JPH06234178A - Moisture permeable composite sheet and manufacture thereof - Google Patents
Moisture permeable composite sheet and manufacture thereofInfo
- Publication number
- JPH06234178A JPH06234178A JP2259393A JP2259393A JPH06234178A JP H06234178 A JPH06234178 A JP H06234178A JP 2259393 A JP2259393 A JP 2259393A JP 2259393 A JP2259393 A JP 2259393A JP H06234178 A JPH06234178 A JP H06234178A
- Authority
- JP
- Japan
- Prior art keywords
- film
- moisture
- composite sheet
- permeable composite
- porous film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、透湿性複合シート及び
透湿性複合シートの製造方法に関し、更に詳しくは、延
伸配向によるＭＤ方向およびＣＤ方向の強度差、引き裂
き強度が改善されており、更には、シート表面が改質さ
れ、特に感圧接着剤等を用いた場合に、その表面接着性
／剥離特性をコントロールすることが可能である透湿性
複合シートおよびその製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a moisture-permeable composite sheet and a method for producing a moisture-permeable composite sheet. More specifically, the strength difference in the MD and CD directions due to stretch orientation and the tear strength are improved. The present invention relates to a moisture-permeable composite sheet which has a modified sheet surface and can control the surface adhesiveness / peelability thereof, particularly when a pressure-sensitive adhesive or the like is used, and a method for producing the same.
【０００２】[0002]
【従来の技術】従来、多孔性フィルムの引き裂き強度を
向上させるために、該多孔性フィルムと紙類、不織布、
織物、網、フィルム等の補強材とを接合一体化した複合
シートが提案されている。このような、多孔性フィルム
に補強材としてフィルム状物等を積層した複合シート
は、機械的強度は改良されるものの、透湿性が殆ど損な
われるという欠点がある。2. Description of the Related Art Conventionally, in order to improve the tear strength of a porous film, the porous film and papers, non-woven fabrics,
A composite sheet in which a reinforcing material such as a woven fabric, a net, or a film is joined and integrated has been proposed. Such a composite sheet in which a film-like material or the like is laminated on a porous film as a reinforcing material has improved mechanical strength, but has a drawback that moisture permeability is almost impaired.
【０００３】そこで、上記欠点を解消するために種々の
提案がなされている。例えば、特開昭６２−２７０６３
９号公報には、無機充填剤を含む熱可塑性樹脂からなる
透湿性フィルムと不織布等の材料を複合一体化した通気
性の複合シートが提案されている。また、特開昭６３−
２８６３３０号公報には、不織布とポリオレフィン系多
孔性シートとを、その間に熱接着性多孔シートを用いて
部分的に接着させることにより多孔性シートを補強した
複合シートが提案されている。Therefore, various proposals have been made to solve the above drawbacks. For example, JP-A-62-27063
No. 9 discloses a breathable composite sheet in which a moisture permeable film made of a thermoplastic resin containing an inorganic filler and a material such as a non-woven fabric are combined and integrated. In addition, JP-A-63-
Japanese Patent No. 286330 proposes a composite sheet in which a non-woven fabric and a polyolefin-based porous sheet are partially adhered by using a heat-adhesive porous sheet therebetween to reinforce the porous sheet.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、上述し
た透湿性複合シートは、いずれも引き裂き強度を向上さ
せるために不織布等を多孔性フィルムに複合一体化して
補強したものであり、その表面特性をコントロールする
ものではない。従って、これらの透湿性複合シートに対
して、付け剥しを目的として感圧接着剤等を用いる場合
には、感圧接着剤を剥す際に不織布を構成する繊維が抜
けたり、破断したりして該接着剤に付着し、再び感圧接
着剤を接着させる際に接着力の低下を起こす等の問題を
生ずる。However, in each of the above-mentioned moisture-permeable composite sheets, in order to improve the tear strength, a nonwoven fabric or the like is compositely integrated and reinforced with a porous film, and its surface characteristics are controlled. Not something to do. Therefore, when a pressure-sensitive adhesive or the like is used for the purpose of attaching / detaching to / from these moisture-permeable composite sheets, the fibers constituting the nonwoven fabric may come off or break when the pressure-sensitive adhesive is peeled off. When the pressure-sensitive adhesive is adhered to the adhesive and the pressure-sensitive adhesive is adhered again, a problem such as a decrease in adhesive strength occurs.
【０００５】従って、本発明の目的は、透湿性を低下さ
せることなく、延伸配向によるＭＤ方向およびＣＤ方向
の強度差が改善され、且つ引き裂き強度が向上してお
り、更にはシート表面が改質され、特に感圧接着剤等を
用いた場合に、その表面接着性／剥離特性をコントロー
ルすることができる透湿性複合シートおよびその製造方
法を提供することにある。Therefore, the object of the present invention is to improve the strength difference in the MD and CD directions due to the stretch orientation and to improve the tear strength without lowering the moisture permeability, and further to improve the sheet surface. In particular, it is an object of the present invention to provide a moisture-permeable composite sheet capable of controlling the surface adhesiveness / peelability thereof when a pressure-sensitive adhesive or the like is used, and a manufacturing method thereof.
