 일으키는 경향이 있다.
실리콘 오일이 어느 정도는 효과적인 이형제가 될 수 있으나, 대부분의 경우 실리콘 오일은 윤활특성, 특히 가동부위에 있어서는 윤활성이 충분하지 못하다. 또한 탄화수소계 오일 또는 폴리에틸렌을 사용하면, 다이표면상 및 다이의 외부에 분해산물이 형성되는 원인이 될 수 있다. 다이 표면 그 자체상에 분해산물이 형성되면 주조 성능이 저하하고, 표면의 착색이 발생하며, 아울러 다이의 사용수명이 단축된다. 다이의 외측에 존재하는 부착물은 장애물이 될뿐아니라, 제거하기가 어려워, 효과적인 용매가 존재하지 않는한, 기계적 마모를 피할 수 없다. 다이의 접합면 상에 부착물이 존재하면 다이가 완전히 밀폐되는 것을 방해하여, 주물의 치수 정밀도를 해하게 된다.
따라서, 다이캐스팅 기술분야에서는 다이 표면을 "촉촉히"하기에 적절한 표면활성과, 고르게 유동할 수 있는 적당한 점도범위를 가지면서, 주조 공정중에 다이 표면상에 그대로 존재함과 동시에 적절히 제거될 수 있어 깨끗한 주물과 다이표면을 제공할 수 있는 개선된 윤활제/이형제가 요구되게 되었다. 본 명세서 및 특허청구의 범위에서 사용되는 "윤활제"와 "이형제"는 상호 동일한 대상을 지칭하는 서로 다른 표현일 뿐이다.
본 발명자들은 폴리프로필렌의 사용이 상기한 요건을 충족시키고 게다가 본 발명에서 기술한 것과 같은 그 용도가 예기치 않은 독특한 결과를 제공한다는 것을 알아내어 본 발명을 완성하였다. 전형적으로, 폴리프로필렌은 담체 내에 미분된 분산액으로 적용할 수 있으며, 일반적으로 폴리프로필렌은 다이 표면상에 분무되어 수성 담체의 증발후 폴리프로필렌의 표면막으로 잔류할 수 있도록 수성 에멀젼으로 제제하는 것이 바람직하다.
넓은 의미에서, 본 발명은 액체 담체중에 폴리프로필렌을 함유하는 새로운 다이 윤활제/이형제 조성물에 관한 것이다.
본 발명을 더욱 구체적으로 기술하면,
(a) 평균분자량이 약 500 내지 약 300,000인 폴리프로필렌 약 0.01 내지 약 40중량%,
(b) 실리콘 오일 0 내지 약 50중량%,
(c) 조성물을 구성하는 성분들이 에멀젼 형태로 유지되도록 보조작용을 하는 유화제 약 0.01 내지 약 8중량%, 및
(d) 부식방지제 0 내지 약 5중량%와, 잔부의 물을 포함하여 이루어지는, 수성 다이 윤활제/이형제 조성물에 관한 것이다.
본 발명은 또한 방법적인 측면에서 보면, 액체 담체중에 폴리프로필렌을 함유하는 다이 윤활제/이형제 조성물로 다이를 처리하는 단계, 금속제품을 다이캐스팅하는 단계 및 다이로부터 제품을 분리해내는 단계로 이루어지는 금속부품 또는 금속제품의 다이캐스팅 방법과, 또한 상기 방법에 의해 형성된 제품에 관한 것이다.
본 발명에 적합한 폴리프로필렌은 일반적으로 평균분자량이 약 500내지 약 300,000, 바람직하기는 약 2,500 내지 약 10,000이며, 가장 바람직한 결과는 평균분자량이 약 4,000 내지 약 5,000인 폴리프로필렌을 사용한 경우에 얻어진다. 폴리프로필렌은 고체 형태이어야 하며, 소위, 예컨데 비교적 예리한 융점(예를 들면 약 120 내지 180℃의 범위)을 갖는 결정성 폴리프로필렌이 이상적이다.
