JPH10129740A - Light-shading paper cup - Google Patents
Light-shading paper cupInfo
- Publication number
- JPH10129740A JPH10129740A JP8285348A JP28534896A JPH10129740A JP H10129740 A JPH10129740 A JP H10129740A JP 8285348 A JP8285348 A JP 8285348A JP 28534896 A JP28534896 A JP 28534896A JP H10129740 A JPH10129740 A JP H10129740A
- Authority
- JP
- Japan
- Prior art keywords
- cup
- light
- paper
- layer
- black ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は金属探知機が適用可
能な遮光性を有する紙製遮光カップに関するものであ
り、特に遮光層が著しく改善された紙製遮光カップの提
供に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a paper light-shielding cup having a light-shielding property applicable to a metal detector, and more particularly to a paper light-shielding cup having a significantly improved light-shielding layer.
【０００２】[0002]
【従来の技術】従来より内容物の光劣化防止のための紙
製遮光カップや容器として、厚紙原紙にアルミニウム箔
やアルミニウム層を積層されたものが知られている。特
に紙製遮光カップとして、代表的な例にアイスクリーム
カップがあり、外光や陳列冷凍ケース中の蛍光灯の光な
どによって、例えば内容物であるアイスクリーム中のビ
タミンや乳成分の破壊や変化、あるいは抹茶成分の変色
や味覚変化などを防止する目的で、アルミニウム箔など
による遮光層を施したものが多くある。2. Description of the Related Art Conventionally, as a paper light-shielding cup or container for preventing light deterioration of a content, a cardboard base paper having an aluminum foil or an aluminum layer laminated on a cardboard base paper is known. In particular, a typical example of a paper shading cup is an ice cream cup, which can be destroyed or changed by, for example, external light or the light of a fluorescent lamp in a display freezing case, for example, vitamins and milk components in the ice cream as a content. In many cases, a light-shielding layer made of aluminum foil or the like is applied for the purpose of preventing discoloration or change in taste of the matcha component.
【０００３】しかし、特に液体食品（飲料）やアイスク
リームなどの内容物について、品質管理の一環として金
属系切り粉等の混入を検査するための金属探知機を使用
するケースが多くなり、この場合には、アルミニウム箔
やアルミニウム蒸着物のように金属系からなる遮光層は
金属探知器の使用による検査とその管理を阻害するもの
であった。また、アルミニウム箔やアルミニウム蒸着物
などによる遮光性を施された紙製遮光カップや容器は、
使用後の廃棄物処理として焼却処理する場合が多いが、
焼却炉のロストル（火格子）に溶けたアルミニウムが絡
み動きを悪くし、焼却効率を低下させ、ロストルの損傷
などの問題があり、さらにアルミニウムが焼却によりア
ルミナに変化し、焼却残滓の埋め立て処分時の加湿によ
って、焼却残滓中のアルミナに吸着されていた有毒なア
ンモニアガスが発生するという問題が生じている。[0003] However, there are many cases where a metal detector is used for inspecting the mixing of metal chips as a part of quality control, especially for contents such as liquid foods (drinks) and ice cream. However, a light-shielding layer made of a metal, such as an aluminum foil or an aluminum deposit, hinders inspection and management by using a metal detector. In addition, paper light-shielding cups and containers that are made light-shielding by aluminum foil or aluminum deposits,
It is often incinerated as waste after use,
Aluminum melted in the incinerator's rostral (grate) deteriorates entanglement, reduces incineration efficiency, and has other problems, such as damage to the rostral. In addition, aluminum is converted to alumina by incineration, and when incineration residue is landfilled. Due to the humidification, the toxic ammonia gas adsorbed on the alumina in the incineration residue is generated.
【０００４】そこで、アルミニウム箔やアルミニウム蒸
着物に代えた非金属の遮光層として、図２に示すように
墨インキ層（１０）としたものが考えられ、実施もされ
ていた。この場合のカップブランク（２）として、図２
（ｂ）に示すように厚紙原紙（１２）の表面（カップの
外側にあたる面）が、内容物の絵柄や品質表示などを表
す絵柄印刷層（１６）とその絵柄印刷層（１６）などを
保護するための透明ポリエチレン（以下透明ＰＥと略
す）層（１８）から成り、厚紙原紙（１２）の裏面（カ
ップの内側にあたる面）は、遮光性を付与するためカッ
プブランク（２）全面に墨インキ（１０）層を施され、
この墨インキ層（１０）がカップ内面（食品内容物と触
れる面）に出ると見た目に悪く、非衛生的な感じとなる
のを防止し、商品価値を高める目的で乳白ポリエチレン
（乳白ＰＥと略す）（１５）を押し出しラミネートした
構成のカップブランク（２）となっていた。Therefore, a black ink layer (10) as shown in FIG. 2 has been considered and practiced as a non-metallic light-shielding layer in place of aluminum foil or aluminum vapor deposition. As the cup blank (2) in this case, FIG.
