JPH06248480A - Detergent composition of aqueous drawing agent for stainless steel and washing method - Google Patents
Detergent composition of aqueous drawing agent for stainless steel and washing methodInfo
- Publication number
- JPH06248480A JPH06248480A JP6108293A JP6108293A JPH06248480A JP H06248480 A JPH06248480 A JP H06248480A JP 6108293 A JP6108293 A JP 6108293A JP 6108293 A JP6108293 A JP 6108293A JP H06248480 A JPH06248480 A JP H06248480A
- Authority
- JP
- Japan
- Prior art keywords
- acid
- cleaning
- stainless steel
- agent
- salts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ステンレスの伸線加工
時に用いる水系伸線剤用洗浄剤組成物、およびこの組成
物を利用した洗浄方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cleaning composition for water-based wire drawing agents used during wire drawing of stainless steel, and a cleaning method using this composition.
【０００２】[0002]
【従来の技術】従来から、ステンレスの伸線加工時には
伸線剤ないし潤滑剤として、炭化水素油、フッ素樹脂、
ステアリン酸カルシウム、二硫化モリブデンなどが用い
られている。そこで、伸線加工により得られたステンレ
ス伸線には、これら伸線剤、潤滑剤が付着していること
になり、この付着伸線剤を洗浄、除去することが必要と
なる。従来、伸線剤の洗浄法としては、トリクロロエチ
レン、パークロロエチレン等の塩素系溶剤を用いて浸漬
洗浄、超音波洗浄、蒸気洗浄、ブラッシング等を行なう
ことが知られている。また、ベンゼン、トルエン、キシ
レン等のＢＴＸ溶剤とノニオン界面活性剤等の界面活性
剤とを組み合わせた洗浄剤を用い、浸漬洗浄する方法も
知られている。2. Description of the Related Art Conventionally, as a wire drawing agent or a lubricant when drawing stainless steel, hydrocarbon oil, fluororesin,
Calcium stearate, molybdenum disulfide, etc. are used. Therefore, these wire drawing agents and lubricants are attached to the stainless wire drawn by the wire drawing process, and it is necessary to wash and remove the attached wire drawing agents. Conventionally, as a method for cleaning a wire drawing agent, it is known to carry out immersion cleaning, ultrasonic cleaning, steam cleaning, brushing, etc. using a chlorine-based solvent such as trichlorethylene or perchlorethylene. Also known is a method of immersion cleaning using a cleaning agent that is a combination of a BTX solvent such as benzene, toluene, xylene, and a surfactant such as a nonionic surfactant.
【０００３】しかし、このように有機溶剤を使用する方
法では、地球環境を汚染するばかりか、作業環境上の問
題も大きい。また、鉱酸の使用も知られているが、洗浄
後にステンレス伸線に錆が発生し、腐食性の点で問題が
ある。そこで、有機溶剤を全く用いない洗浄剤の開発が
求められており、炭化水素油を主体とした伸線加工油お
よびステアリン酸、パルミチン酸のＣａ，Ｍｇ，Ｂａ，
Ｎａ，Ｋ，Ｌｉ塩等の金属石けんに対しては、現在、水
酸化カリウム等の強アルカリと両性界面活性剤とを組み
合わせた伸線加工油用洗浄剤が知られており、また、キ
レート剤としてのエチレンジアミンテトラ酢酸塩、グル
コン酸塩を配合した例が記載されている（特開平１−２
８３３９４号公報）。However, such a method using an organic solvent not only pollutes the global environment, but also poses a serious work environment problem. Further, the use of mineral acid is also known, but there is a problem in terms of corrosivity because rust is generated on the stainless wire after cleaning. Therefore, there is a demand for the development of a cleaning agent that does not use any organic solvent. Wire drawing oil mainly composed of hydrocarbon oil and stearic acid, palmitic acid Ca, Mg, Ba,
For metallic soaps such as Na, K and Li salts, a detergent for wire drawing processing oil, which is a combination of a strong alkali such as potassium hydroxide and an amphoteric surfactant, is currently known, and a chelating agent. An example in which ethylene diamine tetraacetate and gluconate are blended as described in Japanese Patent Application Laid-Open No. 1-2
83394 publication).
