JPH0621869Y2 - Laminated material for extrusion tubes - Google Patents
Laminated material for extrusion tubesInfo
- Publication number
- JPH0621869Y2 JPH0621869Y2 JP1987054272U JP5427287U JPH0621869Y2 JP H0621869 Y2 JPH0621869 Y2 JP H0621869Y2 JP 1987054272 U JP1987054272 U JP 1987054272U JP 5427287 U JP5427287 U JP 5427287U JP H0621869 Y2 JPH0621869 Y2 JP H0621869Y2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- synthetic resin
- laminated material
- extruded tube
- biaxially stretched
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】 ［産業上の利用分野］ 本考案は、練り歯磨，糊，練りがらし等のペースト状物
質が収容される押出しチューブ容器の容器胴部に成形さ
れる積層材、すなわち、押出しチューブ用積層材に関す
る。[Detailed Description of the Invention] [Industrial field of application] The present invention relates to a laminated material formed on a container body of an extruded tube container containing a paste-like substance such as toothpaste, paste, and paste, that is, , A laminated material for extruded tubes.
［従来の技術］ 練り歯磨、糊，練りがらし等に代表されるペースト状物
（流動〜半流動性物質）が収容されている押出しチュー
ブ容器は、所定の物性を有する積層材で成形されている
容器胴部に別製の肩部を具備する首部が貼着された容器
本体と、前記首部に嵌着されるキャップとで構成される
のが一般的である。[Prior Art] An extruded tube container containing a paste-like substance (fluid to semi-fluid substance) represented by toothpaste, paste, paste, etc. is formed of a laminated material having predetermined physical properties. It is generally composed of a container main body in which a neck portion having a separately-made shoulder portion is attached to an existing container body portion, and a cap fitted in the neck portion.
前記押出しチューブ容器における容器胴部には、押出し
チューブ容器における必然の物性である腰の強さが発揮
されなければならなく、前記容器胴部を構成する積層材
中には腰の強さを現出させる関係上、剛性に優れた性質
を有する紙層が必須の構成層として利用され、例えば、 合成樹脂層／着色合成樹脂層／ 紙層／金属箔層／合成樹脂層 の積層構成からなるチューブ用積層材が利用されてい
た。In the container body of the extruded tube container, the waist strength, which is an indispensable physical property in the extruded tube container, must be exhibited, and the waist strength appears in the laminated material forming the container body. A paper layer having excellent rigidity is used as an essential constituent layer for the purpose of taking it out. For example, a tube having a laminated structure of synthetic resin layer / colored synthetic resin layer / paper layer / metal foil layer / synthetic resin layer. Laminated material was used.
［考案が解決しようとする問題点］ ところで、従来の押出しチューブ用積層材においては、
該積層材の積層構成中に存在する紙層が極めて耐水性に
乏しいものであるため、チューブ容器胴部における積層
材の貼り合わせ部分に露出している積層材端面の紙層部
分から浸入する水の影響で、積層材の層同士の間で剥離
が生じ、本来の包装の機能を完全に維持し得なくなる欠
点を有している。[Problems to be solved by the invention] By the way, in the conventional extruded tube laminated material,
Since the paper layer existing in the laminated structure of the laminated material is extremely poor in water resistance, water penetrating from the paper layer portion of the end surface of the laminated material exposed at the portion where the laminated material is bonded in the body part of the tube container. Due to the influence of (3), peeling occurs between the layers of the laminated material, and there is a drawback that the original packaging function cannot be completely maintained.
このため、チューブ容器胴部における積層材の貼り合わ
せ部分に積層材端面が露出することのないように種々の
付加工程を加えたチューブ容器胴部も提案されている
が、本来のチューブ容器胴部の成形工程に加えて積層材
端面処理のための付加工程が必要であり、成形が繁雑で
ある。For this reason, a tube container body part in which various additional steps are added so that the laminated material end face is not exposed at the laminated material bonding part in the tube container body part is proposed, but the original tube container body part In addition to the molding process of (1), an additional process for treating the end surface of the laminated material is required, and molding is complicated.
また、前記従来の押出しチューブ用積層材は、その構成
中に金属箔層を埋没させることによってガスバリヤー性
を得るものであり、該積層材によって得られるチューブ
容器胴部が不透明となるため、使用期間中における内填
物の残存量等を視認することができなく、不便を来すこ
とが生じている。Further, the conventional extruded tube laminated material is to obtain a gas barrier property by burying a metal foil layer in the structure thereof, and the tube container body obtained by the laminated material becomes opaque. It is not possible to visually confirm the remaining amount of the filling material during the period, which causes inconvenience.