As shown in (b), the surface of the cardboard base paper (12) (the surface corresponding to the outside of the cup) protects the picture print layer (16) representing the picture and quality indication of the contents and the picture print layer (16). The base material (12) is made of a transparent polyethylene (hereinafter abbreviated as transparent PE) layer (18). (10) layered,
When the black ink layer (10) comes out of the inner surface of the cup (the surface that comes into contact with the food contents), it is unattractive and unhygienic, and milky polyethylene (abbreviated as milky white PE) for the purpose of increasing its commercial value. ) (15) was extruded and laminated to form a cup blank (2).
【０００５】[0005]
【発明が解決しようとする課題】しかし、上記の従来技
術である紙製遮光カップ（１）の構成において二つの問
題点があった。すなわちその一つは、全面に墨インキ層
（１０）で遮光層としたカップブランク（２）を用い
て、紙製遮光カップ（１）を成形すると、図２（ａ）に
示すように、カップブランク（２）の継ぎ目である胴部
端面（３０）および折り曲げられた底部端面（３２）に
墨インキ層（１０）がはみ出て、見た目に悪く非衛生的
印象を与えることであり、二つ目の問題点は、乳白ＰＥ
（１５）では、墨インキ層（１０）に対する隠蔽性に欠
け、内容物が食品類である場合は、見た目に悪く、非衛
生的であるという印象を与えるものであった。即ちいず
れも商品価値を低下させるという問題点があった。However, there are two problems in the construction of the above-mentioned prior art paper light-shielding cup (1). That is, one of them is to form a paper light-shielding cup (1) using a cup blank (2) in which a light-shielding layer is formed by a black ink layer (10) on the entire surface, as shown in FIG. The black ink layer (10) protrudes from the body end face (30) and the bent bottom end face (32), which are seams of the blank (2), to give an unsightly and unsanitary impression. The problem is that milky white PE
(15) lacked the concealability of the black ink layer (10), and when the contents were foods, gave an impression that the appearance was poor and unsanitary. That is, there is a problem that the product value is lowered.
【０００６】本発明は、かかる従来技術の問題点を解決
するものであり、その課題とするところは、内容物特に
食品類の品質管理の一環である金属探知器の適用可能な
紙製遮光カップ（１）において、遮光性付与のための墨
インキ層（１０）がカップブランク（２）の継ぎ目であ
るカップ内面の胴部端面（３０）及び折り曲げられた底
部端面（３２）に現れることを防止し、さらに遮光層と
しての墨インキ（１０）を隠蔽する乳白ＰＥ（１５）の
隠蔽性欠如を補うことによって、見た目によく、衛生的
な印象を与え、商品価値を高める紙製遮光カップ（１）
を提供することにある。The present invention has been made to solve the above-mentioned problems of the prior art, and it is an object of the present invention to provide a paper light-shielding cup applicable to a metal detector which is a part of quality control of contents, especially foods. In (1), the black ink layer (10) for imparting light-shielding properties is prevented from appearing on the barrel end face (30) and the bent bottom end face (32) of the inner surface of the cup which is the seam of the cup blank (2). Further, by compensating for the lack of concealing property of the milky white PE (15) that conceals the black ink (10) as a light shielding layer, a paper-made light-shielding cup (1) that gives a pleasing and hygienic impression and enhances commercial value is provided. )
Is to provide.
【０００７】[0007]
【課題を解決するための手段】本発明に於いて上記課題
を達成するために、まず請求項１の発明では、金属層を
含まない、少なくとも厚紙原紙の内側に墨インキ層と乳
白ポリエチレン層の順に積層して成る遮光カップ用原紙
を用いて成形される紙製遮光カップにおいて、該墨イン
キ層がカップブランクの端辺に沿って一定幅の非印刷部
をもった印刷パターンであることを特徴とする紙製遮光
カップとしたものである。In order to achieve the above object, the present invention provides a method for producing a black ink layer and a milky white polyethylene layer at least on the inside of a cardboard base paper which does not include a metal layer. In a paper light-shielding cup formed by using a light-shielding cup base paper layered in order, the black ink layer is a printing pattern having a non-printed portion having a fixed width along an edge of the cup blank. Paper light-shielding cup.
【０００８】また、請求項２の発明では、前記墨インキ
層が、墨インキと白色インキもしくはアルミニウムペー
ストとの混合物であることを特徴とする紙製遮光カップ
としたものである。In the invention according to claim 2, the paper black light-shielding cup is characterized in that the black ink layer is a mixture of black ink and white ink or aluminum paste.
【０００９】また、請求項３の発明では、前記印刷パタ
ーンが、その上に積層された乳白ポリエチレンを介して
白ポリエチレン（以下白ＰＥと略す）フィルムで覆われ
ていることを特徴とする紙製遮光カップとしたものであ
る。According to a third aspect of the present invention, the printing pattern is covered with a white polyethylene (hereinafter abbreviated as white PE) film via a milky white polyethylene laminated thereon. It was a light-shielding cup.