【０００４】一方、伸線加工時に用いる伸線剤の改良も
進み、これまでの炭化水素油を主体とした伸線加工油か
ら、水系伸線剤へと移行しつつある。水系伸線剤は、消
石灰、リン酸カルシウム、ホウ酸カルシウム、ポリアク
リル酸ナトリウム等の無機塩または有機塩などからな
り、さらに、従来の炭化水素油を主体とした伸線加工油
の場合と同様、先に記した種々の金属石けんが併用され
る。On the other hand, the wire drawing agents used during wire drawing have been improved, and the wire drawing agents mainly composed of hydrocarbon oils have been changed to water-based wire drawing agents. The water-based wire drawing agent consists of slaked lime, calcium phosphate, calcium borate, inorganic salts or organic salts such as sodium polyacrylate, and the like, as in the case of conventional wire drawing oils mainly composed of hydrocarbon oils. The various types of metal soaps described in 1 above are used together.
【０００５】[0005]
【発明が解決しようとする課題】本発明は、ステンレス
用水系伸線剤に対して優れた洗浄性能を示し、安全な水
系であり、従来の強アルカリを含む洗浄剤においては、
洗浄液のｐＨが非常に高いアルカリサイドで発泡が増加
してしまうため、これを抑えるｐＨ範囲で使用するもの
であり、しかも排水処理に有利な無リン系の洗浄剤組成
物および洗浄方法を提供するものである。DISCLOSURE OF THE INVENTION The present invention shows an excellent cleaning performance for a water-based wire drawing agent for stainless steel and is a safe water-based agent.
(EN) Provided are a phosphorus-free detergent composition and a cleaning method which are used in a pH range in which the foaming increases on the alkaline side where the pH of the cleaning liquid is extremely high, and which is advantageous for wastewater treatment. It is a thing.
【０００６】[0006]
【課題を解決するための手段】本発明のステンレス用水
系伸線剤の洗浄剤組成物は、低級二塩基性カルボン酸、
オキシカルボン酸、アミノカルボン酸またはこれらの塩
から選ばれる１種以上を含有することを特徴とする。The cleaning composition for an aqueous wire drawing agent for stainless steel according to the present invention comprises a lower dibasic carboxylic acid,
It is characterized by containing one or more selected from oxycarboxylic acids, aminocarboxylic acids or salts thereof.
【０００７】また、本発明のステンレス用水系伸線剤の
洗浄方法は、低級二塩基性カルボン酸、オキシカルボン
酸、アミノカルボン酸またはこれらの塩から選ばれる１
種以上を０．１〜３０重量％含み、さらに必要に応じて
界面活性剤を含む水性洗浄液を用い、ステンレス用水系
伸線剤が付着したステンレス伸線を洗浄することを特徴
とする。The method for cleaning the aqueous wire drawing agent for stainless steel of the present invention is selected from lower dibasic carboxylic acids, oxycarboxylic acids, aminocarboxylic acids or salts thereof.
It is characterized in that the stainless wire drawing to which the aqueous wire drawing agent for stainless steel is adhered is washed with an aqueous cleaning liquid containing 0.1 to 30% by weight of the above species and further containing a surfactant if necessary.
【０００８】[0008]
【発明の実施態様】本発明では主洗浄活性成分として低
級二塩基性カルボン酸、オキシカルボン酸またはアミノ
カルボン酸あるいはこれらの塩が１種または２種以上併
用して用いられる。BEST MODE FOR CARRYING OUT THE INVENTION In the present invention, a lower dibasic carboxylic acid, an oxycarboxylic acid, an aminocarboxylic acid, or a salt thereof is used as the main cleaning active ingredient, either alone or in combination.
