JPH05230429A - Primer composition - Google Patents
Primer compositionInfo
- Publication number
- JPH05230429A JPH05230429A JP3531592A JP3531592A JPH05230429A JP H05230429 A JPH05230429 A JP H05230429A JP 3531592 A JP3531592 A JP 3531592A JP 3531592 A JP3531592 A JP 3531592A JP H05230429 A JPH05230429 A JP H05230429A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- adhesive
- primer
- silica powder
- polyester resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ポリエチレンテレフタ
レートの基材シート上に粘着剤を塗布するために使用す
るプライマー組成物に関する。FIELD OF THE INVENTION The present invention relates to a primer composition used for coating an adhesive on a polyethylene terephthalate substrate sheet.
【０００２】[0002]
【従来の技術】化粧シートや防曇シート等、各種の機能
性シ−トは、貼着作業に便利なよう、その裏面に粘着剤
を塗布し離型紙を当てて、粘着シートの形にしたものが
多い。これらの粘着シートに常用されている粘着剤は、
一般に付着力が強すぎて貼り直し作業のときの剥離が難
しく、また剥離後は粘着剤層に曇りが生じたり粘着剤面
に凹凸ができたりするので、とくに防曇シートのような
透明性が要求される用途には使用できないし、貼り直し
を行なう用途には使用しにくかった。2. Description of the Related Art Various functional sheets such as a decorative sheet and an anti-fog sheet are formed into an adhesive sheet by applying an adhesive to the back surface of the sheet and applying release paper so that it is convenient for sticking work. There are many things. The pressure-sensitive adhesives that are commonly used for these pressure-sensitive adhesive sheets are
Generally, adhesion is too strong and peeling is difficult when re-attaching work, and after peeling, the pressure-sensitive adhesive layer may be fogged or the pressure-sensitive adhesive surface may have irregularities. It could not be used for the required application, and it was difficult to use it for re-pasting.
【０００３】施工が容易で透明性を損うことなくシート
を貼着したり剥離したりすることのできる粘着シートを
与える粘着剤として、エチレン−酢酸ビニル共重合体に
塩化ビニルモノマーをグラフト重合した合成樹脂に、可
塑剤および必要な粘着性付与剤を配合したものが知られ
ている（特公昭５１−２８１０２号）。 しかしこの粘
着剤は、プラスチックシート、とくにポリエチレンテレ
フタレートシートとの接着力に乏しいため、貼り着けや
貼り直しの作業のときに、粘着剤層が基材シートから離
れたり、粘着剤の一部が被着体に残ったりすることが経
験された。An ethylene-vinyl acetate copolymer is graft-polymerized with a vinyl chloride monomer as a pressure-sensitive adhesive which gives a pressure-sensitive adhesive sheet which can be easily attached and peeled without impairing transparency. It is known that a synthetic resin is mixed with a plasticizer and a necessary tackifier (Japanese Patent Publication No. 51-28102). However, since this adhesive has poor adhesion to a plastic sheet, especially a polyethylene terephthalate sheet, the adhesive layer may separate from the base sheet or part of the adhesive may be covered during the attaching or re-adhesion work. It was experienced that it remained on the body.
【０００４】この対策として、基材シートの粘着剤を塗
布する面にプライマーを塗布しておくことが考えられる
が、ポリエステルの基材シートと上記粘着剤の両方に対
して良好な接着力をもつプライマーは多くない。 しか
も両者に対して良好な粘着力をもつプライマーは、ブロ
ッキングを起こしやすい。 粘着シートは、まず表面に
化粧を施したり機能性をもたせた基材の裏面にプライマ
ーを塗布し、巻き取って保管する。 粘着剤を離型紙に
塗布して粘着層を形成し、上記のプライマ−を塗布した
基材をその上に積層することによって、粘着シ−トを形
成する。 ところが、基材にプライマ−を塗布後、保管
している間に、基材とプライマ−とが接着するブロッキ
ングが生じるという欠点があった。As a countermeasure against this, it is conceivable to apply a primer to the surface of the base material sheet on which the pressure-sensitive adhesive is applied, but it has a good adhesive force to both the base material sheet of polyester and the pressure-sensitive adhesive. There are not many primers. Moreover, a primer having good adhesiveness to both of them tends to cause blocking. The pressure-sensitive adhesive sheet is prepared by first applying a primer to the back surface of a base material whose surface is given a make-up or having functionality, and is wound up and stored. An adhesive sheet is formed by applying an adhesive to release paper to form an adhesive layer, and laminating the base material coated with the above primer thereon. However, there is a drawback that blocking occurs due to adhesion between the base material and the primer during storage after coating the base material with the primer.
