JPH07279037A - Knit fabric having ultrahigh strechability and its production - Google Patents
Knit fabric having ultrahigh strechability and its productionInfo
- Publication number
- JPH07279037A JPH07279037A JP9919994A JP9919994A JPH07279037A JP H07279037 A JPH07279037 A JP H07279037A JP 9919994 A JP9919994 A JP 9919994A JP 9919994 A JP9919994 A JP 9919994A JP H07279037 A JPH07279037 A JP H07279037A
- Authority
- JP
- Japan
- Prior art keywords
- yarn
- water
- soluble
- knitted
- knitted fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明はウ−リ−加工糸と水溶性
糸とを使用した編物を水溶性糸を溶出せしめて製造され
た従来のメリヤス生地よりも伸縮性の優れた、またゴム
の伸縮度と同程度又はそれ以上に特に経方向に超高伸縮
性を有する超高伸縮性のメリヤス生地とその製造法に関
するものである。BACKGROUND OF THE INVENTION The present invention relates to a knitted fabric using woolly textured yarn and water-soluble yarn, which is more elastic than a conventional knitted fabric produced by eluting the water-soluble yarn, and rubber. The invention relates to an ultrahigh-stretch knitted fabric having a degree of elasticity equal to or higher than the above, and particularly, an ultrahigh-stretchability in the warp direction, and a method for producing the same.
【０００２】[0002]
【従来の技術】従来一般に緯メリヤス、経メリヤス生地
は通常の平織の織物に比較すれば伸縮性は大であるが、
経編みの場合、緯編みの場合、何れもゴム糸やゴム織物
の伸縮性と比較すれば著しく小さく、ゴムの薄い層をサ
ンドイツチ状に挟んだメリヤス生地はゴムの高伸縮性を
充分生かすことができないうらみがある。2. Description of the Related Art Generally, weft knitted fabrics and warp knitted fabrics have greater elasticity than ordinary plain weave fabrics,
In the case of warp knitting and weft knitting, both are significantly smaller than the elasticity of rubber threads and rubber fabrics, and knitted fabrics with a thin layer of rubber sandwiched in the shape of Saint-Gerache can make full use of the high elasticity of rubber. There is an envy that I cannot do.
【０００３】[0003]
【発明が解決しようとする課題】上記従来のメリヤス生
地に鑑み、本発明はウ−リ−加工糸と水溶性糸とを使用
し、更にそれぞれの糸の編む針のフツクの大きさを変化
させ、即ちウ−リ−加工糸には編む針のフツクを大に
し、水溶性糸には編む針のフツクを小さくしてウエルト
平織組織の編生地、所謂ウエルト天竺編みを作成し、該
編物から湯で水溶性糸を溶出することによつて製造され
た超高伸縮性の特に経方向に伸縮性の大なるウエルト天
竺編生地並びにその製造法を提供することを目的とする
ものである。In view of the above-mentioned conventional knitted fabric, the present invention uses a wooly textured yarn and a water-soluble yarn and further changes the size of the hook of the knitting needle of each yarn. That is, by making the hook of the knitting needle large for the woolly processed yarn and making the hook of the knitting needle small for the water-soluble yarn, a knitted fabric with a welt plain weave structure, so-called welt soft knitting is created, and the knitted fabric is melted into hot water. It is an object of the present invention to provide an ultrahigh-stretch welted cloth with knitted fabric which is produced by eluting the water-soluble yarn with a large amount of elasticity in the warp direction and a method for producing the same.
