JPH08323714A - Decorative aggregate-carrying sheet, its production and sheet to carry decorative aggregate - Google Patents
Decorative aggregate-carrying sheet, its production and sheet to carry decorative aggregateInfo
- Publication number
- JPH08323714A JPH08323714A JP13169295A JP13169295A JPH08323714A JP H08323714 A JPH08323714 A JP H08323714A JP 13169295 A JP13169295 A JP 13169295A JP 13169295 A JP13169295 A JP 13169295A JP H08323714 A JPH08323714 A JP H08323714A
- Authority
- JP
- Japan
- Prior art keywords
- decorative aggregate
- binder layer
- sheet
- aggregate
- decorative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は天然石、セラミックス等
の装飾骨材で表面を装飾した各種形状のプレキャストコ
ンクリート製品、公園、街路等の現場打設景観装飾コン
クリート等の製造に使用する装飾骨材搭載シートおよび
その製造方法ならびに装飾骨材搭載用シートに関するも
のである。The present invention relates to a decorative aggregate used for producing precast concrete products of various shapes whose surfaces are decorated with decorative aggregates such as natural stones and ceramics, and on-site cast landscape decorative concrete such as parks and streets. The present invention relates to a mounting sheet, a manufacturing method thereof, and a decorative aggregate mounting sheet.
【０００２】[0002]
【従来の技術】従来、コンクリート（モルタル等も含
む）の表面を装飾骨材等で飾る方法の一つとして洗い出
し法と呼ばれる工法が用いられてきた。この洗い出し法
では、古くは、装飾骨材を練り込んだコンクリートを型
枠内等に打ち込み、コンクリートが半硬化のうちに、表
面のコンクリートを洗い流して装飾骨材の一部分を露出
させていた。近年では、装飾骨材を練り込んだコンクリ
ートを打ち込んだ後、コンクリートの表面に表面硬化遅
延剤を散布する方法が採られている。さらに、硬化遅延
シートと呼ばれる特殊なシートも用いられてきている。
これらの方法では、コンクリートの表面の硬化を遅ら
せ、コンクリートの内部のみが硬化したところで、未硬
化の表面層を洗い流して、装飾骨材の一部分を露出させ
ている。2. Description of the Related Art Conventionally, a method called a washing-out method has been used as one of the methods for decorating the surface of concrete (including mortar etc.) with decorative aggregate. In this wash-out method, concrete was kneaded with a decorative aggregate in a formwork, etc., and the concrete on the surface was washed out to expose a part of the decorative aggregate while the concrete was half hardened. In recent years, a method has been adopted in which concrete in which a decorative aggregate is kneaded is cast and then a surface hardening retarder is sprinkled on the surface of the concrete. Further, a special sheet called a curing retardation sheet has also been used.
In these methods, the hardening of the surface of the concrete is delayed, and when only the inside of the concrete has hardened, the uncured surface layer is washed away to expose a part of the decorative aggregate.
【０００３】近年、本出願人等は、コンクリートの装飾
骨材の露出に適用できる特殊な装飾骨材搭載シートとこ
れを利用した洗い出しによらない装飾骨材露出工法を提
案した（特公平７−２３９０号公報）。この装飾骨材搭
載シートは、柔軟な支持体上にホットメルト接着剤等か
らなるバインダー層を形成し、バインダー層中に装飾骨
材を部分的に埋め込んだものであり、また装飾骨材露出
工法は、装飾骨材搭載シートを型枠等に設置してコンク
リートを打ち込み、養生してから支持体、バインダー層
からなるバインダーシートを剥離して装飾骨材を露出さ
せるものである。In recent years, the present applicants have proposed a special decorative aggregate-carrying sheet applicable to the exposure of concrete decorative aggregate, and a decorative aggregate exposing method using the same, which is not washed out (Japanese Patent Publication No. 7- 2390 publication). This decorative aggregate-loaded sheet is one in which a binder layer made of a hot melt adhesive or the like is formed on a flexible support, and the decorative aggregate is partially embedded in the binder layer. Is a method in which a sheet for mounting a decorative aggregate is placed on a frame or the like, concrete is poured into the frame, and after curing, the binder sheet including the support and the binder layer is peeled off to expose the decorative aggregate.
【０００４】図３は従来の装飾骨材搭載シートの一部を
模式的に示した断面図である。図に示すように、柔軟な
支持体１上にホットメルト接着剤からなるバインダー層
２が形成され、バインダー層２中に装飾骨材３の一部が
埋没されている。FIG. 3 is a cross-sectional view schematically showing a part of a conventional decorative aggregate mounting sheet. As shown in the figure, a binder layer 2 made of a hot melt adhesive is formed on a flexible support 1, and a part of the decorative aggregate 3 is embedded in the binder layer 2.
【０００５】このような装飾骨材搭載シートにおいて
は、柔軟な支持体１上にホットメルト接着剤からなるバ
インダー層２を設けているから、バインダー層２上に装
飾骨材３を載せてバインダー層２の溶融温度まで加熱す
ると、装飾骨材３は自重でバインダー層２中に沈降す
る。In such a sheet for mounting the decorative aggregate, since the binder layer 2 made of a hot melt adhesive is provided on the flexible support 1, the decorative aggregate 3 is placed on the binder layer 2 to form the binder layer. When heated to the melting temperature of 2, the decorative aggregate 3 settles in the binder layer 2 under its own weight.
【０００６】図３に示した装飾骨材搭載シートを用いた
装飾骨材露出工法においては、図４に示すように、装飾
骨材搭載シートを型枠等に設置してコンクリート４を打
ち込み、養生してからバインダーシートを剥離して、装
飾骨材３を露出させる。In the decorative aggregate exposing method using the decorative aggregate mounting sheet shown in FIG. 3, as shown in FIG. 4, the decorative aggregate mounting sheet is placed on a mold or the like, and concrete 4 is driven in to cure. After that, the binder sheet is peeled off to expose the decorative aggregate 3.
【０００７】[0007]
【発明が解決しようとする課題】上記洗い出し法におい
ては、製品の形状に制限がある、模様や絵や文字を表現
することが困難である、環境汚染対策が必要である、熟
練を要する等の問題があった。In the above washing-out method, the shape of the product is limited, it is difficult to express patterns, pictures and characters, environmental pollution countermeasures are required, skill is required, etc. There was a problem.