【０００６】[0006]
【課題を解決するための手段】本発明は、熱可塑性樹脂
及び充填剤を含有する樹脂組成物を溶融成形してフィル
ムとなし、次いで該フィルムを延伸処理して得られた多
孔性フィルムの片面あるいは両面に、無数の孔部を有し
且つ上記多孔性フィルムよりも引き裂き強度の高い、通
気性の開孔フィルムを接合してなることを特徴とする透
湿性複合シートを提供することにより、上記目的を達成
したものである。The present invention relates to a porous film obtained by melt-molding a resin composition containing a thermoplastic resin and a filler to form a film, and then subjecting the film to a stretching treatment. Alternatively, by providing a moisture-permeable composite sheet characterized in that it has an infinite number of pores on both sides and has a higher tear strength than the porous film, and a breathable apertured film is bonded to the porous film. It has achieved its purpose.
【０００７】また本発明は、上記透湿性複合シートを好
適に製造する方法として、熱可塑性樹脂及び充填剤を含
有する樹脂組成物を該熱可塑性樹脂の融点以上の温度で
溶融成形してフィルムとなし、次いで該フィルムを該融
点以下の温度で延伸処理して得た多孔性フィルムの片面
あるいは両面に、無数の孔部を有し且つ上記多孔性フィ
ルムよりも引き裂き強度の高い、通気性の開孔フィルム
を接合一体化することを特徴とする透湿性複合シートの
製造方法を提供するものである。The present invention also provides a method for suitably producing the above-mentioned moisture-permeable composite sheet, which comprises melt-molding a resin composition containing a thermoplastic resin and a filler at a temperature higher than the melting point of the thermoplastic resin to form a film. None, and then, the porous film obtained by subjecting the film to a stretching treatment at a temperature of the melting point or less has innumerable pores on one side or both sides, and has a higher tear strength than the above-mentioned porous film and has a breathable opening. The present invention provides a method for producing a moisture-permeable composite sheet, which is characterized by joining and integrating a perforated film.
【０００８】[0008]
【作用】本発明の透湿性複合シートは、透湿性の多孔性
フィルムに無数の孔部を有する開孔フィルムを複合一体
化してある。そして、上記透湿性複合シートの上記開孔
フィルム側に対して感圧接着剤等を接着した場合、該シ
ートの構成物が接着剤に付着することがなく、付け剥し
が容易である。In the moisture-permeable composite sheet of the present invention, a moisture-permeable porous film is combined with a perforated film having innumerable pores. When a pressure sensitive adhesive or the like is adhered to the perforated film side of the moisture permeable composite sheet, the constituents of the sheet do not adhere to the adhesive and can be easily attached and removed.
【０００９】[0009]
【実施例】以下に、図面を参照しながら、本発明の実施
例を詳細に説明する。図１は、本発明の透湿性複合シー
トの１実施例を示す平面図であり、図２は、その拡大斜
視図であり、図３は、図２のＩ−Ｉ’断面図である。Embodiments of the present invention will be described in detail below with reference to the drawings. 1 is a plan view showing an embodiment of a moisture-permeable composite sheet of the present invention, FIG. 2 is an enlarged perspective view thereof, and FIG. 3 is a sectional view taken along line II ′ of FIG.
【００１０】図１に示す本実施例の透湿性複合シート１
０は、熱可塑性樹脂及び充填剤を含有する樹脂組成物を
溶融成形してフィルムとなし、次いで該フィルムを延伸
処理して得られた多孔性フィルム１１の片面に、無数の
孔部１３を有し且つ上記多孔性フィルムよりも引き裂き
強度の高い、通気性の開孔フィルム１２を接合してな
る。The moisture-permeable composite sheet 1 of this embodiment shown in FIG.
In the case of 0, the resin composition containing a thermoplastic resin and a filler was melt-molded to form a film, and then the film was stretched to have a number of pores 13 on one side thereof. In addition, a breathable apertured film 12 having a tear strength higher than that of the porous film is joined.
【００１１】更に詳細には、上記透湿性複合シート１０
は、図２及び図３に示すように、上記多孔性フィルム１
１と、その片面側に接合された上記開孔フィルム１２と
からなり、上記開孔フィルムは、無数の孔部１３を有し
ており、無数の開孔底部１４と、無数の頂部１５と、該
開孔底部１４と該頂部１５とをそれぞれ連結する筒状壁
部１６とを具備し、上記頂部１５がホットメルト接着剤
（図示せず）を介して上記多孔性シートに接合されてい
る。そして、上記孔部１３は、一個の上記開孔底部１４
と、隣合う複数の上記頂部１５と、それらを連結する１
個の筒状壁部１６とからそれぞれ形成された連通孔構造
からなっている。More specifically, the moisture-permeable composite sheet 10 described above.
As shown in FIGS. 2 and 3, the porous film 1
1 and the perforated film 12 bonded to one side thereof, the perforated film has an innumerable hole portion 13, an innumerable hole bottom portion 14, an innumerable top portion 15, It has a cylindrical wall portion 16 connecting the hole bottom portion 14 and the top portion 15 respectively, and the top portion 15 is joined to the porous sheet via a hot melt adhesive (not shown). And the said hole part 13 is one said hole bottom part 14
And a plurality of the tops 15 adjacent to each other and connecting them 1
It has a communication hole structure formed from the individual cylindrical wall portions 16.
【００１２】上記多孔性シート１１は、熱可塑性樹脂お
よび充填剤を含有する組成物を溶融成形してフィルムと
なし、次いで該フィルムを延伸処理して得たものであ
る。ここで、上記溶融成形及び延伸処理は、公知の方法
を特に制限なく行うことができる。The porous sheet 11 is obtained by melt-molding a composition containing a thermoplastic resin and a filler to form a film, and then stretching the film. Here, the melt molding and the stretching treatment can be performed by known methods without particular limitation.
