JPH07246684A - Decorative sheet - Google Patents
Decorative sheetInfo
- Publication number
- JPH07246684A JPH07246684A JP6545594A JP6545594A JPH07246684A JP H07246684 A JPH07246684 A JP H07246684A JP 6545594 A JP6545594 A JP 6545594A JP 6545594 A JP6545594 A JP 6545594A JP H07246684 A JPH07246684 A JP H07246684A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- layer
- resin
- impregnated
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は家具、キヤビネツト、学
習机等の表面化粧に使用可能であり、且つラツピング加
工、Ｖカツト加工にも使用できる紙を基材とした低価格
な化粧シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a paper-based low-cost decorative sheet which can be used for surface makeup of furniture, cabinets, study desks, etc. and can also be used for wrapping and V-cutting.
【０００２】[0002]
【従来の技術】従来、水平面用の化粧シートの代表的な
ものは高圧メラミン化粧板やジアリルフタレート化粧シ
ートが使用されているが、これらは物理的及び化学的性
質は優れているものの、含浸工程、プレス工程を要する
ので、大がかりな製造設備を必要とし高価なものになる
上に、柔軟性がないためラツピング加工ないしＶカツト
加工には不向きなものであつた。それに替わるものとし
て硬質のポリ塩化ビニルシートを使用したものないしは
印刷紙に樹脂含浸を施した紙を使用したもの等が考えら
れるが、両者共にラツピング加工ないしＶカツト加工の
加工適性は備えているが、前者は局部荷重ふくれ（クリ
ープ）、耐熱性の問題があり表面の物理的及び化学的性
質が劣る、また後者のものでは耐磨耗性、紙の層間剥離
等の物理的性質が不充分であるという欠点があつた。2. Description of the Related Art Conventionally, high-pressure melamine decorative boards and diallylphthalate decorative sheets have been used as typical decorative sheets for horizontal surfaces, but these have excellent physical and chemical properties, but impregnation process Since it requires a pressing step, it requires a large-scale manufacturing facility and is expensive, and it is not suitable for lapping or V-cutting due to its lack of flexibility. As an alternative, one using a hard polyvinyl chloride sheet or one using a paper impregnated with a printing paper is conceivable, but both of them have processing suitability for lapping or V-cutting. , The former has a problem of local load swelling (creep) and heat resistance, and the physical and chemical properties of the surface are inferior, while the latter has insufficient physical properties such as abrasion resistance and delamination of paper. There was a shortcoming.
【０００３】[0003]
【発明が解決しようとする課題】本発明の目的は、局部
荷重ふくれが発生せず、耐磨耗性、耐熱性に優れた、水
平面での使用が可能であるとともに、ラツピング加工な
いしＶカツト加工にも適した、焼却時に有害ガスが発生
しないので公害の問題のない、低価格な化粧シートを提
供することである。SUMMARY OF THE INVENTION The object of the present invention is to prevent local load swelling, to have excellent wear resistance and heat resistance, to be used on a horizontal surface, and to perform lapping or V-cutting. It is also an object of the present invention to provide a low-priced decorative sheet that is also suitable for use as it does not generate harmful gas during incineration and does not cause pollution problems.
【０００４】[0004]
【課題を解決するための手段】保護層、印刷層、表裏両
面へのコーテイングにより熱硬化性樹脂が含浸された第
１紙層、接着剤層、表面ないし表裏両面へのコーテイン
グにより熱硬化性樹脂が含浸された第２紙層を順に積層
した構成からなることを特徴とする化粧シートである。[Means for Solving the Problems] Protective layer, printing layer, first paper layer impregnated with thermosetting resin by coating on both front and back surfaces, adhesive layer, thermosetting resin by coating on front surface and front and back surfaces A decorative sheet having a configuration in which second paper layers impregnated with are laminated in order.
【０００５】前記接着剤層が２液硬化型ウレタン樹脂、
エポキシ樹脂、押出ポリオレフイン樹脂のいずれかから
なることを特徴とする上記の化粧シートである。The adhesive layer is a two-component curing type urethane resin,
The decorative sheet is made of either an epoxy resin or an extruded polyolefin resin.
