JPH0768164A - Carbon dioxide fixing material and carbon dioxide fixing filter - Google Patents
Carbon dioxide fixing material and carbon dioxide fixing filterInfo
- Publication number
- JPH0768164A JPH0768164A JP21984593A JP21984593A JPH0768164A JP H0768164 A JPH0768164 A JP H0768164A JP 21984593 A JP21984593 A JP 21984593A JP 21984593 A JP21984593 A JP 21984593A JP H0768164 A JPH0768164 A JP H0768164A
- Authority
- JP
- Japan
- Prior art keywords
- carbon dioxide
- filter
- cement
- fine particles
- dioxide fixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、空気清浄器に関し、特
に空気中の微細粒子などの浮遊物の除去のみならず、二
酸化炭素をも吸着固定して室内環境を化学的に改善しよ
うとするものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an air purifier, and in particular, it intends not only to remove suspended matters such as fine particles in the air but also to adsorb and fix carbon dioxide to chemically improve the indoor environment. It is a thing.
【０００２】[0002]
【従来の技術】従来の空気清浄器は、単に空気中の浮遊
物質を取り除くことを目的とするものであり、浮遊物を
除去する能力を向上させるために、フィルターをプレフ
ィルタおよびメインフィルタの複数種類のフィルタとし
て多段に構成したり、プレフィルタを通過した後の微細
な浮遊物を除去する能力を向上させるために、高電圧が
印加された電極部に空気流を通過させて帯電させ後段で
の固定能を高めるなどの方法が提案されている。しかし
ながら、このような空気清浄器では、空気中の微細な塵
埃を除去することはできても二酸化炭素のようなガスを
除去することはできなかった。2. Description of the Related Art A conventional air purifier is intended only to remove suspended solids in the air, and in order to improve the ability to remove suspended solids, a filter is used as a pre-filter or a main filter. In order to configure multiple types of filters or to improve the ability to remove fine suspended matter after passing through the pre-filter, an air stream is passed through the electrode section to which a high voltage is applied to charge it Methods such as increasing the immobilization ability have been proposed. However, with such an air purifier, fine dust in the air can be removed, but a gas such as carbon dioxide cannot be removed.
【０００３】産業活動の発展や内燃機関の使用量の増加
等によって、空気中の二酸化炭素（ＣＯ2）や酸化硫黄
が増加し様々な環境への悪影響が懸念されている。この
ような状況下にあって、発明者らは、コンクリート廃材
を粉砕して得た微粒子やコンクリート工場から排出され
るスラッジが二酸化炭素固定能力を有することに着目し
て、これら産業廃棄物を二酸化炭素固定材として利用す
ることを提案してきた。その利用形態として、図７に示
すようにコンクリート廃材を粉砕した微粒子を空気清浄
器の前段に設けたダクト３１内のフィルタ３３上に層状
３４に載置して二酸化炭素固定材として用いたところ、
二酸化炭素を固定することが確認された。ここで、フィ
ルタ３３の直径が１０ｃｍで、二酸化炭素固定材の層３
４の厚みが０．５ｃｍの空気清浄器用二酸化炭素固定フ
ィルタを構成し、この空気清浄器を動作させたところ、
吸入口３２での二酸化炭素濃度が６００ｐｐｍの空気を
吸引すると排出口３５では二酸化炭素濃度を５０ｐｐｍ
とすることができた。しかしながら、このように微粒子
状の二酸化炭素固定材を用いた場合には、二酸化炭素固
定材層での圧力降下が大きく毎分２リットル（２ｌ／ｍ
ｉｎ）の流量を得るためには、通常の空気清浄器に用い
られるようなファンでは吸引能力が不足し、真空ポンプ
で３６吸引させることが必要であった。Due to the development of industrial activities and the increase in the amount of use of internal combustion engines, carbon dioxide (CO 2 ) and sulfur oxide in the air are increased, and there is a concern that they may adversely affect various environments. Under such circumstances, the inventors have focused on the fact that fine particles obtained by crushing concrete waste materials and sludge discharged from a concrete factory have a carbon dioxide fixing ability, and are It has been proposed to use it as a carbon fixing material. As a form of its use, as shown in FIG. 7, when fine particles obtained by pulverizing concrete waste material were placed as a carbon dioxide fixing material on a filter 33 in a duct 31 provided in the preceding stage of an air purifier in a layered form 34,
It was confirmed to fix carbon dioxide. Here, the diameter of the filter 33 is 10 cm, and the layer 3 of the carbon dioxide fixing material is
A carbon dioxide fixed filter for an air purifier having a thickness of 4 of 0.5 cm was constructed, and when this air purifier was operated,
When air with a carbon dioxide concentration of 600 ppm is sucked in at the suction port 32, the carbon dioxide concentration is 50 ppm at the discharge port 35.
