CN106585258A - Flexible travertine-simulated patch stone and preparation method thereof - Google Patents
Flexible travertine-simulated patch stone and preparation method thereof Download PDFInfo
- Publication number
- CN106585258A CN106585258A CN201710070051.5A CN201710070051A CN106585258A CN 106585258 A CN106585258 A CN 106585258A CN 201710070051 A CN201710070051 A CN 201710070051A CN 106585258 A CN106585258 A CN 106585258A
- Authority
- CN
- China
- Prior art keywords
- stone
- parts
- color
- preparation
- hole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a flexible travertine-simulated patch stone and a preparation method thereof. According to the method, spots or patterns are formed on templates by using graded mixed slurry in multiple colors through a multi-layer spraying and overlapping method so that the mottled and rich-colored naturally-changing texture of natural stones can be formed, and further cavities and gap structures are formed through the template. Therefore, a manufactured patch can completely show the appearance effect of natural travertine. Meanwhile, the flexible travertine-simulated patch stone is mottled and rich in color and natural in texture change, has cavities and gap structures similar to those of natural travertine, has the same appearance effect as natural travertine, and also has the characteristic of bendability.
Description
Technical field
The present invention relates to architectural decoration material field, in particular to flexible imitative hole stone patch stone and preparation method thereof.
Background technology
Natural cavity stone is a kind of continental deposit rock, there is the hole that form is different, while color spot is miscellaneous, texture-rich, matter
The rich change of sense, has special charm used in elevation of building decoration.But natural cavity stone material is crisp, and price is high, in reality
Border is using above there is many limitation.
In order to solve natural cavity stone limitation in use, people copy the color and texture of natural cavity stone, produce
Various manually imitative hole stone materials.The appearance of these artificial imitative hole stone materials, not only solves natural cavity stone in actual use
Defect, while also reducing fitting-up cost, beautified building structure.
Like product in the market be all it is simple by raw material by mould compressing, the raw material face of employing
Color, level are single with state, are at most rendered with the colorant of coating class on surface.
However, by obtained in existing method hole stone, be only capable of from decorative pattern showing the hole hole structure of hole stone, its face in shape
Color, texture are single stiff, it is impossible to embody the naturally mottled color of hole stone comprehensively, and abundant texture change and multi-level skin texture is tied
Structure
In view of this, it is special to propose the present invention.
The content of the invention
The first object of the present invention is to provide a kind of preparation method of flexible imitative hole stone patch stone, in methods described, is led to
Method formation spot or decorative pattern that the mixture slurry for matching somebody with somebody multiple color, level sprays superposition in template using multilayer are crossed, so as to
The mottled abundant color of lithotome, the texture of natural trend can be formed, further in addition formed by template shape cavity, gap
Structure, thus the apparent effect for embodying natural cavity stone that obtained patch stone can be complete.
The second object of the present invention is to provide a kind of flexible imitative hole stone patch stone, the flexible imitative hole stone paster stone of the present invention
Variegation refutes abundant, texture change nature, while also have the cavity similar to natural cavity stone and gap structure, with Natural Cave
The apparent effect of stone identical.Further, the flexible imitative hole stone patch stone of the present invention has good flexibility, it is possible to bend, because
And there is good practicality, can be suitable for different environment and space.
In order to realize the above-mentioned purpose of the present invention, spy employs the following technical solutions：
A kind of preparation method of flexible imitative hole stone patch stone, the preparation method comprises the steps：
Primary colours, spot and the decorative pattern color of hole stone is copied in decomposition, selects the quartz sand or stone flour of respective color；
According to decompose the color, by the quartz sand/stone flour of selected color, resin emulsion, auxiliary agent, wood fibre and
After water mixing, the mixture slurry of respective color is respectively obtained；
The mixture slurry of respective color is sprayed in template, spot or decorative pattern is formed；
Lamination sprays the mixture slurry of the hole ground mass color to be copied, and covers the spot or decorative pattern, forms facing sand
Glue-line；
Glass fiber mesh is flatly paved to be embedded in facing mastic bed；
Mixture slurry is scraped in facing mastic bed superimposed layer batch, is formed and is strengthened mastic bed, and be dried；
The demoulding, and in the side coating weathering protective layer of spraying spottiness or decorative pattern, drying and moulding.
