JPH06321669A - Method for decorating tile surface by deposition of particle - Google Patents
Method for decorating tile surface by deposition of particleInfo
- Publication number
- JPH06321669A JPH06321669A JP11292593A JP11292593A JPH06321669A JP H06321669 A JPH06321669 A JP H06321669A JP 11292593 A JP11292593 A JP 11292593A JP 11292593 A JP11292593 A JP 11292593A JP H06321669 A JPH06321669 A JP H06321669A
- Authority
- JP
- Japan
- Prior art keywords
- particles
- tile
- glaze
- refractoriness
- transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明はタイル表面の粒子担持に
よる加飾方法に係り、特に、タイル表面に高耐火度の粒
子を所定のパターンに付着させることにより、著しく装
飾性に優れ、高級感のある加飾タイルを製造する方法に
関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decoration method by supporting particles on a tile surface, and in particular, by adhering particles having a high refractory degree to a tile surface in a predetermined pattern, the tile surface has a remarkably excellent decorative property and a high-class feeling. The present invention relates to a method of manufacturing a decorative tile having a texture.
【０００２】[0002]
【従来の技術】従来、タイルの加飾方法としては、素焼
きタイルの表面にベース釉を釉掛けした後焼成し、次い
で絵具釉で模様付けした後焼成する方法がある。2. Description of the Related Art Conventionally, as a method for decorating tiles, there is a method in which a surface of a unglazed tile is glazed with a base glaze, followed by firing, then patterning with a paint glaze, and then firing.
【０００３】[0003]
【発明が解決しようとする課題】上記従来の加飾方法で
は、絵具釉による模様付けのみであるため、化粧面は比
較的平坦で、立体感、高級感に乏しいものであった。In the above-mentioned conventional decorating method, only the patterning by the paint glaze is used, so that the decorative surface is relatively flat, and the three-dimensional effect and the high-grade feeling are poor.
【０００４】一方、近年、生活水準の向上に伴い、タイ
ルの装飾性についても、様々な趣向や工夫、変化、独創
性が求められると共に、より一層高級感のあるものが好
まれるようになってきている。On the other hand, in recent years, as the standard of living has improved, various tastes, contrivances, changes, and originality have been demanded for the decorativeness of tiles, and more luxurious ones have been preferred. ing.
【０００５】本発明は上記従来の実情に鑑みてなされた
ものであって、タイル表面に高耐火度の粒子を所定のパ
ターンに付着させることにより、著しく装飾性に優れ、
高級感のある加飾タイルを製造することができるタイル
表面の粒子担持による加飾方法を提供することを目的と
する。The present invention has been made in view of the above-mentioned conventional circumstances, and by adhering particles having a high refractory degree in a predetermined pattern on the tile surface, the decorative property is remarkably excellent.
An object of the present invention is to provide a decoration method by carrying particles on the surface of a tile, which can produce a decorative tile having a high-grade feeling.
【０００６】[0006]
【課題を解決するための手段】本発明のタイル表面の粒
子担持による加飾方法は、素焼きタイルの表面にベース
釉を掛けて焼成し、該ベース釉の表面に所定パターンに
糊付けし、この糊面上に高耐火度の粒子を付着させ、こ
の粒子を覆うように透明又は半透明釉を掛けた後、焼き
付けるようにしたことを特徴とする。A method of decorating a tile surface by carrying particles on a tile surface according to the present invention is a method in which a surface of a unglazed tile is coated with a base glaze and baked, and the surface of the base glaze is pasted in a predetermined pattern. It is characterized in that particles having a high refractory degree are attached to the surface, transparent or semitransparent glaze is applied so as to cover the particles, and then baking is performed.
【０００７】以下に図面を参照して本発明を詳細に説明
する。The present invention will be described in detail below with reference to the drawings.
【０００８】図１は本発明のタイル表面の粒子担持によ
る加飾方法の一実施例方法を説明する断面図である。FIG. 1 is a sectional view for explaining a method of embodying a decorating method by carrying particles on a tile surface according to the present invention.
【０００９】図示の如く、本発明の方法においては、素
焼きタイル１の表面にベース釉２を掛けて焼成した後、
ベース釉２の表面に所定パターンに糊３を付ける（図１
（ａ））。次いで、この糊３面上にジルコニアビーズ４
等の高耐火度の粒子を付着させ、その後、この粒子を覆
うように透明釉５又は半透明釉を掛けた後、焼き付け
る。As shown in the figure, in the method of the present invention, after the base glaze 2 is applied to the surface of the unglazed tile 1 and fired,
Adhesive 3 is applied to the surface of base glaze 2 in a predetermined pattern (Fig. 1
(A)). Next, the zirconia beads 4 are placed on the surface of this glue 3.