【００１０】また、請求項４の発明では、前記墨インキ
層が、墨インキと白色インキもしくはアルミニウムペー
ストインキとの混合物であり、かつ前記印刷パターン
が、その上に積層された乳白ポリエチレンを介して白ポ
リエチレンフィルムで覆われていることを特徴とする紙
製遮光カップとしたものである。[0010] In the invention according to claim 4, the black ink layer is a mixture of black ink and white ink or aluminum paste ink, and the printing pattern is formed via milky white polyethylene laminated thereon. A light-shielding cup made of paper, which is covered with a white polyethylene film.
【００１１】[0011]
【発明の実施の形態】以下本発明の実施の形態を説明す
る。本発明の内容物特に食品類の品質管理の一環である
金属探知器の適用可能な紙製遮光カップは、図１（ａ）
〜（ｄ）に示すように、金属層を含まない、少なくとも
厚紙原紙（１２）の内側に墨インキ層（１０）と乳白Ｐ
Ｅ（１５）の順に積層して成る遮光性カップ用原紙を用
いて成形される紙製遮光カップ（１）において、図１
（ａ）に示すようにその墨インキ層（１０）がカップブ
ランク（２）の端辺に沿って一定幅の非印刷部（２２）
をもったカップブランク（２）より小さめの印刷パター
ン（２０）であることを特徴とする紙製遮光カップとし
たものである。Embodiments of the present invention will be described below. FIG. 1 (a) shows a paper light-shielding cup applicable to a metal detector which is a part of quality control of the contents of the present invention, particularly foods.
As shown in (d), at least the black ink layer (10) and the milky white P
FIG. 1 shows a paper light-shielding cup (1) molded using light-shielding cup base paper laminated in the order of E (15).
As shown in (a), the black ink layer (10) is a non-printed part (22) having a fixed width along the edge of the cup blank (2).
A light-shielding cup made of paper, characterized in that the printing pattern (20) is smaller than the cup blank (2).
【００１２】また、前記墨インキ層（１０）が、図１
（ｃ）に示すように墨インキと白色インキもしくはアル
ミペーストインキとの混合物から成る灰色インキ（１０
ａ）である紙製遮光カップ（１）としたものである。Further, the black ink layer (10) is formed as shown in FIG.
As shown in (c), a gray ink (10) composed of a mixture of black ink and white ink or aluminum paste ink.
a) The light-shielding cup (1) made of paper as in (a).
【００１３】さらにまた、前記印刷パターン（２０）が
図１（ｄ）に示すようにその上に積層された乳白ＰＥ
（１５）を介して白ＰＥフィルム（１４）で覆われてい
ることを特徴とする紙製遮光カップ（１）としたもので
ある。Furthermore, as shown in FIG. 1 (d), the printing pattern (20) has a milky white PE layered thereon.
A paper light-shielding cup (1) characterized by being covered with a white PE film (14) via (15).
【００１４】さらにまた、前記墨インキ層（１０）が、
墨インキと白色インキもしくはアルミニウムペーストイ
ンキとの混合物から成り、かつ前記印刷パターン（２
０）がその上に積層された乳白ＰＥ（１５）を接着剤と
して白ＰＥフィルム（１４）で覆われていることを特徴
とする紙製遮光カップ（１）としたものである。Further, the black ink layer (10) is
A mixture of black ink and white ink or aluminum paste ink, and the printing pattern (2)
No. 0) is a paper light-shielding cup (1) characterized by being covered with a white PE film (14) using the milky white PE (15) laminated thereon as an adhesive.
【００１５】本発明の金属層を含まない遮光カップ用原
紙とは、紙製遮光カップに一般的に使用されているアル
ミニウム箔を用いないことで、アルミニウムを蒸着した
合成樹脂フィルムや紙は、前述のように金属探知機に影
響のない蒸着膜厚であれば必要に応じて使用するもので
ある。The base paper for a light-shielding cup containing no metal layer according to the present invention is defined as a synthetic resin film or paper on which aluminum is vapor-deposited by using no aluminum foil commonly used for paper light-shielding cups. If necessary, any film thickness that does not affect the metal detector can be used.
【００１６】まず、カップブランク（２）の端辺に沿っ
て一定幅の非印刷部（２２）をもったカップブランク
（２）より小さめの印刷パターン（２０）について説明
する。この印刷パターン（２０）がカップブランク
（２）全面に施すことにより、紙製遮光カップ（１）の
内面の継ぎ目の胴部端面（３０）及び底部端面（３２）
に墨インキ層（１０）が現れ、見た目に悪く、非衛生的
な感触を防ぐためにカップブランク（２）より小さめの
墨インキ層（１０）によって印刷パターン（２０）を形
成するものであり、この印刷パターン（２０）の形成に
は、グラビア印刷法が好ましい。オフセット印刷法やス
クリーン印刷法でも可能であるが、カップの厚紙原紙
（１２）が高生産性を考慮した巻き取り（ロール）状で
あることから、グラビア印刷が最適であり、オフセット
印刷法では得られない高遮光性が得られるためでもあ
る。First, a printing pattern (20) smaller than the cup blank (2) having a non-printing portion (22) having a constant width along the edge of the cup blank (2) will be described. The printing pattern (20) is applied to the entire surface of the cup blank (2), so that the body end surface (30) and the bottom end surface (32) of the seam on the inner surface of the paper shading cup (1).