【０００８】また、これらの問題は上記装飾骨材搭載シ
ート、上記装飾骨材露出工法によりほとんど解決された
が、この装飾骨材搭載シート、装飾骨材露出工法におい
ては、完成したコンクリート製品や構築物からバインダ
ーシートを除去するのに比較的大きな力を必要とする。
すなわち、溶融したバインダー層２が装飾骨材３に接触
していると、バインダー層２と装飾骨材３とが互いにぬ
れやすい場合には、バインダー層２は装飾骨材３の表面
に界面張力で拡がり這い上がるから、装飾骨材３の周囲
でバインダー層２は凹面メニスカスを形成する。このた
め、図４に示すように、装飾骨材３の表面に拡張してい
ったバインダー層２の先端部分５は装飾骨材３とコンク
リート４の間に挾まれ、コンクリート４に機械的に捕捉
されるから、先端部分５を捕捉する力がバインダーシー
トの引き剥がしに対して大きな抵抗力となる。Further, these problems have been mostly solved by the above-mentioned decorative aggregate loading sheet and the above-mentioned decorative aggregate exposing method. In this decorative aggregate loading sheet and decorative aggregate exposing method, the finished concrete product or structure is completed. Relatively high force is required to remove the binder sheet from the.
That is, when the molten binder layer 2 is in contact with the decorative aggregate 3, when the binder layer 2 and the decorative aggregate 3 are easily wetted with each other, the binder layer 2 is applied to the surface of the decorative aggregate 3 by interfacial tension. Since it spreads and creeps up, the binder layer 2 forms a concave meniscus around the decorative aggregate 3. Therefore, as shown in FIG. 4, the tip portion 5 of the binder layer 2 that has expanded to the surface of the decorative aggregate 3 is sandwiched between the decorative aggregate 3 and the concrete 4 and mechanically trapped in the concrete 4. Therefore, the force of capturing the tip portion 5 becomes a great resistance force against the peeling of the binder sheet.
【０００９】この発明は上述の課題を解決するためにな
されたもので、小さな力でバインダーシートを引き剥が
すことができる装飾骨材搭載シート、その製造方法、装
飾骨材搭載用シートを提供することを目的とする。The present invention has been made to solve the above-mentioned problems, and provides a decorative aggregate mounting sheet capable of peeling a binder sheet with a small force, a method of manufacturing the same, and a decorative aggregate mounting sheet. With the goal.
【００１０】[0010]
【課題を解決するための手段】この目的を達成するた
め、この発明においては、柔軟な支持体上に柔軟なバイ
ンダー層を形成し、上記バインダー層中に装飾骨材の一
部を埋没した装飾骨材搭載シートにおいて、上記バイン
ダー層の上記装飾骨材の周囲の表面を平坦にする。To achieve this object, in the present invention, a decoration in which a flexible binder layer is formed on a flexible support and a part of the decorative aggregate is embedded in the binder layer. In the aggregate mounting sheet, the surface of the binder layer around the decorative aggregate is flattened.
【００１１】また、柔軟な支持体上に柔軟なバインダー
層を形成し、上記バインダー層中に装飾骨材の一部を埋
没した装飾骨材搭載シートにおいて、上記バインダー層
の上記装飾骨材の周囲の表面を凸面にする。Further, in a decorative aggregate mounting sheet in which a flexible binder layer is formed on a flexible support and a part of the decorative aggregate is buried in the binder layer, the binder aggregate has a periphery of the decorative aggregate. Make the surface of the convex.
【００１２】これらの場合、上記バインダー層をホット
メルト系粘着剤で構成する。In these cases, the binder layer is composed of a hot melt adhesive.
【００１３】また、上記装飾骨材搭載シートを製造する
方法において、上記装飾骨材の表面に親水性物質を付着
せしめた後、上記装飾骨材を上記バインダー層中に部分
的に埋没せしめる。In the method for producing the decorative aggregate-loaded sheet, a hydrophilic substance is adhered to the surface of the decorative aggregate, and then the decorative aggregate is partially embedded in the binder layer.
【００１４】また、上記装飾骨材搭載シートを製造する
方法において、上記装飾骨材の表面に上記バインダー層
に対して非相溶性の粉末を付着せしめた後、上記装飾骨
材を上記バインダー層中に部分的に埋没せしめる。Further, in the method for producing the above-mentioned sheet for mounting the decorative aggregate, after the powder incompatible with the binder layer is adhered to the surface of the decorative aggregate, the decorative aggregate is added to the binder layer. It is partially buried in.
【００１５】また、上記装飾骨材搭載シートを製造する
方法において、上記バインダー層の表面に上記バインダ
ー層に対して非相溶性の粉末を一様に付着せしめた後、
上記バインダー層を溶融して上記装飾骨材を上記バイン
ダー層中に部分的に埋没せしめる。Further, in the method for producing the above-mentioned sheet for mounting the decorative aggregate, after the powder incompatible with the binder layer is uniformly attached to the surface of the binder layer,
The binder layer is melted to partially embed the decorative aggregate in the binder layer.
【００１６】また、上記装飾骨材搭載シートを製造する
方法において、上記バインダー層の溶融粘度が５０００
Ｐａ・ｓを下回らない温度で、上記装飾骨材を上記バイ
ンダー層中に部分的に埋没せしめる。In the method for producing the decorative aggregate-loaded sheet, the binder layer has a melt viscosity of 5000.
The decorative aggregate is partially embedded in the binder layer at a temperature not lower than Pa · s.
【００１７】また、柔軟な支持体上に柔軟なバインダー
層を形成した装飾骨材搭載用シートにおいて、上記バイ
ンダー層の表面にタルク粉末を一様に付着せしめる。Further, in the decorative aggregate loading sheet in which a soft binder layer is formed on a soft support, talc powder is uniformly attached to the surface of the binder layer.
【００１８】この場合、上記タルク粉末に脂肪酸の金属
塩を含有せしめる。In this case, the talc powder contains a metal salt of fatty acid.
【００１９】[0019]
【作用】この装飾骨材搭載シートにおいては、装飾骨材
近傍のバインダー層が装飾骨材とコンクリートとの間に
挾まれることがない。In this decorative aggregate mounting sheet, the binder layer in the vicinity of the decorative aggregate is not caught between the decorative aggregate and concrete.
【００２０】また、装飾骨材の表面に親水性物質を付着
せしめた後、装飾骨材をバインダー層中に部分的に埋没
せしめたときには、バインダー層は親油性であるから、
バインダー層の装飾骨材表面への這い上がりを抑えるこ
とができる。When the decorative aggregate is partially embedded in the binder layer after the hydrophilic substance is attached to the surface of the decorative aggregate, the binder layer is lipophilic,
Crawling of the binder layer onto the surface of the decorative aggregate can be suppressed.
