JPH09122571A - 非電導性表面の静電ラツカー塗装法 - Google Patents

非電導性表面の静電ラツカー塗装法

Info

Publication number
JPH09122571A
JPH09122571A JP8276822A JP27682296A JPH09122571A JP H09122571 A JPH09122571 A JP H09122571A JP 8276822 A JP8276822 A JP 8276822A JP 27682296 A JP27682296 A JP 27682296A JP H09122571 A JPH09122571 A JP H09122571A
Authority
JP
Japan
Prior art keywords
coating
conductive
lacquer
electrostatic
lacquered
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP8276822A
Other languages
English (en)
Other versions
JP4036495B2 (ja
Inventor
Friedrich Dipl Chem Dr Jonas
フリードリヒ・ヨナス
Udo Guntermann
ウド・グンターマン
Klaus Lerch
クラウス・レルヒ
Arthur Boehnke
アルトウール・ベーンケ
Hans Basten
ハンス・バステン
Peter Thometzek
ペーター・トメツエク
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bayer AG
Original Assignee
Bayer AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bayer AG filed Critical Bayer AG
Publication of JPH09122571A publication Critical patent/JPH09122571A/ja
Application granted granted Critical
Publication of JP4036495B2 publication Critical patent/JP4036495B2/ja
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

(57)【要約】 【課題】 良好な非電導性表面の静電ラッカー塗装法の
提供。 【解決手段】 ポリピロール、ポリアニリンまたはポリ
チオフェンの群からの有機電導性重合体からなる電導性
層を表面に適用し、この層をついで静電ラッカー塗装す
る。

