JPH06321668A - Method for decorating tile - Google Patents
Method for decorating tileInfo
- Publication number
- JPH06321668A JPH06321668A JP11292793A JP11292793A JPH06321668A JP H06321668 A JPH06321668 A JP H06321668A JP 11292793 A JP11292793 A JP 11292793A JP 11292793 A JP11292793 A JP 11292793A JP H06321668 A JPH06321668 A JP H06321668A
- Authority
- JP
- Japan
- Prior art keywords
- glaze
- color
- tile
- pattern
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明はタイルの加飾方法に係
り、特に、素焼きタイルにベース釉を釉掛けした後焼成
し、次いで絵具釉で模様付けした後焼成するタイルの加
飾方法において、絵具釉とベース釉との模様や色を重ね
合わせることにより、独特の美麗な化粧面を得る方法に
関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for decorating tiles, and more particularly, in a method for decorating tiles in which unglazed tiles are glazed with a base glaze and then baked, and then patterned with a paint glaze and then baked. The present invention relates to a method of obtaining a unique and beautiful makeup surface by superimposing patterns and colors of paint glaze and base glaze.
【０００２】[0002]
【従来の技術】従来、タイルの加飾方法として、素焼き
タイルにベース釉を釉掛けした後焼成し、次いで絵具釉
で模様付けした後焼成する方法がある。2. Description of the Related Art Conventionally, as a method for decorating tiles, there is a method in which an unbaked tile is glazed with a base glaze and then fired, then patterned with a paint glaze, and then fired.
【０００３】従来のタイルの加飾方法では、絵具釉によ
る模様付け部分には、下層のベース釉の色や模様が浮き
出ることがないように、絵具釉に隠蔽力を付与すべく、
ジルコニアを５〜１０重量％程度含有させている。In the conventional tile decorating method, the paint glaze is provided with concealing power so that the color and pattern of the base glaze of the lower layer does not stand out in the pattern-glazed pattern portion.
Zirconia is contained in an amount of about 5 to 10% by weight.
【０００４】[0004]
【発明が解決しようとする課題】上記従来の方法では絵
具釉による模様付けには、絵具釉の色及び模様のみが表
出するため、単調なものとならざるを得ない。In the above-mentioned conventional method, the patterning with the paint glaze shows only the color and the pattern of the paint glaze, so that it must be monotonous.
【０００５】一方で、近年、生活水準の向上に伴い、タ
イルの装飾性にも様々な趣向や工夫、変化、独創性が求
められている。On the other hand, in recent years, along with the improvement of living standards, various tastes, ingenuity, changes, and originality are required for the decorativeness of tiles.
【０００６】本発明は上記従来の実情に鑑みてなされた
ものであり、絵具釉による模様付け部分に、絵具釉と下
層ベース釉の模様や色を重ね合わせることにより、独特
な装飾性、美観をかもし出すタイル化粧面を得ることが
できるタイルの加飾方法を提供することを目的とする。The present invention has been made in view of the above-mentioned conventional circumstances, and by superimposing the pattern and color of the paint glaze and the lower layer base glaze on the patterning part with the paint glaze, unique decorativeness and aesthetic appearance can be obtained. It is an object of the present invention to provide a method for decorating a tile that can obtain a decorative tile surface.
【０００７】[0007]
【課題を解決するための手段】本発明のタイルの加飾方
法は、素焼きタイルにベース釉を釉掛けした後焼成し、
次いで絵具釉で模様付けした後焼成するタイルの加飾方
法において、該絵具釉のジルコニア含有量を実質的に皆
無とすることによって、該絵具釉の透光性を高め、ベー
ス釉の模様又は色と絵具釉の模様又は色とを重畳させる
ようにしたことを特徴とする。[Means for Solving the Problems] A method for decorating a tile according to the present invention is as follows: a unglazed tile is glazed with a base glaze and then baked.
Then, in a method of decorating a tile that is baked after being patterned with a paint glaze, by substantially eliminating the zirconia content of the paint glaze, the translucency of the paint glaze is increased, and the pattern or color of the base glaze. And the pattern or color of the paint glaze are superimposed.
【０００８】以下に本発明を詳細に説明する。The present invention will be described in detail below.
【０００９】本発明の方法において使用される絵具釉
は、隠蔽剤であるジルコニアを実質的に含まないもので
ある。ジルコニアを含む絵具釉では、下層のベース釉の
模様や色を絵具釉による模様付け部分に表出させること
ができない。The paint glaze used in the method of the present invention is substantially free of the masking agent zirconia. In the case of paint glaze containing zirconia, the pattern and color of the base glaze in the lower layer cannot be exposed in the pattern part of the paint glaze.
【００１０】本発明で使用される絵具釉の具体的な配合
としては、例えば、次のようなものが挙げられる。Specific examples of the paint glaze used in the present invention include the following.