A black ink layer (10) appears on the black ink layer (10), and the print pattern (20) is formed by a black ink layer (10) smaller than the cup blank (2) in order to prevent unsightly and unsanitary feel. The gravure printing method is preferable for forming the print pattern (20). Offset printing or screen printing is possible, but gravure printing is most suitable because the cardboard base paper (12) of the cup is in a roll shape considering high productivity. This is also because a high light-shielding property that cannot be obtained is obtained.
【００１７】印刷パターン（２０）の形状は、図１
（ａ）に示すように、カップブランク（２）より小さめ
で、カップブランク（２）の端辺に沿って一定幅の非印
刷部（２２）をもったものであり、この一定幅は、カッ
プの大きさによっても異なるが例えば通常のアイスクリ
ームカップでは、２ｍｍ〜５ｍｍ程度が好ましい。ま
た、墨インキ（１０）による印刷パターン（２０）の厚
さは、１μｍ〜３μｍが得られるが、例えば３μｍの墨
インキ（１０）層をもったカップブランク（２）の透過
率の測定結果は、自然光１０００ルックス下では、約
０．０２で、５０００ルックス下では、約０．０３であ
り、充分な遮光性が得られることが実証されている。こ
の墨インキ層（１０）の厚さは厚い方が好ましいことは
いうまでもないが、グラビア印刷法にて一回刷で得られ
る厚さに限度があり、約３μｍが限界値である。The shape of the print pattern (20) is shown in FIG.
As shown in (a), the cup blank (2) is smaller than the cup blank (2) and has a non-printing portion (22) having a constant width along the edge of the cup blank (2). For example, in a normal ice cream cup, it is preferably about 2 mm to 5 mm. The thickness of the printing pattern (20) formed by the black ink (10) is 1 μm to 3 μm. For example, the measurement result of the transmittance of a cup blank (2) having a 3 μm black ink (10) layer is as follows. It is about 0.02 under 1,000 lux of natural light, and about 0.03 under 5000 lux, and it is proved that sufficient light-shielding properties can be obtained. Needless to say, the thickness of the black ink layer (10) is preferably thicker, but there is a limit to the thickness that can be obtained by one-time printing by the gravure printing method, and the limit value is about 3 μm.
【００１８】グラビア用墨インキとしては、トルエンや
酢酸エチルなどの有機溶剤系インキまたは水溶性インキ
のいずれも可能であるが、環境保全の面から水溶性墨イ
ンキが好ましい。As the gravure black ink, any of an organic solvent-based ink such as toluene and ethyl acetate or a water-soluble ink can be used, but a water-soluble black ink is preferable from the viewpoint of environmental protection.
【００１９】次に、紙製遮光カップ（１）の内面に施さ
れた墨インキ層（１０）を隠蔽する目的で乳白ＰＥを押
し出しラミネートするが、この乳白ＰＥ（１５）のみで
は隠蔽性が十分とはいえず、特に前記のように印刷パタ
ーン（２０）とすることによって、非印刷部（２２）と
の境界にコントラストができ見た目にも好ましくない即
ち商品価値のおとる状態のものであった。この状態を改
善する目的で、墨インキに白インキまたはアルミニウム
ペーストを混合して略灰色インキ（１０ａ）としたもの
である。Next, for the purpose of concealing the black ink layer (10) applied to the inner surface of the paper-made light-shielding cup (1), the milky white PE is extruded and laminated. However, in particular, by using the printing pattern (20) as described above, the boundary with the non-printing portion (22) has a contrast, which is unfavorable in appearance, that is, has a commercial value. . For the purpose of improving this state, black ink is mixed with white ink or aluminum paste to obtain a substantially gray ink (10a).
【００２０】この乳白ＰＥ（１５）層の形成は、ＰＥに
酸化チタンを混入した樹脂の押し出しラミネーションに
よって行われ、厚さ２０μｍ〜４０μｍの層が形成され
る。得られた乳白ＰＥ（１５）層の隠蔽性は酸化チタン
の混入率と層の厚さによって決まるが、生産性や経済性
から混入率２０％〜３０％、厚さは上記のように２０μ
ｍ〜４０μｍが望ましい。ここで因みに白ＰＥフィルム
（１４）の隠蔽性を反射濃度で評価してみた。先ず厚紙
原紙（１２）にグラビア用墨インキを施したものの反射
濃度は、約１．６０で、その上に酸化チタン混入率３０
％、厚さ３０μｍの乳白ＰＥ（１５）を押し出しラミネ
ートしたものの反射濃度は、１．０５であった。この隠
蔽性に規制はなくあくまでも感覚的に善し悪しを判断せ
ざるを得ないが、少なくともこの反射濃度１．０５では
満足のいく値とは程遠く、商品価値の劣るものであっ
た。The formation of the milky white PE (15) layer is performed by extrusion lamination of a resin in which titanium oxide is mixed into PE, and a layer having a thickness of 20 μm to 40 μm is formed. The hiding power of the obtained milky white PE (15) layer is determined by the mixing ratio of titanium oxide and the thickness of the layer. From the viewpoint of productivity and economy, the mixing ratio is 20% to 30%, and the thickness is 20 μm as described above.
m to 40 μm is desirable. Here, the hiding power of the white PE film (14) was evaluated by reflection density. First, the base paper (12) coated with black ink for gravure has a reflection density of about 1.60, and a titanium oxide mixing ratio of 30 on it.
