JPS6126810B2 - - Google Patents
Info
- Publication number
- JPS6126810B2 JPS6126810B2 JP14075178A JP14075178A JPS6126810B2 JP S6126810 B2 JPS6126810 B2 JP S6126810B2 JP 14075178 A JP14075178 A JP 14075178A JP 14075178 A JP14075178 A JP 14075178A JP S6126810 B2 JPS6126810 B2 JP S6126810B2
- Authority
- JP
- Japan
- Prior art keywords
- parts
- lead
- chlorine
- resin
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
本発明は難燃性、耐熱性、耐初期着色性の改善
された塩素含有樹脂組成物に関する。 塩素含有樹脂、例えば塩化ビニル樹脂は熱およ
び光に曝されるとその分子内で脱塩酸に起因する
熱分解を起しやすく、このため加工製品の色調の
悪化、機械的性質の劣化、機械的性質の劣化、電
気絶縁性の低下等を生じ著るしく不利益を招く。
かかる不利益をさけるために、従来種々の安定剤
が使用され、この中でも特に鉛白、三塩基性硫酸
鉛、塩基性リン酸鉛、三塩基性マレイン酸鉛、ス
テアリン酸鉛等の鉛化合物が最も優れており、ま
た低価格であるため多用されている。 また、近年加工製品の難燃性が強く要望されて
きており、この目的のため塩素含有樹脂は元来は
自己消火性を持つているのであるが、尚不満足で
あるため難燃剤として塩素化パラフインないしは
ホウ酸亜鉛を添加することが多く行われている。 しかしこうした難燃剤を添加した場合、樹脂の
加工時の耐熱性にしばしば低下をきたすという欠
点があり、その改良が強く要望されている。 このような現状に鑑み、本発明者等は鋭意研究
を重ねた結果、難燃性を保持しながら、同時に耐
熱性、初期着色性の優れた塩素含有樹脂組成物の
開発に成功したものである。 即ち本発明は塩素含有樹脂にａ）塩素化パラフ
インおよびホウ酸亜鉛の１種、ｂ）鉛安定剤、
ｃ）多価アルコールを含有せしめてなる塩素含有
樹脂組成物を提供するものである。 本発明組成物に使用され得る塩素化パラフイン
およびホウ酸亜鉛は一般市販のものを用いること
ができ、これの好適な配合量は樹脂100部に対し
て１〜50部である。また鉛安定剤としては例えば
鉛白、三塩基性硫酸鉛、塩基性亜硫酸鉛、二塩基
性亜リン酸鉛、二塩基性フタル酸鉛、三塩基性マ
レイン酸鉛、塩基性ケイ酸鉛、ステアリン酸鉛、
サリチル酸鉛等を挙げることができる。これらの
好適な配合量は樹脂100部に対して0.05〜10重量
部である。 次に、本発明で用いる多価アルコール類として
はジプロピレングリコール、グリセリン、ジグリ
セン、マンニトール、ソルビトール、ペンタエリ
スリトール、トリ及びジペンタエリスリトール等
のポリペンタエリスリトール、ポリエチレングリ
コール、ポリプロピレングリコール等のポリグリ
コール、トリメチロールプロバン、トリスヒドロ
キシエチルイソシアヌレート、ペンタエリストー
ルステアリン酸エステル、ネオペンチルアルコー
ル等を包含する。これら多価アルコールの好適な
使用量は樹脂100部に対し0.1〜５重量部である。 本発明によれば上記化合物を組合わせることに
