JPH0766515B2 - Magnetic recording paper - Google Patents
Magnetic recording paperInfo
- Publication number
- JPH0766515B2 JPH0766515B2 JP62101158A JP10115887A JPH0766515B2 JP H0766515 B2 JPH0766515 B2 JP H0766515B2 JP 62101158 A JP62101158 A JP 62101158A JP 10115887 A JP10115887 A JP 10115887A JP H0766515 B2 JPH0766515 B2 JP H0766515B2
- Authority
- JP
- Japan
- Prior art keywords
- magnetic recording
- aluminum
- white pigment
- magnetic
- coating layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 本発明は、磁気記録紙に関するものである。特に、磁気
記録層面の隠蔽性、平滑性が優れ、磁気記録層面に可視
情報を印刷することを可能にしたことを特徴とする磁気
記録紙を提供することを目的とするものである。The present invention relates to a magnetic recording paper. In particular, it is an object of the present invention to provide a magnetic recording paper which has excellent concealing properties and smoothness on the surface of the magnetic recording layer and enables visible information to be printed on the surface of the magnetic recording layer.
磁気記録紙の磁気記録層面は、磁性塗料の色調が、その
儘原紙に付与されるために茶褐色、暗黒色等の色調を呈
し、可視情報を印刷することが出来ず、利用されていな
い。したがつて、必要な可視情報は、磁気記録層と反対
の面に、通常の印刷方式、カーボン熱転写方式あるいは
キレート層、感熱記録層等を設けキレート印刷方式、感
熱記録方式等で印字されているのが実情で、従来、磁気
記録層面上に印刷することについては何等考慮されず、
遊んだ状態になっている。一方、磁気記録紙には、磁気
ヘツドとの接触によるスペースロスのない平滑性が要求
されている。The magnetic recording layer surface of the magnetic recording paper is not used because the color tone of the magnetic coating material is dark brown, dark black or the like because it is applied to the base paper, and the visible information cannot be printed. Therefore, the necessary visible information is printed on the surface opposite to the magnetic recording layer by a normal printing method, a carbon thermal transfer method or a chelate layer, a heat sensitive recording layer or the like, and a chelate printing method, a heat sensitive recording method or the like. However, in the past, no consideration was given to printing on the surface of the magnetic recording layer,
It is playing. On the other hand, the magnetic recording paper is required to have smoothness without space loss due to contact with the magnetic head.
本発明は、磁気記録層上に可視情報の記録の可能性につ
いて検討した結果、比較的少量の塗被量でもってアルミ
塗被層と白色顔料塗被層を設けるだけで磁気記録層の茶
褐色を隠敝することが出来、しかも、平滑性が優れ、磁
気記録特性を何等阻害することなく、また、自動販売機
を想定した発券テストにも何等支障のないことを見出
し、完成させたものである。The present invention, as a result of studying the possibility of recording visible information on the magnetic recording layer, provides a dark brown color of the magnetic recording layer only by providing an aluminum coating layer and a white pigment coating layer with a relatively small coating amount. It was completed after discovering that it can be hidden, has excellent smoothness, does not hinder magnetic recording characteristics at all, and does not hinder ticket issuing tests assuming vending machines. .
すなわち、本発明は、原紙上に磁性粉末と接着剤とを主
成分とする磁性塗料を塗被し、磁気記録層を設け、次い
で、該磁気記録層上に、アルミニユーム粉末と接着剤と
を主成分とする水性アルミ塗料を塗被し、アルミ塗被層
を設け、更に、該アルミ塗被層上に、白色顔料と接着剤
とを主成分とする水性白色顔料塗料を塗被し、白色度64
％以上の白色顔料塗被層を設けたことを特徴とする磁気
記録紙である。That is, in the present invention, a magnetic coating material containing magnetic powder and an adhesive as main components is coated on a base paper to provide a magnetic recording layer, and then the aluminum powder and the adhesive are mainly formed on the magnetic recording layer. A water-based aluminum paint as a component is applied to form an aluminum coating layer, and further, an aqueous white pigment paint containing a white pigment and an adhesive as a main component is applied onto the aluminum coating layer to obtain a whiteness degree. 64
% Of the white pigment coating layer is provided on the magnetic recording paper.
以下、本発明の技術的事項について詳述する。Hereinafter, technical matters of the present invention will be described in detail.