%, And the reflection density of an extruded and laminated milky PE (15) having a thickness of 30 μm was 1.05. There is no restriction on this concealing property, and it is inevitable to judge whether it is good or bad sensuously. However, at least this reflection density of 1.05 is far from a satisfactory value, and the commercial value is inferior.
【００２１】そこで墨インキと白インキを混合したイン
キの場合を上記と同様の方法で隠蔽性の評価をしてみ
た。グラビア用墨インキとグラビア用白インキ（いずれ
も水溶性）を１対１で混合した灰色インキを用いて、厚
紙原紙（１２）に印刷したものの反射濃度は０．９６で
あった。さらにその上に酸化チタン混入率３０％、厚さ
３０μｍの乳白ＰＥ（１５）を押し出しラミネートした
ものの反射濃度は０．５５であった。この程度の反射濃
度であれば、ほぼ商品価値のあるものと判断した。Therefore, the concealing property of the ink obtained by mixing the black ink and the white ink was evaluated in the same manner as described above. The reflection density was 0.96 when printed on cardboard base paper (12) using gray ink obtained by mixing gravure black ink and gravure white ink (all water-soluble) in a one-to-one correspondence. Further, a white PE (15) having a mixing ratio of titanium oxide of 30% and a thickness of 30 μm was extruded and laminated thereon, and the reflection density was 0.55. At this level of reflection density, it was determined that the product had almost commercial value.
【００２２】また、墨インキとアルミニウムペーストイ
ンキを１対１に混合し、厚紙原紙（１２）にグラビア印
刷したものの反射濃度は、１．０５であった。さらにそ
の上に酸化チタン混入率３０％、厚さ３０μｍの乳白Ｐ
Ｅ（１５）を押し出しラミネートしたものの反射濃度は
０．６０であった。この場合の濃度は、白インキの場合
より僅かに効果が少ないが、商品価値のあるものと判断
した。なお、アルミニウムペーストインキは金属探知機
が適用可能であることは確認済である。The reflection density of a one-to-one mixture of black ink and aluminum paste ink and gravure printing on cardboard base paper (12) was 1.05. Further, a milky white P having a mixing ratio of titanium oxide of 30% and a thickness of 30 μm is further formed thereon.
The reflection density of E (15) extruded and laminated was 0.60. The density in this case was slightly less effective than that of the white ink, but was judged to be of commercial value. It has been confirmed that a metal detector can be applied to the aluminum paste ink.
【００２３】また、墨インキ層（１０）の隠蔽性改善の
ためのもう一方の発明は、印刷パターン（２０）が図１
（ｄ）に示すように、その上に押し出しラミネーション
法で積層された乳白ＰＥ（１５）を接着剤的役割として
白ＰＥフィルム（１４）で覆われていることを特徴とす
る紙製遮光カップ（１）としたものである。In another invention for improving the concealment of the black ink layer (10), the printing pattern (20) is shown in FIG.
As shown in (d), a milky PE (15) laminated thereon by an extrusion lamination method is covered with a white PE film (14) as an adhesive, and the paper light-shielding cup ( 1).
【００２４】ここで使用する白ＰＥフィルム（１４）
は、通常厚さ３０μｍ〜５０μｍが好ましい。これは隠
蔽性からすれば厚さがある方が好ましいがラミネートな
どの生産性と経済性から制限があるためである。White PE film used here (14)
Is usually preferably 30 μm to 50 μm in thickness. This is because it is preferable to have a large thickness in terms of concealment, but there is a limit in terms of productivity and economics of lamination and the like.
【００２５】ここで乳白ＰＥ（１５）で積層された墨イ
ンキ層（１０）から成る印刷パターン（２０）を白ＰＥ
フィルム（１４）で覆った場合の隠蔽性を上記と同様の
反射濃度測定法で評価をしてみた。先ず前述と同様に厚
紙原紙（１２）にグラビア用墨インキを施したものの反
射濃度は、約１．６０で、その上に３０μｍ、酸化チタ
ン混入率３０％の乳白ＰＥ（１５）を押し出しラミネー
トしたものの反射濃度は、１．１５であった。さらにそ
の上に厚さ４０μｍの白ＰＥフィルム（１４）をラミネ
ートしたものの反射濃度は、０．５０であり充分な隠蔽
性を示す値であると評価した。The printing pattern (20) consisting of the black ink layer (10) laminated with the milky white PE (15) is
The concealing property when covered with the film (14) was evaluated by the same reflection density measurement method as described above. First, the gravure black ink was applied to the cardboard base paper (12) in the same manner as described above, but the reflection density was about 1.60, and a milky white PE (15) having a thickness of 30 μm and a titanium oxide mixing ratio of 30% was extruded and laminated thereon. However, the reflection density was 1.15. Furthermore, the reflection density of a laminate of the white PE film (14) having a thickness of 40 μm thereon was 0.50, which was evaluated as a value showing sufficient hiding power.