【００１３】上記熱可塑性樹脂としては、ポリエチレ
ン、ポリプロピレン、ポリブテン等のポリオレフィン系
樹脂、ポリエチレンテレフタレート、ポリブチレンテレ
フタレート等のポリエステル系樹脂、ポリ塩化ビニル等
のビニル系樹脂、ポリ塩化ビニリデン等のビニリデン系
樹脂、これらの混合物等が好ましく用いられる。Examples of the thermoplastic resin include polyolefin resins such as polyethylene, polypropylene and polybutene, polyester resins such as polyethylene terephthalate and polybutylene terephthalate, vinyl resins such as polyvinyl chloride and vinylidene resins such as polyvinylidene chloride. , And mixtures thereof are preferably used.
【００１４】特にポリオレフィン系樹脂として高密度ポ
リエチレン、低密度ポリエチレン、線状低密度ポリエチ
レン、ポリプロピレン、エチレン−プロピレンブロック
共重合体、ポリブテン、エチレン酢酸ビニル共重合体が
好ましく用いることができるが、本発明の透湿性複合シ
ートを衛生用材料、おむつ等に用いる場合は線状低密度
ポリエチレンがしなやかさと強靱性を合わせ持つため好
ましく用いることができる。Particularly, as the polyolefin resin, high density polyethylene, low density polyethylene, linear low density polyethylene, polypropylene, ethylene-propylene block copolymer, polybutene, ethylene vinyl acetate copolymer can be preferably used. When the moisture-permeable composite sheet is used for sanitary materials, diapers, etc., linear low-density polyethylene has both flexibility and toughness and can be preferably used.
【００１５】また上記多孔性シート１１に含まれる充填
剤としては、無機充填剤および有機充填剤が用いられ、
無機充填剤としては、炭酸カルシウム、石膏、タルク、
クレー、カオリン、シリカ、珪藻土、硫酸マグネシウ
ム、硫酸バリウム、燐酸カルシウム、水酸化アルミニウ
ム、酸化亜鉛、酸化チタン、アルミナ、マイカ、ゼオラ
イト、カーボンブラック等が使用され、有機充填剤とし
ては、木粉、パルプ粉、熱硬化性樹脂粉が使用される。
また、上記有機充填剤としては、上記溶融成形する際の
温度以上の溶融点を有する熱可塑性樹脂粉を用いること
ができ、上述の熱可塑性樹脂とは非相溶な熱可塑性樹脂
を用い、溶融混練して上述の熱可塑性樹脂を連続相とし
た海島状に分散させてもよい。また、上記充填剤は単独
で用いても良いしまたは混合して用いても良い。As the filler contained in the porous sheet 11, an inorganic filler and an organic filler are used,
As the inorganic filler, calcium carbonate, gypsum, talc,
Clay, kaolin, silica, diatomaceous earth, magnesium sulfate, barium sulfate, calcium phosphate, aluminum hydroxide, zinc oxide, titanium oxide, alumina, mica, zeolite, carbon black, etc. are used, and as the organic filler, wood powder, pulp. Powder and thermosetting resin powder are used.
Further, as the organic filler, it is possible to use a thermoplastic resin powder having a melting point equal to or higher than the temperature at the time of melt molding, using a thermoplastic resin incompatible with the thermoplastic resin, melted, It is also possible to knead and disperse the above-mentioned thermoplastic resin in a sea-island form as a continuous phase. Further, the above fillers may be used alone or as a mixture.
【００１６】上記充填剤の平均粒径は、３０μ以下のも
のが好ましく、更に好ましくは０．５〜１０μのものが
好ましい。The average particle size of the filler is preferably 30 μm or less, more preferably 0.5 to 10 μm.
【００１７】また、上記多孔性フィルムにおける熱可塑
性樹脂及び充填剤の配合割合は、熱可塑性樹脂１００重
量部に対して、充填剤５０〜２５０重量部であることが
好ましい。上記充填剤の配合割合が、５０重量部未満で
あると、延伸したフィルムまたはシートに連続気孔が充
分形成されず多孔度が低くなり、２５０重量部を超える
と、ポリオレフィン樹脂への分散性不良が生じ延伸後の
強度が低下するので好ましくない。また、多孔性フィル
ムを製造する際には、開孔性、防漏性、延伸性をコント
ロールするために液状ポリブタジエン、液状ポリブテ
ン、液状ポリイソプレン等の液状ゴムを添加して用いる
ことができるが、フィルムの成形に通常用いらている他
の添加剤も、要求される透湿性及び防漏性を損なわない
ものなら使用できる。Further, the mixing ratio of the thermoplastic resin and the filler in the porous film is preferably 50 to 250 parts by weight of the filler with respect to 100 parts by weight of the thermoplastic resin. When the blending ratio of the filler is less than 50 parts by weight, the continuous porosity is not sufficiently formed in the stretched film or sheet and the porosity is low, and when it exceeds 250 parts by weight, the dispersibility in the polyolefin resin is poor. It is not preferable because the strength after stretching is lowered. In addition, when producing a porous film, liquid polybutadiene, liquid polybutene, liquid polyisoprene or other liquid rubber can be added and used in order to control openness, leakproofness, and stretchability. Other additives usually used for forming a film can be used as long as they do not impair the required moisture permeability and leakproofness.
【００１８】上記多孔性フィルムの厚さは、通常、５〜
１５０μのものが使用できるが使用目的にあわせて適宜
選定すれば良い。The thickness of the porous film is usually 5 to 5.
Although 150 μm can be used, it may be appropriately selected according to the purpose of use.