Optionally, in the present invention, in parts by weight, the mixture slurry by 40～60 parts of quartz sands or stone flour, 20
～30 parts of resin emulsions, 3～5 parts of auxiliary agents, 0.1～0.5 part of wood fibre and 15～20 parts of water are mixed.
Optionally, in the present invention, facing mastic bed is prepared in mixture slurry used, and it is 100 that the level of quartz sand or stone flour is matched somebody with somebody
～120 mesh；Strengthen mastic bed to prepare in mixture slurry used, it is 40～60 mesh that the level of quartz sand or stone flour is matched somebody with somebody.
Optionally, in the present invention, the resin emulsion is the one kind in styrene-acrylic emulsion, acrylic emulsion or silicone acrylic emulsion
Or several mixed emulsions.
Optionally, in the present invention, it is described be 2～3 parts of biocide mildewcides, 2～3 parts of antifreezing agents, 2～3 parts of waterproof NMFs,
The mixing of one or more in 8～10 parts of thickeners, 6～8 parts of film forming agents, 5～8 parts of fire retardants and 4～5 parts of dispersants is helped
Agent.
Optionally, in the present invention, the template is silica gel pattern mould.
Optionally, in the present invention, the template is light face die plate or decorative pattern template.
Optionally, in the present invention, the glass fiber mesh is flatly paved to be embedded in facing mastic bed and is specially：By glass fiber mesh
It is laid on facing mastic bed, and glass fiber mesh is flatly paved to be embedded into into facing mastic bed.
Optionally, in the present invention, the drying is to dry or dry.
Further, present invention also offers flexible by obtained in the method for the invention imitate hole stone patch stone.
Compared with prior art, beneficial effects of the present invention are：
In the present invention, according to the colour and skin texture structure of stone material, using artificial operation, assorted mixture slurry is being pressed into stone material
Carry out lamination spraying in the template of prototype facsimile reproduction successively, thus can completely represent the abundant color of natural cavity stone, texture and skin texture,
And color and luster is embodied by stone flour true qualities, will not fade；Meanwhile, the technique of multilayer spraying is it is also possible that flexible imitative hole stone patch stone
The texture of finished product is finer and smoother.Further, the imitative hole stone paster of the present invention has good flexible and machinability, can be not
Apply in environment together and scene.
Specific embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the present invention.It is unreceipted concrete in embodiment
Condition person, the condition advised according to normal condition or manufacturer is carried out.Agents useful for same or the unreceipted production firm person of instrument, are
The conventional products that commercially available purchase is obtained can be passed through.
