KR0121195B1

KR0121195B1 - Adhesive tape

Info

Publication number: KR0121195B1
Application number: KR1019940007109A
Authority: KR
Inventors: 이용인
Original assignee: 이용인; 신화물산주식회사
Priority date: 1994-04-04
Filing date: 1994-04-04
Publication date: 1997-11-04
Also published as: KR950029327A

Abstract

The adhesive tape used to fix the Braun tube of an image equipment with an explosion-proof band is produced by the following; a fiber mesh cloth is used as a substrate, an adhesive layer is formed on one side of the fiber mesh cloth and a coating layer on the other side of that with a resin of two group no having a compatability that is, the mixture composition of low melting point resin and high melting point resin. The characteristic of the adhesive tape according to this invention has no specified melting point in the range of a definite temperature.

Description

Adhesive tape with wide melting point

도면은 본 발명 점착테이프의 단면을 나타낸 것이다.The figure shows the cross section of the adhesive tape of this invention.

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

1 : 점착제층 2 : 섬유망포층1: pressure-sensitive adhesive layer 2: fiber mesh cloth layer

3 : 피막층 4 : 고융점수지3: film layer 4: high melting point resin

5 : 저융점수지 7 : 이형제층5: low melting point resin 7: release agent layer

본 발명은 텔레비젼과 같은 영상 기구에 사용되는 브라운관을 방폭벤드(防爆 Band)로 고정시키는데 사용되는 점착테이프에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to pressure-sensitive adhesive tapes used to fix CRTs in explosion-proof bends used in imaging equipment such as televisions.

브라운관은 내부를 고도의 진공으로 유지하여야 하기 때문에 벽면에 왜곡(歪曲)현상이 일어나기 쉽고 외부의 충격으로 쉽게 파손될 우려가 있으므로 외측면을 금속성의 방폭벤드로 묶어 준 다음 이 방폭벤드를 이용하여 케이스에 고정시키는 방법으로 브라운관을 고정시킨다.Since the CRT must be maintained at a high degree of vacuum, the wall may be easily distorted, and may be easily damaged by external shocks. Fix the CRT in a fixed manner.

이때 방폭벤드가 브라운관을 고정시키는 힘을 브라운관 외측면에 유효하게 전달해 주기 위하여 방폭벤드와 브라운관 사이에 접착부재를 개재시켜야 한다. 이러한 접착부재를 개재시키지 않게 되면 벤드가 미끄러지거나 금속벤드와 유리로된 브라운관이 직접 강한 힘으로 접촉하게 되어 브라운관이 손상될 우려가 있을 뿐만 아니라 외부충격이나 사고에 의하여 브라운관이 폭발하는 경우 파편의 비산범위를 통제할 수 없게 된다.At this time, in order for the explosion-proof bend to effectively transmit the force for fixing the CRT to the CRT outer side, an adhesive member must be interposed between the Explosion-proof bend and the CRT. If the adhesive member is not interposed, the bend slips or the metal bend and the glass tube made of glass come into direct contact with a strong force, which may damage the tube and cause fragments to scatter when the tube is exploded by an external impact or accident. The range is out of control.

이러한 접착부재로서 점착테이프가 널리 이용되고 있다.As such an adhesive member, an adhesive tape is widely used.

본 발명은 섬유망포의 일면은 점착제층을 구성하고 섬유망포의 다른 일면은 상용성(相榕性)이 없고 융점이 다른 두가지 그룹의 수지중에서 선택된 수지를 혼용한 물질로 피막층을 구성시켜 광범위한 융점 범위를 갖도록 한 점착테이프에 관한 것이다.According to the present invention, one side of the fiber mesh fabric constitutes a pressure-sensitive adhesive layer, and the other side of the fiber mesh fabric is composed of a material mixed with a resin selected from two groups of resins having no compatibility and different melting points. It relates to an adhesive tape having a.

