JPH1017674A - Colored resin composition and molding made therefrom - Google Patents
Colored resin composition and molding made therefromInfo
- Publication number
- JPH1017674A JPH1017674A JP17758496A JP17758496A JPH1017674A JP H1017674 A JPH1017674 A JP H1017674A JP 17758496 A JP17758496 A JP 17758496A JP 17758496 A JP17758496 A JP 17758496A JP H1017674 A JPH1017674 A JP H1017674A
- Authority
- JP
- Japan
- Prior art keywords
- pigment
- resin composition
- colored resin
- metal
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、熱可塑性樹脂を用
いた成形品に特殊な意匠性を付与する着色樹脂組成物及
びこれを含有してなる成形品に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a colored resin composition for imparting a special design property to a molded article using a thermoplastic resin, and a molded article containing the same.
【０００２】[0002]
【従来の技術】熱可塑性樹脂を用いた成形品に特殊な意
匠効果としてメタリック感（光沢感）と高彩度の色相と
を付与するために、金属粉末、金属箔膜等や、マイカ粉
に二酸化チタンを表面被覆したいわゆるパール顔料等が
用いられている。熱可塑性樹脂に金属粉末、金属箔膜等
を用いると成形物に容易にメタリック感（光沢感）を付
与できるが、同時に高彩度の色相を得ようとすると、メ
タリック感（光沢感）が顔料の隠蔽力等の作用により失
われてしまう。また、パール顔料を使用すると併用する
顔料によっては高彩度の色相を得られる場合もあるが、
この場合成形物を見る角度により色相が異なって見えた
り、メタリック感（光沢感）が無くなるという現象がお
こる。また、これらの金属粉末、金属箔膜やパール顔料
を使用した成形品は押出成形などの成形加工において、
ダイス口に目ヤニを発生し易く成形品の外観を著しく損
なうという現象も起こしやすい。2. Description of the Related Art In order to give a metallic product (glossiness) and a high color hue as a special design effect to a molded product using a thermoplastic resin, titanium dioxide is added to a metal powder, a metal foil film or the like, or mica powder. A so-called pearl pigment or the like whose surface is coated with is used. When a metal powder or a metal foil film is used for the thermoplastic resin, a metallic feeling (glossiness) can be easily imparted to the molded product. It is lost by the action of force. In addition, when using pearl pigments, depending on the pigment used in combination, a high saturation hue may be obtained,
In this case, a phenomenon occurs in which the hue differs depending on the angle at which the molded product is viewed, and a metallic feeling (glossiness) disappears. In addition, molded products using these metal powders, metal foil films and pearl pigments, in molding processes such as extrusion molding,
The phenomenon that the die opening easily occurs at the die opening and the appearance of the molded product is significantly impaired is also likely to occur.
【０００３】[0003]
【発明が解決しようとする課題】本発明は、見る角度に
よって変化しないメタリック感（光沢感）と高彩度の色
相とを有する、熱可塑性樹脂を用いてなる成形物を得る
ことを目的とする。また、本発明の別の目的は、成形加
工時に目ヤニを発生することなく、特殊な意匠性を有す
る成形品を得ることである。SUMMARY OF THE INVENTION An object of the present invention is to obtain a molded article made of a thermoplastic resin having a metallic feeling (glossiness) which does not change depending on a viewing angle and a high chroma hue. Another object of the present invention is to obtain a molded product having a special design without generating eye burrs during molding.