【０００４】[0004]
【課題を解決するための手段】本発明の第１はいわゆる
天竺編、スム−ス編、フライス編（以下天竺編と総称す
る）と称されるメリヤス生地の製造法において、人造繊
維又は合成繊維のウ−リ−加工糸（以下ウ−リ−加工糸
という）と水溶性糸とを給糸口にたがいちがいに入れて
メリヤス生地を編出し、編成された生地を２５℃以上の
湯で処理して水溶性糸を溶解せしめ、ついでヒ−トセツ
トして仕上げをすることを特徴とする超高伸縮性メリヤ
ス生地の製造法であり、その第２は天竺編と称されるメ
リヤス生地の製造法において、ウ−リ−加工糸と水溶性
糸とを給糸口にたがいちがいに入れて編出された生地を
２５℃以上の湯で処理されて水溶性糸が溶解され、かつ
編出し生地をヒ−トセツトされてなることを特徴とする
超高伸縮性のメリヤス生地であり、その第３はウ−リ−
加工糸と水溶性糸とを供糸口をたがいちがいに入れて編
み、ウ−リ−加工糸の編む針には針のフツクの大きい針
を使用し、水溶性糸の編む針には針のフツクの小さい針
を使用し、この両者の針によつて編出される編物の編目
にテンシヨンを掛け、ウ−リ−加工糸の編目を荒くし、
水溶性糸には編目を詰めてメリヤス生地を編出し、かつ
編生地を２５℃以上の湯で処理して、水溶性糸を溶解せ
しめ、ついで編生地をヒ−トセツトして仕上げをするこ
とを特徴とする超高伸縮性を有するメリヤス生地の製造
法であり、その第４はウ−リ−加工糸と水溶性糸とを給
糸口にたがいちがいに入れ、ウ−リ−加工糸を編む針に
はフツクの大きい針を使用し、水溶性糸を編む針にはフ
ツクの小さい針を使用し、この両者の針によつて編出さ
れる編目をウ−リ−加工糸は目を荒く、水溶性糸は編目
を詰めることによつて編成し、それによつて編出された
メリヤス生地を、２５℃以上の湯で処理して水溶性糸が
溶出され、かつ編生地がヒ−トセツトされてなることを
特徴とする超高伸縮性を有するメリヤス生地に関するも
のである。The first aspect of the present invention is a method for producing a knitted fabric called a so-called tenjiji knitting, a smooth knitting, and a milling knitting (hereinafter collectively referred to as tenjiku knitting), which is an artificial fiber or a synthetic fiber. The woolly textured yarn (hereinafter referred to as the wooly textured yarn) and the water-soluble yarn are put into the yarn feeder in a pair of knitting yarns to knit a knitted fabric, and the knitted fabric is treated with hot water at 25 ° C or higher. Is a method for producing a super-high stretch knitted fabric, which is characterized by dissolving water-soluble yarns and then heat-setting to finish. The second is a method for producing a knitted fabric called Tenjiku knitting. , The wooly textured yarn and the water-soluble yarn are put into the yarn feeder in a pair and then the knitted fabric is treated with hot water at 25 ° C. or higher to dissolve the water-soluble yarn and Super stretchable meri characterized by being set Is a scan fabrics, the third c - Li -
Put the processed yarn and the water-soluble yarn in the yarn feeder and knit them.Use the needle with a large hook for the knitting of the wooly processed yarn.Use the needle hook for the needle of the water-soluble yarn. Using a small needle of, the tension of the knitting of the knitted fabric knitted by both needles is applied to roughen the stitches of the woolly processed yarn,
Knitting the water-soluble yarn with stitches, knitting the knitted fabric, treating the knitted fabric with hot water at 25 ° C or higher to dissolve the water-soluble yarn, and then heat-setting the knitted fabric for finishing. A knitting needle for knitting a wooly textured yarn by putting a wooly textured yarn and a water-soluble yarn in the yarn feeder in a pair to form a knitted fabric having a super-high elasticity. A needle with a large hook is used for the needle and a needle with a small hook is used for the needle for knitting the water-soluble thread, and the stitches that are knitted by these needles are The sex yarn is knitted by packing the knitting, and the knitted fabric knitted thereby is treated with hot water at 25 ° C or higher to dissolve the water-soluble yarn, and the knitted fabric is heat-set. The present invention relates to a knitted fabric having ultra-high elasticity.
【０００５】本発明は素材としてウ−リ−加工糸と水溶
性糸とを使用し、編機としては丸編機（Ｒ２８″，２４
Ｇ，２８６４本）を使用した。 生成幅 １７０cm（ｍ／ｇ），１４５ｇ 加工上り幅 １４５cm（ｍ／ｇ），１２０ｇ の規格に編み上げた。In the present invention, wooly textured yarn and water-soluble yarn are used as materials, and a circular knitting machine (R28 ", 24) is used as a knitting machine.