전형적으로, 폴리프로필렌은 "Emrel 7"(고형분 40%; Hickson and Welch Ltd., 제품)과 같은 수성 에멀젼 형태로 조성물에 사용된다. 다른 형태의 폴리프로필렌, 예를 들어 "Eltex HY-P" 또는 "Eltex RP-P" 제품(Solvay Chemical Co.제품)과 같은 폴리프로필렌 입상체 또는 분말체를 사용할 수 있다. 사용되는 폴리프로필렌은 수성 에멀젼 또는 고체분말 어느 형태로나, 조성물에 분산시킬 수 있다. 본원에 기재한 실시예들로부터 알수 있는 바와 같이, 폴리프로필렌의 분자량은 경우에 따라 "D" 문자를 사용하여 표시하였다. 이것은 달톤(Dalton) 방법이나 또는 분자량을 기술 내지는 표시하는 방법론에 기초한 것이다. 여기에서 사용된 "폴리프로필렌"이란 용어는 폴리프로필렌 단독중합체, 폴리프로필렌 블록 프로필렌-에틸렌 공중합체, 폴리프로필렌 랜덤 프로필렌-에틸렌 공중합체 및 폴리프로필렌 블럭 또는 랜덤 프로필렌 다른 불포화된 탄화수소 단량체 공중합체가 포함되는 것을 의미하며, 그러나 여기에서 사용되는, 상기에서 언급된 폴리프로필렌은 고체 형태이어야 하며, 만일 다른 어느 공중합체 재료(예; 에틸렌, 부텐, 펜텐, 헥센 등)가 존재하는 경우에는, 다른 공중합체 재료는 폴리프로필렌 공중합체의 28몰% 이하, 바람직하게는 20몰% 이하를 차지할 수 있다. 여기에서 사용된 "실제로 순수한 폴리프로필렌"이란 폴리프로필렌 단독중합체와 또한 폴리프로필렌과 공중합된 다른 물질 28몰% 이하를 함유하는 폴리프로필렌 공중합체가 포함되는 것을 의미한다.
조성물중의 폴리프로필렌은 일반적으로 조성물 중 약 0.0l 내지 약 40중량%의 범위내로 존재해야 하며, 바람직한 결과는 폴리프로필렌이 조성물의 약 0.02 내지 약 20중량%의 범위내로 존재하는 경우에 얻어지고, 가장 바람직한 결과는 폴리프로필렌이 조성물의 약 0.1 내지 약 15중량%의 범위내로 존재하는 경우에 얻어지게 된다.
여기에서 사용된 폴리프로필렌 또는 폴리프로필렌 에멀젼은 적절한 유화제 또는 현탁제를 함유하며, 특히, 하기에 언급한 에톡실화 알콜과 같은 비이온계 계면활성제가 본 목적에 유용하다. 본 발명에 따른 윤활제 조성물은 하기에 기술한 바와 같이, 실리콘오일, 미네랄 오일, 부식방지제 등과 같은 다른 성분을 함유하는 것이 바람직할 수도 있다. 여기에 기술된 윤활제 조성물은 최종 용도용 조성물로서 또는 사용직전에 희석하여 사용하는 농축액으로서 제제화할 수 있다. 농축액은 전형적으로 약 1:10 내지 약 1:100인 용적 비율로 희석될 수 있다.
본 발명자들은, 폴리프로필렌을 사용하면 종래의 윤활제/이형제를 사용한 경우와 비교하여 독특하고 놀라울만한 잇점이 얻어진다는 것을 알게되었다. 폴리프로필렌은 깨끗하게, 가장 중요하게는 주물상에 기공을 유발하지 않고, 깨긋이 분해되어 분해산물의 침전물을 거의 남기지 않는다. 주물은 깨끗하고 선명하여 도금과 같은 후속 공정에서 사용하기에 적합하며, 또한 다이와 다이면은 깨끗하게 원상태를 유지하게 된다.