【０００９】低級二塩基性カルボン酸としては、シュウ
酸、マロン酸などが用いられる。オキシカルボン酸とし
ては、クエン酸、グルコン酸、グリコール酸、リンゴ
酸、酒石酸、ヘプトン酸などが挙げられる。アミノカル
ボン酸としては、エチレンジアミンテトラ酢酸（ＥＤＴ
Ａ）、ジエチレントリアミンペンタ酢酸（ＥＤＰＡ）、
ニトリロトリ酢酸（ＮＴＡ）などが挙げられる。As the lower dibasic carboxylic acid, oxalic acid, malonic acid and the like are used. Examples of the oxycarboxylic acid include citric acid, gluconic acid, glycolic acid, malic acid, tartaric acid and heptonic acid. As the aminocarboxylic acid, ethylenediaminetetraacetic acid (EDT
A), diethylenetriaminepentaacetic acid (EDPA),
Examples thereof include nitrilotriacetic acid (NTA).
【００１０】また、これらの塩としては、ナトリウム
塩、カリウム塩、アンモニウム塩等が用いられる。低級
二塩基性カルボン酸、オキシカルボン酸、アミノカルボ
ン酸あるいはこれらの塩は、合計量で本発明の洗浄剤組
成物中に０．５〜１００重量％配合することが好適であ
り、好ましくは２〜５０重量％配合される。As these salts, sodium salts, potassium salts, ammonium salts and the like are used. The lower dibasic carboxylic acid, oxycarboxylic acid, aminocarboxylic acid or salts thereof are preferably added in a total amount of 0.5 to 100% by weight in the detergent composition of the present invention, and preferably 2 ˜50% by weight.
【００１１】本発明の洗浄剤組成物中には、さらにアニ
オン界面活性剤、ノニオン界面活性剤、両性界面活性剤
等の界面活性剤を配合することができる。アニオン界面
活性剤としては、脂肪酸塩類、高級アルコール硫酸エス
テル塩類、液体脂肪油硫酸エステル塩類、脂肪族アミン
および脂肪族アマイドの硫酸塩類、脂肪アルコールリン
酸エステル塩類、二塩基性脂肪酸エステルのスルホン酸
塩類、アルキルアリールスルホン酸塩類、ホルマリン縮
合のナフタリンスルホン酸塩類等が例示される。The detergent composition of the present invention may further contain a surface active agent such as an anionic surface active agent, a nonionic surface active agent or an amphoteric surface active agent. Examples of the anionic surfactant include fatty acid salts, higher alcohol sulfate ester salts, liquid fatty acid sulfate ester salts, sulfate salts of aliphatic amines and aliphatic amides, fatty alcohol phosphate ester salts, sulfonate salts of dibasic fatty acid esters. , Alkylaryl sulfonates, formalin-condensed naphthalene sulfonates, and the like.
【００１２】ノニオン界面活性剤としては、ポリオキシ
アルキレンアルキルエーテル類、ポリオキシエチレンポ
リオキシプロピレンエーテル類、ポリオキシアルキレン
アルキルフェノールエーテル類、ポリオキシアルキレン
アルキルアミン類、化１（一般式Ｉ）で示されるエステ
ル型ノニオン界面活性剤（脂肪酸ポリオキシアルキレン
エステル低級アルキルエーテル）The nonionic surfactants are represented by polyoxyalkylene alkyl ethers, polyoxyethylene polyoxypropylene ethers, polyoxyalkylene alkylphenol ethers, polyoxyalkylene alkylamines, and chemical formula 1 (general formula I). Ester type nonionic surfactant (fatty acid polyoxyalkylene ester lower alkyl ether)
【００１３】[0013]
【化１】Ｒ1ＣＯ(ＯＡ)nＯＲ2 …（Ｉ） （Ｒ1ＣＯ ：長鎖脂肪酸残基 (ＯＡ)n ：エチレンオキサイド、プロピレンオキサイド
またはブチレンオキサイドがｎモル付加していることを
示す Ｒ2 ：低級アルキル基） ソルビタンアルキルエステル類、ポリオキシソルビタン
アルキルエステル類等が挙げられる。ここでポリオキシ
アルキレンとはエチレンオキサイド、プロピレンオキサ
イドまたはブチレンオキサイドが複数モル付加している
ことを示す。Embedded image R 1 CO (OA) nOR 2 ... (I) (R 1 CO: long-chain fatty acid residue (OA) n: indicates that n moles of ethylene oxide, propylene oxide or butylene oxide are added R 2 : Lower alkyl group) sorbitan alkyl esters, polyoxysorbitan alkyl esters and the like. Here, polyoxyalkylene means that a plurality of moles of ethylene oxide, propylene oxide or butylene oxide are added.