First be to decompose primary colours, spot and the decorative pattern color to be copied hole stone in the present invention, select respective color and
The quartz sand or stone flour of grain composition；Using quartz sand or stone flour as spraying paste materials, can not only more naturally imitate
The color and texture of hole stone；Meanwhile, quartz sand and stone flour not fugitive color, further obtained patch stone be not easy to fade, energy
It is enough to use for a long time, and keep decorative effect；
According to the color decomposed, by the mixing of the stone flour of selected color, resin emulsion, auxiliary agent, wood fibre and water
Afterwards, the mixture slurry of respective color is respectively obtained；
Wherein, in parts by weight, the mixture slurry be by 40～60 parts of quartz sands or stone flour, for example quartz sand or
Stone flour can be, but be not limited to 45,50 or 55 parts etc.；20～30 parts of resin emulsions, for example resin emulsion can be, but not limit
In 22,25,27 or 29 parts etc.；3～5 parts of auxiliary agents, such as auxiliary agent can be, but be not limited to 4 parts etc.；0.1～0.5 part of wooden fibre
Dimension, for example wood fibre can be, but be not limited to 0.2,0.3 or 0.4 part etc.；And 15～20 parts of water, such as water can be,
But it is not limited to 16,18 or 19 parts etc.；
Further, it is a kind of or several during the resin emulsion is for styrene-acrylic emulsion, acrylic emulsion either silicone acrylic emulsion
The mixed emulsion planted；
Meanwhile, the auxiliary agent be 2～3 parts of biocide mildewcides, 2～3 parts of antifreezing agents, 2～3 parts of waterproof NMFs, 8～10 parts
The mixed aid of one or more in thickener, 6～8 parts of film forming agents, 5～8 parts of fire retardants and 4～5 parts of dispersants；
After the completion of the mixture slurry of required shades of colour is prepared, begin to carry out formal spraying, specific spraying
Step is as follows：
1) on the silica gel pattern mould for pressing stone material prototype facsimile reproduction, according to required color (that is, according to to be copied hole ground mass color
The required one of which color that decomposition draws), with spray gun spraying ground floor mixture slurry, to form the spot with required form
Point or decorative pattern, in spraying process, can pass through the air pressure of control spraying and the bore of rifle mouth to control the size of spot
Or the thickness of decorative pattern；
Then, other colors according to needed for lamination spraying, in ground floor mixture slurry coating other colors are sprayed successively
Mixture slurry, and enable other blend of colors layer of slurry to cover spot or the flower that the first mixture slurry coating is formed
Line, so as to finally give with the facing mastic bed with hole ground mass color same color, then by high convex portion position on facing mastic bed
Mixture slurry strike off so that facing mastic bed surfacing；
Further, in this step, it is 100～120 mesh that the level of mixture slurry Central Plains work stone sand used or stone flour is matched somebody with somebody；
In finish coat, the less aggregate of particle diameter is selected, can further strengthen the packing on surface and the sophistication of spot；
Because the primary colours of hole stone are often that two kinds of mixture slurry superposition occlusions are formed, so the decomposition of primary colours and spraying time
Sequence is main points, thus in the spraying process of this step, also will be after top layer primary colours first spray covering, high convex portion position mixing slurry
Body strikes off, then sprays covering lower floor primary colours；
2) then, glass fiber mesh is flatly paved to be embedded in facing mastic bed, to consolidate the fastness of facing mastic bed, specifically
Operation is as follows：
Glass fiber mesh is laid on the wet facing mastic bed for just having sprayed, using sponge roller by the institute after tiling
State the online whole face of glass fibre gently to roll, make in the embedded facing mastic bed of glass fiber mesh；
3) and then, batch scrape mixture slurry in facing mastic bed superimposed layer, to form reinforcement mastic bed, and be dried；
Wherein, the drying is for drying or dries；Dry temperature is preferably 20～40 DEG C, it is furthermore preferred that be dried
Temperature is 30 DEG C or so；
Further, in this step, it is 40～60 mesh that the level of mixture slurry Central Plains work stone sand used or stone flour is matched somebody with somebody；Adding
In strong layer, from the big aggregate of particle diameter as raw material, the surface strength of patch stone on the one hand can be to increase；On the other hand also can
Enough embody the pore structure inside the stone of hole.
4) last, be exactly the demoulding, by step 3) in semi-finished product remove from template, then, spraying spottiness or flower
Side coating weathering protective layer (side of mastic bed covering is not reinforced in semi-finished product) of line, coats weathering protective layer, and
Drying or drying forming, obtaining the flexible imitative hole stone patch stone of finished product；
It is common, weathering protective layer be it is transparent, its material can as needed selection acrylic acid, silicon third, organosilicon or
Person's fluorine carbon.
Flexibility imitative hole stone patch stone color, shape and texture and natural cavity stone by obtained by above-mentioned steps is close to, and
And not fugitive color.