브라운관과 철제 벤드 사이에 테이프를 개재시켜 브라운관을 고정시키는 방법에 있어서 철제 벤드를 350∼400℃ 정도로 가열, 팽창시킨 후 냉각시킬 때의 철제벤드의 수축력에 의하여 고정시키는 방법(일명 Heat banding 방식 또는 Heat shrinkage-열수축, 방식이라함)과 철제벤드를 200℃ 이하의 낮은 온도로 가열시키고 80∼200℃의 저융점의 열용융성 점착제로 점착제층을 구성시킨 점착테이프를 개재시켜 열용융 점착제의 접착력으로 고정시키는 방법(일명 tension banding 방식 또는 POP 방식이라고 함)이 있다. 열수축 방식은 접착력은 강하나 고온에서 작업이 이루어지므로 자동화에 어려움이 있고 텐숀벤딩 방식은 접착력은 떨어지나 비교적 저온에서 수행하므로 자동화에 적합한 이점이 있다.In the method of fixing the brown tube by interposing a tape between the brown tube and the iron bend, the iron bend is fixed by the contraction force of the iron bend when the iron bend is heated and expanded to about 350 to 400 ° C. and cooled (aka heat banding method or heat shrinkage-heat shrink) and the iron bend to a low temperature of 200 ° C or less, and a heat-melting adhesive having a low melting point of 80 to 200 ° C. There is a method of fixing (called tension banding method or POP method). The heat shrink method is difficult to automate because the adhesive force is strong but the work is performed at a high temperature, and the tension bending method is suitable for automation because it is performed at a relatively low temperature although the adhesive force is inferior.

따라서 종래의 점착테이프는 브라운관의 고정방식에 따라 서로 다른 융점을 갖는 점착테이프를 각각 별도로 사용하지 않으면 않되었다.Therefore, the conventional adhesive tape had to use a separate adhesive tape having a different melting point according to the fixing method of the CRT.

공정에 따라 이종의 점착테이프를 사용하게 됨에 따라 점착테이프를 표준화하기가 어렵게 되고 공정별로 별도의 점착테이프를 준비 관리하여야 한다는 불편을 감소하고 있는 실정이다.As different types of adhesive tapes are used depending on the process, it is difficult to standardize the adhesive tapes and the inconvenience of preparing and managing a separate adhesive tape for each process is reduced.

본 발명의 목적은 금속벤드와 접촉되는 피막층의 융점이 200℃ 이상의 고융점 범위와 80℃ 이하의 저융점 범위를 동시에 만족시켜 주므로서 열수축 방식에 의한 브라운관 고정방식이나 텐숀방식에 의한 브라운관 고정방식에 모두 적합한 점착테이프를 제공하고저 하는데 있다.It is an object of the present invention to satisfy the high melting point range of 200 ° C. or higher and the low melting point range of 80 ° C. or lower while simultaneously satisfying the melting point of the coating layer in contact with the metal bend. All are to provide a suitable adhesive tape.

이하 본 발명의 점착테이프 제조방법을 실시예를 들어 설명한다.Hereinafter, the adhesive tape manufacturing method of the present invention will be described with reference to Examples.

[실시예]EXAMPLE

염화비닐수지(융점 : 212℃) 100중량부를 메틸 에틸 케톤 300중량부에 용해하여 용액 A를 얻는다. 다음 비닐클로라이드의 비닐 이소부틸 에텔(융점 75℃) 100중량부를 톨루엔 300중량부에 융해시켜 용액 B를 얻는다.100 parts by weight of vinyl chloride resin (melting point: 212 ° C.) is dissolved in 300 parts by weight of methyl ethyl ketone to obtain solution A. Next, 100 parts by weight of vinyl isobutyl ether of vinyl chloride (melting point 75 ° C.) is melted to 300 parts by weight of toluene to obtain solution B.

상기 용액 A와 B를 A와 B의 혼합비율로 2 : 1의 용량비로 혼합한다. 필요한 경우 중점제의 첨가로 점도를 조절하여 코팅재를 만든다.The solutions A and B are mixed in a mixing ratio of A and B at a volume ratio of 2: 1. If necessary, the viscosity is controlled by the addition of a midpoint agent to form a coating.

여기에서 사용되는 점착제는 이 분야에서 이미 사용되고 있는 아크릴계의 공지의 점착제의 일종이다.The adhesive used here is a kind of acryl-type known adhesive already used in this field.

이형지에 상기의 아크릴계 점착제를 도포한 후 건조장치에서 용제를 완전히 휘발시켜 점착제층(1)을 형성시키고 이 점착제층(1)에 64목 정도의 나이론 섬유망포(2)를 합지(合地)한다.After applying the acrylic adhesive to the release paper, the solvent is completely volatilized in a drying apparatus to form an adhesive layer (1), and the nylon fiber mesh cloth (2) of about 64 necks is laminated on the adhesive layer (1). .

나이론 섬유망포층에 상기의 피막층(3)을 형성시켜 주기 위하여 상기의 코팅재를 도포한 후 건조장치에서 용제의 휘발, 건조시켜 피막층(3)를 형성한다. 다음 피막층(3)의 표면에 이형제를 도포하여 이형제층(7)을 형성시킨다.In order to form the coating layer 3 on the nylon fiber mesh layer, after coating the coating material, a solvent is volatilized and dried in a drying apparatus to form the coating layer 3. Next, a release agent is applied to the surface of the coating layer 3 to form the release agent layer 7.