Description

【発明の詳細な説明】
【０００１】本発明は、非電導性表面の静電ラッカー塗
装法に関する。
【０００２】過去数十年において、低溶媒及び／または
無溶媒の静電ラッカー塗装法は、環境問題から暫時重要
性が増してきた。粉末ラッカー塗装法は無溶媒ラッカー
塗装法の例である。この場合、熱可塑性または架橋性重
合体粉末を、ラッカー塗装すべき表面に適用し、ついで
加熱により一緒に焼結及び／または溶融してラッカーフ
ィルムを形成させる。
【０００３】金属のような電導性材料の場合、重合体粉
末及び／またはラッカーは、好ましくは静電ラッカー塗
装によって適用される。静電ラッカー塗装に必要とされ
る粉末ラッカー粒子の荷電は、粒子の高圧電極との直接
的な接触により行うことができる。更なる可能性は、摩
擦電気発生挙動を利用する摩擦での電荷の適用である。
【０００４】静電ラッカー塗装に対して、ラッカー塗装
すべき物体の表面は電導性でなければならない。プラス
チックは普通絶縁性であるから、それを静電ラッカー塗
装する前に電導性にしなければならない。この目的のた
めに、電導性充填剤例えばカーボンブラックまたは金属
酸化物をプラスチックに適用することができる。この欠
点は、カーボンブラックの場合成形部品が黒色となり、
また金属酸化物の場合非常に高程度の充填剤が必要とな
り、それが貧弱な機械的性質をもたらすということであ
る。
【０００５】プラスチック表面を電導性にする他の可能
性は、電導性ラッカーでコーテイングすることを含んで
なる。カーボンブラックを充填した電導性ラッカーを用
いる場合、これもまた表面が黒色となり、透明性及び／
または光コーテイングをもたらすのが困難となる。
【０００６】今回、有機電導性重合体が、静電ラッカー
塗装すべきプラスチックに対する電導性コーテイングと
して非常に適当であることが発見された。
【０００７】それゆえに、本発明は、ラッカー塗装に先
だって、非電導性表面を、電導性有機重合体でコーテイ
ングする、非電導性表面の静電ラッカー塗装法に関す
る。
【０００８】適当な有機重合体の例は、ポリピロール、
ポリアニリン及びポリチオフェン及び／またはその誘導
体である。非電導性表面に電導性コーテイングを付与す
るには、異なる方法が使用できる。適当な方法の例は次
の通りである。
【０００９】１．ヨ−ロッパ特許第３３９３４０号に記
述されているような３、４−ジエチレンジオキシチオフ
ェンの重合実施例を用いて、電導性重合体を、非電導性
表面上にその場で生成させる方法。
【００１０】２．電導性重合体を、微分散形及び／また
はコロイドまたは溶解形で含むラッカーで塗装する方
法。適当なコーテイング溶液の例は、トルエン、キシレ
ンまたはメチルイソブチルケトンのような溶媒中のポリ
アミン分散液［例えばインコブレンド−ラック（Ｉｎｃ
ｏｂｌｅｎｄ−ＬａｃｋR）及び／またはバ−シコン
（ＶｅｓｉｏｎR）］或いはヨ−ロッパ特許第５８９５
２９号に記述されているようなポリピロ−ルで荷電した
ラテックスである。ヨ−ロッパ特許第４４０９５７号及
び独国公開特許第４２１１４５９号に記述されているよ
うなポリチオフェン誘導体は好適である。
【００１１】これらの特許明細書に記述され且つ単量体
としての３、４−エチレンジオキシチオフェンに由来
し、更に重合体カルボン酸またはスルホン酸に由来する
ポリアニオンを含む水性ポリチオフェン分散液及び／ま
たは溶液は、特に好適である。これらの溶液を用いれ
ば、黒色のカーボンブラックを充填したコーテイングの
欠点を有さない実質的に無色で、透明な電導性コーテイ
ングが生成できる。
【００１２】本発明の方法でラッカー塗装できるプラス
チックの例は、ポリアミド、ポリスルホン、ポリカーボ
ネホト、ポリイミド、ポリエステル、ＡＢＳ、ポリスチ
レン、ポリアクリレホト、ポリ塩化ビニル及びこれらの
ブレンド及び共重合体、並びにジュロマ−例えばフェノ
ール樹脂、エポキシ樹脂、エポキシジイソシアヌレ−ト
樹脂から作られるものである。
【００１３】プラスチックは、無機材料、例えばカオリ
ンまたはガラス繊維のような通常の充填剤を含有してい
