JPH0820530A - Plaster substrate for percutaneous medicine - Google Patents
Plaster substrate for percutaneous medicineInfo
- Publication number
- JPH0820530A JPH0820530A JP17472294A JP17472294A JPH0820530A JP H0820530 A JPH0820530 A JP H0820530A JP 17472294 A JP17472294 A JP 17472294A JP 17472294 A JP17472294 A JP 17472294A JP H0820530 A JPH0820530 A JP H0820530A
- Authority
- JP
- Japan
- Prior art keywords
- resin layer
- transdermal drug
- layer
- transdermal
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、例えばパップ剤等の経
皮薬層を形成するための貼付による経皮薬用基材に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a base material for transdermal drug delivery, which is applied to form a transdermal drug layer such as a poultice.
【０００２】[0002]
【従来の技術】貼着用経皮薬における経皮薬層を形成す
るための経皮薬用基材としては、綿、レーヨン及び合成
繊維等の不織布や織布そのものを利用したり、あるい
は、これらの不織布や織布からなる基材シートに発泡ポ
リウレタン又はポリウレンの樹脂層を形成したものを利
用している。2. Description of the Related Art Non-woven fabrics and woven fabrics such as cotton, rayon and synthetic fibers can be used as a transdermal drug base for forming a transdermal drug layer in an adhesive transdermal drug patch, or A base sheet made of a non-woven fabric or a woven fabric and having a resin layer of foamed polyurethane or polyurene is used.
【０００３】そして、貼付による経皮薬用基材の片面に
経皮薬と接着剤とを含有する経皮薬層をコーティングに
よって形成した後、該経皮薬層面にシリコーン塗工フィ
ルム等のライナー（剥離シート）を積層したものを、貼
着用経皮薬として使用している。Then, a transdermal drug layer containing a transdermal drug and an adhesive is formed on one surface of a transdermal drug substance by sticking by coating, and then a liner such as a silicone coating film ( A laminate of release sheets) is used as a transdermal patch.
【０００４】かかる構成による貼着用経皮薬の使用は、
該貼着用経皮薬からライナーを引き剥すことによって、
経皮薬と接着剤とを含有する経皮薬層を露出させた上
で、該経皮薬層面を皮膚の所定面に当接し、貼着して行
なっている。The use of the transdermal patch for attachment having such a constitution is as follows.
By peeling the liner from the adhesive transdermal drug,
The transdermal drug layer containing the transdermal drug and the adhesive is exposed, and then the surface of the transdermal drug layer is brought into contact with a predetermined surface of the skin and affixed thereto.
【０００５】[0005]
【発明が解決しようとする課題】ところで、前述の構成
による貼着用経皮薬に利用されている経皮薬用基材は、
以下のような欠点を有している。By the way, the transdermal drug base material used in the transdermal patch for adhesion according to the above-mentioned constitution is
It has the following drawbacks.
【０００６】すなわち、綿、レーヨン及び合成繊維等に
よる不織布や織布そのものからなる貼付による経皮薬用
基材は、経皮薬層を形成する面が粗面であるため、ま
た、不織布や織布からなる基材シートに発泡ポリウレタ
ン又はポリウレンの樹脂層を形成した貼付による経皮薬
用基材は、発泡ポリウレタン又はポリウレンの樹脂層の
厚さが不均一になるため、これらの経皮薬用基材に対し
て均一な厚さの経皮薬層をコーティング方法によって形
成することができない。[0006] That is, a transdermal drug substance base made of a non-woven fabric made of cotton, rayon, synthetic fibers or the like or a woven fabric itself has a rough surface on which a transdermal drug layer is formed. A transdermal medicinal substrate prepared by sticking a resin layer of foamed polyurethane or polyurene on a base sheet made of is because the thickness of the resin layer of foamed polyurethane or polyurene becomes uneven, In contrast, a transdermal drug layer having a uniform thickness cannot be formed by a coating method.
