JPS6365092A - 金属用防錆剤 - Google Patents
金属用防錆剤Info
- Publication number
- JPS6365092A JPS6365092A JP20804686A JP20804686A JPS6365092A JP S6365092 A JPS6365092 A JP S6365092A JP 20804686 A JP20804686 A JP 20804686A JP 20804686 A JP20804686 A JP 20804686A JP S6365092 A JPS6365092 A JP S6365092A
- Authority
- JP
- Japan
- Prior art keywords
- metal
- compd
- rust
- film
- fluorine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
[産業上の利用分野]
本発明は金属用防錆剤に関するものである。
[従来の技術及びその問題点]
従来がら金属に対する防錆剤としてペンシイシダゾール
、ベンゾトリアゾール等の各種アミン化合物、鉱物油、
オレフィン系オイル、リン酸化合物等が用いられている
が、その効果は充分でなく、特に亜硫酸ガスや塩水雰囲
気下での防錆力は皆無に近いものであった。一方、プリ
ント配線板やI 、C,等の電子部品の防錆処理に当っ
ては、導電性を損なわないことも必要とA されることもあり、導電性を阻害しないと同時に防錆力
の高い防錆剤が求められている。
、ベンゾトリアゾール等の各種アミン化合物、鉱物油、
オレフィン系オイル、リン酸化合物等が用いられている
が、その効果は充分でなく、特に亜硫酸ガスや塩水雰囲
気下での防錆力は皆無に近いものであった。一方、プリ
ント配線板やI 、C,等の電子部品の防錆処理に当っ
ては、導電性を損なわないことも必要とA されることもあり、導電性を阻害しないと同時に防錆力
の高い防錆剤が求められている。
[問題点を解決するための手段]
本発明は従来の技術では充分でなかった前述の欠点を解
消し又、前述の要望に答えようとするものであり、ポリ
フルオロアルキル基及びメルカプト基を有する化合物か
らなることを特徴とする金属用防錆剤に関するものであ
る。
消し又、前述の要望に答えようとするものであり、ポリ
フルオロアルキル基及びメルカプト基を有する化合物か
らなることを特徴とする金属用防錆剤に関するものであ
る。
本発明におけるポルフルオロアルキル基(以下Rrと略
す)及びメルカプト基を有する化合物(以下含フツ素化
合物と略す)として好適な具体例は以下の通りである。
す)及びメルカプト基を有する化合物(以下含フツ素化
合物と略す)として好適な具体例は以下の通りである。
R(02HaSH
Rr C2Ha 0COCH25H
Rt C00C2Ha 5H
RrCH2111:HCH20COC+aH370CO
CH2SH Rr CON HO2H45H RrCON(C2Hs)C2HaSH Rr SO2NHO2Ha SH )Q− RtSO2N(C2Hs)GzHaSHRrC2HaC
ONHC?HaSH RrC2HaS02N(C2)1s)C2HnSHRr
CONHC2H40COCH2S)IRrSO2NHC
2HaOCOCHzSHRtCH2CHCH20COR 0COC1hSH CH−C−DC2H4Rr 0H−C−OG2HaSH1 Rtとしては、炭素数1〜21個、好ましくは4〜16
個の直鎖状又は分岐状のポリフルオロアルキル基であり
、好ましくはパーフルオロアルキル基であるが、末端部
に水素原子又は塩素原子を含むもの、あるいはオキシパ
ーフルオロアルキレン基を含有するもの等も使用可能で
ある。
CH2SH Rr CON HO2H45H RrCON(C2Hs)C2HaSH Rr SO2NHO2Ha SH )Q− RtSO2N(C2Hs)GzHaSHRrC2HaC
ONHC?HaSH RrC2HaS02N(C2)1s)C2HnSHRr
CONHC2H40COCH2S)IRrSO2NHC
2HaOCOCHzSHRtCH2CHCH20COR 0COC1hSH CH−C−DC2H4Rr 0H−C−OG2HaSH1 Rtとしては、炭素数1〜21個、好ましくは4〜16