Embodiment 1
Flexible imitative hole stone patch stone is prepared according to step as described below：
(1) decompose primary colours, spot and the decorative pattern color to be copied hole stone, select the quartz sand and stone of respective color
Powder；
According to the color decomposed, by the stone flour of 40 parts of selected colors, 20 parts of resin emulsions, 5 parts of auxiliary agents, 0.5 part of wood
After matter fiber and 20 parts of water mixing, the mixture slurry of stone flour color is made；
According to the color decomposed, by the quartz sand of 60 parts of selected colors, 30 parts of resin emulsions, 3 parts of auxiliary agents, 0.5 part
After wood fibre and 15 parts of water mixing, the mixture slurry of quartz sand color is made；
Wherein, it is 100～120 mesh that the level of stone flour and quartz sand is matched somebody with somebody；
(2) mixture slurry of the stone flour color is sprayed in template, forms spot or decorative pattern；
The mixture slurry of lamination sputtered quartz sand color, and the spot or decorative pattern are covered, facing mastic bed is formed, and will
Surface strikes off；
(3) glass fiber mesh is laid on the wet facing mastic bed for just having sprayed, will be after tiling using sponge roller
The online whole face of the glass fibre gently roll, make in the embedded facing mastic bed of glass fiber mesh；
(4) and then, according to the required color of classification, by the stone flour of 50 parts of selected colors, 20 parts of resin emulsions, 5 parts of auxiliary agents,
After 0.5 part of wood fibre and 20 parts of water mixing, the mixture slurry of stone flour color is made；
Wherein, it is 40～60 mesh that the level of stone flour is matched somebody with somebody；
Then, the mixture slurry of the stone flour color is scraped in facing mastic bed superimposed layer batch, is formed and is strengthened mastic bed, and 30
Dry at DEG C；
(5) demoulding, and in the side coating weathering protective layer of spraying spottiness or decorative pattern, as drying and moulding, embodiment 1
The imitative hole stone patch stone of flexibility.
Embodiment 2
Flexible imitative hole stone patch stone is prepared according to step as described below：
(1) decompose primary colours, spot and the decorative pattern color to be copied hole stone, select the quartz sand and stone of respective color
Powder；
According to the color decomposed, by the stone flour of 60 parts of selected colors, 30 parts of resin emulsions, 3 parts of auxiliary agents, 0.5 part of wood
After matter fiber and 15 parts of water mixing, the mixture slurry of stone flour color is made；
According to the color decomposed, by the stone flour of 50 parts of selected colors, 20 parts of resin emulsions, 4 parts of auxiliary agents, 0.5 part of wood
After matter fiber and 20 parts of water mixing, the mixture slurry of quartz sand color is made；
Wherein, it is 100～120 mesh that the level of stone flour is matched somebody with somebody；
(2) mixture slurry of the quartz sand color is sprayed in template, forms spot or decorative pattern；
Lamination sprays the mixture slurry of stone flour color, and covers the spot or decorative pattern, forms facing mastic bed, and by table
Face strikes off；
(3) glass fiber mesh is laid on the wet facing mastic bed for just having sprayed, will be after tiling using sponge roller
The online whole face of the glass fibre gently roll, make in the embedded facing mastic bed of glass fiber mesh；
(4) and then, according to the required color of classification, the quartz sand of 55 parts of selected colors, 25 parts of resin emulsions, 3 parts are helped
After agent, 0.5 part of wood fibre and 15 parts of water mixing, the mixture slurry of stone flour color is made；
Wherein, it is 40～60 mesh that the level of quartz sand is matched somebody with somebody；
Then, the mixture slurry of the stone flour color is scraped in facing mastic bed superimposed layer batch, is formed and is strengthened mastic bed, and 30
Dry at DEG C；
(5) demoulding, and in the side coating weathering protective layer of spraying spottiness or decorative pattern, as drying and moulding, embodiment 2
The imitative hole stone patch stone of flexibility.
