JPWO2011145524A1 - Composition and adhesive - Google Patents
Composition and adhesive Download PDFInfo
- Publication number
- JPWO2011145524A1 JPWO2011145524A1 JP2012515863A JP2012515863A JPWO2011145524A1 JP WO2011145524 A1 JPWO2011145524 A1 JP WO2011145524A1 JP 2012515863 A JP2012515863 A JP 2012515863A JP 2012515863 A JP2012515863 A JP 2012515863A JP WO2011145524 A1 JPWO2011145524 A1 JP WO2011145524A1
- Authority
- JP
- Japan
- Prior art keywords
- component
- meth
- acrylate
- adhesive
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
高い接着強度と高い耐水性を示す組成物の提供。下記（Ａ）〜（Ｄ）成分を含有してなる組成物。（Ａ）成分は、一般式〔１〕で表されるイソシアヌル環誘導体（Ｂ）成分は、水酸基を有する（メタ）アクリレート、（Ｃ）成分は、シランカップリング剤、（Ｄ）成分は、光重合開始剤を含有する組成物。更にアルキル基を有する（メタ）アクリレートを含有しても良い。偏光フィルム用、シクロオレフィンポリマー用、ポリカーボネート用、トリアセチルセルロース用、ポリビニルアルコール用、ガラス用の接着剤として使用しても良い。Provision of a composition exhibiting high adhesive strength and high water resistance. A composition comprising the following components (A) to (D). (A) component is an isocyanuric ring derivative represented by the general formula [1] (B) component is a (meth) acrylate having a hydroxyl group, (C) component is a silane coupling agent, (D) component is light A composition containing a polymerization initiator. Furthermore, you may contain the (meth) acrylate which has an alkyl group. You may use as an adhesive agent for polarizing films, for cycloolefin polymers, for polycarbonate, for triacetyl cellulose, for polyvinyl alcohol, and for glass.
Description
本発明は、組成物に関し、とりわけ当該組成物からなる接着剤に関する。 The present invention relates to a composition, and more particularly to an adhesive comprising the composition.
シクロオレフィンポリマーは、電子材料、光学レンズ及び医療材料等の用途に使用されている。シクロオレフィンポリマーは極性が小さく、表面に多くの官能基を持たないことから、難被着体として知られている。このようなシクロオレフィン系樹脂を接着する接着剤としては、溶剤型接着剤やホットメルト接着剤が挙げられる。 Cycloolefin polymers are used in applications such as electronic materials, optical lenses and medical materials. Cycloolefin polymers are known as difficult adherends because of their low polarity and lack of many functional groups on the surface. Examples of the adhesive for adhering such a cycloolefin-based resin include a solvent-type adhesive and a hot-melt adhesive.
オレフィン系樹脂を接着する方法としては、特許文献１に開示されているように、プライマーによる処理を行ってから瞬間接着剤により接着するという方法が挙げられる。 As a method for adhering the olefin-based resin, as disclosed in Patent Document 1, there is a method of adhering with an instantaneous adhesive after performing a treatment with a primer.
特許文献２には、ガラス、金属、ポリフェニレンスルフィドのような結晶性エンジニアリングプラスチック、ポリカーボネートのような透明性エンジニアリングプラスチック等の各種プラスチック材料等、様々な被着体に対して一様に高い接着強さを有し、耐熱性および耐湿性が良好で、剛性にも優れるエネルギー線硬化性樹脂組成物が開示されている。当該樹脂組成物は、分子量が５００〜５０００のジエン系或いは水素添加されたジエン系の（メタ）アクリレート、特定構造の飽和炭化水素をエステル結合を介して有する単官能（メタ）アクリレート、水酸基含有（メタ）アクリレート、多官能性（メタ）アクリレート、光重合開始剤、および酸化防止剤を含有する。 Patent Document 2 discloses uniform high adhesion strength to various adherends such as glass, metal, crystalline engineering plastic such as polyphenylene sulfide, and various plastic materials such as transparent engineering plastic such as polycarbonate. An energy ray-curable resin composition that has good heat resistance and moisture resistance and excellent rigidity is disclosed. The resin composition contains a diene (meth) acrylate having a molecular weight of 500 to 5000 or a hydrogenated diene (meth) acrylate, a monofunctional (meth) acrylate having a saturated hydrocarbon having a specific structure via an ester bond, and a hydroxyl group-containing ( Contains a (meth) acrylate, a polyfunctional (meth) acrylate, a photopolymerization initiator, and an antioxidant.
液晶表示関連分野等に用いられる偏光フィルムは、通常ポリビニルアルコール（ＰＶＡ）にヨウ素や顔料を吸着させたものを一軸延伸して製造される。このポリビニルアルコール系偏光フィルムは熱や水分により収縮し、偏光性能の低下をきたすため、その表面に保護フィルムが貼合されたものが偏光板である。 A polarizing film used in a liquid crystal display-related field or the like is usually produced by uniaxially stretching a material obtained by adsorbing iodine or a pigment to polyvinyl alcohol (PVA). Since this polyvinyl alcohol-type polarizing film shrinks due to heat or moisture and lowers the polarizing performance, a polarizing plate is a film in which a protective film is bonded to the surface.
偏光板の保護フィルムには通常、トリアセチルセルロースが使用されている。 Usually, triacetyl cellulose is used for the protective film of the polarizing plate.
偏光フィルムに保護フィルムを貼合せるための接着剤としては、従来からポリビニルアルコール系の水溶液が広く使用されている（特許文献３）。 Conventionally, polyvinyl alcohol-based aqueous solutions have been widely used as adhesives for laminating a protective film to a polarizing film (Patent Document 3).
特許文献４は、半導体素子と、半導体素子搭載用支持部材とを接着するための接着剤に関し、アルカリ現像液によるパターン形成性に優れ、露光後の十分な再接着性を有し、フィルム状に形成した場合には低温貼り付け性にも優れた感光性接着剤組成物を提供することを目的として、（Ａ）アルカリ可溶性ポリマーと、（Ｂ）熱硬化性樹脂と、（Ｃ）一種又は複数の放射線重合性化合物と、（Ｄ）光開始剤とを含有し、組成物中の全放射線重合性化合物の混合物の５％重量減少温度が２００℃以上である感光性接着剤組成物が開示されている。そして、放射線重合性化合物としてイソシアヌル酸エチレンオキサイド変性ジ又はトリアクリレートが挙げられており、これにより硬化後の接着性及び耐熱性を特に良好なものとすることが記載されている。 Patent Document 4 relates to an adhesive for adhering a semiconductor element and a support member for mounting a semiconductor element, and is excellent in pattern formability with an alkali developer, has sufficient re-adhesion after exposure, and is in a film form. For the purpose of providing a photosensitive adhesive composition having excellent low-temperature sticking properties when formed, (A) an alkali-soluble polymer, (B) a thermosetting resin, and (C) one or more. A photosensitive adhesive composition containing a radiation polymerizable compound of (D) and (D) a photoinitiator, wherein the 5% weight loss temperature of the mixture of all radiation polymerizable compounds in the composition is 200 ° C. or more is disclosed. ing. And as a radiation polymerizable compound, isocyanuric acid ethylene oxide modified di or triacrylate is mentioned, and it is described that this makes the adhesiveness and heat resistance after curing particularly good.
溶剤型接着剤は、溶剤を使用する。溶剤型接着剤は、人体に有害である上、溶剤の揮発に時間がかかり、接着強度自体も十分なものが得られない。 A solvent type adhesive uses a solvent. Solvent-type adhesives are harmful to the human body, and it takes time for the solvent to evaporate, so that sufficient adhesive strength itself cannot be obtained.
