JPH0533309A - Parking facility structure and execution method thereof - Google Patents

Parking facility structure and execution method thereof

Info

Publication number
JPH0533309A
JPH0533309A JP3186301A JP18630191A JPH0533309A JP H0533309 A JPH0533309 A JP H0533309A JP 3186301 A JP3186301 A JP 3186301A JP 18630191 A JP18630191 A JP 18630191A JP H0533309 A JPH0533309 A JP H0533309A
Authority
JP
Japan
Prior art keywords
layer
resin
fiber
aggregate
thermosetting resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP3186301A
Other languages
Japanese (ja)
Other versions
JP3163447B2 (en
Inventor
Shuya Tsuji
修也 辻
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DIC Corp
Original Assignee
Dainippon Ink and Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=16185932&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=JPH0533309(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Dainippon Ink and Chemicals Co Ltd filed Critical Dainippon Ink and Chemicals Co Ltd
Priority to JP18630191A priority Critical patent/JP3163447B2/en
Publication of JPH0533309A publication Critical patent/JPH0533309A/en
Application granted granted Critical
Publication of JP3163447B2 publication Critical patent/JP3163447B2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

PURPOSE:To improve performance by successively laminating each layer of a high molecular composition having a specific tensile elongation rate, adhesives as required, a fiber-reinforced thermosetting resin and surface pavement on a base body. CONSTITUTION:A film type or sheet-shaped high molecular composition having a tensile elongation rate of 30% or more in JISK6301 is prepared, and applied or bonded with a base body such as the housetop, indoors, underground section, etc., of a building. Adhesives such as an urethane group are further applied as required. A fiber-reinforced thermosetting resin layer composed of an unsaturated polymer ester resin, etc., and glass fiber, etc., is formed onto the adhesives. A surface pavement layer consisting of a resin/aggregate or cement mortar/ aggregate is further formed preferably onto the resin layer. Accordingly, light- weight tough waterproof structure can be formed on the new or existing base body while abrasion resistance, oil resistance and travelling can be improved.

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【産業上の利用分野】本発明は、耐摩耗性、耐油性、強
度、防水性、施工性に優れる土木建築物の屋外あるいは
建物内部の駐車場構造体および駐車場施工法に関するも
のである。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a parking lot structure and a parking lot construction method for an outdoor or internal portion of a civil engineering building having excellent wear resistance, oil resistance, strength, waterproofness and workability.

【0002】[0002]

【従来の技術】近年乗用車等車両数の増加と共に、都市
部での駐車場不足が大きな問題になってきた。その対策
としてビル屋上、あるいは建物内部、地下等を施工し駐
車場として利用する工法が採用されてきた。これらは建
物の付帯施設となるため、当然のことながら防水機能も
要求されるが、自動車の通行などを前提とする特殊な条
件に対応出来ることが必要である。すなわち防水材と舗
装材の両方の機能が要求される。現在の一般的な仕様と
しては、アスファルト防水材の上に押さえ層として4〜
8cm厚のアスファルト合材やコンクリートを打設し舗装
として使用する。
2. Description of the Related Art With the increase in the number of vehicles such as passenger cars in recent years, the shortage of parking lots in urban areas has become a serious problem. As a countermeasure, a construction method has been adopted in which the roof of the building, the inside of the building, or the underground is constructed and used as a parking lot. Since these are incidental facilities to the building, they are naturally required to have a waterproof function, but it is necessary to be able to cope with special conditions premised on the passage of cars. That is, the functions of both a waterproof material and a paving material are required. Currently, the general specifications are 4 to 4 as a pressing layer on the asphalt waterproof material.
8 cm thick asphalt mixture or concrete is placed and used as pavement.

【0003】この仕様の問題点は1)防水層の上に重量
の大きいアスファルト合材やコンクリートをのせるので
建物の梁や柱の設計荷重を大きくする必要がある。2)
防水層の上にアスファルト合材等を打設する場合、転圧
機やしきならし機等の重機類を使用したとき、防水層を
傷つけ漏水につながる。3)防水層を補修する場合、押
さえ層が邪魔になり作業が難しい。
Problems with this specification are as follows: 1) Since a heavy asphalt mixture or concrete is placed on the waterproof layer, it is necessary to increase the design load of the beams and columns of the building. 2)
When casting asphalt mixture on the waterproof layer, when using heavy machinery such as a compacting machine or a leveling machine, the waterproof layer may be damaged and lead to water leakage. 3) When repairing the waterproof layer, the pressing layer is an obstacle and the work is difficult.

【0004】[0004]

【発明が解決しようとする課題】即ち、駐車場の防水性
能としての基本条件は、(1)大規模建物が多いため駆
体コンクリートのひびわれや挙動に対して十分追従性が
あること。(2)寒冷地を含め、低温時において車の衝
撃振動などに耐ええる十分な柔軟性があること。(3)
車の発進、停止などによるせん断負荷に対し耐えるこ
と。(4)耐ガソリン、耐重油性等に優れることであ
る。
That is, the basic conditions for waterproofing of a parking lot are: (1) Since there are many large-scale buildings, there is sufficient followability to cracks and behavior of the concrete. (2) Sufficient flexibility to withstand shock and vibration of the car at low temperatures, including in cold regions. (3)
Withstand shearing loads such as when the vehicle starts and stops. (4) It has excellent resistance to gasoline and heavy oil.

【0005】[0005]

【課題を解決するための手段】本発明者は、上記課題を
解決するため鋭意研究の結果、高強度で腐食性に優れる
強化プラスチック層と柔軟性に優れるゴム材層を組み合
わせ防水層仕様とし、滑り止め樹脂/骨材層を舗装層と
して使用することで、優れた駐車場構造体および駐車場
施工法になることを見い出し本発明を完成するに到っ
た。
Means for Solving the Problems As a result of intensive research to solve the above-mentioned problems, the present inventors have made a waterproof layer specification by combining a reinforced plastic layer having high strength and excellent corrosiveness and a rubber material layer having excellent flexibility, The inventors have found that the use of a non-slip resin / aggregate layer as a pavement layer provides an excellent parking lot structure and parking lot construction method, and completed the present invention.

【0006】すなわち上から、(A)表面舗装層好まし
くは滑り止め樹脂/骨材層、(B)繊維強化熱硬化性樹
脂層、(C)繊維強化熱硬化樹脂層用接着剤層、(D)
JISK6301での引張り伸び率が30%以上の高分
子組成物層、(E)基体からなる駐車場構造体及びその
施工法を提供するものである。次に本発明を詳細に説明
する。
That is, from the top, (A) surface pavement layer, preferably non-slip resin / aggregate layer, (B) fiber-reinforced thermosetting resin layer, (C) adhesive layer for fiber-reinforced thermosetting resin layer, (D) )
A parking lot structure comprising a polymer composition layer having a tensile elongation of 30% or more according to JIS K6301, a (E) substrate, and a construction method thereof. Next, the present invention will be described in detail.

