JPH07279413A - Form for placing concrete and sheet for sticking on form - Google Patents
Form for placing concrete and sheet for sticking on formInfo
- Publication number
- JPH07279413A JPH07279413A JP6691794A JP6691794A JPH07279413A JP H07279413 A JPH07279413 A JP H07279413A JP 6691794 A JP6691794 A JP 6691794A JP 6691794 A JP6691794 A JP 6691794A JP H07279413 A JPH07279413 A JP H07279413A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- alkali
- concrete
- water
- formwork
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、繰返し使用のためのコ
ンクリート打設用型枠及びその型枠のコンクリート接触
面に貼付けられる型枠貼付用シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a concrete placing mold for repeated use and a mold sticking sheet stuck to the concrete contact surface of the mold.
【０００２】[0002]
【従来の技術】コンクリート打設用型枠に関して、ポリ
プロピレン等の摩擦係数の小さいシートを打設コンクリ
ートと接触する型枠表面に仮留めし、これを縁切り材と
することが行われている。2. Description of the Related Art Regarding a concrete pouring formwork, a sheet having a small coefficient of friction such as polypropylene is temporarily fastened to the surface of the formwork that comes into contact with the pouring concrete and used as an edging material.
【０００３】また、例えば特開昭６３−５５２６４号や
特開平１−１５８１７９号などの公報に見られるよう
に、シート材を透水，通気のため不織布としたり、不織
布から成る透水性のベースシートの上に、細孔を多数設
けたポリプロピレン等のフィルムを接着させたりしてお
り、透水性ないしは吸水性を持たせたシート材を打設コ
ンクリートと接触する型枠表面に貼付け、これにより型
枠の縁切りつまり剥離，脱型を容易にすると共に、打設
コンクリートの表面を緻密に美しく仕上げることが提案
されている。こうした技術は、ジャンプフォーム工法等
の繰返し使用を図る大型型枠工法において、作業効率を
向上させる上で型枠の離型性を高めることが重要である
ことから、注目されている。Further, as disclosed in, for example, JP-A-63-55264 and JP-A-1-158179, a sheet material is made of a non-woven fabric for water permeation and ventilation, or a water-permeable base sheet made of non-woven fabric. A film of polypropylene or the like with a large number of pores is adhered to the top, and a sheet material having water permeability or water absorption is attached to the surface of the formwork that comes into contact with the cast concrete. It has been proposed to facilitate edge cutting, peeling, and demolding, and to finish the surface of the cast concrete in a precise and beautiful manner. Such a technique has been attracting attention because it is important to enhance the mold releasability of the formwork in order to improve the work efficiency in a large formwork method such as a jump form construction method that is repeatedly used.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、そうし
た従来のものでは、型枠表面へ貼付けたシート材はコン
クリートを一回打設する毎に使い捨てすることになり、
コスト高になるという問題があった。そして、型枠の再
使用に際して、古いシート材を剥して新しいものに貼替
えなければならず、シート材の剥し作業，貼付け作業に
手間がかかり、作業性が悪い。However, in such a conventional one, the sheet material attached to the surface of the mold is thrown away every time concrete is placed,
There was a problem of high cost. When reusing the formwork, the old sheet material must be peeled off and replaced with a new one, which requires time and labor for peeling off and pasting the sheet material, resulting in poor workability.
【０００５】本発明は前記の事情に鑑みてなされたもの
であり、その目的は、型枠の繰り返し使用に際してシー
ト材の貼替えが不要で、施工の省力化が図れるコンクリ
ート打設用型枠及び型枠貼付用シートを提供することに
ある。The present invention has been made in view of the above circumstances, and an object of the present invention is to form a concrete pouring formwork, which does not require reattachment of sheet materials when the formwork is repeatedly used, and saves labor in construction. It is to provide a sheet for attaching a formwork.
【０００６】[0006]
【課題を解決するための手段】前記目的を達成するため
本発明は、耐アルカリ性及び耐水性のシートを型枠のコ
ンクリート接触面に貼付け、そのシートに予め凝結遅延
剤とアルカリ可溶性エマルジョンを含浸させたことを特
徴とする。In order to achieve the above object, the present invention is to apply an alkali-resistant and water-resistant sheet to a concrete contact surface of a formwork, and impregnate the sheet with a setting retarder and an alkali-soluble emulsion in advance. It is characterized by that.
【０００７】また、打設コンクリートと接触する型枠面
に貼付けられるシートであって、そのシート素材が耐ア
ルカリ性及び耐水性を有し、かつ該シートに予め凝結遅
延剤とアルカリ可溶性エマルジョンを含浸させたことを
特徴とする。[0007] Further, the sheet is a sheet to be attached to the surface of the mold which comes into contact with the cast concrete, the sheet material having alkali resistance and water resistance, and the sheet is previously impregnated with a setting retarder and an alkali-soluble emulsion. It is characterized by that.
