CN2752261Y - Metallized polished glazing ceramic product - Google Patents

Metallized polished glazing ceramic product Download PDF

Info

Publication number
CN2752261Y
CN2752261Y CN 200420093958 CN200420093958U CN2752261Y CN 2752261 Y CN2752261 Y CN 2752261Y CN 200420093958 CN200420093958 CN 200420093958 CN 200420093958 U CN200420093958 U CN 200420093958U CN 2752261 Y CN2752261 Y CN 2752261Y
Authority
CN
China
Prior art keywords
pattern
polished
ceramic
titanium
patterns
Prior art date
Application number
CN 200420093958
Other languages
Chinese (zh)
Inventor
陈满坚
Original Assignee
陈满坚
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 陈满坚 filed Critical 陈满坚
Priority to CN 200420093958 priority Critical patent/CN2752261Y/en
Application granted granted Critical
Publication of CN2752261Y publication Critical patent/CN2752261Y/en

Abstract

The utility model discloses a metallized polished glazing ceramic product which comprises a green brick, and a pattern layer is made on the upper surface of the green brick. The pattern upper surface of the pattern layer is coated with two or more than two transparent blocks with a smooth surface, which are formed by sintering frit powder and slots formed between the transparent blocks are filled with metal plating layers. The surface of the polished glazing ceramic tile made of the utility model is glistened, has colorful patterns and has transparent and lustrous feeling. Titanium gold, titanium sliver or other metal materials are plated between the patterns to draw the outline of the patterns. The utility model has the advantages of good stereo perception, and colorful pattern as pearls and gems, and is a luxurious and high-class decorative ceramic tile.