個の直鎖状又は分岐状のポリフルオロアルキル基であり
、好ましくはパーフルオロアルキル基であるが、末端部
に水素原子又は塩素原子を含むもの、あるいはオキシパ
ーフルオロアルキレン基を含有するもの等も使用可能で
ある。
Rは炭素数1〜lOのアルキル基である。
本発明の防錆剤は通常、含フツ素化合物を水あるいは有
機溶剤中に分散又は溶解させて用いるものである。これ
を、防錆処理すべき金属表面にスプレー、刷毛塗り又は
浸漬法により処理し、乾燥して含フツ素化合物の被膜を
形成する方法が適当である。その他、冷媒や冷凍機油と
ともに用いて、冷凍装置における金属部材の防錆に使用
可能である。水又は有機溶剤へ分散させる場合には、ノ
ニオン系、アニオン系、カチオン系、非イオン系又は両
性基等各種の界面活性剤の1種又は2種以上の混合物を
使用できる。有機溶剤としては、アセトン、メチルイソ
プロピルケトン、メチルエチルケトン等のケトン類、酢
酸メチル、酢酸エチル、酢酸イソアミル等のエステル類
、メタノール、エタノール、イソプロピルアルコール等
のアルコール類、ジエチルエーテル、ジオキサン等のエ
ーテル類、n−へブタン、n−へキサン、ベンゼン、ト
ルエン、キシレン等の炭化水素類、メチルクロロホルム
、トリクロロエチレン、テトラクロロエチレン、テトラ
クロロジフルオロエタン、 1,1.2−トリクロロト
リフルオロエタン、ジクロロテトラフルオロエタン、履
−キシレンへキサフルオリド等のハロゲン化炭化水素類
の1a又は2種以上の混合物を使用できる。
機溶剤中に分散又は溶解させて用いるものである。これ
を、防錆処理すべき金属表面にスプレー、刷毛塗り又は
浸漬法により処理し、乾燥して含フツ素化合物の被膜を
形成する方法が適当である。その他、冷媒や冷凍機油と
ともに用いて、冷凍装置における金属部材の防錆に使用
可能である。水又は有機溶剤へ分散させる場合には、ノ
ニオン系、アニオン系、カチオン系、非イオン系又は両
性基等各種の界面活性剤の1種又は2種以上の混合物を
使用できる。有機溶剤としては、アセトン、メチルイソ
プロピルケトン、メチルエチルケトン等のケトン類、酢
酸メチル、酢酸エチル、酢酸イソアミル等のエステル類
、メタノール、エタノール、イソプロピルアルコール等
のアルコール類、ジエチルエーテル、ジオキサン等のエ
ーテル類、n−へブタン、n−へキサン、ベンゼン、ト
ルエン、キシレン等の炭化水素類、メチルクロロホルム
、トリクロロエチレン、テトラクロロエチレン、テトラ
クロロジフルオロエタン、 1,1.2−トリクロロト
リフルオロエタン、ジクロロテトラフルオロエタン、履
−キシレンへキサフルオリド等のハロゲン化炭化水素類
の1a又は2種以上の混合物を使用できる。
分散液中又は溶液中にジグロロジフルオロメタン、モノ
フルオロトリクロロメタン、ジクロロテトラフルオロエ
タン等の噴射剤を添加して、適当な容器に充てんすれば
、スプレー処理用に使用することができる。水中又は溶
剤中の含フツ素化合物の配合量は、通常0.01〜20
重量%、好ましくは0.05〜5重量%である。
フルオロトリクロロメタン、ジクロロテトラフルオロエ
タン等の噴射剤を添加して、適当な容器に充てんすれば
、スプレー処理用に使用することができる。水中又は溶
剤中の含フツ素化合物の配合量は、通常0.01〜20
重量%、好ましくは0.05〜5重量%である。
本発明の防錆剤は、前記含フツ素化合物の働きにより、
金属の導電性を損なうことなく、防錆力の持続性が高い
という特徴を有している。
金属の導電性を損なうことなく、防錆力の持続性が高い
という特徴を有している。
これらの時機を阻害しない限り1本発明の防錆処理剤に
は、貨来から知られている防錆油や錆止め剤を併用して
もよい、防錆油としては、ギヤ油、マシン油、スピンド
ル油、モーター油、タービン油、白灯油、軽油、ミネラ
ルターペン、ペトロラタム等を、又、錆止め剤としては
、ペンタエリトリットモノオレエートやソルビタンモノ
オレエート等のエステル類、オイザルコシン等のカルボ
ン酸類、オレイルアミンオレエート等の有機アミン塩、
モノオレイルリン酸等のリン酸エステル、石油又は合成
スルホネートのNa塩等のスルホン酸塩等を挙げること
ができる。