【０００８】[0008]
【作用】本発明の作用について述べると、コンクリート
を打設後、型枠に貼付けたシートのアルカリ可溶性エマ
ルジョンが、コンクリートに含まれているアルカリ成分
によって溶解する。その一方、コンクリートが徐々に硬
化してその強度が発現されてくるが、アルカリ可溶性エ
マルジョンが溶解した後は凝結遅延剤がコンクリートと
接触し、コンクリートの表面部についてはその凝結が遅
延される。このため、コンクリートとシートとの間の付
着力が弱くなり、従ってシートを容易に剥すことが可能
で、脱型を容易に行うことができる。この型枠貼付用シ
ートは、耐アルカリ性及び耐水性のものなので、型枠の
本体を保護することができ、繰り返し使用が可能であ
る。The operation of the present invention will be described. After pouring concrete, the alkali-soluble emulsion of the sheet attached to the form is dissolved by the alkali component contained in the concrete. On the other hand, the concrete gradually hardens to develop its strength, but after the alkali-soluble emulsion is dissolved, the setting retarder comes into contact with the concrete, and the setting of the surface portion of the concrete is delayed. For this reason, the adhesive force between the concrete and the sheet is weakened, so that the sheet can be easily peeled off and the demolding can be easily performed. Since this formwork sheet is alkali and water resistant, it can protect the body of the formwork and can be used repeatedly.
【０００９】したがって、型枠を使用する毎に、凝結遅
延材及びアルカリ可溶性エマルジョンをシートへ塗布，
含浸させれば、シートを繰り返して使用でき、型枠への
シート材の貼替えが不要となる。Therefore, each time the mold is used, the set retarder and the alkali-soluble emulsion are applied to the sheet,
Once impregnated, the sheet can be used repeatedly and there is no need to reattach the sheet material to the formwork.
【００１０】[0010]
【実施例】以下、本発明の実施例につき、添付図面を参
照して説明する。図１は、本発明の好適な一実施例を示
す断面図である。同図はコンクリートをすでに打設した
状態を示している。Embodiments of the present invention will be described below with reference to the accompanying drawings. FIG. 1 is a sectional view showing a preferred embodiment of the present invention. The figure shows a state in which concrete has already been poured.
【００１１】コンクリート打設用型枠１には、打設コン
クリート５と接触する面に、耐アルカリ性及び耐水性の
シート２が貼付けられている。そして、シート２の表面
には予め凝結遅延剤３とアルカリ可溶性エマルジョン４
が含浸されている。On the concrete pouring formwork 1, an alkali-resistant and water-resistant sheet 2 is attached to the surface which comes into contact with the pouring concrete 5. The set retarder 3 and the alkali-soluble emulsion 4 are previously formed on the surface of the sheet 2.
Is impregnated.
【００１２】シート２の素材としては、ポリプロピレン
等の摩擦係数の小さいものが好ましく、耐アルカリ性及
び耐水性の素材から不織布あるいは織布を構成して、シ
ート材に透水性ないしは吸水性を持たせる。ここでは、
シート２に杉本産業の商品名「ミズニック・シート」を
使用した。このシートは、空気を内包した突起を多数形
成した合成樹脂フイルム製ベースシートに、セメント粒
子は通さない特殊な不織布を貼り合わせ、裏面を粘着処
理して離型紙を裏打ちしたものであり、離型紙をはが
し、型枠１の打設コンクリート５との接触面へ貼付ける
ようになっている。The material of the sheet 2 is preferably a material having a small friction coefficient such as polypropylene, and a non-woven fabric or a woven fabric is made of a material having alkali resistance and water resistance to impart water permeability or water absorption to the sheet material. here,
The Sugimoto Sangyo product name "Mizunikku Sheet" was used for Sheet 2. This sheet consists of a synthetic resin film base sheet with a large number of protrusions containing air, bonded with a special non-woven fabric that does not allow cement particles to pass through, and the back side is adhesively treated to line the release paper. It is designed to be peeled off and attached to the contact surface of the formwork 1 with the cast concrete 5.