G, 2864). Generation width 170 cm (m / g), 145 g Processing finished width 145 cm (m / g), knitted to the standard of 120 g.
【０００６】本発明に使用の例えば丸編機（福原産業株
式会社製を使用）において、先ずウ−リ−加工糸と水溶
性糸とを重量比１：１でコ−ドレイン調に、即ち給糸口
にたがいちがいに入れて編立てをするのであるが、ウ−
リ−加工糸を編む針には針のフツクの大きいものを使用
し、水溶性糸を編む針には針のフツクを小さくする。こ
の種の針によつて本発明の所謂ウエルト天竺編が編出さ
れる。編目に上の方のダイヤルの吸い込み即ち編目のニ
ツト目を作る山のウ−リ−加工糸にテンシヨンを掛け、
同様に下の方のシリンダ−のウ−リ−加工糸にもテンシ
ヨンを掛けるようにする。また水溶性糸の方には上の方
のダイヤルも下の方のシリンダ−も共にテンシヨンを掛
けず、ウ−リ−加工糸：水溶性糸＝２：１の割合で送り
込むようにする。かつ丸編機の上のダイヤルと下のシリ
ンダ−とに入つている針のフツクの大きいウ−リ−加工
糸の編目を無くし、針のフツクの小さい水溶性糸には編
目を詰めるようにする。上記のようにして本発明の所謂
ウエルト天竺編が編出される。この編出された生地の水
溶性糸を２５℃以上の湯で溶出して、場合によつては種
々の色に染色して１２０℃以上でヒ−トセツトして仕上
げをする。In a circular knitting machine (used by Fukuhara Sangyo Co., Ltd.) used in the present invention, first, a wooly textured yarn and a water-soluble yarn are mixed in a weight ratio of 1: 1 in a co-drain style, that is, in a feeding manner. The knitting is done by putting it in a tug of warp at the yarn end.
The needle for knitting the re-processed yarn should have a large hook and the needle for knitting the water-soluble yarn should have a small hook. With this type of needle, the so-called welt stitch knitting of the present invention is set up. Suction the upper dial to the stitch, that is, apply tension to the woolly processed yarn of the mountain that makes the stitch of the stitch.
Similarly, tension is applied to the wooly textured yarn of the lower cylinder. Further, neither the upper dial nor the lower cylinder is tensioned with respect to the water-soluble yarn, and the wooly processed yarn: water-soluble yarn = 2: 1 is fed. Also, eliminate the stitches of the wooly-processed yarn with the large hooks of the needles that are contained in the upper dial and the lower cylinder of the circular knitting machine, and fill the stitches with the water-soluble yarns with the small hooks of the needles. . As described above, the so-called welted cloth of the present invention is created. The water-soluble yarns of the knitted fabric are eluted with hot water at 25 ° C or higher, dyed in various colors in some cases, and heat-set at 120 ° C or higher for finishing.
【０００７】ウ−リ−加工糸としては捲縮人造繊維、ナ
イロン、ポリエステル、ビニロン、アクリルの糸のウ−
リ−加工糸及びそれらの混紡糸が使用され、特にウ−リ
−ナイロン加工糸又はウ−リ−ポリエステル加工糸が好
適に使用される。捲縮人造繊維のみでは糸の強度が低
く、合成繊維との混紡糸が好適に使用される。また水溶
性糸はＣＭＣ糸（カルボキシメチルセルロ−ス糸）、Ｃ
ＥＣ糸（カルボキシエチルセルロ−ス糸）、アルギン酸
繊維糸又は水溶性ポリビニルアルコ−ル糸が使用され
る。特に水溶性ポリビニルアルコ−ル糸が好適に使用さ
れる。それぞれの糸の太さやフイラメント数は編出され
る超高伸縮性メリヤス生地、特に経方向に高伸縮メリヤ
ス生地に好適な糸の太さ、フイラメント数を選択して使
用することが可能である。As the wooly processed yarn, a crimped artificial fiber, nylon, polyester, vinylon, acrylic yarn wool is used.