Embodiment 3
Flexible imitative hole stone patch stone is prepared according to step as described below：
(1) decompose primary colours, spot and the decorative pattern color to be copied hole stone, select the quartz sand and stone of respective color
Powder；
According to the color decomposed, by the quartz sand of 55 parts of selected colors, 25 parts of resin emulsions, 5 parts of auxiliary agents, 0.5 part
After wood fibre and 20 parts of water mixing, the mixture slurry of stone flour color is made；
According to the color decomposed, by the quartz sand of 40 parts of selected colors, 25 parts of resin emulsions, 3 parts of auxiliary agents, 0.5 part
After wood fibre and 15 parts of water mixing, the mixture slurry of quartz sand color is made；
Wherein, it is 100～120 mesh that the level of quartz sand is matched somebody with somebody；
(2) mixture slurry of the stone flour color is sprayed in template, forms spot or decorative pattern；
The mixture slurry of lamination sputtered quartz sand color, and the spot or decorative pattern are covered, facing mastic bed is formed, and will
Surface strikes off；
(3) glass fiber mesh is laid on the wet facing mastic bed for just having sprayed, will be after tiling using sponge roller
The online whole face of the glass fibre gently roll, make in the embedded facing mastic bed of glass fiber mesh；
(4) and then, according to the required color of classification, by the stone flour of 40 parts of selected colors, 25 parts of resin emulsions, 5 parts of auxiliary agents,
After 0.5 part of wood fibre and 20 parts of water mixing, the mixture slurry of stone flour color is made；
Wherein, it is 40～60 mesh that the level of stone flour is matched somebody with somebody；
Then, the mixture slurry of the stone flour color is scraped in facing mastic bed superimposed layer batch, is formed and is strengthened mastic bed, and 30
Dry at DEG C；
(5) demoulding, and in the side coating weathering protective layer of spraying spottiness or decorative pattern, as drying and moulding, embodiment 3
The imitative hole stone patch stone of flexibility.
Comparative example 1
According to the imitative hole stone patch stone of the methods described of embodiment 1 manufacture, wherein, in the mixture slurry used in comparative example 1, and
Wood fibre is not used.
Comparative example 2
According to the imitative hole stone patch stone of the methods described of embodiment 2 manufacture, wherein, in the mixture slurry used in comparative example 2, and
Wood fibre is not used.
Comparative example 3
According to the imitative hole stone patch stone of the methods described of embodiment 3 manufacture, wherein, in the mixture slurry used in comparative example 3, and
Wood fibre is not used.
Experimental example 1
Respectively by 100 pieces of embodiments 1 and comparative example 1；Embodiment 2 and comparative example 2；And embodiment 3 is made with comparative example 3
The imitative hole stone patch stone packet for obtaining is contrasted.
As a result find, according to imitative hole stone patch stone surface no cracking prepared by feed process in embodiment, and it is corresponding with
Imitative hole stone patch stone described in comparative example 1-3 obtained by feed process then has local cracking.
Further, by embodiment imitative hole stone patch stone bending after restore, the imitative hole stone chip surface after recovery without
Cracking phenomena；Identical experiment is carried out with imitative hole stone patch stone prepared in comparative example, the imitative hole stone patch of comparative example is as a result found
There is upon bending, easily local surfaces crackle in slabstone.
As can be seen here, with the imitative hole stone patch stone significant performance of flexibility obtained by raw material of the present invention and method more.
Further, the wood fibre for being added can also effectively improve the adhesion strength and anti-cracking performance of product, while so that dry
Dry process evenly, and reduces surface checking.
In the present invention, by the color of primary colours, spot and decorative pattern according to imitated hole stone, respective color and particle diameter are selected
The natural siliceous sand of size or building stones powder add special macromolecule emulsion to make slurry, the color, skin texture structure according to stone material,
Determine spraying order, quantity and the mode of various slurries, slurry be sprayed on successively on the silica gel pattern mould by stone material prototype facsimile reproduction,
The abundant color of natural cavity stone, texture and skin texture can not only completely be represented, and color and luster is embodied by stone flour true qualities, will not be faded.