【０００７】また、綿、レーヨン及び合成繊維等による
不織布や織布そのものからなる貼付による経皮薬用基材
は、経皮薬層を形成する際のコーティング剤が経皮薬用
基材中に浸透するため、高価な経皮薬成分が無駄にな
る。[0007] Further, in the transdermal drug substance base made of a non-woven fabric or woven fabric itself made of cotton, rayon, synthetic fibers or the like, the coating agent for forming the transdermal drug layer penetrates into the transdermal drug substance substrate. Therefore, expensive transdermal drug components are wasted.
【０００８】また、不織布や綿織布からなる基材シート
に発泡ポリウレタン又はポリウレンの樹脂層を形成した
貼付による経皮薬用基材は、経皮薬成分の種類によって
は、発泡ポリウレタン又はポリウレンの樹脂層が経時的
に侵され、経皮薬層の薬効が低下する等の問題がある。Further, a transdermal medicinal substrate obtained by sticking a resin layer of foamed polyurethane or polyurene on a base sheet made of a non-woven fabric or cotton woven fabric is a foamed polyurethane or polyurene resin depending on the type of transdermal drug component. There is a problem that the layer is eroded over time, and the efficacy of the transdermal drug layer decreases.
【０００９】これに対して本発明は、不織布や織布から
なる基材シートの軽量性及び柔軟性を殆ど損なわずに、
上記問題を悉く解消した貼付による経皮薬用基材であっ
て、しかも廉価に供給し得る経皮薬用基材を提供する。On the other hand, according to the present invention, the lightness and flexibility of the base sheet made of non-woven fabric or woven fabric are hardly impaired,
(EN) Provided is a transdermal drug substance substrate by sticking which solves the above problems, and which can be inexpensively supplied.
【００１０】[0010]
【課題を解決するための手段】本発明は、通気性を有す
る基材シートと、該基材シート上に積層されている樹脂
層とからなる貼付による経皮薬用基材であって、基材シ
ート上に積層されている樹脂層が、接着性ポリオレフィ
ン系樹脂層とポリエステル樹脂層とからなる貼付による
経皮薬用基材にすることにより、上記問題を解決するこ
とができる。The present invention relates to a transdermal medicated substrate which comprises an air-permeable base sheet and a resin layer laminated on the base sheet, which is attached to the skin. The above-mentioned problem can be solved by using a resin layer laminated on the sheet as a transdermal drug substance base which is composed of an adhesive polyolefin-based resin layer and a polyester resin layer by sticking.
【００１１】また本発明は、前記構成において、通気性
を有する基材シートを、綿、レーヨン、ポリエステル繊
維、ナイロン繊維、及びポリプロピレン繊維のなかから
選択される不織布又は織布で形成することにより、上記
問題を解決することができる。Further, in the present invention, in the above constitution, the breathable base sheet is formed of a nonwoven fabric or a woven fabric selected from cotton, rayon, polyester fiber, nylon fiber, and polypropylene fiber, The above problem can be solved.
【００１２】本発明の貼付による経皮薬用基材における
通気性を有する基材シートとしては、綿、レーヨン、ポ
リエステル繊維、ナイロン繊維、及びポリプロピレン繊
維のなかから選択される不織布又は織布等が好適であ
り、特に３０〜３００ｇ／ｍ2程度の目付を有する不織
布が好ましい。As the air-permeable base sheet for the transdermal drug substance of the present invention, a non-woven fabric or a woven fabric selected from cotton, rayon, polyester fiber, nylon fiber and polypropylene fiber is suitable. In particular, a nonwoven fabric having a basis weight of about 30 to 300 g / m 2 is preferable.
