JPH0892046A - Hair cosmetic - Google Patents

Abstract

PURPOSE: To obtain a hair cosmetic containing each specific acrylic resin for hair dressing and an ester, excellent in setting performance and set-retaining property to the hair and capable of imparting a dazzling and charming luster to the hair. CONSTITUTION: This hair cosmetic comprises blending (A) a resin for hair dressing obtained by copolymerizing (i) 6-35wt.% monomer selected from (meth) acrylic acid and itaconic acid with (ii) 15-50wt.% 10-18C aliphatic alcohol ester of acrylic acid and/or methacrylic acid [e.g. decyl (meth)acrylate], (iii) 15-50wt.% 4-8C aliphatic alcohol ester of acrylic acid and/or methacrylic acid [e.g. n-butyl (meth)acrylate] and (iv) 0-25wt.% another vinyl-based monomer, and then neutralizing the resultant copolymer by a water-soluble basic substance, with (B) an ester (e.g. stearyl caproate) of the formula R<1> -CO-O-R<2> (R<1> , R<2> are each a 6-18C linear or branched hydrocarbon).

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a hair cosmetic composition which imparts a dazzlingly fascinating luster to hair and has an excellent set holding power.

[0002]

2. Description of the Related Art Conventionally, resins such as polyvinylpyrrolidone type polymers, acidic polyvinyl ether type polymers, acidic acrylic type polymers and cationic polymers have been used in hair cosmetics for the purpose of fixing hair. In recent years, a hair styling resin which is blended and has good solubility in liquefied petroleum gas (LPG) made of an acrylic resin alkanolamine has been developed (JP-A-3-
No. 206023, JP-A-3-203024). Also, for the purpose of giving gloss to the hair, hydrocarbon oil,
Oils and fats, polyhydric alcohols, normal temperature liquid silicone oil,
Since oils such as esters are blended, the needs for such a function have recently become extremely high. However, when an oil component is added in order to give gloss to a component having a high hair fixing power, there is a problem that the setting property is reduced (compared to the one without addition).

[0003]

[Means for Solving the Problems] The inventors of the present invention have conducted diligent research in order to overcome such problems. as a result,
It was found that by combining a specific acrylic resin alkanolamine solution and a specific ester, a hair cosmetic composition having excellent settability and also having good gloss can be obtained.
The present invention has been completed based on this finding.

That is, the present invention is a hair cosmetic characterized by containing the following component (A) and component (B).

(A) A hair styling resin obtained by copolymerizing the following polymerizable monomers a to d and neutralizing it with a water-soluble organic basic substance. a. At least one monomer selected from the group consisting of acrylic acid, methacrylic acid and itaconic acid 6.0-3
5.0% by weight b. 10 to 10 carbon atoms of acrylic acid and / or methacrylic acid
At least one monomer consisting of an ester of 18 aliphatic alcohols 15.0 to 50.0% by weight c. Acrylic acid and / or methacrylic acid having 4 to 8 carbon atoms
At least one monomer consisting of ester of aliphatic alcohol of 15.0 to 50.0% by weight d. Other vinyl monomers 15.0-50.0% by weight

(B) General formula (I):

[0007]

Embedded image R ¹ —CO—O—R ² (I)

(R ¹ and R ² represent a linear or branched hydrocarbon group having 6 to 18 carbon atoms), and one or more kinds of the ester.

Further, in the present invention, as the monomer of the component (A), a monomer to which the following e component is further added is included.

E. General formula (II):

[0011]

[Chemical 5]

(Wherein R ³ and R ⁴ are a hydrogen atom or a methyl group, R ⁵ is an alkyl group having 1 to 8 carbon atoms or C (CH ₃ ) ₂ CHCOCH ₃ ). −
At least 1 selected from alkyl-substituted acrylamide
Seed monomer 5.0 to 50.0% by weight

In the hair styling resin of the component (A) used in the present invention, the monomer a is involved in the hydrophilicity and hair washability of the resin, and the amount thereof is 6.0 to 35.0% by weight, preferably Is 10.0 to 30.0% by weight. The amount used is 6.0
If it is less than 5% by weight, the resulting film is poorly soluble in water and the hair washing property is poor, while if it exceeds 35.0% by weight, the amount of moisture absorption increases and the tackiness becomes remarkable. Monomer a
The unsaturated carboxylic acid monomer selected from the group consisting of acrylic acid, methacrylic acid and itaconic acid can be used alone or in combination.