よつて優れた難燃性を維持しながら、樹脂成型品
の熱安定性、初期着色性を顕著に改善することが
できる。また電線被覆用配合においては電気絶縁
性を害することもなく好適に用いることができ
る。 本発明組成物においては上述の如き成分以外に
も他の安定剤成分や安定化助剤成分を配合せしめ
てもよい。その目的や用途に応じて適宜、可塑
剤、充填剤、酸化防止剤、金属石鹸、着色剤、滑
剤、発泡剤、帯電防止剤、紫外線吸収剤等の各種
添加剤を配合することができる。安定剤成分や他
の添加剤はそのまま樹脂に加えるか、混合したワ
ンパツク形態あるいは造粒して一体化した複合粒
状物形態であつてもよい。 本発明に適用し得る塩素含有樹脂にはポリ塩化
ビニル、塩化ビニルと他のモノマー、例えば酢酸
ビニル、エチレン、マレイン酸、アクリロニトリ
ル、プタジエン、スチレン、塩化ビニリデン等と
の共重合体、ポリ塩化ビニリデン、塩素化ポリオ
レフイン、塩化ゴム等がある。 以下に本発明組成物の各種配合における性能試
験結果を参考例と共に示す。 実施例 １ 塩化ビニル樹脂100重量部に対し、ジオクチル
フタレート50部、塩素化パラフイン20部、炭酸カ
ルシウム20部、三塩基性硫酸鉛2.0部及び第１表
に示す化合物の所定量を加えて、ロール温度180
℃で５分間混練して0.2mm厚のシートを作製し
た。次いでこのシートを180℃のギヤオーブン中
に曝露して耐熱性を試験した。また上記シート片
の燃焼試験を行つたところいずれも良好な自己消
火性を示した。
された塩素含有樹脂組成物に関する。 塩素含有樹脂、例えば塩化ビニル樹脂は熱およ
び光に曝されるとその分子内で脱塩酸に起因する
熱分解を起しやすく、このため加工製品の色調の
悪化、機械的性質の劣化、機械的性質の劣化、電
気絶縁性の低下等を生じ著るしく不利益を招く。
かかる不利益をさけるために、従来種々の安定剤
が使用され、この中でも特に鉛白、三塩基性硫酸
鉛、塩基性リン酸鉛、三塩基性マレイン酸鉛、ス
テアリン酸鉛等の鉛化合物が最も優れており、ま
た低価格であるため多用されている。 また、近年加工製品の難燃性が強く要望されて
きており、この目的のため塩素含有樹脂は元来は
自己消火性を持つているのであるが、尚不満足で
あるため難燃剤として塩素化パラフインないしは
ホウ酸亜鉛を添加することが多く行われている。 しかしこうした難燃剤を添加した場合、樹脂の
加工時の耐熱性にしばしば低下をきたすという欠
点があり、その改良が強く要望されている。 このような現状に鑑み、本発明者等は鋭意研究
を重ねた結果、難燃性を保持しながら、同時に耐
熱性、初期着色性の優れた塩素含有樹脂組成物の
開発に成功したものである。 即ち本発明は塩素含有樹脂にａ）塩素化パラフ
インおよびホウ酸亜鉛の１種、ｂ）鉛安定剤、
ｃ）多価アルコールを含有せしめてなる塩素含有
樹脂組成物を提供するものである。 本発明組成物に使用され得る塩素化パラフイン
およびホウ酸亜鉛は一般市販のものを用いること
ができ、これの好適な配合量は樹脂100部に対し
て１〜50部である。また鉛安定剤としては例えば
鉛白、三塩基性硫酸鉛、塩基性亜硫酸鉛、二塩基
性亜リン酸鉛、二塩基性フタル酸鉛、三塩基性マ
レイン酸鉛、塩基性ケイ酸鉛、ステアリン酸鉛、
サリチル酸鉛等を挙げることができる。これらの
好適な配合量は樹脂100部に対して0.05〜10重量
部である。 次に、本発明で用いる多価アルコール類として
はジプロピレングリコール、グリセリン、ジグリ
セン、マンニトール、ソルビトール、ペンタエリ
