JPH11241259A - Nonwoven fabric, wiping cloth and face cloth - Google Patents
Nonwoven fabric, wiping cloth and face clothInfo
- Publication number
- JPH11241259A JPH11241259A JP10045152A JP4515298A JPH11241259A JP H11241259 A JPH11241259 A JP H11241259A JP 10045152 A JP10045152 A JP 10045152A JP 4515298 A JP4515298 A JP 4515298A JP H11241259 A JPH11241259 A JP H11241259A
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- sea
- island
- fabric according
- composite fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ソフトな表面タッ
チを有するにも拘らず腰がある上に、成形性にも優れた
不織布、ワイピングクロスおよび表皮材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a nonwoven fabric, a wiping cloth and a skin material, which have a soft surface touch but are stiff and excellent in formability.
【０００２】[0002]
【従来の技術】従来から不織布は、製編織する工程を要
しない簡便な布帛として、各種用途に重宝に用いられて
いるが、タッチ特性と腰、さらに成形性まで満足する３
拍子揃った不織布は、存在しなかった。2. Description of the Related Art Conventionally, nonwoven fabrics have been used for various purposes as simple fabrics that do not require a knitting or weaving process.
There was no nonwoven fabric with uniform beat.
【０００３】たとえば、ワイピングクロスとしては、ワ
イピング性能を上げるために極細繊維で構成された編織
物や不織布が使用されてきた。また、表皮材や土木用な
どではレギュラーポリエステル繊維からなる不織布が使
用されてきた。[0003] For example, as a wiping cloth, a knitted or woven fabric made of ultrafine fibers has been used in order to improve wiping performance. Further, nonwoven fabrics made of regular polyester fibers have been used for skin materials and civil engineering.
【０００４】[0004]
【発明が解決しようとする課題】かかる従来ワイピング
クロスは、極細繊維で構成された編織物や不織布であ
り、腰がないものばかりで、力が入りにくく取り扱い性
が悪いので、眼鏡など小物の拭き取りには良いものの、
力のかかる大物の拭き取りには向かないという問題を有
するものであった。また、表皮材や土木用の不織布は、
ゴワゴワした感触のものでしかなかったし、さらに成型
性も乏しいものであった。Such a conventional wiping cloth is a knitted or woven fabric made of ultrafine fibers, and has no rigidity. It is hard to apply force and has poor handling properties. Although good for
This method has a problem that it is not suitable for wiping a large heavy object. In addition, non-woven fabrics for skin materials and civil engineering
It had only a rough feel and had poor moldability.
【０００５】本発明は、かかる従来不織布の問題点に鑑
み、ソフトな表面タッチを有するにも拘らず腰がある上
に、成形性にも優れた、３拍子揃った不織布、さらに取
り扱い性がよくて、汚れ拭き取り性に優れたワイピング
クロスおよびタッチ性および成型性に優れた表皮材を提
供せんとするものである。In view of the problems of the conventional nonwoven fabric, the present invention provides a three-time uniform nonwoven fabric which is not only soft but has a stiffness in spite of having a soft touch, and is excellent in formability. Accordingly, it is an object of the present invention to provide a wiping cloth excellent in dirt wiping property and a skin material excellent in touch property and moldability.
【０００６】[0006]
【課題を解決するための手段】本発明は、かかる課題を
解決するために次のような手段を採用する。すなわち、
本発明の不織布は、海島型複合繊維で構成された不織布
であり、該海島型複合繊維の少なくとも一部がフィブリ
ル化されていることを特徴とするものであり、本発明の
ワイピングクロスおよび表皮材は、かかる不織布で構成
されていることを特徴とするものである。The present invention employs the following means to solve the above-mentioned problems. That is,
The nonwoven fabric of the present invention is a nonwoven fabric composed of sea-island composite fibers, wherein at least a part of the sea-island composite fibers is fibrillated, and the wiping cloth and skin material of the present invention are provided. Is characterized by being constituted by such a nonwoven fabric.