【０００５】プライマーに既知のブロッキング防止剤、
たとえばエチレン−酢酸ビニル共重合体や、それとポリ
塩化ビニルとの混合物を添加すると、接着力が低下して
プライマーとしての機能を維持できない。Anti-blocking agents known for primers,
For example, when an ethylene-vinyl acetate copolymer or a mixture of it and polyvinyl chloride is added, the adhesive force is reduced and the function as a primer cannot be maintained.
【０００６】[0006]
【発明が解決しようとする課題】本発明の目的は、ポリ
エチレンテレフタレートの基材シートと前記のグラフト
重合体からなる粘着剤の層とを、ブロッキングを起こす
ことなく強固に接着させることのできるプライマー組成
物を提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to provide a primer composition capable of firmly adhering a polyethylene terephthalate base sheet and a pressure-sensitive adhesive layer made of the above graft polymer without blocking. To provide things.
【０００７】[0007]
【課題を解決するための手段】本発明のプライマー組成
物は、エチレン−酢酸ビニル共重合体に塩化ビニルモノ
マーをグラフト重合した合成樹脂に可塑剤または可塑剤
および粘着性付与剤を配合した粘着剤を、ポリエチレン
テレフタレートの基材シート上に塗布するためのプライ
マー組成物であって、ガラス転移点が２〜６０℃、軟化
点が８０〜１６５℃、分子量が５，０００〜２５，００
０の範囲、好ましくはガラス転移点が６〜１０℃、軟化
点が１１０〜１１５℃、分子量が１８，０００〜２５，
０００の範囲にあるポリエステル樹脂に、シリカ粉末を
配合してなる。The primer composition of the present invention is a pressure-sensitive adhesive comprising a synthetic resin obtained by graft-polymerizing an ethylene-vinyl acetate copolymer with a vinyl chloride monomer and a plasticizer or a plasticizer and a tackifier. Is a primer composition for coating on a base material sheet of polyethylene terephthalate, having a glass transition point of 2 to 60 ° C., a softening point of 80 to 165 ° C., and a molecular weight of 5,000 to 25,000.
0, preferably a glass transition point of 6 to 10 ° C, a softening point of 110 to 115 ° C, a molecular weight of 18,000 to 25,
A silica resin is blended with a polyester resin in the range of 000.
【０００８】粘着剤の好ましい態様は、エチレンと酢酸
ビニルとのモノマー比率が３０〜６０％：７０：４０％
であるエチレン−酢酸ビニルコポリマーに、塩化ビニル
を、コポリマーとモノマーの比が５０〜７５％：５０〜
２５％となるようにグラフト重合した合成樹脂１００重
量部に、２０〜７５重量部の可塑剤を配合したものであ
る。A preferred embodiment of the pressure-sensitive adhesive has a monomer ratio of ethylene to vinyl acetate of 30 to 60%: 70: 40%.
The ethylene-vinyl acetate copolymer is vinyl chloride, and the copolymer-to-monomer ratio is 50-75%: 50-
20 to 75 parts by weight of a plasticizer is added to 100 parts by weight of a synthetic resin graft-polymerized to 25%.
【０００９】可塑剤は、ポリ塩化ビニル用の可塑剤と同
様のものでよく、たとえば、フタル酸エステル系、脂肪
族二塩基酸エステル系、無機酸エステル系、ポリエステ
ル系、エポキシ系の可塑剤を用いる。The plasticizer may be the same as the plasticizer for polyvinyl chloride. For example, a phthalic acid ester-based, aliphatic dibasic acid ester-based, inorganic acid ester-based, polyester-based or epoxy-based plasticizer may be used. To use.
【００１０】必要に応じて添加する粘着性の付与材の例
は、ロジンまたは変性ロジンの誘導体、テルペン変性
体、フェノール系樹脂であり、その添加量は、グラフト
重合樹脂１００重量部あたり５〜１５０重量部が適切で
ある。Examples of tackifiers to be added as necessary are rosin or modified rosin derivatives, terpene modified products, and phenolic resins, and the addition amount thereof is 5 to 150 per 100 parts by weight of the graft polymerization resin. Weight parts are appropriate.