【００１９】上記開孔フィルム１２は、無数の孔部１３
を有しており、無数の開孔底部１４と、裏側が空隙とな
っている凸状曲面からなる無数の頂部１５と、開孔底部
１４と該頂部１５とをそれぞれ連結する筒状壁部１６を
具備し、上記孔部１３が、一個の上記開孔底部１４と、
隣合う複数の上記頂部１５と、それらを連結する１個の
筒状壁部１６とからそれぞれ形成された連通孔構造から
なっている。The perforated film 12 has innumerable holes 13
And an innumerable hole bottom portion 14, an innumerable top portion 15 composed of a convex curved surface having a void on the back side, and a cylindrical wall portion 16 connecting the hole bottom portion 14 and the apex portion 15, respectively. And the hole portion 13 has one hole bottom portion 14 and
It has a communication hole structure formed by a plurality of adjacent top portions 15 and one tubular wall portion 16 connecting them.
【００２０】上記開孔フィルムを形成する材料として
は、ポリエチレン、ポリプロピレン、ポリブテン等のポ
リオレフィン系樹脂、ポリエチレンテレフタレート、ポ
リブチレンテレフタレート等のポリエステル系樹脂、ポ
リ塩化ビニル等のビニル系樹脂、ポリ塩化ビニリデン等
のビニリデン系樹脂、これらの混合物等の熱可塑性樹脂
が好ましく用いられる。Materials for forming the above-mentioned apertured film include polyolefin resins such as polyethylene, polypropylene and polybutene, polyester resins such as polyethylene terephthalate and polybutylene terephthalate, vinyl resins such as polyvinyl chloride and polyvinylidene chloride. The thermoplastic resin such as the vinylidene-based resin and the mixture thereof are preferably used.
【００２１】また、上記開孔フィルムを形成するには、
上記熱可塑性樹脂を用いてフィルムを形成した後、予備
加熱すると共に負圧をかけて開孔させる方法、加熱され
たニードルにり熱可塑性樹脂フィルムに開孔部を設ける
方法、突起を有するエンボスロールにより開孔を付与す
る方法等により形成することができる。To form the apertured film,
After forming a film using the thermoplastic resin, a method of preheating and applying a negative pressure to open a hole, a method of forming a hole in the thermoplastic resin film by a heated needle, an embossing roll having a protrusion Can be formed by a method of providing openings.
【００２２】また、上記開孔フィルム１２において、上
記孔部１３の大きさ及び数量は、本発明の透湿性複合シ
ートとしての透湿性を阻害せず且つ充分な引き裂き強度
を発揮するように選定すればよいが、更に、該開孔フィ
ルム面に対する感圧接着テープ等の感圧接着剤の付け剥
しに際して、所望の接着強度を発揮するように選定する
のが好ましい。即ち、上記開孔底部１４の周辺部分を形
成する上記筒状壁部１６の上方壁面は、直接感圧接着剤
と張り合わされ、これが直接接着に寄与するので、その
面積および形状と接着強度には相関関係があり、上記孔
部１３の周辺部分である上記筒状壁部１６の上方壁面
が、感圧接着剤との接着に多く寄与するほど、並びに上
記孔部１３の面積が小さく、存在密度が高いほど接着強
度が高くなる。Further, in the perforated film 12, the size and number of the perforations 13 should be selected so as not to impair the moisture permeability of the moisture-permeable composite sheet of the present invention and to exert sufficient tear strength. However, it is preferable that the pressure-sensitive adhesive such as a pressure-sensitive adhesive tape is attached to and removed from the surface of the perforated film so that the desired adhesive strength is exhibited. That is, the upper wall surface of the cylindrical wall portion 16 forming the peripheral portion of the hole bottom portion 14 is directly adhered to the pressure-sensitive adhesive, which directly contributes to the adhesion. There is a correlation, and the more the upper wall surface of the cylindrical wall portion 16 that is the peripheral portion of the hole portion 13 contributes to the adhesion with the pressure-sensitive adhesive, and the smaller the area of the hole portion 13 is, the more the existence density is. The higher the value, the higher the adhesive strength.
【００２３】従って、上記開孔底部１４の数量、存在密
度、面積、形状は、用いる感圧接着剤の接着力を考慮し
て選定するのが好ましく、好ましい具体例としては、存
在密度，約１００〜約５０００個／ｃｍ2 、開孔面積，
約０．００１〜１００ｍｍ2、上記筒状壁部の高さ，約
０．１〜１０ｍｍ、上記筒状壁部の傾斜角度，約３０〜
１５０°、線幅，約０．１〜１０ｍｍ、目開，約０．１
〜１０ｍｍとすることができる。Therefore, it is preferable to select the number, the existing density, the area, and the shape of the hole bottoms 14 in consideration of the adhesive force of the pressure-sensitive adhesive to be used. As a preferable specific example, the existing density is about 100. ~ About 5000 pieces / cm 2 , open area,
About 0.001 to 100 mm 2 , the height of the tubular wall portion, about 0.1 to 10 mm, the inclination angle of the tubular wall portion, about 30 to
150 °, line width, about 0.1-10 mm, open, about 0.1
It can be set to 10 mm.