先づ、原紙としては、坪量40〜300g/m2の上質紙、加工
原紙等を使用することが出来るが、特に限定はされな
い。First, as the base paper, high-quality paper having a basis weight of 40 to 300 g / m 2 , processed base paper and the like can be used, but the base paper is not particularly limited.
原紙上に設けられる磁気記録層は、磁性粉末と接着剤と
を主成分とし、磁性粉末としては、γ−酸化鉄、コバル
トで変性したγ−酸化鉄、酸化クローム、バリウムフエ
ライト等を使用することが出来る。また、接着剤として
は、ポリビニルアルコールのような水溶性接着剤やスチ
レン・ブタジエン共重合体、メチルメタアクリレート・
ブタジエン共重合体、スチレン・ブタジエン・メチルメ
タアクリレート共重合体、アクリル系樹脂、酢酸ビニル
系樹脂等のラテックスエマルジョンあるいはポリウレタ
ン樹脂、塩化ビニル樹脂、ポリエステル樹脂等を使用す
ることが出来る。そして、これら磁性粉末と接着剤とを
主成分とする磁性塗料は、水性系あるいは有機溶剤系の
いづれかで調整され供されるが、水性系の方が経済的で
好ましい。有機溶剤としては、トルエン、キシレン、ブ
タノール等を使用することが出来る。The magnetic recording layer provided on the base paper contains magnetic powder and an adhesive as main components, and as the magnetic powder, γ-iron oxide, γ-iron oxide modified with cobalt, chrome oxide, barium ferrite, etc. should be used. Can be done. As the adhesive, a water-soluble adhesive such as polyvinyl alcohol, a styrene-butadiene copolymer, a methylmethacrylate
A butadiene copolymer, a styrene / butadiene / methyl methacrylate copolymer, a latex emulsion of an acrylic resin, a vinyl acetate resin or the like, a polyurethane resin, a vinyl chloride resin, a polyester resin or the like can be used. The magnetic coating material containing the magnetic powder and the adhesive as main components is prepared in either an aqueous system or an organic solvent system, and the aqueous system is more economical and preferable. As the organic solvent, toluene, xylene, butanol or the like can be used.
かくして調製される磁性塗料は、エアーナイフコータ
ー、メーヤバーコーター、ブレードコーター、ロールコ
ーター、グラビアコーター等で原紙上に塗被、乾燥さ
れ、磁気記録層は設けられる。The magnetic coating material thus prepared is coated on the base paper with an air knife coater, a Mayer bar coater, a blade coater, a roll coater, a gravure coater, etc. and dried to form a magnetic recording layer.
本発明においては、先ず、原紙上に設けられた磁気記録
層上に、アルミニユーム粉末と接着剤とを主成分とする
水性アルミ塗料を塗被、乾燥し、アルミ塗被層を設け
る。In the present invention, first, a magnetic recording layer provided on a base paper is coated with a water-based aluminum paint containing aluminum powder and an adhesive as main components and dried to form an aluminum coating layer.
磁気記録層上にアルミ塗被層を設けるにあたり調製され
る水性アルミ塗料に供されるアルミニユーム粉末は、酸
化され易く、金属光沢を消失し易いためにペースト状に
加工されたアルミペースト顔料が使用される。そして、
アルミペースト顔料には、リーフイングタイプとノンリ
ーフイングタイプがあるが、本発明ではいずれも使用す
ることが出来る。その組成は、通常ステアリン酸、ミネ
ラルスピリツト等の添加剤をアルミニユーム箔と共にボ
ールミル等の粉砕機により任意の粒径に加工される。The aluminum powder used for the water-based aluminum paint prepared when the aluminum coating layer is formed on the magnetic recording layer is easily oxidized and easily loses its metallic luster, so that an aluminum paste pigment processed into a paste form is used. It And
There are leafing type and non-leafing type aluminum paste pigments, and any of them can be used in the present invention. Its composition is usually processed into an arbitrary particle size by a crusher such as a ball mill together with an aluminum foil and additives such as stearic acid and mineral spirits.