【００１４】両性界面活性剤としては、アルキルベタイ
ン、アルキルジメチルアミンオキサイド等が挙げられ
る。なお、上記界面活性剤の例示において、「アルキ
ル」とは二重結合を有するアルケニル基をも包含する概
念である。Examples of the amphoteric surfactant include alkyl betaine and alkyl dimethylamine oxide. In addition, in the example of the said surfactant, "alkyl" is the concept which also includes the alkenyl group which has a double bond.
【００１５】本発明の洗浄剤に界面活性剤を配合するこ
とにより、水リンス性が向上し、さらに洗浄力の増大も
しくは二硫化モリブデンの分散性が向上する。二硫化モ
リブデンの分散性が良好となると、二硫化モリブデンが
付着したステンレス伸線の洗浄に効果を発揮する。界面
活性剤を配合する場合は、洗浄剤組成物中に０．０５〜
９９．５重量％配合することが好適であり、好ましくは
０．１〜２５重量％である。本発明の洗浄剤組成物中に
は、さらに必要に応じ付加成分として、キレート剤、低
温安定化剤、消泡剤、酸化防止剤、防腐剤等を配合する
ことができる。By adding a surfactant to the detergent of the present invention, the water rinsing property is improved, and further the cleaning power or the dispersibility of molybdenum disulfide is improved. When the dispersibility of molybdenum disulfide is good, it is effective for cleaning stainless wire drawn with molybdenum disulfide. When a surfactant is added, it may be added to the detergent composition in an amount of 0.05 to
It is suitable to add 99.5% by weight, and preferably 0.1 to 25% by weight. If desired, a chelating agent, a low temperature stabilizer, a defoaming agent, an antioxidant, an antiseptic agent and the like can be added to the detergent composition of the present invention as additional components.
【００１６】本発明の洗浄剤組成物を用いて洗浄するに
際しては、低級二塩基性カルボン酸、オキシカルボン
酸、アミノカルボン酸あるいはそれらの塩の少なくとも
１種以上を、合計量で０．１〜３０重量％、好ましくは
０．５〜１５重量％含む洗浄液を調製し、この洗浄液に
より水系伸線剤付着ステンレス伸線を洗浄することが、
洗浄性、活性剤の残存量の低減性の点から好ましい。洗
浄方法としては、浸漬洗浄法、超音波洗浄法、ブラッシ
ング、電解洗浄法等の公知の洗浄方法をすべて利用する
ことができる。また、界面活性剤を使用する場合は、洗
浄液中に界面活性剤が０．０１〜１０重量％含まれるこ
とが好ましく、より好ましくは０．１〜５重量％であ
る。In the case of washing with the detergent composition of the present invention, at least one kind of lower dibasic carboxylic acid, oxycarboxylic acid, aminocarboxylic acid or salts thereof is added in a total amount of 0.1 to 0.1. It is possible to prepare a cleaning liquid containing 30% by weight, preferably 0.5 to 15% by weight, and wash the aqueous wire drawing agent-attached stainless wire with this cleaning liquid.
It is preferable in terms of detergency and reduction of the remaining amount of the activator. As a cleaning method, all known cleaning methods such as an immersion cleaning method, an ultrasonic cleaning method, brushing, and an electrolytic cleaning method can be used. When a surfactant is used, the cleaning liquid preferably contains 0.01 to 10% by weight, and more preferably 0.1 to 5% by weight.