【００２４】尚、本実施例においては、上述の開孔フィ
ルム１２により説明したが、本発明において用いること
ができる開孔フィルムは、上述の例に限定されるもので
はなく、例えば、熱可塑性樹脂から成るネット材等を使
用することもできる。また、上記多孔性フィルムと開孔
フィルムとの接合について、本実施例においては、ホッ
トメルト接着剤を用いた例により説明したが、これに限
定されるものではなく、例えば、加熱により接合するこ
とができる。In this embodiment, the perforated film 12 described above has been described, but the perforated film that can be used in the present invention is not limited to the above-mentioned examples. For example, a thermoplastic resin can be used. It is also possible to use a net material or the like. Further, the joining of the porous film and the perforated film has been described in the present embodiment with an example using a hot melt adhesive, but the present invention is not limited to this, for example, joining by heating. You can
【００２５】次いで、図４を参照して、本発明の透湿複
合シートの他の実施例について説明する。また、図４
は、本発明の透湿性複合シートの他の実施例を示す断面
図である。図４に示す透湿性複合シート１０Ａは、多孔
性フィルム１１Ａの両面に、上述の開孔フィルム１２Ａ
と同様の開孔フィルム１２Ａが接合されてなるものであ
る。このように、多孔性フィルムの両面に開孔フィルム
を設けることにより、上記透湿性複合シートの上記開孔
フィルム側に対して感圧接着剤等を接着した場合に、該
シートの構成物が接着剤に付着することがなく、付け剥
しが容易となる。Next, another embodiment of the moisture-permeable composite sheet of the present invention will be described with reference to FIG. Also, FIG.
FIG. 6 is a cross-sectional view showing another embodiment of the moisture-permeable composite sheet of the present invention. The moisture-permeable composite sheet 10A shown in FIG. 4 has the above-described apertured film 12A on both sides of the porous film 11A.
A perforated film 12A similar to the above is joined. In this way, by providing an apertured film on both sides of the porous film, when a pressure sensitive adhesive or the like is adhered to the apertured film side of the moisture-permeable composite sheet, the composition of the sheet adheres. It does not adhere to the agent and can be easily attached and removed.
【００２６】更に、図５を参照して、本発明の透湿複合
シートの他の実施例について説明する。図５は、本発明
の透湿性複合シートの更に他の実施例を示す断面図であ
る。図４に示す透湿性複合シート１０Ｂは、多孔性フィ
ルム１１Ｂの両面に、開孔フィルム１２Ｂが接合されて
なるものであり、該開孔フィルム１２Ｂは、孔部１３Ｂ
を有し、開孔底部１４Ｂと、上記多孔性フィルム１１Ｂ
に接合された頂部１５Ｂと、該開孔底部１４Ｂと該頂部
１５Ｂとをそれぞれ連結する筒状壁部１６Ｂとからなる
列、及び孔部１３Ｂよりも小さい孔部１３Ｂ’を有し、
開孔底部１４Ｂよりも小さい開孔底部１４Ｂ’と、上記
頂部１５Ｂよりも大きく多孔性フィルム１１Ｂに接合さ
れた頂部１５Ｂ’と、筒状壁部１６Ｂよりも小さく該開
孔底部と該頂部とをそれぞれ連結する筒状壁部１６Ｂ’
とからなる列により形成されている。このような構造と
することにより、接着性／剥離特性を更に向上させるこ
とができる。Further, another embodiment of the moisture-permeable composite sheet of the present invention will be described with reference to FIG. FIG. 5 is a cross-sectional view showing still another embodiment of the moisture-permeable composite sheet of the present invention. The moisture-permeable composite sheet 10B shown in FIG. 4 is formed by joining the perforated films 12B to both surfaces of the porous film 11B, and the perforated film 12B has pores 13B.
Having a hole bottom 14B and the porous film 11B.
A top portion 15B joined to each other, a row composed of a cylindrical wall portion 16B connecting the opening bottom portion 14B and the top portion 15B, and a hole portion 13B 'smaller than the hole portion 13B,
An opening bottom portion 14B 'smaller than the opening bottom portion 14B, a top portion 15B' larger than the top portion 15B and joined to the porous film 11B, and an opening bottom portion and the top portion smaller than the tubular wall portion 16B. Cylindrical wall part 16B 'to be respectively connected
It is formed by a row consisting of and. With such a structure, the adhesiveness / peelability can be further improved.
【００２７】次いで、本発明の透湿性複合シートの製造
方法の好ましい一実施態様について説明する。図６は、
本発明の透湿性複合シートの製造方法において好ましく
用いることができる製造装置を示す斜視図である。Next, a preferred embodiment of the method for producing a moisture-permeable composite sheet of the present invention will be described. Figure 6
It is a perspective view which shows the manufacturing apparatus which can be preferably used in the manufacturing method of the moisture-permeable composite sheet of this invention.
【００２８】図６において、製造装置２０は、図４に示
す如く、多孔性フィルムの片面に開孔フィルムを接合す
る装置であり、ロール状に巻回された開孔フィルム１２
を繰り出す繰り出し装置２１、上記繰り出し装置２１の
下流側に配置され、上記繰り出し装置２１により繰り出
された開孔フィルム１２にホットメルト接着剤を塗工す
るロールコーター２２、上記ロールコーター２２の下流
に設置され、ロール状に巻回された多孔性フィルム１１
を繰り出す繰り出し機２３、上記繰り出し機２３の下流
上方に配置され、ホットメルト接着剤を塗工した開孔フ
ィルム１２と上記多孔性フィルム１１とを接合一体化し
て透湿性複合シート１０とするニップロール２４、及び
ニップロール２４の下流に設置され、上記透湿性複合シ
ート１０を巻き取る巻取機２５とからなる。In FIG. 6, as shown in FIG. 4, the manufacturing apparatus 20 is an apparatus for joining the perforated film to one side of the porous film, and the perforated film 12 wound in a roll shape.