本発明の水性アルミ塗料は、このようなアルミペースト
顔料と接着剤とを主成分とし、この外に添加剤あるいは
塗料調製剤等を配合したものである。接着剤としては、
カゼイン、デンプン、ゼラチン、大豆蛋白、ポリビニル
アルコール等の水溶性接着剤やスチレン・ダタジエン共
重合体、スチレン・ブタジエン・メチルメタアクリレー
ト共重合体、アクリル系樹脂、酢酸ビニル樹脂、ポリエ
ステル樹脂等のラテックスエマルジョンあるいは合成樹
脂エマルジョンを使用することが出来る。The water-based aluminum coating composition of the present invention comprises such an aluminum paste pigment and an adhesive as main components, and an additive or a coating preparation agent and the like in addition thereto. As an adhesive,
Water-soluble adhesives such as casein, starch, gelatin, soybean protein, polyvinyl alcohol, etc., styrene / datadiene copolymer, styrene / butadiene / methyl methacrylate copolymer, acrylic resin, vinyl acetate resin, polyester resin latex emulsion, etc. Alternatively, a synthetic resin emulsion can be used.
添加剤としては、一般のクレーコーテイング用水性顔料
塗料に使用されている増粘剤、分散剤、消泡剤、潤滑
剤、着色剤等を使用することが出来、いずれも必要に応
じて使用すれば良い。As the additive, a thickener, a dispersant, an antifoaming agent, a lubricant, a colorant, etc., which are used in a general water-based pigment coating for clay coating, can be used, and any of them may be used as necessary. Good.
アルミペースト顔料、接着剤、その他添加剤等よりなる
水性アルミ塗料は、pHを７の中性になるように調製する
ことが肝要である。しかし、酸性又はアルカリ性になる
場合には、ポリビニルアルコールやカゼイン等を添加し
て保護コロイドをつくつてからエマルジヨン類を添加す
れば中性にならなくても使用出来る。It is important to adjust the pH of a water-based aluminum paint comprising an aluminum paste pigment, an adhesive agent, and other additives so that the pH thereof becomes 7 neutral. However, when it becomes acidic or alkaline, it can be used without becoming neutral by adding polyvinyl alcohol, casein or the like to form a protective colloid and then adding emulsions.
このようなアルミペースト顔料および接着剤を主成分と
する水性アルミ塗料は、紙の水性コーテイング法におい
て通常使用されている各種ミキサーで充分に分散させて
調製される。その際、添加剤として、分散剤、滑剤、着
色剤、耐水化剤、消泡剤、塗料粘度調整剤等を適宜配合
すれば良い。The water-based aluminum coating composition containing such an aluminum paste pigment and an adhesive as a main component is prepared by sufficiently dispersing it in various mixers usually used in the water-based coating method for paper. At that time, as an additive, a dispersant, a lubricant, a colorant, a water-proofing agent, a defoaming agent, a paint viscosity modifier, and the like may be appropriately added.
かくして調製された水性アルミ塗料は、エアーナイフコ
ーター、ブレードコーター、ロールコーター、グラビア
コーター等で原紙上に設けられた磁気記録層上に塗被、
乾燥され、アルミ塗被層は設けられる。そして、アルミ
塗被層は、磁気記録層の磁気特性を低下させないように
することが必要で、水性アルミ塗料の塗被量は、２〜6g
/m2で、好ましくは３〜5g/m2で、磁気特性の低下は、全
く認められなかった。特に、本発明のアルミ塗被層の場
合には、比較的少量の塗被量でもつて磁気記録層の茶褐
色を隠蔽することが出来る。The thus-prepared water-based aluminum paint is coated on the magnetic recording layer provided on the base paper with an air knife coater, a blade coater, a roll coater, a gravure coater, or the like,
It is dried and the aluminum coating layer is applied. The aluminum coating layer is required not to deteriorate the magnetic characteristics of the magnetic recording layer, and the coating amount of the water-based aluminum coating is 2 to 6 g.
/ m 2 , preferably 3 to 5 g / m 2 , no deterioration in magnetic properties was observed. In particular, in the case of the aluminum coating layer of the present invention, the brown color of the magnetic recording layer can be covered with a relatively small coating amount.
更に、本発明では、アルミ塗被層上には、白色顔料と接
着剤とを主成分とする水性白色顔料塗料を塗被、乾燥し
白色度64％以上の白色顔料塗被層を設けることにより隠
蔽性、平滑性が優れ、磁気記録層面に印刷を可能にした
磁気記録紙を得ることが出来る。Furthermore, in the present invention, by coating an aqueous white pigment coating material containing a white pigment and an adhesive as the main components on the aluminum coating layer, and drying to provide a white pigment coating layer having a whiteness of 64% or more. It is possible to obtain a magnetic recording paper that has excellent concealing properties and smoothness and that can be printed on the surface of the magnetic recording layer.