【００１７】洗浄液のｐＨは、弱アルカリ、中性ないし
酸性とすることが好ましく、具体的にはｐＨ１１以下、
好ましくはｐＨ９以下とする。洗浄液のｐＨが１１を超
えて強アルカリ性となると、発泡性が大きくなり、ま
た、所定量の洗浄液で多くの伸線を洗浄できる能力、い
わゆるスタミナ洗浄性が低下する。The pH of the cleaning liquid is preferably weak alkali, neutral or acidic, and specifically, pH 11 or less,
The pH is preferably 9 or less. When the pH of the cleaning liquid exceeds 11 and becomes strongly alkaline, the foaming property becomes large, and the ability to clean a large number of drawn wires with a predetermined amount of cleaning liquid, so-called stamina cleaning property, deteriorates.
【００１８】洗浄後は、温水による浸漬すすぎあるいは
スプレーリンスが効果的であり、洗浄液を能率的に除去
することができる。また、ノニオン界面活性剤を洗浄液
中に添加、配合した場合には、ノニオン界面活性剤の曇
点より１０〜１５℃程度低い温度ですすぐことにより、
ノニオン界面活性剤の残存量を低減できる。After washing, immersion rinsing with warm water or spray rinsing is effective, and the washing liquid can be efficiently removed. Also, when a nonionic surfactant is added to the cleaning liquid and blended, by rinsing at a temperature about 10 to 15 ° C lower than the cloud point of the nonionic surfactant,
The remaining amount of nonionic surfactant can be reduced.
【００１９】[0019]
【発明の効果】本発明によれば、伸線加工後のステンレ
ス伸線に付着した水系伸線剤および金属石鹸に対して優
れた効果を発揮し、また、洗浄時にステンレス伸線を腐
食して錆を発生することもなく、しかも水性で安全な洗
浄剤および洗浄方法が実現できる。EFFECTS OF THE INVENTION According to the present invention, it exerts an excellent effect on the water-based wire drawing agent and metal soap attached to the drawn stainless steel wire, and also corrodes the drawn stainless steel during cleaning. It is possible to realize a safe and water-based cleaning agent and a cleaning method without generating rust.
【００２０】[0020]
【実施例】以下、実施例を挙げて本発明をさらに詳細に
説明するが、それに先立って実施例で採用した評価方法
を説明する。EXAMPLES The present invention will be described in more detail below with reference to examples, but prior to that, the evaluation method adopted in the examples will be described.
【００２１】（１） 洗浄力の評価方法 ホウ酸、ケイ酸、硫酸塩等の混合物／金属石鹸／二硫化
モリブデンを用いて伸線加工されたステンレス伸線を、
７０〜８０℃で３０秒間、撹拌しながら浸漬洗浄した
後、２０〜２５℃の水で３０秒間、撹拌すすぎによりリ
ンスした。洗浄後のステンレス伸線の外観を、目視によ
り以下の基準で評価し洗浄力とした。 ◎：伸線剤残着がなく非常に良好 ○：伸線剤残着がほとんどなく良好 △：伸線剤残着がわずかにあり、やや悪い ×：伸線剤が残着し悪い（未洗浄の状態）(1) Method for evaluating detergency A stainless wire drawn by using a mixture of boric acid, silicic acid, sulfate, etc./metal soap / molybdenum disulfide is drawn.