【００１３】通気性を有する基材シートの片面に形成す
る接着性ポリオレフィン系樹脂層とポリエステル樹脂層
とは、溶融押し出し機を利用する共押し出しによって形
成するのが好適であり、接着性ポリオレフィン系樹脂層
の厚さが５〜２０μｍ程度、ポリエステル樹脂層の厚さ
が５〜５０μｍ程度に形成される。The adhesive polyolefin resin layer and the polyester resin layer formed on one side of the air-permeable base sheet are preferably formed by coextrusion using a melt extruder, and the adhesive polyolefin resin The layer thickness is about 5 to 20 μm, and the polyester resin layer thickness is about 5 to 50 μm.
【００１４】なお、接着性ポリオレフィン系樹脂層とポ
リエステル樹脂層との積層樹脂層を形成する際に利用す
るポリエステル樹脂は、接着性ポリオレフィン系樹脂層
との間に強固な接着強度を有するポリエステル樹脂層が
形成されることの理由により、低結晶性のポリエステル
樹脂、すなわち３０％以下の結晶化度を有する低結晶性
ポリエステル樹脂や非結晶性ポリエステル樹脂が好まし
い。The polyester resin used when forming the laminated resin layer of the adhesive polyolefin resin layer and the polyester resin layer is a polyester resin layer having a strong adhesive strength with the adhesive polyolefin resin layer. A low crystalline polyester resin, that is, a low crystalline polyester resin or an amorphous polyester resin having a crystallinity of 30% or less is preferable for the reason that the above is formed.
【００１５】[0015]
【作用】本発明の貼付による経皮薬用基材は、通気性を
有する基材シートと、該基材シート上に積層されている
樹脂層とからなり、基材シート上に積層されている樹脂
層が、接着性ポリオレフィン系樹脂層とポリエステル樹
脂層とからなるものである。The base material for transdermal drug delivery according to the present invention comprises a base sheet having air permeability and a resin layer laminated on the base sheet, and the resin laminated on the base sheet. The layer comprises an adhesive polyolefin resin layer and a polyester resin layer.
【００１６】かかる構成による本発明の貼付による経皮
薬用基材における接着性ポリオレフィン系樹脂層とポリ
エステル樹脂層との積層樹脂層は、通気性を有する基材
シートと接着性ポリオレフィン系樹脂層とが当接するよ
うにして積層されることは勿論である。The laminated resin layer of the adhesive polyolefin-based resin layer and the polyester resin layer in the transdermal medicinal substrate according to the present invention having such a constitution has a breathable substrate sheet and an adhesive polyolefin-based resin layer. Needless to say, they are laminated so as to be in contact with each other.
【００１７】上記構成からなる本発明の貼付による経皮
薬用基材は、ポリエステル樹脂層面が平滑になり、かつ
積層樹脂層の厚さが均一になり、しかも経皮薬層と接す
るポリエステル樹脂層が、経皮薬層中の経皮薬成分によ
って経時的に侵されるようなことがない。In the transdermal drug substance base of the present invention having the above-mentioned constitution, the surface of the polyester resin layer is smooth, the laminated resin layer has a uniform thickness, and the polyester resin layer in contact with the transdermal drug layer is , The transdermal drug substance in the transdermal drug layer does not cause temporal damage.
【００１８】また、従来の基材シートに発泡ポリウレタ
ン又はポリウレンの樹脂層をコーティング方法によって
形成した経皮薬用基材に比較して、基材シートに対する
樹脂層を押し出し積層法で形成するものであるために、
経皮薬用基材を廉価に供給することができる。Further, as compared with a conventional transdermal medicinal base material in which a resin layer of foamed polyurethane or polyurene is formed on a base material sheet by a coating method, the resin layer on the base material sheet is formed by extrusion lamination method. for,
The transdermal drug substance can be supplied at a low price.
【００１９】[0019]
【実施例】以下、本発明の貼付による経皮薬用基材の具
体的な構成を、実施例に基づいて説明する。EXAMPLES The specific constitution of the transdermal drug carrier of the present invention will be described below with reference to Examples.