てもよい。本発明の方法によれば、羊毛例えば圧縮板パ
ネル、ガラス、酸化アルミニウムのセラミックス、窒化
ケイ素、陶器から作られた非電導性表面もラッカー塗装
できる。
【００１４】電導性重合体分散液及び／または溶液は、
単独でまたは結合剤と組み合わせて使用できる。適当な
結合剤の例は、ポリウレタン、ポリ酢酸ビニル、ポリア
クリレート、不飽和ポリエステル樹脂及び／またはこれ
らの混合物である。
【００１５】結合剤は、好ましくは水性分散液または乳
化液または溶液として使用できる。
【００１６】電導性コーテイングは、＜１０10Ω／□の
表面抵抗をもたらす量で適用され、良好な静電ラッカー
塗装を可能にする。
【００１７】一般的に言えば、０．０５−５０μｍ、好
ましくは０．１−５μｍの層の厚さがこの目的のために
必要である。
【００１８】この適用は、公知の技術で、例えば噴霧、
浸液、はけ塗り、印刷によって行われる。
【００１９】コーテイングを、適用後に乾燥する。乾燥
は、室温または２５０℃まで、好ましくは２５０℃の高
温で行われる。
【００２０】電導性重合体及び随時結合剤の水性分散液
には、低級アルコール例えばメタノール、エタノール、
イソプロパノール或いはケトン例えばアセトン或いは開
鎖または環式アミド例えばＮ−メチルピロリドンのよう
な補助溶媒を添加してもよい。
【００２１】更なる添加剤の例は、表面活性剤、例えば
長鎖脂肪族またはアラリファチックスルホン酸の塩であ
る。
【００２２】付着促進剤、例えば有機シラン例えば３−
グリシドプロピルトリメトキシシランも、付着を改善す
るために添加できる。
【００２３】ついでこのコーテイングした表面を、公知
の方法により静電ラッカー塗装する。
【００２４】好ましくは、プラスチックは粉末ラッカー
塗装される。適当な粉末ラッカー系の例は、エポキシ樹
脂粉末ラッカー、ポリアクリレ−ト粉末ラッカー、無水
カルボン酸、カルボン酸またはポリイソシアネ−トで架
橋されるヒドロキシ官能性ポリエステル、多官能性エポ
キシドで架橋されるカルボキシル官能性ポリエステル、
例えばトリグリシジルイソシアネ−トである。
【００２５】粉末ラッカーコーテイングを適用した後、
これを昇温度で一緒に焼結及び／または溶融させる。こ
の温度は、５０−３００℃、好ましくは１００−２５０
℃である。
【００２６】過去では非電導性部品を先ず他の方法によ
って別にラッカー塗装しなければならず、ついでこれを
静電ラッカー塗装した金属部品と組み合わせなければな
らなかったのに対して、金属及びプラスチックの組み合
わせ物を、静電ラッカー塗装により一つの作業工程で一
緒にラッカー塗装できるということは、本発明の方法の
大きな利点である。
【００２７】
【実施例】
実施例 １ ガラス繊維を充填したポリアミド６、６の丸いプラスチ
ック板（ガラス３０重量％）（直径６ｃｍ、厚さ３ｍ
ｍ）を、５００ｒｐｍでの遠心ラッカー塗装により次の
溶液をラッカー塗装した。
【００２８】 ３、４−ポリエチレンジオキシチオフェン／ポリスチレンスルホネ−ト溶液、 １．３％水溶液［ＡＩ４０７１，バイエル社（Ｂａｙｅｒ）］ １０.０ｇ Ｎ−メチルピロリドン ０.６ｇ ３−グリシドプロピルトリメトキシシラン ０.２ｇ イソプロパノール １２.５ｇ 水 ２.５ｇ コーテイング後、層を５０℃の温空気で乾燥した。乾燥
後、厚さ約１．０μｍの層を得た。
【００２９】このようにコーテイングした板は、３ｋΩ
／□の表面抵抗を有した。この板に、トリグリシジルイ
ソシアネ−ト［アラルジット（ＡｒａｌｄｉｔR）ＴＴ
８１０，チバ−ガイギ−社（Ｃｉｂａ−Ｇｅｉｇｙ Ａ
Ｇ）］及びカルボキシル基を含むポリエステル［ウララ
ック（ＵｒａｌａｃR）４２００、ＤＳＭ Ｎ．Ｖ．］
に基づき、結合剤に関する二酸化チタン５０％を含有す
る粉末ラッカーを静電噴霧した。このラッカー粉末は均
一且つ完全に本発明のコーテイングを被覆した。ついで
粉末ラッカーを、空気循環炉中において、１０分間１８
０℃に加熱した。
【００３０】冷却後、プラスチックに良く付着した高光
沢のラッカーコーテイングを得た［グリッド・カット