【００２６】次に、墨インキの隠蔽性改善のためのさら
にもう一方の発明は、前記墨インキ（１０）層が、墨イ
ンキと白色インキもしくはアルミニウムペーストインキ
との混合物であり、かつ前記印刷パターン（２０）がそ
の上に積層された乳白ＰＥ（１５）を接着剤的役割をし
て白ＰＥフィルム（１４）で覆われている紙製遮光カッ
プ（１）としたものであり、墨インキ層（１０）の隠蔽
性改善により一層の効果が期待されるものである。Next, still another invention for improving the concealability of black ink is that the black ink (10) layer is a mixture of black ink and white ink or aluminum paste ink, and the printing pattern is (20) is a paper light-shielding cup (1) covered with a white PE film (14), serving as an adhesive, with the milky white PE (15) laminated thereon, A further effect is expected by the improvement of the concealing property of (10).
【００２７】ここで墨インキと白インキを混合したイン
キを使用し、かつ墨インキ層（１０）を乳白ＰＥ（１
５）で積層した場合の隠蔽性を上記と同様の反射濃度測
定法で評価をしてみた。グラビア用墨インキとグラビア
用白インキ（いずれも水溶性）を１対１で混合し、厚紙
原紙（１２）に印刷したものの反射濃度は０．９８であ
った。さらにその上に３０μｍ、酸化チタン混入率３０
％の乳白ＰＥ（１５）を押し出しラミネートしたものの
反射濃度は、０．６０であった。さらにまたその上に厚
さ４０μｍの白ＰＥフィルム（１４）をラミネートした
ものの反射濃度は、０．３５でありより一層の隠蔽性効
果を示す値であった。Here, an ink obtained by mixing black ink and white ink is used, and the black ink layer (10) is made of milk white PE (1).
The concealing property in the case of lamination in 5) was evaluated by the same reflection density measurement method as described above. The gravure black ink and the gravure white ink (both water-soluble) were mixed one-to-one and printed on cardboard base paper (12). The reflection density was 0.98. On top of that, 30 μm and a titanium oxide mixing ratio of 30 μm
% Of the milky PE (15) extruded and laminated, the reflection density was 0.60. Further, the reflection density of a white PE film (14) having a thickness of 40 μm laminated thereon was 0.35, which was a value showing a further concealing effect.
【００２８】以上の墨インキ層（１０）の隠蔽性評価試
験結果から、反射濃度で０．６５以下好ましくは０．５
５以下であれば、目的の商品価値の低下防止となるもの
と評価した。From the results of the above hiding evaluation test of the black ink layer (10), the reflection density is 0.65 or less, preferably 0.5 or less.
When the value was 5 or less, it was evaluated that the reduction in the target commercial value was prevented.
【００２９】[0029]
【実施例】次に本発明を実施例により、本発明を具体的
に説明する。 ＜実施例１＞以下の紙製遮光カップの製造条件及び材料
とした。 厚紙原紙（１２）‥‥坪量３００ｇ／ｍ2 のカップ原紙 透明ＰＥ層（１８）‥‥厚さ４０μｍ、押し出しラミネ
ーション 墨インキ層（１０）‥‥墨インキ（ニューＬＰスーパー
・東洋インキ製造社製）と白インキ（ニューＬＰスーパ
ー・東洋インキ製造社製）を１対１混合した灰色インキ 印刷パターン化‥‥非印刷部（２２）の幅３ｍｍ、グラ
ビア印刷法にて厚さ３μｍに形成 乳白ＰＥ（１５）‥‥酸化チタン混入率３０％、押し出
しラミネーション法で厚さ３０μｍに形成Next, the present invention will be described in detail with reference to examples. Example 1 The following manufacturing conditions and materials were used for the paper light-shielding cup. Cardboard base paper (12) カ ッ プ 300 g / m 2 basis weight cup base paper Transparent PE layer (18) ４０ 40 μm thickness, extrusion lamination Black ink layer (10) ‥‥ Black ink (New LP Super, manufactured by Toyo Ink Manufacturing Co., Ltd.) ) And white ink (New LP Super, Toyo Ink Mfg. Co., Ltd.) mixed one-to-one. Printing patterning. 3mm width of non-printing area (22), 3μm thickness by gravure printing. (15) Titanium oxide mixing rate 30%, formed by extrusion lamination method to a thickness of 30 μm
【００３０】以上の条件にて、内容量１２０ｍｌのアイ
スクリームカップを作成した。その紙製遮光カップの遮
光性評価のための自然光１０００ルックス下での透過率
は、０．０２であり、墨インキ層の隠蔽性評価のための
反射濃度は、０．６０であった。即ち外光及び冷凍ケー
ス内の蛍光灯に対する遮光性はほぼ満足のいける値であ
り、アイスクリームカップ内部の墨インキ層がカップ内
面の継ぎ目胴部端面にはみ出ることがなく、印刷パター
ンもカップ内面からはほぼ目立たなく商品価値の損なわ
ない反射濃度のものであった。また、金属探知機には反
応のないカップであった。Under the above conditions, an ice cream cup having a content of 120 ml was prepared. The transmittance under 1,000 lux of natural light for evaluating the light-shielding property of the paper light-shielding cup was 0.02, and the reflection density for evaluating the opacity of the black ink layer was 0.60. That is, the light-shielding property against external light and the fluorescent lamp in the freezing case is a value that is almost satisfactory, the black ink layer inside the ice cream cup does not protrude to the end face of the seam barrel on the inner surface of the cup, and the printing pattern is also from the inner surface of the cup. Had a reflection density that was almost inconspicuous and did not impair the commercial value. In addition, the cup did not respond to the metal detector.