【００２１】また、装飾骨材の表面にバインダー層に対
して非相溶性の粉末を付着せしめた後、装飾骨材をバイ
ンダー層中に部分的に埋没せしめたときには、バインダ
ー層の装飾骨材表面への這い上がりを抑えることができ
る。上記装飾骨材搭載シートを製造する方法において、
バインダー層の表面にバインダー層に対して非相溶性の
粉末を一様に付着せしめた後、バインダー層を溶融して
装飾骨材をバインダー層中に部分的に埋没せしめたとき
には、バインダー層が溶融してもバインダー層の表面を
バインダー層に対して非相溶性の粉末が被っているか
ら、バインダー層が装飾骨材との界面張力により装飾骨
材表面に拡がるのを阻害することができる。Further, when a powder which is incompatible with the binder layer is adhered to the surface of the decorative aggregate and then the decorative aggregate is partially embedded in the binder layer, the surface of the decorative aggregate of the binder layer is It is possible to suppress the creeping up to. In the method for manufacturing the decorative aggregate-loaded sheet,
When the powder that is incompatible with the binder layer is uniformly applied to the surface of the binder layer and then the binder layer is melted to partially embed the decorative aggregate in the binder layer, the binder layer melts. However, since the surface of the binder layer is covered with the powder which is incompatible with the binder layer, it is possible to prevent the binder layer from spreading to the surface of the decorative aggregate due to the interfacial tension with the decorative aggregate.
【００２２】また、バインダー層の溶融粘度が５０００
Ｐａ・ｓを下回らない温度で、装飾骨材をバインダー層
中に部分的に埋没せしめたときには、装飾骨材表面への
バインダー層の這い上がりを抑えることができる。The melt viscosity of the binder layer is 5000
When the decorative aggregate is partially embedded in the binder layer at a temperature not lower than Pa · s, it is possible to prevent the binder layer from creeping to the surface of the decorative aggregate.
【００２３】また、柔軟な支持体上に柔軟なバインダー
層を形成した装飾骨材搭載用シートにおいて、バインダ
ー層の表面にタルク粉末を一様に付着せしめたときに
は、装飾骨材をバインダー層中に部分的に埋没せしめた
ときに、バインダー層の装飾骨材表面への這い上がりを
抑えることができる。Further, in the decorative aggregate loading sheet in which a flexible binder layer is formed on a flexible support, when the talc powder is uniformly attached to the surface of the binder layer, the decorative aggregate is placed in the binder layer. When it is partially buried, the binder layer can be prevented from climbing up to the surface of the decorative aggregate.
【００２４】また、タルク粉末に脂肪酸の金属塩を含有
せしめたときには、タルク粉末で表面を処理したバイン
ダー層上に装飾骨材を載せて加熱したとき、脂肪酸の金
属塩はバインダー層の表面に薄く広がって装飾骨材とバ
インダー層との接着力を低下させる。When the talc powder contains a fatty acid metal salt, when the decorative aggregate is placed on the binder layer whose surface has been treated with the talc powder and heated, the fatty acid metal salt becomes thin on the surface of the binder layer. It spreads and reduces the adhesive strength between the decorative aggregate and the binder layer.
【００２５】[0025]
【実施例】図１は本発明に係る装飾骨材搭載シートの一
部を模式的に示した断面図である。図に示すように、柔
軟な支持体１１上にホットメルト系粘着剤からなる柔軟
なバインダー層１２が形成され、バインダー層１２中に
装飾骨材１３の一部分が埋没され、バインダー層１２の
装飾骨材１３の周囲の表面が平坦である。EXAMPLE FIG. 1 is a sectional view schematically showing a part of the decorative aggregate-mounted sheet according to the present invention. As shown in the figure, a flexible binder layer 12 made of a hot-melt adhesive is formed on a flexible support 11, and a part of the decorative aggregate 13 is embedded in the binder layer 12 to form a decorative bone of the binder layer 12. The surface around the material 13 is flat.
【００２６】図２は本発明に係る他の装飾骨材搭載シー
トの一部を模式的に示した断面図である。図に示すよう
に、柔軟な支持体１１上にホットメルト系粘着剤からな
る柔軟なバインダー層１４が形成され、バインダー層１
４中に装飾骨材１３の一部分が埋没され、バインダー層
１４の装飾骨材１３の周囲の表面が凸面である。FIG. 2 is a sectional view schematically showing a part of another decorative aggregate-carrying sheet according to the present invention. As shown in the figure, a flexible binder layer 14 made of a hot-melt adhesive is formed on a flexible support 11 to form a binder layer 1
A part of the decorative aggregate 13 is buried in the inside of No. 4, and the surface of the binder layer 14 around the decorative aggregate 13 is a convex surface.
【００２７】図１、図２に示した装飾骨材搭載シートに
おいては、装飾骨材１３の近傍のバインダー層１２、１
４が装飾骨材１３とコンクリートとの間に挾まれること
がないから、バインダー層１２、１４の一部がコンクリ
ートに機械的に捕捉されないので、バインダーシートの
引き剥がし力はバインダー層１２、１４の装飾骨材１３
およびコンクリートに対する接着力のみに依存するた
め、小さな力でバインダーシートを引き剥がすことがで
きる。また、図１、図２に示した装飾骨材１３の埋め込
み程度と図３に示した装飾骨材３の埋め込み程度とが等
しい場合には、装飾骨材１３とコンクリートとの接触面
積が装飾骨材３とコンクリートとの接触面積より大きく
なるから、コンクリートによる装飾骨材１３の保持力が
コンクリートによる装飾骨材３の保持力より大きい。In the decorative aggregate loading sheet shown in FIGS. 1 and 2, the binder layers 12, 1 in the vicinity of the decorative aggregate 13 are provided.
Since 4 is not caught between the decorative aggregate 13 and the concrete, part of the binder layers 12, 14 is not mechanically trapped in the concrete, so the peeling force of the binder sheet is Decorative aggregate 13
Also, since it depends only on the adhesive force to concrete, the binder sheet can be peeled off with a small force. When the embedding degree of the decorative aggregate 13 shown in FIGS. 1 and 2 is equal to the embedding degree of the decorative aggregate 3 shown in FIG. 3, the contact area between the decorative aggregate 13 and the concrete is the decorative bone. Since the contact area between the material 3 and the concrete is larger, the holding force of the decorative aggregate 13 by concrete is larger than the holding force of the decorative aggregate 3 by concrete.
【００２８】また、装飾骨材１３を埋め込んだバインダ
ーシートは柔軟であるから、コンクリート打設時の型枠
に装着し易く、しかもコンクリート製品等からバインダ
ーシートを除去する際に引き剥がしやすい。Further, since the binder sheet in which the decorative aggregate 13 is embedded is flexible, it is easy to mount the binder sheet on a mold at the time of placing concrete, and moreover, it is easy to peel it off when removing the binder sheet from concrete products or the like.