【0007】本発明に用いる基本(E)とは、例えば、
セメントコンクリート、アスファルトコンクリート、JI
S5403(石綿スレート)、ALC板、PC板、FRP、プラスチ
ック、木質物、金属などの単独あるいは組み合わせで構
成されたもので、その形状はいずれのものでもよく、構
造物の表面であれば球面、曲面、延長面、平面、斜面等
いずれでも良い。通常、セメントコンクリート、アスフ
ァルトコンクリートの平面、斜面である。
The basic (E) used in the present invention is, for example,
Cement concrete, asphalt concrete, JI
S5403 (asbestos slate), ALC plate, PC plate, FRP, plastic, wood, metal, etc. are used alone or in combination, any shape may be used, and if the surface of the structure is spherical, It may be a curved surface, an extended surface, a flat surface, an inclined surface, or the like. Usually, it is a plane or slope of cement concrete or asphalt concrete.

【0008】本発明に用いるJISK6301に規定する引張伸
び率が30%以上の高分子組成物層(D)としては、塗膜
型樹脂組成物とシート状体が挙げられるが、前者の場合
にはコンクリート、金属等の堅固な基本は、必要に応じ
て下地処理、プライマー処理等を行うとよい。
Examples of the polymer composition layer (D) having a tensile elongation of 30% or more specified in JIS K6301 used in the present invention include a coating film type resin composition and a sheet-like body. In the former case, For solid foundations such as concrete and metal, it is advisable to carry out a base treatment, a primer treatment, etc., if necessary.

【0009】基本(E)と塗膜型樹脂組成物(D)との層間に
使用するプライマーとは、一般公知のプライマーで、例
えば一液湿気硬化型ウレタンプライマー、ビスフェノー
ルA型エポキシ/ポリアミン系プライマー、不飽和ポリ
エステル系プライマー等を用いることができる。
The primer used between the layers of the base (E) and the coating film type resin composition (D) is a generally known primer, for example, a one-component moisture curing type urethane primer, a bisphenol A type epoxy / polyamine type primer. An unsaturated polyester-based primer or the like can be used.

【0010】引張り伸び率が30%以上の高分子組成物層
(D)の材質が、シート状体の場合、基本との接着には接
着剤を使用する。この接着剤には、大別して有機溶剤系
と非有機溶剤系は、エマルジョン型及び主剤と硬化剤を
混合して使用する二液反応型があり、いずれも有機溶剤
を含有しないものである。この接着剤は、基体とシート
状体のみならず、シート状体を複数重ねて用いる場合に
はシート状体相互の接着剤としても使用される。
Polymer composition layer having a tensile elongation of 30% or more
When the material of (D) is a sheet, an adhesive is used to bond it to the base. This adhesive is roughly classified into an organic solvent type and a non-organic solvent type, an emulsion type and a two-component reaction type in which a main agent and a curing agent are mixed and used, and none of them contains an organic solvent. This adhesive is used not only as a substrate and a sheet-shaped body, but also as an adhesive agent between sheet-shaped bodies when a plurality of sheet-shaped bodies are used in piles.

【0011】本発明のJISK6301での引張伸び率が30%以
上の高分子組成物層(D)としては、具体的には次のよ
うなものである。塗膜型樹脂組成物としては、JISA6910
複層仕上塗材、JISA6910ではポリマーセメント系複層仕
上塗材、合成樹脂Em(Emはエマルジョンを示す、以下同
様)系複層仕上げ塗材、反応硬化形合成樹脂エマルジョ
ン系複層仕上塗材等の主材層が該当する。上記JISA6910
のポリマーセメント系複層塗材とは結合材としてセメン
ト及び混和用ポリマーデイスパージョンとは、JISA6023
で規定するアクリル系、酢酸ビニル系などのEm合成樹脂
である。
Specific examples of the polymer composition layer (D) having a tensile elongation of 30% or more according to JIS K6301 of the present invention are as follows. As the coating film type resin composition, JIS A6910
Multi-layer finish coating material, polymer cement-based multi-layer finish coating material in JIS A6910, synthetic resin Em (Em stands for emulsion, the same applies hereinafter) -based multi-layer finish coating material, reaction-curable synthetic resin emulsion-based multi-layer finish coating material, etc. The main material layer of is applicable. Above JIS A6910
Cement as a binder and polymer dispersion for admixture is JIS A 6023.
It is an Em synthetic resin such as an acrylic resin or vinyl acetate resin specified in.

【0012】また、上記合成樹脂Em系複層塗材とはアク
リル系、酢酸ビニル系などの合成樹脂Emである。また、
上記反応硬化型合成樹脂Emとはエポキシ樹脂などの反応
硬化型合成樹脂Emである。また上記合成樹脂溶液系複層
仕上塗材とは、アクリル系、ビニル系などの合成樹脂を
キシレン、トルエンなどの有機溶剤で溶解したもの及び
エポキシ系、ウレタン系などの反応硬化型合成樹脂をキ
シレン、トルエンなどの有機溶剤で溶解したものであ
る。
Further, the synthetic resin Em-based multi-layer coating material is a synthetic resin Em such as acrylic or vinyl acetate. Also,
The reaction-curable synthetic resin Em is a reaction-curable synthetic resin Em such as an epoxy resin. Further, the above-mentioned synthetic resin solution-based multi-layer finish coating material is a synthetic resin of acrylic type, vinyl type or the like dissolved in an organic solvent such as xylene or toluene, or a reaction curable synthetic resin of epoxy type, urethane type or the like is xylene. , Dissolved in an organic solvent such as toluene.

【0013】JISA6021(屋根防水用塗膜材)とは、ウレ
タンゴム系1類及び2類、アクリルゴム系、クロロプレ
ンゴム系、アクリル樹脂系、ゴムアスファルト系などが
ある。ウレタンゴム系1類及び2類とは、NCO基を持っ
た化合物を主な原料とする主剤と、架橋剤、充填剤など
を主な成分とする硬化剤とよりなる2成分系ウレタンゴ
ム系防水材で、その品質で1類と2類に区別している。
JIS A6021 (roof waterproof coating material) includes urethane rubber type 1 and type 2, acrylic rubber type, chloroprene rubber type, acrylic resin type, rubber asphalt type and the like. Urethane rubber type 1 and 2 are two-component urethane rubber type waterproof consisting of a main agent whose main raw material is a compound having an NCO group and a curing agent whose main components are a crosslinking agent and a filler. The material is classified into the 1st class and the 2nd class according to its quality.