【０００６】第１紙層及び第２紙層のそれぞれ片面に、
コーテイングにより熱硬化性樹脂を含浸させ、前記第１
紙層及び前記第２紙層の熱硬化性樹脂を含浸させた面同
志を接着剤により貼合し、前記第１紙層の非貼合面にコ
ーテイングにより熱硬化性樹脂を含浸させ、その面に印
刷層及び保護層を形成することを特徴とする化粧シート
の製造方法である。On one side of each of the first paper layer and the second paper layer,
The thermosetting resin is impregnated by coating, and the first
The thermosetting resin-impregnated surfaces of the paper layer and the second paper layer are bonded together with an adhesive, and the non-bonded surface of the first paper layer is impregnated with the thermosetting resin by coating, and the surfaces are bonded together. A method for producing a decorative sheet, comprising forming a printing layer and a protective layer on the surface.
【０００７】[0007]
【作用】化粧シートの基材を、それぞれコーテイングに
より熱硬化性樹脂を含浸させた第１紙層及び第２紙層の
２層の積層体で構成することにより、基材に厚みをもた
せることができると共に、基材として紙を使用している
にかかわらず層間強度が強いため、平面化粧用途に使用
しても局部荷重ふくれが発生せず、且つラツピング加工
ないしＶカツト加工にも使用可能な低価格の化粧シート
が得られる。The base material of the decorative sheet can be made thick by forming the base material of the decorative sheet with a laminate of two layers of the first paper layer and the second paper layer, each of which is impregnated with the thermosetting resin by coating. In addition, since the interlayer strength is strong regardless of using paper as the base material, local load swelling does not occur even when it is used for flat makeup, and it can be used for lapping or V-cutting. You can get a decorative sheet at a reasonable price.
【０００８】[0008]
【実施例】以下、図面を引用して本発明を説明する。図
１は本発明の化粧シートの積層構成を示す図であつて、
１は第１紙層、２は第２紙層、３は接着剤層、４は印刷
層、4aはベタ印刷層、4bは絵柄印刷層、５は保護層をそ
れぞれ表す。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below with reference to the drawings. FIG. 1 is a diagram showing a laminated structure of a decorative sheet of the present invention,
Reference numeral 1 is a first paper layer, 2 is a second paper layer, 3 is an adhesive layer, 4 is a printing layer, 4a is a solid printing layer, 4b is a pattern printing layer, and 5 is a protective layer.
【０００９】本発明の化粧シートの構成は図１に示すよ
うに、紙の両面へのコーテイングにより熱硬化性樹脂が
含浸された第１紙層１と、紙の片面ないし両面へのコー
テイングにより熱硬化性樹脂が含浸された第２紙層２と
を接着剤層３により積層した基材の第１紙層１の表面に
ベタ印刷層4aと絵柄印刷層4bからなる印刷層４を設け、
その全面を覆つて保護層５が形成された構成からなる。As shown in FIG. 1, the constitution of the decorative sheet of the present invention is such that the first paper layer 1 impregnated with the thermosetting resin by coating on both sides of the paper and the heat treatment by coating on one side or both sides of the paper. A printing layer 4 comprising a solid printing layer 4a and a pattern printing layer 4b is provided on the surface of the first paper layer 1 of the base material in which the second paper layer 2 impregnated with the curable resin is laminated with the adhesive layer 3.
The protective layer 5 is formed so as to cover the entire surface.