Further, the imitative hole stone patch stone obtained by the present invention has good pliability, can bend, and upon bending also not
Cracking occurs and layering of rupturing, with good practicality, and varying environment and the different fields for needing can be applied to
In conjunction.
Meanwhile, in the present invention, the slurry matched somebody with somebody using multiple color, level is sprayed superposition on forming panel and forms spot or flower
Line, the method for drying or drying aftershaping so that it is mottled rich that the imitative hole stone patch stone of obtained flexibility can form lithotome
Rich color, the texture of natural trend, along with cavity, gap structure that template is formed, the apparent effect of natural cavity stone is just complete
Whole shows.
Although illustrate and describing the present invention with specific embodiment, but will be appreciated that without departing substantially from the present invention's
Many other changes and modification can be made in the case of spirit and scope.It is, therefore, intended that in the following claims
Including all such changes and modifications belonged in the scope of the invention.
Claims (10)
1. a kind of flexibility imitates the preparation method of hole stone patch stone, it is characterised in that the preparation method comprises the steps：
Primary colours, spot and the decorative pattern color of hole stone is copied in decomposition, selects the quartz sand or stone flour of respective color；
According to the color decomposed, the quartz sand/stone flour of selected color, resin emulsion, auxiliary agent, wood fibre and water are mixed
After conjunction, the mixture slurry of respective color is respectively obtained；
The mixture slurry of respective color is sprayed in template, spot or decorative pattern is formed；
Lamination sprays the mixture slurry of the hole ground mass color to be copied, and covers the spot or decorative pattern, forms facing mastic bed；
Glass fiber mesh is flatly paved to be embedded in facing mastic bed；
Mixture slurry is scraped in facing mastic bed superimposed layer batch, is formed and is strengthened mastic bed, and be dried；
The demoulding, and in the side coating weathering protective layer of spraying spottiness or decorative pattern, drying and moulding.
2. flexibility according to claim 1 imitates the preparation method of hole stone patch stone, it is characterised in that according to parts by weight
Meter, the mixture slurry by 40～60 parts of quartz sands or stone flour, 20～30 parts of resin emulsions, 3～5 parts of auxiliary agents, 0.1～0.5 part
Wood fibre and 15～20 parts of water are mixed.
3. flexibility according to claim 2 imitates the preparation method of hole stone patch stone, it is characterised in that prepared by facing mastic bed
In mixture slurry used, it is 100～120 mesh that the level of quartz sand or stone flour is matched somebody with somebody；Strengthen mastic bed to prepare in mixture slurry used, stone
It is 40～60 mesh that the level of sand or stone flour is matched somebody with somebody.
4. the preparation method of flexible imitative hole stone patch stone according to claim 1, it is characterised in that the resin emulsion is
One or several mixed emulsion in styrene-acrylic emulsion, acrylic emulsion or silicone acrylic emulsion.
5. flexibility according to claim 1 imitates the preparation method of hole stone patch stone, it is characterised in that the auxiliary agent is 2～3
Part biocide mildewcide, 2～3 parts of antifreezing agents, 2～3 parts of waterproof NMFs, 8～10 parts of thickeners, 6～8 parts of film forming agents, 5～8 parts
The mixed aid of one or more in fire retardant and 4～5 parts of dispersants.
6. flexibility according to claim 1 imitates the preparation method of hole stone patch stone, it is characterised in that the template is silica gel
Template.
7. flexibility according to claim 6 imitates the preparation method of hole stone patch stone, it is characterised in that the template is light face
Template or decorative pattern template.
8. flexibility according to claim 1 imitates the preparation method of hole stone patch stone, it is characterised in that the glass fiber mesh
It is flatly paved to be embedded in facing mastic bed and is specially：Glass fiber mesh is laid on facing mastic bed, and glass fiber mesh is tiled
In embedded facing mastic bed.
9. flexibility according to claim 1 imitates the preparation method of hole stone patch stone, it is characterised in that the drying is to dry
Or drying.
10. it is flexible obtained in the method by any one of claim 1-9 to imitate hole stone patch stone.