【0014】ここで、JISA6021のアクリルゴム系とは、
アクリル酸アルキルエステルを主な原料とする非加硫ア
クリルゴムに充填材などを配合したアクリルゴムEm系組
成物である。アクリル樹脂系とはアクリル酸エステル、
メタクリル酸エステルを主な原料とする組成物である。
ゴムアスファルト系とはアスファルトとスチレン・ブタ
ジェンあるいはクロロプレンゴム等のゴム材を主な成分
とするゴムアスファルトEm組成物である。クロロプレン
ゴム系とは、クロロプレンを主な原料とし、充填剤など
を配合したクロロプレンゴム溶液系防水剤である。ゴム
アスファルト系とは、アスファルトとゴムを主な成分と
するゴムアスファルトエマルジョン系防水剤である。
Here, the JIS A6021 acrylic rubber type is
This is an acrylic rubber Em-based composition in which a filler and the like are mixed with non-vulcanized acrylic rubber whose main material is alkyl acrylate. Acrylic resin system means acrylic acid ester,
It is a composition containing methacrylic acid ester as a main raw material.
The rubber asphalt type is a rubber asphalt Em composition containing asphalt and a rubber material such as styrene / butadiene or chloroprene rubber as main components. The chloroprene rubber-based is a chloroprene rubber solution-based waterproofing agent containing chloroprene as a main raw material and a filler and the like. Rubber asphalt-based is a rubber asphalt emulsion-based waterproofing agent containing asphalt and rubber as main components.

【0015】本発明で使用する塗膜型樹脂組成物で好ま
しく使用されるのは、基体の亀裂追従性等を考慮した場
合、JISA6021の各製品、JISA6910の伸張型合成樹脂Em系
複層塗材等である。これら各種塗膜型樹脂組成物には、
樹脂のほかに必要により骨材、粘度安定剤、ノニオン性
界面活性剤、消泡剤、凍結防止剤、分散剤、湿潤剤、防
腐剤、pH調整剤、増粘剤、造膜助剤、各種充填剤、顔
料、セメント、繊維質材料等の一部又は全部を配合して
も良い。充填剤、セメント等の粉体を混入した場合、引
張伸び率が小さくなる。伸び率が30%未満になった場
合、亀裂追従性が著しく悪くなる。好ましい引張り伸び
率は50%以上、さらに好ましくは100%以上である。
The coating film type resin composition used in the present invention is preferably used in consideration of the crack followability of the substrate and the like, each product of JIS A6021 and the stretch type synthetic resin Em-based multi-layer coating material of JIS A6910. Etc. These various coating film type resin compositions include
In addition to resins, aggregates, viscosity stabilizers, nonionic surfactants, defoamers, antifreeze agents, dispersants, wetting agents, preservatives, pH adjusters, thickeners, film-forming aids, and various other resins You may mix | blend some or all of a filler, a pigment, cement, a fibrous material, etc. When powder such as filler or cement is mixed, the tensile elongation becomes small. When the elongation rate is less than 30%, the crack followability is significantly deteriorated. The tensile elongation is preferably 50% or more, more preferably 100% or more.

【0016】また、シート状体からなる高分子組成物層
(D)とは、次のようなものである。すなわち、JISA600
8、JISA6009に限定されている合成高分子ルーフィング
材、基布その他を積層した合成高分子ルーフィング材等
である。
Further, a polymer composition layer comprising a sheet-like body
(D) is as follows. That is, JISA600
8. Synthetic polymer roofing materials limited to JIS A6009, synthetic polymer roofing materials laminated with a base cloth and the like.

【0017】これらのルーフィング材には、エチレン
プロピレンゴム、ブチルゴムなどの加硫ゴム系ルーフィ
ング、塩化ビニル共重合体などの塩化ビニル樹脂系ルー
フィング、エチレン酢酸ビニル共重合樹脂系ルーフィン
グ等があるこれらの各材料その他を積層したものがJISA
6009品である。
These roofing materials include vulcanized rubber-based roofing such as ethylene propylene rubber and butyl rubber, vinyl chloride resin-based roofing such as vinyl chloride copolymer, and ethylene-vinyl acetate copolymer resin-based roofing. JISA is a stack of materials and others.
It is 6009 items.

【0018】本発明の必要により用いられる繊維強化熱
硬化樹脂層用接着剤層(C)とは、液状で塗布できる形
態の接着剤により塗布形成されるものである。その種類
としては、ウレタン系、エポキシ系、ビニルエステル
系、不飽和ポリエステル系、アクリル系等がある。現場
施工であることを考慮した場合、水分と反応するイソシ
アネート基を有するウレタン系接着剤が好ましい。イソ
シアネート基を有するウレタン系接着剤とは、ポリイソ
シアネートとポリオールを反応させて得られる末端にイ
ソシアネート(NCO)基を有するウレタンプレポリマー
からなる湿気硬化型接着剤である。
The adhesive layer (C) for the fiber-reinforced thermosetting resin layer, which is optionally used in the present invention, is formed by applying an adhesive in a liquid form. The types thereof include urethane type, epoxy type, vinyl ester type, unsaturated polyester type, acrylic type and the like. Considering that it is applied on site, urethane adhesives having isocyanate groups that react with water are preferable. The urethane-based adhesive having an isocyanate group is a moisture-curable adhesive made of a urethane prepolymer having an isocyanate (NCO) group at the terminal, which is obtained by reacting a polyisocyanate and a polyol.

【0019】これらのイソシアネート及びポリオールの
両成分は分子末端がイソシアネートになるような割合
で、公知慣用のウレタン化反応を通してウレタンプレポ
リマーとされる。次いで、このウレタンプレポリマーは
希釈可能な溶剤で希釈されて、樹脂分10〜70重量%、好
ましくは15〜50重量%の樹脂溶液が調整される。
Both of these isocyanate and polyol components are made into a urethane prepolymer through a known and conventional urethane-forming reaction in such a proportion that the molecular ends become isocyanate. Next, the urethane prepolymer is diluted with a dilutable solvent to prepare a resin solution having a resin content of 10 to 70% by weight, preferably 15 to 50% by weight.