【００２９】なお、柔軟な支持体に適合する材料とし
て、ポリエチレンテレフタレート、延伸ポリプロピレ
ン、架橋ポリエチレン等のプラスチックフィルム、およ
び各種紙、不織布、布等よりなるシートがある。これら
の何れも使用可能であるが、機械的強度が大きく耐熱
性、耐水性に富んだポリエチレンテレフタレートのよう
なプラスチックフィルムが特に適している。Materials suitable for the flexible support include plastic films such as polyethylene terephthalate, oriented polypropylene and crosslinked polyethylene, and sheets made of various papers, non-woven fabrics, cloths and the like. Any of these can be used, but a plastic film such as polyethylene terephthalate, which has high mechanical strength and high heat resistance and water resistance, is particularly suitable.
【００３０】また、バインダー層としては、スチレン・
ブタジエン・スチレン ブロック共重合体、スチレン・
イソプレン・スチレン ブロック共重合体、スチレン・
エチレン／ブチレン・スチレン ブロック共重合体、エ
チレン・酢酸ビニル共重合体等をエラストマーとするホ
ットメルト組成物、なかでもホットメルト系粘・接着
剤、特にホットメルト系粘着剤が好適である。As the binder layer, styrene.
Butadiene / styrene block copolymer, styrene /
Isoprene / styrene block copolymer, styrene /
A hot melt composition using an ethylene / butylene / styrene block copolymer, an ethylene / vinyl acetate copolymer or the like as an elastomer, and among them, a hot melt adhesive / adhesive, particularly a hot melt adhesive is preferable.
【００３１】また、装飾骨材を埋め込んだバインダー層
の装飾骨材の周囲の表面を平坦または凸面にするには、
(１)装飾骨材の表面をバインダー層にぬれにくいように
処理する方法、(２)バインダー層の表面を装飾骨材にぬ
れにくいように処理する方法、(３)加熱して装飾骨材を
埋め込む際に装飾骨材表面に這い上がりにくいバインダ
ー層を使用する方法、(４)バインダー層が装飾骨材表面
に這い上がりにくい条件（例えば温度条件）で装飾骨材
をバインダー層に埋め込む方法等がある。To make the surface around the decorative aggregate of the binder layer in which the decorative aggregate is embedded flat or convex,
(1) A method of treating the surface of the decorative aggregate so that the binder layer does not easily get wet, (2) A method of treating the surface of the binder layer so that it does not easily get wet with the decorative aggregate, (3) Heating to give the decorative aggregate When embedding, a method of using a binder layer that does not easily creep up on the surface of the decorative aggregate, (4) a method of embedding the decorative aggregate in the binder layer under conditions (for example, temperature conditions) in which the binder layer does not easily climb up to the surface of the decorative aggregate, etc. is there.
【００３２】そして、装飾骨材の表面をバインダー層に
対してぬれにくくするには、装飾骨材の表面に水、エチ
レングリコール等の親水性物質を付着させる方法、タル
ク、炭酸カルシウム等の無機粉末や有機ポリマー粉末等
のバインダー層に対して非相溶性の粉末を装飾骨材の表
面に付着させる方法等が利用できる。In order to prevent the surface of the decorative aggregate from getting wet with the binder layer, a method of attaching a hydrophilic substance such as water or ethylene glycol to the surface of the decorative aggregate, an inorganic powder such as talc or calcium carbonate. It is possible to use a method of adhering a powder that is incompatible with the binder layer such as an organic polymer powder or the like to the surface of the decorative aggregate.
【００３３】装飾骨材の表面に親水性物質を付着させる
方法においては、バインダー層は親油性であるから、バ
インダー層の装飾骨材表面への這い上がりを抑えること
ができるので、バインダー層の装飾骨材の周囲の表面が
平坦、凸面の装飾骨材搭載シートを容易に製造すること
ができる。また、装飾骨材の表面にバインダー層に対し
て非相溶性の粉末を付着させる方法においては、バイン
ダー層の装飾骨材表面への這い上がりを抑えることがで
きるから、バインダー層の装飾骨材の周囲の表面が平
坦、凸面の装飾骨材搭載シートを製造することができ
る。なお、高温で装飾骨材を埋め込む場合には、粉末を
付着させる方法が適している。In the method of attaching the hydrophilic substance to the surface of the decorative aggregate, since the binder layer is lipophilic, it is possible to prevent the binder layer from creeping up to the surface of the decorative aggregate. It is possible to easily manufacture a decorative aggregate mounting sheet having a flat surface around the aggregate and a convex surface. Further, in the method of adhering the powder which is incompatible with the binder layer on the surface of the decorative aggregate, it is possible to suppress the creeping up of the binder layer onto the decorative aggregate surface. It is possible to manufacture a decorative aggregate-loaded sheet having a flat peripheral surface and a convex surface. When embedding the decorative aggregate at high temperature, a method of attaching powder is suitable.
【００３４】この際、粉末としては滑り性の良いタルク
などの微粉末が特に有効である。また、タルク粉末の量
が少な過ぎると、タルク粉末がバインダー層の全面を被
覆できないし、逆にタルク粉末の量が多過ぎると、タル
ク粉末の厚い層が生じて、装飾骨材がバインダー層に十
分埋没しない。したがって、バインダー層面へのタルク
粉末の付着量は３〜１０ｇ／ｍ2が適当である。At this time, as the powder, fine powder such as talc having good slipperiness is particularly effective. Further, if the amount of talc powder is too small, the talc powder cannot cover the entire surface of the binder layer, and if the amount of talc powder is too large, a thick layer of talc powder is produced, and the decorative aggregate becomes a binder layer. Not buried enough. Therefore, it is appropriate that the amount of talc powder adhered to the binder layer surface is 3 to 10 g / m 2 .