【０００７】[0007]
【発明の実施の形態】本発明は、上述課題、すなわち、
タッチ特性と腰、さらに成形性まで満足する３拍子揃っ
た不織布について、鋭意検討したところ、海島型複合繊
維を特定な形態に処理して構成した不織布とすることに
より、かかる課題を一挙に解決することを究明したもの
である。DETAILED DESCRIPTION OF THE INVENTION The present invention has been made to solve the above-mentioned problems, namely,
After a thorough study of non-woven fabrics with three beats that satisfy the touch characteristics, waist, and even moldability, these problems can be solved at once by processing the sea-island type conjugate fiber into a specific non-woven fabric. That is what we have determined.
【０００８】本発明の不織布は、海島型複合繊維で構成
されたもので、かつ、その海島型複合繊維の少なくとも
一部、好ましくは１０〜８０％、さらに好ましくは５０
〜７５％がフィブリル化されているものである。すなわ
ち、非フィブリル化部分は、海島型複合繊維のままで存
在することを意味するものである。この非フィブリル化
部分が、腰および成形性に関与するものである。勿論、
フィブリル化されて形成された極細繊維が、汚れ拭き取
り性を有するものである。[0008] The nonwoven fabric of the present invention is composed of sea-island composite fibers, and at least a part of the sea-island composite fibers, preferably 10 to 80%, more preferably 50 to 50%.
~ 75% is fibrillated. That is, the non-fibrillated portion means that it exists as a sea-island composite fiber. This non-fibrillated portion is responsible for the stiffness and moldability. Of course,
The ultrafine fibers formed by fibrillation have the property of wiping off dirt.
【０００９】かかるフィブリル化されて形成された極細
繊維は、該海島型複合繊維の島成分で構成されるもので
あり、ワイピング性能および繊維強度の上から、好まし
くは０．０００１〜０．５ｄ、さらに好ましくは０．０
１〜０．２ｄの単糸繊度を有するものである。The ultrafine fibers formed by fibrillation are composed of island components of the sea-island composite fibers, and preferably have a wiping performance and a fiber strength of 0.0001 to 0.5 d, More preferably 0.0
It has a single yarn fineness of 1 to 0.2 d.
【００１０】本発明の不織布は、かかるフィブリル化部
分を有するところに特徴を有するが、かかるフィブリル
化は、該不織布形成時の機械的刺激、つまり、主として
ニードルパンチングやウォータージェットパンチングな
どのパンチング処理によって、該不織布全体に形成され
る。つまり、該不織布の内部に存在するフィブリル化
は、パンチング処理により惹起され、勿論内部に存在す
る極細繊維は、このパンチング処理により形成されるも
のである。The nonwoven fabric of the present invention is characterized by having such a fibrillated portion. The fibrillation is performed by mechanical stimulation during the formation of the nonwoven fabric, that is, mainly by punching treatment such as needle punching or water jet punching. , Formed on the entire nonwoven fabric. That is, the fibrillation existing inside the nonwoven fabric is caused by the punching process, and, of course, the ultrafine fibers existing inside the nonwoven fabric are formed by the punching process.
【００１１】また、該不織布の表面に存在するフィブリ
ル化されて形成される極細繊維も、かかるパンチング処
理によって形成されるものもあるが、仕上げ工程で掛け
られるバフィング処理により形成されるものが含まれ
る。すなわち、本発明の不織布は、パンチング処理した
だけのものでも、十分に本発明の効果を有するものであ
るが、さらに品質を改善するために該不織布表面をバフ
ィングなどの起毛処理を施すことにより、ゴミのように
付着した破壊ポリマを除去するとともに、表面部の非フ
ィブリル化部分、つまり海島型複合繊維部分のフィブリ
ル化を促進させることができ、その結果、不織布内部よ
り表面にフィブリル化されて形成された極細繊維が、リ
ッチに存在させることができ、さらにソフトなタッチ特
性を付与することができたものである。勿論、それによ
って、汚れ拭き取り性も大幅に改善されるものである。[0011] Further, the ultrafine fibers formed on the surface of the nonwoven fabric by fibrillation may be formed by such a punching process, but include those formed by a buffing process applied in a finishing step. . That is, the nonwoven fabric of the present invention, even if only subjected to a punching treatment, has a sufficient effect of the present invention, but by further raising the nonwoven fabric surface such as buffing to further improve the quality, It is possible to remove the broken polymer attached like garbage and to promote the fibrillation of the non-fibrillated part of the surface, that is, the sea-island type composite fiber part. As a result, the fibril is formed on the surface from the inside of the nonwoven fabric. The obtained ultrafine fibers can be made to exist in a rich manner, and can impart soft touch characteristics. Of course, thereby, the dirt wiping property is also greatly improved.