ホットメルト接着剤は、接着剤を溶融させる手間及び装置が必要である。この接着剤も十分な接着強度を得ることができない。ホットメルト接着剤を用いる場合、シクロオレフィンポリマーを予め加熱しておけば、接着強度は向上するが、樹脂が変形してしまうという新たな問題が発生する。 The hot melt adhesive requires labor and equipment for melting the adhesive. This adhesive also cannot obtain sufficient adhesive strength. When a hot melt adhesive is used, if the cycloolefin polymer is heated in advance, the adhesive strength is improved, but a new problem that the resin is deformed occurs.
特許文献１に開示されている接着方法によれば、プライマー処理に手間がかかるという問題がある上、接着強度も十分なものが得られない。 According to the adhesion method disclosed in Patent Document 1, there is a problem that it takes time and effort for primer treatment, and a sufficient adhesion strength cannot be obtained.
特許文献２は、（メタ）アクリレートを含有することを特徴とするエネルギー線硬化性樹脂組成物が開示されている。しかし、イソシアヌル酸誘導体を含有する記載はされておらず、且つトリアセチルセルロースを被着体とした記載はされていない。 Patent Document 2 discloses an energy ray curable resin composition containing (meth) acrylate. However, there is no description that contains an isocyanuric acid derivative, and no description that uses triacetyl cellulose as an adherend.
特許文献３は、各種光学フィルムに対して浸透性を有する基材浸透性モノマーを使用した接着剤組成物が開示されている。このような組成物は基材フィルムを侵し光学特性低下の点で好ましくない。 Patent Document 3 discloses an adhesive composition using a base-penetrating monomer that has permeability to various optical films. Such a composition is unfavorable in that it erodes the base film and deteriorates optical properties.
特許文献４は、トリアセチルセルロースを被着体とした記載はされておらず、且つ本発明で必須のシランカップリング剤を必須としない。本発明は熱硬化性樹脂とアルカリ可溶性ポリマーを必須としない。熱硬化性樹脂とアルカリ可溶性ポリマーを必須とした場合、紫外線による硬化阻害及び接着性の点で、好ましくない。本発明は水酸基を有する(メタ)アクリレートを、接着性を向上するために、必須としている。 Patent Document 4 does not describe triacetylcellulose as an adherend, and does not require an essential silane coupling agent in the present invention. The present invention does not require a thermosetting resin and an alkali-soluble polymer. When a thermosetting resin and an alkali-soluble polymer are essential, it is not preferable from the viewpoint of curing inhibition by UV rays and adhesiveness. In the present invention, a (meth) acrylate having a hydroxyl group is essential for improving adhesiveness.
本発明はそのような実情に鑑みてなされたものである。本発明は、例えば、シクロオレフィンポリマー、ポリカーボネート、トリアセチルセルロース、ポリビニルアルコール、及びガラスに対して、短時間で十分な接着強度を発現でき、高い耐水性をもつ無溶剤型で環境に優しい接着剤の提供を目的とする。 The present invention has been made in view of such circumstances. The present invention is, for example, a solvent-free and environmentally friendly adhesive that can exhibit sufficient adhesive strength in a short time to cycloolefin polymer, polycarbonate, triacetyl cellulose, polyvinyl alcohol, and glass, and has high water resistance. The purpose is to provide.
本発明者は、前記の課題を解決するべく鋭意研究を重ね、本発明に至ったものである。 The present inventor has intensively studied to solve the above-described problems and has arrived at the present invention.
即ち、本発明は一側面において、下記（Ａ）〜（Ｄ）成分を含有してなる組成物である。
（Ａ）成分は、一般式〔１〕で表されるイソシアヌル環誘導体（一般式〔１〕中のＸ1及びＸ2は（メタ）アクリロイルオキシ基を示し、Ｘ3はヒドロキシル基又は（メタ）アクリロイルオキシ基を示し、Ｒ1、Ｒ2及びＲ3は炭素数１〜４の炭化水素基を示す。）
（Ｃ）成分は、シランカップリング剤
（Ｄ）成分は、光重合開始剤That is, in one aspect, the present invention is a composition containing the following components (A) to (D).
Component (A) is an isocyanuric ring derivative represented by the general formula [1] (X 1 and X 2 in the general formula [1] represent a (meth) acryloyloxy group, and X 3 represents a hydroxyl group or (meth) An acryloyloxy group is shown, and R 1 , R 2 and R 3 are hydrocarbon groups having 1 to 4 carbon atoms.)
本発明に係る組成物の一実施形態においては、更に（Ｅ）成分として、一般式〔２〕で表される（メタ）アクリレートを含有する。
一般式〔２〕 Ｒ−Ｏ−Ｒ’
（式中、Ｒは（メタ）アクリロイル基を示し、Ｒ’は炭素数５〜１８個のアルキル基を示す。）In one Embodiment of the composition based on this invention, (meth) acrylate represented by General formula [2] is further contained as (E) component.
General formula [2] R—O—R ′
(In the formula, R represents a (meth) acryloyl group, and R ′ represents an alkyl group having 5 to 18 carbon atoms.)
本発明に係る組成物の別の一実施形態においては、組成物の硬化物の貯蔵弾性率Ｅ’が０．０００００１〜１００００ＭＰａ（２３℃）の範囲内である。 In another embodiment of the composition according to the present invention, the storage elastic modulus E ′ of the cured product of the composition is in the range of 0.000001 to 10,000 MPa (23 ° C.).
本発明に係る組成物の更に別の一実施形態においては、（Ａ）成分が、イソシアヌル酸エチレンオキサイド変性トリ（メタ）アクリレート、イソシアヌル酸エチレンオキサイド変性ジ（メタ）アクリレート、イソシアヌル酸エチレンオキサイド変性トリ／ジ（メタ）アクリレート混合物、イソシアヌル酸プロピレンオキサイド変性トリ（メタ）アクリレート、イソシアヌル酸プロピレンオキサイド変性ジ（メタ）アクリレート、イソシアヌル酸ブチルオキサイド変性トリ（メタ）アクリレート及びイソシアヌル酸ブチルオキサイド変性ジ（メタ）アクリレートからなる群から選ばれる１種又は２種以上である。 In still another embodiment of the composition according to the present invention, the component (A) is an isocyanuric acid ethylene oxide modified tri (meth) acrylate, isocyanuric acid ethylene oxide modified di (meth) acrylate, isocyanuric acid ethylene oxide modified tri / Di (meth) acrylate mixture, isocyanuric acid propylene oxide modified tri (meth) acrylate, isocyanuric acid propylene oxide modified di (meth) acrylate, isocyanuric acid butyl oxide modified tri (meth) acrylate and isocyanuric acid butyl oxide modified di (meth) One or more selected from the group consisting of acrylates.
本発明に係る組成物の更に別の一実施形態においては、（Ａ）成分が組成物の５〜８０質量％を占め、（Ａ）成分及び（Ｂ）成分の合計１００質量部中、（Ａ）成分：（Ｂ）成分＝１０〜９９：１〜９０（質量比）であり、（Ｃ）成分の使用量は、（Ａ）成分及び（Ｂ）成分の合計１００質量部に対して、０．００１〜１０質量部であり、（Ｄ）成分の使用量は、（Ａ）成分及び（Ｂ）成分の合計１００質量部に対して、０．００１〜３０質量部である。 In still another embodiment of the composition according to the present invention, the component (A) occupies 5 to 80% by mass of the composition, and the total amount of the component (A) and the component (B) is 100 parts by mass. ) Component: (B) component = 10 to 99: 1 to 90 (mass ratio), and the usage amount of the (C) component is 0 with respect to 100 parts by mass of the total of the (A) component and the (B) component. 0.001 to 10 parts by mass, and the amount of component (D) used is 0.001 to 30 parts by mass with respect to a total of 100 parts by mass of component (A) and component (B).