【0020】この希釈溶剤として代表的なものは、トル
エン、キシレン、酢酸エチル、メチルエチルケトン又は
セロソルブアセテートなどのごときイソシアネートとは
反応しないものであり、これらは単独で、あるいは混合
されて、ウレタン化反応の初期からポリオール成分と有
機イソシアネート成分と共に用いられる。
Typical diluting solvents are those which do not react with isocyanates such as toluene, xylene, ethyl acetate, methyl ethyl ketone or cellosolve acetate, and these are used alone or in a mixture to react with each other in the urethanization reaction. Used from the beginning with the polyol component and the organic isocyanate component.

【0021】上記末端イソシアネート基を有するプレポ
リマーは、必要に応じてセメント類、体質顔料、着色
剤、増粘剤、レベリング剤、消泡剤等の各種添加剤を配
合して接着剤とされる。 接着剤とした後、ハケ、ロー
ラーバケ等を用いた手による塗装が通常行われるが、機
械によるスプレー吹きつ塗装で可能であり、このように
して形成された塗膜は空気中の水分ですみやかに硬化す
る。
The above-mentioned prepolymer having an isocyanate group is used as an adhesive by blending various additives such as cements, extender pigments, colorants, thickeners, leveling agents and defoaming agents, if necessary. . After being used as an adhesive, it is usually painted by hand using a brush, roller brush, etc., but it can be spray-painted by a machine, and the coating film formed in this way can be quickly washed with water in the air. Hardens.

【0022】上記は(D)層 に(C)層を設ける場合で
あったが、特開昭57ー94056号公報に記載されたものに代
表されるような希釈性溶剤分の非常に少ない一液湿気硬
化型ウレタン塗料と称せられるものを用いれば、その塗
布層はJIS A6021 屋根塗膜用防水材適合する材料とな
り、膜厚を厚く保持することができるので、この塗布層
により(D)層と(C)層を兼用させることもでき、
(C)層を設けなくとも(B)層との接着を強固にするこ
とができる。
The above is the case where the layer (C) is provided on the layer (D), but a very small amount of diluting solvent such as that described in JP-A-57-94056 is used. If you use what is called a liquid moisture-curable urethane paint, the coating layer will be a material compatible with JIS A6021 waterproof material for roof coatings, and you can keep the film thickness thick, so this coating layer (D) layer And (C) layer can be combined,
Even if the (C) layer is not provided, the adhesion with the (B) layer can be strengthened.

【0023】本発明における繊維強化熱硬化樹脂層
(B)に用いられる熱硬化性樹脂としては、不飽和ポリ
エステル樹脂、ビニルエステル樹脂、エポキシ樹脂、フ
ェノール樹脂等であり、好ましくは不飽和ポリマーエス
テル樹脂、ビニルエステル樹脂である。
The thermosetting resin used in the fiber-reinforced thermosetting resin layer (B) in the present invention is an unsaturated polyester resin, vinyl ester resin, epoxy resin, phenol resin or the like, preferably unsaturated polymer ester resin. , Vinyl ester resin.

【0024】不飽和ポリエステル樹脂としては、α,βー
不飽和二塩基酸叉はその酸無水物と、芳香族飽和二塩基
酸叉はその酸無水物と、グリコール類の重縮合によって
製造され、場合によっては酸成分として脂肪族或いは脂
環族飽和二塩基酸を併用して製造された不飽和ポリエス
テル30〜80 重量部を、α,βー不飽和単量体70〜20重量
部に溶解して得られるものが挙げられる。また、ビニル
エステル樹脂とは、不飽和ポリエステルの末端をビニル
変性したもの、及びエポキシ樹脂骨格の末端をビニル変
性したものである。これらは、必要により増粘剤、充填
剤、硬化触媒、硬化促進剤、低収縮化剤等を添加する
が、特に硬化触媒、硬化促進剤の添加は有用である。
The unsaturated polyester resin is produced by polycondensation of an α, β-unsaturated dibasic acid or acid anhydride thereof, an aromatic saturated dibasic acid or acid anhydride thereof, and a glycol. In some cases, 30 to 80 parts by weight of an unsaturated polyester produced by using an aliphatic or alicyclic saturated dibasic acid together as an acid component is dissolved in 70 to 20 parts by weight of an α, β-unsaturated monomer. It can be obtained by. The vinyl ester resin is a resin obtained by vinyl-modifying the end of an unsaturated polyester and a resin obtained by vinyl-modifying the end of an epoxy resin skeleton. If necessary, a thickener, a filler, a curing catalyst, a curing accelerator, a low-contracting agent and the like are added to these, and it is particularly useful to add the curing catalyst and the curing accelerator.

【0025】着色剤としては、従来公知の有機及び無機
の染料、顔料がいずれも使用できるが、なかでも耐熱
性、透明性に優れ、かつ不飽和ポリエステル等の硬化を
著しく妨害することのないものが好ましく用いられる。
As the colorant, conventionally known organic and inorganic dyes and pigments can be used, but among them, those having excellent heat resistance and transparency and which do not significantly interfere with the curing of unsaturated polyester and the like. Is preferably used.

【0026】本発明で用いる繊維強化材とは、例えば、
ガラス繊維、アミド、アラヒド、ビニロン、ポリエステ
ル、フェノール等の有機繊維、カーボン繊維、金属繊
維、セラミック繊維あるいはそれらの組合わせである。
施工性、経済性を考慮した場合、好ましいのはガラス繊
維、有機繊維である。繊維の形態は、平織り、朱子織
り、マット状等があるが、施工性、厚み保持等よりマッ
ト状が好ましい。またガラスロービングを 20〜100 mm
にカットして、チョップドストランドにして使用するこ
とも可能である。
The fiber reinforcement used in the present invention is, for example,
They are glass fibers, organic fibers such as amide, arahede, vinylon, polyester and phenol, carbon fibers, metal fibers, ceramic fibers or a combination thereof.
Considering workability and economy, glass fiber and organic fiber are preferable. The fibers may be in the form of plain weave, satin weave, matte or the like, but matte is preferred in view of workability and thickness retention. In addition, glass roving 20 ~ 100 mm
It is also possible to use it by cutting it into chopped strands.

【0027】充填剤としては、炭酸カルシウム粉、クレ
ー、アルミナ粉、硅石粉、タルク、硫酸バリウム、シリ
カパウダー、ガラス粉、ガラスビーズ、マイカ、水酸化
アルミニウム、セルロース系、硅砂、川砂、寒水石、大
理石屑、砕石などの公知のものが挙げられ、なかでも硬
化時半透明性を与えるのでガラス粉、水酸化アルミニウ
ム、硫酸バリウムなどが好ましい。
As the filler, calcium carbonate powder, clay, alumina powder, silica powder, talc, barium sulfate, silica powder, glass powder, glass beads, mica, aluminum hydroxide, cellulosic, silica sand, river sand, cold water stone, Known materials such as marble dust and crushed stone are mentioned, and among them, glass powder, aluminum hydroxide, barium sulfate and the like are preferable because they give semitransparency upon curing.