【００１１】基材シートは、適宜のプラスチックシート
またはそれと紙などの積層材に粘着シートの用途に応じ
て、その表面や内部に化粧を施したり、機能性コーティ
ングを施したりしたものである。 化粧の手段は、隠蔽
層の形成（つまりベタ印刷）、絵柄の印刷、金属の蒸
着、エンボスなどがあり、機能性コーティングとは、防
曇、防眩、帯電防止などを目的とするコーティングであ
る。 基材シートに使用するプラスチックは任意であっ
て、その例をあげれば、ポリエチレンテレフタレート、
アクリル樹脂、ポリ塩化ビニルである。 易接着処理を
施せば、フッ素樹脂シートのような接着性の低い材料を
使用することもできる。 易接着処理には、よく知られ
ているようにコロナ放電、プラズマ放電、プライマ−塗
布などの手法があり、処理を施したポリエチレンテレフ
タレ−トのフィルムが市販されている。The base sheet is an appropriate plastic sheet or a laminated material such as paper and the like, which has a surface or the inside thereof provided with a makeup or a functional coating, depending on the use of the adhesive sheet. Means of makeup include formation of a concealing layer (that is, solid printing), printing of patterns, vapor deposition of metal, embossing, etc., and functional coating is a coating for the purpose of antifogging, antiglare, antistatic, etc. .. The plastic used for the base sheet is arbitrary, and examples thereof include polyethylene terephthalate,
Acrylic resin and polyvinyl chloride. A material having low adhesiveness such as a fluororesin sheet can be used if it is subjected to an easy-adhesion treatment. As is well known, the easy adhesion treatment includes corona discharge, plasma discharge, primer coating, and the like, and a treated polyethylene terephthalate film is commercially available.
【００１２】基材シート裏面へのプライマーの塗布はロ
ールコーター、グラビアコーターなどの既知の塗布手段
に従えばよい。 プライマーの塗布量は十分な接着力を
与え、かつブロッキングを防止するという観点から、
０．２〜２．０ｇ／ｍ2（乾燥時）の範囲が好ましい。The primer may be applied to the back surface of the base material sheet by a known coating means such as a roll coater or a gravure coater. The amount of primer applied gives sufficient adhesion, and from the viewpoint of preventing blocking,
The range of 0.2 to 2.0 g / m 2 (dry) is preferable.
【００１３】シリカ粉末の粒径についていえば、粒径が
０．５μｍ以上のものが、取扱いや樹脂への分散が容易
であり、基材シートの透明性を維持する点では１５μｍ
以下のものが好ましい。 粒径が大きいものだけを使用
すると、ブロッキング効果は高いが透明性が劣る。 一
方、粒径の小さいものだけ使用すると、透明性はよいが
ブロッキング防止効果が出ない。 従って、ある程度は
粒径の分布が広いものを配合するほうがよい。 とく
に、粒径が１〜２μｍのものと３〜５μｍのものとを、
樹脂中に、それぞれ０．７〜１．５重量％および０．１
〜０．３重量％の範囲で分散すると、透明性を損うこと
なくブロッキング防止効果が得られて好ましい。With respect to the particle size of the silica powder, particles having a particle size of 0.5 μm or more are easy to handle and disperse in a resin, and in order to maintain the transparency of the base sheet, the particle size is 15 μm.
The following are preferred. If only a large particle size is used, the blocking effect is high but the transparency is poor. On the other hand, when only those having a small particle size are used, the transparency is good but the blocking preventing effect is not obtained. Therefore, it is better to blend a material having a wide particle size distribution to some extent. Especially, those having a particle size of 1 to 2 μm and those having a particle size of 3 to 5 μm are
0.7 to 1.5% by weight and 0.1, respectively, in the resin
When it is dispersed in the range of 0.3 to 0.3% by weight, the antiblocking effect can be obtained without impairing the transparency, which is preferable.
【００１４】[0014]
【作用】本発明において粘着剤に使用するポリエステル
樹脂の物性を前記のように限定した理由は、以下のとお
りである。The reason for limiting the physical properties of the polyester resin used for the pressure-sensitive adhesive in the present invention as described above is as follows.