실리콘 오일은, 윤활제 조성물에 사용하는 경우, 다수의 여러가지 시판물 중에서 임의로 선택될 수 있다. 그러한 실리큰 오일의 전형적인예를 들면 유니온 카바이드사의 "L-42", 다우 코닝사의 "203", 제너랄일렉트릭사의 "SF-1080" 및 "Wacker TN"으로 알려져 있는 실리콘 오일 제품이 있다. 동일한 실리콘 오일들이 예컨데, "Wacker TNE", 유니온 카바이드 사의 "LE-420/HS", 제너랄 일렉트릭사의 "SM-2154" 및 다우 코닝사의 "No.290"과 같은 상품명으로 수성 유탁화된 형태로 시판되고 있다. 실리콘 오일은 바람직하기는 유기 변성된 폴리실록산 실리콘 오일이다. 실리콘 오일은 조성물의 0 내지 약 50중량%의 범위내로 존재할 수 있으며, 더 바람직한 결과는 실리콘 오일이 약 0.1 내지 약23중량%의 범위내로 즌재하는 경우에 얻어지고, 가장 바람직한 결과는 실리콘 오일 또는 실리콘 유체가 조성물의 약 0.5 내지 약 13중량%의 범위내로 존재하는 경우에 얻어진다.
조성물에 사용하는 유화제는 조성물 중의 성분들을 액체 담체 내에서 유화된 형태로 유지시키는 작용을 하며, 일반적으로 비 이온계 유화제가 사용된다. 유화제는 일반적으로 조성물의 약 0.01 내지 약 8중량%의 범위내로 존재해야 한다. 바람직한 결과는 유화제가 약 0.02 내지 약 6중량%의 범의내로 존재하는 경우에 얻어지고, 가장 바람직한 결과는 유화제가 조성물의 약 0.1 내지 5중량%의 범위내로 존재하는 경우이다.
전형적인 유화제 또는 습윤제 및 분산제는 다음과 같다: 에톡실화 알콜[예. Genapol×060 및 Genapol×080(훽스트 케미칼사 제품)]; 노닐 페놀알콜[예. Antarox CO-530 및 Antarox CO-630(롱뿔랑 케미칼사 제품 [lgepol CO-530 또는 CO-630이란 상품명으로 미국에서 시판중임])] 및 에톡실화 캐스터 오일[예. Emulan-EL(BASF사 제품)]도 사용 가능하다.
여기에서 언급된 부식방지제는 조성물중에 임의로 함유하는 성분으로서, 일반적으로 윤활제 조성물의 0 내지 약 5중량%의 범위내로 존재할 수 있다. 바람직하기는 부식방지제가 조성물의 약 0.01 내지 약 4중량%의 범위내로 존재하는 경우이고, 가장 적합한 결과는 부식방지제가 조성물의 약 0.1 내지 약 3중량%의 범위내로 존재하는 경우에 얻어진다. 적합한 부식방지제의 예로는 아질산 나트륨, 나트륨 벤조에이트, 트리에탄올아민 염, 케미나이트 10-01 및 베크로산(Becrosan) BTO(Carl Becker GmBH 제품)이다.
미네랄 오일, 합성 또는 천연오일, 방부제, 소포제 또는 살균제와 같은, 다른 첨가제들을 윤활제 조성물에 사용할 수도 있다. 이들 다른 첨가제를 사용할 경우, 이들은 일반적으로 조성물의 약 0.02 내지 약 35중량%의 범위내로 존재해야 하며, 바람직한 결과는 이들 다른 첨가제가 조성물의 약 0.1 내지 약 30중량%의 범위내로 존재하는 경우에 얻어진다. 살균제 또는 방부제는 제품의 변질을 방지할 목적으로 사용되며, 적합한 살균제는 방향족 화합물들의 합성혼합물, 즉 이소티아질론 및 클로로아세트아미드와 n-포르말과의 혼합물인, Acticide BX(토르 캐미칼스사 제품, 영국); 또는 Emulcid(토르 케미칼스사 제품), 또는 Grotan BK(스터링 인더스트리얼사 제품)(이들 양 후자의 물질은 헥사히드로-1,3,5(트리스(2-히드록시에틸)-s-트리아진 이다)이 포함한다.
조성물에 사용되는 액체 담체는 물이 바람직하나, 미네랄 오일 또는 미네랄 주정(spirit)을 사용할 수도 있다.
다음 실시예는 본 발명을 설명하기 위해 제공된 것이며, 이들 실시예로 본 발명을 제한하기 위한 것은 아니다. 모든 실시예에서 사용된 물질은 중량% 이다.