【００２０】実施例１ ５０ｇ／ｍ2 のレーヨン製不織布からなる基材シートの
片面に、溶融押し出し機から、接着性ポリオレフィン系
樹脂（アドマーＡＴ４９９：三井石油化学工業(株)
製）と低結晶性ポリエステル樹脂（ＧＸＰ−６０：東洋
紡績 (株) 製）とを、下記の条件によって共押し出し
後、冷却し、厚さ１５μｍの接着性ポリオレフィン系樹
脂層と厚さ１５μｍのポリエステル樹脂層とによる共押
し出し樹脂層を形成し、基材シート／接着性ポリオレフ
ィン系樹脂層／低結晶性ポリエステル樹脂層からなる貼
付による経皮薬用基材を得た。Example 1 An adhesive polyolefin resin (Admer AT499: Mitsui Petrochemical Industry Co., Ltd.) was applied to one surface of a substrate sheet made of rayon non-woven fabric of 50 g / m 2 from a melt extruder.
And a low crystalline polyester resin (GXP-60: manufactured by Toyobo Co., Ltd.) are co-extruded under the following conditions and then cooled, and an adhesive polyolefin resin layer having a thickness of 15 μm and a polyester having a thickness of 15 μm are used. A co-extruded resin layer was formed with the resin layer, and a transdermal drug substance substrate was obtained by sticking the substrate sheet / adhesive polyolefin-based resin layer / low crystalline polyester resin layer.
【００２１】接着性ポリオレフィン系樹脂とポリエステ
ル樹脂との共押し出し条件： スピード：８０ｍ／ｍｉｎ． 押し出し機：９０ｍｍφ、Ｌ／Ｄ＝２９ Ｔダイ：７５０ｍｍ幅、Ｔダイ温度：２６０℃ 押し出し量：２５ｋｇ／ＨCoextrusion conditions of adhesive polyolefin resin and polyester resin: Speed: 80 m / min. Extruder: 90 mmφ, L / D = 29 T die: 750 mm width, T die temperature: 260 ° C. Extrusion amount: 25 kg / H
【００２２】続いて、上記貼付による経皮薬用基材の低
結晶性ポリエステル樹脂層面に、サリチル酸エステルを
主成分とするパップ剤と天然ゴム系粘着剤とを含有する
コーティング剤をコーティングして経皮薬層を形成した
後、該経皮薬層の上に、シリコーン塗工フィルムのライ
ナーを積層することにより、貼着用経皮薬を得た。Then, the surface of the low crystalline polyester resin layer of the transdermal drug substance by the above-mentioned application is coated with a coating agent containing a salientyl ester-based poultice and a natural rubber adhesive. After forming the drug layer, a liner of a silicone coated film was laminated on the transdermal drug layer to obtain a transdermal patch for sticking.
【００２３】この貼着用経皮薬の製造においては、均一
な経皮薬層を形成することができた。In the production of this transdermal patch, a uniform transdermal patch could be formed.
【００２４】また、この貼着用経皮薬を４０℃、６０％
の環境の下に２か月間保存した後、経皮薬用基材のポリ
エステル樹脂層面を観察したところ、経皮薬層の影響に
よるポリエステル樹脂層面の侵食はみられなかった。Also, this transdermal patch is applied at 40 ° C, 60%
When the polyester resin layer surface of the percutaneous drug base was observed after being stored in the above environment for 2 months, no erosion of the polyester resin layer surface due to the effect of the transdermal drug layer was observed.
【００２５】比較例１ ５０ｇ／ｍ2 のレーヨン製不織布からなる基材シートの
片面に、ポリウレタン樹脂（レザミンＮＥ−３０８：大
日精化 (株) 製）によるコーティング剤をコンマコータ
ーでコーティングし、厚さ３０μｍのポリウレタン樹脂
層を形成することにより、基材シート／ポリウレタン樹
脂層からなる比較のための貼付による経皮薬用基材を得
た。Comparative Example 1 A coating material of polyurethane resin (Resamine NE-308: manufactured by Dainichiseika Co., Ltd.) was coated on one side of a base sheet made of rayon non-woven fabric of 50 g / m 2 with a comma coater to form a thick film. By forming a polyurethane resin layer having a thickness of 30 μm, a transdermal medicated base material comprising a base material sheet / polyurethane resin layer for comparison was obtained.