I was able to However, in the case of using the particulate carbon dioxide fixing material as described above, the pressure drop in the carbon dioxide fixing material layer is large and 2 liters / min (2 l / m 2).
In order to obtain a flow rate of (in), the suction capacity is insufficient with a fan used in a normal air purifier, and it has been necessary to suction 36 times with a vacuum pump.
【０００４】[0004]
【発明が解決しようとする課題】上記のような二酸化炭
素の固定に主眼点を置いて、二酸化炭素固定材を微粒子
状態で利用する方法では、微粒子が層状に存在するので
圧力損失が大きくなり、送風圧力の小さな一般的なファ
ンであるラジアルファン（ｒａｄｉａｌ ｆａｎ）を用
いることができず、強力な吸引力を有する真空ポンプを
用いて圧力損失以上の圧力を加えて強制的に空気を注入
もしくは排出を行なう必要があった。また、微粒子状の
二酸化炭素固定異材を用いるときには微粒子フィルター
の交換時に微粒子が飛散し、微粒子自体の交換も面倒な
ものであることから一般的な使用が制限されるおそれが
あった。本発明は、コンクリート廃材やセメント工場か
ら排出されるスラッジを使用して圧力損失の少ない空気
清浄器に用いるに好適な二酸化炭素固定材を提供するこ
とを目的とする。さらに本発明は、コンクリート廃材や
セメント工場から排出されるスラッジを使用して圧力損
失が少なくかつ取扱が容易な空気清浄器に用いるに好適
な二酸化炭素固定フィルタを提供することを目的とす
る。In the method of using the carbon dioxide fixing material in the form of fine particles, focusing on the fixation of carbon dioxide as described above, since the fine particles exist in a layered state, the pressure loss becomes large, It is not possible to use a radial fan, which is a general fan with a small blowing pressure, and a vacuum pump with a strong suction force is used to apply pressure above the pressure loss and forcefully inject or discharge air. Had to do. Further, when a particulate carbon dioxide-fixed foreign material is used, the particulates scatter when the particulate filter is replaced, and the particulate replacement itself is troublesome, so there is a risk that general use will be limited. It is an object of the present invention to provide a carbon dioxide fixing material suitable for use in an air purifier having a small pressure loss by using concrete waste materials and sludge discharged from a cement factory. A further object of the present invention is to provide a carbon dioxide fixed filter suitable for use in an air purifier that uses small amounts of waste concrete and sludge discharged from a cement plant and has a small pressure loss and is easy to handle.
【０００５】[0005]
【課題を解決するための手段】上記課題を解決するため
に、本発明は、コンクリート廃材を粉砕して得た微粒子
またはコンクリート工場から排出されるスラッジまたは
コンクリート廃材を粉砕して得た微粒子およびコンクリ
ート工場から排出されるスラッジと、消石灰または生石
灰またはセメントの何れかもしくは消石灰または生石灰
またはセメントの２種以上の組合せとを混合した混合物
を成型した粒状物で空気清浄器に用いるに好適な二酸化
炭素固定材を構成した。さらに、本発明は、空気清浄器
に用いるに好適な二酸化炭素固定材を構成する粒状物の
形状を球形または多面体または円柱形または多角柱形も
しくは表面に溝を有する多角柱形の何れかまたはこれら
の２種以上が混ざったものとした。また、本発明は、コ
ンクリート廃材を粉砕して得た微粒子またはコンクリー
ト工場から排出されるスラッジまたはコンクリート廃材
を粉砕して得た微粒子およびコンクリート工場から排出
されるスラッジと、消石灰または生石灰またはセメント
の何れかもしくは消石灰または生石灰またはセメントの
２種以上の組合せとを混合した混合物の粒状物を織布ま
たは編布または不織布もしくは紙からなる袋状体または
筒状体である通気性のある収納容器に収容して空気清浄
器に用いるに好適な二酸化炭素固定フィルタを構成し
た。In order to solve the above problems, the present invention provides fine particles obtained by crushing concrete waste material or fine particles and concrete obtained by crushing sludge or concrete waste material discharged from a concrete factory. Carbon dioxide fixation suitable for use in an air purifier in the form of granules formed by molding a mixture of sludge discharged from a factory and slaked lime or quick lime or cement or a combination of two or more kinds of slaked lime or quick lime or cement The material was constructed. Furthermore, the present invention provides that the shape of the particulate matter constituting the carbon dioxide fixing material suitable for use in an air purifier is spherical, polyhedral, cylindrical, polygonal prismatic, or polygonal prismatic having a groove on the surface, or these. It is assumed that two or more of the above are mixed. The present invention also provides fine particles obtained by crushing concrete waste material or sludge discharged from a concrete factory or fine particles obtained by crushing concrete waste material and sludge discharged from a concrete factory, and either slaked lime, quick lime or cement. Or slaked lime, quick lime, or a mixture of a mixture of two or more kinds of cement is contained in a breathable container which is a bag-shaped body or a tubular body made of woven fabric, knitted fabric, non-woven fabric or paper. Then, a carbon dioxide fixed filter suitable for use in an air purifier was constructed.