【0028】硬化触媒としては、不飽和ポリエステル樹
脂、ビニルエステル樹脂等に作用するもので、例えば、
アゾイソブチロニトリルのようなアゾ化合物、ターシャ
リーブチルパーベンゾエート、ターシャリーパーオクト
エート、ベンゾイルパーオキサイド、メチルエチルケト
ンパーオキサイド、ジクミルパーオキサイド等の有機過
酸化物等を挙げることができ、不飽和ポリエステル樹脂
100 重量部に対して通常0.3〜3 重量部の範囲で用いる
ことができる。
The curing catalyst acts on unsaturated polyester resin, vinyl ester resin, etc.
Azo compounds such as azoisobutyronitrile, tertiary butyl perbenzoate, tertiary per octoate, benzoyl peroxide, methyl ethyl ketone peroxide, organic peroxides such as dicumyl peroxide, and the like, unsaturated polyester resin
Usually, it can be used in the range of 0.3 to 3 parts by weight with respect to 100 parts by weight.

【0029】硬化促進剤としては、有機酸の金属塩類特
にコバルト塩、例えばナフテン酸コバルト、オクチル酸
コバルト、アセチルアセトンコバルト等が使用される。
As the curing accelerator, metal salts of organic acids, especially cobalt salts such as cobalt naphthenate, cobalt octylate, and acetylacetone cobalt are used.

【0030】本発明の構造体を施工するには、基体
(E)上に柔軟性のある引張り伸び率が30%以上の高分
子組成物層(D)を形成させるが、上述した JISA 6021
やJISA 6910 の塗膜型の場合は、その液状組成物を金ゴ
テやスプレー等の装置を用いて施工する。また、JISA 6
008 やJISA 6009 に代表されるシート状体を使用する場
合は、各種接着剤を用いて基体(A)に張り付ける。
To apply the structure of the present invention, a flexible polymer composition layer (D) having a tensile elongation of 30% or more is formed on a substrate (E).
In the case of the JIS A 6910 coating type, the liquid composition is applied using a device such as a gold iron or spray. Also, JIS A 6
When a sheet-shaped body represented by 008 or JIS A 6009 is used, it is attached to the base (A) using various adhesives.

【0031】次に(D)層が、塗膜型の場合は硬化させ
た後、また、シート状体の場合はそのまま、例えばNCO
基を有する接着剤を上記した如く金ゴテ等で塗布し、繊
維強化熱硬化樹脂層用接着剤層(C)を形成する。この
ようにすると、(D)層に混入した水分あるいは付着し
た空気中の水分によりNCO 基が反応して接着剤層の接着
性が向上する。
Next, when the layer (D) is a coating type, it is cured, and when it is a sheet, it is left as it is, for example, NCO.
The adhesive having a base is applied with a gold soldering iron or the like as described above to form the adhesive layer (C) for the fiber-reinforced thermosetting resin layer. By doing so, the NCO group reacts with the water mixed in the (D) layer or the water in the attached air to improve the adhesiveness of the adhesive layer.

【0032】(B)層の施工は、繊維強化熱硬化樹脂層用
接着剤層(C)上に上記熱硬化性樹脂の層を塗布してそ
の上に上記繊維強化材をのせるか、この繊維強化材を繊
維強化熱硬化樹脂層用接着剤層層(C)上にのせて熱硬
化性樹脂を含浸させ、硬化させて繊維強化熱硬化樹脂層
(B)を形成する。また、このような作業を軽減するた
め、SMC,BMC 等の既に上記熱硬化性樹脂を上記繊維強化
材に含浸させた成形材料(プリプレグ)を用いても良
い。
The construction of the layer (B) is carried out by applying the layer of the thermosetting resin on the adhesive layer (C) for the fiber-reinforced thermosetting resin layer and then placing the fiber reinforcing material on the layer. A fiber reinforced material is placed on the adhesive layer layer (C) for the fiber reinforced thermosetting resin layer, impregnated with the thermosetting resin, and cured to form the fiber reinforced thermosetting resin layer (B). Further, in order to reduce such work, a molding material (prepreg) such as SMC, BMC or the like in which the above-mentioned thermosetting resin has been impregnated in the above-mentioned fiber reinforced material may be used.

【0033】本発明の表面舗装層(A)は、好ましくは
滑り止め樹脂/骨材もしくはセメントモルタル/骨材か
らなるもので、その厚みは、好ましくは1〜30mm、特
に好ましくは3〜15mmである。樹脂/骨材とは、充填
材と樹脂との混合物に骨材を添加したものであり、好ま
しくは樹脂100重量部に対して骨材を200〜900
重量部、特に好ましくは300〜500重量部添加した
ものである。
The surface pavement layer (A) of the present invention is preferably composed of a non-slip resin / aggregate or cement mortar / aggregate, and its thickness is preferably 1 to 30 mm, particularly preferably 3 to 15 mm. is there. The resin / aggregate is a mixture of a filler and a resin to which the aggregate is added, and preferably 200 to 900 of the aggregate is added to 100 parts by weight of the resin.
Parts by weight, particularly preferably 300 to 500 parts by weight are added.

【0034】この樹脂としては、塗料、床材、防水材、
舗装材等の土木建築用に使用されている樹脂でヤング率
の大きい樹脂、すなわち硬くて伸びの小さい樹脂が好ま
しく、例えば、エポキシ系樹脂、アクリル系樹脂、ビニ
ルエステル樹脂、ウレタン系樹脂、不飽和ポリエステル
樹脂等が使用される。更に車の発進、停止などによるせ
ん断負荷に対し十分に耐えるためには、樹脂と骨材の接
着力が大きいことが重要な要件で、それにはヤング率の
大きい樹脂、すなわち硬くて伸びの小さい樹脂であるこ
とは重要である。
As this resin, paint, floor material, waterproof material,
Among the resins used for civil engineering and construction such as pavement materials, those with a large Young's modulus, that is, resins that are hard and have a small elongation, are preferable.For example, epoxy resins, acrylic resins, vinyl ester resins, urethane resins, unsaturated resins. Polyester resin or the like is used. Furthermore, in order to sufficiently withstand the shear load due to starting and stopping of the car, it is an important requirement that the adhesive strength between the resin and the aggregate is large. Is important.

