JPS61101498A - Production of molybdenum oxide whisker - Google Patents
Production of molybdenum oxide whiskerInfo
- Publication number
- JPS61101498A JPS61101498A JP22007484A JP22007484A JPS61101498A JP S61101498 A JPS61101498 A JP S61101498A JP 22007484 A JP22007484 A JP 22007484A JP 22007484 A JP22007484 A JP 22007484A JP S61101498 A JPS61101498 A JP S61101498A
- Authority
- JP
- Japan
- Prior art keywords
- molybdenum
- molybdenum oxide
- compound
- flake
- oxide whisker
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
「技術分野」
本発明は、棒状もしくはフレーク状をなす酸化モリブデ
ンウィスカーの製法に関する。DETAILED DESCRIPTION OF THE INVENTION TECHNICAL FIELD The present invention relates to a method for producing rod-shaped or flake-shaped molybdenum oxide whiskers.
「従来技術およびその問題点」
金属酸化物は、棒状、線状、針状、フレーク状などの形
状をなすことがあり、ウィスカーと呼ばれている。ウィ
スカーを形成する金属酸化物としては、これまでに酸化
アルミニウム（Ａｌ２Ｏ２）、酸化亜鉛（ＺｎＯ） 、
酸化ベリリウム（Ｂｅｄ） 、酸化マグネシウム（Ｍｇ
Ｏ）などが知られている。これらのウィスカーは、上記
のような特殊な形状をなすと共に極めて強固なため、現
在プラスチックのフィラーどして利用されているが、そ
の他各種用途への利用が検討されている。"Prior Art and its Problems" Metal oxides may have a shape such as a rod, a line, a needle, or a flake, and are called whiskers. Metal oxides that form whiskers include aluminum oxide (Al2O2), zinc oxide (ZnO),
Beryllium oxide (Bed), Magnesium oxide (Mg
O) etc. are known. These whiskers have the above-mentioned special shape and are extremely strong, so they are currently used as fillers in plastics, but their use in various other applications is also being considered.
このように、各種の金属酸化物からなるウィスカーが知
られているが、酸化モリブデン（Ｍ２Ｏ３）については
未だウィスカーを形成することが知られておらず、その
性状も明らかでなかった。As described above, whiskers made of various metal oxides are known, but molybdenum oxide (M2O3) has not yet been known to form whiskers, and its properties have not been clarified.
「発明の目的」
本発明の目的は、新規な工業用材料として各種用途への
応用が期待される酸化モリブデンウィスカーの製法を提
供することにある。"Object of the Invention" An object of the present invention is to provide a method for producing molybdenum oxide whiskers, which are expected to be applied to various uses as a new industrial material.
「発明の構成」
本発明の酸化モリブデンウィスカーの製法は、有機モリ
ブデン化合物を酸素含有雰囲気中で、該イフ機モリブデ
ン化合物の熱分解温度以上で加熱焼成することを特徴と
している。"Structure of the Invention" The method for producing molybdenum oxide whiskers of the present invention is characterized by heating and baking an organic molybdenum compound in an oxygen-containing atmosphere at a temperature equal to or higher than the thermal decomposition temperature of the organic molybdenum compound.
次に、本発明をより具体的に説明する。Next, the present invention will be explained in more detail.
本発明で使用する有機モリブデン化合物としては、例え
ばジオキシアセチルアセトネートモリブデン（■）、ア
セチルアセトネートモリブデン（ｖｒ） 、 ａ−ヒド
ロキシキノリンモリブデン（■）、ジエチルジチオカル
バミン酸モリブデン（Ｖｌ）などの錯体化合物が挙げら
れる。Examples of the organic molybdenum compounds used in the present invention include complex compounds such as molybdenum dioxyacetylacetonate (■), molybdenum acetylacetonate (vr), molybdenum a-hydroxyquinoline (■), and molybdenum diethyldithiocarbamate (Vl). can be mentioned.