[실시예 1]
상기 조성물은 최종 용도를 위해, 대략 1:40 용적부의 비율로 물을 가해 희석시킨다. 희석한 조성물은 약 10 내지 15초 동안 다이표면에 살포하고 다이캐스트 부품, 예컨데, 매니폴드, 기어박스 케이싱, 락카 카바등과 같은 자동차 엔진부품을 형성시킨다.
[실시예 2]
상기 조성물은 최종 용도를 위해, 대략 l:40 용적부의 비율로 물을 가해 희석시킨다. 희석한 조성물은 약 10 내지 15초 동안 다이표면에 살포하고 다이캐스트 부품, 예컨데, 매니폴드, 기어박스 케이싱, 락카 카바등과 같은 자동차 엔진부품을 형성시킨다.
[실시예 3]
[실시예 4]
[실시예 5]
[실시예 6]
[실시예 7]
[실시예 8]
[실시예 9]
[실시예 10]
실시예 2와 같이 수행하나, 단 폴리프로필렌 에멀젼 대신에 폴리프로필렌 분말(평균입경 0.2 내지 2 미크론)을, 제품중 폴리프로필렌의 함량이 실시예 2에서 폴리프로필렌 에멀젼을 사용한 경우와 동일하게 될 수 있는 비율로 사용하였다.
[실시예 11]
상기한 내용을 요약하면, 폴리프로필렌을 압력 다이캐스팅 및/또는 스퀴즈 캐스팅에 적용하기 위해 여기에 기술된 윤활제 조성물에 사용하며, 폴리프로필렌이 수성 에멀젼 또는 미세분말 어느 형태이던 간에, 다음과 같은 독특한 장점 및 잇점을 제공할 수 있다는 것이다:
(1) 오염이 감소된 깨끗하고 선명한 주물,
(2) 다이 상에의 경질 침전물 형성의 감소 경향,
(3) 현저하게 향상된 다이 윤활성 및 이형성,
(4) 이형제 제품의 사용에 있어서의 개선된 경제성,
(5) 솔더링의 발생 감소 경향과, 그리고,
(6) 본 발명의 윤활제 조성물을 적용(예. 분무처리 또는 기타 다이 표면에 적용)할 경우,
히트블럭(heat block) 또는 다이 표면에 본 발명의 조성물을 쿠킹하면, 윤활제의 연속막을 그대로 보존하면서, 열이 매우 균일하게 다이에 가해질 수 있기 때문에, 매우 중요한 온도 플래토우(Plateau) 범위가 발생(선행기술의 조성물은 플래토우보다는 피크를 가진다)되고 선행기술의 조성물에 비해 습윤화 온도의 상승이 가능(이것은 사이클 시간을 개선하고 시간당 제조되는 부품을 더 많이 생산할 수 있다)하다는 사실에 기인하여 압력다이캐스팅에 탁월한 효과를 얻을 수 있다.
본 발명의 목적, 잇점 및/또는 장점을 충족시킬 수 있는 본 발명의 바람직한 실시형태로 본 발명을 기술하였으나, 첨부된 특허청구의 범위를 벗어나지 않는한 본 발명을 개량, 변경 및 변화시킬 수 있음을 잘 알수 있을 것이다.

Claims (24)

  1. (a) 실질적으로 순수하며, 프로필렌 중합체 또는 프로필렌 공중합체 형태이고, 평균분자량이 500 내지 300,000인 고체형태의 폴리프로필렌 0.01 내지 40중량%, (b) 실리콘 오일 0.1 내지 50중량%, (c) 조성물을 구성하는 성분들이 에멀젼 형태로 유지되도록 보조작용을 하는 유화제 0.01 내지 8중량%, 및 (d) 부식방지제 0.01 내지 5중량%와, 잔부의 액체 담체를 포함하여 이루어지는 것을 특징으로 하는 액체 담체계 다이캐스팅용 윤활제/이형제 조성물.