【００１０】第１紙層１に使用する紙としては、晒ケミ
カルパルプを原料とし長網、円網等のヤンキーマシンで
抄造した片艶の薄葉紙で、白色度が高く紙質強度の大き
い建材用プリント用紙を使用する。紙の厚さとしては坪
量２３〜６５ｇ／ｍ2 のものが使用できるが、２３〜３
０ｇ／ｍ2 の厚さのものが適当である。第１紙層１とし
て、上記のような表面が平滑な片艶の薄葉紙を使用し、
平滑面に印刷を行うことにより優れた印刷適性が得られ
る。第２紙層２として、第１紙層１に使用する紙と同質
の紙を使用するか、ないしはクラフトパルプからなる紙
質強度の大きい上質紙等が使用できる。第２紙層２には
印刷を行わないので表面平滑性は必要でない。厚さとし
ては坪量２３〜６５ｇ／ｍ2 のものが適当である。第１
紙層１ないし第２紙層２に使用する紙として、上記の紙
以外にアクリルアミド、エポキシアミド等を添加して紙
間強度を強くした紙間強化紙を使用してもよい。The paper used for the first paper layer 1 is a single-gloss thin paper made from bleached chemical pulp as a raw material by a Yankee machine such as a Fourdrinier or a cylinder, and has a high whiteness and a strong paper quality. Use paper. As for the thickness of the paper, a paper having a basis weight of 23 to 65 g / m 2 can be used, but it is 23 to 3
A thickness of 0 g / m 2 is suitable. As the first paper layer 1, a thin luster paper having a smooth surface as described above is used,
By printing on a smooth surface, excellent printability can be obtained. As the second paper layer 2, paper of the same quality as the paper used for the first paper layer 1 can be used, or high-quality paper made of kraft pulp having high paper strength can be used. Since the second paper layer 2 is not printed, surface smoothness is not required. The suitable thickness is 23 to 65 g / m 2 . First
As the paper used for the paper layer 1 or the second paper layer 2, in addition to the above-mentioned paper, a paper-reinforced paper having an increased paper-to-paper strength by adding acrylamide, epoxyamide or the like may be used.
【００１１】第１紙層１及び第２紙層２への樹脂の含浸
は、樹脂液中へデイツピングする方法ではなく、グラビ
ア印刷用ベタ版を使用したグラビアコートないしはコー
ターを使用したロールコート等により、紙の表面に樹脂
液を塗布し表面から樹脂液を紙の層間に含浸させるよう
にして行う。上記方法をとることによりグラビア印刷機
ないしはコーターにより容易に紙への樹脂液の含浸を実
施することができる。第１紙層１への樹脂の含浸は紙の
表裏両面から行うのであるが、紙表面の平滑面への樹脂
の含浸においては表面の平滑性が損なわれないようにす
る必要がある。第２紙層２への樹脂の含浸は、紙の表裏
両面含浸を行つてもよいが、紙の第１紙層１と積層する
面のみに含浸するだけでもよい。他方の面は化粧シート
を合板等の基材に積層するための接着剤が紙層に浸透し
て紙の層間が強化される。The first paper layer 1 and the second paper layer 2 are not impregnated with resin by a method of dipping into a resin liquid, but by a gravure coat using a solid plate for gravure printing or a roll coat using a coater. The resin liquid is applied to the surface of the paper, and the resin liquid is impregnated between the paper layers from the surface. By using the above method, the resin solution can be easily impregnated into the paper by using a gravure printing machine or a coater. Although the first paper layer 1 is impregnated with the resin from both the front and back sides of the paper, it is necessary to prevent the smoothness of the surface from being impaired when impregnating the smooth surface of the paper with the resin. The resin may be impregnated into the second paper layer 2 by impregnating both sides of the paper, but may be impregnated only on the surface of the paper laminated with the first paper layer 1. On the other surface, an adhesive for laminating the decorative sheet on a base material such as plywood penetrates into the paper layers to strengthen the paper layers.