【０００４】[0004]
【課題を解決するための手段】本発明者は、検討の結
果、熱可塑性樹脂と、スパッタリング法で金属表面に顔
料を被覆したスパッタリング顔料とを含有してなる着色
樹脂組成物を用ることによって、成形品に光沢感と高彩
度の色相を同時に付与させる事が可能である事を見出し
た。さらに、係るスパッタリング顔料を含有した着色樹
脂組成物に、フッ化ビニリデン・ヘキサフルオロプロピ
レン共重合体を、あるいは、フッ化ビニリデン・ヘキサ
フルオロプロピレン共重合体とポリアルキレンオキサイ
ドとを含有する事によって、本発明の着色樹脂組成物を
成形加工する際に、成形加工中にダイス口に目ヤニを容
易に発生しない事を見出し、本発明に至ったもので、本
発明は、前記の従来の様々な欠点を改良し、光沢感と高
彩度の色相を同時に付与させる着色樹脂組成物を提供
し、さらに、係る着色樹脂組成物を使用した時、外観を
損なわない成形品を提供するものである。As a result of the study, the present inventor has found that a colored resin composition comprising a thermoplastic resin and a sputtered pigment having a metal surface coated with a pigment by a sputtering method is used. It has been found that it is possible to simultaneously impart glossiness and high saturation hue to a molded product. Further, by adding a vinylidene fluoride-hexafluoropropylene copolymer, or a vinylidene fluoride-hexafluoropropylene copolymer and a polyalkylene oxide to the colored resin composition containing the sputtering pigment, When molding the colored resin composition of the present invention, it has been found that eye mold is not easily generated in a die opening during the molding process, and the present invention has been achieved. To provide a colored resin composition that simultaneously imparts a glossiness and a high chroma hue, and further provides a molded article that does not impair the appearance when the colored resin composition is used.
【０００５】即ち、第１の発明は、熱可塑性樹脂と、ス
パッタリング法で金属表面を顔料で被覆したスパッタリ
ング顔料とを含有することを特徴とする着色樹脂組成物
である。[0005] That is, a first invention is a colored resin composition comprising a thermoplastic resin and a sputtered pigment having a metal surface coated with a pigment by a sputtering method.
【０００６】第２の発明は、金属が鱗片状またはフレー
ク状であることを特徴とする第１の発明記載の着色樹脂
組成物である。A second invention is the colored resin composition according to the first invention, wherein the metal is in the form of scale or flakes.
【０００７】第３の発明は、金属がアルミニウムである
ことを特徴とする第１の発明または第２の発明記載の着
色樹脂組成物である。A third invention is the colored resin composition according to the first invention or the second invention, wherein the metal is aluminum.
【０００８】第４の発明は、熱可塑性樹脂が、ポリオレ
フィン系樹脂、ポリスチレン系樹脂、ポリカーボネート
系樹脂、ポリブチレテレフタレート系樹脂、ポリエチレ
テレフタレート系樹脂からなる群より選ばれる１種以上
の樹脂であることを特徴とする第１の発明ないし第３の
発明いずれか記載の着色樹脂組成物である。In a fourth aspect, the thermoplastic resin is at least one resin selected from the group consisting of polyolefin resins, polystyrene resins, polycarbonate resins, polybutylene terephthalate resins, and polyethylene terephthalate resins. A colored resin composition according to any one of the first to third inventions.
【０００９】第５の発明は、顔料を含有することを特徴
とする第１の発明ないし第４の発明いずれか記載の着色
樹脂組成物である。A fifth invention is the colored resin composition according to any one of the first to fourth inventions, which comprises a pigment.
【００１０】第６の発明は、フッ化ビニリデン・ヘキサ
フルオロプロピレン共重合体を含有することを特徴とす
る第１の発明ないし第５の発明いずれか記載の着色樹脂
組成物である。A sixth invention is the colored resin composition according to any one of the first to fifth inventions, comprising a vinylidene fluoride-hexafluoropropylene copolymer.
【００１１】第７の発明は、ポリアルキレンオキサイド
を含有することを特徴とする第６の発明記載の着色樹脂
組成物である。A seventh invention is the colored resin composition according to the sixth invention, which comprises a polyalkylene oxide.
【００１２】第８の発明は、第１の発明ないし第７の発
明いずれか記載の着色樹脂組成物を含有してなる成形品
である。An eighth invention is a molded article containing the colored resin composition according to any one of the first invention to the seventh invention.
