JPS588754A - Amino resin molding material - Google Patents
Amino resin molding materialInfo
- Publication number
- JPS588754A JPS588754A JP10763981A JP10763981A JPS588754A JP S588754 A JPS588754 A JP S588754A JP 10763981 A JP10763981 A JP 10763981A JP 10763981 A JP10763981 A JP 10763981A JP S588754 A JPS588754 A JP S588754A
- Authority
- JP
- Japan
- Prior art keywords
- amino resin
- molding material
- resin
- parts
- resin molding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
本発明は配線器具、電気器具等に用いられるアミノ樹脂
成形材料に関するもので、その目的とするところは成形
品の耐rンサートクラック性とドリル加工性を向上させ
ることにある。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to an amino resin molding material used for wiring devices, electric appliances, etc., and its purpose is to improve insert crack resistance and drill workability of molded products. be.
従来、アミノ樹脂成形品の耐イン→1−−1−クフック
性やドリル加工性を向上させるためにはスチレンゴム、
ニトリルゴム等を添加していたがアミノ樹脂と相溶性が
、ケいため成形時のガス抜は性、成形品外観に問題があ
った。Conventionally, styrene rubber,
Although nitrile rubber and the like were added, it was not compatible with the amino resin, causing problems in degassing during molding and in the appearance of the molded product.
本発明はト記欠点を解決するもので、アミノ樹脂と相溶
性のある弾性体を含有させることによっ”C成形性、成
形品外観のよい耐インサートクラツク性、ドIJ ル加
工性に優れたアミノ樹脂成形材料を得ることができたも
のである。The present invention solves the above-mentioned drawbacks by containing an elastic material that is compatible with an amino resin, resulting in excellent C moldability, good insert crack resistance, and IJ molding processability with a good appearance of the molded product. It was possible to obtain an amino resin molding material.
次に本発明の詳細な説明する。本発明に用いるアミノ樹
脂はユリア樹脂、メラミン樹脂、グアナミン樹脂、フェ
ノール変性メラミン樹脂等であり液状乃至固型状の各れ
でもよい。アミノ樹脂と相溶性のある弾性体としてはブ
チフール、アクリル系樹脂等がよく液状乃至固型状の各
れでもよい。Next, the present invention will be explained in detail. The amino resin used in the present invention may be a urea resin, a melamine resin, a guanamine resin, a phenol-modified melamine resin, etc., and may be in either liquid or solid form. As the elastic body compatible with the amino resin, butyfur, acrylic resin, etc. are preferable, and the elastic body may be either liquid or solid.
アミノ樹脂、弾性体以外の添加物としてはアミノ樹脂成
形材料として一般に用いられる硬化剤、離型剤、基材、
充填剤、着色剤等をそのまま用いることができ、E記材
料を混合、混練、粉砕し或は必要に応じて造粒しアミノ
樹脂成形材料を得るものである。Additives other than amino resin and elastomer include curing agents, mold release agents, base materials, which are commonly used as amino resin molding materials.
Fillers, coloring agents, etc. can be used as they are, and the amino resin molding material can be obtained by mixing, kneading, pulverizing, or, if necessary, granulating the materials listed in E.
以F本発明を実施例にもとすいて説明する。Hereinafter, the present invention will be explained based on examples.
実施例1
残留水分10重量%(以下単に%と記す)の固型メラミ
ン樹脂60重量部C以下単に部と記す)に対し木粉a部
、フタル酸o5部、ヌテアリン酸亜鉛】部、着色剤1部
、アクリル樹脂0.8部を添加し混合、混線、粉砕して
メラミン樹脂成形材料を得た。Example 1 60 parts by weight of a solid melamine resin with residual moisture of 10% (hereinafter simply referred to as %), a part of wood flour, 5 parts of phthalic acid, 5 parts of zinc nateate, and a coloring agent. 1 part of acrylic resin and 0.8 part of acrylic resin were added, mixed, mixed, and crushed to obtain a melamine resin molding material.
実施例2
樹脂含有量60%のユリア樹脂初期縮合物1800部に
対して塩化アンモニウム0.8部、水酸化ナトリウム部
、バルブzoo部、分子量1100のプチヲール18部
を添加し混合、混練、乾燥して乾燥品を得、該乾燥品1
00部に対してステアリン酸亜鉛0.5部、着色剤0.
5部を加えボールミルで着色、粉砕してアミノ樹脂成形
材料を得た。Example 2 To 1800 parts of a urea resin initial condensate with a resin content of 60%, 0.8 parts of ammonium chloride, part of sodium hydroxide, part of valve zoo, and 18 parts of petit wort with a molecular weight of 1100 were added, mixed, kneaded, and dried. to obtain a dried product, and the dried product 1
0.00 parts, 0.5 parts of zinc stearate, 0.0 parts of colorant.
5 parts were added, colored with a ball mill, and crushed to obtain an amino resin molding material.
比較例
実施例2と同じ樹脂含有1に60%のユリア樹脂初期縮
合物1800部に対して塩化アンモニウム0.8部、水
酸化ナトリウム0.1部、パルプ260部を添加し混合
、混線、乾燥して乾燥品を得、該乾燥品100部に対し
てステアリン酸亜鉛0.6部、着色剤0.6部を加えボ
ールミルで着色、粉砕してアミノ樹脂成形材料を得た。Comparative Example To the same resin content 1 as in Example 2, 0.8 parts of ammonium chloride, 0.1 part of sodium hydroxide, and 260 parts of pulp were added to 1800 parts of a 60% urea resin initial condensate, mixed, mixed, and dried. A dry product was obtained, and 0.6 parts of zinc stearate and 0.6 parts of a coloring agent were added to 100 parts of the dry product, colored with a ball mill, and pulverized to obtain an amino resin molding material.
実施例1及び2と比較例のアミノ樹脂成形材料を金属イ
ンサート成形しインサート周辺のクラック発生状況及び
成形品のドリル加工性を試験した結果は第1表に示すよ
うに本発明のアミノ樹脂成形材料から得られた成形品の
耐インサートクラツク性及びドリル加工性はよく本発明
の優れていることを確認した。The amino resin molding materials of Examples 1 and 2 and Comparative Examples were metal insert molded, and the occurrence of cracks around the inserts and the drill workability of the molded products were tested. The results are shown in Table 1. It was confirmed that the insert crack resistance and drill workability of the molded product obtained from the method were excellent, and were superior to those of the present invention.
第 1 表 特許出願人 松下電工株式会社 代理人弁理士9.竹 元 敏 丸 (#1か2名)Chapter 1 Table patent applicant Matsushita Electric Works Co., Ltd. Representative patent attorney9. Bamboo Moto Toshimaru (#1 or 2 people)
Claims (2)
ことを特徴とするアミノ樹脂成形材料。(1) An amino resin molding material characterized by containing an elastic body that is compatible with the amino resin.
求の範囲第1項記載のアミノ樹脂成形材料。(2) The amino resin molding material according to claim 1, wherein the elastic body is a synthetic resin.