【０００６】[0006]
【実施例】図１は、本発明になる二酸化炭素固定材から
なるフィルタを使用した空気清浄器の概念を示す断面図
である。図において、空気清浄器１は、清浄器本体２の
正面から内部に向けて設けられた風洞３と、該風洞内に
設けられたフィルタ群４と、前記風洞の清浄器本体の正
面から遠ざかった終端に設けられたファン５と、排気用
ダクト６を介して清浄器本体表面に設けられた排気口７
と、該空気清浄器の運転を制御する制御手段８とから構
成される。1 is a sectional view showing the concept of an air purifier using a filter made of a carbon dioxide fixing material according to the present invention. In the figure, the air purifier 1 is located away from the front of the purifier body of the wind tunnel, the wind tunnel 3 provided inward from the front of the purifier body 2, the filter group 4 provided in the wind tunnel. A fan 5 provided at the end and an exhaust port 7 provided on the surface of the purifier body via an exhaust duct 6
And a control means 8 for controlling the operation of the air purifier.
【０００７】ファン５は、風洞３の終端側に設けたブラ
ケット９に固定されたモータ１０に取り付けられてい
る。モータ１０が回転すると、モータの回転軸に固定さ
れたラジアルファン５は回転し、ファンの羽根の間にあ
る空気は遠心力によってファンの外側に送り出され排気
用ダクト６を経由して排気口７から排出される。従っ
て、フィルタ群４の内側は負圧となって機器本体の外か
ら空気を吸引し、空気流をフィルタ群に通過させる。The fan 5 is attached to a motor 10 fixed to a bracket 9 provided on the terminal side of the wind tunnel 3. When the motor 10 rotates, the radial fan 5 fixed to the rotating shaft of the motor rotates, and the air between the blades of the fan is sent out to the outside of the fan by the centrifugal force and goes through the exhaust duct 6 to the exhaust port 7. Emitted from. Therefore, the inside of the filter group 4 becomes a negative pressure to suck air from the outside of the main body of the device and allow the air flow to pass through the filter group.
【０００８】フィルタ群４は、プレフィルタ１１と、二
酸化炭素固定フィルタ１２と、高電圧荷電電極１３と、
メインフィルタ１４から構成される。プレフィルタ１１
は、網状体の通気性の高い物質で構成され、吸引された
空気中に浮遊する比較的大きな浮遊物を取り除く働きを
する。二酸化炭素固定フィルタ１２は、本発明の特徴を
なすフィルタで、例えば後述する図２および図３に示す
構成を有しており、空気中の二酸化炭素を吸着固定す
る。高電圧荷電電極１３は、高電圧電源に接続されたワ
イヤ状の電極が複数本平行に設けられており、制御手段
８から高電圧が印加されている。プレフィルタを通過し
てきた空気がこの電極を通過するときに該電極から浮遊
している塵埃に電荷を与え、浮遊塵埃は荷電される。メ
インフィルタ１４は、微細な空隙を有するフィルタ材で
構成されるとともに例えば接地されて、荷電された浮遊
塵埃を確実にフィルタに吸引保持する。The filter group 4 includes a pre-filter 11, a carbon dioxide fixing filter 12, a high voltage charging electrode 13,
It is composed of the main filter 14. Pre-filter 11
Is composed of a highly breathable substance in the form of a mesh and serves to remove relatively large suspended matter suspended in the sucked air. The carbon dioxide fixing filter 12 is a filter that is a feature of the present invention, and has a configuration shown in FIGS. 2 and 3 described later, for example, and adsorbs and fixes carbon dioxide in the air. The high-voltage charging electrode 13 is provided with a plurality of wire-shaped electrodes connected in parallel to a high-voltage power source, and a high voltage is applied from the control means 8. When the air that has passed through the pre-filter passes through this electrode, it gives an electric charge to the dust floating from the electrode, and the floating dust is charged. The main filter 14 is composed of a filter material having fine voids and is grounded, for example, to reliably suck and hold charged floating dust in the filter.