【００３１】＜実施例２＞実施例１の条件に、厚さ４０
μｍの白ＰＥフィルム（１４）をラミネーションにて付
加し、内容量＊＊＊ｍｇのアイスクリームカップを作成
した。<Embodiment 2> Under the conditions of Embodiment 1, a thickness of 40
A white PE film (14) of μm was added by lamination to prepare an ice cream cup having a content of *** mg.
【００３２】その紙製遮光カップの遮光性評価のための
自然光１０００ルックス下での透過率は、０．０２で実
施例１と同値であり、墨インキ層の隠蔽性評価のための
反射濃度は、０．３３であった。即ち外光及び冷凍ケー
ス内の蛍光灯に対する遮光性はほぼ満足のいける値であ
り、アイスクリームカップ内部の墨インキ層がかっ内面
の継ぎ目胴部端面や底部端面にはみ出ることなく、印刷
パターンもほぼ目立たなく実施例１よりさらに商品価値
の損なわない低い反射濃度のものであった。また、金属
探知機には反応のないカップであった。The transmittance of the paper light-shielding cup under natural light of 1,000 lux for evaluating the light-shielding property was 0.02, which is the same value as in Example 1, and the reflection density for evaluating the opacity of the black ink layer was , 0.33. That is, the light-shielding property against the external light and the fluorescent lamp in the freezing case is a value that is almost satisfactory, and the black ink layer inside the ice cream cup does not protrude to the end face of the seam barrel or the bottom end face of the inside of the cup, and the print pattern is almost conspicuous. However, the reflection density was lower than that of Example 1 without impairing the commercial value. In addition, the cup did not respond to the metal detector.
【００３３】[0033]
【発明の効果】本発明は以上の構成であるから、下記に
示す如き効果がある。即ち、紙製遮光カップにおいて、
遮光層となる墨インキ層がカップブランクの端辺に沿っ
て一定幅の非印刷部をもった印刷パターンであるから、
カップ内面の継ぎ目胴部端面や底部端面に墨インキ層が
はみ出ることがなく、衛生的で商品価値を低下させない
効果がある。As described above, the present invention has the following effects. That is, in a paper light-shielding cup,
Because the black ink layer, which is the light-shielding layer, is a print pattern having a non-printed part with a fixed width along the edge of the cup blank,
The black ink layer does not protrude from the end face of the joint body or the bottom face of the inner surface of the cup, which is hygienic and has the effect of not reducing the commercial value.
【００３４】また、遮光層としての墨インキ層が、墨イ
ンキと白インキもしくはアルミニウムペーストインキと
の混合物からなるため、カップ内面での隠蔽性が向上
し、商品価値を低下させない効果がある。Further, since the black ink layer as the light-shielding layer is made of a mixture of black ink and white ink or aluminum paste ink, the concealing property on the inner surface of the cup is improved and there is an effect that the commercial value is not reduced.
【００３５】また、遮光層としての印刷パターンが、そ
の上に積層された乳白ポリエチレンを介して白ポリエチ
レンフィルムで覆われているからカップ内面での隠蔽性
が向上し、商品価値を低下させない効果がある。Further, since the print pattern as the light-shielding layer is covered with the white polyethylene film via the milky white polyethylene laminated thereon, the concealability on the inner surface of the cup is improved, and the effect of not reducing the commercial value is obtained. is there.
【００３６】さらにまた、遮光層を墨インキと白インキ
もしくはアルミニウムペーストインキとの混合物とし、
さらにその遮光層がその上に積層された乳白ポリエチレ
ンを介して白ポリエチレンフィルムで覆われているから
カップ内面での隠蔽性がより一層向上し、商品価値をよ
り低下させない効果がある。Further, the light-shielding layer is a mixture of black ink and white ink or aluminum paste ink,
Further, since the light-shielding layer is covered with the white polyethylene film via the milky white polyethylene laminated thereon, the concealability on the inner surface of the cup is further improved, and there is an effect that the commercial value is not further reduced.
