JPS58204059A - Paint - Google Patents

Abstract

PURPOSE:To provide paint which has good workability, can be coated on weak wood, etc. and can form a lightweight sandy surface texture having excellent elasticity, heat insulating properties, etc. when applied on furnishings, building board, etc., by mixing a synthetic resin paint component, a pigment and cork powder. CONSTITUTION:70-80% synthetic resin paint component such as non-rigid urethane resin paint, 10-20% pigment and 10% cork powder having a particle size of 100 mesh are mixed together to obtain paint.

Description

[Detailed description of the invention]
By mixing the pigment and cork powder in the greasy coating 1 and using cork powder as an adulterant, it is possible to create a mixture similar to the one using diamond sand in 1). Precipitating acid in the resin coated book 1 and painting while stirring constantly, there is no need for any special coating techniques.

Also, the cell tissue is small (about /111111'/, 0
By using cork powder with a large number of pores, it has good compatibility with resin paints and pigments, and does not cause cracks on the painted surface after painting, making it ideal. Being able to obtain sandy skin.

By obtaining a paint that forms a light and soft sandy surface, it can be applied easily even to fragile objects, and when applied to interior panels of buildings, etc., it has good elasticity and heat retention. Also, it is possible to obtain an interior board with extremely excellent soundproofing properties.

By using inexpensive cork powder as the material that makes up the sandy surface, the finished surface after painting is 1j'i+ fdl.
The paint is cheap, and pigments of different colors can be used without being affected by the color, so it is a divine color paint such as electrolytic primary color paint or mixed color paint. It is also possible to obtain. etc.

Conventionally, artificial fat-absorbing paints such as lacquer (a mixture of pigments and diamond sand) have been used as paints to create a sandy texture on the painted surface after painting. II Since it is a mixture of natural resin paint, pigment, and diamond sand in a predetermined ratio, when painting with this paint, diamond sand settles in the coating solution, so 1/I'! The paint must be constantly stirred while being painted, and since Kongo 6/ν is not compatible with other resin paints or pigments, cracks may sometimes occur on the dried painted surface. Not only that, but
Kongo with a high specific IF (due to l'ν, it is a weak target)
It is not suitable for decorative objects, and since the painted surface does not have an ammunition gradient of 1/[(Rice temperature resistance) or resistance to 7. It is not suitable as a paint for coating (11), and historically, since expensive diamond sand is used, the resulting paint is expensive, and even inexpensive coating products are expensive. Ta.

The present invention relates to a paint intended to eliminate the above-mentioned conventional drawbacks, and examples thereof will be described below.

1 Actual gun example/" After polishing the surface of the veneer with a width of about 9.0 crrr and a length of about 1/germ using an ordinary Sangu, apply an undercoat of urethane resin paint to this surface, and then apply this coat to the surface. After drying the surface, polish the surface with +TF degree Sangu, then apply soft urethane resin paint 3! To Og, the black pigment SOg was crushed into a fine powder of about 100 pieces using a granulator, and the paint made by mixing it with 33g of cork powder was sprayed for painting. After applying the above-mentioned veneer to the entire surface, a coating layer of 2 tons was formed on the entire surface, and after drying naturally for about 2 hours, 1
-A soft urethane resin paint is applied and the 11-thorn coating is applied to form a chemically coated rice board.As a result, what does the painted surface look like? 4'', mixed with $10 = 1 lux of powder (1f finer sand tllll skin can be produced than this).

1 Example 2]! 8t-1 method approx. 90 t-In-kt J' i person/g
To the surface of the erm -> Polish the surface of the machine with J paper, then apply soft urethane resin paint 3 to this polished surface! Paint fL' mixed with 33 g of J cork powder;
fr- put it in Sokawa's old blowing machine and paint it, lJ
After drying the painted surface and polishing the surface with a Sangu, the paint consisting of urethane resin paint, pigment, and cork powder mixed in the same ratio as MiJ is sprayed onto the painted surface using a mist machine. Spray on the entire painted surface to a thickness/
Then, I applied a double layer of fir-degree acid formation to the painted part of the Ω bridge, allowed it to dry naturally for about 2 hours, and then applied a soft urethane resin paint for 41 coats and finished it. I did-
As a result, it was possible to form a strong [corrugated] surface with meat Pi and a thin sandy surface on the surface.

As described in +iii, the paint according to the present invention is a synthetic resin paint 7.
This is because it is characterized by forming a light and soft skin on the painted surface after painting by mixing 70-20% pigment and 70% cork powder. Since the cork powder that makes up the sandy surface is extremely clumpy, the cork powder will not settle even if left for a while during painting. It is possible to eliminate feces, and when painting, it is possible to apply ordinary resin paint.
If painted in the curvature of li, there will be no problem with q1/l]
Since the paint is made of natural material, it does not require any special painting techniques, and since it uses cork powder, which has extremely small cell structures and many pores, it has good compatibility with synthetic resin paints and pigments. After painting, it does not cause cracks on the painted surface and lower the F of the product equipment, and it also does not peel off easily due to the 1γ/M of the main rule etc., making it ideal. Sandy skin? '
+x It has the certainty of being a paint, and can be applied to fragile wood surfaces without any problems. If l is painted on architectural interiors, it will have elasticity and heat retention.
It is "I fil" to form an excellent interior board on the interior of the building, and to use inexpensive cork powder. In addition, there are special effects such as being able to obtain electrolytic powder, kana primary color φ materials, and mixed color paint without being affected by cork powder mixed in.

Claims (1)

[Claims] Synthetic resin paint 70~gOchitoface1') / 0~. 20
A paint that is characterized by forming a light bc (I) filler surface on the painted surface after painting by mixing 70 g of cork powder.