【００１１】絵具釉配合（重量部） 顔料：０．１〜５０ フリット：５０〜９９．９ なお、本発明において、ベース釉配合としては特に制限
はなく、従来一般に使用されているものを用いることが
できる。Paint glaze blending (parts by weight) Pigment: 0.1-50 Frit: 50-99.9 In the present invention, the base glaze blending is not particularly limited, and those commonly used conventionally are used. You can
【００１２】本発明の方法は、例えば、常法に従って得
られた素焼きタイルの表面にベース釉を釉掛けした後焼
成し、次いで、上記ジルコニアを含有しない絵具釉で模
様付けした後１１００〜１２５０℃で焼成することによ
り、容易に実施することができる。The method of the present invention is, for example, 1100 to 1250 ° C. after the base glazing is glazed on the surface of the unglazed tile obtained according to a conventional method, then baked, and then patterned with the above-mentioned paint glazing not containing zirconia. It can be easily carried out by firing at.
【００１３】[0013]
【作用】白色顔料であるジルコニアを実質的に含有しな
い絵具釉であれば、隠蔽力が殆どなく、従って、下層の
ベース釉の色や模様を絵具釉による模様付け部分に表出
させることができ、ベース釉の模様又は色と絵具釉の模
様又は色との重畳により、従来にない独特の装飾性に優
れたタイル化粧面が得られる。[Function] With a paint glaze that does not substantially contain zirconia, which is a white pigment, there is almost no hiding power, and therefore the color or pattern of the base glaze in the lower layer can be exposed in the pattern part of the paint glaze. By superimposing the pattern or color of the base glaze and the pattern or color of the paint glaze, it is possible to obtain a tile decorative surface excellent in decorativeness that is unique to the conventional art.
【００１４】[0014]
【実施例】以下に実施例及び比較例を挙げて本発明をよ
り具体的に説明する。EXAMPLES The present invention will be described more specifically with reference to Examples and Comparative Examples below.
【００１５】実施例１ 下記配合のベース釉でベース釉層を形成したタイルのベ
ース釉層表面に、ジルコニアを含有しない下記配合の絵
具釉を用いて模様付けした後１１１０℃で３０分間焼成
した。その結果、形成された模様付け部分は、ベース釉
の色と絵具釉の色とが重畳し、著しく美麗な化粧タイル
が得られた。Example 1 The surface of a base glazed layer of a tile having a base glazed layer formed with a base glaze of the following composition was patterned using a paint glaze of the following composition containing no zirconia, and then baked at 1110 ° C. for 30 minutes. As a result, in the formed patterned portion, the color of the base glaze and the color of the paint glaze were superimposed, and a remarkably beautiful decorative tile was obtained.
【００１６】ベース釉配合（重量部） 長石：４０ 石灰：１５ 亜鉛華：５ 粘土：５ 珪砂：２ ジルコニア：１３ フリット：１０絵具釉配合（重量部） 顔料：５（Ｐ−４０：日陶産業） フリット：９５ 比較例１ 絵具釉として、ジルコニアを含有する下記配合の絵具釉
を用いたこと以外は実施例１と同様に行なった。その結
果、絵具釉による模様付け部分はベース釉が完全に隠蔽
されており、絵具釉の色のみによる単調なものであっ
た。 Base glaze blend (parts by weight) Feldspar: 40 Lime: 15 Zinc white: 5 Clay: 5 Silica sand: 2 Zirconia: 13 Frit: 10 Paint glaze blend (part by weight) Pigment: 5 (P-40: Nitto Sangyo Frit: 95 Comparative Example 1 The same procedure as in Example 1 was performed except that a paint glaze containing zirconia and having the following composition was used as the paint glaze. As a result, the base glaze was completely concealed in the pattern portion with the paint glaze, and it was monotonous only with the color of the paint glaze.
【００１７】絵具釉配合（重量部） ジルコニア：５ 顔料：５（Ｐ−４０：日陶産業） フリット：９５ Paint glaze blending (parts by weight) Zirconia: 5 Pigment: 5 (P-40: Nisto Sangyo) Frit: 95
【００１８】[0018]
【発明の効果】以上詳述した通り、本発明のタイルの加
飾方法によれば、素焼きタイルにベース釉を釉掛けした
後焼成し、次いで絵具釉で模様付けした後焼成するタイ
ルの加飾方法において、隠蔽力のない絵具釉を用いるこ
とにより、下層のベース釉の模様や色と絵具釉の模様や
色を重畳させて、従来にない独特な装飾性を有する加飾
タイルを得ることができる。As described in detail above, according to the tile decorating method of the present invention, the tiles to be fired after glazeing the base glaze on the unglazed tile and then firing and then patterning with the paint glaze and firing. In the method, by using a paint glaze that has no hiding power, it is possible to obtain a decorative tile having a unique decorativeness that is unprecedented by superimposing the pattern or color of the base glaze on the lower layer and the pattern or color of the paint glaze. it can.
Claims (1)
焼成し、次いで絵具釉で模様付けした後焼成するタイル
の加飾方法において、該絵具釉のジルコニア含有量を実
質的に皆無とすることによって、該絵具釉の透光性を高
め、ベース釉の模様又は色と絵具釉の模様又は色とを重
畳させるようにしたことを特徴とするタイルの加飾方法1. A method for decorating a tile in which a base glaze is glazed on a unglazed tile, then fired, and then patterned with a paint glaze, and the tile is substantially free of zirconia content. A method for decorating a tile, characterized in that the translucency of the paint glaze is improved by superposing the pattern or color of the base glaze and the pattern or color of the paint glaze.