JPH10113223A - Cosmetic cotton - Google Patents
Cosmetic cottonInfo
- Publication number
- JPH10113223A JPH10113223A JP8272248A JP27224896A JPH10113223A JP H10113223 A JPH10113223 A JP H10113223A JP 8272248 A JP8272248 A JP 8272248A JP 27224896 A JP27224896 A JP 27224896A JP H10113223 A JPH10113223 A JP H10113223A
- Authority
- JP
- Japan
- Prior art keywords
- cotton
- denier
- fiber
- weight
- cosmetic cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は化粧水や乳液などを
塗布する場合や化粧、マニキュア落としの際などに使用
される化粧綿に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cosmetic cotton used for applying a lotion or a milky lotion, for makeup, for removing nail polish, and the like.
【０００２】[0002]
【従来の技術】従来、この種の化粧綿には、肌に安全で
ソフト感及び適度な吸水性、耐水性があり、かつ厚みを
有し所望のコシ・ボリューム感をあることが要求されて
いる。2. Description of the Related Art Conventionally, this type of cosmetic cotton has been required to have a safe and soft feeling on the skin, appropriate water absorption and water resistance, and to have a desired thickness and stiffness and volume. I have.
【０００３】このため一般には、１００％綿を使用しシ
ート化しそれを数層に折り返した状態で熱シールしてな
るものが一般的であったが、高価でしかも綿屑が肌に付
着する欠点があった。For this reason, in general, a sheet made of 100% cotton and heat-sealed in a state where the sheet is folded into several layers is generally used. However, it is expensive and the cotton dust adheres to the skin. was there.
【０００４】そこで、これらの欠点を解決するため、実
公昭５８−３９６０８号公報にはレーヨンステープル繊
維のような化学繊維からなる内部層をレーヨン比率の高
い外装材で包んだ化粧綿が開示されている。かかる化粧
綿は、比較的安価に製造でき、適度な吸水・耐水性はあ
るが、コシ・ボリューム感が得られないという欠点を有
している。本発明者らは、これらの欠点を改良し、適度
な吸水性・耐水性があり、かつ、所望のコシ・ボリュー
ム感のある化粧綿を得るため鋭意検討した結果、本発明
に到達した。In order to solve these drawbacks, Japanese Utility Model Publication No. 58-39608 discloses a cosmetic cotton in which an inner layer made of a chemical fiber such as rayon staple fiber is wrapped with an outer material having a high rayon ratio. I have. Such cosmetic cotton can be manufactured relatively inexpensively and has moderate water absorption and water resistance, but has the drawback that a firm and voluminous feeling cannot be obtained. The present inventors have intensively studied to improve these drawbacks and to obtain cosmetic cotton having appropriate water absorption and water resistance and a desired firmness and volume, and as a result, the present invention has been achieved.
【０００５】[0005]
【発明が解決しようとする課題】本発明の目的は、上記
従来技術の欠点を解決し、従来技術では得られなかった
吸水性・耐水性とコシ・ボリューム感をいずれも優れた
ものとした化粧綿を提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to solve the above-mentioned drawbacks of the prior art, and to provide a cosmetic composition having excellent water absorbency, water resistance and stiffness / volume, which cannot be obtained by the prior art. To provide cotton.
【０００６】[0006]
【課題を解決するための手段】本発明の化粧綿は、上記
課題を解決するために次の構成を有する。すなわち、不
織布からなる内部層と、該内部層を包む外装材とからな
る化粧綿において、不織布が、次に示す［Ａ］、
［Ｂ］、［Ｃ］および［Ｄ］からなることを特徴とする
化粧綿。Means for Solving the Problems The cosmetic cotton of the present invention has the following constitution in order to solve the above problems. That is, in a cosmetic cotton consisting of an inner layer made of a nonwoven fabric and an exterior material wrapping the inner layer, the nonwoven fabric has the following [A],
A cosmetic cotton comprising [B], [C] and [D].