【００１３】[0013]
【発明の実施の形態】本発明において用いられる熱可塑
性樹脂としては、ポリオレフィン系樹脂、ポリスチレン
系樹脂、ポリカーボネート系樹脂、ポリブチレンテレフ
タレート系樹脂、ポリエチレンテレフタレート系樹脂等
が挙げられ、自動車バンパー用としては、ポリエチレ
ン、ポリプロピレン、ポリブテン等のポリオレフィン系
樹脂が好ましく、特にポリプロピレンが好ましい。DESCRIPTION OF THE PREFERRED EMBODIMENTS The thermoplastic resins used in the present invention include polyolefin resins, polystyrene resins, polycarbonate resins, polybutylene terephthalate resins, polyethylene terephthalate resins, and the like. Polyolefin resins such as polyethylene, polypropylene, and polybutene are preferred, and polypropylene is particularly preferred.
【００１４】本発明において用いられる金属は、鱗片
状、フレーク状、粉状、粒状、顆粒状不定型、いずれで
あっても良いが、成形品にメタリック感（光沢感）を与
えるためには鱗片状、フレーク状であることが好まし
い。ここで用いられる金属の大きさとしては、１μｍ〜
１０００μｍの範囲が好ましく、特に２０μｍ〜２００
μｍの範囲であることが好ましい。金属が１μｍ未満だ
とメタリック感（光沢感）があまり付与できない。一
方、金属が１０００μｍよりも大きくなると、成形品表
面から金属が突出し易く、成形品の外観を損ないやす
い。また、本発明において用いられる金属としては、
金、銀、銅、錫、ニッケル、鉄、アルミニウム等いずれ
であっても良いが、価格、汎用性、錆の発生等の観点か
らアルミニウムが好ましい。The metal used in the present invention may be any of flakes, flakes, powders, granules, and irregular shaped granules. And flakes. The size of the metal used here is 1 μm to
The range of 1000 μm is preferable, and particularly 20 μm to 200 μm.
It is preferably in the range of μm. If the metal is less than 1 μm, a metallic feeling (glossiness) cannot be provided much. On the other hand, when the metal is larger than 1000 μm, the metal tends to protrude from the surface of the molded product, and the appearance of the molded product is easily damaged. Further, as the metal used in the present invention,
Any of gold, silver, copper, tin, nickel, iron, aluminum and the like may be used, but aluminum is preferred from the viewpoint of price, versatility, rust generation and the like.
【００１５】本発明においてスパッタリング法に用いら
れる顔料としては、モノアゾ、ジスアゾ、縮合アゾ等の
アゾ系顔料、シアニングリーン、シアニンブルー等のフ
タロシアニン系顔料、アンスラキノン、キナクリドン、
ペリレン、ペリノン、キノフタロン、イソインドリノ
ン、ジオキサジン、スレン、等の縮合多環系顔料、ジケ
トピロロピロール系顔料等があげられる。The pigment used in the sputtering method of the present invention includes azo pigments such as monoazo, disazo and condensed azo, phthalocyanine pigments such as cyanine green and cyanine blue, anthraquinone, quinacridone, and the like.
Condensed polycyclic pigments such as perylene, perinone, quinophthalone, isoindolinone, dioxazine, and sulene; and diketopyrrolopyrrole pigments.
【００１６】本発明において用いられるスパッタリング
顔料は、前記した金属表面に前記の顔料をスパッタリン
グ法によって被覆したものであり、金属１００重量部を
２０〜１００部の顔料で被覆することが好ましい。The sputtering pigment used in the present invention is obtained by coating the above-mentioned metal surface with the above-mentioned pigment by a sputtering method, and it is preferable to coat 100 parts by weight of the metal with 20 to 100 parts of the pigment.
【００１７】スパッタリング法は、一般的には不活性ガ
スを満たした低圧あるいは真空容器中でそのガスをイオ
ン化し、そのイオンをターゲットとよばれる固体面に衝
突させて得られるターゲットの分子を、その付近の物体
面に付着させる方法である。The sputtering method generally ionizes a gas in a low-pressure or vacuum vessel filled with an inert gas, and collides the ions with a solid surface called a target to convert molecules of the target. This is a method of attaching to a nearby object surface.