【００３５】また、タルク粉末に脂肪酸の金属塩、特に
ステアリン酸の金属塩を添加すると効果はさらに向上す
る。すなわち、ステアリン酸の金属塩をタルク粉末に添
加して使用した場合には、タルク粉末で表面を処理した
バインダー層上に装飾骨材を載せて加熱したとき、ステ
アリン酸の金属塩は表面に薄く広がって装飾骨材とバイ
ンダー層との接着力を低下させるから、バインダーシー
トの引き剥がし力を軽減させる。なお、タルク粉末に対
するステアリン酸の金属塩の添加量を２％以上にする
と、バインダーシートの引き剥がし力低減効果が顕著に
なる。また、ステアリン酸の金属塩の添加量が５〜１０
％程度でバインダーシートの引き剥がし力低減効果はほ
ぼ飽和し、これ以上添加しても効果の増大はほとんどみ
られない。しかも、ステアリン酸の金属塩の添加量がさ
らに多くなると、バインダーシートの装飾骨材保持力も
徐々に低下する。したがって、ステアリン酸の金属塩の
添加量は２〜１０％が最適である。なお、ステアリン酸
の金属塩としてはステアリン酸リチウム、ステアリン酸
ナトリウム、ステアリン酸カリウム、ステアリン酸カル
シウム、ステアリン酸マグネシウム、ステアリン酸スト
ロンチウム、ステアリン酸バリウム、ステアリン酸亜
鉛、ステアリン酸アルミニウム等を用いることができ
る。The effect is further improved by adding a metal salt of a fatty acid, especially a metal salt of stearic acid, to the talc powder. That is, when the metal salt of stearic acid is used by adding it to the talc powder, when the decorative aggregate is placed on the binder layer whose surface is treated with the talc powder and heated, the metal salt of stearic acid becomes thin on the surface. Since it spreads and the adhesive force between the decorative aggregate and the binder layer is reduced, the peeling force of the binder sheet is reduced. When the amount of the metal salt of stearic acid added to the talc powder is 2% or more, the effect of reducing the peeling force of the binder sheet becomes remarkable. Further, the addition amount of the metal salt of stearic acid is 5 to 10
%, The effect of reducing the peeling force of the binder sheet is almost saturated, and even if it is added more, the effect is hardly increased. Moreover, when the amount of the metal salt of stearic acid added is further increased, the decorative aggregate holding power of the binder sheet is gradually reduced. Therefore, the optimum addition amount of the metal salt of stearic acid is 2 to 10%. As the metal salt of stearic acid, lithium stearate, sodium stearate, potassium stearate, calcium stearate, magnesium stearate, strontium stearate, barium stearate, zinc stearate, aluminum stearate and the like can be used.
【００３６】また、バインダー層中への装飾骨材の埋め
込みをバインダー層の溶融粘度が高い温度条件で行なう
と、装飾骨材の表面へのバインダー層の這い上がりを抑
えることができる。すなわち、溶融したバインダー層の
装飾骨材表面への拡がりやすさはバインダー層の溶融粘
度に依存し、粘度が高い場合には、両者が互いにぬれや
すい物質であっても拡がりにくい。したがって、装飾骨
材がバインダー層中に沈降できる最高粘度領域、すなわ
ち最低温度領域で装飾骨材の埋め込みを行なえば、バイ
ンダー層の這い上がりを抑えることができる。この場合
の溶融粘度は約５０００Ｐａ・ｓ以上が適当である。When the embedding of the decorative aggregate in the binder layer is carried out under the temperature condition that the melt viscosity of the binder layer is high, the creeping of the binder layer onto the surface of the decorative aggregate can be suppressed. That is, the ease with which the molten binder layer spreads on the surface of the decorative aggregate depends on the melt viscosity of the binder layer, and when the viscosity is high, it is difficult for the two to spread even if they are mutually wettable substances. Therefore, by embedding the decorative aggregate in the highest viscosity region where the decorative aggregate can settle in the binder layer, that is, in the lowest temperature region, creeping up of the binder layer can be suppressed. In this case, the melt viscosity is suitably about 5000 Pa · s or more.
【００３７】また、柔軟な支持体上に柔軟なバインダー
層を形成した装飾骨材搭載用シートにおいて、バインダ
ー層の表面にタルク粉末を一様に付着せしめたときに
は、装飾骨材をバインダー層中に部分的に埋没せしめた
ときに、バインダー層の装飾骨材表面への這い上がりを
抑えることができるから、バインダー層の装飾骨材の周
囲の表面が平坦、凸面の装飾骨材搭載シートを製造する
ことができる。Further, in a decorative aggregate loading sheet having a flexible binder layer formed on a flexible support, when the talc powder is uniformly attached to the surface of the binder layer, the decorative aggregate is placed in the binder layer. Since it is possible to prevent the binder layer from creeping up to the surface of the decorative aggregate when it is partially buried, it is possible to manufacture a sheet for mounting the decorative aggregate having a flat and convex surface around the binder aggregate of the decorative aggregate. be able to.
【００３８】つぎに、具体的な実施例につきより詳細に
説明する。これらの実施例は本発明の一部を示すもので
あって、本発明がこれらに限定されないことは勿論であ
る。Next, specific examples will be described in more detail. These examples show a part of the present invention, and the present invention is not limited to them.
【００３９】（実施例１）厚さ５０μｍのポリエステル
フィルムからなる支持体にスチレン・ブタジエン・スチ
レンブロック共重合体をベースとするホットメルト系粘
着剤からなるバインダー層を０．７ｍｍの厚さに塗工し
てなる６００ｍｍ×６００ｍｍのシートを作製した。こ
のシートのバインダー層上に、平均粒径約１０μｍのタ
ルク粉末をスポンジを用いて約４ｇ／ｍ2塗布して装飾
骨材搭載用シートを作製した。この装飾骨材搭載用シー
トに平均粒径約７ｍｍの天然石を載せ、１４０℃の熱風
乾燥機にて２０分加熱して天然石をバインダー層中に沈
めた。これにより各天然石が粒径の約１／３程度バイン
ダー層中に埋没した装飾骨材搭載シートを得た。この装
飾骨材搭載シートのバインダー層の天然石の周辺の表面
は凸面であった。Example 1 A support layer made of a polyester film having a thickness of 50 μm was coated with a binder layer made of a hot-melt pressure-sensitive adhesive based on styrene / butadiene / styrene block copolymer to a thickness of 0.7 mm. A processed 600 mm × 600 mm sheet was produced. On the binder layer of this sheet, talc powder having an average particle size of about 10 μm was applied using a sponge at about 4 g / m 2 to prepare a sheet for mounting a decorative aggregate. A natural stone having an average particle size of about 7 mm was placed on the decorative aggregate loading sheet and heated in a hot air dryer at 140 ° C. for 20 minutes to sink the natural stone in the binder layer. As a result, a sheet for mounting decorative aggregate was obtained in which each natural stone was buried in the binder layer in about 1/3 of the particle size. The surface around the natural stone of the binder layer of this decorative aggregate-carrying sheet was convex.
【００４０】この装飾骨材搭載シートの天然石面を上に
して底辺６００ｍｍ×６００ｍｍの型枠に入れ、その上
にモルタルを打設し、６０℃で４時間蒸気養生してモル
タルを硬化させた。モルタル温度が室温に下がったとこ
ろでバインダーシートを引き剥がした。バインダーシー
トは手で軽く剥がすことができた。The natural stone surface of this decorative aggregate-carrying sheet was placed in a mold frame having a bottom of 600 mm × 600 mm, and mortar was placed on the mold, and steam-cured at 60 ° C. for 4 hours to cure the mortar. The binder sheet was peeled off when the mortar temperature fell to room temperature. The binder sheet could be lightly peeled off by hand.