【０００７】［Ａ］：単繊維の繊度が１〜５デニールで
ある、サイドバイサイド型複合ポリエステル系短繊維 ［Ｂ］：単繊維の繊度が０．１〜１０デニールである、
鞘成分を低融点ポリエステルとし、芯成分をポリエチレ
ンテレフタレートとする芯鞘型複合ポリエステル系短繊
維 ［Ｃ］：単繊維の繊度が１〜１０デニールである、非複
合ポリエチレンテレフタレート短繊維 ［Ｄ］：綿[A]: Side-by-side type composite polyester staple fiber having a fineness of 1 to 5 denier of a single fiber [B]: Fineness of a single fiber is 0.1 to 10 denier,
Core-sheath type composite polyester staple fiber having a low melting point polyester as a sheath component and polyethylene terephthalate as a core component [C]: non-composite polyethylene terephthalate short fiber having a single fiber fineness of 1 to 10 denier [D]: cotton
【０００８】[0008]
【発明の実施の形態】本発明の化粧綿は、不織布からな
る内部層と、該内部層を包む外装材とからなる。ここ
で、不織布は、ポリエステル系短繊維及び綿からなる。
ポリエステル系短繊維には、通常、ウェッブを形成する
際に脱落などの絡合不良やネップを発生しないように、
押込型捲縮付与装置などを使用して適度な捲縮が付与さ
れている。BEST MODE FOR CARRYING OUT THE INVENTION The cosmetic cotton of the present invention comprises an inner layer made of a non-woven fabric and an exterior material surrounding the inner layer. Here, the nonwoven fabric is made of polyester short fibers and cotton.
In polyester-based short fibers, usually, when forming a web, so as not to cause entanglement defects such as falling off and neps,
Appropriate crimps are applied using a press-type crimp applying device or the like.
【０００９】ここで、本発明においては、ポリエステル
系短繊維として、次の少なくとも３種のものを混合して
用いる必要がある。Here, in the present invention, it is necessary to use a mixture of at least the following three types as polyester short fibers.
【００１０】１つ目は、単繊維の繊度が１〜５デニール
である、サイドバイサイド型複合ポリエステル系短繊維
であり、これは、通常、固有粘度差が０．０５〜０．１
０である異種ポリエステルが、第１図に示す様にサイド
バイサイド型構造に複合化された単繊維構造を有する。
かかるサイドバイサイド型複合ポリエステル系短繊維
は、５０〜１５０℃の熱処理で捲縮が顕在化し、それに
より、繊維同士の絡合性が良くなり、単繊維がばねの様
な働きをして膨らみ感・ボリューム感を生じることとな
る。ここで、捲縮が顕在化するとは、熱処理により繊維
が収縮して、例えば１３〜１９山 ／２５ｍｍであった
捲縮数が５０〜８０／２５ｍｍの様に多くなることであ
る。また、かかるサイドバイサイド型複合ポリエステル
系短繊維を用いると、後記する不織布の製造時に行う熱
処理が低温で行えるためコスト的に有利であるという利
点もある。膨らみ感・ボリューム感をより顕著なものと
する観点から、および後述する他のポリエステル系短繊
維の混率との関係から、この短繊維の不織布に含まれる
混率は、２０〜３０重量％であるのが好ましい。The first type is a side-by-side type conjugated polyester short fiber having a single fiber fineness of 1 to 5 denier, which usually has a difference in intrinsic viscosity of 0.05 to 0.1.
As shown in FIG. 1, the dissimilar polyester of 0 has a single fiber structure compounded into a side-by-side structure.