【００１２】本発明の海島型複合繊維は、極細繊維を製
造するときに通常採用される構造のものを使用すること
ができ、好ましくは１〜５ｄ、さらに好ましくは２〜４
ｄの単糸繊度を有するものである。かかる海島型複合繊
維の海成分は、ポリエステルあるいはポリスチレンが使
用され、島成分は、ポリエステルあるいはポリアミドが
使用される。本発明の海島型複合繊維における特徴は、
パンチング処理によって、フィブリル化され易い海成分
で構成されているところにある。すなわち、該海成分の
ポリマに、１０％重量以下の易破壊性物質を含有させた
ところに特徴を有する。かかる易破壊性物質としては、
ポリエチレングリコールおよびポリビニルアルコールか
ら選ばれた少なくとも１種を使用することができる。か
かる易破壊性物質を含有（混合）する海成分は、パンチ
ングのみならず、後工程でのバフィング処理によっても
十分フィブリル化を達成させる性質を有するものであ
る。勿論、本発明の不織布は、かかるパンチング処理に
よって、フィブリル化のみを達成するものではなく、当
然、絡合一体化させる機能を備えたものであり、これに
よって、本発明の不織布という一体化されたシートを提
供することができるものである。なお、かかる海成分に
親油性成分を配合すると、油吸着機能を付与することも
できる。As the sea-island type conjugate fiber of the present invention, those having a structure usually employed when producing ultrafine fibers can be used, preferably 1 to 5d, more preferably 2 to 4d.
It has a single yarn fineness of d. As the sea component of such a sea-island composite fiber, polyester or polystyrene is used, and as the island component, polyester or polyamide is used. The features of the sea-island composite fiber of the present invention are as follows:
It is located in a sea component that is easily fibrillated by punching. That is, the present invention is characterized in that the polymer of the sea component contains 10% by weight or less of an easily breakable substance. Such easily destructible substances include:
At least one selected from polyethylene glycol and polyvinyl alcohol can be used. The sea component containing (mixing) such an easily breakable substance has a property of sufficiently achieving fibrillation not only by punching but also by buffing treatment in a subsequent step. Of course, the nonwoven fabric of the present invention does not achieve only fibrillation by such a punching treatment, but naturally has a function of entanglement and integration, whereby the nonwoven fabric of the present invention is integrated. A sheet can be provided. In addition, when a lipophilic component is blended with such a sea component, an oil adsorption function can be imparted.
【００１３】かかる海島型複合繊維は、好ましくは島／
海＝９０／１０〜３０／７０、さらに好ましくは７０／
３０〜５０／５０の重量比率で複合されているものであ
る。かかる海島型複合繊維の島成分は、好ましくは１０
〜４０島、さらに好ましくは１３〜２０島の島数のもの
で構成されているものである。The sea-island type composite fiber is preferably an island /
Sea = 90 / 10-30 / 70, more preferably 70 /
It is compounded at a weight ratio of 30 to 50/50. The island component of such a sea-island composite fiber is preferably 10
It is composed of 40 to 40 islands, more preferably 13 to 20 islands.
【００１４】以下、本発明を図面により説明する。Hereinafter, the present invention will be described with reference to the drawings.
【００１５】図１は、本発明の不織布の一例を示す模式
図である。この図は、海島型複合繊維１を絡合させた不
織布であり、該海島型複合繊維１がフィブリル化され
て、海成分２の一部が欠落し、島成分が極細繊維として
残存したものである。FIG. 1 is a schematic view showing an example of the nonwoven fabric of the present invention. This figure shows a non-woven fabric in which sea-island composite fibers 1 are entangled. The sea-island composite fibers 1 are fibrillated, a part of the sea component 2 is missing, and the island component remains as a fine fiber. is there.