【0035】セメントモルタル/骨材とは、水分散系樹
脂、ラテックス、エマルジョンに対して、セメントを混
合したものであり、その混合比は好ましくはセメント1
00重量部に対して水40〜70重量部からなり、樹脂
が固形分で5〜30重量部である。この場合の骨材の添
加量は、セメント100重量部に対し200〜900重
量部、特に好ましくは300〜500重量部である。こ
の樹脂としては、ポリマセメント用と称される樹脂であ
れば、例えば、エポキシ系樹脂、アクリル系樹脂、ビニ
ルエステル樹脂、ウレタン系樹脂、ポリエステル系樹
脂、SBR、NBR、エチレン・酢酸ビニル樹脂等が使
用される。
Cement mortar / aggregate is a mixture of water-dispersed resin, latex and emulsion with cement, and the mixing ratio is preferably cement 1.
It is composed of 40 to 70 parts by weight of water with respect to 00 parts by weight, and the resin is 5 to 30 parts by weight in solid content. In this case, the amount of aggregate added is 200 to 900 parts by weight, and particularly preferably 300 to 500 parts by weight, based on 100 parts by weight of cement. As this resin, if it is a resin called for polymer cement, for example, epoxy resin, acrylic resin, vinyl ester resin, urethane resin, polyester resin, SBR, NBR, ethylene-vinyl acetate resin, etc. used.

【0036】本発明の表面舗装層(A)用の滑り止め用
骨材の使用方法には、一般に骨材その他の充填材と混合
して混合材料としてから散布、または塗布して使う場合
と、骨材を塗布した樹脂の上から散布するニ−ト工法の
場合とがあるが、本発明ではどちらでも良い。
The anti-slip aggregate for the surface pavement layer (A) of the present invention is generally used by mixing it with an aggregate or other filler and then spraying or applying it. There is a case of a nit construction method in which the resin is applied with an aggregate and the spray is applied on the resin.

【0037】本発明で使用される骨材とは、例えばシリ
カを主成分とする砂、砂利、砕石その他これに類似する
材料をいう。粒径の大きさが5mmふるいを重量で85%
以上通過する細粒の細粒材と5mmふるいに重量で85%
以上とどまる粗粒の粗粒材があり両者を単独で使用する
場合が多い、滑り止め舗装層として使う場合は該細粒が
好ましい。
The aggregate used in the present invention means, for example, sand, gravel, crushed stone or the like having silica as a main component and similar materials. 85% by weight of particle size 5 mm sieve
85% by weight of fine-grained material and 5mm sieve that pass through above
There are many coarse-grained materials that remain as described above, and both are often used alone. When used as a non-slip pavement layer, the fine-grained materials are preferable.

【0038】またニ−ト工法の場合には、摩耗性に優れ
る高硬度のエメリ−や硅砂が好ましく、その粒子径も滑
り止め効果を発揮させるには4号硅砂以上が好ましい。
骨材には天然骨材と、人工骨材がある。前者として川砂
利、川砂、山砂利、 山砂、海砂利、 海砂がある。後者
は、岩石、粘土、産業副産物等を原料としこれを加工し
たものであって、砕石、砕砂、硅砂、スラグ砕石・砕
砂、人工軽量等がある。また骨材の一部に充填材として
用いられる微粉末を併用しても良い。
In the case of the nit construction method, high hardness emery and silica sand which are excellent in abrasion resistance are preferable, and the particle size thereof is preferably No. 4 silica sand or more in order to exert the anti-slip effect.
Aggregates include natural aggregates and artificial aggregates. The former includes river gravel, river sand, mountain gravel, mountain sand, sea gravel, and sea sand. The latter is obtained by processing rock, clay, industrial by-products, etc. as raw materials, and includes crushed stone, crushed sand, silica sand, crushed slag stone / crushed sand, artificial light weight, and the like. Fine powder used as a filler may be used in combination with a part of the aggregate.

【0039】充填材としては、炭酸カルシウム粉、クレ
ー、アルミナ粉、硅石粉、タルク、硫酸バリウム、シリ
カパウダー、ガラス粉、ガラスビーズ、マイカ、水酸化
アルミニウム、セルロース糸、硅砂、川砂、寒水石、大
理石屑、砕石など公知のものが挙げられ、炭酸カルシウ
ム、ガラス粉、水酸化アルミニウム、硫酸バリウムなど
が好ましい。
As the filler, calcium carbonate powder, clay, alumina powder, silica powder, talc, barium sulfate, silica powder, glass powder, glass beads, mica, aluminum hydroxide, cellulose thread, silica sand, river sand, cold water stone, Known materials such as marble dust and crushed stone can be mentioned, and calcium carbonate, glass powder, aluminum hydroxide, barium sulfate and the like are preferable.

【0040】本発明の他の効果は、基体の亀裂に対する
被覆層の亀裂追従性能の向上にある。実用上被覆層の亀
裂現象が発生するのは、従来の屋上防水施工方法では、
アスファルト防水層の上に抑えモルタルを打設している
場合が多い。一般にこの仕様は、アスファルト防水層の
上に幅約3000×長さ3000×厚さ60mmの押えモルタルを打
設し、約30mm幅の伸縮目地を設けている。
Another effect of the present invention is to improve the crack-following performance of the coating layer against the cracks in the substrate. In practical use, the crack phenomenon of the coating layer occurs in the conventional roof waterproofing method,
In many cases, mortar is placed on top of the asphalt waterproof layer. Generally, in this specification, a press mortar with a width of about 3000 x a length of 3000 x a thickness of 60 mm is placed on the asphalt waterproof layer, and an expansion joint of about 30 mm width is provided.

【0041】こうした構造体の漏水を補修する場合、押
さえモルタルの上から直接新しい防水層を設ける。その
ため、この伸縮目地が温度変化、建物の振動等で動くと
き、押えモルタル上の新設防水層に応力が伝播し、防水
層が負荷を受ける。この負荷が大きかったり、小さくて
も繰り返し回数が多い場合には、補修防水層の破断につ
ながる。本発明の構造体は、こうした既設の防水層上に
も設けることができることは言うまでもない。
When repairing water leakage of such a structure, a new waterproof layer is provided directly on the pressing mortar. Therefore, when the expansion joint moves due to temperature change, building vibration, etc., stress propagates to the new waterproof layer on the presser mortar, and the waterproof layer receives a load. If this load is large, or if it is small and the number of repetitions is large, the repair waterproof layer will be broken. It goes without saying that the structure of the present invention can be provided on such an existing waterproof layer.