【０００９】本発明を特徴付ける二酸化炭素固定フィル
タ１２の詳細について、その斜視図である図２および断
面図である図３を用いて説明する。二酸化炭素固定フィ
ルタ１２は、例えばプラスチック性のフレーム１５内に
収容された、収納容器に収納されたフィルタ部材１６か
ら構成される。フィルタ部材１６は、通気性の良い濾布
からなる収納容器１７に収容された二酸化炭素固定材１
８から構成される。収納容器１７は、合成繊維や天然繊
維からなる織布、編布、不織布もしくは紙等の通気性の
良い素材が用いられている。この収納容器は、上記素材
を円筒状に形成しその下端１９を縫ったり熱圧着したり
接着剤で接着することによって閉じられて袋状に形成さ
れる。この袋状の収納容器１７に、後述する方法で得ら
れた二酸化炭素固定材１８が収容され、その上端２０を
下端部と同様に閉じることによってフィルタ部材１６が
構成されている。Details of the carbon dioxide fixed filter 12 which characterizes the present invention will be described with reference to FIG. 2 which is a perspective view thereof and FIG. 3 which is a sectional view thereof. The carbon dioxide fixed filter 12 is composed of, for example, a filter member 16 housed in a housing container housed in a plastic frame 15. The filter member 16 is a carbon dioxide fixing material 1 housed in a container 17 made of a filter cloth having good air permeability.
It is composed of 8. The storage container 17 is made of a material having good air permeability such as woven cloth, knitted cloth, non-woven cloth, or paper made of synthetic fiber or natural fiber. This storage container is formed into a bag shape by closing the lower end 19 of the material formed into a cylindrical shape by sewing, thermocompression bonding or adhering with an adhesive. The bag-shaped storage container 17 stores the carbon dioxide fixing material 18 obtained by the method described later, and the upper end 20 is closed in the same manner as the lower end to form the filter member 16.
【００１０】二酸化炭素固定材１８は、コンクリート廃
材を粉砕して得られた微粒子やコンクリート工場から排
出されるスラッジを濾過・乾燥した後粉砕した微細粒子
を、消石灰や生石灰もしくはセメント等と混練し造粒の
後乾燥した、ペレット状のものが用いられる。一例とし
て、直径３ｍｍで長さ１０ｍｍの多孔性の円柱状のペレ
ットとすることができる。さらに、ペレットの形状は球
形とすることも可能であるし、造粒乾燥したものを再び
粉砕して不整形としたものも使用できる。The carbon dioxide fixing material 18 is produced by kneading fine particles obtained by crushing concrete waste material and sludge discharged from a concrete factory, filtering and drying, and then crushing fine particles with slaked lime, quick lime or cement. Pellets that are dried after granules are used. As an example, a porous columnar pellet having a diameter of 3 mm and a length of 10 mm can be used. Further, the pellets may have a spherical shape, or granulated and dried pellets may be crushed again to be irregularly shaped.
【００１１】図４を用いて、ペレットの各種断面形状を
示す。図４ａは、円柱状のペレット１８の長手方向表面
に２条の切り込み１８ｔを入れた例であり、ペレットの
表面積を大きくするとともに二酸化炭素が表面から芯の
方向に順次吸着固定されるとき中心部まで十分に利用で
きるようにした形状である。図４ｂは、ペレット１８の
断面形状を多角形とした例であり、同一体積の二酸化炭
素固定材のとき、より大きな表面積を得られるようにし
た例である。図４ｃは、ペレット１８の断面形状を切り
込み１８ｔのある多角形とした例で、図４ｂの多角形の
例に比してさらに大きな表面積を得られるようにした例
である。Various sectional shapes of the pellet are shown with reference to FIG. FIG. 4a is an example in which two cuts 18t are formed on the longitudinal surface of a cylindrical pellet 18, and when the surface area of the pellet is increased and carbon dioxide is sequentially adsorbed and fixed in the direction from the surface to the core, the central portion It is a shape that can be fully used. FIG. 4b is an example in which the cross-sectional shape of the pellet 18 is polygonal, and a larger surface area can be obtained when the carbon dioxide fixing material has the same volume. FIG. 4c is an example in which the cross-sectional shape of the pellet 18 is a polygon having a notch 18t, and is an example in which a larger surface area can be obtained as compared with the polygonal example of FIG. 4b.