In such side-by-side type composite polyester short fibers, crimps become apparent by heat treatment at 50 to 150 ° C., whereby the entanglement between the fibers is improved, and the single fibers act like a spring to give a feeling of swelling. This results in a sense of volume. Here, the expression of the crimp means that the fiber shrinks due to the heat treatment, and the number of crimps increases from 13 to 19 ridges / 25 mm to 50 to 80/25 mm, for example. The use of such side-by-side type composite polyester short fibers also has the advantage of being advantageous in terms of cost because heat treatment performed during the production of a nonwoven fabric described later can be performed at a low temperature. From the viewpoint of making the feeling of swelling and volume more remarkable, and from the relationship with the mixing ratio of other polyester short fibers described below, the mixing ratio of the short fibers contained in the nonwoven fabric is 20 to 30% by weight. Is preferred.
【００１１】２つ目は、異種成分ポリマー同士が、第２
図に示す如く芯鞘型構造に複合化された芯鞘型複合ポリ
エステル系短繊維であり、鞘成分は低融点ポリエステ
ル、好ましくは融点が１００〜１６０℃であるポリエス
テルを使用し、芯成分はポリエチレンテレフタレート、
好ましくはホモポリエチレンテレフタレートを使用す
る。この短繊維は、バインダーとして作用する。この短
繊維を用いることにより、後述する不織布製造時の熱処
理で低融点ポリマーが溶融し、他の短繊維と接着するこ
とで、綿屑が肌へと付着するのを防ぎ、不織布の形状を
固定させることができる。かかる観点から、この短繊維
の不織布中の混率は、１０〜２０重量％が好ましい。ま
た、本発明で用いるバインダー繊維は芯鞘型構造を有す
るので、鞘のポリマーが溶融した後でも芯の成分が単繊
維として残ることができ、不織布の強度を向上できると
いう利点もある。[0011] The second is that the different component polymers are in the second position.
As shown in the figure, it is a core-sheath composite polyester staple fiber composited into a core-sheath type structure, and a sheath component is a low-melting polyester, preferably a polyester having a melting point of 100 to 160 ° C. Terephthalate,
Preferably, homopolyethylene terephthalate is used. This short fiber acts as a binder. By using these short fibers, the low-melting-point polymer is melted by the heat treatment during non-woven fabric production described below and adheres to other short fibers, preventing cotton dust from adhering to the skin and fixing the shape of the non-woven fabric. Can be done. From this viewpoint, the mixing ratio of the short fibers in the nonwoven fabric is preferably from 10 to 20% by weight. Further, since the binder fiber used in the present invention has a core-sheath type structure, there is also an advantage that the core component can remain as a single fiber even after the sheath polymer is melted, and the strength of the nonwoven fabric can be improved.
【００１２】３つ目は、単繊維の繊度が１〜１０デニー
ル、好ましくは、３〜６デニールである、非複合ポリエ
チレンテレフタレート短繊維である。この短繊維は、前
述した複合ポリエステル系短繊維とは異なり、ポリエチ
レンテレフタレート、好ましくはホモポリエチレンテレ
フタレートを主体とする、複合化していない実質的に均
質な短繊維である。これを使用することにより、不織布
にボリューム感をもたせることができる。かかる繊度が
小さすぎると、不織布にコシ・ボリューム感を持たせる
ことができず、大きすぎると、不織布にガサツキ感が生
じてしまう。またこの短繊維は、コシ、ボリューム感を
適度なものとし、前記した他のポリエステル系短繊維の
混率との関係から、不織布に含まれる混率を、２５〜３
５重量％とするのが好ましい。The third type is a non-composite polyethylene terephthalate short fiber having a single fiber fineness of 1 to 10 denier, preferably 3 to 6 denier. This short fiber is a non-composite substantially homogeneous short fiber mainly composed of polyethylene terephthalate, preferably homopolyethylene terephthalate, unlike the above-mentioned conjugate polyester-based short fiber. By using this, the nonwoven fabric can have a sense of volume. If the fineness is too small, the nonwoven fabric cannot have a firm and voluminous feel, and if it is too large, the nonwoven fabric will have a rough feeling. In addition, this short fiber has a moderate stiffness and volume, and the mixing ratio of the nonwoven fabric is 25 to 3 in view of the mixing ratio of the other polyester short fibers.