アルミ塗被層上に白色顔料塗被層を設けるにあたり調製
される水性白色顔料塗料に供される顔料としては、クレ
ー、炭酸カルシウム、水酸化アルミニウム、硫酸バリウ
ム、サチンホワイト、亜鉛華、アルミナゼオライト、プ
ラスチックピグメント等紙のコーテイングに通常使用さ
れているものでよい。一方、接着剤としては、カゼイ
ン、テンプン、ゼラチン、大豆蛋白、ポリビニルアルコ
ール等の水溶性接着剤やスチレン・ブタジエン共重合
体、スチレン・ブタジエン、メチルメタアクリレート共
重合体、アクリル系樹脂、酢酸ビニル樹脂、ポリエステ
ル樹脂等のラテツクスエマルジヨンあるいは合成樹脂エ
マルジヨンを使用することが出来る。The pigment used in the aqueous white pigment paint prepared in providing the white pigment coating layer on the aluminum coating layer, clay, calcium carbonate, aluminum hydroxide, barium sulfate, satin white, zinc white, alumina zeolite, It may be one commonly used for coating paper such as plastic pigments. On the other hand, as the adhesive, water-soluble adhesives such as casein, tempun, gelatin, soybean protein, and polyvinyl alcohol, styrene / butadiene copolymer, styrene / butadiene, methyl methacrylate copolymer, acrylic resin, vinyl acetate resin A latex emulsion such as a polyester resin or a synthetic resin emulsion can be used.
このような白色顔料と接着剤とを主成分とした水性白色
顔料塗料は、紙の水性コーテイング法において通常使用
されている各種ミキサーで充分に攪はん、分散させて調
製される。その際、助剤として、分散剤、滑剤、着色
剤、耐水化剤、消泡剤、塗料粘度調整剤等を適宜配合し
ても差し支えはない。The water-based white pigment paint containing such a white pigment and an adhesive as main components is prepared by sufficiently stirring and dispersing them in various mixers that are usually used in the water-based coating method for paper. At that time, as an auxiliary agent, a dispersant, a lubricant, a colorant, a water-proofing agent, an antifoaming agent, a paint viscosity modifier, etc. may be appropriately blended.
かくして調製された水性白色顔料塗料は、エアーナイフ
コーター、ブレードコーター、ロールコーター、グラビ
アコーター等でアルミ塗被層上に塗被、乾燥され、白色
顔料塗被層は設けられる。更に、白色顔料塗被層を平滑
にするためにスーパーキヤレンダー、グロスキヤレンダ
ー等で処理すると印刷性をより向上させることが出来、
効果的である。The thus-prepared aqueous white pigment coating composition is coated on an aluminum coating layer with an air knife coater, blade coater, roll coater, gravure coater, etc. and dried to form a white pigment coating layer. Furthermore, in order to make the white pigment coating layer smooth, it is possible to further improve the printability by treating with a super calender, a gloss calender, etc.
It is effective.
白色顔料塗被層は、磁気記録層の磁気特性を低下させな
いようにすることが必要で、水性白色顔料塗料の塗被量
は、アルミ塗被層との相乗効果により少なくすることが
出来、２〜8g/m2で、好ましくは３〜7g/m2で、充分効果
が得られる。The white pigment coating layer is required not to deteriorate the magnetic characteristics of the magnetic recording layer, and the coating amount of the aqueous white pigment coating material can be reduced by the synergistic effect with the aluminum coating layer. -8 g / m 2 , preferably 3-7 g / m 2 is sufficient to obtain the effect.
本発明の磁気記録紙は、磁気記録層上に比較的塗被量の
少ないアルミ塗被層と白色度64％以上の白色顔料塗料塗
被層とを設けるだけで、その相乗効果によって、磁気記
録層の着色を隠敝することが出来る。そして、磁気記録
層面上に可視情報の印刷を可能にし、記録情報量を多く
することが出来る。しかも、磁気記録層面の平滑性を改
善することが出来、磁気ヘッドとのスペースロスがなく
磁気出力特性には、全く影響がなく、発券適性を有する
磁気記録紙を得ることが出来る。The magnetic recording paper of the present invention has a relatively small coating amount on the magnetic recording layer and a white pigment coating layer having a whiteness of 64% or more. The coloring of layers can be hidden. The visible information can be printed on the surface of the magnetic recording layer, and the amount of recorded information can be increased. Moreover, the smoothness of the surface of the magnetic recording layer can be improved, there is no space loss with the magnetic head, the magnetic output characteristics are not affected at all, and a magnetic recording paper having ticketing suitability can be obtained.