これに対して本考案は、その積層工程中に前述の紙層と
金属箔層とに代えて、ガスバリヤー性と剛性とを兼備す
るエチレン・ビニルアルコール共重合体あるいはポリ塩
化ビニリデン樹脂の二軸延伸合成樹脂フィルムによる剛
性を有する中間層を具備するものであり、前記従来の紙
層を具備するチューブ用積層材や金属箔層を具備するチ
ューブ用積層材では得られない内填物の視認可能な透明
性と、紙層によって奏されるものと同様の腰の強さ（剛
性）と、金属箔層によって奏されるものと同様のガスバ
リヤー性とを発現する紙無し押出しチューブ用積層材を
提供する。On the other hand, in the present invention, in place of the above-mentioned paper layer and metal foil layer during the laminating process, the biaxial of ethylene / vinyl alcohol copolymer or polyvinylidene chloride resin having both gas barrier property and rigidity is provided. It has a rigid intermediate layer made of a stretched synthetic resin film, and it is possible to visually check the internal filler that cannot be obtained with the conventional tube laminate having the paper layer and the tube laminate having the metal foil layer. A laminated material for a paperless extruded tube that exhibits excellent transparency, a stiffness (rigidity) similar to that achieved by the paper layer, and a gas barrier property similar to that achieved by the metal foil layer. provide.
［問題点を解決するための手段］ 本考案の紙無し押出しチューブ用積層材は、押出しチュ
ーブ容器の容器胴部に成形されたときに該容器胴部の外
側層となる外層がヒートシール性能を有する合成樹脂層
で構成され、同じく容器胴部に成形されたときに該容器
胴部の内側層となる内層が同じくヒートシール性能を有
する合成樹脂層で構成され、かつ、前記外層と内層との
間には、エチレン・ビニルアルコール共重合体あるいは
ポリ塩化ビニリデン樹脂の二軸延伸合成樹脂フィルムに
よる剛性を有する中間層が位置している３層構成からな
る。[Means for Solving the Problems] In the laminated material for a paperless extruded tube of the present invention, the outer layer, which is an outer layer of the extruded tube container, is an outer layer of the extruded tube container having a heat-sealing performance. Comprised of a synthetic resin layer having, the inner layer which is also an inner layer of the container body when formed into a container body is also composed of a synthetic resin layer having heat sealing performance, and the outer layer and the inner layer A three-layer structure in which an intermediate layer having rigidity made of a biaxially stretched synthetic resin film of an ethylene / vinyl alcohol copolymer or a polyvinylidene chloride resin is located in between.
そして、前記中間層を構成している二軸延伸合成樹脂フ
ィルムには部分的な印刷模様層が形成されており、平面
視の状態で前記印刷模様層によって隠蔽される部分以外
は全体として透明〜半透明部分とされており、かつ全体
としてガスバリヤー性を有している。The biaxially stretched synthetic resin film forming the intermediate layer has a partial printed pattern layer formed thereon, and is transparent as a whole except for a portion hidden by the printed pattern layer in a plan view. It is a semi-transparent part and has gas barrier properties as a whole.
以上の通りの構成からなる本考案の紙無し押出しチュー
ブ用積層材によって得られる容器胴部は、積層材におけ
る先の透明〜半透明部分を通して内填物を視認し得る。The container body obtained by the laminated material for a paperless extruded tube of the present invention having the above-described configuration can visually recognize the internal filler through the transparent to translucent portion of the laminated material.
本考案の紙無し押出しチューブ用積層材における外層は
ヒートシール性能を有する合成樹脂で構成されることは
前記した通りであるが、この外層は保護層の機能をも果
すものであり、かつ、ガスバリヤー性を有する二軸延伸
合成樹脂フィルム、すなわちエチレン・ビニルアルコー
ル共重合体あるいはポリ塩化ビニリデン樹脂による二軸
延伸合成樹脂フィルムに付されている印刷模様層が透視
し得るように、また、押出しチューブ用積層材による押
出しチューブ容器内の内填物が視認し得るように、透明
〜半透明層とされている。As described above, the outer layer of the laminated material for a paperless extruded tube of the present invention is composed of a synthetic resin having a heat-sealing property, but this outer layer also functions as a protective layer, and the gas is A biaxially stretched synthetic resin film having a barrier property, that is, an extruded tube so that the printed pattern layer attached to the biaxially stretched synthetic resin film made of an ethylene / vinyl alcohol copolymer or a polyvinylidene chloride resin can be seen through. The transparent to semi-transparent layer is formed so that the filling material in the extruded tube container made of the laminated material can be visually recognized.