【００１２】次に、二酸化炭素固定部材１８の製造方法
の一例を、製造の流れを示す図５を用いて説明する。コ
ンクリート廃材を粉砕して得た微粒子やコンクリート工
場の洗浄済み液を沈殿させ乾燥させて得たセメント系ス
ラッジと消石灰や生石灰ならびにセメントをミキサーに
投入して十分混練した後、通常の造粒機を用いて所定の
粒径に造粒する。次いで、通常の乾燥機で乾燥して所定
粒径の粒状体を得える。このとき、造粒機で造粒した粒
状体を球形整粒機で整粒した後乾燥することによって、
球形と粒径を一層均一なものとすることができる。こう
して得られた二酸化炭素固定材１８を収納容器１７に収
納して上部を閉じると詰め替え式フィルタ部材１６が得
られる。これらの詰め替え式フィルタ部材１６をフレー
ム１５に収容してカートリッジ式フィルタとすることも
できる。また、ミキサで混練された原材料を押出機を用
いて所定の直径の線状体に押出し加工した後所定の長さ
に裁断することによって、柱状のペレットを得ることが
できる。このとき押出し加工によって得られる線状体の
断面形状を円形に限らず前述の多角形状もしくは星型な
どの切り込み部を有する多角形状とすることによって、
表面積を大きくするとともに収納容器１７に収納したと
きのペレット間の空間を大きくして二酸化炭素固定能力
を増大させるとともに二酸化炭素固定フィルタにおける
圧力損失を少なくすることもできる。Next, an example of a method of manufacturing the carbon dioxide fixing member 18 will be described with reference to FIG. 5 showing a manufacturing flow. After the fine particles obtained by crushing the concrete waste material and the washed liquid of the concrete factory are precipitated and dried, the cement-based sludge and the slaked lime, quick lime, and cement are put into a mixer and sufficiently kneaded, and then an ordinary granulator is used. It is used to granulate to a predetermined particle size. Then, it is dried by an ordinary dryer to obtain a granular body having a predetermined particle size. At this time, by drying the granules granulated by the granulator after sizing by the spherical granulator,
The sphere and particle size can be made more uniform. When the carbon dioxide fixing material 18 thus obtained is stored in the storage container 17 and the upper part is closed, the refillable filter member 16 is obtained. The refillable filter member 16 may be housed in the frame 15 to form a cartridge filter. Further, columnar pellets can be obtained by extruding the raw material kneaded by the mixer into a linear body having a predetermined diameter by using an extruder and then cutting it into a predetermined length. At this time, the cross-sectional shape of the linear body obtained by extrusion processing is not limited to a circular shape, but is a polygonal shape having a notched portion such as the polygonal shape or star shape described above.
It is also possible to increase the surface area and the space between the pellets when stored in the storage container 17 to increase the carbon dioxide fixing ability and reduce the pressure loss in the carbon dioxide fixing filter.
【００１３】セメント系のスラッジ１０００ｇとコンク
リート廃材を粉砕して得た微粒子１０００ｇと消石灰と
を混合して押出加工機を用いて直径３ｍｍの線状体を形
成し、長さ１０ｍｍに切断した後乾燥機で乾燥したペレ
ットを、換気扇のフィルタに用いる不織布を用いて製造
した収納容器に収納した二酸化炭素固定フィルタ１２を
空気清浄器に用いたときには、１３０ｍ3／ｈの風量が
得られ、吸入側の二酸化炭素の濃度が３５０ｐｐｍであ
ったものが排出口では３００ｐｐｍとなった。これに対
応する例として、コンクリート廃材を粉砕して得た微粒
子を同様の収納容器に収容したフィルタを用いた場合に
は、このフィルタの圧力損失が極めて大きくなりフィル
タ周囲からの漏洩によると解釈される現象によって、吸
入側と排出側での二酸化炭素量に測定できる差は見出さ
れなかった。1000 g of cement-based sludge, 1000 g of fine particles obtained by crushing concrete waste and slaked lime were mixed to form a linear body having a diameter of 3 mm using an extruder, cut into a length of 10 mm, and then dried. When the carbon dioxide fixed filter 12 stored in the storage container made of the nonwoven fabric used for the filter of the ventilation fan is used for the air cleaner, the air volume of 130 m 3 / h is obtained and What had a carbon dioxide concentration of 350 ppm was 300 ppm at the discharge port. As an example corresponding to this, when using a filter containing fine particles obtained by crushing concrete waste material in a similar storage container, the pressure loss of this filter becomes extremely large and it is interpreted that it is due to leakage from around the filter. No measurable difference was found in the amount of carbon dioxide between the inhalation side and the exhalation side.