나이론 섬유망포 대신에 유리섬유, 폴리에스텔섬유, 아크릴섬유, 면섬유로 된 망포나 이들을 합사한 혼방 섬유망포를 사용할 수도 있다. 또한 아크릴계 점착제 대신에 고무계 점착제를 사용할 수 있다.Instead of nylon fiber mesh cloth, mesh cloth made of glass fiber, polyester fiber, acrylic fiber, cotton fiber or blended fiber fiber cloth of these may be used. In addition, a rubber pressure sensitive adhesive can be used instead of the acrylic pressure sensitive adhesive.

이와같이 제조된 점착테이프 200℃ 이하의 낮은 온도에서는 물론 400℃ 이상의 높은 온도에서도 철제벤드의 가온 온도에 따라 융착될 수 있다.The adhesive tape thus prepared may be fused according to the heating temperature of the iron bend at a low temperature of 200 ° C. or less, as well as a high temperature of 400 ° C. or more.

이 점착테이프는 철제벤드의 가열온도인 200∼400℃ 범위내 어느 온도에서나 용융된다. 즉, 일정온도 범위내에서 특정융점을 갖지 않고 철제벤드의 가온온도에 따라 융착되는 특징을 갖게 된다.The adhesive tape is melted at any temperature within the range of 200 to 400 ° C., which is the heating temperature of the iron bend. That is, it does not have a specific melting point within a certain temperature range is characterized by being fused according to the heating temperature of the iron bend.

여기에서 융점 200℃ 이상의 수지 중에서 선택된 고융점수지와 융점 80℃ 이하의 수지중에서 선택된 저융점수지는 서로 상용성(相榕性)이 없어야 한다.Here, the high melting point resin selected from the resin having a melting point of 200 ° C. or higher and the low melting point resin selected from the resin having a melting point of 80 ° C. or lower should not be compatible with each other.

고융점수지로서는 가교성 아크릴공중합체(acryl copolymer), 우레탄(urethane)수지, 에폭시(Epoxy)수지, 폴리에스텔(polyester)수지, 페놀(phenol)수지, 멜라민(Melamine)수지, 폴리아세탈(polyacetal), 폴리염화비닐(polyvinyl chloride), 아미노(Amino) 수지 중에서 선택하여 사용할 수 있다.High melting point resins include crosslinkable acrylic copolymers, urethane resins, epoxy resins, polyester resins, phenol resins, melamine resins, and polyacetals. , Polyvinyl chloride, amino (Amino) resin can be selected and used.

저융점수지로서는 열가소성 아크릴 공중합체 로진에스텔(Rosin ester), 비닐클라이드의 이소부틸에텔수지, 아크릴비닐아세탈수지, 에틸렌비닐아세테이트수지, 폴리에텔렌왁스, 에스텔왁스 등에서 선택하여 사용할 수 있다.The low melting point resin can be selected from thermoplastic acrylic copolymer rosin ester, isobutyl ether resin of vinyl chloride, acryl vinyl acetal resin, ethylene vinyl acetate resin, polyethylene wax, ester wax and the like.

본 발명 테이프의 특징은 브라운관의 고온 고정 방식에서나 저온 고정 방식 모두에 적합하다는데 있다.The characteristic of the tape of the present invention is that it is suitable for both the high temperature fixing method and the low temperature fixing method of the CRT.

고온 고정방식에서는 종래의 방법과 같이 이용하는데 아무 문제가 없으며 저온 고정 방식에서의 접착 메카니즘은 다음과 같다.In the high temperature fixing method, there is no problem in using it as in the conventional method, and the adhesion mechanism in the low temperature fixing method is as follows.

본 발명의 피막층(3)은 80℃ 이하의 저융점 수지(5)와 200℃ 이상의 고융점 수지(4)의 균일한 혼합물로 구성되어 있고 상기 그중의 수지가 서로 상용성이 없으며 저융점수지의 양이 고융점수지양의 50% 정도 밖에 되지 않으므로 저융점수지가 고융점수지 중에 균일하게 분포된 상태로 구성된다.The coating layer (3) of the present invention is composed of a homogeneous mixture of a low melting point resin (5) of 80 ° C. or lower and a high melting point resin (4) of 200 ° C. or higher. Since the amount is only about 50% of the high melting point balance, the low melting point resin is composed of a uniformly distributed state in the high melting point resin.

따라서 이 피막층의 표면이 저융점수지의 융점이상, 예를 들면 150℃ 정도로 가열된다 하더라도 저융점수지는 고융점수지로 둘러 쌓여 있으므로 용융되지 않는다.Therefore, even if the surface of the coating layer is heated above the melting point of the low melting point resin, for example, about 150 ° C., the low melting point resin is surrounded by the high melting point resin and thus does not melt.