【００４１】（実施例２）厚さ５０μｍのポリエステル
フィルムからなる支持体に実施例１と同様のホットメル
ト系粘着剤からなるバインダー層を０．５ｍｍの厚さに
塗工してなる６００ｍｍ×６００ｍｍのシートを作製
し、このシートのバインダー層上にステアリン酸マグネ
シウム７％を含む平均粒径約１０μｍのタルク粉末をス
ポンジを用いて約４ｇ／ｍ2塗布して、装飾骨材搭載用
シートを作製した。この装飾骨材搭載用シートに平均粒
径約５ｍｍの天然石を載せ、１４０℃の熱風乾燥機にて
１５分加熱して、天然石をバインダー層中に沈めた。こ
れにより各天然石が粒径の約１／３程度バインダー層中
に埋没した装飾骨材搭載シートを得た。この装飾骨材搭
載シートのバインダー層の天然石の周辺の表面はほぼ平
坦であった。(Example 2) 600 mm x 600 mm obtained by applying a binder layer made of the same hot-melt pressure-sensitive adhesive as in Example 1 to a support made of a polyester film having a thickness of 50 µm to a thickness of 0.5 mm. A sheet for mounting the decorative aggregate is produced by applying a talc powder containing 7% magnesium stearate and having an average particle size of about 10 μm on the binder layer of the sheet with a sponge at about 4 g / m 2. did. A natural stone having an average particle size of about 5 mm was placed on the decorative aggregate loading sheet and heated for 15 minutes by a hot air dryer at 140 ° C. to sink the natural stone in the binder layer. As a result, a sheet for mounting decorative aggregate was obtained in which each natural stone was buried in the binder layer in about 1/3 of the particle size. The surface around the natural stone of the binder layer of this decorative aggregate-carrying sheet was almost flat.
【００４２】この装飾骨材搭載シートの天然石面を上に
して底辺６００ｍｍ×６００ｍｍの型枠に入れ、その上
にモルタルを打設し、６０℃で４時間蒸気養生してモル
タルを硬化させた。モルタル温度が室温に下がったとこ
ろでバインダーシートを引き剥がした。バインダーシー
トは手で軽く剥がすことができた。This decorative aggregate-carrying sheet was placed in a frame having a bottom of 600 mm × 600 mm with the natural stone surface facing upward, mortar was placed on the frame, and steam-cured at 60 ° C. for 4 hours to cure the mortar. The binder sheet was peeled off when the mortar temperature fell to room temperature. The binder sheet could be lightly peeled off by hand.
【００４３】（実施例３）厚さ５０μｍのポリエステル
フィルムからなる支持体に実施例１と同様のホットメル
ト系粘着剤からなるバインダー層を０．７ｍｍの厚さに
塗工してなる６００ｍｍ×６００ｍｍの装飾骨材搭載用
シートを作製した。この装飾骨材搭載用シートのバイン
ダー層の１１０℃における溶融粘度は約６５００Ｐａ・
ｓであった。このバインダー層上に平均粒径約７ｍｍの
天然石を載せ１１０℃の熱風乾燥機にて４０分加熱し
て、天然石をバインダー層中に沈めた。この工程により
各天然石が粒径の約１／３程度バインダー層中に埋没し
た装飾骨材搭載シートを得た。この装飾骨材搭載シート
のバインダー層の天然石の周辺の表面はほぼ平坦であっ
た。(Example 3) 600 mm x 600 mm obtained by applying a binder layer made of the same hot-melt pressure-sensitive adhesive as in Example 1 to a support made of a polyester film having a thickness of 50 µm to a thickness of 0.7 mm. A sheet for mounting the decorative aggregate of was prepared. The melt viscosity of the binder layer of this decorative aggregate loading sheet at 110 ° C. is about 6500 Pa.
It was s. A natural stone having an average particle size of about 7 mm was placed on the binder layer and heated with a hot air dryer at 110 ° C. for 40 minutes to sink the natural stone into the binder layer. Through this step, a sheet for mounting the decorative aggregate in which each natural stone was buried in the binder layer to about 1/3 of the particle size was obtained. The surface around the natural stone of the binder layer of this decorative aggregate-carrying sheet was almost flat.
【００４４】（実施例４）厚さ５０μｍのポリエステル
フィルムからなる支持体に実施例１と同様のホットメル
ト系粘着剤からなるバインダー層を０．７ｍｍの厚さに
塗工してなる６００ｍｍ×６００ｍｍの装飾骨材搭載用
シートを作製した。この装飾骨材搭載用シートのバイン
ダー層上に、表面にタルク粉末を付着させた平均粒径約
７ｍｍの天然石を載せ、１４０℃の熱風乾燥機にて２０
分加熱して、天然石をバインダー層中に沈めた。これに
より各天然石が粒径の約１／３程度バインダー層中に埋
没した装飾骨材搭載シートを得た。この装飾骨材搭載シ
ートのバインダー層の天然石の周辺の表面は凸面であっ
た。(Example 4) 600 mm x 600 mm obtained by applying a binder layer made of the same hot-melt pressure-sensitive adhesive as in Example 1 to a support made of a polyester film having a thickness of 50 µm to a thickness of 0.7 mm. A sheet for mounting the decorative aggregate of was prepared. On the binder layer of this decorative aggregate loading sheet, natural stone with an average particle size of about 7 mm having talc powder adhered to the surface was placed, and a natural air dryer at 140 ° C. was used for 20 minutes.
The natural stones were submerged in the binder layer by heating for a minute. As a result, a sheet for mounting decorative aggregate was obtained in which each natural stone was buried in the binder layer in about 1/3 of the particle size. The surface around the natural stone of the binder layer of this decorative aggregate-carrying sheet was convex.