この外層は、例えば低密度ポリエチレン，中密度ポリエ
チレン，高密度ポリエチレン，線状低密度ポリエチレ
ン，ポリプロピレン、エチレン−酢酸ビニル共重合体，
エチレン−アクリル酸共重合体，エチレン−メタクリル
酸共重合体，エチレンやプロピレンとカルボン酸化合物
との共重合体，エチレン−α・オレフィン共重合体，ポ
リアクリロニトリル，ポリアミド等の合成樹脂で形成さ
れるのが普通である。This outer layer is, for example, low density polyethylene, medium density polyethylene, high density polyethylene, linear low density polyethylene, polypropylene, ethylene-vinyl acetate copolymer,
Made of synthetic resin such as ethylene-acrylic acid copolymer, ethylene-methacrylic acid copolymer, copolymer of ethylene or propylene and carboxylic acid compound, ethylene-α / olefin copolymer, polyacrylonitrile, polyamide Is normal.
内層は前記外層と同様にヒートシール性能を有する合成
樹脂で構成されるが、該内層は押出しチューブ容器内に
収容される内填物と接する層であるから、内填物が飲，
食品である場合には、その衛生上の問題からポリオレフ
ィンで構成されるのが好適である。The inner layer is composed of a synthetic resin having a heat-sealing property like the outer layer, but since the inner layer is a layer in contact with the inner filler contained in the extruded tube container, the inner filler is
In the case of food, it is preferable to be composed of polyolefin because of its hygienic problems.
なお、剛性を有する中間層として使用される二軸延伸合
成樹脂フィルムは、エチレン・ビニルアルコール共重合
体またはポリ塩化ビニリデン樹脂によるフィルムで、ガ
スバリヤー性と剛性とを兼備する。この二軸延伸合成樹
脂フィルムは、ベタ刷りの隠蔽層となるようなことのな
い部分印刷模様層を具備している。該印刷模様層は、二
軸延伸合成樹脂フィルムの表面に形成されていても、あ
るいは裏面に形成されていても良い。The biaxially stretched synthetic resin film used as the intermediate layer having rigidity is a film made of ethylene / vinyl alcohol copolymer or polyvinylidene chloride resin and has both gas barrier property and rigidity. This biaxially stretched synthetic resin film has a partially printed pattern layer that does not serve as a solid-state masking layer. The printed pattern layer may be formed on the front surface or the back surface of the biaxially stretched synthetic resin film.
更に、前記紙無し押出しチューブ用積層材において、外
層と内層とが同質の合成樹脂で構成される場合には、前
記積層材から押出しチューブ容器の容器胴部を成形する
際の熱溶着工程が極めて容易であり、封緘部の接着強度
に優れた容器胴部が得られる。Further, in the paperless extruded tube laminated material, when the outer layer and the inner layer are made of the same synthetic resin, the heat welding step when molding the container body of the extruded tube container from the laminated material is extremely A container body that is easy and has excellent adhesive strength at the sealing portion can be obtained.
また、同じく優れた接着強度が得られるという理由で、
容器胴部に接合される肩部や首部も前記積層材の最外層
と最内層とを構成している熱可塑性合成樹脂と同質の合
成樹脂で形成されている押出しチューブ容器とされるの
が最も好適である。Also, because the same excellent adhesive strength can be obtained,
It is most preferable that the shoulder portion and the neck portion joined to the container body are also extruded tube containers made of the same synthetic resin as the thermoplastic synthetic resin forming the outermost layer and the innermost layer of the laminated material. It is suitable.
更に、前記本考案の紙無し押出しチューブ用積層材は、
各層間を接着する接着剤を利用した貼り合わせ工程によ
って、あるいは中間層となる二軸延伸フィルムに対して
所定の各層を押出しコーティングするか、更には接着剤
を利用する貼り合わせ工程と押出しコーティングとを併
用する等して得られる。Further, the laminated material for a paperless extruded tube of the present invention is
By a bonding process using an adhesive that bonds each layer, or by extrusion-coating each predetermined layer on a biaxially stretched film that is an intermediate layer, or by a bonding process using an adhesive and extrusion coating. It is obtained by using together.