A textured yarn and a blended yarn thereof are used, and a textured wooly nylon or textured wooly polyester is particularly preferably used. The crimped artificial fiber alone has a low yarn strength, and a blended yarn with a synthetic fiber is preferably used. The water-soluble thread is CMC thread (carboxymethyl cellulose thread), C
EC yarn (carboxyethyl cellulose yarn), alginic acid fiber yarn or water-soluble polyvinyl alcohol yarn is used. In particular, water-soluble polyvinyl alcohol yarn is preferably used. Regarding the thickness and the number of filaments of each thread, it is possible to select and use the thread thickness and the number of filaments which are suitable for the super-high-stretch knitted fabric to be knitted, particularly the highly stretchable knitted fabric in the warp direction.
【０００８】[0008]
【実施例】４０〜１５０ｄ／２０〜４０フイラメント
（Ｆ）のウ−リ−ナイロン加工糸と２０〜1000ｄ／１〜
１５０Ｆの水溶性ポリビニルアルコ−ル糸とを上記した
Ｒ２８″、２４Ｇ 2864本、丸編機（福原産業株式会社
製）を使用して、 生成幅 １７０cm（ｍ／ｇ），１４５ｇ 加工上り幅 １４７cm（ｍ／ｇ），２００ｇ に仕上げた。この場合のウ−リ−ナイロン加工糸と水溶
性ポリビニルアルコ−ル糸とを１：１にコ−ドレイン調
に、即ち給糸口にたがいちがいに入れて編み、先ずウ−
リ−ナイロン加工糸を編む針には針のフツクを大きく
し、また水溶性ポリビニルアルコ−ル糸で編む針には糸
のフツクを小さくし、この両方の針によつて編出される
編目に上のダイヤルの吸い込み（編目を作る山の部
分）、即ちウ−リ−ナイロン加工糸の方にテンシヨンを
掛け、下のシリンダ−にも同様にウ−リ−ナイロン加工
糸にテンシヨンを掛ける。また水溶性ポリビニルアルコ
−ル糸の方は上のダイヤルも下のシリンダ−も先にテン
シヨンを掛けず、ウ−リ−ナイロン加工糸：水溶性ポリ
ビニルアルコ−ル糸の送り速度を２：１として送り込む
ようにする。上のダイヤル、下のシリンダ−に入つてい
る針のフツクの大きいウ−リ−ナイロン加工糸の編目を
荒くし、針のフツクの小さい水溶性ポリビニルアルコ−
ル糸には編目を詰めるようにする。このようにしてウエ
ルト天竺編が編出される。この編出された生地を水溶性
ポリビニルアルコ−ル糸を溶出するために６０℃の熱湯
で処理し、ポリビニルアルコ−ル糸の溶出処理は２５℃
以上、１００℃以下であればよい。染色でブラツクに染
めて160 ℃でヒ−トセツトをして仕上げた。EXAMPLE 40-150 d / 20-40 filament (F) wooly nylon processed yarn and 20-1000 d / 1-
Using R28 ″, 24G 2864 filaments and circular knitting machine (manufactured by Fukuhara Sangyo Co., Ltd.) with 150 F water-soluble polyvinyl alcohol yarn, production width 170 cm (m / g), 145 g processing rising width 147 cm ( m / g), 200 g, in which case the wooly nylon processed yarn and the water-soluble polyvinyl alcohol yarn are knitted in a 1: 1 cord-rain style, that is, put into the yarn feeder in a pair and knitted. First of all,
The needle for knitting nylon-processed yarn has a large needle hook, and the needle for knitting with water-soluble polyvinyl alcohol yarn has a small needle hook. The suction of the dial of (2) (the portion of the mountain where the stitch is formed), that is, the tension on the wooly nylon processed yarn is applied, and the tension on the wooly nylon processed yarn is also applied to the lower cylinder. For the water-soluble polyvinyl alcohol yarn, neither the upper dial nor the lower cylinder is tensioned first, and the feeding speed of wooly nylon processed yarn: water-soluble polyvinyl alcohol yarn is set to 2: 1. I will send it in. Wool with large hook in the upper dial and lower cylinder-Woolly made of nylon-processed yarn with coarse stitches, water-soluble polyvinyl alcohol with small needle hook
The stitches should be packed in the le thread. In this way, the Welt Tenjiku edition is created. The knitted fabric is treated with hot water at 60 ° C to dissolve the water-soluble polyvinyl alcohol yarn, and the polyvinyl alcohol yarn is eluted at 25 ° C.