【００１５】ガラス転移点および軟化点の上限をそれぞ
れ６０℃，１６５℃とし、分子量の下限を５，０００と
したのは、これらの限界を超えるポリエステル樹脂は、
接着力が弱く、プライマーとして使用するには不十分だ
からである。 一方で、ガラス転移点および軟化点の下
限をそれぞれ２℃，８０℃とし、分子量の上限を２５，
０００としたのは、これらの限界を超えるポリエステル
樹脂は、接着力が強すぎて、シリカ粉末を添加してもブ
ロッキングを防止できないからである。The upper limits of the glass transition point and the softening point are set to 60 ° C. and 165 ° C., respectively, and the lower limit of the molecular weight is set to 5,000. For polyester resins exceeding these limits,
This is because the adhesive strength is weak and insufficient for use as a primer. On the other hand, the lower limits of the glass transition point and the softening point are 2 ° C and 80 ° C, respectively, and the upper limit of the molecular weight is 25,
The reason for setting the value to 000 is that polyester resins exceeding these limits have too strong an adhesive force to prevent blocking even if silica powder is added.
【００１６】[0016]
【実施例】下記のポリエステル樹脂およびポリエステル
樹脂とシリカ粉末の混合物を用意した。 このうち、N
o．８〜１１は本発明のプライマー組成物であり、中で
も、No．１０および１１とは好ましい態様である。 N
o．１〜７および１２は比較例である。Example The following polyester resin and a mixture of polyester resin and silica powder were prepared. Of these, N
o. Nos. 8 to 11 are the primer compositions of the present invention. 10 and 11 are preferred embodiments. N
o. 1 to 7 and 12 are comparative examples.
【００１７】 表 １ ポリエステル樹脂 シリカ粉末（重量％） No． ガラス転移点 軟化点 分子量 １〜２ ３〜５ ℃ ℃ μｍ μｍ １ ７０ １１０ ２５，０００ − − ２ ２４ １１０ ５，０００ − − ３ ２ １１５ ２０，０００ − − ４ ６０ １６５ ２０，０００ − − ５ １５ ８０ ２０，０００ − − ６ ７７ １８０ ２０，０００ − − ７ −２０ ９８ ２０，０００ − − ８ ７０ １１０ ２５，０００ ２．０ − ９ ７０ １１０ ２５，０００ − ０．５ １０ ７０ １１０ ２５，０００ ０．５ ０．１ １１ ７０ １１０ ２５，０００ ０．７ ０．１ １２ −２０ ９８ ２０，０００ ０．７ ０．１ 上記の樹脂および混合物をメチルエチルケトンとトルエ
ンとの１：１混合溶剤で、固形分が２０％になるまで希
釈してプライマーとした。Table 1 Polyester resin silica powder (% by weight) No. Glass transition point Softening point Molecular weight 1-2 3-5 ℃ ℃ μm μm 1 70 110 25,000 − − 2 24 110 5,000 − − 3 2 115 20,000 − − 4 60 165 20,000 − − 5 15 80 20,000 − − 6 77 180 20,000 − − 7-20 98 20,000--8 70 70 110 25,000 2.0-9 970 110 25,000-0.5 10 70 110 110 25,000 0.5 0.1 11 11 70 110 25,000 0.7 0.1 12 -20 98 20,000 0.7 0.1 The above resin and mixture were diluted with a 1: 1 mixed solvent of methyl ethyl ketone and toluene until the solid content became 20% to prepare a primer.
【００１８】基材シートとして（タイアホイル製）を用
意し、その上に上記のプライマーをグラビアコートし、
室温で１分間乾燥させて、塗布量が０．５ｇ／ｍ2のプ
ライマー層を設けた。As a base material sheet (made of tire foil) is prepared, on which the above-mentioned primer is gravure coated,
After drying at room temperature for 1 minute, a primer layer having a coating amount of 0.5 g / m 2 was provided.
【００１９】基材シートと同様なＰＥＴシート上に、上
記の各基材シートをプライマー層を挟んで重ね、１kg／
cm2の荷重をかけながら４０℃の温度に１週間置いた後
に、ブロッキングが発生するか否かを観察した。 ブロ
ッキングの生じなかったものを○、シートの一部にブロ
ッキングがみられたものを△、シートの全面にブロッキ
ングが生じていたものを×とした。 結果を表２に示
す。On a PET sheet similar to the base sheet, the above base sheets are superposed with a primer layer in between, and 1 kg /
After placing at a temperature of 40 ° C. for 1 week while applying a load of cm 2 , it was observed whether blocking occurred. The case where blocking did not occur was evaluated as ◯, the case where blocking was observed on a part of the sheet was evaluated as Δ, and the case where blocking was generated on the entire surface of the sheet was evaluated as x. The results are shown in Table 2.