It is preferably 5% by weight.
【００１３】本発明において不織布に用いる綿として
は、特に限定されるものではない。綿を混入させること
により、一般的に疎水性であるポリエステル系繊維の不
織布において不足してしまう吸水性や柔らかさを付与す
ることができる。かかる観点から、綿の不織布中の混率
は、２５〜３５重量％であることが好ましい。The cotton used for the nonwoven fabric in the present invention is not particularly limited. By mixing cotton, water absorption and softness, which are generally insufficient in a nonwoven fabric of a polyester fiber that is hydrophobic, can be imparted. From such a viewpoint, the mixing ratio in the cotton nonwoven fabric is preferably 25 to 35% by weight.
【００１４】上記要件を満たす不織布とすることによ
り、吸水性・耐水性とコシ・ボリューム感をいずれも優
れたものとし、化粧綿に適したものとすることができ
る。By using a non-woven fabric satisfying the above requirements, both water absorption and water resistance and stiffness and volume can be improved, and the non-woven fabric can be made suitable for cosmetic cotton.
【００１５】かかる不織布を内部層して、それを外装材
で包んで化粧綿となす。本発明において用いる外装材
は、直接肌に触れる部分であり、その素材としては、
綿、またはレーヨンなどの化学繊維が用いられる。[0015] The non-woven fabric is internally layered and wrapped with an exterior material to form a cosmetic cotton. The exterior material used in the present invention is a portion that directly touches the skin, and as the material,
Chemical fibers such as cotton or rayon are used.
【００１６】本発明の化粧綿の一例を第３図に示した。
３は化粧水など吸蔵用の不織布内部層で、４は外装材
で、５はシール部分である。FIG. 3 shows an example of the cosmetic cotton of the present invention.
Numeral 3 denotes an inner layer of a nonwoven fabric for storing a lotion or the like, numeral 4 denotes an exterior material, and numeral 5 denotes a sealing portion.
【００１７】このような化粧綿を得る方法としては、例
えば次の様なものがある。上記したポリエステル系短繊
維と綿とをカードマシンにより開綿し、ウェッブを形成
し、７０〜２３０℃、好ましくは９０〜１５０℃で熱セ
ットして不織布となす。その後、かかる不織布を内部層
３として、外装材４で両側からサンドイッチ状に積層
し、周辺部を所要数箇所において内部層３と外装材４を
一緒に加圧加熱してシールして化粧綿となす。As a method for obtaining such a cosmetic cotton, for example, there is the following method. The above-mentioned polyester-based short fiber and cotton are opened by a card machine to form a web, and heat-set at 70 to 230 ° C, preferably 90 to 150 ° C, to form a nonwoven fabric. Thereafter, the nonwoven fabric is laminated as an inner layer 3 on both sides of the outer material 4 in a sandwich form, and the inner layer 3 and the outer material 4 are pressurized and heated together at a required number of places at the peripheral portion to seal the fabric. Eggplant
【００１８】[0018]
【実施例】以下実施例により本発明を具体的に説明す
る。The present invention will be described in detail with reference to the following examples.
【００１９】（実施例１）次の構成からなる原綿を混綿
し、オープナー及びカードマシンによりウェッブを形成
した。その後、熱処理ドラムにより熱接着することで目
付７０ｇ／ｍ2の不織布内部層を得た。(Example 1) Raw cotton having the following constitution was mixed, and a web was formed with an opener and a card machine. Thereafter, the non-woven fabric inner layer having a basis weight of 70 g / m 2 was obtained by heat bonding with a heat treatment drum.