本発明に係る組成物の更に別の一実施形態においては、（Ｅ）成分が、２−エチルへキシル（メタ）アクリレート、ノニル（メタ）アクリレート、イソデシル（メタ）アクリレート、ｎ−ラウリル（メタ）アクリレート及びトリデシル（メタ）アクリレートからなる群のうちの１種又は２種以上である。 In yet another embodiment of the composition according to the present invention, the component (E) is 2-ethylhexyl (meth) acrylate, nonyl (meth) acrylate, isodecyl (meth) acrylate, n-lauryl (meth). One or more of the group consisting of acrylate and tridecyl (meth) acrylate.
本発明に係る組成物の更に別の一実施形態においては、（Ａ）成分が組成物の５〜８０質量％を占め、（Ａ）成分及び（Ｂ）成分の合計１００質量部中、（Ａ）成分：（Ｂ）成分＝１０〜９９：１〜９０（質量比）であり、（Ａ）成分、（Ｂ）成分及び（Ｅ）成分の合計１００質量部中、（Ａ）成分：（Ｂ）成分：（Ｅ）成分＝１０〜８０：１〜７０：１５〜８０（質量比）であり、（Ｃ）成分の使用量は、（Ａ）成分、（Ｂ）成分及び（Ｅ）成分の合計１００質量部に対して、０．００１〜１０質量部であり、（Ｄ）成分の使用量は、（Ａ）成分、（Ｂ）成分及び（Ｅ）成分の合計１００質量部に対して、０．００１〜３０質量部である。 In still another embodiment of the composition according to the present invention, the component (A) occupies 5 to 80% by mass of the composition, and the total amount of the component (A) and the component (B) is 100 parts by mass. ) Component: (B) component = 10 to 99: 1 to 90 (mass ratio), and (A) component: (B) in a total of 100 parts by mass of (A) component, (B) component and (E) component. ) Component: (E) component = 10-80: 1-70: 15-80 (mass ratio), and the amount of component (C) used is that of component (A), component (B) and component (E). It is 0.001-10 mass parts with respect to a total of 100 mass parts, and the usage-amount of (D) component is with respect to a total of 100 mass parts of (A) component, (B) component, and (E) component. 0.001 to 30 parts by mass.
本発明は別の一側面において、本発明に係る組成物からなる接着剤である。 In another aspect, the present invention is an adhesive comprising the composition according to the present invention.
本発明に係る接着剤は一実施形態において、偏光フィルム用接着剤である。 In one embodiment, the adhesive according to the present invention is an adhesive for a polarizing film.
本発明に係る接着剤は別の一実施形態において、シクロオレフィンポリマー用接着剤である。 In another embodiment, the adhesive according to the present invention is a cycloolefin polymer adhesive.
本発明に係る接着剤は更に別の一実施形態において、シクロオレフィンポリマー、ポリカーボネート、トリアセチルセルロース、ポリビニルアルコール及びガラスからなる群から選ばれる１種又は２種以上の基材用に使用される。 In still another embodiment, the adhesive according to the present invention is used for one or more substrates selected from the group consisting of cycloolefin polymer, polycarbonate, triacetylcellulose, polyvinyl alcohol and glass.
本発明は更に別の一側面において、本発明に係る接着剤を用いて被着体同士を接着してできた接着体である。 In yet another aspect, the present invention is an adhesive body formed by bonding adherends to each other using the adhesive according to the present invention.
本発明に係る接着体は一実施形態において、被着体が、シクロオレフィンポリマー、ポリカーボネート、トリアセチルセルロース、ポリビニルアルコール及びガラスからなる群から選ばれる１種又は２種以上である。 In one embodiment of the adhesive according to the present invention, the adherend is one or more selected from the group consisting of cycloolefin polymer, polycarbonate, triacetylcellulose, polyvinyl alcohol and glass.
本発明の組成物は、シクロオレフィンポリマー、ポリカーボネート、トリアセチルセルロース、ポリビニルアルコール、及びガラスに対して、短時間で十分な高い接着強度と高い耐水性を示すという特徴を有する。そして、本発明の組成物は、無溶剤型であるため、環境に優しい。 The composition of the present invention is characterized by exhibiting sufficiently high adhesive strength and high water resistance in a short time with respect to cycloolefin polymer, polycarbonate, triacetyl cellulose, polyvinyl alcohol, and glass. And since the composition of this invention is a solventless type, it is environmentally friendly.
（Ａ）成分は、一般式〔１〕で表されるイソシアヌル環誘導体（一般式〔１〕〕中のＸ1及びＸ2は（メタ）アクリロイルオキシ基を示し、Ｘ3はヒドロキシル基又は（メタ）アクリロイルオキシ基を示し、Ｒ1、Ｒ2及びＲ3は炭素数１〜４の炭化水素基、典型的にはアルキレン基を示す。）である。Component (A) is an isocyanuric ring derivative represented by general formula [1] (X 1 and X 2 in general formula [1] represent a (meth) acryloyloxy group, and X 3 represents a hydroxyl group or (meta ) Represents an acryloyloxy group, and R 1 , R 2 and R 3 represent a hydrocarbon group having 1 to 4 carbon atoms, typically an alkylene group.
イソシアヌル酸誘導体の中では、耐水性の点で、イソシアヌル酸エチレンオキサイド変性ジ（メタ）アクリレート、イソシアヌル酸エチレンオキサイド変性トリ（メタ）アクリレート、イソシアヌル酸エチレンオキサイド変性トリ／ジ（メタ）アクリレート混合物からなる群のうちの１種又は２種以上が好ましい。 Among the isocyanuric acid derivatives, isocyanuric acid ethylene oxide modified di (meth) acrylate, isocyanuric acid ethylene oxide modified tri (meth) acrylate, and isocyanuric acid ethylene oxide modified tri / di (meth) acrylate mixture in terms of water resistance. One or more of the groups are preferred.
（Ｂ）水酸基含有（メタ）アクリレートとしては、１個以上の（メタ）アクリロイル基を有するモノマーの中で、水酸基を含有するものが挙げられる。 Examples of the (B) hydroxyl group-containing (meth) acrylate include those having a hydroxyl group among monomers having one or more (meth) acryloyl groups.
水酸基含有モノマーとしては、２−ヒドロキシエチル（メタ）アクリレート、２−ヒドロキシブチル（メタ）アクリレート、４−ヒドロキシブチル（メタ）アクリレート、２−ヒドロキシプロピル（メタ）アクリレート、脂肪族エポキシ（メタ）アクリレート（ダイセルＵＣＢ社製「Ｅｂｅｃｒｙｌ１１１」「Ｅｂｅｃｒｙｌ１１２」）、エピクロロヒドリン（以下ＥＣＨという）変性アリル（メタ）アクリレート（ナガセ化成社製「デコナールアクリレートＤＡ−１１１」）、ブタンジオールモノ（メタ）アクリレート、水酸基含有カプロラクトン（メタ）アクリレート、ジプロピレングリコール（メタ）アクリレート、ＥＣＨ変性フェノキシ（メタ）アクリレート、ポリプロピレングリコール（メタ）アクリレート（ｎ＝５−１３）、エチレンオキサイド（以下ＥＯという）変性コハク酸（メタ）アクリレート、β−カルボキシエチル（メタ）アクリレート、水酸基含有ジアクリル化イソシアヌレート、ＥＣＨ変性フタル酸ジ（メタ）アクリレート、ＥＣＨ変性プロピレングリコールジ（メタ）アクリレート、プロピレンオキサイド（以下ＰＯ変性という）ビスフェノールＡジグリシジルエーテルジ（メタ）アクリレート、ＥＣＨ変性グリセロールトリ（メタ）アクリレート、ＥＯ変性リン酸メタクリレート、ポリエチレングリコール−ポリプロピレングリコールメタクリレート、２−ヒドロキシ−３−フェノキシプロピル（メタ）アクリレート等が挙げられる。これらの１種又は２種以上を使用しても良い。 As the hydroxyl group-containing monomer, 2-hydroxyethyl (meth) acrylate, 2-hydroxybutyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, aliphatic epoxy (meth) acrylate ( Daicel UCB “Ebecryl 111” “Ebecryl 112”), epichlorohydrin (hereinafter referred to as ECH) modified allyl (meth) acrylate (“Negase Chemical Co., Ltd.“ Deconal Acrylate DA-111 ”), butanediol mono (meth) acrylate, Hydroxyl group-containing caprolactone (meth) acrylate, dipropylene glycol (meth) acrylate, ECH-modified phenoxy (meth) acrylate, polypropylene glycol (meth) acrylate (n = 5-13), Ren oxide (hereinafter referred to as EO) modified succinic acid (meth) acrylate, β-carboxyethyl (meth) acrylate, hydroxyl group-containing diacrylated isocyanurate, ECH modified phthalic acid di (meth) acrylate, ECH modified propylene glycol di (meth) acrylate , Propylene oxide (hereinafter referred to as PO-modified) bisphenol A diglycidyl ether di (meth) acrylate, ECH-modified glycerol tri (meth) acrylate, EO-modified phosphate methacrylate, polyethylene glycol-polypropylene glycol methacrylate, 2-hydroxy-3-phenoxypropyl (Meth) acrylate etc. are mentioned. One or more of these may be used.