  2. 제1항에 있어서, 상기 성분 (a)가 0.02 내지 20중량%의 양으로 존재하고, 성분 (b)가 0.1 내지 23중량%의 양으로 존재하고, 성분 (c)가 0.02 내지 6중량%의 양으로 존재하고, 성분 (d)가 0.01 내지 4중량%의 양으로 존재하며, 상기 폴리프로필렌의 평균분자량이 2500 내지 10,000인 것을 특징으로 하는 조성물.
  3. 제2항에 있어서, 상기 성분 (a)가 0.1 내지 15중량%의 양으로 존재하고, 성분 (b)가 0.5 내지 13중량%의 양으로 존재하고, 성분 (c)가 0.1 내지 5중량%의 양으로 존재하고, 성분 (d)가 0.1 내지 3중량%의 양으로 존재하며, 상기 폴리프로필렌의 평균분자량이 4000 내지 5,000인 것을 특징으로 하는 조성물.
  4. 제1항에 있어서, 상기한 폴리프로필렌이 미분된 분산형태이고, 잔부가 물인 것을 특징으로 하는 조성물.
  5. 제4항에 있어서, 상기한 조성물이 합성 또는 천연오일, 방부제 또는 살균제로 이루어진 그룹에서 선택된 1종 이상의 첨가제 0.02 내지 35중량%를 더욱 포함하는 것을 특징으로 하는 조성물.
  6. 제1항에 있어서, 상기한 폴리프로필렌이 2500 내지 10,000인 평균분자량을 갖는 것을 특징으로 하는 조성물.
  7. (a) 실질적으로 순수하며, 필수적으로 프로필렌 중합체 또는 프로필렌 공중합체로 구성되고, 평균분자량이 500 내지 300,000인 고체형태의 폴리프로필렌 0.01 내지 40중량%, (b) 실리콘 오일 0.1 내지 50중량%, (c) 조성물을 구성하는 성분들이 에멀젼 형태로 유지되도록 보조작용을 하는 유화제 0.01 내지 8중량%, 및 (d) 부식방지제 0.01 내지 5중량%와 잔부의 액체 담체를 포함하여 이루어지는, 액체 담체에 분산된 폴리프로필렌을 함유하는 다이 윤활제/이형제 조성물로 다이를 처리하는 단계, 금속제품을 다이캐스팅하는 단계와 다이로부터 제품을 분리해내는 단계로 이루어지는 것을 특징으로 하는 금속제품의 다이캐스팅 방법.
  8. 제7항에 있어서, 상기 성분 (a)가 0.02 내지 20중량%의 양으로 존재하고, 성분 (b)가 0.1 내지 23중량%의 양으로 존재하고, 성분 (c)가 0.02 내지 6중량%의 양으로 존재하고, 성분 (d)가 0.01 내지 4중량%의 양으로 존재하며, 상기 폴리프로필렌의 평균분자량이 2500 내지 10,000인 것을 특징으로 하는 방법.
  9. 제8항에 있어서, 상기한 폴리프로필렌이 미분된 분산형태이고, 잔부가 물인 것을 특징으로 하는 방법.
  10. 제9항에 있어서, 상기한 조성물이 합성 또는 천연오일, 방부제 또는 살균제로 이루어진 그룹에서 선택된 1종 이상의 첨가제 0.1 내지 35중량%를 더욱 포함하는 것을 특징으로 하는 방법.
  11. (a) 평균분자량이 500 내지 300,000인, 실질적으로 순수한 폴리 프로필렌 고체 0.01 내지 40중량%, (b) 실리콘 오일 0.1 내지 50중량%, (c) 조성물을 구성하는 성분들이 에멀젼 형태로 유지되도록 보조작용을 하는 유화제 0.01 내지 8중량%, 및 (d) 부식방지제 0.01 내지 5중량%와, 잔부의 액체 담체로 이루어지는, 액체 담체에 분산된 폴리프로필렌을 함유하는 다이 윤활제/이형제 조성물로 다이를 처리하는 단계, 금속제품을 다이캐스팅하는 단계와 다이로부터 제품을 분리해내는 단계로 이루어지는 것을 특징으로 하는 금속제품의 다이캐스팅방법.