As long as it is 100 ° C. or lower, it is sufficient. It was dyed in black by dyeing and heat-set at 160 ° C for finishing.
【０００９】本発明のウエルト天竺編の製品は経、緯の
伸度、特に経の伸度が下記に示すように著しく大で、ゴ
ムの薄片をサンドウイツチ状に挟み込んで接着してゴム
の縦、横の高伸度、高収縮によく耐え、破れたり、布の
形態がくずれることが全くない。超高伸縮性を利用した
インナ−その他の衣料製品、水着、ウエツトス−ツ、レ
オタ−ド、各種トレ−ニングウエア−、その他スポ−ツ
用品、湿布薬の裏張り生地、サポ−タ、その他の衣料品
用等の用途に好適に使用される。The product of the welted plain knitted fabric of the present invention has remarkably large warp and weft elongations, in particular, warp elongations, as shown below. Withstands high lateral elongation and high shrinkage, and does not tear or break the shape of the fabric. Inner and other clothing products that utilize ultra-high elasticity, swimwear, wetsuits, leotards, various training wear, other sporting goods, backing cloth for poultices, supporters, etc. It is preferably used for applications such as clothing.
【００１０】本発明のメリヤス生地の経、緯の伸度。Ｊ
ＩＳ Ｌ１０１８、メリヤス生地試験方法（グラブ法）
により試験した結果を下の表に示した。 試験条件：試験機の種類、定速伸長形式、引張伸度 １
０cm/min 上記に示すように本発明品は従来の比較品に対して経方
向、緯方向ともに著しく大である。The warp and weft elongation of the knitted fabric of the present invention. J
IS L1018, Knitted fabric test method (Grab method)
The results tested according to Table 1 are shown in the table below. Test conditions: type of tester, constant speed extension type, tensile elongation 1
0 cm / min As shown above, the product of the present invention is significantly larger than the conventional comparative product in both the longitudinal direction and the weft direction.
【００１１】[0011]
【発明の効果】本発明は従来のウエルト天竺編のメリヤ
ス生地に比較して著しく高伸縮度であり、特に従来のメ
リヤス生地に比較して経方向の伸縮率が大である。しか
も本発明の生地が水溶性糸を溶出しているにも拘らず、
生地が緻密でインナ−その他の衣料製品、水着、ウエツ
トス−ツその他のスポ−ツ用等のはげしい使用に耐え、
長期の使用が可能である。INDUSTRIAL APPLICABILITY The present invention has a remarkably high degree of expansion and contraction as compared with the conventional knitted fabric of welted cloth, and particularly has a large expansion and contraction rate in the longitudinal direction as compared with the conventional knitted fabric. Moreover, despite the fact that the fabric of the present invention elutes the water-soluble yarn,
The material is dense and can withstand heavy use such as inner and other clothing products, swimwear, wet suits and other sports,
It can be used for a long time.
Claims (6)
編（以下天竺編と総称する）と称されるメリヤス生地の
製造法において、人造繊維又は合成繊維のウ−リ−加工
糸（以下ウ−リ−加工糸という）と水溶性糸とを給糸口
にたがいちがいに入れてメリヤス生地を編出し、編成さ
れた生地を２５℃以上の湯で処理して水溶性糸を溶解せ
しめ、ついでヒ−トセツトして仕上げをすることを特徴
とする超高伸縮性メリヤス生地の製造法。1. In a method for producing a knitted fabric called so-called “Tenji-knit”, “Smooth” knitting, or “Milling” knitting (hereinafter collectively referred to as “Tenji-knitting”), a woolly processed yarn of artificial fiber or synthetic fiber -Re-processed yarn) and a water-soluble yarn are put into the yarn feeder in a pair of pieces to knit a knitted fabric, and the knitted fabric is treated with hot water at 25 ° C or higher to dissolve the water-soluble yarn, and then -A method for producing super-high-stretch knitted fabrics, which is characterized by finishing and finishing.