【００２６】続いて、上記貼付による経皮薬用基材のポ
リウレタン樹脂層面に、サリチル酸エステルを主成分と
するパップ剤と天然ゴム系粘着剤とを含有するコーティ
ング剤をコーティングして経皮薬層を形成した後、該経
皮薬層の上に、シリコーン塗工フィルムのライナーを積
層することにより、比較のための貼着用経皮薬を得た。Then, a coating agent containing a patch containing salicylate as a main component and a natural rubber adhesive is coated on the surface of the polyurethane resin layer of the percutaneous drug base by the above-mentioned application to form a transdermal drug layer. After forming, a liner of a silicone-coated film was laminated on the transdermal drug layer to obtain a transdermal drug patch for comparison.
【００２７】この貼着用経皮薬の製造においては、経皮
薬用基材のポリウレタン樹脂層の不均一な厚みに影響さ
れて、均一な厚さの経皮薬層を形成することができなか
った。In the production of this transdermal patch, it was impossible to form a transdermal patch having a uniform thickness due to the uneven thickness of the polyurethane resin layer of the transdermal patch base. .
【００２８】また、この比較のための貼着用経皮薬を４
０℃、６０％の環境の下に２か月間保存した後、経皮薬
用基材のポリウレタン樹脂層面を観察したところ、経皮
薬層の影響によるポリウレタン樹脂層面の侵食が若干み
られた。For the comparison, a transdermal patch for sticking is 4
After storage for 2 months in an environment of 0 ° C. and 60%, the surface of the polyurethane resin layer of the transdermal drug substance base was observed, and some erosion of the surface of the polyurethane resin layer due to the effect of the transdermal drug layer was observed.
【００２９】[0029]
【発明の効果】本発明の貼付による経皮薬用基材によれ
ば、通気性を有する基材シートの軽量性及び柔軟性が損
なわれることがなく、また、均一な厚さの経皮薬層をコ
ーティング方法によって形成することができ、しかも、
経皮薬層中の経皮薬成分によって経皮薬用基材が経時的
に侵食されるようなことがないため、高品質の貼着用経
皮薬が、廉価に得られるようになる。EFFECTS OF THE INVENTION According to the base material for transdermal drug delivery according to the present invention, the lightness and flexibility of the air-permeable base material sheet are not impaired, and the transdermal drug layer having a uniform thickness is provided. Can be formed by a coating method, and
Since the transdermal drug substance in the transdermal drug layer does not erode the transdermal drug substance over time, a high-quality patchy transdermal drug can be obtained at a low price.
Claims (2)
シート上に積層されている樹脂層とからなる貼付による
経皮薬用基材であって、基材シート上に積層されている
樹脂層が、接着性ポリオレフィン系樹脂層とポリエステ
ル樹脂層とからなることを特徴とする貼付による経皮薬
用基材。1. A base material for transdermal drug delivery, which comprises an air-permeable base sheet and a resin layer laminated on the base sheet, the resin being laminated on the base sheet. A layer for transdermal medicinal application, wherein the layer comprises an adhesive polyolefin resin layer and a polyester resin layer.
ーヨン、ポリエステル繊維、ナイロン繊維、及びポリプ
ロピレン繊維のなかから選択される不織布又は織布から
なることを特徴とする請求項１に記載の貼付による経皮
薬用基材。2. The breathable base sheet is made of a non-woven fabric or a woven fabric selected from cotton, rayon, polyester fiber, nylon fiber, and polypropylene fiber. Base material for transdermal drug application.