【００２０】 ［原綿構成］ （１）ホモポリエチレンテレフタレート短繊維 ６デニール、繊維長５１ｍｍ ３０重量％ （２）固有粘度差が０．０９である２種の主たる構成成分がポリエチレンテレフ タレートからなるサイドバイサイド型複合短繊維 ２デニール、繊維長５１ｍｍ ２５重量％ （３）ホモポリエチレンテレフタレートを芯、イソフタル酸共重合ポリエチレン テレフタレート（融点１１０℃）を鞘とした芯鞘型複合短繊維 ２デニール、繊維長５１ｍｍ １５重量％ （４）綿 ３０重量％ その後、綿とレーヨンからなる不織布を内部層の両面に
重ね、熱圧着ロールによりヒートシールし、カッターに
より切断して５ｃｍ×６ｃｍの化粧綿を得た。[Raw Cotton Composition] (1) Homopolyethylene terephthalate short fiber 6 denier, fiber length 51 mm 30% by weight (2) Side-by-side type in which two main constituent components having an intrinsic viscosity difference of 0.09 are polyethylene terephthalate 2 denier composite short fiber, fiber length 51 mm, 25% by weight (3) Core-sheath type composite short fiber 2 denier having a core of homopolyethylene terephthalate and a sheath of isophthalic acid copolymerized polyethylene terephthalate (melting point 110 ° C.), fiber length 51 mm, 15 weight % (4) Cotton 30% by weight Thereafter, a nonwoven fabric made of cotton and rayon was laminated on both sides of the inner layer, heat-sealed with a thermocompression roll, and cut with a cutter to obtain a 5 cm × 6 cm cosmetic cotton.
【００２１】得られた化粧綿について、３０人のモニタ
ーテストを行ったところ、化粧水の吸水性・耐水性に優
れ、コシ・ボリューム感の性能が優れているとの結果で
あった。結果を表１に示す。The obtained cotton wool was subjected to a monitor test by 30 persons. The results showed that the water absorption was excellent in water absorption and water resistance, and that it was excellent in stiffness and volume. Table 1 shows the results.
【００２２】（実施例２）原綿構成を次のとおりに変更
した以外は、実施例１と同様にして化粧綿を得た。(Example 2) Cosmetic cotton was obtained in the same manner as in Example 1 except that the structure of the raw cotton was changed as follows.
【００２３】 ［原綿構成］ （１）ホモポリエチレンテレフタレート短繊維 ３デニール、繊維長５１ｍｍ ３０重量％ （２）固有粘度差が０．０９である２種の主たる構成成分がポリエチレンテレフ タレートからなるサイドバイサイド型複合短繊維 ２デニール、繊維長５１ｍｍ ２５重量％ （３）ホモポリエチレンテレフタレートを芯、イソフタル酸共重合ポリエチレン テレフタレート（融点１１０℃）を鞘とした芯鞘型複合短繊維 ２デニール、繊維長５１ｍｍ １５重量％ （４）綿 ３０重量％ 実施例１と同様にモニターテストを行ったところ、化粧
水の吸水性・耐水性に優れ、コシ・ボリューム感の性能
が優れているとの結果であった。結果を表１に示す。[Raw cotton composition] (1) Homopolyethylene terephthalate short fiber 3 denier, fiber length 51 mm 30% by weight (2) Side-by-side type in which two main constituent components having an intrinsic viscosity difference of 0.09 are polyethylene terephthalate 2 denier composite short fiber, fiber length 51 mm, 25% by weight (3) Core-sheath type composite short fiber 2 denier having a core of homopolyethylene terephthalate and a sheath of isophthalic acid copolymerized polyethylene terephthalate (melting point 110 ° C.), fiber length 51 mm, 15 weight % (4) Cotton 30% by weight A monitor test was carried out in the same manner as in Example 1. As a result, the results were that water absorption and water resistance of the lotion were excellent, and that the performance of stiffness and volume was excellent. Table 1 shows the results.
【００２４】（実施例３）原綿構成を次のとおりに変更
した以外は、実施例１と同様にして化粧綿を得た。(Example 3) Cosmetic cotton was obtained in the same manner as in Example 1, except that the structure of the raw cotton was changed as follows.