Particles having a high refractory degree such as the above are adhered, and then a transparent glaze 5 or a semitransparent glaze is applied so as to cover the particles, followed by baking.
【００１０】本発明において、高耐火度の粒子として
は、ジルコニアビーズの他、炭化ケイ素等のファインセ
ラミックス粒子等を用いることができる。In the present invention, as the high refractory particles, fine ceramic particles such as silicon carbide can be used in addition to zirconia beads.
【００１１】この粒子の大きさは、過度に小さいと本発
明の粒子担持による装飾性付与効果が十分でなく、逆に
過度に大きいと粒子の付着性が悪くなるなどの不具合を
生じる恐れがあることから、粒子の粒径は０．５〜２ｍ
ｍ程度であることが好ましい。If the size of the particles is excessively small, the effect of imparting the decorative property by the particles carried by the present invention is not sufficient, and if the size of the particles is excessively large, there is a possibility that the adhesion of the particles deteriorates. Therefore, the particle size is 0.5-2m
It is preferably about m.
【００１２】このような高耐火度粒子を付着させる糊と
しては、通常市販されている糊を用いることができ、こ
のような糊はその適当量をプリント印刷等により所定の
模様形状にベース釉面上に付着させる。As the paste for adhering such high refractory particles, a commercially available paste can be used. An appropriate amount of such paste is printed into a predetermined pattern shape by base printing and the like. Adhere on top.
【００１３】このようにして所定パターンに付着させた
糊面上に高耐火度粒子を付着させるには、高耐火度粒子
をベース釉面上の全体に散布した後、過剰の高耐火度粒
子をふりはらうなどして除去すれば良い。In order to adhere the high refractory particles on the paste surface adhered in the predetermined pattern in this manner, the high refractory particles are sprayed over the entire base glaze surface, and then the excessive high refractory particles are removed. It may be removed by pretending.
【００１４】高耐火度粒子を付着させた後、この高耐火
度粒子を覆うように釉掛けする透明釉又は半透明釉とし
ては、例えば、下記配合のものを用いることができる
が、下記配合のものに何ら限定されるものではない。As the transparent glaze or the semitransparent glaze to which the high refractory particles are adhered and then glazed so as to cover the high refractory particles, for example, those having the following composition can be used. It is not limited to anything.
【００１５】透明釉配合（重量部）Ｉ 長石：３０ 粘土：７ 石灰：１８ 亜鉛華：７ 炭酸バリウム：１０ アルミナ：３ フリット：２５半透明釉配合（重量部）II 長石：５０ 珪砂：１５ 粘土：５ 石灰：１５ 亜鉛華：１０ フリット：５ これらの透明釉又は半透明釉は、高耐火度粒子の付着部
分及びその周辺にのみ掛けても良く、タイルの表面全体
に掛けても良い。 Transparent glaze compound (weight part) I Clay: 30 Clay: 7 Lime: 18 Zinc white: 7 Barium carbonate: 10 Alumina: 3 Frit: 25 Semi-transparent glaze compound (weight part) II Feldspar: 50 Silica sand: 15 Clay : 5 Lime: 15 Zinc white: 10 Frit: 5 These transparent glazes or semi-transparent glazes may be hung only on the portion where the high refractory particles are attached and the periphery thereof, or may be hung on the entire surface of the tile.
【００１６】ここで、透明釉を用いた場合には高耐火度
粒子が明確に視認されるものが得られ、半透明釉を用い
た場合には、高耐火度粒子がボカシ模様として視認され
るものが得られる。Here, when transparent glaze is used, high refractory particles are clearly visible, and when semitransparent glaze is used, high refractory particles are visually recognized as a blur pattern. Things are obtained.
【００１７】透明釉又は半透明釉は、高耐火度粒子の剥
離を防止し得る程度に掛ければ良く、通常の場合、焼成
後の厚さで１０〜５０μｍ程度に釉掛けされる。The transparent glaze or the semitransparent glaze may be applied to such an extent that the high-refractory particles can be prevented from peeling off, and in general, the thickness after firing is about 10 to 50 μm.