브라운관에 철제벤드를 고정시킬때 본 발명의 점착테이프를 브라운관 주위에 점착제면 쪽으로 감는다. 그 표면에 가열된 철제벤드가 테이프의 피막층과 접촉되도록 감는다.When fixing the iron bend to the CRT, the adhesive tape of the present invention is wound around the CRT toward the adhesive side. The iron bend heated on the surface is wound to be in contact with the film layer of the tape.

철제벤드와 테이프가 압착되는 순간 압착되는 힘에 의하여 피막층이 파괴되면 저융점수지가 융점이상으로 가열된 철제벤드와 접촉되면서 용융되며 섬유망포를 중심으로 점착제와 용융된 저융점수지가 혼합되면서 철제벤드의 자연냉각과 함께 접착 고정되는 것이다.When the film layer is destroyed by the pressing force when the steel bend and the tape are pressed, the low melting point resin is melted in contact with the heated iron bend above the melting point, and the adhesive and the molten low melting point resin are mixed around the fiber mesh cloth. Along with the natural cooling of the adhesive will be fixed.

본 발명의 점착테이프는 종래의 열수축방식에서 종래의 열수축 방식에서 사용하던 테이프는 피막층 200℃ 이상의 고융점을 갖는 폴리에스텔 필름등을 적층(Lamination)하여 사용하였으나 본 발명의 테이프 제조공정에서는 필름적층공정이 필요없게 되며, 테이프 생산 전공정을 한코팅 설비에서 일괄 생산할 수 있어 생산성이 향상될 뿐 아니라 브라운관 조립공정의 생산성도 크게 향상시킬 수 있으며 피막층(3)의 두께를 임의로 조정할 수 있고 색상도 임의로 조정할 수 있다는 이점을 갖게 된다.In the adhesive tape of the present invention, the tape used in the conventional heat shrink method is used by laminating a polyester film having a high melting point of 200 ° C. or higher on the coating layer, but in the tape manufacturing process of the present invention, the film lamination step is performed. Since the entire tape production process can be produced in one coating facility, the productivity can be improved, and the productivity of the CRT assembly process can be greatly improved, and the thickness of the coating layer 3 can be arbitrarily adjusted, and the color can be arbitrarily adjusted. You will have the advantage that you can.

또한 테이프 피막층(3)의 융점이 200℃ 이상의 고융점 범위와 80℃ 이하의 저융점 범위를 동시에 만족시킬 수 있으므로 열수축방식에 의한 브라운관 고정방법이나 텐숀방식에 의한 브라운관 고정방식 모두에 적합하다.Further, since the melting point of the tape coating layer 3 can satisfy both the high melting point range of 200 ° C. or higher and the low melting point range of 80 ° C. or lower, it is suitable for both the CRT fixing method by the heat shrink method and the CRT fixing method by the tension method.

또한 브라운관의 고정작업 중 절단하고저 하는 경우 필름을 적층한 테이프는 절단이 용이하지 않아 절단기(Cutter)의 칼날을 자주 교체해 주어야 하나 본 발명의 테이프는 섬유망포의 결에 따라 세로 또는 가로방향으로 손으로도 쉽게 절단할 수 있는 이점이 있다.In addition, when cutting during the fixing of the CRT, the laminated film tape is not easy to cut, so the blade of the cutter must be replaced frequently, but the tape of the present invention is hand-held vertically or horizontally according to the texture of the fiber cloth. There is also an advantage that can be easily cut.

Claims

In the pressure-sensitive adhesive tape, a fibrous cloth is used as a base material, and an adhesive layer is formed on one surface of the fiber cloth, and a coating layer is formed of a mixed composition of a low melting point resin and a high melting point resin having no compatibility on the other surface. An adhesive tape having a broad melting point in which the mold layer is formed on the surface.

The low melting point resin which is incompatible with the high melting point resin is a thermoplastic acrylic copolymer, rosin ester, isobutyl ethyl resin of vinyl chloride, acryl vinyl acetal resin, ethylene vinyl acetate resin, polyethylene wax, ester wax. High melting point resin which is incompatible with low melting point resin is selected from crosslinkable acrylic copolymer, urethane resin, epoxy resin, polyester resin, phenol resin, melamine resin, polyacetal resin, polyvinyl chloride, amino resin Adhesive tape with a wide melting point.

The pressure-sensitive adhesive tape of claim 1, wherein the fiber mesh is a nylon fiber, an acrylic fiber, a glass fiber, a polyester fiber, a cotton fiber, or a mixed fiber mesh cloth in which the fibers are fused together.