The monomer b is involved in the lipophilicity, softness and hair washability of the resin, and its amount used is 15.0 to 50.0% by weight,
It is preferably 20.0 to 45.0% by weight. When the amount used is less than 15.0% by weight, the obtained film is hard and the flaking phenomenon easily occurs. On the other hand, it is 5
If it exceeds 0.0% by weight, the resulting film becomes very soft and becomes tacky, resulting in poor washability. Specific examples of the monomer b include, for example, decyl (meth) acrylate, lauryl (meth) acrylate, myristyl (meth) acrylate, palmityl (meth) acrylate, stearyl (meth) acrylate, oleyl (meth) acrylate, tridecyl (meth). ) A synthetic alcohol (meth) acrylate such as acrylate can be used alone or in combination.

The monomer c is also the lipophilicity and flexibility of the hair styling resin.
It is involved in hair washability, and the amount used is 15.0 to 50.0% by weight, preferably 20.0 to 45.0% by weight. When the amount used is less than 15.0% by weight, the solubility in liquefied petroleum gas becomes poor, while it is 50.0% by weight.
If it exceeds, the hair washability will be poor. Specific examples of the monomer c include, for example, n-butyl (meth) acrylate, isobutyl (meth) acrylate, tertiary butyl (meth) acrylate, n-hexyl (meth) acrylate, n-octyl (meth) acrylate, 2-Ethylhexyl (meth) acrylate and the like can be used alone or in combination. Comparing the monomer b with the monomer c, the former has a greater effect on the lipophilicity of the resin and the effect of impairing the hair washability than the latter, but the latter also contributes to the solubility in liquefied petroleum gas. Is greater. In order to further improve the solubility in liquefied petroleum gas, the total amount of the monomer b and the monomer c is preferably 41.0% by weight or more.

The monomer d is involved in the hardness of the film and the solubility in liquefied petroleum gas, and the amount used is 0 to 25.0% by weight, and is used as necessary. The amount used is preferably 1.0% by weight or more in order to obtain the desired effect sufficiently, but if it exceeds 25.0% by weight, the solubility in liquefied petroleum gas becomes poor. . Specific examples of the monomer d include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, ethoxyethyl (meth) acrylate, acrylonitrile, (meth) acrylamide, vinyl acetate, styrene,
Vinylpyrrolidone and the like can be used alone or in combination. Among the monomers d, methyl acrylate, ethyl acrylate, propyl acrylate, ethoxyethyl acrylate, acrylonitrile, acrylamide,
When vinylpyrrolidone is used, a relatively flexible film is obtained, and when methylmethacrylate, ethylmethacrylate, propylmethacrylate, ethoxyethylmethacrylate, methacrylamide, vinyl acetate, or styrene is used, it is harder and more sticky than the former. Less film is obtained.

The hair styling resin of the present invention basically copolymerizes the aforesaid weighting monomers a to d, but it is preferable to further add the following monomer e.

The monomer e contributes to the improvement of the setting force under high temperature and high humidity without impairing the solubility in liquefied petroleum gas, and adjusts the hardness of the film. The amount used is 5.0 to 50.0% by weight, preferably 10.0 to 4
It is 5.0% by weight. When the amount used is less than 5.0% by weight, there is no improvement in the set under high temperature and high humidity, while
If it exceeds 50.0% by weight, the film becomes hard and the texture is impaired. Specific examples of the monomer e include, for example, diacetone (meth) acrylamide,
N, N-dimethyl (meth) acrylamide, N-isopropyl (meth) acrylamide, N-octyl (meth)
Acrylamide and the like can be used alone or in combination. Especially when the monomer e is diacetone acrylamide, an excellent setting force can be maintained under high temperature and high humidity.