本発明ではこれらの有機モリブデン化合物を例えばアル
ミナ基板、磁性ルツボ、石英容器等の耐熱性開口容器な
どに入れ、酸素含有雰囲気中で焼成する。ここで、酸素
含有雰囲気とは、酸素もしくは酸素を含有する雰囲気の
意味であり、例えば酸素中や空気中であればよい。焼成
温度は、有機モリブデン化合物が熱分解する温度以上と
する。In the present invention, these organic molybdenum compounds are placed in, for example, an alumina substrate, a magnetic crucible, a heat-resistant open container such as a quartz container, and fired in an oxygen-containing atmosphere. Here, the oxygen-containing atmosphere means oxygen or an atmosphere containing oxygen, and may be, for example, oxygen or air. The firing temperature is set to be higher than the temperature at which the organic molybdenum compound thermally decomposes.
焼成によって有機成分は酸化分解して飛散し、モリブデ
ンが酸化されて酸化モリブデン（Ｍｏ０３ ）のウィス
カーが形成される。By firing, organic components are oxidized and decomposed and scattered, and molybdenum is oxidized to form whiskers of molybdenum oxide (Mo03).
こうして得られた酸化モリブデンウィスカーは線状、棒
状、フレーク状など種々の形状をなす。The molybdenum oxide whiskers thus obtained have various shapes such as linear, rod-like, and flake-like shapes.
線状、棒状のものの大きさは、太さ数ｐｇ〜数十ｇｍ、
長さ数百用ｍ〜数ｍｍ程度であり、フレーク状のものの
大きさは、厚さ数舊ｍ〜数百ｐｍ、幅数十ＩＬｍ〜数百
ルエ、長さ数百Ｉｊ、ｆｆｉ〜数１１１Ｉ程度である。The size of the linear and rod-shaped items ranges from several pg to several tens of gm,
The length is about several hundred m to several mm, and the size of the flake-like material is several meters to several hundred pm in thickness, several tens of ILm to several hundred lumes in width, and several hundred Ij, ffi to several 111 I in length. That's about it.
「発明の実施例」
実施例１
有機モリブデン化合物としてジオキシアセチルアセトネ
ートモリブデン（ＶＴ）の錯体化合物をアルミナ基板に
１ｇ乗せ、空気中にて７００”０で３時間焼成を行なっ
た。その結果、第１図、第２図および第３図に示すよう
な形状の醇化モリブデンウィスカーが形成された。すな
わち、この酸化モリブデンウィスカーは、線状もしくは
棒状のものと、フレーク状もしくは薄片状のものとから
なっている。線状もしくは棒状のものは、太さ８０ｐｍ
程度、長さ３ａ＋ｍ程度であり、フレーク状もしくは薄
片状のものは厚さ１０ｇｍ＋、幅１００ルｍ、長さ５ｍ
ｍ程度である。そして、これらの酸化モリブデンウィス
カーの収量は３００ｍｇであった。"Embodiments of the Invention" Example 1 1 g of a complex compound of dioxyacetylacetonate molybdenum (VT) as an organic molybdenum compound was placed on an alumina substrate and fired in air at 700"0 for 3 hours. As a result, Molybdenum oxide whiskers were formed in the shapes shown in Figures 1, 2, and 3.In other words, these molybdenum oxide whiskers were divided into linear or rod-like shapes and flake-like or flake-like ones. .Thickness of wire or rod is 80pm.
The size and length are about 3a+m, and the flake-like or thin flake-like ones are 10gm+ thick, 100m wide, and 5m long.
It is about m. The yield of these molybdenum oxide whiskers was 300 mg.
実施例２
有機モリブデン化合物としてアセチルアセトネートモリ
ブデン（ＶＴ）の錯体化合物をアルミナ基板に０．５ｇ
乗せ、空気中にて７５０ ”０で２時間焼成を行なった
。その結果、線状、棒状、フレーク状等をなす各種形状
の酸化モリブデンウィスカーが形成された。Example 2 0.5 g of a complex compound of acetylacetonate molybdenum (VT) as an organic molybdenum compound was placed on an alumina substrate.