［実施例］ 以下、本考案の紙無し押出しチューブ用積層材の具体的
な構成を、製造実施例を以って説明する。[Examples] Hereinafter, a specific configuration of the laminated material for a paperless extruded tube of the present invention will be described with reference to manufacturing examples.
実施例 リニアー低密度ポリエチレンフィルム［タマポリ（株）
製：ＵＢ−１，150μ］２枚と、二軸延伸エチレン・ビ
ニルアルコール共重合体フィルム［エバールＸＬフィル
ム：１５μ，（株）クラレ製］に部分印刷模様層をグラ
ビア印刷法にて形成したフィルムとを準備し、前記二軸
延伸エチレン・ビニルアルコール共重合体フィルムの非
印刷面とリニアー低密度ポリエチレンフィルムの１枚と
を２液硬化型ウレタン系接着剤にて貼り合わせた後、得
られた貼り合わせフィルムの印刷面ともう一枚のリニア
ー低密度ポリエチレンフィルムとを、同じく２液硬化型
ウレタン系接着剤で貼着し、図面にて示される積層構
成、すなわち、リニアー低密度ポリエチレン樹脂層（15
0μ）からなる外層２と、接着剤Ｓ１と、裏面に印刷模
様層Ｍを有する二軸延伸エチレン・ビニルアルコール共
重合体フィルム層（１５μ）からなる剛性を有する中間
層３と、接着剤Ｓ２と、リニアー低密度ポリエチレン樹
脂層（150μ）からなる内層４との積層構成による本考
案の実施例品たる紙無し押出しチューブ用積層材１を得
た。Examples Linear low-density polyethylene film [Tama Poly Co., Ltd.
Made: UB-1,150μ] and a biaxially stretched ethylene / vinyl alcohol copolymer film [Eval XL film: 15μ, made by Kuraray Co., Ltd.] with a partially printed pattern layer formed by a gravure printing method. Was prepared, and the non-printed surface of the biaxially stretched ethylene / vinyl alcohol copolymer film and one piece of the linear low-density polyethylene film were bonded together with a two-component curing type urethane adhesive, and then obtained. The printed surface of the laminated film and another linear low-density polyethylene film are adhered with the same two-component curing type urethane adhesive, and the laminated structure shown in the drawing, that is, the linear low-density polyethylene resin layer ( 15
0 μ) outer layer 2, an adhesive S 1 , a biaxially stretched ethylene / vinyl alcohol copolymer film layer (15 μ) having a printed pattern layer M on the back surface, and a rigid intermediate layer 3, and an adhesive S 1. A laminated material 1 for a paperless extruded tube, which is an example product of the present invention, having a laminated constitution of 2 and an inner layer 4 made of a linear low-density polyethylene resin layer (150 μ) was obtained.
得られた紙無し押出しチューブ用積層材を利用し、熱溶
着法により押出しチューブ容器の容器胴部を成形したと
ころ、従来の積層構成中に紙層が存在している積層材か
ら得られた容器胴部が有する指触感と全く同様の指触感
を有する腰の強いものが得られた。Using the obtained laminated material for extruded tube without paper, a container body of an extruded tube container was formed by a heat welding method, and a container obtained from a laminated material in which a paper layer is present in a conventional laminated structure A strong product having the same feel as that of the body was obtained.
また、二軸延伸エチレン・ビニルアルコール共重合体フ
ィルムに付されている美麗なグラビア印刷層が優れた印
刷効果を現出しており、意匠性においても優れた作用を
奏しており、また、印刷模様層以外の部分（平面視で）
は、容器内部を容易に視認し得る透明性を有していた。In addition, the beautiful gravure printing layer attached to the biaxially stretched ethylene / vinyl alcohol copolymer film exhibits an excellent printing effect, and also has an excellent effect in terms of designability. Parts other than layers (in plan view)
Had transparency such that the inside of the container was easily visible.