スリトール、トリ及びジペンタエリスリトール等
のポリペンタエリスリトール、ポリエチレングリ
コール、ポリプロピレングリコール等のポリグリ
コール、トリメチロールプロバン、トリスヒドロ
キシエチルイソシアヌレート、ペンタエリストー
ルステアリン酸エステル、ネオペンチルアルコー
ル等を包含する。これら多価アルコールの好適な
使用量は樹脂100部に対し0.1〜５重量部である。 本発明によれば上記化合物を組合わせることに
よつて優れた難燃性を維持しながら、樹脂成型品
の熱安定性、初期着色性を顕著に改善することが
できる。また電線被覆用配合においては電気絶縁
性を害することもなく好適に用いることができ
る。 本発明組成物においては上述の如き成分以外に
も他の安定剤成分や安定化助剤成分を配合せしめ
てもよい。その目的や用途に応じて適宜、可塑
剤、充填剤、酸化防止剤、金属石鹸、着色剤、滑
剤、発泡剤、帯電防止剤、紫外線吸収剤等の各種
添加剤を配合することができる。安定剤成分や他
の添加剤はそのまま樹脂に加えるか、混合したワ
ンパツク形態あるいは造粒して一体化した複合粒
状物形態であつてもよい。 本発明に適用し得る塩素含有樹脂にはポリ塩化
ビニル、塩化ビニルと他のモノマー、例えば酢酸
ビニル、エチレン、マレイン酸、アクリロニトリ
ル、プタジエン、スチレン、塩化ビニリデン等と
の共重合体、ポリ塩化ビニリデン、塩素化ポリオ
レフイン、塩化ゴム等がある。 以下に本発明組成物の各種配合における性能試
験結果を参考例と共に示す。 実施例 １ 塩化ビニル樹脂100重量部に対し、ジオクチル
フタレート50部、塩素化パラフイン20部、炭酸カ
ルシウム20部、三塩基性硫酸鉛2.0部及び第１表
に示す化合物の所定量を加えて、ロール温度180
℃で５分間混練して0.2mm厚のシートを作製し
た。次いでこのシートを180℃のギヤオーブン中
に曝露して耐熱性を試験した。また上記シート片
の燃焼試験を行つたところいずれも良好な自己消
火性を示した。
【表】
【表】
実施例 ２
塩化ビニル樹脂100重量部に対し、ジオクチル
フタレート50部、塩素化パラフイン20部、炭酸カ
ルシウム20部、ステアリン酸鉛1.5部および第２
表に示す化合物の所定量を加えて実施例１と同様
の方法でシートを作成した。次いでこのシートを
180℃のギヤオーブン中に曝露して耐熱性を試験
した。また前記シートを170℃で５分間プレス加
工を行つて耐初期着色性を肉眼で評価した。
フタレート50部、塩素化パラフイン20部、炭酸カ
ルシウム20部、ステアリン酸鉛1.5部および第２
表に示す化合物の所定量を加えて実施例１と同様
の方法でシートを作成した。次いでこのシートを
180℃のギヤオーブン中に曝露して耐熱性を試験
した。また前記シートを170℃で５分間プレス加
工を行つて耐初期着色性を肉眼で評価した。
【表】
実施例 ３
塩化ビニル樹脂100重量部に対し、ジオクチル
フタレート50部、ホウ酸亜鉛20部、ステアン酸バ
リウム1.0部、および第３表に示す化合物の所定
量を加えて実施例１と同様の方法でシートを作成
し、耐熱性および耐初期着色性を試験した。
フタレート50部、ホウ酸亜鉛20部、ステアン酸バ
リウム1.0部、および第３表に示す化合物の所定
量を加えて実施例１と同様の方法でシートを作成
し、耐熱性および耐初期着色性を試験した。
Claims (1)
- １ 塩素含有樹脂にａ）塩素化パラフインおよび
ホウ酸亜鉛の１種、ｂ）鉛安定剤、ｃ）多価アル
コールを含有せしめることを特徴とする塩素含有
樹脂組成物。