は、貨来から知られている防錆油や錆止め剤を併用して
もよい、防錆油としては、ギヤ油、マシン油、スピンド
ル油、モーター油、タービン油、白灯油、軽油、ミネラ
ルターペン、ペトロラタム等を、又、錆止め剤としては
、ペンタエリトリットモノオレエートやソルビタンモノ
オレエート等のエステル類、オイザルコシン等のカルボ
ン酸類、オレイルアミンオレエート等の有機アミン塩、
モノオレイルリン酸等のリン酸エステル、石油又は合成
スルホネートのNa塩等のスルホン酸塩等を挙げること
ができる。
本発明の防錆剤により処理可能な物品は、鉄鋼素材をは
じめ、各種輸送用機械製品、カメラや時計等の精密機械
製品、あるいは各!i主電気は電子機器等何ら限定され
ないが、特に防錆処理により、金属の導電性が損なわれ
ることをきらう、物品が好適である。その具体例はプリ
ント基板の回路部分、各種コネクター、IC、コンデン
サー等の部品のリード線等である。
じめ、各種輸送用機械製品、カメラや時計等の精密機械
製品、あるいは各!i主電気は電子機器等何ら限定され
ないが、特に防錆処理により、金属の導電性が損なわれ
ることをきらう、物品が好適である。その具体例はプリ
ント基板の回路部分、各種コネクター、IC、コンデン
サー等の部品のリード線等である。
[実施例]
「防錆効果を見るための試験方法」
本発明の含フツ素化合物及び各種化合物を各々フロンR
−113(1,1,2−トリクロロトリフルオロエタン
)中に0.5wt%溶解させた溶液中に、2cmX5c
層X O,2cmの銅板及び、その銅板上に銀メッキを
施したテストピースを浸漬後乾燥させ防錆処理した。
−113(1,1,2−トリクロロトリフルオロエタン
)中に0.5wt%溶解させた溶液中に、2cmX5c
層X O,2cmの銅板及び、その銅板上に銀メッキを
施したテストピースを浸漬後乾燥させ防錆処理した。
チオ硫酸ナトリウム水溶液(水200g/チオ硫酸ナト
リウム8g)に 10m文の10%硫酸水溶液を加えた
混合液を入れてラップで密閉した2文のビーカー中へ混
合液に直接ふれないように、前記テストピースを放置し
、48時間後のテストピース表面の状態を観察した。
リウム8g)に 10m文の10%硫酸水溶液を加えた
混合液を入れてラップで密閉した2文のビーカー中へ混
合液に直接ふれないように、前記テストピースを放置し
、48時間後のテストピース表面の状態を観察した。
「導電性を阻害しない効果を見るための試験方法」
前記鋼板製のテストピース面から5cmの間隔をあけて
、電極を設置し100Vの電圧下にテスターでその間の
抵抗値を測定した。
、電極を設置し100Vの電圧下にテスターでその間の
抵抗値を測定した。
防錆効果評価基準
に全面サビ発生
2:はとんど全面にサビ発生
3ニ一部サビ発生
4:わずかにサビ発生
5:全く腐食せず
[発明の効果コ
本発明の防錆剤により、処理された金属表面には本発明
における前記含フツ素化合物の単分子又はそれに近い極
めて薄い被膜が形成されているため、含フツ素重合体等
の厚い被膜に比べ、金属の導電性を損なうことが少ない
、又、この含フツ素化合物は、低分子化合物でありなが
ら、メルカプト基のような官能基を有しているため、金
属表面との密着性が良好であり、防錆効果の持続性にも
優れている。亜硫酸ガスや塩水等の過酷な条件下におい
ても銀や相等各種金属に対する防錆効果が高い。
における前記含フツ素化合物の単分子又はそれに近い極
めて薄い被膜が形成されているため、含フツ素重合体等
の厚い被膜に比べ、金属の導電性を損なうことが少ない
、又、この含フツ素化合物は、低分子化合物でありなが
ら、メルカプト基のような官能基を有しているため、金
属表面との密着性が良好であり、防錆効果の持続性にも
優れている。亜硫酸ガスや塩水等の過酷な条件下におい
ても銀や相等各種金属に対する防錆効果が高い。
一方、本発明の防錆剤はこれら防錆効果のみばかりでな
くポリフルオロアルキル基の有する撥水撥油性、防湿性
、防汚性、低庁擦性などを付与することもできる。
くポリフルオロアルキル基の有する撥水撥油性、防湿性
、防汚性、低庁擦性などを付与することもできる。
Claims (1)
- (1)ポリフルオロアルキル基及びメルカプト基を有す
る化合物からなることを特徴とする金属用防錆剤。