【００１２】含浸させる樹脂の量としては、使用する紙
の厚さにもよるが、紙のそれぞれの表面に３〜１５ｇ／
ｍ2 の範囲で塗布するのが好ましい。含浸する樹脂液の
塗布はグラビアコートないしロールコート等の方法で行
うのであるが、グラビアコートの場合には１回で塗布量
を多くするのが困難であるために、塗布量を多くする場
合にはグラビア印刷機の２ユニツト以上を使用して塗布
してもよい。未処理の紙の片面から１回のコーテイング
により塗布量を多くして樹脂を含浸させようとすると、
樹脂液が紙の裏面にまで浸透して裏抜けが発生しコーテ
イング作業に支障をきたすので、その場合には裏抜けし
ない程度の量を２回に分けて塗布し含浸させるのが好ま
しい。裏面に浸透防止層が形成されている場合には１回
のコーテイングで塗布量を多くすることができる。The amount of the resin to be impregnated depends on the thickness of the paper to be used, but is 3 to 15 g / on each surface of the paper.
It is preferable to apply in the range of m 2 . The resin solution to be impregnated is applied by a method such as gravure coating or roll coating. However, in the case of gravure coating, it is difficult to increase the application amount at one time. May be applied using two or more units of a gravure printing machine. If you try to impregnate the resin with a single coating from one side of untreated paper to increase the coating amount,
Since the resin liquid penetrates to the back surface of the paper and strike-through occurs, which hinders the coating work, in such a case, it is preferable to apply and impregnate in an amount such that the strike-through does not occur. When the permeation preventive layer is formed on the back surface, the coating amount can be increased by one coating.
【００１３】紙への含浸に使用する樹脂としては、ウレ
タン樹脂、エポキシ樹脂、不飽和ポリエステル樹脂、ジ
アリルフタレート樹脂、尿素樹脂等の熱硬化性樹脂が使
用できる。ラツピング加工、Ｖカツト加工用に使用する
場合には、上記熱硬化性樹脂の中でも柔軟性のあるタイ
プの樹脂を使用するのが好ましい。また、含浸した紙に
柔軟性をもたせるために、上記の熱硬化性樹脂にスチレ
ン−ブタジエン共重合体、アクリロニトリル−ブタジエ
ン共重合体等の合成ゴムを添加して使用することも可能
である。As the resin used for impregnating paper, thermosetting resins such as urethane resin, epoxy resin, unsaturated polyester resin, diallyl phthalate resin and urea resin can be used. When used for lapping and V-cut processing, it is preferable to use a flexible type resin among the thermosetting resins. Further, in order to impart flexibility to the impregnated paper, it is also possible to add a synthetic rubber such as a styrene-butadiene copolymer or an acrylonitrile-butadiene copolymer to the above thermosetting resin before use.
【００１４】樹脂が含浸された第１紙層１と第２紙層２
とを積層するための接着剤層３としては、ウレタン系樹
脂からなる接着剤ないしは熱溶融押出されたポリオレフ
イン系樹脂が適する。ウレタン系接着剤を使用してドラ
イラミネーシヨンにより積層する方法、エポキシ系接着
剤を使用して積層する方法が一般的であるが、ポリエチ
レン、エチレン−αオレフイン共重合体、エチレン−酢
酸ビニル共重合体等のポリオレフイン樹脂を使用して押
出ラミネーシヨンにより積層する方法を採用することも
できる。ウレタン系接着剤を使用してドライラミネーシ
ヨンする場合の接着剤の塗布量としては５〜１５ｇ／ｍ
2 の範囲であり、ポリオレフイン樹脂の押出ラミネーシ
ヨンの場合には２０〜３０ミクロンの厚さが適当であ
る。ウレタン系接着剤を使用したドライラミネーシヨン
により積層する方法では耐熱性が優れ、ポリオレフイン
樹脂を使用して押出ラミネーシヨンにより積層する方法
では柔軟性、厚さを付与することができるので用途によ
り使い分けすることが必要である。First paper layer 1 and second paper layer 2 impregnated with resin
As the adhesive layer 3 for laminating and, an adhesive made of a urethane resin or a polyolefin melt resin extruded by heat is suitable. Although a method of laminating by dry lamination using a urethane adhesive and a method of laminating using an epoxy adhesive are common, polyethylene, ethylene-α olefin copolymer, ethylene-vinyl acetate copolymer It is also possible to employ a method of laminating by means of extrusion lamination using a polyolefin resin such as coalesced. The amount of adhesive applied when dry laminating using a urethane adhesive is 5 to 15 g / m
It is in the range of 2 , with a thickness of 20 to 30 microns being suitable for extrusion lamination of polyolefin resins. Dry lamination using a urethane adhesive has excellent heat resistance, and extrusion lamination using a polyolefin resin gives flexibility and thickness, so it can be used depending on the application. It is necessary.
