JPS59102910A - 含水ゲルの製造方法 - Google Patents
含水ゲルの製造方法Info
- Publication number
- JPS59102910A JPS59102910A JP21319982A JP21319982A JPS59102910A JP S59102910 A JPS59102910 A JP S59102910A JP 21319982 A JP21319982 A JP 21319982A JP 21319982 A JP21319982 A JP 21319982A JP S59102910 A JPS59102910 A JP S59102910A
- Authority
- JP
- Japan
- Prior art keywords
- added
- acrylamide
- polymerization
- polyacrylic acid
- gel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明は、常温で重合する非シキソトロビソクな高含水
ゲルの製造方法に閏するものである。
ゲルの製造方法に閏するものである。
含水ゲルは各種担体、具の他広い範囲に於て利用出来る
が、非シキソトロビソクで高粘性のものが常温で得られ
れば、形状化や生産性も良く、現場注型重合等も容易で
あるが、本発明に於て、ポリアクリル酸塩とアクリルア
ミドの水溶液に少量のＮ、Ｎ−メチレンビスアクリルア
ミドを加えることにより容品にレドックス重合し、得ら
れるものの物性も高含水、高強度、高粘弾性であって、
上記のニーズを充足することが判明した。
が、非シキソトロビソクで高粘性のものが常温で得られ
れば、形状化や生産性も良く、現場注型重合等も容易で
あるが、本発明に於て、ポリアクリル酸塩とアクリルア
ミドの水溶液に少量のＮ、Ｎ−メチレンビスアクリルア
ミドを加えることにより容品にレドックス重合し、得ら
れるものの物性も高含水、高強度、高粘弾性であって、
上記のニーズを充足することが判明した。
以下、本発明の好適実施例を説明する。
ポリアクリル酸１％水溶液７５０ｇに水酸化ナトリウム
４８％水溶液３ｇとＡ７！ ０ 約１９％とＮａ Ｏ
約２０％を含む液体アルミン酸ソーダ水溶液８ｇを加え
た溶液に、アクリルアミド３８ｇとＮ、Ｎ−メチレンヒ
スアクリルアミド０． ４ｇを加えて溶解した後、０．
１〜０．２ｇ程度の亜ニヂオン酸ナトリウムとベルオク
ソニ値酸ナトリウムを順次加えると、数分後に重合が開
始さ４Ｌると共に高粘弾性でタンク性のないものとなり
、５分後には容易に容器から取り出仕る状態となる。重
合物は強靭で、厚さ１０ｃｍ程度のものを指頭で押圧ず
れば底面迄凹むが、指頭をＰ］ｌＩせば直ちに復元する
高粘悼性を有する。
４８％水溶液３ｇとＡ７！ ０ 約１９％とＮａ Ｏ
約２０％を含む液体アルミン酸ソーダ水溶液８ｇを加え
た溶液に、アクリルアミド３８ｇとＮ、Ｎ−メチレンヒ
スアクリルアミド０． ４ｇを加えて溶解した後、０．
１〜０．２ｇ程度の亜ニヂオン酸ナトリウムとベルオク
ソニ値酸ナトリウムを順次加えると、数分後に重合が開
始さ４Ｌると共に高粘弾性でタンク性のないものとなり
、５分後には容易に容器から取り出仕る状態となる。重
合物は強靭で、厚さ１０ｃｍ程度のものを指頭で押圧ず
れば底面迄凹むが、指頭をＰ］ｌＩせば直ちに復元する
高粘悼性を有する。
尚、一般的な傾向としては、ポリアクリル酸に加えるア
ルミニウムイオンとＮ、Ｎ−メチレンヒスアクリルアミ
ドの量が多くなれば固さを増し、少なければ粘性を増す
傾向にあり、還元剤を亜二チオン酸す１リウムに代えて
硫酸第一鉄を使用場れば重合開始が更に早くなり、ベル
オクソニ硫酸−Ｊ−１リウムより溶解性の悪いカリウム
塩等を使用すれば重合開始時期を遅らせることが出来る
。
ルミニウムイオンとＮ、Ｎ−メチレンヒスアクリルアミ
ドの量が多くなれば固さを増し、少なければ粘性を増す
傾向にあり、還元剤を亜二チオン酸す１リウムに代えて
硫酸第一鉄を使用場れば重合開始が更に早くなり、ベル
オクソニ硫酸−Ｊ−１リウムより溶解性の悪いカリウム
塩等を使用すれば重合開始時期を遅らせることが出来る
。
以上の如く本発明によれば、高強度、高粘弾性の高含水
ゲルを容品に製造することが出来るが、特に本発明方法
は、添加試薬の量の変化により任意に重合物の物性を変
更することが出来るし、触媒の選択により重合速度を任
意に変更することも出来る特徴を有する。
ゲルを容品に製造することが出来るが、特に本発明方法
は、添加試薬の量の変化により任意に重合物の物性を変
更することが出来るし、触媒の選択により重合速度を任
意に変更することも出来る特徴を有する。
特許出願人 エスレン化工株式会社
Claims (1)
- 一価の陽イオンとアルミニウムイオンを加えたポリアク
リル酸水溶液にアクリルアミドとＮ、 Ｎ−メチレン
ビスアクリルアミドを添加し、更にレドックス触媒を加
えて常１温で重合することを特徴とする含水ゲルの製造
方法。