By copolymerizing these polymerizable monomers a to d or a to e, and adding a water-soluble organic basic substance to the obtained resin-containing liquid, a copolymer resin is preferably added to
It is made neutral and water-soluble at a neutralization rate of 0.0 to 100%. Examples of the water-soluble organic basic substance include aqueous ammonia, morpholine, (mono-, di- or tri) ethanolamine, (mono-, di- or tri) isopropanolamine, aminomethylpropanolamine, aminoethylpropanolamine, aminomethylpropanediol. , Aminoethylpropanediol and the like can be used alone or in combination. In particular, when an organic amine is used, a resin composition containing no water can be obtained, which is suitable for producing an aerosol that repels water. The resin composition obtained as described above has an average molecular weight of 5,000.
It is about 200,000 and can be used as the lipophilic solvent solution obtained by the above copolymerization or as a water-containing solvent system. When the hair styling resin of the component (A) is blended with the hair cosmetic composition, the blending amount is 0.1 to 30.0% by weight, preferably 1.0 to 20.0% by weight. 0.1% by weight
If it is less than 3% by weight, the desired effect cannot be obtained, and if it exceeds 30.0% by weight, stickiness may occur.

The ester of the component (B) used in the present invention is represented by the above general formula (I), and R ¹ in the formula,
R ² has 6 to 18 carbon atoms. It is a colorless to pale yellow transparent oil liquid at room temperature. If the specific structure is shown by chemical name, stearyl caproate, palmityl caprylate, myristyl caprate, lauryl laurate, decyl myristate, octyl palmitate, stearyl stearate, myristyl myristate, palmityl palmitate, stearyl stearate. Etc. The compounding amount of the ester of the component (B) is 0.
It is 01 to 40.0% by weight, preferably 0.1 to 25.0% by weight. This is because if the amount is less than 0.1% by weight, the desired effect cannot be obtained, and if the amount exceeds 40.0% by weight, no further improvement in the effect can be seen.

The dosage form of the present invention is optional and can be any one of solubilizing system, emulsifying system, powder dispersion system, oil-water two-phase system, and oil-water-powder.
Any type such as a layer system may be used, and various additives may be added to form a hair cream, a hair lotion, or a hair mist (non-gas type). Furthermore, it can be pressurized and enclosed together with a propellant to form an aerosol. As the propellant, liquefied petroleum gas (LPG) containing propane, butane and isobutane as main components, dimethyl ether and compressed gas such as carbon dioxide gas and nitrogen gas, or a mixture thereof can be used. Of these, liquefied petroleum gas (LPG) is particularly preferable. The mixing ratio of the undiluted solution containing the component (A) and the ingredient (B) and the propellant is 5 to 9 undiluted solution.
95 to 5 parts by weight of propellant is preferable to 5 parts by weight.

[0022]

EXAMPLES The present invention will be described in more detail with reference to Examples and Comparative Examples. The present invention is not limited to this. All compounding amounts are weight%.

Raw Material Production Example 1 (Production of Hairdressing Resin A) A 1-liter four-necked flask equipped with a reflux condenser, a thermometer, a glass tube for nitrogen substitution, a dropping funnel and a stirrer was charged with a.
Methacrylic acid 20%, b. Myristyl acrylate 35
%, C. 35% ethylhexyl methacrylate, d. Polymerizable monomer 200 consisting of 10% methyl methacrylate
Parts, ethyl alcohol 100 parts, polymerization initiator 0.5-4
Parts are added and polymerization is carried out for 5 hours under reflux (about 80 ° C.) under a nitrogen stream. After the polymerization, the mixture was cooled, and an ethyl alcohol solution of a water-soluble organic basic substance (aminomethyl propanol (AMP)) was added at 50 ° C. to obtain a hair styling resin A.