水酸基含有（メタ）アクリレートの中では、接着性の点で、２−ヒドロキシエチル（メタ）アクリレート、ＥＣＨ変性フェノキシ（メタ）アクリレート、２−ヒドロキシ−３−フェノキシプロピル（メタ）アクリレートからなる群のうちの１種以上が好ましく、２−ヒドロキシエチル（メタ）アクリレート及び／又は２−ヒドロキシ−３−フェノキシプロピル（メタ）アクリレートがより好ましい。 Among the hydroxyl group-containing (meth) acrylates, from the group consisting of 2-hydroxyethyl (meth) acrylate, ECH-modified phenoxy (meth) acrylate, and 2-hydroxy-3-phenoxypropyl (meth) acrylate, in terms of adhesiveness. One or more of these are preferable, and 2-hydroxyethyl (meth) acrylate and / or 2-hydroxy-3-phenoxypropyl (meth) acrylate are more preferable.
（Ｃ）成分は、シランカップリング剤である。シランカップリング剤としては、γ−クロロプロピルトリメトキシシラン、ビニルトリメトキシシラン、ビニルトリクロルシラン、ビニルトリエトキシシラン、ビニルプロピルトリメトキシシラン、ビニル−トリス（β−メトキシエトキシ）シラン、γ−メタクリロキシプロピルトリメトキシシラン、γ−アクリロキシプロピルトリメトキシシラン、β−（３，４−エポキシシクロヘキシル）エチルトリメトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、γ−メルカプトプロピルトリメトキシシラン、γ−アミノプロピルトリエトキシシラン、Ｎ−β−（アミノエチル）−γ−アミノプロピルトリメトキシシラン、Ｎ−β−（アミノエチル）−γ−アミノプロピルメチルジメトキシシラン、γ−ユレイドプロピルトリエトキシシラン、ヒドロキシエチル（メタ）アクリレートリン酸エステル、（メタ）アクリロキシオキシエチルアシッドフォスフェート、（メタ）アクリロキシオキシエチルアシッドフォスフェートモノエチルアミンハーフソルト等が挙げられる。これらの中では、接着性の点で、γ−グリシドキシプロピルトリメトキシシラン、γ−（メタ）アクリロキシプロピルトリメトキシシラン及びビニルプロピルトリメトキシシランからなる群のうちの１種又は２種以上が好ましく、γ−グリシドキシプロピルトリメトキシシランがより好ましい。 (C) A component is a silane coupling agent. As silane coupling agents, γ-chloropropyltrimethoxysilane, vinyltrimethoxysilane, vinyltrichlorosilane, vinyltriethoxysilane, vinylpropyltrimethoxysilane, vinyl-tris (β-methoxyethoxy) silane, γ-methacryloxy Propyltrimethoxysilane, γ-acryloxypropyltrimethoxysilane, β- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-amino Propyltriethoxysilane, N-β- (aminoethyl) -γ-aminopropyltrimethoxysilane, N-β- (aminoethyl) -γ-aminopropylmethyldimethoxysilane, γ-ureidopropyltriethoxysilane, Dorokishiechiru (meth) acrylate phosphate esters, (meth) acrylate Roxio carboxyethyl acid phosphate, and (meth) acrylate Roxio carboxyethyl acid phosphate Tomono ethylamine half salt and the like. Among these, in terms of adhesiveness, one or more of the group consisting of γ-glycidoxypropyltrimethoxysilane, γ- (meth) acryloxypropyltrimethoxysilane and vinylpropyltrimethoxysilane Is preferable, and γ-glycidoxypropyltrimethoxysilane is more preferable.
（Ｄ）成分は、光重合開始剤である。 The component (D) is a photopolymerization initiator.
光重合開始剤としては、紫外線重合開始剤や可視光重合開始剤等が挙げられる。紫外線重合開始剤としては、ベンゾイン系、ベンゾフェノン系、アセトフェノン系等が挙げられる。可視光重合開始剤としては、アシルホスフィンオキサイド系、チオキサントン系、メタロセン系、キノン系、α−アミノアルキルフェノン系等が挙げられる。 Examples of the photopolymerization initiator include an ultraviolet polymerization initiator and a visible light polymerization initiator. Examples of the ultraviolet polymerization initiator include benzoin, benzophenone, and acetophenone. Examples of visible light polymerization initiators include acylphosphine oxides, thioxanthones, metallocenes, quinones, and α-aminoalkylphenones.
光重合開始剤としては、ベンゾフェノン、４−フェニルベンゾフェノン、ベンゾイル安息香酸、２，２−ジエトキシアセトフェノン、ビスジエチルアミノベンゾフェノン、ベンジル，ベンゾイン、ベンゾイルイソプロピルエーテル、ベンジルジメチルケタール、１−ヒドロキシシクロヘキシルフェニルケトン、チオキサントン、２−メチルチオキサントン、２，４−ジメチルチオキサントン、イソプロピルチオキサントン、２，４−ジエチルチオキサントン、２，４−ジイソプロピルチオキサントン、１−（４−イソプロピルフェニル）２−ヒドロキシ−２−メチルプロパン−１−オン、１−（４−（２−ヒドロキシエトキシ）−フェニル）−２−ヒドロキシ−２−メチル−１―プロパン−１−オン、２−ヒドロキシ−２−メチル−１−フェニルプロパン−１−オン、カンファーキノン、２，４，６−トリメチルベンゾイルジフェニルホスフィンオキサイド、ビス（２，４，６−トリメチルベンゾイル）−フェニルホスフィンオキサイド、２−メチル−１−（４−（メチルチオ）フェニル）−２−モルフォリノプロパン−１−オン、２−ベンジル―２−ジメチルアミノ−１−（４−モルフォリノフェニル）−１−ブタノン−１、２−ジメチルアミノ−２−（４−メチル−ベンジル）−１−（４−モリフォリン−４−イル−フェニル）−ブタン−１−オン、ビス（２，６−ジメトキシベンゾイル）−２，４，４−トリメチル−ペンチルホスフィンオキサイド等が挙げられる。これらの中では、ベンジルジメチルケタール及び／又はビス（２，４，６−トリメチルベンゾイル）−フェニルホスフィンオキサイドが好ましい。 As photopolymerization initiators, benzophenone, 4-phenylbenzophenone, benzoylbenzoic acid, 2,2-diethoxyacetophenone, bisdiethylaminobenzophenone, benzyl, benzoin, benzoylisopropyl ether, benzyldimethyl ketal, 1-hydroxycyclohexyl phenyl ketone, thioxanthone 2-methylthioxanthone, 2,4-dimethylthioxanthone, isopropylthioxanthone, 2,4-diethylthioxanthone, 2,4-diisopropylthioxanthone, 1- (4-isopropylphenyl) 2-hydroxy-2-methylpropan-1-one 1- (4- (2-hydroxyethoxy) -phenyl) -2-hydroxy-2-methyl-1-propan-1-one, 2-hydroxy-2-methyl-1-phen Rupropan-1-one, camphorquinone, 2,4,6-trimethylbenzoyldiphenylphosphine oxide, bis (2,4,6-trimethylbenzoyl) -phenylphosphine oxide, 2-methyl-1- (4- (methylthio) phenyl ) -2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -1-butanone-1,2-dimethylamino-2- (4-methyl-benzyl) ) -1- (4-Morifolin-4-yl-phenyl) -butan-1-one, bis (2,6-dimethoxybenzoyl) -2,4,4-trimethyl-pentylphosphine oxide, and the like. Among these, benzyldimethyl ketal and / or bis (2,4,6-trimethylbenzoyl) -phenylphosphine oxide is preferable.