【0042】一般に既設の防水層では、この問題を解決
する手法として、目地部では絶縁工法と呼ばれる、目地
部で人工地盤と防水層が密着されていない方法を採用す
る場合が多い。当然のことながら、この絶縁工法も本発
明の構造体及び施工法に採用され含まれる。
In general, in the existing waterproof layer, as a method for solving this problem, a method called an insulating method at the joint, in which the artificial ground and the waterproof layer are not in close contact at the joint, is often adopted. As a matter of course, this insulating method is also adopted and included in the structure and construction method of the present invention.

【0043】このようにして得られる駐車場構造体を土
木建築物に用いれば、多くの駐車場を提供するだけでな
く、建築物の防水構造体を提供することができ、その場
合亀裂追従性等に優れるので、地震等により基体に亀裂
が発生してもこれを覆い、漏水を防止することができ
る。
If the parking lot structure thus obtained is used in a civil engineering building, not only a large number of parking lots can be provided but also a waterproof structure of the building can be provided. Since it is excellent in, for example, even if a crack is generated in the substrate due to an earthquake or the like, it can be covered to prevent water leakage.

【0044】[0044]

【実施例】以下に、本発明を実施例と比較例で詳細に説
明するが、文中「部」、「%」は特に断わりのない限り
重量基準である。
EXAMPLES The present invention will be described in detail below with reference to examples and comparative examples. In the text, "part" and "%" are based on weight unless otherwise specified.

【0045】(実施例1〜10、比較例1〜2) <試験体作成方法> 1.樹脂モルタル(m)の舗装表面層:配合組成 樹脂−−−100部、5号珪砂−−−200部、3号珪
砂−−−100部 2.ニート工法(n)の舗装表面層:厚み11mmスレー
ト板上に2mmの樹脂塗膜を作成、その上にエメリーを6
Kg/m2散布して試験体を作成した。 3.PC・M: ポリマーセメントモルタル舗装表面層 セメント−−−100部 5号珪砂−−−300部 3号珪砂−−−200部 CF−550−−−10(エ
マルジョン樹脂)部 水−−− 45部(*W(水)/C(セメント)=4
0) これらを表面舗装層としてJISA−1451建築材料および建
築構成部分の摩耗性試験及びJISA−5705ビニル
床試験に準拠に基づいてJISK2238マシン油での
耐油性試験を行い表1、表2に結果を示した。
(Examples 1 to 10 and Comparative Examples 1 and 2) <Method for preparing specimen> 1. Pavement surface layer of resin mortar (m): Compound composition resin --- 100 parts, No. 5 silica sand --- 200 parts, No. 3 silica sand --- 100 parts 2. Neat construction method (n) pavement surface layer: 11 mm thick A 2 mm resin coating film is made on a slate plate, and 6 emery layers are formed on it.
A test body was prepared by spraying Kg / m 2 . 3. PC / M: Polymer cement mortar pavement surface layer cement --- 100 parts No. 5 silica sand --- 300 parts No. 3 silica sand --- 200 parts CF-550--10 (emulsion resin) part Water --- 45 parts (* W (water) / C (cement) = 4
0) Using these as the surface pavement layer, an abrasion resistance test of JIS A-1451 building materials and building components and a JIS K-5705 vinyl floor test based on JIS K2238 machine oil oil resistance test was performed, and the results are shown in Tables 1 and 2. showed that.

【0046】[0046]

【表1】 表中の略号は以下の通りである。 EP:エポキシ樹脂,UPE:不飽和ポリエステル樹
脂、AS:アクリルシラップ樹脂,VE:ビニルエステ
ル樹脂、PC:ポリマーセメントモルタル、AsB:ア
スファルト・ブロック、AsC:アスファルト・コンク
リート
[Table 1] The abbreviations in the table are as follows. EP: Epoxy resin, UPE: Unsaturated polyester resin, AS: Acrylic syrup resin, VE: Vinyl ester resin, PC: Polymer cement mortar, AsB: Asphalt block, AsC: Asphalt concrete

【0047】[0047]

【表2】 [Table 2]

【0048】実施例10 既設の鉄骨鉄筋コンクリート造り屋上800m2に本発
明の駐車場構造体を既設防水層の熱アスファルト防水/
厚み5cmの押さえコンクリートを基体としその上に次の
ような仕様で施工した。
Example 10 A parking lot structure of the present invention is provided on an existing steel-framed reinforced concrete rooftop 800 m 2 in which the existing waterproof layer is hot asphalt waterproof /
A 5 cm thick pressed concrete was used as the base material, and the following specifications were applied.

【0049】(D)層として伸び450%の藤倉化成
(株)のアクリルゴムエマルジョンを2mm塗布硬化乾燥
後、(C)層として繊維強化熱硬化性樹脂層用接着剤層
としての1液湿気硬化型ウレタン(プライマー PD、
大日本インキ化学工業(株))を0.2kg/m2塗布。硬
化乾燥後、(B)層として繊維強化熱硬化性樹脂層を施
工した。繊維としてガラスマット#450g/m2を1プ
ライ、熱硬化性樹脂としての不飽和ポリエステル樹脂
(大日本インキ化学工業(株)、ポリライトFR−20
0)をガラス含有率約25%になるよう積層した。次に
(A)層の表面舗装層を樹脂/骨材として、エポキシ樹
脂(エホ゜ニッケEC850、日本ケミカル建設(株))と4号珪砂と
を15/85の比率で樹脂モルタルをつくり、5mm厚み
の滑り止め表面舗装層(樹脂/骨材)を施工した。施工
2年経過後、耐摩耗性、耐油性、強度、防水性、施工性
に優れる土木建築物の駐車場として問題なく使用されて
いる。
An acrylic rubber emulsion of Fujikura Kasei Co., Ltd. having an elongation of 450% is applied as a layer (D) to a thickness of 2 mm, followed by curing and drying, and then as a layer (C), a one-part moisture curing as an adhesive layer for a fiber-reinforced thermosetting resin layer. Type urethane (primer PD,
Apply 0.2 kg / m 2 of Dainippon Ink and Chemicals Co., Ltd. After curing and drying, a fiber-reinforced thermosetting resin layer was applied as the (B) layer. 1 ply of glass mat # 450g / m 2 as fiber, unsaturated polyester resin as thermosetting resin
(Dainippon Ink and Chemicals, Inc., Polylite FR-20
0) was laminated so that the glass content was about 25%. Next, using the surface pavement layer of layer (A) as a resin / aggregate, an epoxy resin (Eponikke EC850, Nippon Chemical Construction Co., Ltd.) and No. 4 silica sand were made into a resin mortar with a ratio of 15/85, and a thickness of 5 mm was obtained. A non-slip surface pavement layer (resin / aggregate) was applied. After two years of construction, it has been used without problems as a parking lot for civil engineering buildings that has excellent wear resistance, oil resistance, strength, waterproofness, and workability.