The product was placed on the substrate and fired in the air at 750"0 for 2 hours. As a result, molybdenum oxide whiskers of various shapes such as linear, rod-like, flake-like, etc. were formed.
実施例３
有機モリブデン化合物として８−ヒドロキシキノリンモ
リブデン（ＶＴ）の錯体化合物をアルミナ基板に０．５
ｇ乗せ、空気中にて８００℃で１時間焼成を行なった。Example 3 A complex compound of 8-hydroxyquinoline molybdenum (VT) as an organic molybdenum compound was deposited on an alumina substrate at a rate of 0.5
g, and calcined in air at 800° C. for 1 hour.
その結果、線状、棒状、フレーク状等をなす各種形状の
酸化モリブデンウィスカーが形成された。As a result, molybdenum oxide whiskers of various shapes such as linear, rod-like, flake-like, etc. were formed.
実施例４
有機モリブデン化合物としてジエチルジチオカルバミン
酸モリブデン（ＶＩ）の錯体化合物をアルミナ基板に０
．５ ｇ乗せ、空気中にて８５０℃で１時間焼成を行な
った。その結果、線状、棒状、フレーク状等をなす各種
形状の酸化モリブデンウィスカーが形成された。Example 4 A complex compound of molybdenum diethyldithiocarbamate (VI) as an organic molybdenum compound was deposited on an alumina substrate.
．． 5 g was placed on top and baked at 850° C. for 1 hour in air. As a result, molybdenum oxide whiskers of various shapes such as linear, rod-like, flake-like, etc. were formed.
また、実施例１〜４の焼成を酸素雰囲気中で行なっても
同様な結果が得られた。Furthermore, similar results were obtained even when firing Examples 1 to 4 in an oxygen atmosphere.
なお、実施例１〜４で得られたウィスカーは、Ｘ線回折
の結果、いずれも酸化モリブデンウィスカー（Ｍｏ０３
）であることが確認された。Note that the whiskers obtained in Examples 1 to 4 were all molybdenum oxide whiskers (Mo03) as a result of X-ray diffraction.
) was confirmed.
「発明の効果」
以上説明したように、本発明によれば、有機モリブデン
化合物を酸素含有雰囲気中で、有機モリブデン化合物の
熱分解温度以上で加熱焼成することにより、酸化モリブ
デンウィスカーを容易に得ることができる。そして、こ
うして得られた酸化モリブデンウィスカーは、線状、棒
状、フレーク状等の種々の形状をなし、プラスチック用
フィラー等各種工業材料としての用途が期待される。"Effects of the Invention" As explained above, according to the present invention, molybdenum oxide whiskers can be easily obtained by heating and firing an organic molybdenum compound in an oxygen-containing atmosphere at a temperature higher than the thermal decomposition temperature of the organic molybdenum compound. Can be done. The molybdenum oxide whiskers thus obtained have various shapes such as linear, rod-like, and flake-like shapes, and are expected to be used as various industrial materials such as fillers for plastics.
【図面の簡単な説明】
第１図、第２図および第３図は、いずれも本発明によっ
て得られた酸化モリブデンウィスカーの粒子構造を示す
１５倍の顕微鏡写真である。
区 区
−Ｃ，二BRIEF DESCRIPTION OF THE DRAWINGS FIGS. 1, 2 and 3 are all 15x micrographs showing the particle structure of molybdenum oxide whiskers obtained by the present invention. Ward Ward-C, 2
Claims (1)
リブデン化合物の熱分解温度以上で加熱焼成することを
特徴とする酸化モリブデンウィスカーの製法。1. A method for producing molybdenum oxide whiskers, which comprises heating and baking an organic molybdenum compound at a temperature higher than the thermal decomposition temperature of the organic molybdenum compound in an oxygen-containing atmosphere.