  12. 제11항에 있어서, 상기 성분 (a)가 0.1 내지 15중량%의 양으로 존재하고, 성분 (b)가 0.5 내지 13중량%의 양으로 존재하고, 성분 (c)가 0.1 내지 5중량%의 양으로 존재하고, 성분 (d)가 0.1 내지 3중량%의 양으로 존재하는 것을 특징으로 하는 방법.
  13. 제11항에 있어서, 상기한 액체담체가 물이고, 폴리프로필렌이 단독 중합체 형태로 존재하는 것을 특징으로 하는 방법.
  14. 제12항에 있어서, 상기한 조성물이 합성 또는 천연오일, 방부제 또는 살균제로 이루어진 그룹에서 선택된 1종 이상의 첨가제 0.02 내지 35중량%를 더욱 포함하는 것을 특징으로 하는 방법.
  15. 제11항에 있어서, 상기 성분 (a)가 0.02 내지 20중량%의 양으로 존재하고,성분 (b)가 0.1 내지 23중량%의 양으로 존재하고, 성분 (c)가 0.02 내지 6중량%의 양으로 존재하고, 성분 (d)가 0.01 내지 4중량%의 양으로 존재하며, 상기 폴리프로필렌의 평균분자량이 2500 내지 10,000인 것을 특징으로 하는 방법.
  16. 제14항에 있어서, 상기한 액체담체가 물인 것을 특징으로 하는 방법.
  17. 제12항에 있어서, 상기한 조성물이 합성 또는 천연오일, 방부제 또는 살균제로 이루어진 그룹에서 선택된 1종 이상의 첨가제 0.1 내지 35중량%를 더욱 포함하고, 상기한 폴리프로필렌이 단독 중합체 형태인 것을 특징으로 하고 방법.
  18. (a) 평균분자량이 500 내지 300,000이고, 실질적으로 순수한 폴리프로필렌 단독중합체 고체형태인 폴리프로필렌 0.01 내지 40중량%, (b) 실리콘 오일 0.1 내지 50중량%, (c) 조성물을 구성하는 성분들이 에멀젼 형태로 유지되도록 보조작용을 하는 유화제 0.01 내지 8중량%, 및 (d) 부식방지제 0.01 내지 5중량%와, 잔부의 액체 담체를 포함하여 이루어지는 것을 특징으로 하는 액체담체계 다이캐스팅용 윤활제/이형제 조성물.
  19. 제18항에 있어서, 상기 성분 (a)가 0.1 내지 15중량%의 양으로 존재하고, 성분 (b)가 0.5 내지 13중량%의 양으로 존재하고, 성분 (c)가 0.1 내지 5중량%의 양으로 존재하고, 성분 (d)가 0.1 내지 3중량%의 양으로 존재하는 것을 특징으로 하는 조성물.
  20. 제18항에 있어서, 상기한 액체 담체가 물인 것을 특징으로 하는 조성물.
  21. 제19항에 있어서, 상기한 조성물이 합성 또는 천연오일, 방부제 또는 살균제로 이루어진 그룹에서 선택된 1종 이상의 첨가제 0.02 내지 35중량%를 더욱 포함하는 것을 특징으로 하는 조성물.
  22. 제18항에 있어서, 상기 성분 (a)가 0.02 내지 20중량%의 양으로 존재하고, 성분 (b)가 0.1 내지 23중량%의 양으로 존재하고, 성분 (c)가 0.02 내지 6중량%의 양으로 존재하고, 성분 (d)가 0.01 내지 4중량%의 양으로 존재하며, 상기 폴리프로필렌의 평균분자량이 2500 내지 10,000인 것을 특징으로 하는 조성물.
  23. 제22항에 있어서, 상기한 액체 담체가 물인 것을 특징으로 하는 조성물.
  24. 제23항에 있어서, 상기한 조성물이 합성 또는 천연오일, 방부제 또는 살균제로 이루어진 그룹에서 선택된 1종 이상의 첨가제 0.1 내지 35중량%를 더욱 포함하는 것을 특징으로 하는 조성물.
KR1019930016415A 1992-08-27 1993-08-24 금속의다이캐스팅용윤활제조성물및다이캐스팅방법 KR100303128B1 (ko)