【0050】実施例11 既設の鉄骨鉄筋コンクリート造り屋上400m2に本発明
の駐車場構造体を既設防水層の熱アスファルト防水/厚
み5cmの押さえ密粒アスファルトコンクリート(13)
を基体(E)とし、その上に次のような仕様で施工し
た。
Example 11 The existing parking structure of the present invention is installed on 400 m 2 of the roof of an existing steel-framed reinforced concrete structure. The existing waterproof layer is hot asphalt waterproof / 5 cm thick pressed dense asphalt concrete (13).
Was used as a base material (E), and the following specifications were applied on it.

【0051】(D)層に伸び600%の1液硬化型ウレ
タン(大日本インキ化学工業(株)の商品名フラットー
1)を2mm厚みで塗布し、硬化、乾燥後、(C)層の繊
維強化熱硬化性樹脂層用接着剤層として1液湿気硬化型
ウレタン(大日本インキ化学工業(株)、プライマーP
D)を0.2kg/m2塗布し、硬化、乾燥後(B)層に繊
維強化熱硬化性樹脂層を施工した。繊維としてガラスマ
ット#450g/m2を1プライ、熱硬化性樹脂として
の不飽和ポリエステル樹脂(大日本インキ化学工業
(株)ポリライトFR−200)をガラス含有率約25
%になるよう積層した。次に(A)層の滑り止め舗装層
(樹脂/骨材)として、アクリル樹脂(三菱レーヨン
(株)製品、アクリトーンFS-415)を2mmの厚みで塗布し、そ
の上にの骨材(住友金属鉱山(株)商品、エメリー)を
樹脂層が完全に隠ぺいされるまで散布、未付着のエメリ
ーをスイパーで処理した。施工2年経過後、耐摩耗性、
耐油性、強度、防水性、施工性に優れる土木建築物の駐
車場として問題なく使用できることを確認した。
A 1-component curable urethane (trade name: Flat-1 manufactured by Dainippon Ink and Chemicals, Inc.) having a elongation of 600% is applied to the layer (D) in a thickness of 2 mm, cured and dried, and then the fiber of the layer (C) is used. One-component moisture-curable urethane as an adhesive layer for reinforced thermosetting resin layer (Dainippon Ink and Chemicals, Inc., Primer P
D) was applied at 0.2 kg / m 2 , cured and dried, and a fiber-reinforced thermosetting resin layer was applied to the layer (B). One ply of glass mat # 450 g / m 2 as a fiber and an unsaturated polyester resin (Polylite FR-200, Dainippon Ink and Chemicals Co., Ltd.) as a thermosetting resin have a glass content of about 25.
It laminated so that it might become%. Next, as a non-slip pavement layer (resin / aggregate) of layer (A), acrylic resin (Mitsubishi Rayon
Co., Ltd. product, Acritone FS-415) is applied with a thickness of 2 mm, and the aggregate (Sumitomo Metal Mining Co., Ltd. product, Emery) is sprayed on it until the resin layer is completely hidden Emery was treated with a sweeper. After 2 years of construction, wear resistance,
It has been confirmed that it can be used without problems as a parking lot for civil engineering buildings, which has excellent oil resistance, strength, waterproofness, and workability.

【0052】[0052]

【発明の効果】このようにして得られる本発明の構造体
を建築物の屋上、屋内、地下等、建築物と併設される駐
車場に用いれば軽量で強靱な防水構造が得られ、また耐
摩耗性、耐油性、走行性、防水性に優れた駐車場構造体
を得ることが出来る。
When the structure of the present invention thus obtained is used in a parking lot such as a rooftop, indoors, or underground of a building, which is attached to the building, a lightweight and tough waterproof structure can be obtained and the durability can be improved. It is possible to obtain a parking lot structure having excellent wear resistance, oil resistance, running performance, and waterproofness.

【0053】更に本発明の駐車場工法および駐車場構造
体は、新設の建築物のみでなく、既設の古い建築物の施
工物の上からも施工ができリホーム用としても利用出来
る。
Further, the parking lot construction method and the parking lot structure of the present invention can be used not only for new construction but also for construction of existing constructions of old constructions and can be used for rehome.

Claims (5)

【特許請求の範囲】[Claims] 【請求項1】上から (A)表面舗装層、 (B)繊維強化熱硬化性樹脂層、 (C)必要により繊維強化熱硬化性樹脂層用接着剤層、 (D)JISK6301での引張り伸び率が30%以上
の高分子組成物層、 (E)基体 からなる駐車場構造体。
1. From the top, (A) a surface pavement layer, (B) a fiber-reinforced thermosetting resin layer, (C) an adhesive layer for the fiber-reinforced thermosetting resin layer if necessary, and (D) a tensile elongation according to JIS K6301. A parking lot structure comprising a polymer composition layer having a ratio of 30% or more, and (E) a substrate.
【請求項2】(D)層の高分子組成物層が、塗膜型樹脂
組成物である請求項1記載の駐車場構造体。
2. The parking lot structure according to claim 1, wherein the polymer composition layer of the layer (D) is a coating film type resin composition.
【請求項3】(A)の表面舗装層が、樹脂/骨材からな
るであることを特徴とする請求項1記載の駐車場構造
体。
3. The parking lot structure according to claim 1, wherein the surface pavement layer of (A) is made of resin / aggregate.
【請求項4】(A)表面舗装層が、セメントモルタル/
骨材からなることを特徴とする請求項1記載の駐車場構
造体。
4. (A) The surface pavement layer is cement mortar /
The parking lot structure according to claim 1, wherein the parking lot structure is made of an aggregate.
【請求項5】基体(E)上に、JISK6301での引
張り伸び率が30%以上の高分子組成物層(D)、必要
により繊維強化熱硬化性樹脂層用接着剤層(C)、繊維
強化熱硬化性樹脂層(B)及び表面舗装層(A)の順に
を施工することを特徴とする駐車場施工法。
5. A polymer composition layer (D) having a tensile elongation of 30% or more according to JIS K6301 on a substrate (E), an adhesive layer (C) for a fiber-reinforced thermosetting resin layer, and a fiber if necessary. A parking lot construction method characterized by constructing a reinforced thermosetting resin layer (B) and a surface pavement layer (A) in this order.
JP18630191A 1991-07-25 1991-07-25 Parking structure and its construction method Expired - Lifetime JP3163447B2 (en)