［考案の作用および効果］ 本考案の紙無し押出しチューブ用積層材は、該積層材を
構成する積層構成中に紙層を具備することがなく、か
つ、従来のチューブ用積層材において腰の強さを発現さ
せるために必須，不可欠とされていた紙層の奏する作用
を、ガスバリヤー性と剛性とを有する二軸延伸合成樹脂
フィルム、すなわちエチレン・ビニルアルコール共重合
体フィルムまたは塩化ビニリデン樹脂による二軸延伸フ
ィルムで発現させるものである。[Operation and Effect of the Invention] The laminated material for a paperless extruded tube of the present invention does not have a paper layer in the laminated structure constituting the laminated material, and is strong in the conventional laminated material for a tube. The function of the paper layer, which has been indispensable and essential for achieving the desired effect, is produced by a biaxially stretched synthetic resin film having gas barrier properties and rigidity, that is, an ethylene / vinyl alcohol copolymer film or a vinylidene chloride resin. It is expressed by an axially stretched film.
従って、本考案の紙無し押出しチューブ用積層材は、例
えば練り歯磨のように水と接触しやすい環境下で使用さ
れても、吸湿による積層材の層間剥離が生ずるというよ
うなことがなく、極めて優れた耐水性能を具備するチュ
ーブ容器胴部が得られるという作用，効果を奏する。Therefore, the laminated material for a paperless extruded tube of the present invention does not cause delamination of the laminated material due to moisture absorption even when used in an environment where it is likely to come into contact with water, such as toothpaste. This has the function and effect of obtaining a tube container body having excellent water resistance.
また、本考案の紙無し押出しチューブ用積層材は、前記
ガスバリヤー性を有するだけでなく押出しチューブ用積
層材に腰の強さ（剛性）をもたらす二軸延伸合成樹脂フ
ィルムによる剛性を有する中間層を具備しているので、
従来の紙層を具備する積層材と全く同様の指触感を有す
るとともに、金属箔層を具備する積層材と同様にガスバ
リヤー性に優れた性質を有するチューブ容器胴部とな
る。In addition, the laminated material for a paperless extruded tube of the present invention not only has the above-mentioned gas barrier property, but also has the rigidity of the biaxially stretched synthetic resin film that provides the extruded tube laminated material with rigidity (rigidity). Since it has
The tube container body has the same feel and feel as a laminated material having a conventional paper layer, and has the same excellent gas barrier properties as a laminated material having a metal foil layer.
更に、本考案の紙無し押出しチューブ用積層材は、該積
層材の積層構成中に紙層や金属箔等からなる内填物に対
する隠蔽層となる層が無く、しかも印刷模様層は部分的
に形成されている印刷模様層である、すなわち、平面視
の状態で印刷模様層が存する以外の部分が透明〜半透明
とされているため、該部分から内填物を容易に透視し得
ることにより、消費者に安心感を与える押出しチューブ
容器が得られる。Further, the laminated material for a paperless extruded tube of the present invention does not have a layer serving as a concealing layer for an internal filler such as a paper layer or a metal foil in the laminated structure of the laminated material, and the printed pattern layer is partially formed. It is a printed pattern layer that is formed, that is, since the portion other than the printed pattern layer in a plan view is transparent to translucent, it is possible to easily see through the filling material from the portion. An extruded tube container that gives consumers a sense of security is obtained.
更にまた、本考案の紙無し押出しチューブ用積層材は、
剛性を有する中間層であるガスバリヤー性を有する二軸
延伸合成樹脂フィルムに予め印刷模様層が付されている
フィルムを使用しているので、複雑なしかも美麗な印刷
層による意匠効果が奏されるチューブ容器胴部が得られ
る。Furthermore, the laminated material for a paperless extruded tube of the present invention is
A biaxially stretched synthetic resin film having gas barrier properties, which is an intermediate layer having rigidity, is provided with a printed pattern layer in advance, so that a complicated and beautiful printed layer provides a design effect. A tube container body is obtained.