【００１３】凝結遅延剤３は、これと接触する打設コン
クリート５の表面部の凝結を遅らせるためのものであ
り、例えばグルコン酸，グルコン酸ソーダ，乳酸，リグ
ニンスルホン酸，タンニン酸，フミン酸等の有機酸及び
その塩類、グルコノデルタラクトン等のラクトン類、グ
ルコース，フラクトース，ショ糖，乳糖，麦芽糖，マル
トトリース，デキストリン，グリコーゲン等の糖類、リ
ン酸，ホウ酸，ケイ弗化ソーダ等の無機酸及びその塩類
等がある。The setting retarder 3 is for delaying the setting of the surface of the cast concrete 5 which comes into contact therewith, and for example, gluconic acid, sodium gluconate, lactic acid, ligninsulfonic acid, tannic acid, humic acid, etc. Organic acids and salts thereof, lactones such as gluconodelta lactone, glucose, fructose, sucrose, lactose, maltose, maltotrise, dextrin, sugars such as glycogen, and inorganic acids such as phosphoric acid, boric acid, and sodium fluorosilicate. And its salts.
【００１４】アルカリ可溶性エマルジョン４は、アルカ
リに溶解するものの水には不溶解であり、これは凝結遅
延剤３を保護するためのものであって、コンクリート打
設前の水洗いによる掃除や降雨等により型枠１が水に濡
れたとしても当該エマルジョンが水に不溶解であるため
保護膜となり、凝結遅延剤３が流失されることはない。The alkali-soluble emulsion 4 is soluble in alkali but insoluble in water. This is for protecting the setting retarder 3, and is used for cleaning by washing with water before placing concrete or by rainfall. Even when the mold 1 is wet with water, the emulsion is insoluble in water and thus serves as a protective film, so that the setting retarder 3 is not washed away.
【００１５】凝結遅延剤３とアルカリ可溶性エマルジョ
ン４とは、予め混合しておいて、その混合物をシート２
に塗布するようにしてもよい。もちろん、先に凝結遅延
剤３を塗布し、その上にアルカリ可溶性エマルジョン４
を塗布すればよく、アルカリ可溶性エマルジョン４が最
表層となるように形成すればよい。The setting retarder 3 and the alkali-soluble emulsion 4 are mixed in advance, and the mixture is mixed into the sheet 2.
You may make it apply | coat to. Of course, the setting retarder 3 is applied first, and then the alkali-soluble emulsion 4 is applied.
May be applied, and the alkali-soluble emulsion 4 may be formed as the outermost layer.
【００１６】コンクリート５を打設すると、コンクリー
ト５に含まれているアルカリ成分によってアルカリ可溶
性エマルジョン４が溶解する。この溶解は数分から十数
分で進行し、その一方、コンクリート５が徐々に硬化し
てその強度が発現されてくるが、アルカリ可溶性エマル
ジョン４が溶解した後は凝結遅延剤３がコンクリート５
と接触することになるので、コンクリート５の表面部に
ついてはその凝結が遅延される。このため、コンクリー
ト５とシート２との間の付着力が弱くなり、養生を充分
に行った後でもシート２を容易に剥すことが可能で、脱
型を容易に行うことができる。When the concrete 5 is poured, the alkali-soluble emulsion 4 is dissolved by the alkali component contained in the concrete 5. This dissolution proceeds in a few minutes to a dozen minutes, while the concrete 5 is gradually hardened to develop its strength, but after the alkali-soluble emulsion 4 is dissolved, the setting retarder 3 is added to the concrete 5
As a result, the setting of the surface of the concrete 5 is delayed. For this reason, the adhesive force between the concrete 5 and the sheet 2 is weakened, the sheet 2 can be easily peeled off even after sufficient curing, and the demolding can be easily performed.
【００１７】そして、シート２は、耐アルカリ性及び耐
水性のものなので、型枠１の本体を保護することができ
る。また、シート２に透水性ないしは吸水性を持たせて
あるので、コンクリート５の養生時には、当該コンクリ
ート中の余剰水と気泡がシート２を介して外部へ排出さ
れることになる。このため、打設コンクリート表層部の
余剰水が速やかに抜けて水セメント比が減少し、強度の
発現が早まり、早期に脱型することが可能になると共
に、気泡アバタの発生を抑止することができ、コンクリ
ート表面を緻密に美しく仕上げることができる。Since the sheet 2 has alkali resistance and water resistance, the main body of the mold 1 can be protected. Further, since the sheet 2 is made to be water-permeable or water-absorbent, when the concrete 5 is cured, excess water and bubbles in the concrete are discharged to the outside through the sheet 2. For this reason, surplus water in the surface layer of the cast concrete is quickly drained, the water-cement ratio is reduced, the strength development is accelerated, and the mold can be released early, and the occurrence of bubble avatars can be suppressed. The concrete surface can be finely and beautifully finished.