Raw Material Production Example 2 (Production of Hairdressing Resin B) A 1-liter four-necked flask equipped with a reflux condenser, a thermometer, a glass tube for nitrogen substitution, a dropping funnel and a stirrer was charged with a.
Methacrylic acid 20%, b. Myristyl acrylate 35
%, C. 25% ethylhexyl methacrylate, d. Methyl methacrylate 10%, e. 200 parts of a polymerizable monomer consisting of 10% of dimethylacrylamide, 100 parts of ethyl alcohol, and 0.5 to 4 parts of a polymerization initiator are added, and polymerization is carried out under a nitrogen stream under reflux (about 80 ° C.) for 5 hours. After the polymerization, the mixture was cooled, and an ethyl alcohol solution of a water-soluble organic basic substance (aminomethyl propanol (AMP)) was added at 50 ° C. to obtain a hair styling resin B.

Examples 1 and 2, Comparative Examples 1 to 5 Hair sprays were prepared according to the formulations shown in Table 1 below. In the table, the hair styling resin A and the hair styling resin B are those produced by the above-mentioned respective raw material production examples, and are the amounts converted into the resin solid content of 100%.

(1) Setting power of the obtained hair spray,
The results of evaluation of (2) set sustainability and (3) gloss are also shown in Table 1. The evaluation methods are as follows.

(1) Setting Power 50 professional panelists used each sample and sensory evaluated whether or not the setting power after coating and drying was excellent.

(2) Sustainability of set 50 expert panelists used each sample and sensory-evaluated whether or not the set ability after 6 hours of ordinary daily life was excellent.

(3) Gloss 50 professional panelists used each sample and sensory evaluated whether or not the gloss after coating and drying was excellent.

For each of the above items (1) to (3), when the number of panels that are felt to be excellent is 1 to 20, × 21 to 4
When 0 people were evaluated as Δ, when 41 to 45 people were evaluated as ◯, and when 46 to 50 people were evaluated as ⊚.

[0031]

[Table 1] ─────────────────────────────────── Examples Comparative examples ───── ── ──────────── 1 2 1 2 3 4 5 ──────────────────────────────── ──── Butylene glycol 2.0 2.0 2.0 2.0 2.0 2.0 2.0 Polyethylene (100) hydrogenated castor oil ester 1.0 1.0 1.0 1.0 1.0 1.0 1.0 Octyl myristate 5.0 5.0 5.0 − − − 5.0 Hairdressing resin A 3.0 − − 3.0 − − − Hairdressing Resin B − 3.0 − − 3.0 − − Polyvinylpyrrolidone / vinyl acetate copolymer − − − − − 3.0 3.0 Ethanol 34.0 34.0 37.0 39.0 39.0 39.0 34.0 Ion-exchanged water 5.0 5.0 5.0 5.0 5.0 5.0 5.0 LPG (4.0 kg / cm ² at20 ℃) 50.0 50.0 50.0 50.0 50.0 50.0 50.0 Perfume Appropriate amount Adequate amount Adequate amount Adequate amount Adequate amount ────────────────────── ──────────── (1) Set power ◎ ◎ × ◎ ◎ ○ △ (2) Set durability ○ ◎ × ○ ◎ ○ △ (3) Gloss ◎ ◎ ◎ △ △ △ ○ ── ──────────────────────────────────

Examples 3 and 4, Comparative Examples 6 to 10 Hair mousses were prepared according to the formulations shown in Table 2 below.
Evaluation was performed in the same manner as in Example 1.

[0033]

[Table 2] ─────────────────────────────────── Examples Comparative examples ───── ── ──────────── 3 4 6 7 8 9 10 ─────────────────────────────── ──── Propylene glycol 3.0 3.0 3.0 3.0 3.0 3.0 3.0 Polyoxyethylene (10) Polyoxypropylene (20) Decyl tetradecyl ether 3.0 3.0 3.0 3.0 3.0 3.0 3.0 Polyoxyethylene (9) Lauryl ether 1.0 1.0 1.0 1.0 1.0 1.0 1.0 Palmyl laurate 10.0 10.0 10.0 − − − 10.0 Hairdressing resin A 5.0 − − 5.0 − − − Hairdressing resin B − 5.0 − − 5.0 − − Polyvinyl alcohol / vinyl acetate copolymer − − − − − 5.0 5.0 Ethanol 10.0 10.0 10.0 10.0 10.0 10.0 10.0 Ion-exchanged water 58.0 58.0 63.0 68.0 68.0 68.0 58.0 LPG (4.0 kg / cm ^{2 at} 20 ℃) 10.0 10.0 10.0 10.0 10.0 10.0 10.0 Fragrance Amount Amount Amount Amount Amount Amount Amount Amount Amount Amount Amount ─────────────────────────────── ───── (1) Set power ◎ ◎ × ◎ ◎ ○ △ (2) Set persistence ○ ◎ × ○ ◎ ○ △ (3) Gloss ◎ ◎ ◎ △ △ △ ○ ───────── ──────────────────────────