すなわち、表面の平滑性に優れた性質を有する二軸延伸
合成樹脂フィルムに印刷層を形成しるものであるから、
印刷が良好であり、複雑な絵柄を現出させ得る等の特徴
を存するものである。特に従来の押出しチューブ用積層
材における印刷層が、中間層と最内層との積層シートの
中間層の表面に印刷を施し、更に前記中間層の表面に最
外層を形成することにより現出されるか、あるいは積層
材の表面に印刷を施すことによって現出されるかしてい
たものと比較し、予め印刷層が形成されている二軸延伸
合成樹脂フィルムにおける印刷層によって得られる前述
の作用，効果は極めて顕著である。That is, since the printing layer is formed on the biaxially stretched synthetic resin film having excellent surface smoothness,
The printing is good, and it has features such that a complicated pattern can be revealed. In particular, a printed layer in a conventional extruded tube laminate is revealed by printing on the surface of the intermediate layer of the laminated sheet of the intermediate layer and the innermost layer, and further forming an outermost layer on the surface of the intermediate layer. Or, the above-mentioned effect obtained by the printing layer in the biaxially stretched synthetic resin film in which the printing layer is formed in advance, as compared with the one which is revealed by applying the printing to the surface of the laminated material, The effect is extremely remarkable.
更にまた、本考案の紙無し押出しチューブ用積層材は、
外層，中間層，内層をそれぞれ構成する合成樹脂と、場
合によって使用される接着剤とで構成されるものである
から、構成が単純であるため、安価に製造し得る。Furthermore, the laminated material for a paperless extruded tube of the present invention is
Since it is composed of the synthetic resin constituting each of the outer layer, the intermediate layer, and the inner layer and the adhesive agent used in some cases, the structure is simple and therefore the manufacturing cost can be reduced.
図は本考案の紙無し押出しチューブ用積層材の１実施例
品を模型的に示す断面図である。 １：紙無し押出しチューブ用積層材、２：外層、３：エ
チレン・ビニルアルコール共重合体あるいはポリ塩化ビ
ニリデン樹脂の二軸延伸合成樹脂フィルムによる剛性を
有する中間層、４：内層、Ｓ１，Ｓ２：接着剤。FIG. 1 is a cross-sectional view showing a model of one embodiment of the laminated material for a paperless extruded tube of the present invention. 1: Laminated material for extruded tube without paper, 2: Outer layer, 3: Intermediate layer having rigidity by biaxially stretched synthetic resin film of ethylene / vinyl alcohol copolymer or polyvinylidene chloride resin, 4: inner layer, S 1 , S 2 : Adhesive.
Claims (3)
る外層と、同じくヒートシール性能を有する合成樹脂層
による内層と、前記外層と内層との間に位置するエチレ
ン・ビニルアルコール共重合体あるいはポリ塩化ビニリ
デン樹脂の二軸延伸合成樹脂フィルムによる剛性を有す
る中間層とからなる３層構成の積層材で、前記中間層を
構成している二軸延伸合成樹脂フィルムには部分的な印
刷模様層が形成されており、平面視の状態において前記
印刷模様層が存在する部分以外の部分においては、全体
として透明〜半透明であり、かつガスバリヤー性を有す
ることを特徴とする紙無し押出しチューブ用積層材。1. An outer layer made of a synthetic resin layer having heat sealability, an inner layer made of a synthetic resin layer having heat sealability, and an ethylene / vinyl alcohol copolymer or polychlorine located between the outer layer and the inner layer. A laminated material having a three-layer structure composed of a biaxially stretched synthetic resin film of vinylidene resin and an intermediate layer having rigidity, and a partially printed pattern layer is formed on the biaxially stretched synthetic resin film forming the intermediate layer. The laminated material for a paperless extruded tube is characterized in that it is transparent to translucent as a whole and has a gas barrier property in a portion other than the portion where the printed pattern layer is present in a plan view. .
ィルムに対して、ヒートシール性能を有する合成樹脂層
による外層と内層とが、押出しコーティング層で形成さ
れている実用新案登録請求の範囲第１項記載の紙無し押
出しチューブ用積層材。2. A utility model registration request wherein an outer layer and an inner layer of a synthetic resin layer having heat sealing performance are formed by extrusion coating layers with respect to a biaxially stretched synthetic resin film constituting an intermediate layer. A laminated material for a paperless extruded tube according to claim 1.
ィルムに対して、ヒートシール性能を有する合成樹脂層
による外層と内層とが、接着剤で貼着されている合成樹
脂フィルム層で形成されている実用新案登録請求の範囲
第１項記載の紙無し押出しチューブ用積層材。3. A synthetic resin film layer in which an outer layer and an inner layer made of a synthetic resin layer having a heat-sealing property are attached with an adhesive to a biaxially stretched synthetic resin film constituting an intermediate layer. The laminated material for a paperless extruded tube according to claim 1, which has been formed.