さらに、実施例によって本発明を説明する。Furthermore, the present invention will be described with reference to examples.
実施例１ 磁気塗料配合組成 重量部 γ−酸化鉄 100 ポリビニルアルコール 30 スチレン・ブタジエンラテックス 20 メラミン・ホルムアルデヒド樹脂 ５ 水性アルミ塗料配合組成 重量部 アルミペーストAW−600 100 （ノンリーフイングタイプ） ポリビニールアルコール 20 スチレン・ブタジエンラテックス 50 分散剤 ３ 水性白色顔料塗料配合組成 重量部 酸化チタン 100 トリポリリン酸ソーダ 0.3 酸化デンプン 10 カルボキシ変性メチルメタアクリレート・ ブタジエンラテツクス 20 上記磁気塗料配合組成で水性磁気塗料を調製し、坪量15
7g/m2の加工原紙に塗被し、永久磁石で配合後乾燥し、
塗被量が40g/m2の磁気記録層を設けた。次いで、上記水
性アルミ塗料配合組成の水性アルミ塗料を調製し、磁気
記録層上に塗被、乾燥し、塗被量が3g/m2のアルミ塗被
層を設けた。更に、上記水性白色顔料塗料配合組成の水
性白色顔料塗料を調製し、アルミ塗被層上に塗被、乾燥
し、塗被量が5g/m2の白色顔料塗被層を設けた本発明の
磁気記録紙を得た。Example 1 Composition of magnetic paint Part by weight γ-iron oxide 100 Polyvinyl alcohol 30 Styrene-butadiene latex 20 Melamine-formaldehyde resin 5 Composition of water-based aluminum paint Part by weight Aluminum paste AW-600 100 (non-leafing type) Polyvinyl alcohol 20 Styrene -Butadiene latex 50 dispersant 3 Water-based white pigment coating composition weight part Titanium oxide 100 Sodium tripolyphosphate 0.3 Oxidized starch 10 Carboxy-modified methyl methacrylate-Butadiene latex 20 Aqueous magnetic coating composition was prepared with the above magnetic coating composition and basis weight. 15
Coat on 7g / m 2 processed base paper, mix with a permanent magnet and dry,
A magnetic recording layer having a coating amount of 40 g / m 2 was provided. Next, an aqueous aluminum coating composition having the above-mentioned aqueous aluminum coating composition was prepared, coated on the magnetic recording layer and dried to provide an aluminum coating layer having a coating amount of 3 g / m 2 . Furthermore, an aqueous white pigment coating composition of the above aqueous white pigment coating composition is prepared, coated on an aluminum coating layer and dried, and the coating amount of the white pigment coating layer of the present invention is 5 g / m 2 . A magnetic recording paper was obtained.
実施例２ 水性アルミ塗料配合組成を下記に変へた以外は実施例１
と同様にし、塗被量が5g/m2のアルミ塗被層および塗被
量が2g/m2の白色顔料塗被層を設け、本発明の磁気記録
紙を得た。Example 2 Example 1 except that the composition of the water-based aluminum coating composition was changed to the following.
In the same manner as, laydown an aluminum coating layer and a coverage of from 5 g / m 2 is provided with a white pigment coated layer of 2 g / m 2, to obtain a magnetic recording sheet of the present invention.
水性アルミ塗料配合組成 重量部 アルミペーストAW−10 100 （ノンリーフイングタイプ） 分散剤 ５ ポリビニルアルコール ３ ソープレスアクリルエマルジヨン 60 実施例３ 実施例１と同様にし、下記水性アルミ塗料配合組成およ
び水性白色顔料塗料配合組成で塗被量が、3g/m2のアル
ミ塗被層および塗被量が、5g/m2の白色顔料塗被層を設
け、スーパーキヤレンダー仕上げをし本発明の磁気記録
紙を得た。Aqueous aluminum paint compounding composition by weight Aluminum paste AW-10 100 (non-leafing type) Dispersant 5 Polyvinyl alcohol 3 Sopress acrylic emulsion 60 Example 3 The same aqueous aluminum paint compounding composition and aqueous white pigment as in Example 1 were prepared. The coating amount in the coating composition, the aluminum coating layer of 3 g / m 2 and the coating amount, the white pigment coating layer of 5 g / m 2 is provided, the magnetic recording paper of the present invention with a super-calendered finish. Obtained.