【００２０】別に、エチレン−酢酸ビニルコポリマー６
０％に塩化ビニルモノマー４０％をグラフト重合した樹
脂１００重量部に、フタル酸ジオクチル（可塑剤）を２
５重量部配合し、これをメチルエチルケトンとトルエン
との１：１混合溶剤６００重量部に分散させて粘着剤を
用意した。Separately, ethylene-vinyl acetate copolymer 6
Dioctyl phthalate (plasticizer) was added to 100 parts by weight of a resin obtained by graft-polymerizing 40% of vinyl chloride monomer to 0%.
5 parts by weight were mixed, and this was dispersed in 600 parts by weight of a 1: 1 mixed solvent of methyl ethyl ketone and toluene to prepare an adhesive.
【００２１】厚さ２５μｍの離型紙「セラピールＢＬ−
改」（東洋メタライジング製）上に上記の粘着剤をロー
ルコートし、１００℃の温度で１分間加熱乾燥させて、
厚さ１０μｍの粘着剤層を設けた。A 25 μm-thick release paper "Therapy BL-
"Kai" (manufactured by Toyo Metalizing Co., Ltd.) is roll-coated with the above-mentioned pressure-sensitive adhesive, and dried by heating at a temperature of 100 ° C for 1 minute.
An adhesive layer having a thickness of 10 μm was provided.
【００２２】この離型紙と前記のプライマー処理した基
材シートを、粘着剤層とプライマー層とが接するように
重ねてラミネートした。 得られた１２種の粘着シート
を２５mm幅に切断し、以下の剥離試験によって、プライ
マーと粘着剤との接着性を調べた。This release paper and the above-mentioned primer-treated base sheet were laminated so that the pressure-sensitive adhesive layer and the primer layer were in contact with each other. The obtained 12 kinds of pressure-sensitive adhesive sheets were cut into a width of 25 mm, and the adhesion between the primer and the pressure-sensitive adhesive was examined by the following peel test.
【００２３】試験Ａ それぞれの粘着シートを、離型紙を外してガラス板に貼
着した。 これらのガラス板を室温に２４時間置いた後
に、ガラス板から粘着シートを３００mm/minの速度で１
８０°の角度に剥離した。 Test A Each adhesive sheet was attached to a glass plate with the release paper removed. After placing these glass plates at room temperature for 24 hours, the adhesive sheets were removed from the glass plates at a speed of 300 mm / min for 1 hour.
It was peeled off at an angle of 80 °.
【００２４】試験Ｂ 試験Ａと同様に各粘着シートを貼着したガラス板を用意
し、これを７０℃の温度に７日間置いた後、試験Ａと同
じ条件で粘着シートをガラス板から剥離した。 試験Ｃ 同種の粘着シートを２枚ずつ用意し、粘着面どうしを貼
り合わせた。 これらのシートを室温に１分間置いた後
に、一方の粘着シートを他方の粘着シートから３００mm
/minの速度で９０°の角度に剥離した。[0024]Exam B Prepare a glass plate to which each adhesive sheet is attached, as in Test A
Then, after placing it at a temperature of 70 ° C. for 7 days,
The adhesive sheet was peeled from the glass plate under the same conditions. Test C Prepare two adhesive sheets of the same type and attach the adhesive surfaces together
Got together After placing these sheets at room temperature for 1 minute
In addition, one adhesive sheet is 300mm from the other adhesive sheet.
It was peeled off at an angle of 90 ° at a speed of / min.
【００２５】試験Ｄ 試験Ｃと同じ試験を、剥離速度を３０cm/secに変えて行
なった。 Test D The same test as test C was carried out with the peel rate changed to 30 cm / sec.
【００２６】各試験後に剥離した粘着シートを観察し
て、粘着剤層とプライマー層とが密着していたものを
○、粘着剤層が基材シートから浮き上がっていたものを
△、粘着剤がガラスまたは他の粘着シートに転着したも
のを×とした。Observation of the pressure-sensitive adhesive sheet that had been peeled off after each test revealed that the adhesive layer and the primer layer were in close contact with each other, the adhesive layer was lifted from the substrate sheet, and the adhesive was glass. Alternatively, the one transferred to another adhesive sheet was marked with x.