Description

A kind of metallizing is thrown the glaze ceramic
Technical field
The utility model relates to a kind of ceramic, relates in particular to metallizing and throws the glaze ceramic.
Background technology
Golden ceramic is a kind of ornament of top grade, with its noble quality, magnificent and be subjected to the favor in market deeply.Existing golden ceramic is a planar products, and following several manufacture craft is arranged: silk screen print method, and promptly ceramic burns till through after the silk screen printing; The decal paper method promptly earlier is prefabricated into marble paper with Jinsui River, and ceramic burns till behind decal paper; Describe or spraying method, promptly ceramic manually describe or spray gun spraying after burn till.The ceramic that these several technologies are made lacks stereoscopic sensation, shows slightly stiff, visually dislikes flat slightly.
Summary of the invention
The purpose of this utility model provides the metallizing that a kind of stereoscopic sensation is strong, the surface is glittering and translucent, decorative effect is splendid and throws the glaze ceramic.
Metallizing of the present utility model is thrown the glaze ceramic, comprise adobe, adobe upper surface pattern-making layer, the patterned surfaces of described patterned layer cover the transparent block of two or more than two surface smoothing that is formed by the frit powder sintering, filler metal coating in the groove that forms between the transparent block.
Metallizing of the present utility model throw the glaze ceramic brick surface glittering and translucent as jewel, appear coloury pattern, then plate with titanium between the pattern, titanium is silver-colored or other metallic substance, and pattern is carried out sketching the contours of skeletal lines, decorated, interspersed.Titanium-gold-plating or titanium silver layer and transparent block concave-convex surface are inconsistent, and stereoscopic sensation is very strong, have to enrich changeable light diffusion effect, and be bright-colored, shining as color as pearl, the jewel, lively, attractive in appearance far beyond the plane ceramic tile.The ceramic tile that the utility model makes not only has abundant stereoscopic sensation but also has transparent feel and reflecting feel, is a kind of luxurious, high-grade ornamental ceramic tile.
Description of drawings
Fig. 1 a makes raw material adobe synoptic diagram of the present utility model.
Fig. 1 b is the side-view of Fig. 1 a.
Fig. 2 a is the adobe of making pattern.
Fig. 2 b is the side-view of Fig. 2 a.
Fig. 3 is the structural representation behind the molten stone flour on the spreading.
Fig. 4 is the structural representation that plates behind the metal level.
Fig. 5 is the utility model finished product structural representation.
Fig. 6 makes process flow sheet of the present utility model.
Embodiment
As shown in Figure 6, the utility model is produced according to following processing step successively:
(1) surface treatment is carried out in adobe 1;
Fig. 1 a, 1b are depicted as manufactured adobe 1, with cotton, distilled water its ceramic upper surface stain are removed, and dry then.
(2) at adobe upper surface impressing pattern;
Shown in Fig. 2 a, 2b, at adobe 1 surperficial impressing pattern layer 2, can adopt making of pattern half tone and printing machine to carry out pattern and print, the order number of printing screen is 200~250 orders.Also can adopt other skill and technique such as drafting, massed glaze or applique to carry out design producing.Pattern 21 can be made into coloury pattern, is good with lithotome or jewel line especially.In the present embodiment, pattern 21 is divided into a plurality of Polygonss in irregular shape by skeletal lines 22.
(3) spreading frit powder;
As shown in Figure 3,, then leave a blank, thereby form frit bisque 3 with many grooves 32 corresponding to the position of skeletal lines 22 at the upper surface spreading frit powder 31 of pattern 21.
The thickness of frit powder 31 spreadings is moderate, if spreading must be thin excessively, the finished product stereoscopic sensation that then makes is not strong; Or spreading gets blocked uply, and then the transparency of finished product is undesirable.The coefficient of expansion of frit powder is slightly less than the adobe coefficient of expansion, and is complementary with it.The powder fineness of frit powder is 80~200 orders, its major ingredient following (mass percent):
SiO 2 55~65% MgO 0.2~0.3% Al 2O 3?8~9%
K 2O 2~4% Fe 2O 3 0.1~0.2% Na 2O 1~2%
CaO 2~3% ZnO% 2.5~4% BaO 2.5~3.5%
ZrO 2 0.1~0.5% B 2O 3%?15~20%
The order number of frit paving silk screen is 40~60 orders.
(4) burn till;
The ceramic tile that above-mentioned steps is obtained is carried out three times and is burnt till, and firing temperature is 1000~1030 ℃, and firing period is 40~60 minutes.After burning till, frit powder 31 is formed transparent block 33, appears pattern 21, seems glittering and translucent.
(5) shown in Figure 4, the work in-process upper surface after burning till plates titanium, titanium silver or other metallic substance 4, makes metal plating fill up groove 32 and is covered in monoblock work in-process ceramic tile upper surface;
(6) polishing;
The upper surface that plates behind titanium, titanium silver or other metallic substance is carried out polished finish, grind off the metal plating that is covered in transparent block 33 surfaces, then leave the metal cladding 42 that is covered in from the pattern 22 in the groove 32, metal cladding 42 has different senses of touch and impression with transparent block 33 surfaces, has formed concavo-convex inconsistent top layer.
Through further finally obtaining finished product behind the pick.Finished bricks is level and smooth, glittering and translucent at the master pattern part surface, can see through the pattern that transparent block 33 is seen color class bright-coloured.Metal cladding 42 reaches the strong decorative effect of sketching the contours, interspersing round transparent block 33, and is beautiful as dazzling as jewel, the seven color pearls.
The product that the utility model makes reaches following technical indicator after tested:
Acid resistance: A level
Alkaline resistance properties: A level
Hardness: 6 grades of Mohs
Wear resistance: 2 grades

Claims (2)

1, a kind of metallizing is thrown the glaze ceramic, comprise adobe (1), adobe (1) upper surface pattern-making layer (2), it is characterized in that: the patterned surfaces of described patterned layer (2) covers the transparent block (33) of two or more than two surface smoothing that is formed by frit powder (31) sintering, the interior filler metal coating of groove (32) (42) that forms between the transparent block (33).
2, metallizing according to claim 1 is thrown the glaze ceramic, and it is characterized in that: described metal plating (42) is titanium-gold-plating, titanium silver layer.
CN 200420093958 2004-10-14 2004-10-14 Metallized polished glazing ceramic product CN2752261Y (en)