【００３７】また、遮光層にアルミニウム箔などの金属
層が含まないので、内容物に金属系切り粉等の混入を管
理する金属探知機の使用が可能であり、またカップの使
用後の焼却処理において、ロストル（火格子）を傷める
こともなく、焼却残滓からの有害ガスの発生もない環境
調和型の紙製遮光カップを提供する効果がある。Further, since the light-shielding layer does not include a metal layer such as an aluminum foil, it is possible to use a metal detector for controlling the mixing of metal-based chips or the like into the contents, and to incinerate the cup after use. In this case, there is an effect of providing an environment-friendly paper light-shielding cup that does not damage a grate and does not generate harmful gas from incineration residues.
【図１】（ａ）は本発明の実施の形態を示すカップブラ
ンクの展開面である。（ｂ）は本発明の実施の形態を示
す紙製遮光カップの斜視図である。（ｃ）は本発明の実
施の形態を示すカップブランクの側断面図である。
（ｄ）は本発明の実施の形態を示すカップブランクの他
の側断面図である。FIG. 1 (a) is a development surface of a cup blank showing an embodiment of the present invention. (B) is a perspective view of a paper light-shielding cup showing an embodiment of the present invention. (C) is a side sectional view of the cup blank showing the embodiment of the present invention.
(D) is another side sectional view of the cup blank showing the embodiment of the present invention.
【図２】（ａ）は従来の実施の形態を示すカップを斜視
図で表した説明図である。（ｂ）は従来の実施の形態を
示すカップブランクを側断面で表した説明図であFIG. 2A is an explanatory diagram showing a perspective view of a cup according to a conventional embodiment. (B) is explanatory drawing which represented the cup blank which shows the conventional embodiment in the side cross section.
１‥‥紙製遮光カップ ２‥‥カップブランク ２ａ‥‥灰色インキカップブランク ２ｂ‥‥白ＰＥカップブランク １０‥‥墨インキ層 １０ａ‥‥灰色インキ １２‥‥厚紙原紙 １４‥‥白ＰＥフィルム １５‥‥乳白ＰＥ １６‥‥絵柄印刷層 １８‥‥透明ＰＥ層 ２０‥‥印刷パターン ２２‥‥非印刷部 ３０‥‥胴部端面 ３２‥‥底部端面 1 Paper shading cup 2 Cup blank 2a Gray ink cup blank 2b White PE cup blank 10 Black ink layer 10a Gray ink 12 Cardboard 14 White PE film 15 {Milk white PE 16} Picture print layer 18 >> Transparent PE layer 20 >> Print pattern 22 >> Non-printed part 30 >> Body end face 32 >> Bottom end face
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ｂ３２Ｂ 27/32 Ｂ３２Ｂ 27/32 Ｚ Ｂ６５Ｄ 3/22 Ｂ６５Ｄ 3/22 Ｂ (72)発明者 関口 博喜 東京都台東区台東１丁目５番１号 凸版印 刷株式会社内 (72)発明者 菊地 和也 東京都台東区台東１丁目５番１号 凸版印 刷株式会社内──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 6 Identification code FI B32B 27/32 B32B 27/32 Z B65D 3/22 B65D 3/22 B (72) Inventor Hiroki Sekiguchi 1-chome, Taito-ku, Tokyo No. 5-1 Letterpress Printing Co., Ltd. (72) Inventor Kazuya Kikuchi 1-15-1 Taito, Taito-ku, Tokyo Letterpress Printing Co., Ltd.
Claims (4)
２の内側に墨インキ層１０と乳白ポリエチレン層１５の
順に積層して成る遮光カップ用原紙を用いて成形される
紙製遮光カップ１において、その墨インキ層１０がカッ
プブランク２の端辺に沿って一定幅の非印刷部２２をも
った印刷パターン２０であることを特徴とする紙製遮光
カップ。1. A cardboard base paper 1 containing no metal layer.
In a paper light-shielding cup 1 formed using a light-shielding cup base paper formed by laminating a black ink layer 10 and a milk-white polyethylene layer 15 in this order on the inside of the paper blank 2, the black ink layer 10 extends along the edge of the cup blank 2. A light-shielding cup made of paper, characterized in that it is a printing pattern 20 having a non-printing portion 22 having a constant width.
ンキもしくはアルミニウムペーストインキとの混合物か
ら成ることを特徴とする請求項１記載の紙製遮光カッ
プ。2. A paper light-shielding cup according to claim 1, wherein said black ink layer comprises a mixture of black ink and white ink or aluminum paste ink.
れている乳白ポリエチレン１５を介して白ポリエチレン
フィルム１４で覆われていることを特徴とする請求項１
記載の紙製遮光カップ。3. The printed pattern 20 is covered with a white polyethylene film 14 via a milky white polyethylene 15 laminated thereon.
Paper shading cup as described.
ンキもしくはアルミニウムペーストインキとの混合物か
ら成り、かつ前記印刷パターン２０が、その上に積層さ
れている乳白ポリエチレン１５を介して白ポリエチレン
フィルム１４で覆われていることを特徴とする請求項１
記載の紙製遮光カップ。4. The black ink layer 10 is made of a mixture of black ink and white ink or aluminum paste ink, and the printing pattern 20 is formed on a white polyethylene film via a milky white polyethylene 15 laminated thereon. 2. The method as claimed in claim 1, wherein the first cover is covered with a second cover.
Paper shading cup as described.