JPS6145332B2 - - Google Patents
Info
- Publication number
- JPS6145332B2 JPS6145332B2 JP14349883A JP14349883A JPS6145332B2 JP S6145332 B2 JPS6145332 B2 JP S6145332B2 JP 14349883 A JP14349883 A JP 14349883A JP 14349883 A JP14349883 A JP 14349883A JP S6145332 B2 JPS6145332 B2 JP S6145332B2
- Authority
- JP
- Japan
- Prior art keywords
- adhesive
- film
- adhesive layer
- sheet
- insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は絶縁接着性シートに関し、薄型家電製
品例えば電卓におけるプレートカバーの固定に使
用するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to an insulating adhesive sheet, which is used for fixing a plate cover in a thin home appliance, such as a calculator.
薄型家電製品においては、第１図に示すよう
に、電気部品収納穴１′，………を有する樹脂成
型体２′にプレートカバー（金属製）３′をシート
状接着剤４′により接着することがある。このシ
ート状接着剤４′の使用目的は、電子部品５′とプ
レートカバー３′との間の電気絶縁の万全を期す
ると共にプレートカバー３′の固定を行うことに
あり、第２図に示すように絶縁フイルム４１′の
両面に接着層４２′，４２′を設けたものを使用し
ている。このシート状接着剤４′はロール巻き状
態で保管、運搬するのが通常であり、ロール巻き
により互に接触した接着剤層間のブロツキングを
防止するためにセパレータ４３′を設けている。 In the case of thin home appliances, as shown in Fig. 1, a plate cover (made of metal) 3' is adhered to a resin molded body 2' having electrical component storage holes 1', . . . with a sheet adhesive 4'. Sometimes. The purpose of using this sheet adhesive 4' is to ensure complete electrical insulation between the electronic component 5' and the plate cover 3' and to fix the plate cover 3', as shown in FIG. In this way, an insulating film 41' with adhesive layers 42', 42' provided on both sides is used. This sheet-like adhesive 4' is normally stored and transported in the form of a roll, and a separator 43' is provided to prevent blocking between the adhesive layers that come into contact with each other due to the roll.
ところで、第１図において、電子部品収納用穴
以外の部分の絶縁フイルムは上記した絶縁（電子
部品とプレートカバーとの間に絶縁）に対しては
用をなしておらず、かえつて製品の薄型化（超薄
型化においては、絶縁フイルムの厚みでも問題に
なる）に不利である。又、ロール体から巻き解い
たのち、セパレータは全て廃棄しており、不経済
である。 By the way, in Fig. 1, the insulating film in the area other than the hole for storing electronic components has no use for the above-mentioned insulation (insulation between the electronic components and the plate cover), and on the contrary, it reduces the thinness of the product. (In ultra-thin design, the thickness of the insulating film also becomes a problem.) Moreover, after unwinding from the roll body, all the separators are discarded, which is uneconomical.
本発明に係る絶縁接着性シートは、かゝる不合
理を解消し得る構成であり、両面接着性であつ
て、少なくとも片面の接着剤層を常温で非粘着性
あるいは弱粘着性とした接着性シートの非粘着性
あるいは弱粘着性接着剤層にセパレート用兼絶縁
用のフイルムを設けたことを特徴とするものであ
る。 The insulating adhesive sheet according to the present invention has a structure that can eliminate such unreasonableness, and is adhesive on both sides, with the adhesive layer on at least one side being non-adhesive or weakly adhesive at room temperature. It is characterized in that a film for separation and insulation is provided on the non-adhesive or weakly adhesive adhesive layer of the sheet.
以下、図面により本発明を説明する。 The present invention will be explained below with reference to the drawings.
第３図において、１は両面接着性のシートであ
り、少なくとも片面の接着剤層１１には、常温で
非粘着性又は弱粘着性（JIS.Z.0237のもとで20〜
500ｇ／50mm）のものを使用してある。他面の接
着剤層１２には、常温で非粘着性（弱粘着性を含
む）又は粘着性の何れをも使用でき、特に後者の
場合は支持体１２１に接着剤１２２を塗布、含浸
したものを使用する。２は接着剤層１１に仮着し
たセパレート用（ロール巻きした場合に相互に接
触する接着剤層１１，１２間のブロツキングを防
止するためのもの）兼絶縁用のフイルムである。 In FIG. 3, 1 is a double-sided adhesive sheet, and the adhesive layer 11 on at least one side has non-adhesive or weakly adhesive properties at room temperature (20 to 20% under JIS.Z.0237).