【００１５】印刷層４を形成するインキとしては、耐磨
耗性、含浸樹脂に対する接着性の優れたウレタン樹脂、
アクリル樹脂、メラミン樹脂等からなるインキを使用す
る。保護層５としては、ウレタン樹脂、アミノアルキツ
ド樹脂、エポキシ樹脂、尿素樹脂、メラミン樹脂等の熱
硬化性樹脂が使用できる。保護層５の厚さは５〜２０ミ
クロンの範囲で用途に応じて設定する。保護層５の艶は
上記の樹脂に炭酸カルシウム、炭酸マグネシウム、タル
ク、硫酸バリウム、シリカ、酸化チタン等の無機質充填
剤の適量添加して調整することができる。As the ink for forming the printing layer 4, a urethane resin having excellent abrasion resistance and adhesiveness to the impregnated resin,
Ink made of acrylic resin, melamine resin, etc. is used. As the protective layer 5, a thermosetting resin such as urethane resin, amino alkyd resin, epoxy resin, urea resin or melamine resin can be used. The thickness of the protective layer 5 is set in the range of 5 to 20 μm according to the application. The gloss of the protective layer 5 can be adjusted by adding an appropriate amount of an inorganic filler such as calcium carbonate, magnesium carbonate, talc, barium sulfate, silica or titanium oxide to the above resin.
【００１６】本発明の化粧シートの製造方法は、第１紙
層１を構成する片艶紙の艶のない面及び第２紙層２を構
成する紙の片面にそれぞれ樹脂をコーテイングにより含
浸させた後に、両者の樹脂含浸面同士を接着剤層３によ
り積層する。次いで上記積層体の第１紙層１を構成する
片艶紙の艶面に樹脂をコーテイングして含浸し、その面
にグラビア印刷によりベタ印刷層4aと絵柄印刷層4bから
なる印刷層４を設け、更にその上にグラビア印刷ないし
はコーテイングにより保護層を形成する。必要により第
２紙層２を構成する紙の接着面と反対の面にコーテイン
グにより樹脂を含浸して化粧シートが完成する。第２紙
層２を構成する紙の接着面と反対の面への樹脂の含浸
は、化粧シートを基材に積層する際の接着剤の含浸によ
り紙の層間が強化されるので必ずしも必要ではない。こ
のようにしてコーテイングにより紙力を強化した紙同士
を積層した複合紙は中心部が強化されているので、同等
の厚みで構成した含浸により強化した紙と比較して強化
効率がよい。In the method for producing a decorative sheet of the present invention, a resin is impregnated on the matte side of the first glossy paper constituting the first paper layer 1 and on one side of the paper constituting the second paper layer 2 by coating. Later, the resin-impregnated surfaces of both are laminated with the adhesive layer 3. Then, a resin is coated on the glossy surface of the single-sided glossy paper constituting the first paper layer 1 of the laminate to impregnate it with a printing layer 4 including a solid printing layer 4a and a pattern printing layer 4b by gravure printing. Further, a protective layer is formed thereon by gravure printing or coating. If necessary, the surface of the second paper layer 2 opposite to the adhesive surface of the paper is coated with a resin to complete the decorative sheet. It is not always necessary to impregnate the surface of the second paper layer 2 opposite to the adhesive surface of the paper with the resin, because the paper layer is reinforced by the adhesive when the decorative sheet is laminated on the base material. . Since the central portion of the composite paper in which the papers whose paper strength has been strengthened by coating are laminated in this way is reinforced, the reinforcing paper has better efficiency than papers reinforced by impregnation having the same thickness.