【００１４】図６を用いて他の実施例を説明する。この
実施例では、大量の二酸化炭素を吸着・固定できるよう
にした例であり、二酸化炭素固定フィルタ２９は紙・布
・プラスチック・金属等からなる筒状体２１の底部を通
気性の良好な濾布２２でふさぐとともに上部を通気性の
良好な上蓋２３で閉じた収納容器２４に収納された二酸
化炭素固定材ペレット１８とから構成される。二酸化炭
素固定フィルタ２９は、漏斗状の空間２８を有するフィ
ルタ固定台２５の漏斗状部２８に設けた連通した多孔を
有する支持部材２６上に載置される。該支持部材２６は
その周囲がゴム等のパッキング材２７で固定され、漏斗
状部２８の排出口から空気を吸引することにより、支持
部材２６およびパッキング２７上に載置されたフィルタ
２９が固定される。二酸化炭素固定フィルタ２９の収納
容器２１は、金属やプラスチックの様な通気性を有さな
い材料であってもよく、紙や布の様な通気性を有する材
料で構成されてもよい。さらに収納容器２１の周壁上方
にペレット１８がこぼれない程度の細孔を開けることに
よって、圧力低下を少なくすることも可能である。Another embodiment will be described with reference to FIG. This embodiment is an example in which a large amount of carbon dioxide can be adsorbed and fixed, and the carbon dioxide fixing filter 29 filters the bottom of the tubular body 21 made of paper, cloth, plastic, metal or the like with good air permeability. The carbon dioxide fixing material pellets 18 are housed in a housing container 24 which is covered with a cloth 22 and whose upper portion is closed by an upper lid 23 having good air permeability. The carbon dioxide fixing filter 29 is placed on the supporting member 26 having a continuous porous structure provided in the funnel-shaped portion 28 of the filter fixing base 25 having the funnel-shaped space 28. The periphery of the support member 26 is fixed by a packing material 27 such as rubber. By sucking air from the outlet of the funnel-shaped portion 28, the support member 26 and the filter 29 placed on the packing 27 are fixed. It The storage container 21 of the carbon dioxide fixed filter 29 may be made of a material having no air permeability such as metal or plastic, or may be made of a material having air permeability such as paper or cloth. Further, it is possible to reduce the pressure drop by forming pores above the peripheral wall of the storage container 21 to the extent that the pellets 18 do not spill.
【００１５】別の角度から、二酸化炭素固定材の必要料
を試算すると、以下のようになる。間口３．６ｍ、奥行
き５．４ｍ、高さ２ｍの部屋を考え、仮定として、 室内と室外との空気の入れ変わりはない。 室内に二酸化炭素発生源はない。 室内の二酸化炭素濃度は４００ｐｐｍである。 とすると室内の空気量Ｖは、 Ｖ＝５．４×３．６×２＝３８．８８ｍ3 空気は１気圧、０℃において、２２．４ｌ／ｍａｌであ
るから、この室内での二酸化炭素のｍａｌ数は、 ３８．８８÷２２．４×４００×１／１０6≒０．６８
ｍａｌ であり、二酸化炭素の単位あたりの重量は４４ｇ／ｍａ
ｌであるから、二酸化炭素の総重量は、 ０．６８×４４＝２９．９ｇである。 この室内の二酸化炭素濃度を５０ｐｐｍまで減少させよ
うとすると、総重量で３．７ｇまで押さえなければなら
ない。つまり、二酸化炭素固定部材は、 ２９．９−３．７＝２６．２ｇ の二酸化炭素を吸着することが必要である。セメント系
のスラッジ１０００ｇとコンクリート廃材を粉砕して得
た微粒子１０００ｇと消石灰とからなるペレットは１Ｋ
ｇ当り０．３３Ｋｇの二酸化炭素を吸着できるので、 ２６．２÷３３０＝７９．４ｇ のペレットが有れば、この室内の二酸化炭素濃度を５０
ｐｐｍに減少させることができる。From a different angle, the required charges for the carbon dioxide fixing material are calculated as follows. Considering a room with a frontage of 3.6 m, a depth of 5.4 m, and a height of 2 m, it is assumed that there is no exchange of air between the inside and outside of the room. There is no carbon dioxide source in the room. The carbon dioxide concentration in the room is 400 ppm. Then, the amount V of air in the room is: V = 5.4 × 3.6 × 2 = 38.88 m 3 Since air is 22.4 l / mal at 1 atm and 0 ° C., the amount of carbon dioxide in this room is The mal number is 38.88 ÷ 22.4 × 400 × 1/10 6 ≈0.68
and the weight per unit of carbon dioxide is 44 g / ma.