【００１８】本発明の着色樹脂組成物は、熱可塑性樹脂
とスパッタリング顔料を含有するものであるが、成形品
を所望の色相に微調整するために、さらに顔料を含有し
ていてもよい。この時用いられる顔料としては、スパッ
タリング顔料を得る際に使用されたものを挙げることが
できる。また、酸化チタン、チタンイエロー、群青、酸
化鉄、などの無機顔料やカーボンブラックを使用するこ
とができる。Although the colored resin composition of the present invention contains a thermoplastic resin and a sputtering pigment, it may further contain a pigment in order to finely adjust a molded product to a desired hue. Examples of the pigment used at this time include those used when obtaining a sputtering pigment. In addition, inorganic pigments such as titanium oxide, titanium yellow, ultramarine, iron oxide, and the like, and carbon black can be used.
【００１９】本発明の着色樹脂組成物は、そのまま成形
に供されるいわゆる着色ペレットであってもよいし、
（スパッタリング顔料＋顔料）を高濃度に含有するペレ
ット状の着色剤（マスターバッチ）いずれであってもよ
い。前者の場合、着色樹脂組成物をそのまま押し出し成
形、射出成形、吹き込み成形、真空成形等種々の成形加
工をして、成形品を得る。また、後者の場合、着色樹脂
組成物を、さらに熱可塑性樹脂で希釈し上記と同様にし
て成形品を得る。本発明の着色樹脂組成物は、熱可塑性
樹脂／スパッタリング顔料＝９９．９／０．１から５０
／５０の割合で配合することが好ましい。成形品中にス
パッタリング顔料を０．１％程度含有すればメタリック
感（光沢感）が得られる。また、顔料を含有する場合、
スパッタリング顔料は、（スパッタリング顔料＋顔料）
中に３％以上配合されることが好ましい。The colored resin composition of the present invention may be so-called colored pellets directly used for molding,
Any of a pellet-shaped colorant (master batch) containing (sputtering pigment + pigment) at a high concentration may be used. In the former case, the colored resin composition is subjected to various molding processes such as extrusion molding, injection molding, blow molding, and vacuum molding to obtain a molded product. In the latter case, the colored resin composition is further diluted with a thermoplastic resin to obtain a molded article in the same manner as described above. The colored resin composition of the present invention has a thermoplastic resin / sputtering pigment = 99.9 / 0.1 to 50
/ 50 is preferably blended. If the molded article contains about 0.1% of a sputtering pigment, a metallic feeling (glossiness) can be obtained. Also, when containing a pigment,
Sputtering pigment is (sputtering pigment + pigment)
It is preferable that 3% or more be contained therein.
【００２０】本発明の着色樹脂組成物は、前述したよう
に熱可塑性樹脂、スパッタリング顔料、顔料等を含有す
るものであるが、さらにフッ化ビニリデン・ヘキサフル
オロプロピレン共重合体、またはフッ化ビニリデン・ヘ
キサフルオロプロピレン共重合体及びポリアルキレンオ
キサイドを含有することができる。フッ化ビニリデン・
ヘキサフルオロプロピレン共重合体等は、着色樹脂組成
物を成形加工する際に発生しやすい目ヤニを抑制・防止
する機能を有する。目ヤニとは、押出機で成形加工した
着色樹脂組成物が、押出機の先端部であるダイから吐出
される際、ダイ開口部周囲に堆積するものの総称であ
る。発生原因としては押出機内部で熱劣化した着色樹脂
組成物が、劣化していない部位からダイ口で分離し徐々
に炭化していくと考えられ、押し出し成形では成形品の
美観を損ねたり作業効率を低下させる原因となるので、
係る成形加工に供する着色樹脂組成物の場合は特にフッ
化ビニリデン・ヘキサフルオロプロピレン共重合体等を
配合することが好ましい。The colored resin composition of the present invention contains a thermoplastic resin, a sputtering pigment, a pigment and the like as described above, and further contains a vinylidene fluoride-hexafluoropropylene copolymer or vinylidene fluoride. It may contain a hexafluoropropylene copolymer and a polyalkylene oxide. Vinylidene fluoride
Hexafluoropropylene copolymer and the like have a function of suppressing and preventing eye repelling which is likely to occur when molding the colored resin composition. The term “resin” is a general term for a colored resin composition formed and processed by an extruder, which is deposited around a die opening when the colored resin composition is discharged from a die which is a tip of the extruder. It is considered that the cause of the occurrence is that the colored resin composition thermally degraded inside the extruder separates from the undegraded part at the die mouth and gradually carbonizes. May cause a decrease in
In the case of a colored resin composition to be subjected to such a molding process, it is particularly preferable to incorporate a vinylidene fluoride-hexafluoropropylene copolymer or the like.