【００１６】本発明のワイピングクロスおよび表皮材
は、かかる不織布で構成されたものであり、たとえば、
ワイピングクロスとして優れた汚れ拭き取り性を有する
が、さらに好ましくは５００ｇ／ｍ2 以上の高目付のも
のであると、優れた腰を有するものを提供することがで
き、取り扱い性を向上させることができ、さらにまた、
該不織布にメッシュシートを積層させたものを用いるこ
とにより、形態安定性のよいワイピングクロスを提供す
ることもできる。The wiping cloth and the skin material of the present invention are made of such a nonwoven fabric.
It has excellent dirt wiping properties as a wiping cloth, but it is more preferable that the wiping cloth has a high basis weight of 500 g / m 2 or more. And also
By using the nonwoven fabric laminated with a mesh sheet, it is possible to provide a wiping cloth having good form stability.
【００１７】また、本発明の表皮材は、海成分のポリエ
ステルあるいはポリスチレンを利用するものであり、た
とえばワイピングクロスに比して比較的海成分が多く配
合された構造の海島型複合繊維を使用するのが、成形性
にすぐれたものを提供する上から好ましい。かかる不織
布は、さらに別の樹脂と複合させたり、さらに該不織布
にメッシュシートを積層させたものを用いることによ
り、形態安定性のよい表皮材とすることもできる。The skin material of the present invention utilizes polyester or polystyrene as a sea component. For example, a sea-island composite fiber having a structure in which a relatively large amount of a sea component is blended as compared with a wiping cloth is used. It is preferable from the viewpoint of providing a material having excellent moldability. Such a non-woven fabric can be made into a skin material with good form stability by further compounding it with another resin or using a non-woven fabric laminated with a mesh sheet.
【００１８】[0018]
【実施例】次に、実施例および比較例を挙げて、本発明
をさらに詳細に説明する。Next, the present invention will be described in more detail with reference to Examples and Comparative Examples.
【００１９】実施例１ 島成分としてポリエチレンテレフタレート、海成分とし
てポリエチレングリコールを５％混合したポリスチレン
からなる成分比５７／４３、島数１６、複合繊度３．８
ｄ、島繊度０．１４ｄ、繊維長５１mmの海島型複合繊維
の原綿を用い、２５００本／cm2 のニードルパンチによ
り目付５００ｇ／ｍ2 の短繊維不織布を作製した。不織
布を構成する繊維２０本を無作為に抽出し、フィブリル
化している部分の長さとフィブリル化していない部分の
長さを測定したところ、フィブリル化している部分の長
さは全繊維長に対し約５０％であった。EXAMPLE 1 Polyethylene terephthalate as an island component and polystyrene mixed with 5% polyethylene glycol as a sea component had a component ratio of 57/43, a number of islands of 16, and a composite fineness of 3.8.
d, a short fiber nonwoven fabric having a basis weight of 500 g / m 2 was prepared by using a raw cotton of sea-island type composite fiber having an island fineness of 0.14 d and a fiber length of 51 mm by needle punching at 2500 fibers / cm 2 . Twenty fibers constituting the nonwoven fabric were randomly extracted, and the length of the fibrillated portion and the length of the non-fibrillated portion were measured. The length of the fibrillated portion was about 10% of the total fiber length. It was 50%.
【００２０】比較例１ 実施例１においてポリエチレングリコールを混合せずに
同様の不織布を作製した。フィブリル化している部分の
長さは全繊維長に対し５％以下であった。Comparative Example 1 A similar nonwoven fabric was prepared in Example 1 without mixing polyethylene glycol. The length of the fibrillated portion was 5% or less of the total fiber length.
【００２１】比較例２ 実施例１の海成分を抽出し、島繊維のみからなるワイピ
ングクロスを作製した。目付は約３００ｇ／ｍ2 であっ
た。Comparative Example 2 The marine component of Example 1 was extracted to produce a wiping cloth consisting of island fibers only. The basis weight was about 300 g / m 2 .