A feeding device 21 for feeding the hot-melt adhesive, a roll coater 22 arranged on the downstream side of the feeding device 21 for applying a hot-melt adhesive to the perforated film 12 fed by the feeding device 21, and installed downstream of the roll coater 22. Rolled porous film 11
And a nip roll 24 which is arranged on the downstream side of the above-mentioned feeding machine 23 and which joins and integrates the perforated film 12 coated with a hot melt adhesive and the porous film 11 into the moisture-permeable composite sheet 10. , And a winder 25 that is installed downstream of the nip roll 24 and winds the moisture-permeable composite sheet 10.
【００２９】また、上記ロールコーター２２は、上記開
孔フィルム１２の下方にてその上端が上記開孔フィルム
１２と接するように設置され、適量のホットメルト接着
剤を上記開孔フィルム１２に塗工するグラビアロール２
２Ａ、上記開孔フィルム１２の上方に設置され、上記開
孔フィルム１２をグラビアロール２２Ａに押しつけるバ
ックロール２２Ｂ、及び上記グラビアロール２２Ａの下
方に設置され、ホットメルト接着剤を蓄えて上記グラビ
アロール２２Ａに供給する液パン２２Ｃにより構成され
ている。The roll coater 22 is installed below the perforated film 12 so that its upper end is in contact with the perforated film 12, and an appropriate amount of hot melt adhesive is applied to the perforated film 12. Gravure Roll 2
2A, a back roll 22B that is installed above the perforated film 12 and presses the perforated film 12 against the gravure roll 22A, and is installed below the gravure roll 22A, and stores the hot melt adhesive and the gravure roll 22A. It is composed of a liquid pan 22C for supplying to the.
【００３０】なお、本実施例においては、上記ホットメ
ルト接着剤を塗工するものとして、ロールコーターを例
として説明したが、この例に限るものではなく、スプレ
ー方式あるいはスクリーンコーター等で塗工する方式の
装置であってもよく、かかる方式は本発明の製造方法に
おける加工速度や、用いる素材の選定によって適宜選択
することができる。また、スプレー方式による塗工は、
スパイラルスプレー等の多孔性フィルムの透湿性を阻害
しないものが好ましい。また、必要な大きさに切断する
工程は、図示していないが、上記巻取機２５の前に切断
する装置を導入しても良い。In this embodiment, a roll coater has been described as an example of applying the hot melt adhesive, but the present invention is not limited to this example, and a spray method or a screen coater is used for application. An apparatus of a system may be used, and such a system can be appropriately selected depending on the processing speed in the manufacturing method of the present invention and the selection of the material used. In addition, spray coating
Those that do not impair the moisture permeability of the porous film such as spiral spray are preferable. Although not shown in the figure, the step of cutting into a required size may be performed by introducing a cutting device before the winder 25.
【００３１】次いで、本実施態様による、上記透湿性複
合シート１０の製造方法について説明する。先ず、ロー
ル上に巻回された上記開孔フィルム１２が、上記繰り出
し装置２１によって繰り出され、上記ロールコーター２
２によりホットメルト接着剤を塗工される。次いで、上
記開孔フィルム１２が更に繰り出されて、上記繰り出し
装置２１によって繰り出された多孔性フィルム１１と重
ね合わせられた後、上記ニップロール２４によって接合
一体化され、透湿性複合フィルム１０が得られ、得られ
た透湿性複合フィルム１０は、上記巻取機２５により巻
き取られる。Next, a method of manufacturing the moisture-permeable composite sheet 10 according to this embodiment will be described. First, the perforated film 12 wound on a roll is delivered by the delivery device 21, and the roll coater 2
2 applies a hot melt adhesive. Next, the perforated film 12 is further unrolled, and after being superposed on the porous film 11 unrolled by the unrolling device 21, they are joined and integrated by the nip roll 24 to obtain the moisture-permeable composite film 10, The obtained moisture-permeable composite film 10 is wound by the winding machine 25.
【００３２】また、本実施例においては、多孔性フィル
ムの片面に開孔フィルムを接合する製造方法について説
明したが、両面に接合することもできる。例えば、上記
繰り出し機２１を２つ設けて、更にその間に上記繰り出
し機２３を設置する等した製造装置を用いて、上述の方
法と同様の方法により、接合することにより行うことが
できる。Further, in this embodiment, the manufacturing method in which the perforated film is joined to one side of the porous film has been described, but it is also possible to join to both sides. For example, it can be carried out by joining by the same method as the above, using a manufacturing apparatus in which two feeding machines 21 are provided and the feeding machine 23 is installed between them.
【００３３】以下に、具体的な実施例に基づいて本発明
の透湿性複合シートについて更に詳細に説明する。The moisture-permeable composite sheet of the present invention will be described below in more detail based on specific examples.
【００３４】〔実施例１〕ポリエチレン（三井石油化学
（株）製）１００重量部と、炭酸カルシウム（白石工業
（株）製）１５０重量部とを混合した樹脂組成物を、溶
融成形してフィルムとなし、次いで該フィルムを延伸処
理して得られた多孔性フィルムと、ポリエチレン（三井
石油化学（株）製）から成る厚さ０．６mmのフィルムを
予備加熱すると共に負圧をかけて開孔させた開孔フィル
ムとを、ゴム系ホットメルト接着剤（日東化成工業
（株）製）を、図６に示す上述の製造装置を用いて、ロ
ールコーターにより塗工して、接合一体化し、透湿複合
シートを得た。なお、上記開孔フィルムの、線幅は０．
５mm、目開は０．５mm、フィルム表面からフィルムの垂
直方向にのびる隆起した孔部を形成する壁部の高さは
０．３mmである。Example 1 A resin composition obtained by mixing 100 parts by weight of polyethylene (manufactured by Mitsui Petrochemical Co., Ltd.) and 150 parts by weight of calcium carbonate (manufactured by Shiraishi Industry Co., Ltd.) was melt-molded to form a film. Then, a 0.6 mm-thick film made of polyethylene (manufactured by Mitsui Petrochemical Co., Ltd.) and a porous film obtained by stretching the film was preheated and a negative pressure was applied to open the film. A rubber hot melt adhesive (manufactured by Nitto Kasei Kogyo Co., Ltd.) was applied to the perforated film with a roll coater using the above-described manufacturing apparatus shown in FIG. A wet composite sheet was obtained. The line width of the apertured film was 0.