【００２１】フッ化ビニリデン・ヘキサフルオロプロピ
レン共重合体と共に用いられるポリアルキレンオキサイ
ドとしては、ポリエチレンオキサイド、ポリプロピレン
オキサイド、塩素化ポリエーテル（別称ペントン）等が
挙げられ、ポリエチレンオキサイドが好ましい。Examples of the polyalkylene oxide used together with the vinylidene fluoride-hexafluoropropylene copolymer include polyethylene oxide, polypropylene oxide, chlorinated polyether (also known as pentone), and polyethylene oxide is preferred.
【００２２】フッ化ビニリデン・ヘキサフルオロプロピ
レン共重合体、またはフッ化ビニリデン・ヘキサフルオ
ロプロピレン共重合体及びポリアルキレンオキサイド
は、熱可塑性樹脂に対して、３０〜１０００ｐｐｍ用い
ることが好ましい。The vinylidene fluoride-hexafluoropropylene copolymer, or the vinylidene fluoride-hexafluoropropylene copolymer and polyalkylene oxide are preferably used in an amount of 30 to 1000 ppm based on the thermoplastic resin.
【００２３】本発明の着色樹脂組成物は、熱可塑性樹脂
とスパッタリング顔料とを含有するものであるが、さら
に中・低分子量ポリエチレンワックス、エチレンビスス
テアリルアマイド、ステアリンサン亜鉛、ステアリンサ
ンカルシウム等の金属石鹸類等をスパッタリング顔料な
らびに顔料の分散剤として、酸化防止剤、紫外線吸収剤
等を着色樹脂組成物ならびに本発明の着色樹脂組成物か
らなる成形品の劣化を防止するために本発明の効果を損
なわない範囲で適宜配合することができる。The colored resin composition of the present invention contains a thermoplastic resin and a sputtered pigment, and further contains a metal such as a medium or low molecular weight polyethylene wax, ethylene bisstearyl amide, zinc stearate zinc, calcium stearate and the like. Soaps and the like as a sputtering pigment and a pigment dispersant, an antioxidant, an ultraviolet absorber and the like to prevent the deterioration of the colored resin composition and the molded article made of the colored resin composition of the present invention. It can be appropriately compounded within a range that does not impair.
【００２４】[0024]
【実施例】本発明を実施例によりさらに詳細に説明す
る。 実施例１〜６ 表１に示す配合の着色樹脂組成物を単軸溶融混練機で造
粒し、係る着色樹脂組成物を用いて押し出し成形機で１
２０×２ｍｍ（幅×厚さ）のシート成形品を成形した。
成形加工時の目ヤニの発生の有無、及びシート成形品を
目視で観察し光沢感と色相の方向性について評価し、そ
の結果を表３に示した。 造粒条件：シリンダ温度＝２２０℃ スクリュ径３０ｍｍ Ｌ／Ｄ＝３４ スクリュ回転数 １００ｒ．ｐ．ｍ． シート成形条件：シリンダ温度＝２２０℃ スクリュ径３０ｍｍ Ｌ／Ｄ＝３４ スクリュ回転数 １００ｒ．ｐ．ｍ．EXAMPLES The present invention will be described in more detail with reference to Examples. Examples 1 to 6 A colored resin composition having the composition shown in Table 1 was granulated by a uniaxial melt kneader, and the colored resin composition was extruded by an extruder using the colored resin composition.