（ｇｒｉｄ ｃｕｔ）０］。
【００３１】ガラス繊維を充填したポリアミド６（ガラ
ス３０重量％）、ポリスルホン［ウデル（ＵＤＥＬR）
１７００、アムコ社（Ａｍｕｃｏ Ｉｎｃ.）製］、ガ
ラス及び酸化アルミニウムセラミックスでも、同様に良
好な結果が得られた。
【００３２】対照例 本発明によるコーテイングを含まないガラス板及びポリ
カーボネートを、粉末ラッカーで静電噴霧した。ラッカ
ー粉末はいくつかのスポットで板を被覆するにすぎなか
った。
【００３３】実施例 ２ 実施例１におけるごとく遠心ラッカー塗装により、プラ
スチック及びガラス板を次の処方物で被覆した。
【００３４】 処方物ａ） ３、４−ポリエチレンジオキシチオフェン／ポリスチレンスルホネ−ト溶液、 １．３％水溶液［ＡＩ４０７１，バイエル社（Ｂａｙｅｒ）］ ４.２０ｇ Ｎ−メチルピロリドン ０.６ｇ ポリアクリレ−ト分散液［モ−リス（ＭｏｗｌｉｔｈＲ）ＤＭ７７１， ヘキスト社（Ｈｏｅｃｈｓｔ ＡＧ）］，固体含量５０％ １.８ｇ イソプロパノ−ル ４.０ｇ 水 ２.０ｇ コーテイング後、２．５ｘ１０6Ω／□の表面抵抗を有
する厚さ約０．８μｍの層を得た。
【００３５】 処方物ｂ） ３、４−ポリエチレンジオキシチオフェン／ポリスチレンスルホネ−ト溶液、 １．３％水溶液［ＡＩ４０７１，バイエル社（Ｂａｙｅｒ）］ ８.３ｇ Ｎ−メチルピロリドン ０.５ｇ ポリ酢酸ビニル分散液［モ−リス（ＭｏｗｌｉｔｈR）ＤＣ， ヘキスト社（Ｈｏｅｃｈｓｔ ＡＧ）］，固体含量５６％ １.６ｇ イソプロパノ−ル ２.０ｇ コーテイング後、４ｘ１０7Ω／□の表面抵抗を有する厚さ約０．２μｍの層 を得た。処方物ｃ） ３、４−ポリエチレンジオキシチオフェン／ポリスチレンスルホネ−ト溶液、 １．３％水溶液［ＡＩ４０７１，バイエル社（Ｂａｙｅｒ）］ ６.０ｇ Ｎ−メチルピロリドン ０.２ｇ ポリウレタン分散液［バイヒドロ−ル（ＢａｙｈｙｄｒｏｌR）ＬＳ２９５３， バイエル社（Ｂａｙｅｒ ＡＧ）］，固体含量５０％ １.８ｇ ３−グリシドプロピルトリメトキシシラン ０.２ｇ イソプロパノ−ル ０.６ｇ コーテイング後、２ｘ１０7Ω／□の表面抵抗を有する
厚さ約０．８μｍの層を得た。
【００３６】コ−テイングを乾燥した後、実施例１にお
けるごとく板に粉末ラッカーを噴霧し、ついでラッカー
を加熱した。すべての場合に均一で、良く付着した高光
沢のラッカーコーテイングが得られた。
───────────────────────────────────────────────────── フロントページの続き (72)発明者 クラウス・レルヒ ドイツ47800クレーフエルト・ボーデルシ ユビングシユトラーセ16 (72)発明者 アルトウール・ベーンケ ドイツ47800クレーフエルト・マクデブル ガーシユトラーセ49 (72)発明者 ハンス・バステン ドイツ47839クレーフエルト・ウンテルム シユテーク66 (72)発明者 ペーター・トメツエク ドイツ47800クレーフエルト・シヤイブラ ーシユトラーセ83

Claims (4)

    【特許請求の範囲】
  1. 【請求項１】 ポリピロ−ル、ポリアニリンまたはポリ
    チオフェンの群からの有機電導性重合体からなる電導性
    層を表面に適用し、この層を公知の方法により静電的に
    ラッカー塗装することを特徴とする、非電導性表面の静
    電ラッカー塗装法。
  2. 【請求項２】 ３、４−ポリエチレンジオキシチオフェ
    ンを電導性重合体として使用する請求項１記載の方法。
  3. 【請求項３】 ３、４−ポリエチレンジオキシチオフェ
    ンを水性分散液または溶液として使用する請求項２記載
    の方法。
  4. 【請求項４】 ３、４−ポリエチレンジオキシチオフェ
    ン調製物が有機または無機結合剤も含有する請求項３記
    載の方法。
JP27682296A 1995-10-02 1996-09-30 非電導性表面の静電ラツカー塗装法 Expired - Fee Related JP4036495B2 (ja)