において、ウ−リ−加工糸と水溶性糸とを給糸口にたが
いちがいに入れて編出された生地を２５℃以上の湯で処
理されて水溶性糸が溶解され、かつ編出生地をヒ−トセ
ツトされてなることを特徴とする超高伸縮性のメリヤス
生地。2. In a method for producing a knitted fabric called "Tenji-knit", a fabric formed by putting a wooly textured yarn and a water-soluble yarn into a yarn feeder in a pair of tapers and braided the mixture in hot water at 25 ° C. or higher. A super-high stretch knitted fabric which is characterized in that it is treated to dissolve the water-soluble yarn, and the knitted fabric is heat-set.
たがいちがいに入れて編み、ウ−リ−加工糸の編む針に
はフツクの大きい針を使用し、水溶性糸を編む針にはフ
ツクの小さい針を使用し、この両者の針によつて編出さ
れる編物の編目にテンシヨンを掛け、ウ−リ−加工糸の
編目を荒くし、水溶性糸には編目を詰めてメリヤス生地
を編み出し、編成された生地を２５℃以上の湯で処理し
て、水溶性糸を溶解せしめ、ついでヒ−トセツトして仕
上げをすることを特徴とする超高伸縮性を有するメリヤ
ス生地の製造法。3. A woolly textured yarn and a water-soluble yarn are knitted by putting them in a pair at the yarn feeder, and a needle with a large hook is used for knitting the wooly textured yarn. A small hook is used as the knitting needle, a tension is applied to the stitches of the knitted fabric that is knitted by these needles, the stitches of the wooly textured yarn are roughened, and the stitches of the water-soluble yarn are packed. The knitted fabric is knitted, and the knitted fabric is treated with hot water at 25 ° C or higher to dissolve the water-soluble yarn and then heat-set to finish the knitted fabric. Manufacturing method.
たがいちがいに入れ、ウ−リ−加工糸を編む針にはフツ
クの大きい針を使用し、水溶性糸を編む針にはフツクの
小さい針を使用し、この両者の針によつて編出される編
目をウ−リ−加工糸は荒く、水溶性糸は編目を詰め、そ
れによつて編出されたメリヤス生地を２５℃以上の湯で
処理されて水溶性糸が溶出され、かつ編生地をヒ−トセ
ツトされてなることを特徴とする超高伸縮性を有するメ
リヤス生地。4. A needle for knitting a water-soluble yarn, in which a woolly textured yarn and a water-soluble yarn are put into a yarn feeder in a pair and a needle having a large hook is used for knitting the wooly textured yarn. For this, a small hook is used, and the stitches that are knitted by both needles are coarse, the wooly textured yarn is coarse, and the water-soluble yarn is filled with the stitches. A knitted fabric which is treated with hot water at a temperature of ℃ or above to elute the water-soluble yarn and heat-set the knitted fabric.
加工糸又はウ−リ−ポリエステル加工糸、水溶性糸とし
てポリビニルアルコ−ル糸を使用する請求項１又は３記
載の超高伸縮性メリヤス生地の製造法。5. The ultra-high stretchability according to claim 1 or 3, wherein a wooly textured yarn or wooly polyester textured thread is used as the wooly textured thread, and a polyvinyl alcohol thread is used as the water soluble thread. Method of manufacturing sex knit fabric.
加工糸又はウ−リ−ポリエステル加工糸、水溶性糸とし
てポリビニルアルコ−ル糸を使用する請求項２又は４記
載の超高伸縮性メリヤス生地。6. The ultra-high stretch according to claim 2, wherein the wooly textured yarn is a wooly nylon textured yarn or a wooly polyester textured yarn, and the water soluble yarn is a polyvinyl alcohol yarn. Sex knit fabric.