水性アルミ塗料配合組成 重量部 アルミペースト0500M 100 （リーフイングタイプ） 分散剤 ３ カゼイン 10 アンモニア １ カルボキシ変性メチルメタアクリレート・ ブタジエンラテツクス 50 水性白色顔料塗被組成配合 重量部 カオリン 75 炭酸カルシウム 25 トリポリリン酸ソーダ 0.3 カゼイン ７ アンモニア 0.7 スチレン・ブタジエンラテツクス 16 実施例４ 水性アルミ塗料配合組成を下記に変へた以外は実施例３
と同様にし、塗被量が5g/m2のアルミ塗被層および塗被
量が3g/m2の白色顔料塗被層を設け本発明の磁気記録紙
を得た。Composition of water-based aluminum paint Part by weight Aluminum paste 0500M 100 (Leafing type) Dispersant 3 Casein 10 Ammonia 1 Carboxy-modified methylmethacrylate butadiene latex 50 Water-based white pigment coating composition Weight part Kaolin 75 Calcium carbonate 25 Sodium tripolyphosphate 0.3 Casein 7 Ammonia 0.7 Styrene-Butadiene Latex 16 Example 4 Example 3 except that the composition of the water-based aluminum coating composition was changed to the following.
In the same manner as, laydown an aluminum coating layer and a coverage of from 5 g / m 2 was obtained a magnetic recording sheet of the present invention is provided with a white pigment coating layer of 3 g / m 2.
水性アルミ塗料配合組成 重量部 アルミペーストAW−500B 100 （ノンリーフイングタイプ） 分散剤 ４ カゼイン 20 アクリルエマルジヨン 80 比較例１ 実施例１において、磁気記録層およびアルミ塗被層を設
けただけの磁気記録紙を比較用とした。Composition of water-based aluminum paint Part by weight Aluminum paste AW-500B 100 (Non-leafing type) Dispersant 4 Casein 20 Acrylic emulsion 80 Comparative Example 1 In Example 1, magnetic recording was performed only by providing a magnetic recording layer and an aluminum coating layer. Paper was used for comparison.
比較例２ 実施例１において、磁気記録層を設けただけの磁気記録
紙を比較用とした。Comparative Example 2 In Example 1, the magnetic recording paper only provided with the magnetic recording layer was used for comparison.
各実施例および比較例で得られた磁気記録紙について品
質試験を行なった。品質試験の結果は、次表の通りで、
本発明の磁気記録紙は、磁気記録層上にアルミ塗被層お
よび白色顔料塗被層を設けても磁気特性を全く損なうこ
となく、隠敝性の優れた白色度64％以上の白色度の高い
磁気記録層を得ることが出来、印刷性を付与することが
出来た。そして、発券適性にも何等支障がなく、本発明
の磁気記録紙は、満足の行くものであることが判る。A quality test was conducted on the magnetic recording papers obtained in the respective examples and comparative examples. The results of the quality test are as shown in the table below.
The magnetic recording paper of the present invention has a whiteness of 64% or more with excellent concealability without impairing the magnetic properties even if an aluminum coating layer and a white pigment coating layer are provided on the magnetic recording layer. A high magnetic recording layer could be obtained and printability could be imparted. Further, it can be seen that the ticketing suitability is not hindered and the magnetic recording paper of the present invention is satisfactory.
Claims (1)
する磁性塗料を塗被し、磁気記録層を設け、次いで、該
磁気記録層上に、アルミニユーム粉末と接着剤とを主成
分とする水性アルミ塗料を塗被し、アルミ塗被層を設
け、更に、該アルミ塗被層上に、白色顔料と接着剤とを
主成分とする水性白色顔料塗料を塗被し、白色度64％以
上の白色顔料塗被層を設けたことを特徴とする磁気記録
紙。1. A base paper is coated with a magnetic paint containing magnetic powder and an adhesive as main components to form a magnetic recording layer, and then the aluminum powder and the adhesive are mainly formed on the magnetic recording layer. A water-based aluminum paint as a component is applied to form an aluminum coating layer, and further, an aqueous white pigment paint containing a white pigment and an adhesive as a main component is applied onto the aluminum coating layer to obtain a whiteness degree. Magnetic recording paper provided with a coating layer of white pigment of 64% or more.