500g/50mm) is used. The adhesive layer 12 on the other side can be either non-adhesive (including weakly adhesive) or adhesive at room temperature; especially in the latter case, the adhesive 122 is coated and impregnated on the support 121. use. 2 is a film temporarily attached to the adhesive layer 11 for use as a separate material (to prevent blocking between the adhesive layers 11 and 12 that come into contact with each other when rolled) and as an insulator.
上記接着剤層１１，１２の厚みは、何れにおい
ても0.02〜0.2mmであり、フイルム２の厚みは0.01
〜0.20mmであり、同フイルムの体積抵抗率は1012
Ω−cm以上である。 The thickness of the adhesive layers 11 and 12 is 0.02 to 0.2 mm in both cases, and the thickness of the film 2 is 0.01 mm.
~0.20mm, and the volume resistivity of the film is 10 12
It is Ω-cm or more.
上記の常温で非粘着性ないしは弱粘着性接着剤
１１としては、エチレン−酢酸ビニル共重合
物、アイオノマー、ポリアミド、ポリエステル等
の熱可塑性樹脂に必要に応じて炭化水素系、ロジ
ン系、エステルロジン系、キシレン系、テルペン
系、フエノール系、テルペン−フエノール系等の
樹脂をブレンドしたもの、スチレン−ブタジエ
ンブロツク共重合体にクマロン樹脂、スチレン樹
脂、キシレン樹脂、フエノール変成樹脂等をブレ
ンドしたものを使用できる。これらの樹脂の軟化
点は80゜〜160℃に調整することが望ましい。80
℃よりも低い場合は、常温において粘着性をおび
るようになるし、160℃よりも高い場合は、接着
性の発現に高温度を必要として接着が困難になる
からである。ブレンドする場合は、上記の場
合、熱可塑性樹脂100重量部に対して100重量部以
下とすること、上記の場合は、スチレン−ブタ
ジエンブロツク共重合体100重量部に対して10〜
60重量部とすることが望ましい。これよりも多く
すると、常温において粘着性をおびるようになる
し、高温での接着特性も低下するからであり、
又、の場合、10重量部以下では接着力が著しく
低下するからである。常温での非粘着性を向上さ
せるために、ワツクス、脂肪酸アミド等のアンチ
ブロツキング剤を10重量部以下の範囲で添加する
ことができる。10重量部よりも多く添加すると、
接着力の低下が顕著になる。その他、必要に応じ
て、老化防止剤、充填剤、安定剤、顔料、架橋剤
等を配合できる。 The adhesive 11 that is non-tacky or weakly tacky at room temperature may be a thermoplastic resin such as ethylene-vinyl acetate copolymer, ionomer, polyamide, or polyester, or a hydrocarbon-based, rosin-based, or ester-rosin-based adhesive as required. , blends of xylene-based, terpene-based, phenol-based, terpene-phenol-based resins, etc., and blends of styrene-butadiene block copolymers with coumaron resin, styrene resin, xylene resin, phenol modified resin, etc. can be used. . It is desirable to adjust the softening point of these resins to 80° to 160°C. 80
If it is lower than 160°C, it becomes sticky at room temperature, and if it is higher than 160°C, a high temperature is required to develop adhesiveness, making it difficult to bond. When blending, in the above case, the amount should be 100 parts by weight or less per 100 parts by weight of the thermoplastic resin, and in the above case, it should be 10 to 10 parts by weight per 100 parts by weight of the styrene-butadiene block copolymer.
The amount is preferably 60 parts by weight. If the amount is more than this, it will become sticky at room temperature and the adhesive properties at high temperature will also decrease.
In addition, if the amount is less than 10 parts by weight, the adhesive strength will be significantly reduced. In order to improve non-stick properties at room temperature, an anti-blocking agent such as wax or fatty acid amide may be added in an amount of 10 parts by weight or less. If more than 10 parts by weight is added,
Adhesive strength decreases significantly. In addition, anti-aging agents, fillers, stabilizers, pigments, cross-linking agents, etc. can be added as necessary.