After immersion cleaning at 70 to 80 ° C. for 30 seconds while stirring, it was rinsed by stirring and rinsing with water at 20 to 25 ° C. for 30 seconds. The appearance of the stainless wire drawn after cleaning was visually evaluated as the cleaning power by the following criteria. ◎: Very good with no wire-drawing agent residue ○: Good with almost no wire-drawing agent residue △: Slightly poor with wire-drawing agent residue ×: Poor with wire-drawing agent residue (unwashed) Condition)
【００２２】（２） 二硫化モリブデン（ＭｏＳ2 ）の
分散性の評価方法 各洗浄液に対して、二硫化モリブデンを含む金属石鹸を
０．５％添加し、その分散性を目視により以下の基準で
評価した。 ○：分散性良好 ×：分散せず(2) Method for evaluating dispersibility of molybdenum disulfide (MoS 2 ) 0.5% of metal soap containing molybdenum disulfide was added to each cleaning solution, and the dispersibility was visually observed according to the following criteria. evaluated. ◯: good dispersibility x: not dispersed
【００２３】（３） 腐食性の評価方法 ホウ酸、ケイ酸、硫酸塩等の混合物／金属石鹸／二硫化
モリブデンを用いて伸線加工されたステンレス伸線を、
７０℃で３０分間洗浄液に浸漬した後そのまま風乾し、
表面状態を目視により観察し、以下の基準で評価した。 ○：錆の発生なし ×：錆の発生あり(3) Method of evaluating corrosiveness Stainless steel wire drawn using a mixture of boric acid, silicic acid, sulfate, etc./metal soap / molybdenum disulfide,
After soaking in the cleaning solution at 70 ° C for 30 minutes, air-dry as it is,
The surface condition was visually observed and evaluated according to the following criteria. ◯: No rust occurred ×: Rust occurred
【００２４】（４） 発泡性の評価方法 １００ｍｌのエプトン管に、各洗浄剤に対して金属石鹸
を０．５％添加した水溶液を３０ｍｌ入れ、８０℃まで
加温後１０回上下に振とうし、その直後の泡高を以下の
基準で評価した。 ○：泡高；６０ｍｍ以下（実用上問題のないレベル） ×：泡高；６０ｍｍ以上(4) Method of evaluating foamability In a 100 ml Epton tube, 30 ml of an aqueous solution containing 0.5% metal soap added to each detergent was added, and the mixture was heated up to 80 ° C. and shaken up and down 10 times. The foam height immediately after that was evaluated according to the following criteria. ◯: Bubble height: 60 mm or less (a level that causes no practical problem) ×: Bubble height: 60 mm or more
【００２５】実施例 後記表１および表２に示した組成の洗浄剤組成物を調製
した。ついで、水で所定倍率に希釈して洗浄液を調製
し、洗浄力、腐食性、二硫化モリブデン分散性、発泡性
を評価し、その結果を表１および表２に示した。Example A cleaning composition having the composition shown in Tables 1 and 2 below was prepared. Then, a cleaning liquid was prepared by diluting with water to a predetermined ratio, and the cleaning power, corrosiveness, molybdenum disulfide dispersibility and foamability were evaluated, and the results are shown in Tables 1 and 2.
【００２６】[0026]
【表１】表１：洗浄剤（液）組成および評価方法 実 施 例 １ ２ ３ ４ ５ ６ ７ ８ 洗浄剤組成(wt％) 酸または塩： クエン酸 − 20 − − − 5 94 20 クエン酸Na 40 − − − − − − − リンゴ酸 − − − − 0.5 − − − リンゴ酸Na − − 20 − − − − − シュウ酸 − − − 1.2 − − − − シュウ酸Na − − − − 2 − − − EDTA-Na*1 − − − − − 30 − − NTA-Na*2 − − − 6 − − − − 界面活性剤*3： No.1 − 1 − − − − − − No.2 − − − − − − − 2 No.3 − 1 − − − − 6 − No.4 − − − − − − − 4 No.5 − − − − − − − 2 No.6 − − − − 0.1 − − − 水 60 78 80 92.8 97.4 65 0 72 使用時希釈倍率 8 10 5 2 1 10 25 10 洗浄液濃度(wt％) 5 2.2 4 3.6 2.6 3.5 4 2.8 洗浄液pH 8.2 2.0 8.5 8.5 4.1 7.3 2.0 2.1 評価：洗浄力 ◎ ◎ ○ ○ ○ ○ ◎ ◎ MoS2分散性 × ○ × × ○ × ○ ○ 腐食性 ○ ○ ○ ○ ○ ○ ○ ○ 発泡性 ○ ○ ○ ○ ○ ○ ○ ○ *1) エチレンジアミンテトラ酢酸ナトリウム *2) ニトリロトリ酢酸ナトリウム *3) 界面活性剤 No.1 ポリオキシエチレン(10モル)ノニルフェニルエー
