JPS63252285A - Timepiece side for magnetic resistance - Google Patents
Timepiece side for magnetic resistanceInfo
- Publication number
- JPS63252285A JPS63252285A JP8634387A JP8634387A JPS63252285A JP S63252285 A JPS63252285 A JP S63252285A JP 8634387 A JP8634387 A JP 8634387A JP 8634387 A JP8634387 A JP 8634387A JP S63252285 A JPS63252285 A JP S63252285A
- Authority
- JP
- Japan
- Prior art keywords
- timepiece
- magnetic resistance
- magnetic
- nickel
- timepiece side
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は時計を外部磁界より保護するための時計側に関
するものである。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to a watch side for protecting a watch from external magnetic fields.
本発明は時計側の少なくとも外部露出部以外に軟磁性あ
るいは硬質磁性を有する粒子を含む塗膜を電着塗装など
の方法にて形成し、時計を外部磁界より保護する機能を
付与したもので、従来の軟磁性材、硬質磁性材を加工し
て作った時計側にくらべ、より加工性、コストの点です
ぐれた材料が使用でき処理も簡単である。In the present invention, a coating film containing particles having soft magnetism or hard magnetism is formed on at least the externally exposed part of the watch side by a method such as electrodeposition, and the watch is given the function of protecting the watch from external magnetic fields. Compared to conventional watch parts made by processing soft magnetic materials and hard magnetic materials, materials that are superior in terms of workability and cost can be used and processing is easier.
(従来の技術〕 従来、時計用側としては主として黄銅、洋白。(Conventional technology) Traditionally, the main materials used for watches were brass and nickel silver.
ステンレスなどが使用されていたが、昨今外部磁界より
時計が止まるといったことが問題にされ、その対策とし
て、耐磁性を有する材料により文字板、うらぶた、側な
どが作られている。特に側においては高耐磁(2000
ガウス〜)を要求される場合に、フェライト系ステンレ
ス、クロム−鉄系合金、パーマロイなどの軟磁性、li
i!!貿磁性材料が使用されている。例えば特公昭55
−43070号公報にこのような構成が開示されている
。Stainless steel and other materials were used, but recently there has been a problem with watches stopping due to external magnetic fields, and as a countermeasure to this problem, dials, back lids, sides, etc. are made of anti-magnetic materials. Especially on the side, it has high magnetic resistance (2000
Gauss~), soft magnetic materials such as ferritic stainless steel, chromium-iron alloys, permalloy, etc.
i! ! Trade magnetic materials are used. For example,
Such a configuration is disclosed in Japanese Patent No.-43070.
しかしながら、軟磁性、硬質磁性材料を加工することは
、従来の黄銅などを加工する場合に比べ、機械加工性、
研磨性といった点ではるかに劣り時計側のデザインの自
由度といった点で制約があり、また加工コストも高くな
るという欠点を有していた。However, processing soft magnetic and hard magnetic materials has lower machinability than conventional materials such as brass.
It was far inferior in terms of polishability, had limitations in terms of freedom of design on the watch side, and had the drawbacks of high processing costs.
本発明はこのような問題点を除去し、frg4な時計側
を提供することを目的とする。The present invention aims to eliminate such problems and provide an frg4 watch side.
C問題点を解決するための手段〕
本発明では、軟磁性、硬質磁性材でなく加工が容易な黄
銅等の材料を使用し、少なくとも外部に露出する部分以
外を軟磁性あるいはVf!質磁性を有する粒子を含む塗
膜を形成した時計側とした。Means for Solving Problem C] In the present invention, a material such as brass that is easy to process is used instead of a soft magnetic or hard magnetic material, and at least the parts other than those exposed to the outside are made of soft magnetic or Vf! The watch side was coated with a coating containing magnetic particles.
ここにおいて、前記塗膜が従来のものにかわり、耐磁性
を保持する作用を果たすものである。Here, the coating film functions to maintain magnetic resistance in place of the conventional coating film.
以下実施例により本発明の詳細な説明する。The present invention will be explained in detail below with reference to Examples.
黄銅など従来より使用される加工性の良い材料により形
成した時計側に所望の表面仕上9表面処理を行ない、装
飾性上必要な部分をマスキングし鉄−コバルト、鉄−ニ
ッケル、ニッケルーホウ素などの軟磁性、硬質磁性材粒
子を含む塗膜を形成した。The watch side, which is made of conventionally used materials with good workability, such as brass, is subjected to surface treatment to achieve the desired surface finish (9), masking the areas necessary for decoration, and applying metal coatings such as iron-cobalt, iron-nickel, nickel-boron, etc. A coating film containing soft magnetic and hard magnetic material particles was formed.
このように形成した時計側を、耐磁性材料で形成された
文字板、うらぶたと組み合せて耐磁性をテストした所、
500ガウスの耐磁性が得られた。We tested the anti-magnetic properties by combining the watch side formed in this way with a dial and back lid made of anti-magnetic material.
Magnetic resistance of 500 Gauss was obtained.
ここにおいて塗膜の形成方法としては、アニオンあるい
はカチオン系電着塗装液に前記粒子を加えて行なう電着
塗装が側のような立体形状のものに均一に被膜を形成す
るという意味で効果的である。Here, as a method for forming a coating film, electrodeposition coating, which is performed by adding the particles to an anionic or cationic electrodeposition coating liquid, is effective in the sense that it forms a uniform coating on three-dimensional objects such as sides. be.
また塗膜の厚みとしては、20ミクロン程度以上あれば
耐磁効果は出るが、より厚くなるとその耐磁効果が高く
なる。Further, as for the thickness of the coating film, if it is about 20 microns or more, the antimagnetic effect will be obtained, but the thicker the thickness, the higher the antimagnetic effect.
(発明の効果)
以上述べてきたように本発明によれば、比較的安いコス
トで耐磁効果の高い時計側が可能になる。(Effects of the Invention) As described above, according to the present invention, it is possible to provide a watch with a high anti-magnetic effect at a relatively low cost.
なお、このような塗膜の形成は、文字板の裏面。Note that this type of coating is formed on the back of the dial.
うらぶたの内面に形成しても、同様効果が得られること
はいうまでもない。It goes without saying that the same effect can be obtained by forming it on the inner surface of the lining.
Claims (1)
硬質磁性を有する粒子を含む塗膜を形成したことを特徴
とする耐磁用時計側。An antimagnetic watch side, characterized in that a coating film containing particles having soft magnetism or hard magnetism is formed on at least an area other than the externally exposed part of the watch side.