本発明の接着剤は、各種基材の密着性を一層向上させることを目的に、（Ａ）成分、（Ｂ）成分以外の単官能（メタ）アクリレートをさらに含有することができる。 The adhesive of the present invention can further contain a monofunctional (meth) acrylate other than the component (A) and the component (B) for the purpose of further improving the adhesion of various substrates.
（Ａ）成分や（Ｂ）成分以外の単官能（メタ）アクリレートとしては、（Ｅ）一般式〔２〕で表される（メタ）アクリレートが挙げられる。 Examples of the monofunctional (meth) acrylate other than the component (A) and the component (B) include (E) (meth) acrylate represented by the general formula [2].
一般式〔２〕 Ｒ−Ｏ−Ｒ’
（式中、Ｒは（メタ）アクリロイル基を示し、Ｒ’は炭素数５〜１８個のアルキル基を示す。）General formula [2] R—O—R ′
(In the formula, R represents a (meth) acryloyl group, and R ′ represents an alkyl group having 5 to 18 carbon atoms.)
（Ｅ）成分の単官能（メタ）アクリレートとしては、２−エチルへキシル（メタ）アクリレート、ノニル（メタ）アクリレート、イソデシル（メタ）アクリレート、ｎ−ラウリル（メタ）アクリレート及びトリデシル（メタ）アクリレート等が挙げられる。これらの中では、接着性の点で、ｎ−ラウリル（メタ）アクリレートが好ましい。 As monofunctional (meth) acrylate of component (E), 2-ethylhexyl (meth) acrylate, nonyl (meth) acrylate, isodecyl (meth) acrylate, n-lauryl (meth) acrylate, tridecyl (meth) acrylate, and the like Is mentioned. Among these, n-lauryl (meth) acrylate is preferable in terms of adhesiveness.
式中、Ｒ’の炭素数は５〜１８個が好ましく、６〜１８個がより好ましい。５個以上だと耐水性が向上し、１８個以下だと組成物が析出せず、接着性が向上する。 In the formula, the carbon number of R ′ is preferably 5 to 18, and more preferably 6 to 18. If it is 5 or more, the water resistance is improved, and if it is 18 or less, the composition does not precipitate and the adhesiveness is improved.
本発明の各構成成分の使用量は、例えば、接着剤のシクロオレフィンポリマーに対する接着性が特段に高くなり、且つ、他の被着体に対しても高い接着強さを有するようになる点で、以下の使用量が好ましい。 The amount of each component of the present invention used is, for example, that the adhesiveness of the adhesive to the cycloolefin polymer is particularly high, and that it has high adhesive strength to other adherends. The following amounts are preferred.
（Ａ）成分は組成物の５〜８０質量％を占めることが好ましく、１０〜７０質量％を占めることがより好ましい。 (A) It is preferable that a component occupies 5-80 mass% of a composition, and it is more preferable that it occupies 10-70 mass%.
（Ａ）成分、（Ｂ）成分の配合比率は、（Ａ）成分及び（Ｂ）成分の合計１００質量部中、（Ａ）成分：（Ｂ）成分＝１０〜９９：１〜９０（質量比）が好ましく、２０〜９８：２〜８０（質量比）がより好ましく、５５〜９５：５〜４５（質量比）が最も好ましい。 The blending ratio of the component (A) and the component (B) is (A) component: (B) component = 10 to 99: 1 to 90 (mass ratio) in a total of 100 parts by mass of the component (A) and the component (B). ) Is preferable, 20 to 98: 2 to 80 (mass ratio) is more preferable, and 55 to 95: 5 to 45 (mass ratio) is most preferable.
（Ｅ）成分を使用する場合、（Ａ）成分、（Ｂ）成分、（Ｅ）成分の使用量は、（Ａ）成分、（Ｂ）成分及び（Ｅ）成分の合計１００質量部中、（Ａ）成分：（Ｂ）成分：（Ｅ）成分＝１０〜８０：１〜７０：１５〜８０（質量比）が好ましく、１５〜５０：２〜６０：２５〜６５（質量比）がより好ましく、２０〜４５：３〜４５：３５〜６０（質量比）が最も好ましい。 When using (E) component, the usage-amount of (A) component, (B) component, and (E) component is (A) component, (B) component, and (E) component in total 100 mass parts, A) component: (B) component: (E) component = 10-80: 1-70: 15-80 (mass ratio) are preferable, and 15-50: 2-60: 25-65 (mass ratio) are more preferable. 20-45: 3-45: 35-60 (mass ratio) are the most preferable.
（Ｃ）成分の使用量は、（Ａ）成分、（Ｂ）成分及び必要に応じて使用する（Ｅ）成分の合計１００質量部に対して、０．００１〜１０質量部が好ましく、０．０１〜５質量部がより好ましく、０．１〜３質量部が最も好ましい。 The amount of the component (C) used is preferably 0.001 to 10 parts by mass with respect to a total of 100 parts by mass of the component (A), the component (B) and the component (E) used as necessary. 01-5 mass parts is more preferable, and 0.1-3 mass parts is the most preferable.
（Ｄ）成分の使用量は、（Ａ）成分、（Ｂ）成分及び必要に応じて使用する（Ｅ）成分の合計１００質量部に対して、０．００１〜３０質量部が好ましく、０．１〜２０質量部がより好ましく、０．５〜１５質量部が最も好ましい。 The amount of the component (D) used is preferably 0.001 to 30 parts by mass with respect to 100 parts by mass in total of the component (A), the component (B) and the component (E) used as necessary. 1-20 mass parts is more preferable, and 0.5-15 mass parts is the most preferable.
本発明の組成物は、本発明の目的を損なわない範囲で、グラフト共重合体、溶剤、増量材、補強材、可塑剤、増粘剤、染料、顔料、難燃剤、酸化防止剤、及び界面活性剤等の添加剤を使用することができる。
熱硬化性樹脂とアルカリ可溶性ポリマーの含有量は、接着性や弾性率の点で、樹脂組成物１００質量部中、５質量部以下が好ましく、３質量部以下がより好ましく、１質量部以下が最も好ましく、熱硬化性樹脂とアルカリ可溶性ポリマーを含有しないことが更に好ましい。The composition of the present invention includes a graft copolymer, a solvent, an extender, a reinforcing material, a plasticizer, a thickener, a dye, a pigment, a flame retardant, an antioxidant, and an interface as long as the object of the present invention is not impaired. Additives such as activators can be used.
The content of the thermosetting resin and the alkali-soluble polymer is preferably 5 parts by mass or less, more preferably 3 parts by mass or less, and more preferably 1 part by mass or less in 100 parts by mass of the resin composition in terms of adhesiveness and elastic modulus. Most preferably, it is more preferable not to contain a thermosetting resin and an alkali-soluble polymer.