テル(曇点62℃) No.2 ポリオキシエチレン(15モル)ノニルフェニルエー
テル(曇点71℃) No.3 ポリオキシエチレン(４モル)ポリオキシプロピレ
ン(30モル)エーテル(曇点71℃) No.4 ポリオキシエチレン(７モル)ポリオキシプロピレ
ン(4.5モル)Ｃ12〜Ｃ14２級アルコールエーテル(曇点30
℃) No.5 ポリオキシプロピレン(2.5モル)ラウリルエーテ
ル No.6 ポリオキシエチレン(３モル)ラウリルエーテル硫
酸 エステルナトリウム塩[Table 1] Table 1: Detergent (liquid) composition and evaluation method Example 1 2 3 4 5 6 7 8 Detergent composition (wt%) Acid or salt: Citric acid -20 --- 5 94 20 Citric acid Na 40 − − − − − − − Malic acid − − − − 0.5 − − − Malic acid Na − − 20 − − − − − Oxalic acid − − − 1.2 − − − − Oxalic acid Na − − − − 2 − − − EDTA-Na * 1 − − − − − 30 − − NTA-Na * 2 − − − 6 − − − − Surfactant * 3 : No. 1 − 1 − − − − − − No. 2 − − − − − − − 2 No. 3 − 1 − − − − 6 − No. 4 − − − − − − − 4 No. 5 − − − − − − − 2 No. 6 − − − − 0.1 − − − Water 60 78 80 92.8 97.4 65 0 72 Dilution ratio during use 8 10 5 2 1 10 25 10 Cleaning solution concentration (wt%) 5 2.2 4 3.6 2.6 3.5 4 2.8 Cleaning solution pH 8.2 2.0 8.5 8.5 4.1 7.3 2.0 2.1 Evaluation: Detergency ◎ ◎ ◎ ○ ○ ○ ○ ◎ ◎ ◎ MoS 2 dispersibility × ○ × × ○ × ○ ○ Corrosion ○ ○ ○ ○ ○ ○ ○ ○ Foaming ○ ○ ○ ○ ○ ○ ○ ○ * 1) Sodium ethylenediaminetetraacetate * 2) Sodium nitrilotriacetate * 3) Surfactant No.1 Polyoxyethylene (10 mol) Nonylphenyl ether ( Cloud point 62 ℃) No.2 Polyoxyethylene (15mol) Nonylphenyl ether (Cloud point 71 ℃) No.3 Polyoxyethylene (4mol) Polyoxypropylene (30mol) Ether (Cloud point 71 ℃) No. 4 polyoxyethylene (7 mol) of polyoxypropylene (4.5 mol) C 12 -C 14 2 alcohol ether (cloud point 30
℃) No.5 Polyoxypropylene (2.5 mol) Lauryl ether No.6 Polyoxyethylene (3 mol) Lauryl ether Sulfate ester sodium salt
【００２７】[0027]
【表２】 [Table 2]
Claims (3)
ン酸、アミノカルボン酸またはこれらの塩から選ばれる
１種以上を含有することを特徴とするステンレス用水系
伸線剤の洗浄剤組成物。1. A detergent composition for a water-based wire drawing agent for stainless steel, which comprises one or more selected from lower dibasic carboxylic acids, oxycarboxylic acids, aminocarboxylic acids or salts thereof.
記載の洗浄剤組成物。2. The cleaning composition according to claim 1, which further contains a surfactant.
ン酸、アミノカルボン酸またはこれらの塩から選ばれる
１種以上を０．１〜３０重量％含み、さらに必要に応じ
て界面活性剤を含む水性洗浄液を用い、ステンレス用水
系伸線剤が付着したステンレス伸線を洗浄することを特
徴とするステンレス用水系伸線剤の洗浄方法。3. An aqueous solution containing 0.1 to 30% by weight of one or more kinds selected from lower dibasic carboxylic acids, oxycarboxylic acids, aminocarboxylic acids or salts thereof, and further containing a surfactant if necessary. A method for cleaning an aqueous wire drawing agent for stainless steel, which comprises cleaning a stainless wire drawn with an aqueous wire drawing agent for stainless steel using a cleaning liquid.