Therefore, the total weight of carbon dioxide is 0.68 × 44 = 29.9 g. In order to reduce the carbon dioxide concentration in this room to 50 ppm, the total weight must be suppressed to 3.7 g. That is, the carbon dioxide fixing member needs to adsorb 29.9-3.7 = 26.2 g of carbon dioxide. A pellet consisting of 1000 g of cement-based sludge, 1000 g of fine particles obtained by crushing concrete waste and slaked lime is 1K.
Since 0.33 Kg of carbon dioxide can be adsorbed per g, if there are 26.2 ÷ 330 = 79.4 g of pellets, the carbon dioxide concentration in this room is 50
It can be reduced to ppm.
【００１６】本発明による二酸化炭素固定材は、化学反
応の優先順位から見て、空気中の硫黄酸化物も同時に吸
着することができる。The carbon dioxide fixing material according to the present invention can simultaneously adsorb sulfur oxides in the air in view of the priority of chemical reactions.
【００１７】[0017]
【発明の効果】以上のように、本発明の二酸化炭素固定
材は、コンクリート廃材を粉砕した微粒子やコンクリー
ト工場等より排出されるセメント系のスラッジを消石灰
または生石灰もしくはセメントの単独もしくは組み合わ
せと混合し、通常の造粒機や球形整粒機を用いて円柱状
粒、球形粒等の粒子に成型して二酸化炭素固定材とする
にあたって、消石灰または生石灰もしくはセメントをバ
インダー材として用いているので、コンクリート廃材を
粉砕した微粒子やコンクリート工場等より排出されるセ
メント系のスラッジを造粒および球形整粒してペレット
状に成型して空気清浄器の二酸化炭素固定材として使用
することができ、従来廃棄されていたコンクリート廃材
やセメント系のスラッジの有効活用がはかれる。また、
コンクリート廃材を粉砕した微粒子やコンクリート工場
等より排出されるセメント系のスラッジを消石灰または
生石灰もしくはセメントの単独もしくは組み合わせと混
合し円柱状粒とか球形粒という形状で使用するので、空
気清浄器の二酸化炭素固定フィルター内での圧力損失を
低く押さえることができ、一般的なファン（ｆａｎ）の
利用が可能となる。さらに、コンクリート廃材を粉砕し
た微粒子やコンクリート工場等より排出されるセメント
系のスラッジをペレット状に成型したので、空気清浄器
のフィルタ交換の操作が容易になり、交換に当たって微
粒子の飛散も押さえることができる。INDUSTRIAL APPLICABILITY As described above, the carbon dioxide fixing material of the present invention is obtained by mixing fine particles obtained by crushing concrete waste material and cement sludge discharged from a concrete factory with slaked lime, quick lime or cement alone or in combination. When slaked lime or quick lime or cement is used as a binder material when forming into carbon dioxide fixing material by molding into particles such as columnar particles and spherical particles using an ordinary granulator or spherical sizing machine, concrete is used. It can be used as a carbon dioxide fixing material for air purifiers by granulating and spherically sizing fine particles of waste materials and cement-based sludge discharged from concrete factories, etc. The concrete waste materials and cement-based sludge that had been used can be effectively utilized. Also,
The fine particles of crushed concrete waste and the cement sludge discharged from concrete factories are mixed with slaked lime, quick lime or cement alone or in combination and used in the form of columnar particles or spherical particles. The pressure loss in the fixed filter can be kept low, and a general fan can be used. Furthermore, since fine particles of crushed concrete waste and cement-based sludge discharged from concrete factories are molded into pellets, it is easy to replace the filter in the air purifier, and it is possible to suppress scattering of fine particles during replacement. it can.
【図１】本発明の二酸化炭素固定材を用いた空気清浄器
の概要を示す断面図。FIG. 1 is a sectional view showing an outline of an air purifier using a carbon dioxide fixing material of the present invention.
【図２】本発明の、二酸化炭素固定材を用いたフィルタ
の外観を示す斜視図。FIG. 2 is a perspective view showing the outer appearance of a filter using a carbon dioxide fixing material of the present invention.
【図３】本発明の、二酸化炭素固定材を用いたフィルタ
の構造を示す断面図。FIG. 3 is a sectional view showing a structure of a filter using a carbon dioxide fixing material of the present invention.