【００２７】これらの結果を、ブロッキング性の結果と
あわせて表２に示す。These results are shown in Table 2 together with the results of blocking property.
【００２８】 表 ２ No． ブロッキング性 接 着 性 Ａ Ｂ Ｃ Ｄ １ × ○ ○ ○ ○ ２ × ○ ○ ○ ○ ３ × ○ ○ ○ ○ ４ × ○ ○ ○ ○ ５ × ○ ○ ○ ○ ６ × △ × × × ７ × ○ △ × × ８ ○ ○ ○ ○ ○ ９ ○ ○ ○ ○ ○ １０ △ ○ ○ ○ ○ １１ ○ ○ ○ ○ ○ １２ × ○ △ × ×Table 2 No. Blocking adhesive A B C D 1 × ○ ○ ○ ○ 2 × ○ ○ ○ ○ 3 × ○ ○ ○ ○ 4 × ○ ○ ○ ○ 5 × ○ ○ ○ ○ 6 × △ × × × 7 × ○ △ × × 8 ○ ○ ○ ○ ○ 9 ○ ○ ○ ○ ○ 10 △ ○ ○ ○ ○ 11 ○ ○ ○ ○ ○ 12 × ○ △ × ×
【００２９】[0029]
【発明の効果】本発明のプライマー組成物を使用すれ
ば、エチレン−酢酸ビニルコポリマーと塩化ビニルモノ
マーとのグラフト重合物を主成分とする粘着剤を、ポリ
エチレンテレフタレートのシート上に塗布して、両者
を、ブロッキングを起こすことなく強固に接着させるこ
とができる。 本発明の好ましい態様のプライマー組成
物は、シートの透明性がいっそうよく保たれるから、防
曇シートのような透明性が要求される粘着シートにも使
用できる。When the primer composition of the present invention is used, a pressure sensitive adhesive containing a graft polymer of an ethylene-vinyl acetate copolymer and a vinyl chloride monomer as a main component is coated on a polyethylene terephthalate sheet, Can be firmly adhered without causing blocking. The primer composition according to the preferred embodiment of the present invention can be used for an adhesive sheet such as an anti-fog sheet which requires transparency because the transparency of the sheet is further improved.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０８Ｋ 3/36 Ｃ０８Ｌ 67/02 ＫＪＳ 8933−4Ｊ Ｃ０９Ｄ 167/02 ＰＫＷ 8933−4Ｊ Ｃ０９Ｊ 5/02 ＪＧＰ 6770−4Ｊ 167/02 ＪＦＲ 8933−4Ｊ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Internal reference number FI Technical display location C08K 3/36 C08L 67/02 KJS 8933-4J C09D 167/02 PKW 8933-4J C09J 5/02 JGP 6770-4J 167/02 JFR 8933-4J
Claims (2)
ニルモノマーをグラフト重合した合成樹脂に可塑剤また
は可塑剤および粘着性付与剤を配合した粘着剤を、ポリ
エチレンテレフタレートの基材シート上に塗布するため
のプライマー組成物であって、ガラス転移点が２〜６０
℃、軟化点が８０〜１６５℃、分子量が５，０００〜２
５，０００の範囲にあるポリエステル樹脂に、シリカ粉
末を配合してなるプライマー組成物。1. A pressure-sensitive adhesive comprising a synthetic resin obtained by graft-polymerizing an ethylene-vinyl acetate copolymer with a vinyl chloride monomer and a plasticizer or a plasticizer and a tackifier is applied onto a polyethylene terephthalate base sheet. A glass composition having a glass transition point of 2 to 60
℃, softening point 80 ~ 165 ℃, molecular weight 5,000 ~ 2
A primer composition comprising a polyester resin in the range of 5,000 and silica powder.
μｍのシリカを０．７〜１．５重量％、粒径３〜５μｍ
のシリカを０．１〜０．３重量％配合した請求項１のプ
ライマー組成物。2. The polyester resin has a particle size of 1 to 2
0.7 to 1.5% by weight of silica having a particle size of 3 to 5 μm
The primer composition according to claim 1, wherein 0.1 to 0.3% by weight of the silica is blended.