【００２５】 ［原綿構成］ （１）ホモポリエチレンテレフタレート短繊維 ３デニール、繊維長５１ｍｍ ２５重量％ （２）固有粘度差が０．０７である２種の主たる構成成分がポリエチレンテレフ タレートからなるサイドバイサイド型複合短繊維 ４デニール、繊維長５１ｍｍ ３０重量％ （３）ホモポリエチレンテレフタレートを芯、イソフタル酸共重合ポリエチレン テレフタレート（融点１５０℃）を鞘とした芯鞘型複合短繊維 ４デニール、繊維長５１ｍｍ ２０重量％ （４）綿 ２５重量％ 実施例１と同様にモニターテストを行ったところ、化粧
水の吸水性・耐水性に優れ、コシ・ボリューム感の性能
が優れているとの結果であった。結果を表１に示す。[Raw cotton composition] (1) Homopolyethylene terephthalate short fiber 3 denier, fiber length 51 mm 25% by weight (2) Side-by-side type in which two main constituent components having an intrinsic viscosity difference of 0.07 are polyethylene terephthalate Composite short fiber 4 denier, fiber length 51 mm 30% by weight (3) Core-sheath type composite short fiber 4 core having homopolyethylene terephthalate as a core and isophthalic acid copolymerized polyethylene terephthalate (melting point 150 ° C.) as sheath 4 denier, fiber length 51 mm 20 weight % (4) Cotton 25% by weight A monitor test was carried out in the same manner as in Example 1. As a result, the results were that water absorption and water resistance of the lotion were excellent, and that the performance of stiffness and volume was excellent. Table 1 shows the results.
【００２６】（比較例１）原綿構成を次のとおりに変更
した以外は、実施例１と同様にして化粧綿を得た。(Comparative Example 1) Cosmetic cotton was obtained in the same manner as in Example 1 except that the structure of the raw cotton was changed as follows.
【００２７】 ［原綿構成］ （１）ホモポリエチレンテレフタレートを芯、イソフタル酸共重合ポリエチレン テレフタレート（融点１１０℃）を鞘とした芯鞘型複合短繊維 ２デニール、繊維長５１ｍｍ １５重量％ （２）綿 ８５重量％ 実施例１と同様にモニターテストを行ったところ、化粧
水の吸水性には優れているものの、コシ・ボリューム感
の性能が劣っているとの結果であった。結果を表１に示
す。[Raw Cotton Composition] (1) Core-sheath type composite short fiber having a core of homopolyethylene terephthalate and a sheath of isophthalic acid copolymerized polyethylene terephthalate (melting point 110 ° C.), 2 denier, fiber length 51 mm, 15% by weight (2) Cotton 85% by weight A monitor test was conducted in the same manner as in Example 1. As a result, it was found that although the water absorption of the lotion was excellent, the performance of stiffness and volume was inferior. Table 1 shows the results.
【００２８】（比較例２）原綿構成を次のとおりに変更
した以外は、実施例１と同様にして化粧綿を得た。(Comparative Example 2) Cosmetic cotton was obtained in the same manner as in Example 1 except that the structure of the raw cotton was changed as follows.
【００２９】 ［原綿構成］ （１）ホモポリエチレンテレフタレートを芯、イソフタル酸共重合ポリエチレン テレフタレート（融点１１０℃）を鞘とした芯鞘型複合短繊維 ２デニール、繊維長５１ｍｍ ２０重量％ （２）レーヨン短繊維 ４０重量％ （３）綿 ４０重量％ 実施例１と同様にモニターテストを行ったところ、化粧
水の吸水性には優れているものの、コシ・ボリューム感
の性能が劣っているとの結果であった。結果を表１に示
す。[Raw Cotton Composition] (1) Core-sheath type composite short fiber having a core of homopolyethylene terephthalate and a sheath of isophthalic acid copolymerized polyethylene terephthalate (melting point 110 ° C.), 2 denier, fiber length 51 mm, 20% by weight (2) Rayon Short fiber 40% by weight (3) Cotton 40% by weight A monitor test was conducted in the same manner as in Example 1. As a result, it was found that the water absorption was excellent, but the stiffness and volume feeling were poor. Met. Table 1 shows the results.