Example 5 Hair Liquid Polyethylene Glycol 2.0% by Weight Polyoxyethylene (5) Decyl Tetradecyl Ether 2.0 Stearyl Caprate 12.0 Hairdressing Resin B 4.0 Ethanol 60.0 Ion Exchange Water 20. 0 Perfume

[0035]

As described above, the hair cosmetic composition of the present invention has excellent hair-fixing power (setting power) and fixing lasting power (setting lasting power), and has a dazzlingly fascinating luster to the hair. To give.

Claims (4)

[Claims] 1. A hair cosmetic composition comprising the following component (A) and component (B). (A) A hair styling resin obtained by copolymerizing the following polymerizable monomers a to d and neutralizing it with a water-soluble organic basic substance. a. At least one monomer selected from the group consisting of acrylic acid, methacrylic acid and itaconic acid 6.0-3
5.0% by weight b. 1 carbon atom of acrylic acid and / or methacrylic acid
At least one monomer consisting of an ester of an aliphatic alcohol of 0-18 15.0-50.0% by weight c. 4 carbon atoms of acrylic acid and / or methacrylic acid
To 8 at least one monomer consisting of an ester of an aliphatic alcohol 15.0 to 50.0% by weight d. Other vinyl monomers 0 to 25.0% by weight (B) General formula (I): embedded image R ¹ —CO—O—R ² (I) (R ¹ and R ² have carbon numbers 1 to 2 of an ester represented by 6 to 18 representing a linear or branched hydrocarbon group).
More than seeds. 2. A hair cosmetic composition comprising the following component (A) and component (B). (A) A hair styling resin obtained by copolymerizing the following polymerizable monomers a to e and neutralizing it with a water-soluble organic basic substance. a. At least one monomer selected from the group consisting of acrylic acid, methacrylic acid and itaconic acid 6.0-3
5.0% by weight b. 10 to 10 carbon atoms of acrylic acid and / or methacrylic acid
At least one monomer consisting of an ester of 18 aliphatic alcohols 15.0 to 50.0% by weight c. Acrylic acid and / or methacrylic acid having 4 to 8 carbon atoms
At least one monomer consisting of ester of aliphatic alcohol of 15.0 to 50.0% by weight d. Other vinyl monomers 0 to 25.0% by weight e. General formula (II): (In the formula, R ³ and R ⁴ are a hydrogen atom or a methyl group, R ⁵
Is an alkyl group having 1 to 8 carbon atoms or C (CH ₃ ) ₂
It is CH ₂ COCH ₃ . ) At least one monomer selected from N-alkyl-substituted acrylamides represented by
5.0 to 50.0% by weight (B) General formula (I): embedded image R ¹ —CO—O—R ² (I) (R ¹ and R ² are direct carbon atoms having 6 to 18 carbon atoms) 1 or 2 of an ester represented by a chain or branched hydrocarbon group).
More than seeds. 3. The compounding amount of the component (A) is 0.1 to 30.0.
% By weight, and the compounding amount of the component (B) is 0.01 to 40.
The hair cosmetic composition according to claim 1 or 2, which is 0% by weight. 4. An aerosol type which comprises 5 to 95 parts by weight of a stock solution which is liquid at room temperature and contains 95 to 5 parts by weight of a liquefied gas propellant, which contains the components (A) and (B). 2. The hair cosmetic composition as described in 2.