【００１８】透明釉又は半透明釉を掛けた後は１１００
〜１１５０℃で焼成して加飾タイルを得る。1100 after applying transparent or semi-transparent glaze
Bake at ~ 1150 ° C to obtain decorative tiles.
【００１９】なお、透明釉又は半透明釉の釉掛けに先立
ち、高耐火度粒子を付着させていないベース釉表面に、
通常の絵具釉で絵付けすることもできる。Prior to the glaze of transparent glaze or translucent glaze, the surface of the base glaze on which high refractory particles are not adhered,
You can also paint with normal paint glaze.
【００２０】[0020]
【作用】本発明のタイル表面の粒子担持による加飾方法
では、タイル表面に付着させた高耐火度粒子により、あ
たかも宝石を付着させたような美麗なタイル化粧面が得
られる。この高耐火度粒子は透明釉又は半透明釉により
覆われているため、剥離することはない。また、この高
耐火度粒子は耐火度が高いことから、その後の焼成によ
り形状等が変化することもなく、本来の美観を十分に維
持することができる。According to the method for decorating particles on the tile surface of the present invention, the high refractory particles attached to the tile surface provide a beautiful tile decorative surface as if a jewel was attached. Since the high refractory particles are covered with the transparent glaze or the semitransparent glaze, they are not peeled off. Further, since the high refractory particles have a high refractory degree, the shape and the like do not change due to subsequent firing, and the original aesthetic appearance can be sufficiently maintained.
【００２１】[0021]
【実施例】以下に実施例を挙げて、本発明をより具体的
に説明する。EXAMPLES The present invention will be described in more detail with reference to the following examples.
【００２２】実施例１ 素焼きタイルの表面に前記配合のベース釉Ｉでベース釉
層を形成したタイルのベース釉層表面に、所定パターン
に糊を付け、この糊面上に、高耐火度粒子として粒径１
ｍｍのジルコニアビーズを付着させた。その後、前記配
合の透明釉IIを焼成後の厚さが１０μｍとなるように釉
掛けした後、１１１０℃で３０分間焼成した。Example 1 A paste having a predetermined pattern was applied to the surface of a base glaze layer of a tile in which a base glaze layer was formed with the base glaze I having the above-mentioned composition on the surface of a unglazed tile, and high refractory particles were formed on the paste surface. Particle size 1
mm zirconia beads were attached. Thereafter, the transparent glaze II having the above composition was glazed so that the thickness after firing was 10 μm, and then fired at 1110 ° C. for 30 minutes.
【００２３】得られたタイルは、ジルコニアビーズによ
り美しい宝石様の化粧面が形成され、装飾性、高級感の
著しく高いものであった。The resulting tile had a beautiful jewel-like decorative surface formed of zirconia beads, and was extremely high in decorativeness and high quality.
【００２４】[0024]
【発明の効果】以上詳述した通り、本発明のタイル表面
の粒子担持による加飾方法によれば、高耐火度粒子をタ
イル表面に付着させることにより、美麗で高級感が高
く、独特の優れた装飾性を備える加飾タイルを製造する
ことができる。As described in detail above, according to the decorating method by supporting particles on the tile surface of the present invention, high refractory particles are adhered to the tile surface, so that the tile surface is beautiful, high-grade feeling and unique and excellent. It is possible to manufacture a decorative tile having a decorative property.
【図１】本発明のタイル表面の粒子担持による加飾方法
の一実施例方法を説明する断面図である。FIG. 1 is a cross-sectional view illustrating a method of embodying a decorating method by carrying particles on a tile surface according to the present invention.
１ 素焼きタイル ２ ベース釉 ３ 糊 ４ ジルコニアビーズ ５ 透明釉 1 Uncoated tile 2 Base glaze 3 Paste 4 Zirconia beads 5 Transparent glaze
Claims (1)
焼成し、 該ベース釉の表面に所定パターンに糊付けし、 この糊面上に高耐火度の粒子を付着させ、 この粒子を覆うように透明又は半透明釉を掛けた後、焼
き付けるようにしたことを特徴とするタイル表面の粒子
担持による加飾方法。1. A base glaze is applied to the surface of the unglazed tile and baked, and a paste is adhered to the surface of the base glaze in a predetermined pattern, and high refractory particles are adhered onto the paste surface to cover the particles. A method for decorating particles by supporting particles on a tile surface, which comprises baking after applying a transparent or translucent glaze.