上記接着剤層１２に、常温で非粘着性のもの
（基材に接着剤を塗布、含浸したもの）を使用す
る場合、基材１２１にはレーヨン、和紙、ポリエ
ステル、ポリプロピレンなどの厚さ0.01〜0.10mm
の織布、不織布を用いることができ、接着剤１２
２にはアクリル系、ゴム系、シリコーン系などの
粘着剤やニトリル系、ネオプレン系、エチレン−
酢酸ビニル系、ナイロン系などの接着剤を用いる
ことができる。 When using the adhesive layer 12 that is non-adhesive at room temperature (base material coated with and impregnated with adhesive), the base material 121 is made of rayon, Japanese paper, polyester, polypropylene, etc. with a thickness of 0.01 to 0.10mm
A woven fabric or a non-woven fabric can be used, and the adhesive 12
2 includes adhesives such as acrylic, rubber, and silicone, as well as nitrile, neoprene, and ethylene adhesives.
Vinyl acetate-based adhesives, nylon-based adhesives, and the like can be used.
上記のセパレート用兼絶縁用フイルム２には、
ポリエステル、ポリプロピレン、ポリエチレン等
のフイルムを使用できる。 The above separating and insulating film 2 includes:
Films such as polyester, polypropylene, polyethylene, etc. can be used.
本発明に係る絶縁接着性シートは、例えば次の
ようにして製造することができる。 The insulating adhesive sheet according to the present invention can be manufactured, for example, as follows.
ドライ接着剤（例えばEVA系）を押出し機に
よつてフイルム状（厚さ0.05mm）に押出し、これ
を支持シート（剥離性のシートであり、例えば、
両面をシリコーンで表面離型処理したグラシン紙
を使用できる）上に乗せていく。これとは別に、
粘着剤溶液（例えば、アクリル系）を不織布（例
えば、ポリエステル系、厚さは0.05mm）に塗布し
乾燥し、これを上記支持シート上のドライ接着剤
層に熱ローラによつて貼合せる。次いで、ドライ
接着剤層に剥離用兼絶縁用フイルム（例えば、厚
さ0.05mmのポリエステルフイルム）を熱ローラに
よつて貼合せ（例えば、ローラ温度：100〜110
℃、速度：３m/minの条件で行う）、而るのち、
支持シートを除去する。このようにして得た絶縁
接着性テープはロール巻きした状態で保管、運搬
する。而して、このロール巻き状態において接着
剤層と接着剤層との間にはフイルムが介在してお
り、このフイルムによつて接着剤層間のブロツキ
ングを防止できる。 A dry adhesive (e.g. EVA type) is extruded into a film (0.05 mm thick) using an extruder, and this is then applied to a support sheet (a removable sheet, e.g.
(You can use glassine paper that has been treated with silicone on both sides for release.) Place it on top. Aside from this,
An adhesive solution (eg, acrylic) is applied to a nonwoven fabric (eg, polyester, 0.05 mm thick), dried, and bonded to the dry adhesive layer on the support sheet using a heated roller. Next, a peeling and insulating film (e.g., 0.05 mm thick polyester film) is laminated to the dry adhesive layer using a heated roller (e.g., roller temperature: 100 to 110
℃, speed: 3 m/min), and later,
Remove the support sheet. The insulating adhesive tape thus obtained is stored and transported in a rolled state. In this rolled state, a film is interposed between the adhesive layers, and this film can prevent blocking between the adhesive layers.
第４図は本発明シートを使用した薄型家電製品
におけるプレートカバーの固定構造を示してい
る。 FIG. 4 shows a fixing structure of a plate cover in a thin home appliance using the sheet of the present invention.
第４図において、３は樹脂成型体であり、電子
部品収納用穴３１，………を備え、これら穴３
１，………には電子部品４，………を収納してあ
る。５はプレートカバー（金属製）である。Ａは
本発明に係る絶縁接着性シートであり、１２は接
着剤層（常時、粘着性又はドライの何れでも
可）、１１は常温で非粘着性又は弱粘着性の接着
剤層、２はフイルムである。このフイルム２にお
ける上記の樹脂成型体の電子部品収納用穴３１，
………以外の部分はシーリング加工により除去し
て、接着剤層１１を樹脂成型体３の平面に融着
（加熱あるいは溶剤使用による融着）してある。
而して、フイルム２は電子部品収納用穴３１，…
……の部分においてのみ存在し、このフイルム２
により電子部品４をプレート５から確実に電気的
に絶縁してある。 In FIG. 4, 3 is a resin molded body, which is provided with holes 31 for storing electronic components, and these holes 3
Electronic components 4, . . . are stored in 1, . . . . 5 is a plate cover (made of metal). A is an insulating adhesive sheet according to the present invention, 12 is an adhesive layer (either always sticky or dry), 11 is an adhesive layer that is non-tacky or weakly sticky at room temperature, and 2 is a film. It is. The electronic component storage hole 31 of the resin molded body in this film 2,
The remaining portions are removed by sealing, and the adhesive layer 11 is fused to the flat surface of the resin molded body 3 (fused by heating or using a solvent).