The height is 5 mm, the opening is 0.5 mm, and the height of the wall portion forming a raised hole extending from the film surface in the vertical direction of the film is 0.3 mm.
【００３５】〔実施例２〕開孔フィルムとして、ＤＥＬ
ＮＥＴ Ｘ５５０（三晶（株）製）を用いた以外は、実
施例１と同様にして、透湿複合シートを得た。なお、上
記開孔フィルムの、線幅は約０．４mm、目開は約１mm、
フィルム表面からフィルムの垂直方向にのびる隆起した
孔部を形成する壁部の高さは約０．１mmである。Example 2 DEL was used as an apertured film.
A moisture-permeable composite sheet was obtained in the same manner as in Example 1 except that NET X550 (manufactured by Sansho Co., Ltd.) was used. The line width of the perforated film is about 0.4 mm, the opening is about 1 mm,
The height of the wall forming the raised holes extending from the film surface in the vertical direction of the film is about 0.1 mm.
【００３６】〔実施例３〕開孔フィルムとして、ティー
ロード ＳＫ−２００（山中産業（株）製）を用いた以
外は実施例１と同様にして、透湿複合シートを得た。な
お、上記開孔フィルムの、線幅は約０．１mm、目開は約
０．１mm、フィルム表面からフィルムの垂直方向にのび
る隆起した孔部を形成する壁部の高さは約０．２mmであ
る。[Example 3] A moisture-permeable composite sheet was obtained in the same manner as in Example 1 except that Teelord SK-200 (manufactured by Yamanaka Sangyo Co., Ltd.) was used as the apertured film. In the above-mentioned apertured film, the line width is about 0.1 mm, the opening is about 0.1 mm, and the height of the wall portion forming a raised hole extending from the film surface in the vertical direction of the film is about 0.2 mm. Is.
【００３７】〔比較例１〕ポリエチレン（三井石油化学
（株）製）１００重量部と、炭酸カルシウム（白石工業
（株）製）１５０重量部とを混合した樹脂組成物を、溶
融成形してフィルムとなし、次いで該フィルムを延伸処
理して得られた多孔性フィルムと、ＰＰ／ＰＥ芯鞘繊維
（２デニール、繊維長５１mm）からなる、坪量２０ｇ／
ｍ2 のサクションヒートボンド法による不織布とを、ゴ
ム系ホットメルト接着剤（日東化成工業（株）製）を、
図６に示す上述の製造装置を用いて、ロールコーターに
より塗工して、接合一体化し、透湿複合シートを得た。Comparative Example 1 A resin composition prepared by mixing 100 parts by weight of polyethylene (manufactured by Mitsui Petrochemical Co., Ltd.) and 150 parts by weight of calcium carbonate (manufactured by Shiraishi Industry Co., Ltd.) was melt-molded to form a film. And then comprising a porous film obtained by stretching the film and PP / PE core-sheath fiber (2 denier, fiber length 51 mm), basis weight 20 g /
and non-woven fabric by suction heat-bond method of m 2, rubber-based hot melt adhesive (manufactured by Nitto Kasei Kogyo Co., Ltd.),
Using the above-mentioned manufacturing apparatus shown in FIG. 6, coating was carried out by a roll coater and joining and integration were performed to obtain a moisture permeable composite sheet.
【００３８】〔比較例２〕ポリエチレン（三井石油化学
（株）製）１００重量部と、炭酸カルシウム（白石工業
（株）製）１５０重量部とを混合した樹脂組成物を、溶
融成形してフィルムとなし、次いで該フィルムを延伸処
理して、多孔性フィルムを得た。上記実施例１〜３及び
比較例１及び２で得られた透湿複合シート（比較例２で
は、多孔性フィルム）について、各試験を行った。その
結果および試験方法を表１に示す。Comparative Example 2 A resin composition obtained by mixing 100 parts by weight of polyethylene (manufactured by Mitsui Petrochemical Co., Ltd.) and 150 parts by weight of calcium carbonate (manufactured by Shiraishi Industry Co., Ltd.) was melt-molded to form a film. Then, the film was stretched to obtain a porous film. Each test was performed on the moisture-permeable composite sheet (in Comparative Example 2, a porous film) obtained in Examples 1 to 3 and Comparative Examples 1 and 2. The results and test methods are shown in Table 1.
【００３９】[0039]
【表１】 [Table 1]
【００４０】[0040]
【発明の効果】本発明によれば、透湿性を低下させるこ
となく、延伸配向によるＭＤ方向およびＣＤ方向の強度
差が改善され、且つ引き裂き強度が向上されており、特
に感圧接着剤等を用いた場合に、その表面接着性／剥離
特性をコントロールすることができる透湿性複合シート
およびその製造方法が提供される。従って、本発明の透
湿複合シートは、おむつ等のバックシートとして、に良
好に使用できる。また、本発明の製造方法方法によれ
ば、高速かつ安定的に均一な透湿性複合シートを製造す
ることができる。EFFECTS OF THE INVENTION According to the present invention, the strength difference in the MD direction and the CD direction due to the stretch orientation is improved and the tear strength is improved without lowering the moisture permeability. When used, a moisture-permeable composite sheet capable of controlling its surface adhesion / peelability and a method for producing the same are provided. Therefore, the moisture-permeable composite sheet of the present invention can be favorably used as a back sheet for diapers and the like. Further, according to the manufacturing method of the present invention, a uniform moisture-permeable composite sheet can be manufactured at high speed and stably.
【図１】図１は、本発明の透湿性複合シートの１実施例
を示す平面図である。FIG. 1 is a plan view showing one embodiment of a moisture-permeable composite sheet of the present invention.
【図２】図２は、図１の拡大斜視図である。図３は、図
２のＩ−Ｉ’断面図である。FIG. 2 is an enlarged perspective view of FIG. FIG. 3 is a sectional view taken along the line II ′ of FIG.
【図３】図３は、図２のＩ−Ｉ’断面図である。3 is a cross-sectional view taken along the line I-I ′ of FIG.
【図４】図４は、本発明の透湿性複合シートの他の実施
例を示す断面図である。FIG. 4 is a cross-sectional view showing another embodiment of the moisture-permeable composite sheet of the present invention.
【図５】図５は、本発明の透湿性複合シートの更に他の
実施例を示す断面図である。FIG. 5 is a cross-sectional view showing still another embodiment of the moisture-permeable composite sheet of the present invention.
【図６】図６は、本発明の透湿性複合シートの製造方法
において好ましく用いることができる製造装置を示す斜
視図である。FIG. 6 is a perspective view showing a manufacturing apparatus that can be preferably used in the method of manufacturing a moisture-permeable composite sheet of the present invention.
１０ 透湿性複合シート １１ 多孔性フィルム １２ 開孔フィルム １３ 孔部 １４ 開孔底部 １５ 頂部 １６ 筒状壁部 ２０ 製造装置 ２１ 繰り出し機 ２２ ロールコーター ２３ 繰り出し機 ２４ ニップロール ２５ 巻取機 10 Moisture-permeable composite sheet 11 Porous film 12 Opening film 13 Pore 14 Opening bottom 15 Top 16 Cylindrical wall 20 Manufacturing device 21 Feeder 22 Roll coater 23 Feeder 24 Nip roll 25 Winder
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 // Ｂ２９Ｋ 23:00 105:04 Ｂ２９Ｌ 9:00 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Internal reference number FI technical display area // B29K 23:00 105: 04 B29L 9:00
Claims (5)
組成物を溶融成形してフィルムとなし、次いで該フィル
ムを延伸処理して得られた多孔性フィルムの片面あるい
は両面に、無数の孔部を有し且つ上記多孔性フィルムよ
りも引き裂き強度の高い、通気性の開孔フィルムを接合
してなることを特徴とする透湿性複合シート。1. A porous film obtained by melt-molding a resin composition containing a thermoplastic resin and a filler to obtain a film, and then subjecting the film to a stretching process to form a myriad of pores on one or both sides. And a breathable apertured film having a higher tear strength than the above-mentioned porous film, which are bonded together.
フィルムがポリオレフィン樹脂製であることを特徴とす
る請求項１記載の透湿性複合シート。2. The moisture-permeable composite sheet according to claim 1, wherein the porous film and / or the apertured film is made of a polyolefin resin.
性樹脂及び上記充填剤の配合割合が、熱可塑性樹脂１０
０重量部に対して、充填剤５０〜２５０重量部であるこ
とを特徴とする請求項１記載の透湿性複合シート。3. The mixing ratio of the thermoplastic resin and the filler in the porous film is the thermoplastic resin 10
The moisture-permeable composite sheet according to claim 1, wherein the filler is 50 to 250 parts by weight with respect to 0 parts by weight.
と、裏側が空隙となっている凸状曲面からなる無数の頂
部と、該開孔底部と該頂部とをそれぞれ連結する筒状壁
部とを具備し、上記孔部が、一個の上記開孔底部と、隣
合う複数の上記頂部と、それらを連結する１個の筒状壁
部とからそれぞれ形成された連通孔構造からなってお
り、上記頂部の表面側が上記多孔性フィルムに接合され
ていることを特徴とする請求項１記載の透湿性複合シー
ト。4. The perforated film comprises an innumerable perforated bottom, an innumerable top formed of a convex curved surface having a void on the back side, and a cylindrical wall connecting the perforated bottom and the top, respectively. And a hole portion, and the hole portion has a communication hole structure formed of one hole bottom portion, a plurality of adjacent top portions, and one cylindrical wall portion connecting them. The moisture-permeable composite sheet according to claim 1, wherein the top surface side is joined to the porous film.
組成物を該熱可塑性樹脂の融点以上の温度で溶融成形し
てフィルムとなし、次いで該フィルムを該融点以下の温
度で延伸処理して得た多孔性フィルムの片面あるいは両
面に、無数の孔部を有し且つ上記多孔性フィルムよりも
引き裂き強度の高い、通気性の開孔フィルムを接合一体
化することを特徴とする透湿性複合シートの製造方法。5. A resin composition containing a thermoplastic resin and a filler is melt-molded at a temperature above the melting point of the thermoplastic resin to form a film, and the film is stretched at a temperature below the melting point. A moisture-permeable composite sheet, characterized in that a breathable perforated film having innumerable pores and having a higher tear strength than the porous film is bonded and integrated on one side or both sides of the obtained porous film. Manufacturing method.