【００２２】比較例３ 眼鏡レンズ拭き等の用途に用いられる極細繊維で構成さ
れた織物を供試した。目付は約１００ｇ／ｍ2 であっ
た。Comparative Example 3 A woven fabric composed of ultrafine fibers used for applications such as wiping eyeglass lenses was tested. The basis weight was about 100 g / m 2 .
【００２３】これら４種類のワイピングクロスについ
て、一般人７名に、それぞれ１ヶ月づつ風呂桶掃除と皿
洗い用途に使用してもらい、ワイピング性能および取り
扱い性について評価してもらった。その結果、全員から
実施例１のワイピングクロスのワイピング性能が最も高
く、取り扱い性も問題ないという評価を得た。With respect to these four types of wiping cloths, seven ordinary people were used for bathtub cleaning and dish washing for one month each, and wiping performance and handleability were evaluated. As a result, all the members evaluated that the wiping cloth of Example 1 had the highest wiping performance and had no problem in handling.
【００２４】実施例２ 実施例１と同じ海島型複合繊維の原綿を用い、その不織
布原綿の片面に次のスクリム（メッシュシート）をのせ
て、２５００本／cm2 のニードルパンチによりパンチン
グ処理して、目付５７４ｇ／ｍ2 の不織布をつくった。
得られた不織布の表皮面（スクリム面の反対面）をバフ
ィング処理して、破壊ポリマを排除しながら起毛すると
ともに整毛した。Example 2 The same sea-island type composite fiber as in Example 1 was used, and the following scrim (mesh sheet) was placed on one side of the non-woven fiber, followed by punching with a needle punch of 2500 fibers / cm 2. And a non-woven fabric having a basis weight of 574 g / m 2 .
The skin surface (the surface opposite to the scrim surface) of the obtained nonwoven fabric was subjected to buffing treatment to raise the hair while removing the destruction polymer and to adjust the hair.
【００２５】該スクリムは、総繊度７５Ｄ−７２フィラ
メント、単糸繊度１．０４ｄのポリエステルマルチフィ
ラメントからなる２５００Ｔ／ｍ強撚糸を織糸として、
タテ９８本／inch、ヨコ７６本／inchの織密度で製織さ
れた生織目付７４ｇ／ｍ2 の平織物を用いた。The scrim is a woven yarn of 2500 T / m strong twist yarn composed of polyester multifilament having a total fineness of 75D-72 filaments and a single yarn fineness of 1.04 d.
A plain woven fabric having a raw weave of 74 g / m 2 woven at a weave density of 98 lines / inch and 76 lines / inch in width was used.
【００２６】得られた不織布を表皮材として、該スクリ
ム面側を貼着面とし、その反対面を表皮として用い、椅
子に貼り付けた。Using the obtained nonwoven fabric as a skin material, the scrim surface side was used as a sticking surface, and the opposite surface was used as a skin, and the nonwoven fabric was stuck to a chair.
【００２７】この椅子に貼着された表皮材は、タテ、ヨ
コに寸法安定性に優れ、かつ、極細立毛によるソフトタ
ッチと美観を耐久性よく保持するものであった。The skin material adhered to this chair was excellent in dimensional stability to warp and weft, and had a durable soft touch and aesthetic appearance with extra fine nap.
【００２８】[0028]
【発明の効果】本発明によれば、ソフトタッチ性と優れ
た汚れ拭き取り性と腰を有する上に、さらに成形性に優
れた不織布を提供することができるので、ワイピングク
ロスおよび表皮材として有効な素材を提供することがで
きる。According to the present invention, it is possible to provide a nonwoven fabric which has not only soft touch properties, excellent dirt wiping properties and stiffness, but also excellent moldability, so that it is effective as a wiping cloth and a skin material. Material can be provided.
【図１】 この図は、本発明の不織布およびワイピング
クロスの一例を示す断面図である。FIG. 1 is a cross-sectional view showing an example of a nonwoven fabric and a wiping cloth of the present invention.
１：海島型複合繊維 ２：海成分 ３：フィブリル化されて形成された島成分で構成された
極細繊維1: sea-island composite fiber 2: sea component 3: ultrafine fiber composed of island component formed by fibrillation
Claims (18)
り、該海島型複合繊維の少なくとも一部がフィブリル化
されていることを特徴とする不織布。1. A nonwoven fabric comprising sea-island composite fibers, wherein at least a part of the sea-island composite fibers is fibrillated.