A sheet molded product of 20 × 2 mm (width × thickness) was formed.
Table 3 shows the results of evaluation of glossiness and hue directionality by visually observing the occurrence of die build-up during the molding process, and visually observing the sheet molded product. Granulation conditions: Cylinder temperature = 220 ° C. Screw diameter 30 mm L / D = 34 Screw rotation speed 100r. p. m. Sheet forming conditions: cylinder temperature = 220 ° C., screw diameter 30 mm L / D = 34, screw rotation speed 100 r. p. m.
【００２５】比較例１〜４ 表２に示す配合の着色樹脂組成物を実施例１と同様に単
軸溶融混練機で造粒し、係る着色樹脂組成物を用いて実
施例１と同様に押し出し成形機で１２０×２ｍｍ（幅×
厚さ）のシート成形品を成形し、成形加工時の目ヤニの
発生の有無、及びシート成形品を目視で観察し光沢感と
色相の方向性について評価し、その結果を表３に示し
た。Comparative Examples 1 to 4 A colored resin composition having the composition shown in Table 2 was granulated by a uniaxial melt kneader in the same manner as in Example 1, and extruded in the same manner as in Example 1 using the colored resin composition. 120 × 2 mm (width ×
(Thickness) was molded, and the presence or absence of die build-up at the time of molding was visually observed. The sheet molded product was evaluated for glossiness and hue directionality. The results are shown in Table 3. .
【００２６】[0026]
【表１】 [Table 1]
【００２７】[0027]
【表２】 [Table 2]
【００２８】[0028]
【表３】 [Table 3]
【００２９】[0029]
【発明の効果】本発明によって、見る角度によって変化
しないメタリック感（光沢感）と高彩度の色相とを有す
る、熱可塑性樹脂を用いてなる成形物を得ることができ
るようになった。また、本発明によって、成形加工時に
目ヤニを発生することなく、特殊な意匠性を有する成形
品を得ることができるようになった。According to the present invention, it is possible to obtain a molded article made of a thermoplastic resin having a metallic feeling (glossy feeling) which does not change with the viewing angle and a hue of high chroma. Further, according to the present invention, it is possible to obtain a molded product having a special design property without generating eye burrs during molding.
Claims (8)
属表面を顔料で被覆したスパッタリング顔料とを含有す
ることを特徴とする着色樹脂組成物。1. A colored resin composition comprising a thermoplastic resin and a sputtered pigment having a metal surface coated with a pigment by a sputtering method.
とを特徴とする請求項１記載の着色樹脂組成物。2. The colored resin composition according to claim 1, wherein the metal is in the form of scales or flakes.
する請求項１または２記載の着色樹脂組成物。3. The colored resin composition according to claim 1, wherein the metal is aluminum.
脂、ポリスチレン系樹脂、ポリカーボネート系樹脂、ポ
リブチレテレフタレート系樹脂、ポリエチレテレフタレ
ート系樹脂からなる群より選ばれる１種以上の樹脂であ
ることを特徴とする請求項１ないし３いずれか記載の着
色樹脂組成物。4. The method according to claim 1, wherein the thermoplastic resin is at least one resin selected from the group consisting of a polyolefin resin, a polystyrene resin, a polycarbonate resin, a polybutylene terephthalate resin, and a polyethylene terephthalate resin. The colored resin composition according to any one of claims 1 to 3, wherein
１ないし４いずれか記載の着色樹脂組成物。5. The colored resin composition according to claim 1, further comprising a pigment.
ピレン共重合体を含有することを特徴とする請求項１な
いし５いずれか記載の着色樹脂組成物。6. The colored resin composition according to claim 1, further comprising a vinylidene fluoride-hexafluoropropylene copolymer.
とを特徴とする請求項６記載の着色樹脂組成物。7. The colored resin composition according to claim 6, comprising a polyalkylene oxide.
脂組成物を含有してなる成形品。8. A molded article comprising the colored resin composition according to claim 1.