本発明の組成物の硬化物は、硬化性及び接着性が両立できる点で、０．０００００１〜１００００ＭＰａ（２３℃）の貯蔵弾性率Ｅ’を有することが好ましく、０．００００１〜５０００ＭＰａの貯蔵弾性率Ｅ’を有することがより好ましく、０．００１〜１０００ＭＰａの貯蔵弾性率Ｅ’を有することが最も好ましい。組成物の硬化物の貯蔵弾性率Ｅ’が０．０００００１ＭＰａ以上だと硬化物が硬化し、未反応成分が残らない場合がある。１００００ＭＰａ以下だと硬化物が剛直になりすぎず、接着性が低下しない場合がある。 The cured product of the composition of the present invention preferably has a storage elastic modulus E ′ of 0.000001 to 10000 MPa (23 ° C.), and has a storage elasticity of 0.00001 to 5000 MPa in that both curability and adhesiveness can be achieved. More preferably, it has a modulus E ′, and most preferably a storage elastic modulus E ′ of 0.001 to 1000 MPa. When the storage elastic modulus E ′ of the cured product of the composition is 0.000001 MPa or more, the cured product may be cured and no unreacted component may remain. When it is 10,000 MPa or less, the cured product does not become too rigid, and the adhesiveness may not be lowered.
本発明の組成物は、接着剤として使用できる。本発明の接着剤は、例えば、シクロオレフィンポリマー、ポリカーボネート、トリアセチルセルロース、ポリビニルアルコール及びガラスからなる群から選ばれる１種以上に対して高い接着強度を示し、好ましくはすべてに対して高い接着強度を示す。特に、シクロオレフィンポリマーやトリアセチルセルロースに対して高い接着強度を示す。 The composition of the present invention can be used as an adhesive. The adhesive of the present invention exhibits, for example, high adhesive strength with respect to one or more selected from the group consisting of cycloolefin polymer, polycarbonate, triacetyl cellulose, polyvinyl alcohol and glass, preferably high adhesive strength with respect to all. Indicates. In particular, it exhibits high adhesive strength for cycloolefin polymers and triacetyl cellulose.
本発明のシクロオレフィンポリマーとは、例えば、ノルボルネンや多環ノルボルネン系モノマー等の環状オレフィン（シクロオレフィン）モノマー由来の構成単位を有する熱可塑性樹脂である。シクロオレフィンポリマーとしては、例えば、シクロオレフィンの開環重合体、２種以上のシクロオレフィンを用いた開環共重合体の水素添加物、鎖状オレフィンやビニル基を有する芳香族化合物とシクロオレフィンとの付加共重合体等が挙げられる。又、シクロオレフィンポリマーに、極性基を導入してもよい。 The cycloolefin polymer of the present invention is a thermoplastic resin having a structural unit derived from a cyclic olefin (cycloolefin) monomer such as norbornene or a polycyclic norbornene monomer. Examples of cycloolefin polymers include cycloolefin ring-opening polymers, hydrogenated ring-opening copolymers using two or more cycloolefins, chain olefins, aromatic compounds having a vinyl group, and cycloolefins. The addition copolymer of these is mentioned. Moreover, you may introduce | transduce a polar group into a cycloolefin polymer.
市販のシクロオレフィンポリマーとしては、例えば、独 Ｔｉｃｏｎａ社製の「Ｔｏｐａｓ」、ジェイエスアール社製の「アートン」、日本ゼオン社製の「ゼオノア（ＺＥＯＮＯＲ）」や「ゼオネックス（ＺＥＯＮＥＸ）」、三井化学社製の「アペル」等が挙げられる。 Commercially available cycloolefin polymers include, for example, “Topas” manufactured by Ticona, Germany, “Arton” manufactured by JSR, “ZEONOR” and “ZEONEX” manufactured by Nippon Zeon, Mitsui Chemicals, Inc. “Appel” made by the manufacturer can be mentioned.
トリアセチルセルロースとは、例えば、セルロースを無水酢酸等と反応させて、セルロースの３個の水酸基を全てアセチル化したものをいう。 Triacetylcellulose refers to, for example, a product obtained by reacting cellulose with acetic anhydride or the like to acetylate all three hydroxyl groups of cellulose.
本発明の接着剤の接着方法は、例えば、以下の通りである。被着体２枚のうち少なくとも１枚の被着体表面に接着剤を厚み０．０００１〜５ｍｍになるように塗布し、その後、被着体同士を貼り合わせ、波長２００〜５００ｎｍ、積算光量２００〜６０００ｍＪ／ｃｍ2、照射時間１〜６０秒の条件下で接着剤を硬化し、被着体を接着する方法が好ましい。The adhesive bonding method of the present invention is as follows, for example. An adhesive is applied to at least one adherend surface of the two adherends so as to have a thickness of 0.0001 to 5 mm, and then the adherends are bonded together to have a wavelength of 200 to 500 nm and an integrated light quantity of 200. A method is preferred in which the adhesive is cured and the adherend is adhered under the conditions of ˜6000 mJ / cm 2 and irradiation time of 1 to 60 seconds.
以下、実験例をあげて、本発明を更に詳細に説明する。本発明はこれらに限定されるものではない。実験例に記載の接着剤中の各成分には、以下の化合物を選択し、表１に記載の配合割合で各成分を混合して各実験例の組成物とした。 Hereinafter, the present invention will be described in more detail with reference to experimental examples. The present invention is not limited to these. For each component in the adhesive described in the experimental examples, the following compounds were selected, and each component was mixed at the blending ratio shown in Table 1 to obtain compositions of the experimental examples.
（化合物）
（Ａ）成分：イソシアヌル酸エチレンオキサイド変性トリ／ジアクリレート（東亞合成社製「Ｍ−３１３」、トリ／ジアクリレートはトリアクリレートとジアクリレートの混合物）
（Ａ）成分：イソシアヌル酸エチレンオキサイド変性ジアクリレート（東亞合成社製「Ｍ−２１５」）
（Ａ）成分：イソシアヌル酸エチレンオキサイド変性トリアクリレート（東亞合成社製「Ｍ−３１５」）
（Ｂ）成分：水酸基を含有する（メタ）アクリレートとして、２−ヒドロキシエチルメタクリレート（三菱瓦欺社製「ＧＥ−６１０」）
（Ｂ）成分：２−ヒドロキシ−３−フェノキシプロピルアクリレート（東亞合成社製「Ｍ−５７００」）
（Ｂ）成分：４−ヒドロキシブチルアクリレート（大阪有機化学工業社製「４−ＨＢＡ」）
（Ｃ）成分：シランカップリング剤、γ−グリシドキシプロピルトリメトキシシラン（信越化学社製「ＫＢＭ−４０３」）
（Ｃ）成分：シランカップリング剤、γ−メタクリロキシプロピルトリメトキシシラン（信越化学社製「ＫＢＭ−５０３」）
（Ｄ）成分：光開始剤、ベンジルジメチルケタール（チバ・スペシャルティー・ケミカルズ社製「ＩＲＧＡＣＵＲＥ６５１」）
（Ｄ）成分：ビス（２，４，６−トリメチルベンゾイル）−フェニルホスフィンオキサイド（チバ・スペシャルティー・ケミカルズ社製「ＩＲＧＡＣＵＲＥ８１９」）
（Ｅ）成分：ラウリルメタクリレート（共栄社化学社製「Ｌ」）
（Ｅ）成分：ノニルアクリレート（大阪有機化学工業社製「ＮＯＡＡ」）(Compound)
Component (A): Isocyanuric acid ethylene oxide modified tri / diacrylate (“M-313” manufactured by Toagosei Co., Ltd., tri / diacrylate is a mixture of triacrylate and diacrylate)
Component (A): Isocyanuric acid ethylene oxide-modified diacrylate (“M-215” manufactured by Toagosei Co., Ltd.)
(A) component: Isocyanuric acid ethylene oxide modified triacrylate (“M-315” manufactured by Toagosei Co., Ltd.)
(B) component: As a (meth) acrylate containing a hydroxyl group, 2-hydroxyethyl methacrylate (“GE-610” manufactured by Mitsubishi Kaigai Co., Ltd.)
Component (B): 2-hydroxy-3-phenoxypropyl acrylate (“M-5700” manufactured by Toagosei Co., Ltd.)
Component (B): 4-hydroxybutyl acrylate (“4-HBA” manufactured by Osaka Organic Chemical Industry Co., Ltd.)
(C) Component: Silane coupling agent, γ-glycidoxypropyltrimethoxysilane (“KBM-403” manufactured by Shin-Etsu Chemical Co., Ltd.)
(C) Component: Silane coupling agent, γ-methacryloxypropyltrimethoxysilane (“KBM-503” manufactured by Shin-Etsu Chemical Co., Ltd.)
Component (D): Photoinitiator, benzyldimethyl ketal (“IRGACURE651” manufactured by Ciba Specialty Chemicals)
Component (D): bis (2,4,6-trimethylbenzoyl) -phenylphosphine oxide (“IRGACURE819” manufactured by Ciba Specialty Chemicals)
(E) component: Lauryl methacrylate (“L” manufactured by Kyoeisha Chemical Co., Ltd.)
(E) component: Nonyl acrylate (“NOAA” manufactured by Osaka Organic Chemical Industry Co., Ltd.)
［比較成分］
（Ａ）成分や（Ｅ）成分の比較として、ベンジルメタクリレート（共栄社化学社製「ライトエステルＢＺ」、ホモポリマーガラス転移温度５４℃）
（Ｂ）成分の比較として、ジエチルアミノエチルメタクリレート（共栄社化学社製「ライトエステルＤＥ」）[Comparative ingredients]
As a comparison of the component (A) and the component (E), benzyl methacrylate (“Kyoeisha Chemical Co., Ltd.“ light ester BZ ”, homopolymer glass transition temperature 54 ° C.)
As a comparison of the component (B), diethylaminoethyl methacrylate (Kyoeisha Chemical Co., Ltd. “Light Ester DE”)
各種物性は、次のように測定した。温度２３℃で測定した。 Various physical properties were measured as follows. Measurement was performed at a temperature of 23 ° C.
〔光硬化性〕光硬化性に関しては、ＺＥＯＮＥＸ４８０Ｒ（日本ゼオン社製）試験片（幅２５ｍｍ×長さ２５ｍｍ×厚み２．０ｍｍ）表面に接着剤を厚み０．０８ｍｍになるように塗布した。その後、無電極放電ランプを使用したフュージョン社製硬化装置を用い、波長３７５ｎｍ、積算光量２０００ｍＪ／ｃｍ2の条件にて１５秒間照射し、硬化させた。光硬化性として、硬化率を記載した。硬化率は、ＦＴ−ＩＲを使用し、以下の式により算出した。
（硬化率）＝［１００−（（硬化後の、炭素と炭素の二重結合の吸収スペクトルの強度）／（硬化前の、炭素と炭素の二重結合の吸収スペクトルの強度））］×１００（％）[Photocurability] Regarding photocurability, an adhesive was applied to the surface of a ZEONEX 480R (manufactured by Zeon Corporation) test piece (width 25 mm × length 25 mm × thickness 2.0 mm) to a thickness of 0.08 mm. Thereafter, using a curing device manufactured by Fusion Corporation using an electrodeless discharge lamp, irradiation was carried out for 15 seconds under the conditions of a wavelength of 375 nm and an integrated light amount of 2000 mJ / cm 2 to be cured. Curing rate was described as photocurability. The curing rate was calculated by the following formula using FT-IR.
(Curing rate) = [100-((Intensity of absorption spectrum of carbon-carbon double bond after curing) / (Intensity of absorption spectrum of carbon-carbon double bond before curing))] × 100 (%)
〔シクロオレフィンポリマー接着性評価（ＺＥＯＮＥＸ 試験片間の引張接着強さ）〕ＺＥＯＮＥＸ４８０Ｒ（日本ゼオン社製）試験片（幅２５ｍｍ×長さ２５ｍｍ×厚み２．０ｍｍ）同士を、厚み８０μｍ×幅１１．５ｍｍ×長さ２５ｍｍのテフロン（登録商標）テープをスペーサーとして用い、接着剤を接着させた（接着面積３．１２５ｃｍ2）。硬化後、接着剤で接着した該試験片を用いて引張接着強さを測定した。接着条件は〔光硬化性〕に記載の方法に従った。[Evaluation of cycloolefin polymer adhesion (tensile adhesive strength between ZEONEX test pieces)] ZEONEX 480R (manufactured by Nippon Zeon Co., Ltd.) test pieces (width 25 mm × length 25 mm × thickness 2.0 mm), thickness 80 μm × width 11. An adhesive was adhered using a Teflon (registered trademark) tape of 5 mm × 25 mm in length as a spacer (adhesion area 3.125 cm 2 ). After curing, the tensile bond strength was measured using the test piece bonded with an adhesive. Adhesion conditions followed the method described in [Photocurability].
〔トリアセチルセルロース接着性評価（トリアセチルセルロース（富士フィルム社製）試験片間の剥離接着強さ）〕トリアセチルセルロース（富士フィルム社製）試験片（幅１０ｍｍ×長さ５０ｍｍ×厚み０．０８ｍｍ）同士を、バーコーターを用い、厚み１０μｍで接着させた。硬化後、接着剤で接着した該試験片を用いて１８０°ピール強度を測定した。引張速度は５０ｍｍ／分。 [Triacetylcellulose Adhesive Evaluation (Peeling Adhesive Strength Between Triacetylcellulose (Fuji Film) Test Pieces)] Triacetylcellulose (Fuji Film Corp.) Test Pieces (Width 10 mm × Length 50 mm × Thickness 0.08 mm) ) Were bonded to each other with a thickness of 10 μm using a bar coater. After curing, 180 ° peel strength was measured using the test piece bonded with an adhesive. Tensile speed is 50 mm / min.
〔ポリビニルアルコール接着性評価（ポリビニルアルコール（クラレ社製） 試験片間の剥離接着強さ）〕ポリビニルアルコール（クラレ社製）試験片（幅１０ｍｍ×長さ５０ｍｍ×厚み０．０８ｍｍ）同士を、バーコーターを用い、厚み１０μｍで接着させた。硬化後、接着剤で接着した該試験片を用いて１８０°ピール強度を測定した。引張速度は５０ｍｍ／分。 [Polyvinyl alcohol adhesion evaluation (polyvinyl alcohol (made by Kuraray Co., Ltd.), peel adhesion strength between test pieces)] Polyvinyl alcohol (made by Kuraray Co., Ltd.) test pieces (width 10 mm × length 50 mm × thickness 0.08 mm) The coater was used for adhesion with a thickness of 10 μm. After curing, 180 ° peel strength was measured using the test piece bonded with an adhesive. Tensile speed is 50 mm / min.
〔汎用ポリマー接着性評価（ポリカーボネート（帝人社製） 試験片間の引張接着強さ）〕パンライト（帝人社製）試験片（幅２５ｍｍ×長さ２５ｍｍ×厚み２．０ｍｍ）同士を、厚み８０μｍ×幅１１．５ｍｍ×長さ２５ｍｍのテフロン（登録商標）テープをスペーサーとして用い、接着剤を接着させた（接着面積３．１２５ｃｍ2）。硬化後、接着剤で接着した該試験片を用いて引張接着強さを測定した。接着条件は〔光硬化性〕に記載の方法に従った。[Evaluation of general-purpose polymer adhesion (polycarbonate (manufactured by Teijin Ltd.), tensile adhesive strength between test pieces)] Panlite (manufactured by Teijin Ltd.) specimens (width 25 mm × length 25 mm × thickness 2.0 mm), thickness 80 μm X Adhesive was adhered using a Teflon (registered trademark) tape having a width of 11.5 mm and a length of 25 mm as a spacer (adhesion area: 3.125 cm 2 ). After curing, the tensile bond strength was measured using the test piece bonded with an adhesive. Adhesion conditions followed the method described in [Photocurability].