該海島型複合繊維の１０〜８０％である請求項１記載の
不織布。2. The fibrillation rate of the sea-island type composite fiber is as follows:
The nonwoven fabric according to claim 1, wherein the nonwoven fabric is 10 to 80% of the sea-island type conjugate fiber.
度を有するものである請求項１または２記載の不織布。3. The nonwoven fabric according to claim 1, wherein the sea-island composite fiber has a single yarn fineness of 1 to 5 d.
維が、該海島型複合繊維の島成分である請求項１〜３の
いずれかに記載の不織布。4. The nonwoven fabric according to claim 1, wherein the ultrafine fibers formed by fibrillation are island components of the sea-island composite fibers.
の単糸繊度を有するものである請求項４記載の不織布。5. The method according to claim 1, wherein the ultrafine fibers are from 0.0001 to 0.5 d.
The nonwoven fabric according to claim 4, wherein the nonwoven fabric has a single yarn fineness of:
されて形成された極細繊維が、パインチング処理により
形成されたものである請求項１〜５のいずれかに記載の
不織布。6. The nonwoven fabric according to claim 1, wherein the fibrillated ultrafine fibers present inside the nonwoven fabric are formed by pinching.
されて形成された極細繊維が、バフィング処理により形
成されたものである請求項１〜６のいずれかに記載の不
織布。7. The nonwoven fabric according to claim 1, wherein the fibrillated ultrafine fibers present on the surface of the nonwoven fabric are formed by buffing treatment.
れた極細繊維の比率が内部よりも表面にリッチに存在す
るものである請求項１〜７のいずれかに記載のワイピン
グクロス。8. The wiping cloth according to any one of claims 1 to 7, wherein the nonwoven fabric has a ratio of ultrafine fibers formed by fibrillation, which is richer on the surface than on the inside.
テルあるいはポリスチレンである請求項１〜８のいずれ
かに記載の不織布。9. The nonwoven fabric according to claim 1, wherein the sea component of the sea-island composite fiber is polyester or polystyrene.
性物質を含有するものである請求項９記載の不織布。10. The nonwoven fabric according to claim 9, wherein said sea component contains 10% by weight or less of a frangible substance.
コールおよびポリビニルアルコールから選ばれた少なく
とも１種である請求項１０記載の不織布。11. The nonwoven fabric according to claim 10, wherein the easily breakable substance is at least one selected from polyethylene glycol and polyvinyl alcohol.
ステルあるいはポリアミドである請求項１〜１１のいず
れかに記載の不織布。12. The nonwoven fabric according to claim 1, wherein the island component of the sea-island composite fiber is a polyester or a polyamide.
１０〜３０／７０の重量比率で複合されているものであ
る請求項１〜１２のいずれかに記載の不織布。13. The islands-in-sea composite fiber having an island / sea = 90 /
The nonwoven fabric according to any one of claims 1 to 12, wherein the nonwoven fabric is composited in a weight ratio of 10 to 30/70.
３０〜５０／５０の重量比率で複合されているものであ
る請求項１〜１２のいずれかに記載の不織布。14. The sea-island type composite fiber has an island / sea = 70 /
The nonwoven fabric according to any one of claims 1 to 12, wherein the nonwoven fabric is composited at a weight ratio of 30 to 50/50.
島成分で構成されているものである請求項１〜１４のい
ずれかに記載の不織布。15. The nonwoven fabric according to claim 1, wherein the sea-island composite fiber is composed of 10 to 40 island components.
ュシートが積層されたものである請求項１〜１５のいず
れかに記載の不織布。16. The nonwoven fabric according to claim 1, wherein the nonwoven fabric has a mesh sheet laminated on at least one surface.
織布で構成されていることを特徴とするワイピングクロ
ス。17. A wiping cloth comprising the nonwoven fabric according to claim 1. Description:
織布で構成されていることを特徴とする表皮材。18. A skin material comprising the nonwoven fabric according to claim 1. Description: