JPH08226495A - Toothed belt - Google Patents
Toothed beltInfo
- Publication number
- JPH08226495A JPH08226495A JP3195095A JP3195095A JPH08226495A JP H08226495 A JPH08226495 A JP H08226495A JP 3195095 A JP3195095 A JP 3195095A JP 3195095 A JP3195095 A JP 3195095A JP H08226495 A JPH08226495 A JP H08226495A
- Authority
- JP
- Japan
- Prior art keywords
- denier
- synthetic fiber
- yarn
- thermoplastic synthetic
- toothed belt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は歯付ベルトに関し、特に
基布の摩耗強力に優れた歯付ベルトに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a toothed belt, and more particularly to a toothed belt having a base cloth excellent in abrasion strength.
【0002】[0002]
【従来の技術】従来から、歯付ベルトの耐久性向上を目
的に基布の摩耗強力を改善する提案がなされており、例
えば、実公昭58−50135号公報には経糸と緯糸の
単糸デニール並びに布密度等を限定することにより基布
の摩耗強力等を改善することが開示されているが、さら
に基布の摩耗強力を改善したものが要求されている。2. Description of the Related Art Conventionally, it has been proposed to improve the wear strength of a base fabric for the purpose of improving the durability of a toothed belt. For example, Japanese Utility Model Publication No. 58-50135 discloses a single yarn denier of warp and weft. Further, it is disclosed that the wear strength and the like of the base cloth is improved by limiting the cloth density and the like, but there is a demand for further improvement of the wear strength and the like of the base cloth.
【0003】[0003]
【発明が解決しようとする課題】本発明の目的はかかる
要求に応えた歯付ベルトを提供するものである。SUMMARY OF THE INVENTION An object of the present invention is to provide a toothed belt that meets such a demand.
【0004】[0004]
【課題を解決するための手段】本発明は、歯付ベルトの
噛合面に貼着する基布が、単糸デニールが10〜840
デニールの熱可塑性合成繊維フィラメント糸(A)と熱
可塑性合成繊維マルチフィラメント仮撚加工糸(B)の
交織物であって、該交織物の表面積の50%以上が熱可
塑性合成繊維フィラメント糸(A)で構成されてなるこ
とを特徴とする歯付けベルト、である。SUMMARY OF THE INVENTION In the present invention, the base fabric to be attached to the meshing surface of the toothed belt has a single yarn denier of 10 to 840.
A woven fabric of a denier thermoplastic synthetic fiber filament yarn (A) and a thermoplastic synthetic fiber multifilament false twisted yarn (B), wherein 50% or more of the surface area of the woven fabric is the thermoplastic synthetic fiber filament yarn (A). ) Is a toothed belt, characterized in that.
【0005】基布に用いる糸条の太さ(トータルデニー
ル)と基布強力との関連については実公昭58−501
35号公報等で知られているが、本発明のように同じト
ータルデニールでも単糸デニールが違うと摩耗強力が変
化することについては知られておらず、又、従来用いら
れている単糸デニールの上限は6デニール程度であり、
本発明のように単糸デニールが10デニール以上のもの
を用いるという思想も皆無であった。Regarding the relation between the thickness of the yarn used for the base cloth (total denier) and the strength of the base cloth, it is described in Japanese Utility Model Publication No. 58-501.
No. 35, etc., it is not known that the wear strength changes when the single yarn denier is different even with the same total denier as in the present invention, and the conventionally used single yarn denier. The upper limit of is about 6 denier,
There was no idea of using a single yarn denier of 10 denier or more as in the present invention.
【0006】尚、実公昭58−50135号公報には経
糸と緯糸の単糸デニールの関係について開示されている
が、その理由は織物のストレッチを大きくするためのも
のであり、本発明の技術思想とは全く異なったものであ
る。本発明で用いられる熱可塑性合成繊維フィラメント
糸(A)は、単糸デニールが10〜840デニール、好
ましくは50〜420デニールである必要があり、マル
チフィラメント糸又はモノフィラメント糸で、さらには
両者の複合糸であることが好ましい。10デニール未満
では本発明の目的が達成されず、840デニールを越え
ると基布厚みが厚くなりすぎて歯付ベルトの成形が困難
となる。[0006] Incidentally, Japanese Utility Model Publication No. 58-50135 discloses the relationship between the single yarn denier of the warp and the weft. The reason is to increase the stretch of the woven fabric, and the technical idea of the present invention. Is completely different from. The thermoplastic synthetic fiber filament yarn (A) used in the present invention needs to have a single yarn denier of 10 to 840 denier, preferably 50 to 420 denier, and is a multifilament yarn or a monofilament yarn, and further a composite of both. It is preferably a thread. If it is less than 10 denier, the object of the present invention cannot be achieved, and if it exceeds 840 denier, the thickness of the base fabric becomes too thick, and it becomes difficult to form the toothed belt.
【0007】又、トータルデニールとしては100〜8
40デニール好ましくは200〜420デニールがよ
く、100デニール未満では基布の強力不足、840デ
ニールを越えると基布厚みが厚くなりすぎて歯付ベルト
の成形が困難になることがある。素材としてはナイロン
6、ナイロン66、芳香族ポリアミド、ポリエステル等
公知の素材を用いればよく、必要に応じて艶消し剤、顔
料、光安定剤、熱安定剤、酸化防止剤、帯電防止剤、接
着性向上剤等を添加していてもよい。又、単糸断面は丸
型及びY型、L型、三角等の異型断面を用いてもよい。The total denier is 100 to 8
40 denier is preferably 200 to 420 denier, and if it is less than 100 denier, the strength of the base cloth is insufficient, and if it exceeds 840 denier, the base cloth may be too thick and it may be difficult to form the toothed belt. As the material, known materials such as nylon 6, nylon 66, aromatic polyamide and polyester may be used, and if necessary, matting agent, pigment, light stabilizer, heat stabilizer, antioxidant, antistatic agent, adhesive A property improver or the like may be added. Further, as the cross section of the single yarn, an irregular cross section such as a round shape, a Y shape, an L shape, and a triangle may be used.
【0008】一方、熱可塑性合成繊維マルチフィラメン
ト仮撚加工糸(B)はストレッチ性があればよく、素材
としては熱可塑性合成繊維フィラメント糸(A)と同様
でよく、又、単糸デニールは3〜50デニール好ましく
は6〜30デニール、トータルデニールは100〜84
0デニール好ましくは200〜630デニールが本発明
の目的達成上好ましい。On the other hand, the thermoplastic synthetic fiber multifilament false twist textured yarn (B) may be stretchable, the material may be the same as the thermoplastic synthetic fiber filament yarn (A), and the single yarn denier is 3 -50 denier, preferably 6-30 denier, total denier 100-84
0 denier, preferably 200 to 630 denier is preferred for achieving the object of the present invention.
【0009】本発明では、経糸又は緯糸の一方に熱可塑
性合成繊維フィラメント糸(A)を用い、他方に熱可塑
性合成繊維マルチフィラメント仮撚加工糸(B)を用い
て交織したものであるが(歯付ベルトにおいては、熱可
塑性合成繊維フィラメト糸(A)が歯付ベルトの幅方向
に、熱可塑性合成繊維マルチフィラメント仮撚加工糸
(B)は歯付ベルトの長さ方向になるように配置され
る。) 本発明では交織物の表面積の50%以上、好ましくは6
0〜80%が熱可塑性合成繊維フィラメント糸(A)で
構成されていることに特徴があり、これ未満では本発明
の目的が達成されない。50%以上の表面積にするには
2/2以上の綾組織や朱子組織を利用すればよい。According to the present invention, the thermoplastic synthetic fiber filament yarn (A) is used for one of the warp yarn and the weft yarn, and the thermoplastic synthetic fiber multifilament false twisted yarn (B) is used for the other yarn (the yarn is woven). In the toothed belt, the thermoplastic synthetic fiber filamentate yarn (A) is arranged in the width direction of the toothed belt, and the thermoplastic synthetic fiber multifilament false twisting yarn (B) is arranged in the longitudinal direction of the toothed belt. In the present invention, 50% or more of the surface area of the mixed woven fabric, preferably 6
It is characterized in that 0 to 80% is composed of the thermoplastic synthetic fiber filament yarn (A), and if it is less than this, the object of the present invention is not achieved. To obtain a surface area of 50% or more, a twill structure or satin structure of 2/2 or more may be used.
【0010】又、基布の密度は、従来公知の範囲内で適
宜選定すればよく、例えば、経糸密度並びに緯糸密度と
もに50〜120本/インチ好ましくは60〜100本
/インチがよい。The density of the base cloth may be appropriately selected within a conventionally known range. For example, both the warp density and the weft density are 50 to 120 yarns / inch, preferably 60 to 100 yarns / inch.
【0011】[0011]
【実施例】以下、本発明を実施例で具体的に説明する。
尚、実施例に示した特性の測定方法は下記の通りであ
る。 摩耗強力;JISL−1096 6.17.3摩耗強
さC法(テーバ形法)に準じ、500回摩耗後の引張り
強さ保持率で示す。EXAMPLES The present invention will be specifically described below with reference to examples.
The method of measuring the characteristics shown in the examples is as follows. Abrasion strength: According to JIS L-1096 6.17.3 Abrasion strength C method (Taber type method), the tensile strength retention rate after 500 times abrasion is shown.
【0012】[0012]
【実施例1】経糸に単糸デニールが6〜105デニール
と異なる(トータルデニールは420d一定)ナイロン
66マルチフィラメント糸を用い、緯糸に630d/1
05fのナイロン66マルチフィラメント仮撚加工糸を
用いて2/2綾織物(経糸密度60本/インチ、緯糸密
度58本/インチ;経糸の表面積50%)を作製した。Example 1 Nylon 66 multifilament yarn having a single yarn denier different from 6 to 105 denier (total denier is constant at 420 d) is used for the warp, and 630 d / 1 for the weft.
A 2/2 twill fabric (warp density 60 yarns / inch, weft yarn density 58 yarns / inch; surface area of warp 50%) was produced using 05f nylon 66 multifilament false twisted yarn.
【0013】得られた綾織物は何れも摩耗前の引張り強
力は経方向並びに緯方向共に260kg/3cm幅であ
った。得られた綾織物の摩耗強力は、単糸デニールが1
0デニール以上の、10デニールは50%、60デニー
ルは70%、105デニールは80%と優れたものであ
ったが、10デニール未満の、単糸デニールが6デニー
ルでは35%と劣ったものであった。Each of the obtained twill fabrics had a tensile strength before abrasion of 260 kg / 3 cm width in both warp and weft directions. The abrasion strength of the obtained twill fabric is 1 yarn denier.
It was excellent with 0 denier or more, 10 denier 50%, 60 denier 70%, 105 denier 80%, but less than 10 denier, single yarn denier 35 denier with 35%. there were.
【0014】[0014]
【実施例2】経糸に420d/7f(単糸デニール60
デニール)のナイロン66マルチフィラメント糸を用
い、緯糸に630d/105fのナイロン66マルチフ
ィラメント仮撚加工糸を用いて1/3綾織物(経糸の表
面積25%)、3/1綾織物(経糸の表面積75%)、
5枚朱子織物(経糸の表面積80%)を作製した(何れ
の織物も経糸密度60本/インチ、緯糸密度58本/イ
ンチ)。[Example 2] 420d / 7f (single yarn denier 60)
(Denier) nylon 66 multifilament yarn and 630d / 105f nylon 66 multifilament false twisted yarn are used as weft yarns 1/3 twill fabric (25% surface area of warp), 3/1 twill fabric 75%),
A five-ply satin woven fabric (surface area of warp 80%) was prepared (both woven fabrics have a warp density of 60 yarns / inch and a weft yarn density of 58 yarns / inch).
【0015】得られた織物の摩耗強力は、経糸の表面積
が50%以上の、表面積75%では80%、表面積80
%では85%と優れたものであったが、表面積50%未
満の、表面積25%では40%と劣ったものであった。The abrasion strength of the obtained woven fabric is 80% when the surface area of the warp is 50% or more, 80% when the surface area is 75%, and the surface area is 80%.
%, The surface area was excellent at 85%, but the surface area was less than 50%, and the surface area at 25% was inferior at 40%.
【0016】[0016]
【発明の効果】本発明の歯付ベルトは、従来のものと比
較して、基布の摩耗強力に優れたものである。EFFECTS OF THE INVENTION The toothed belt of the present invention is superior in the abrasion strength of the base fabric as compared with the conventional belt.
Claims (1)
単糸デニールが10〜840デニールの熱可塑性合成繊
維フィラメント糸(A)と熱可塑性合成繊維マルチフィ
ラメント仮撚加工糸(B)の交織物であって、該交織物
の表面積の50%以上が熱可塑性合成繊維フィラメント
糸(A)で構成されてなることを特徴とする歯付ベル
ト。1. A base cloth to be attached to the meshing surface of a toothed belt,
A woven fabric of a thermoplastic synthetic fiber filament yarn (A) having a single yarn denier of 10 to 840 denier and a thermoplastic synthetic fiber multifilament false twisted yarn (B), and 50% or more of the surface area of the woven fabric is heat. A toothed belt comprising a synthetic synthetic fiber filament yarn (A).