【００３０】[0030]
【表１】 [Table 1]
【００３１】[0031]
【発明の効果】本発明の化粧綿は、吸水性・耐水性に優
れるばかりか、コシ・ボリューム感のきわめて良好なも
のである。The cosmetic cotton of the present invention is not only excellent in water absorbency and water resistance, but also very good in firmness and volume.
【図１】本発明に使用する、熱処理で捲縮が顕在化する
ポリエステル系短繊維の単繊維断面図である。FIG. 1 is a cross-sectional view of a single fiber of a polyester-based short fiber used in the present invention, in which a crimp becomes apparent by heat treatment.
【図２】本発明に使用するポリエステル系バインダー短
繊維の単繊維断面図である。FIG. 2 is a single fiber cross-sectional view of a polyester binder short fiber used in the present invention.
【図３】本発明に係る化粧綿の一例を示す概略斜視図で
ある。FIG. 3 is a schematic perspective view showing an example of a cosmetic cotton according to the present invention.
１：鞘（低融点ポリエステル） ２：芯（ポリエチレンテレフタレート） ３：内部層 ４：外装材 ５：シール部 1: sheath (low melting point polyester) 2: core (polyethylene terephthalate) 3: inner layer 4: exterior material 5: seal portion
───────────────────────────────────────────────────── フロントページの続き (72)発明者 梅田 明 愛媛県伊予郡松前町大字筒井1515番地 東 レ株式会社愛媛工場内 ──────────────────────────────────────────────────続 き Continuing from the front page (72) Inventor Akira Umeda 1515 Tsutsui, Matsumae-cho, Iyo-gun, Ehime Pref.
Claims (3)
外装材とからなる化粧綿において、不織布が、次に示す
［Ａ］、［Ｂ］、［Ｃ］および［Ｄ］からなることを特
徴とする化粧綿。 ［Ａ］：単繊維の繊度が１〜５デニールである、サイド
バイサイド型複合ポリエステル系短繊維 ［Ｂ］：単繊維の繊度が０．１〜１０デニールである、
鞘成分を低融点ポリエステルとし、芯成分をポリエチレ
ンテレフタレートとする芯鞘型複合ポリエステル系短繊
維 ［Ｃ］：単繊維の繊度が１〜１０デニールである、非複
合ポリエチレンテレフタレート短繊維 ［Ｄ］：綿1. A cosmetic cotton comprising an inner layer made of a nonwoven fabric and an exterior material surrounding the inner layer, wherein the nonwoven fabric comprises the following [A], [B], [C] and [D]. Characterized by cosmetic cotton. [A]: single-fiber fineness of 1 to 5 denier, side-by-side type composite polyester short fiber [B]: single-fiber fineness of 0.1 to 10 denier,
Core-sheath type composite polyester staple fiber having a low melting point polyester as a sheath component and polyethylene terephthalate as a core component [C]: non-composite polyethylene terephthalate short fiber having a single fiber fineness of 1 to 10 denier [D]: cotton
〜３０重量％、［Ｂ］を１０〜２０重量％、［Ｃ］を２
５〜３５重量％、および［Ｄ］を２５〜３５重量％含ん
でなることを特徴とする請求項１記載の化粧綿。2. The nonwoven fabric has an [A] of 20 per weight.
-30% by weight, [B] 10-20% by weight, [C] 2%
The cosmetic cotton according to claim 1, comprising 5 to 35% by weight and 25 to 35% by weight of [D].
系短繊維が、５０〜１５０℃の熱処理により捲縮が顕在
化することを特徴とする化粧綿。3. Cosmetic cotton characterized in that the side-by-side type polyester short fiber of [A] is exposed to crimp by heat treatment at 50 to 150 ° C.