【００１８】このように、シート２それ自体は耐アルカ
リ性及び耐水性のものなので、繰り返しの使用が可能で
あり、再使用に際して型枠１から剥す手間がもちろん不
要で、型枠１を使用する毎に、凝結遅延材３及びアルカ
リ可溶性エマルジョン４をシート２へ塗布，含浸させれ
ば、繰り返して使用でき、シート材貼替えの手間が省け
て作業性に優れ、コストダウン，施工の省力化が図れ
る。As described above, since the sheet 2 itself has alkali resistance and water resistance, it can be used repeatedly, and it is not necessary to peel it off from the mold 1 for reuse, and each time the mold 1 is used. In addition, if the set retarder 3 and the alkali-soluble emulsion 4 are applied and impregnated on the sheet 2, it can be used repeatedly, the work of replacing the sheet material can be saved, workability is excellent, cost reduction and labor saving of construction can be achieved. .
【００１９】[0019]
【発明の効果】以上詳細に説明したように、本発明にか
かるコンクリート打設用型枠及び型枠貼付用シートによ
れば、コンクリートを打設後、型枠に貼付けたシートの
アルカリ可溶性エマルジョンが、コンクリートに含まれ
ているアルカリ成分によって溶解し、その一方、コンク
リート硬化に伴いその強度が発現されてくるが、アルカ
リ可溶性エマルジョンが溶解した後は凝結遅延剤がコン
クリートと接触し、コンクリートの表面部についてはそ
の凝結が遅延される。このため、コンクリートとシート
との間の付着力が弱くなり、養生を充分に行った後でも
シートを容易に剥すことが可能で、脱型を容易に行うこ
とができるので、型枠の繰り返し使用には有効である。
この型枠貼付用シートは、耐アルカリ性及び耐水性のも
のなので、型枠の本体を保護することができ、型枠の転
用回数を増大することができる。そして、型枠を使用す
る毎に、凝結遅延材及びアルカリ可溶性エマルジョンを
シートへ塗布，含浸させれば、シートは繰り返して使用
でき、型枠に対するシート材貼替えの手間が省けて作業
性に優れ、コストダウン，施工の省力化が図れる。As described in detail above, according to the concrete pouring formwork and the formwork pasting sheet according to the present invention, the alkali-soluble emulsion of the sheet pasted on the formwork after pouring concrete , It is dissolved by the alkaline component contained in the concrete, while its strength is developed as the concrete hardens, but after the alkali-soluble emulsion is dissolved, the set retarder comes into contact with the concrete and the surface of the concrete For that the setting is delayed. For this reason, the adhesive force between the concrete and the sheet is weakened, the sheet can be easily peeled off even after sufficient curing, and the mold can be easily removed. Is effective for.
Since the sheet for applying a mold is resistant to alkali and water, the main body of the mold can be protected and the number of times the mold can be diverted can be increased. Then, each time the mold is used, if the set retarder and the alkali-soluble emulsion are applied and impregnated on the sheet, the sheet can be used repeatedly, and the work of replacing the sheet material on the mold can be saved and workability is excellent. Cost reduction and labor saving of construction can be achieved.
【図１】本発明の一実施例を示す断面図である。FIG. 1 is a sectional view showing an embodiment of the present invention.
１ 型枠 ２ シート ３ 凝結遅延剤 ４ アルカリ可溶性エマルジョン ５ コンクリート 1 Formwork 2 Sheet 3 Set retarder 4 Alkali-soluble emulsion 5 Concrete
───────────────────────────────────────────────────── フロントページの続き (72)発明者 三谷 一房 東京都清瀬市下清戸４丁目640番地 株式 会社大林組技術研究所内 (72)発明者 曽根 隆之 東京都千代田区神田司町２丁目３番地 株 式会社大林組東京本社内 ─────────────────────────────────────────────────── ─── Continuation of front page (72) Inventor Ichibo Mitani 4-640 Shimoseido, Kiyose-shi, Tokyo Inside Obayashi Institute of Technology Co., Ltd. Company Obayashi Tokyo Head Office
Claims (2)
のコンクリート接触面に貼付け、該シートに予め凝結遅
延剤とアルカリ可溶性エマルジョンを含浸させたことを
特徴とするコンクリート打設用型枠。1. A concrete pouring formwork characterized in that an alkali-resistant and water-resistant sheet is attached to a concrete contact surface of a formwork, and the sheet is previously impregnated with a setting retarder and an alkali-soluble emulsion.
付けられるシートであって、該シート素材が耐アルカリ
性及び耐水性を有し、かつ該シートに予め凝結遅延剤と
アルカリ可溶性エマルジョンを含浸させたことを特徴と
する型枠貼付用シート。2. A sheet to be applied to the surface of a mold which comes into contact with cast concrete, wherein the sheet material has alkali resistance and water resistance, and the sheet is previously impregnated with a setting retarder and an alkali-soluble emulsion. A sheet for pasting formwork, which is characterized by