【図４】本発明の二酸化炭素固定材の断面形状を示す
図。FIG. 4 is a view showing a cross-sectional shape of a carbon dioxide fixing material of the present invention.
【図５】本発明の、二酸化炭素固定材の製造過程を示す
流れ図。FIG. 5 is a flow chart showing a process for producing a carbon dioxide fixing material according to the present invention.
【図６】本発明の二酸化炭素固定材を用いたフィルタの
第２の実施例を示す概念図。FIG. 6 is a conceptual diagram showing a second embodiment of a filter using the carbon dioxide fixing material of the present invention.
【図７】微粒子状二酸化炭素固定材を用いる二酸化炭素
固定法を示す概念図。FIG. 7 is a conceptual diagram showing a carbon dioxide fixing method using a particulate carbon dioxide fixing material.
１ 空気清浄器 ２ 空気清浄器本体 ３ 風洞 ４ フィルタ群 ５ ファン ６ 排気ダクト ７ 排気口 ８ 制御手段 ９ ブラケット １０ モータ １１ プレフィルタ １２ 二酸化炭素固定フィルタ １３ 高電圧電極 １４ メインフィルタ １５ フレーム １６ 二酸化炭素固定フィルタ部材 １７ 収納容器 １８ 二酸化炭素固定部材 1 Air Purifier 2 Air Purifier Main Body 3 Wind Tunnel 4 Filter Group 5 Fan 6 Exhaust Duct 7 Exhaust Port 8 Control Means 9 Bracket 10 Motor 11 Pre-filter 12 Carbon Dioxide Fixed Filter 13 High Voltage Electrode 14 Main Filter 15 Frame 16 Carbon Dioxide Fixed Filter member 17 Storage container 18 Carbon dioxide fixing member
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ０１Ｊ 20/28 Ａ 7202−4Ｇ Ｂ０３Ｃ 3/02 Ｂ 3/155 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display location B01J 20/28 A 7202-4G B03C 3/02 B 3/155
Claims (5)
またはコンクリート工場から排出されるスラッジまたは
コンクリート廃材を粉砕して得た微粒子およびコンクリ
ート工場から排出されるスラッジと、消石灰または生石
灰またはセメントの何れかもしくは消石灰または生石灰
またはセメントの２種以上の組合せとを混合した混合物
を成型した粒状物からなることを特徴とする二酸化炭素
固定材。1. Fine particles obtained by crushing concrete waste material or sludge discharged from a concrete factory or fine particles obtained by crushing concrete waste material and sludge discharged from a concrete factory, and either slaked lime, quick lime or cement. Alternatively, a carbon dioxide fixing material comprising a granular material obtained by molding a mixture obtained by mixing slaked lime, quick lime, or a combination of two or more kinds of cement.
円柱形または多角柱形もしくは表面に溝を有する円柱ま
たは多角柱形の何れかまたはこれらの２種以上が混ざっ
たものである請求項１記載の二酸化炭素固定材。2. The shape of the granular material is any one of a spherical shape, a polyhedral shape, a cylindrical shape, a polygonal prism shape, a cylindrical shape having a groove on the surface, a polygonal prism shape, or a mixture of two or more thereof. Carbon dioxide fixing material.
またはコンクリート工場から排出されるスラッジまたは
コンクリート廃材を粉砕して得た微粒子およびコンクリ
ート工場から排出されるスラッジと、消石灰または生石
灰またはセメントの何れかもしくは消石灰または生石灰
またはセメントの２種以上の組合せとを混合した混合物
成型した粒状物を通気性のある収納容器に収容したこと
を特徴とする二酸化炭素固定フィルタ。3. Fine particles obtained by crushing concrete waste material or sludge discharged from a concrete factory or fine particles obtained by crushing concrete waste material and sludge discharged from a concrete factory, and either slaked lime, quick lime or cement. Alternatively, a carbon dioxide fixed filter, characterized in that a mixture-molded granular material obtained by mixing slaked lime, quick lime, or a combination of two or more kinds of cement is contained in an air-permeable storage container.
布もしくは紙からなる袋状体である請求項３記載の二酸
化炭素固定フィルタ。4. The carbon dioxide fixed filter according to claim 3, wherein the storage container is a bag-shaped body made of woven cloth, knitted cloth, non-woven cloth, or paper.
ッジ状とした請求項３記載の二酸化炭素固定フィルタ。5. The carbon dioxide fixed filter according to claim 3, wherein the storage container is stored in a frame to form a cartridge.