【００１７】本発明の化粧シートを合板等の基材にエマ
ルジヨンタイプ接着剤等を使用して積層した化粧板は、
耐磨耗性、耐熱性、耐クリープ性等の表面物性が優れて
いるので、家具、キヤビネツト、学習机等の表面化粧の
用途に使用できるし、合板にＶカツト溝を形成して折り
曲げ加工する用途にも使用できる。また、本発明の化粧
シートで第２紙層２の裏面に樹脂を含浸したタイプのも
のは、異形木材、異形成形品等のラツピング用途に使用
できる。A decorative board in which the decorative sheet of the present invention is laminated on a substrate such as plywood by using an emulsion type adhesive or the like,
It has excellent surface properties such as abrasion resistance, heat resistance and creep resistance, so it can be used for surface makeup applications such as furniture, cabinets, study desks, etc., and V-cut grooves are formed on plywood for bending. It can also be used for purposes. Further, the decorative sheet of the present invention in which the back surface of the second paper layer 2 is impregnated with resin can be used for wrapping applications such as deformed wood and deformed shaped products.
【００１８】実施例１ 第１紙層用の用紙として３０ｇ／ｍ2 の片艶ロール紙
（天間特殊製紙、ＨＰ３０）を使用しその裏面の艶のな
い面にウレタン樹脂をグラビア印刷用ベタ版を使用して
固形分で５ｇ／ｍ2 塗布して樹脂を含浸する一方、第２
紙層用の用紙として同じく３０ｇ／ｍ2 の片艶ロール紙
（天間特殊製紙、ＨＰ３０）を使用してその表面の平滑
面に上記と同様にしてウレタン樹脂を固形分で５ｇ／ｍ
2 塗布して樹脂含浸を行つた後、上記第２紙層用の用紙
の樹脂含浸面に２液硬化型ウレタン系接着剤を１０ｇ／
ｍ2 塗布して、上記第１紙層用の用紙の樹脂含浸面を積
層して２層の紙層からなる積層体を作製し、上記積層体
の第１紙層用の用紙の樹脂含浸していない平滑面にグラ
ビア印刷用ベタ版により５ｇ／ｍ2 の厚さにウレタン系
樹脂を塗布し紙層に含浸させると共に、その面にウレタ
ン系樹脂からなるインキにてグラビア印刷によりベタ印
刷層及び絵柄印刷層を設け、更にその印刷層面にウレタ
ン樹脂からなる保護層を１０ｇ／ｍ2 の厚さに塗布して
化粧シートを作製した。Example 1 A 30 g / m 2 single-gloss roll paper (Tenma Special Paper, HP30) was used as the paper for the first paper layer, and a urethane resin was applied to the matte surface on the back surface of the paper for gravure printing. While applying a solid content of 5 g / m 2 to impregnate the resin with the second
As the paper for the paper layer, 30 g / m 2 single-gloss roll paper (Tenma Special Paper, HP30) was also used, and on the smooth surface thereof, urethane resin was added in a solid content of 5 g / m in the same manner as above.
2 After coating and impregnating with resin, 10g of 2-liquid curing type urethane adhesive is applied to the resin impregnated surface of the paper for the second paper layer.
m 2 is applied and the resin-impregnated surface of the paper for the first paper layer is laminated to prepare a laminate composed of two paper layers, and the paper for the first paper layer of the laminate is impregnated with the resin. On the smooth surface, a urethane plate resin is applied to a thickness of 5 g / m 2 with a solid plate for gravure printing to impregnate the paper layer, and a solid printing layer and A printed pattern layer was provided, and a protective layer made of urethane resin was applied on the printed layer surface to a thickness of 10 g / m 2 to prepare a decorative sheet.