【００４５】（実施例５）厚さ５０μｍのポリエステル
フィルムからなる支持体に実施例１と同様のホットメル
ト系粘着剤からなるバインダー層を０．５ｍｍの厚さに
塗工してなる６００ｍｍ×６００ｍｍの装飾骨材搭載用
シートを作製した。この装飾骨材搭載用シートのバイン
ダー層上に、表面にエチレングリコールを付着させた平
均粒径約５ｍｍの天然石を載せ、１４０℃の熱風乾燥機
にて１５分加熱して、天然石をバインダー層中に沈め
た。これにより各天然石が粒径の約１／３程度バインダ
ー層中に埋没した装飾骨材搭載シートを得た。この装飾
骨材搭載シートのバインダー層の天然石の周辺の表面は
ほぼ平坦であった。(Example 5) 600 mm x 600 mm obtained by applying a binder layer made of the same hot-melt pressure-sensitive adhesive as in Example 1 to a support made of a polyester film having a thickness of 50 µm to a thickness of 0.5 mm. A sheet for mounting the decorative aggregate of was prepared. On the binder layer of this decorative aggregate loading sheet, natural stone with an average particle size of about 5 mm having ethylene glycol adhered on the surface is placed and heated in a hot air dryer at 140 ° C. for 15 minutes to put the natural stone in the binder layer. Submerged in. As a result, a sheet for mounting decorative aggregate was obtained in which each natural stone was buried in the binder layer in about 1/3 of the particle size. The surface around the natural stone of the binder layer of this decorative aggregate-carrying sheet was almost flat.
【００４６】（比較例１）厚さ５０μｍのポリエステル
フィルムからなる支持体に実施例１と同様のホットメル
ト系粘着剤からなるバインダー層を０．７ｍｍの厚さに
塗工してなる６００ｍｍ×６００ｍｍの装飾骨材搭載用
シートを作製した。この装飾骨材搭載用シートのバイン
ダー層上に、平均粒径約７ｍｍの天然石を載せ１４０℃
の熱風乾燥機にて２０分加熱してこの天然石をバインダ
ー層中に沈めた。バインダー層の１４０℃における溶融
粘度は約１８０Ｐａ・ｓであった。これにより各天然石
が粒径の約１／３程度バインダー層中に埋没した装飾骨
材搭載シートを得た。この装飾骨材搭載シートのバイン
ダー層が天然石の面に若干這い上がり、バインダー層の
天然石周辺の表面は凹面状であった。(Comparative Example 1) 600 mm × 600 mm obtained by applying a binder layer made of the same hot-melt pressure-sensitive adhesive as in Example 1 to a support made of a polyester film having a thickness of 50 μm to a thickness of 0.7 mm. A sheet for mounting the decorative aggregate of was prepared. A natural stone with an average particle size of about 7 mm is placed on the binder layer of this decorative aggregate loading sheet at 140 ° C.
This natural stone was submerged in the binder layer by heating for 20 minutes with a hot air drier. The melt viscosity of the binder layer at 140 ° C. was about 180 Pa · s. As a result, a sheet for mounting decorative aggregate was obtained in which each natural stone was buried in the binder layer in about 1/3 of the particle size. The binder layer of this decorative aggregate-loaded sheet crawled up slightly on the surface of the natural stone, and the surface of the binder layer around the natural stone was concave.
【００４７】この装飾骨材搭載シートの天然石面を上に
して底辺６００ｍｍ×６００ｍｍの型枠に入れ、その上
にモルタルを打設し、６０℃で４時間蒸気養生してモル
タルを硬化させた。モルタル温度が室温に下がったとこ
ろでバインダーシートを引き剥がした。このバインダー
シートの引き剥がしには実施例１〜５と比較して大きな
力を要した。The natural stone surface of this decorative aggregate-carrying sheet was placed in a mold frame having a bottom of 600 mm × 600 mm, and mortar was placed on the frame, and steam-cured at 60 ° C. for 4 hours to cure the mortar. The binder sheet was peeled off when the mortar temperature fell to room temperature. Greater force was required to peel off the binder sheet than in Examples 1 to 5.
【００４８】[0048]
【発明の効果】以上説明したように、この発明に係る装
飾骨材搭載シートにおいては、小さな力でバインダーシ
ートを引き剥がすことができる。As described above, in the decorative aggregate mounting sheet according to the present invention, the binder sheet can be peeled off with a small force.
【００４９】また、装飾骨材の表面に親水性物質を付着
せしめた後、装飾骨材をバインダー層中に部分的に埋没
せしめたときには、バインダー層の装飾骨材の周囲の表
面が平坦、凸面の装飾骨材搭載シートを容易に製造する
ことができる。When the decorative aggregate is partially embedded in the binder layer after the hydrophilic substance is adhered to the surface of the decorative aggregate, the surface of the binder layer surrounding the decorative aggregate is flat or convex. The decorative aggregate-equipped sheet can be easily manufactured.
【００５０】また、装飾骨材の表面にバインダー層に対
して非相溶性の粉末を付着せしめた後、装飾骨材をバイ
ンダー層中に部分的に埋没せしめたときには、バインダ
ー層の装飾骨材の周囲の表面が平坦、凸面の装飾骨材搭
載シートを製造することができる。When a powder incompatible with the binder layer is adhered to the surface of the decorative aggregate and then the decorative aggregate is partially embedded in the binder layer, the powder of the decorative aggregate of the binder layer is It is possible to manufacture a decorative aggregate-loaded sheet having a flat peripheral surface and a convex surface.
【００５１】また、上記装飾骨材搭載シートを製造する
方法において、バインダー層の表面にバインダー層に対
して非相溶性の粉末を一様に付着せしめた後、バインダ
ー層を溶融して装飾骨材をバインダー層中に部分的に埋
没せしめたときには、バインダー層の装飾骨材の周囲の
表面が平坦、凸面の装飾骨材搭載シートを製造すること
ができる。In the method for producing the above-mentioned sheet for mounting decorative aggregate, the powder which is incompatible with the binder layer is uniformly adhered to the surface of the binder layer, and then the binder layer is melted to melt the decorative aggregate. When is partially embedded in the binder layer, it is possible to manufacture a decorative aggregate mounting sheet having a flat and convex surface around the decorative aggregate of the binder layer.
【００５２】また、バインダー層の溶融粘度が５０００
Ｐａ・ｓを下回らない温度で、装飾骨材をバインダー層
中に部分的に埋没せしめたときには、バインダー層の装
飾骨材の周囲の表面が平坦、凸面の装飾骨材搭載シート
を容易に製造することができる。The melt viscosity of the binder layer is 5000
When the decorative aggregate is partially embedded in the binder layer at a temperature not lower than Pa · s, a sheet having a flat and convex surface around the decorative aggregate of the binder layer can be easily manufactured. be able to.
【００５３】また、柔軟な支持体上に柔軟なバインダー
層を形成した装飾骨材搭載用シートにおいて、バインダ
ー層の表面にタルク粉末を一様に付着せしめたときに
は、バインダー層の装飾骨材の周囲の表面が平坦、凸面
の装飾骨材搭載シートを製造することができる。Further, in the decorative aggregate loading sheet in which a flexible binder layer is formed on a flexible support, when talc powder is uniformly attached to the surface of the binder layer, the surroundings of the decorative aggregate of the binder layer It is possible to manufacture a sheet for mounting a decorative aggregate having a flat surface and a convex surface.