〔ガラス接着性評価（耐熱ガラス 試験片間の引張接着強さ）〕耐熱ガラスのパイレックス（登録商標）試験片（幅２５ｍｍ×長さ２５ｍｍ×厚み２．０ｍｍ）同士を、厚み８０μｍ×幅１１．５ｍｍ×長さ２５ｍｍのテフロン（登録商標）テープをスペーサーとして用い、接着剤を接着させた（接着面積３．１２５ｃｍ2）。接着条件は〔光硬化性〕に記載の方法に従った。上記条件にて接着剤を硬化させた後、更に、試験片の両裏側に電気化学工業社製接着剤「Ｇ−５５」を使用し、亜鉛メッキ鋼板（幅１００ｍｍ×長さ２５ｍｍ×厚み２．０ｍｍ、エンジニアリングテストサービス社製）を接着させた。硬化後、接着剤で接着した該試験片を用いて引張接着強さを測定した。引っ張り剪断接着強さ（単位：ＭＰａ）は、温度２３℃、湿度５０％の環境下で引張速度１０ｍｍ／分で測定した。[Glass Adhesion Evaluation (Tensile Adhesive Strength Between Heat Resistant Glass Specimens)] Heat-resistant glass Pyrex (registered trademark) specimens (width 25 mm × length 25 mm × thickness 2.0 mm) were joined to each other with a thickness of 80 μm × width 11. An adhesive was adhered using a Teflon (registered trademark) tape of 5 mm × 25 mm in length as a spacer (adhesion area 3.125 cm 2 ). Adhesion conditions followed the method described in [Photocurability]. After the adhesive is cured under the above conditions, an adhesive “G-55” manufactured by Denki Kagaku Kogyo Co., Ltd. is further used on both sides of the test piece, and a galvanized steel sheet (width 100 mm × length 25 mm × thickness 2. 0 mm, manufactured by Engineering Test Service) was adhered. After curing, the tensile bond strength was measured using the test piece bonded with an adhesive. The tensile shear bond strength (unit: MPa) was measured at a tensile rate of 10 mm / min in an environment of a temperature of 23 ° C. and a humidity of 50%.
〔耐水性（ＺＥＯＮＥＸ 試験片間の引張接着強さ）〕前記シクロオレフィンポリマー接着性評価用試験片を６０℃温水に２４時間浸漬し、該試験片を用いて引張接着強さを測定した。 [Water resistance (tensile bond strength between ZEONEX test pieces)] The test piece for evaluation of cycloolefin polymer adhesion was immersed in warm water at 60 ° C for 24 hours, and the tensile bond strength was measured using the test piece.
〔貯蔵弾性率評価（貯蔵弾性率（２３℃））〕温度２３℃で測定した。接着剤を硬化させて、長さ２０ｍｍ×幅５ｍｍ×厚み１ｍｍの硬化物試料を調製した。接着条件は〔光硬化性〕に記載の方法に従った。この硬化物試料を評価した。セイコー電子工業（株）社製テンションモジュールＤＭＳ２１０を使用し、周波数１Ｈｚ、歪み０．０５％の条件で温度を変更して、引っ張りモードで動的粘弾性スペクトルを測定し、２３℃における貯蔵弾性率Ｅ’の値を求めた。 [Evaluation of storage elastic modulus (storage elastic modulus (23 ° C.)]] The temperature was measured at 23 ° C. The adhesive was cured to prepare a cured product sample having a length of 20 mm, a width of 5 mm, and a thickness of 1 mm. Adhesion conditions followed the method described in [Photocurability]. This cured product sample was evaluated. Using a tension module DMS210 manufactured by Seiko Denshi Kogyo Co., Ltd., changing the temperature under conditions of a frequency of 1 Hz and a strain of 0.05%, a dynamic viscoelastic spectrum was measured in a tensile mode, and a storage modulus at 23 ° C The value of E ′ was determined.
表１より本発明は、優れた効果を示す。シクロオレフィンポリマーに対して１．０ＭＰａ以上の引張接着強さを示す。トリアセチルセルロースに対して３．０Ｎ／ｃｍ以上の剥離接着強さを示す。ポリビニルアルコールに対して５．０Ｎ／ｃｍ以上の剥離接着強さを示す。ポリカーボネートに対して４．０ＭＰａ以上の引張接着強さを示す。ガラスに対して５．０ＭＰａ以上の引張接着強さを示す。耐水性試験において、０．３ＭＰａ以上の引張接着強さを示す。実験例１８は（Ｅ）成分を含有していないが、耐水性やポリビニルアルコールへの接着性に優れる。 From Table 1, the present invention shows an excellent effect. A tensile bond strength of 1.0 MPa or more with respect to the cycloolefin polymer. A peel adhesion strength of 3.0 N / cm or more with respect to triacetyl cellulose is shown. A peel adhesion strength of 5.0 N / cm or more with respect to polyvinyl alcohol is shown. It shows a tensile bond strength of 4.0 MPa or more with respect to polycarbonate. It shows a tensile bond strength of 5.0 MPa or more with respect to glass. In the water resistance test, a tensile bond strength of 0.3 MPa or more is shown. Although Experimental example 18 does not contain the (E) component, it is excellent in water resistance and adhesiveness to polyvinyl alcohol.
本発明は、シクロオレフィンポリマー、ポリカーボネート、トリアセチルセルロース、ポリビニルアルコール、及びガラスに対して、短時間で十分な接着性と耐水性を有する。本発明はトリアセチルセルロースへの接着性に優れるので、偏光フィルム用接着剤として使用できる。本発明はシクロオレフィンポリマーへの接着性に優れるので、シクロオレフィンポリマー用接着剤として使用できる。 The present invention has sufficient adhesion and water resistance in a short time with respect to cycloolefin polymer, polycarbonate, triacetyl cellulose, polyvinyl alcohol, and glass. Since this invention is excellent in the adhesiveness to a triacetyl cellulose, it can be used as an adhesive agent for polarizing films. Since this invention is excellent in the adhesiveness to a cycloolefin polymer, it can be used as an adhesive agent for cycloolefin polymers.
Claims (13)
（Ａ）成分は、一般式〔１〕で表されるイソシアヌル環誘導体（一般式〔１〕中のＸ1及びＸ2は（メタ）アクリロイルオキシ基を示し、Ｘ3はヒドロキシル基又は（メタ）アクリロイルオキシ基を示し、Ｒ1、Ｒ2及びＲ3は炭素数１〜４の炭化水素基を示す。）
（Ｃ）成分は、シランカップリング剤
（Ｄ）成分は、光重合開始剤A composition comprising the following components (A) to (D).
Component (A) is an isocyanuric ring derivative represented by the general formula [1] (X 1 and X 2 in the general formula [1] represent a (meth) acryloyloxy group, and X 3 represents a hydroxyl group or (meth) An acryloyloxy group is shown, and R 1 , R 2 and R 3 are hydrocarbon groups having 1 to 4 carbon atoms.)
一般式〔２〕 Ｒ−Ｏ−Ｒ’
（式中、Ｒは（メタ）アクリロイル基を示し、Ｒ’は炭素数５〜１８個のアルキル基を示す。）Furthermore, the (E) component contains the (meth) acrylate represented by General formula [2], The composition of Claim 1 formed.
General formula [2] R—O—R ′
(In the formula, R represents a (meth) acryloyl group, and R ′ represents an alkyl group having 5 to 18 carbon atoms.)