【００１９】実施例２ 実施例１と同様にして２層の紙層からなる積層体を作製
し後、該積層体の第１紙層用の用紙の樹脂含浸していな
い平滑面にロールコート方式により１０ｇ／ｍ2 の厚さ
にウレタン系樹脂を塗布して紙層に含浸させると共に、
実施例１と同様にして印刷層及び保護層を設けた後に、
第２紙層用の用紙の裏面の平滑でない面にロールコート
方式によりウレタン樹脂を１０ｇ／ｍ2 の厚さに塗布し
て紙層に含浸させて化粧シートを作製した。Example 2 A laminate having two paper layers was prepared in the same manner as in Example 1, and the smooth surface not impregnated with resin of the paper for the first paper layer of the laminate was roll-coated. By applying urethane resin to a thickness of 10 g / m 2 to impregnate the paper layer with
After providing the printing layer and the protective layer in the same manner as in Example 1,
A urethane sheet was applied to the non-smooth side of the back surface of the paper for the second paper layer by a roll coating method to a thickness of 10 g / m 2 and impregnated into the paper layer to prepare a decorative sheet.
【００２０】[0020]
【発明の効果】化粧シートの基材を、それぞれ樹脂を含
浸した第１紙層及び第２紙層の２層の積層した積層体か
ら構成し、該積層体の第１紙層の表面に印刷層と保護層
とを設けた化粧シートの構成とすることにより、基材の
紙層の層間強度を向上することができるので、平面化粧
用、ラツピング加工用、Ｖカツト加工用として使用可能
であり、耐磨耗性が優れ、クリープによる局部荷重ふく
れが発生しない、低価格の化粧シートが得られる。EFFECT OF THE INVENTION The base material of the decorative sheet is composed of a laminate in which two layers of a resin-impregnated first paper layer and a second paper layer are laminated, and printed on the surface of the first paper layer of the laminate. Since the interlayer strength of the paper layer of the base material can be improved by forming a decorative sheet having a layer and a protective layer, it can be used for flat makeup, lapping, and V-cut processing. It is possible to obtain a low-cost decorative sheet that has excellent abrasion resistance and does not cause local load swelling due to creep.
【図１】本発明の化粧シートの積層構成を示す図。FIG. 1 is a diagram showing a laminated structure of a decorative sheet of the present invention.
１ 第１紙層 ２ 第２紙層 ３ 接着剤層 ４ 印刷層 4a ベタ印刷層 4b 絵柄印刷層 ５ 保護層 1 1st paper layer 2 2nd paper layer 3 Adhesive layer 4 Printing layer 4a Solid printing layer 4b Pattern printing layer 5 Protective layer
Claims (3)
ングにより熱硬化性樹脂が含浸された第１紙層、接着剤
層、表面ないし表裏両面へのコーテイングにより熱硬化
性樹脂が含浸された第２紙層を順に積層した構成からな
ることを特徴とする化粧シート。1. A protective layer, a printing layer, a thermosetting resin impregnated by coating on both front and back surfaces, a first paper layer, an adhesive layer, a thermosetting resin impregnated by coating on front and back surfaces. A decorative sheet having a structure in which a second paper layer is sequentially laminated.
脂、エポキシ樹脂、押出ポリオレフイン樹脂のいずれか
からなることを特徴とする請求項１記載の化粧シート。2. The decorative sheet according to claim 1, wherein the adhesive layer is made of a two-component curing type urethane resin, an epoxy resin, or an extruded polyolefin resin.
に、コーテイングにより熱硬化性樹脂を含浸させ、前記
第１紙層及び前記第２紙層の熱硬化性樹脂を含浸させた
面同志を接着剤により貼合し、前記第１紙層の非貼合面
にコーテイングにより熱硬化性樹脂を含浸させ、その面
に印刷層及び保護層を形成することを特徴とする化粧シ
ートの製造方法。3. A surface of each of the first paper layer and the second paper layer that is impregnated with a thermosetting resin by coating, and a surface of the first paper layer and the second paper layer that is impregnated with the thermosetting resin. Manufacture of a decorative sheet characterized in that the non-bonded surface of the first paper layer is impregnated with a thermosetting resin by coating, and a printing layer and a protective layer are formed on the surface. Method.