【００５４】また、タルク粉末に脂肪酸の金属塩を含有
せしめたときには、バインダーシートの引き剥がし力を
軽減させることができる。When the talc powder contains a metal salt of a fatty acid, the peeling force of the binder sheet can be reduced.
【図１】この発明に係る装飾骨材搭載シートの一部を模
式的に示した断面図である。FIG. 1 is a sectional view schematically showing a part of a sheet for mounting a decorative aggregate according to the present invention.
【図２】この発明に係る他の装飾骨材搭載シートの一部
を模式的に示した断面図である。FIG. 2 is a cross-sectional view schematically showing a part of another decorative aggregate-mounting sheet according to the present invention.
【図３】従来の装飾骨材搭載シートの一部を模式的に示
した断面図である。FIG. 3 is a cross-sectional view schematically showing a part of a conventional decorative aggregate mounting sheet.
【図４】図３に示した装飾骨材搭載シートを用いた装飾
骨材露出工法の説明図である。FIG. 4 is an explanatory view of a decorative aggregate exposing method using the decorative aggregate mounting sheet shown in FIG.
１１…支持体 １２…バインダー層 １３…装飾骨材 １４…バインダー層 11 ... Support 12 ... Binder layer 13 ... Decorative aggregate 14 ... Binder layer
───────────────────────────────────────────────────── フロントページの続き (72)発明者 岡田 佳和 神奈川県川崎市多摩区登戸3819番地 株式 会社スリオンテック内 (72)発明者 栗村 涼子 神奈川県川崎市多摩区登戸3819番地 株式 会社スリオンテック内 (72)発明者 浜口 哲夫 神奈川県川崎市多摩区登戸3819番地 株式 会社スリオンテック内 (72)発明者 小河 洋征 東京都府中市寿町１−４−３ セルテック 株式会社内 (72)発明者 石垣 和久 東京都府中市寿町１−４−３ セルテック 株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Yoshikazu Okada, 3819 Noborito, Tama-ku, Kawasaki-shi, Kanagawa Sliontech Co., Ltd. (72) Ryoko Kurimura 3819, Noboto, Tama-ku, Kawasaki, Kanagawa (72) ) Inventor Tetsuo Hamaguchi 3819 Noborito, Tama-ku, Kawasaki City, Kanagawa Prefecture Sliontech Co., Ltd. (72) Inventor Hiroyuki Ogawa 1-4-3, Kotobukicho, Fuchu, Tokyo Metropolitan Government (72) Inventor, Kazuhisa Ishigaki, Tokyo 1-4-3 Kotobuki-cho, Celtec Co., Ltd.
Claims (9)
成し、上記バインダー層中に装飾骨材の一部を埋没した
装飾骨材搭載シートにおいて、上記バインダー層の上記
装飾骨材の周囲の表面が平坦であることを特徴とする装
飾骨材搭載シート。1. A decorative aggregate-carrying sheet in which a flexible binder layer is formed on a flexible support and a part of the decorative aggregate is embedded in the binder layer, the periphery of the decorative aggregate of the binder layer. A sheet for mounting decorative aggregate, which has a flat surface.
成し、上記バインダー層中に装飾骨材の一部を埋没した
装飾骨材搭載シートにおいて、上記バインダー層の上記
装飾骨材の周囲の表面が凸面であることを特徴とする装
飾骨材搭載シート。2. A decorative aggregate-carrying sheet in which a flexible binder layer is formed on a flexible support, and a part of the decorative aggregate is embedded in the binder layer, wherein the binder layer surrounds the decorative aggregate. A sheet for mounting decorative aggregate, characterized in that the surface of is a convex surface.
からなることを特徴とする請求項１または２に記載の装
飾骨材搭載シート。3. The decorative aggregate-installed sheet according to claim 1, wherein the binder layer is made of a hot melt adhesive.
ートを製造する方法において、上記装飾骨材の表面に親
水性物質を付着せしめた後、上記装飾骨材を上記バイン
ダー層中に部分的に埋没せしめることを特徴とする装飾
骨材搭載シートの製造方法。4. The method for producing a sheet for mounting decorative aggregate according to claim 1, wherein a hydrophilic substance is adhered to the surface of the decorative aggregate, and then the decorative aggregate is placed in the binder layer. A method of manufacturing a sheet for mounting a decorative aggregate, which is characterized in that the sheet is partially buried.
ートを製造する方法において、上記装飾骨材の表面に上
記バインダー層に対して非相溶性の粉末を付着せしめた
後、上記装飾骨材を上記バインダー層中に部分的に埋没
せしめることを特徴とする装飾骨材搭載シートの製造方
法。5. The method for producing a sheet for mounting a decorative aggregate according to claim 1 or 2, wherein a powder incompatible with the binder layer is adhered to the surface of the decorative aggregate, and then the ornament. A method for producing a decorative aggregate-loaded sheet, characterized in that the aggregate is partially embedded in the binder layer.
ートを製造する方法において、上記バインダー層の表面
に上記バインダー層に対して非相溶性の粉末を一様に付
着せしめた後、上記バインダー層を溶融して上記装飾骨
材を上記バインダー層中に部分的に埋没せしめることを
特徴とする装飾骨材搭載シートの製造方法。6. The method for producing a sheet for mounting decorative aggregate according to claim 1 or 2, after a powder incompatible with the binder layer is uniformly attached to the surface of the binder layer, A method for manufacturing a decorative aggregate-carrying sheet, characterized in that the binder layer is melted to partially bury the decorative aggregate in the binder layer.
ートを製造する方法において、上記バインダー層の溶融
粘度が５０００Ｐａ・ｓを下回らない温度で、上記装飾
骨材を上記バインダー層中に部分的に埋没せしめること
を特徴とする装飾骨材搭載シートの製造方法。7. The method for producing a sheet for mounting decorative aggregate according to claim 1 or 2, wherein the binder aggregate contains the decorative aggregate at a temperature at which the melt viscosity of the binder layer does not fall below 5000 Pa · s. A method of manufacturing a sheet for mounting a decorative aggregate, which is characterized in that the sheet is partially buried.
成した装飾骨材搭載用シートにおいて、上記バインダー
層の表面にタルク粉末を一様に付着せしめたことを特徴
とする装飾骨材搭載用シート。8. A decorative aggregate loading sheet having a flexible binder layer formed on a flexible support, wherein talc powder is uniformly adhered to the surface of the binder layer. Sheet.
しめることを特徴とする請求項８に記載の装飾骨材搭載
用シート。9. The decorative aggregate loading sheet according to claim 8, wherein the talc powder contains a metal salt of a fatty acid.