Thus, the film 2 has holes 31 for storing electronic components,...
It exists only in the part of this film 2.
This ensures that the electronic component 4 is electrically isolated from the plate 5.
上記のプレートカバーの固定構造は次のような
要領によつて組立てることができる。 The plate cover fixing structure described above can be assembled in the following manner.
プレートカバー原板に本発明に係る絶縁接着性
シートを接着剤層において貼合せ、フイルムをシ
ーリング加工し、フイルムの不要部分を除去し、
次いで、原板をプレートカバーの形状に打抜き、
このプレートカバーを樹脂成型体に当接し、而る
のち、上記フイルムの除去により露出せるドライ
接着剤層を樹脂成型体の表面に融着させるように
する。あるいは、上記シーリング加工をし、フイ
ルムの不要部分を除去したシートを一たんロール
巻きしたものを必要長だけ巻き解き、これをプレ
ートカバー原板に貼合せ、而るのち、原板の打抜
き、打抜いたプレートカバーの樹脂成形体への当
接、ドライ接着剤層の樹脂成型体への融着等を順
次に行うようにしてもよい。 The insulating adhesive sheet according to the present invention is laminated to the plate cover original plate in an adhesive layer, the film is sealed, unnecessary parts of the film are removed,
Next, punch out the original plate into the shape of the plate cover,
This plate cover is brought into contact with the resin molding, and then the dry adhesive layer exposed by removing the film is fused to the surface of the resin molding. Alternatively, the sheet that has been subjected to the above sealing process and unnecessary portions of the film removed is rolled up, unrolled to the required length, pasted on the plate cover original plate, and then punched out of the original plate. The contacting of the plate cover to the resin molded body, the fusion of the dry adhesive layer to the resin molded body, etc. may be performed sequentially.
本発明に係る絶縁接着性シートは上述した通り
の構成であり、ロール巻きしたときの接着剤層の
ブロツキングを防止するフイルムをシーリング加
工し、そのフイルムの一部を絶縁用に使用するも
のであつて、フイルムをセパレート用のみならず
絶縁用としても利用でき、その利用価値を高める
ことができる。更に、フイルムに対する接着剤層
が常温で非粘着性であるから、上記シーリング加
工における不要部分の除去を容易に行い得、取扱
いも簡単である。 The insulating adhesive sheet according to the present invention has the structure as described above, and is a film that is sealed to prevent the adhesive layer from blocking when rolled, and a part of the film is used for insulation. Therefore, the film can be used not only for separation but also for insulation, increasing its utility value. Furthermore, since the adhesive layer for the film is non-adhesive at room temperature, unnecessary parts can be easily removed during the sealing process, and handling is also simple.
第１図はプレートカバーの公知の固定構造を示
す説明図、第２図は従来の絶縁接着性シートを示
す説明図、第３図は本発明に係る絶縁接着性シー
トを示す説明図、第４図は本発明シートの使用状
態を示す説明図である。
図において、１１は常温で非粘着性あるいは弱
粘着性の接着剤層、１２は接着剤層、２はセパレ
ート用兼絶縁用フイルムである。
FIG. 1 is an explanatory diagram showing a known fixing structure of a plate cover, FIG. 2 is an explanatory diagram showing a conventional insulating adhesive sheet, FIG. 3 is an explanatory diagram showing an insulating adhesive sheet according to the present invention, and FIG. The figure is an explanatory view showing the usage state of the sheet of the present invention. In the figure, 11 is an adhesive layer that is non-adhesive or weakly adhesive at room temperature, 12 is an adhesive layer, and 2 is a separating and insulating film.
Claims (1)
剤層を常温で非粘着性あるいは弱粘着性とした接
着性シートの非粘着性あるいは弱粘着性接着剤層
にセパレート用兼絶縁用のフイルムを設けたこと
を特徴とする絶縁接着性シート。1 A film for separating and insulating is provided on the non-adhesive or weakly adhesive layer of an adhesive sheet that is double-sided adhesive and has at least one side of the adhesive layer non-adhesive or weakly adhesive at room temperature. An insulating adhesive sheet characterized by: