JPH05186750A - Self-adhesive kraft tape - Google Patents
Self-adhesive kraft tapeInfo
- Publication number
- JPH05186750A JPH05186750A JP4003856A JP385692A JPH05186750A JP H05186750 A JPH05186750 A JP H05186750A JP 4003856 A JP4003856 A JP 4003856A JP 385692 A JP385692 A JP 385692A JP H05186750 A JPH05186750 A JP H05186750A
- Authority
- JP
- Japan
- Prior art keywords
- kraft
- sensitive adhesive
- pressure
- water
- adhesive tape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、クラフト粘着テープに
関し、更に詳しくは、段ボール封緘に使用した後、貼付
したままで段ボールの溶解・再生（リサイクル）が可能
なクラフト粘着テープに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a kraft pressure-sensitive adhesive tape, and more particularly, to a kraft pressure-sensitive adhesive tape which can be melted and recycled (recycled) after being used for sealing a corrugated cardboard and still attached.
【０００２】[0002]
【従来の技術】クラフト粘着テープは、段ボールの封緘
作業性が良いことから生産量が増大している。従来のク
ラフト粘着テープは、クルパック加工したクラフト紙に
ポリエチレンを押出ラミネートして、その表面にシリコ
ンを焼き付けるなどして離型処理を施し、反対面に粘着
剤を塗布したものが主流である。2. Description of the Related Art The production of kraft adhesive tapes is increasing because of the good workability of sealing corrugated board. The conventional kraft pressure-sensitive adhesive tape is mainly made by extrusion-laminating polyethylene on kraft-processed kraft paper, subjecting the surface of the kraft paper to release treatment such as baking silicon, and applying an adhesive on the opposite side.
【０００３】クラフト紙にポリエチレンをラミネートす
るのは、クラフト紙の毛羽立ちを抑え、平滑性を出すた
めである。また、粘着剤は、基材が紙であるため、塗工
が困難なラテックスやエマルジョン型のものは使用され
ず、主として溶液型や無溶剤型のものが汎用されてい
る。The reason why polyethylene is laminated on kraft paper is to suppress fluffing of kraft paper and to provide smoothness. Further, as the pressure-sensitive adhesive, since the base material is paper, latex or emulsion type, which is difficult to apply, is not used, and mainly solution type or solventless type is widely used.
【０００４】クラフト粘着テープの用途は、大半が包装
用であり、特に段ボール包装の際に封緘用として使用さ
れている。使用済の段ボールは、再生利用のために回収
されて、水に溶解される。この段ボール回収の際、梱包
時に貼り付けられたクラフト粘着テープは、大抵の場
合、引き剥されることなく段ボールにそのまま貼り付け
られたままである。このような使用済の段ボールを回収
し、再生利用するに当たっては、ポリエチレンラミネー
ト部が水に溶解しないため、これを別途分離して回収し
なければならない。また、粘着剤に関しても、やはり水
に溶解せずに不純物として残留することになる。したが
って、パルパーで溶解したものをそのままの形で再生使
用することは困難であり、手間とコストがかさむという
問題がある。Most of the applications of the kraft pressure-sensitive adhesive tape are for packaging, and particularly for corrugated cardboard packaging, they are used for sealing. Used cardboard is collected for recycling and dissolved in water. At the time of collecting the corrugated board, the kraft pressure-sensitive adhesive tape attached at the time of packaging is almost always attached to the corrugated board without being peeled off. In collecting and recycling such used cardboard, the polyethylene laminate part does not dissolve in water, so it must be separated and collected separately. In addition, the adhesive also remains as an impurity without being dissolved in water. Therefore, it is difficult to recycle the melted product in the pulper as it is, and there is a problem that it is troublesome and costly.
【０００５】[0005]
【発明が解決しようとする課題】本発明の目的は、使用
済みの段ボールの再生使用に際し、段ボールに貼付した
ままで溶解・再生工程に付することができるクラフト粘
着テープを提供することにある。本発明者らは、鋭意研
究した結果、クレーコート加工したクラフト紙に、粘着
剤として水溶性粘着剤を塗工した粘着テープが上記目的
を達成できることを見いだし、その知見に基づいて本発
明を完成するに至った。SUMMARY OF THE INVENTION An object of the present invention is to provide a kraft pressure-sensitive adhesive tape which can be subjected to a melting / recycling process while being attached to a corrugated cardboard when the cardboard used is reclaimed. As a result of diligent research, the present inventors have found that a pressure-sensitive adhesive tape obtained by coating a clay-coated kraft paper with a water-soluble pressure-sensitive adhesive as the pressure-sensitive adhesive can achieve the above object, and completed the present invention based on the findings. Came to do.
【０００６】[0006]
【課題を解決するための手段】本発明によれば、クレー
コート加工したクラフト紙の片面に、水溶性の粘着剤を
塗工して成ることを特徴とするクラフト粘着テープが提
供される。According to the present invention, there is provided a kraft pressure-sensitive adhesive tape comprising a kraft-coated kraft paper coated on one side with a water-soluble pressure-sensitive adhesive.
【０００７】以下、本発明について詳細に説明する。本
発明で用いる基材は、クラフトパルプを原料として抄紙
したクラフト紙であり、未晒クラフト紙、半晒クラフト
紙、クルパック紙等が挙げられる。このクラフト紙の片
面に、クレーコート加工を施す。The present invention will be described in detail below. The base material used in the present invention is a kraft paper made from kraft pulp as a raw material, and examples thereof include unbleached kraft paper, semi-bleached kraft paper, and Clupak paper. Clay coat processing is applied to one side of this kraft paper.
【０００８】コート加工は、一般に、スチレン−ブタジ
エン系、酢酸ビニル系、メチルメタクリレート−ブタジ
エン系などのラテックスとクレー、酸化チタン、カオリ
ン、炭酸カルシウムなどの白色顔料を混ぜたものを紙基
材にコーティングすることにより行う。これらのコート
加工の中でも、クレー塗工処理が好ましい。コート加工
面には、通常、長鎖アルキル系ポリマーまたはシリコン
系の離型剤で離型処理をする。In the coating process, generally, a paper base material is coated with a mixture of latex such as styrene-butadiene type, vinyl acetate type and methyl methacrylate-butadiene type and white pigment such as clay, titanium oxide, kaolin and calcium carbonate. By doing. Among these coating processes, the clay coating process is preferable. The coated surface is usually subjected to a release treatment with a long-chain alkyl polymer or a silicone release agent.
【０００９】コート加工した面とは反対面の基材上に、
水溶性の粘着剤を塗工する。水溶性の粘着剤としては、
例えば、ベースポリマーとして、ポリビニルアルコー
ル、ポリアクリルアミド、ポリビニルメチルエーテル、
エチルアクリレート−アクリル酸共重合体などのアクリ
ル酸含有ポリマー、デキストリン、ポリビニルピロリド
ンなどを使用したものが挙げられる。これらの中でも、
水溶性のアクリル酸含有ポリマーが好ましい。On the base material opposite to the coated surface,
Apply water-soluble adhesive. As a water-soluble adhesive,
For example, as the base polymer, polyvinyl alcohol, polyacrylamide, polyvinyl methyl ether,
Examples thereof include those using acrylic acid-containing polymers such as ethyl acrylate-acrylic acid copolymer, dextrin, polyvinylpyrrolidone and the like. Among these,
Water soluble acrylic acid containing polymers are preferred.
【００１０】本発明のクラフト粘着テープは、図１に示
すような積層構成を有するものである。即ち、クラフト
原紙（３）の片面にコート部（２）、その上に離型部
（１）を有し、反対面に水溶性の粘着剤層（４）を有し
ている。このような構成のクラフト粘着テープは、基材
・粘着剤ともに水に分散・溶解するため、粘着テープを
貼り付けたままで段ボールをリサイクル工程に付するこ
とができる。The kraft adhesive tape of the present invention has a laminated structure as shown in FIG. That is, the kraft base paper (3) has a coat part (2) on one side, a release part (1) on it, and a water-soluble adhesive layer (4) on the opposite side. Since the kraft pressure-sensitive adhesive tape having such a configuration disperses and dissolves both the base material and the pressure-sensitive adhesive in water, the corrugated cardboard can be subjected to the recycling process with the pressure-sensitive adhesive tape attached.
【００１１】[0011]
【実施例】以下、本発明について実施例および比較例を
挙げて具体的に説明するが、本発明はこれらの実施例の
みに限定されるものではない。EXAMPLES The present invention will be specifically described below with reference to Examples and Comparative Examples, but the present invention is not limited to these Examples.
【００１２】［実施例１］坪量７３ｇ／ｍ2の未晒しク
ラフト原紙にクレーコート加工（富士加工社製のクレー
２５ｇ／ｍ2コーティング）を施して９０ｇ／ｍ2とした
原反に、変性ポリアクリル酸（サイデン化学社製；商品
名ＡＴ８０２）を主成分とした水溶性粘着剤を塗布し、
１００℃で３分間乾燥させてクラフト粘着テープを作成
した（糊厚：４０μｍ）。得られたクラフト粘着テープ
の物性を表１に示す。[Example 1] An unbleached kraft base paper having a basis weight of 73 g / m 2 was subjected to a clay coating process (25 g / m 2 coating of clay manufactured by Fuji Kako Co., Ltd.) to 90 g / m 2, and then modified. Applying a water-soluble adhesive containing polyacrylic acid (manufactured by Saiden Chemical Co .; trade name AT802) as a main component,
A kraft pressure-sensitive adhesive tape was prepared by drying at 100 ° C. for 3 minutes (paste thickness: 40 μm). Table 1 shows the physical properties of the obtained kraft pressure-sensitive adhesive tape.
【００１３】[0013]
【表１】 [Table 1]
【００１４】（脚注） （１）保持力（ＪＩＳ保持力）：ＪＩＳ Ｚ−０２３７
−１１ （２）ボールタック：ＪＩＳ Ｚ−０２３７（傾斜式ボ
ールタック法、１／３２〜３２／３２インチ径の鋼球を
使用し、ボールナンバーで表示） （３）粘着力（ＳＰ粘着力）：ＪＩＳ Ｚ−０２３７−
８ （４）水溶性：次の基準で評価した。 ○；水に対する溶解性が良好、 △；やや残存物があ
る。(Footnote) (1) Holding force (JIS holding force): JIS Z-0237
-11 (2) Ball tack: JIS Z-0237 (inclined ball tack method, using steel balls with a diameter of 1/32 to 32/32 inch and indicated by ball number) (3) Adhesive force (SP adhesive force) : JIS Z-0237-
8 (4) Water solubility: evaluated according to the following criteria. ◯: Good solubility in water, Δ: Some residual substances.
【００１５】表１から明らかなように、本発明のクラフ
ト粘着テープは、常温、高温、低温、あるいは高温高湿
条件下でも良好な粘着特性を示し、しかも水溶性に優れ
ており、段ボール再生用の粘着テープとして好適であ
る。また、このクラフト粘着テープの実用性能の評価結
果を表２に示す。As is clear from Table 1, the kraft pressure-sensitive adhesive tape of the present invention shows good pressure-sensitive adhesive properties even under normal temperature, high temperature, low temperature, or high temperature and high humidity conditions, and is excellent in water solubility. It is suitable as an adhesive tape. Table 2 shows the evaluation results of the practical performance of this kraft adhesive tape.
【００１６】［実施例２］粘着剤層（サイデン化学社
製；ＡＴ８０４）の糊厚を２５μｍとしたこと以外は実
施例１と同様にしてクラフト粘着テープを作成した。評
価結果を表２に示す。Example 2 A kraft pressure-sensitive adhesive tape was prepared in the same manner as in Example 1 except that the adhesive layer (made by Saiden Chemical Co .; AT804) had a thickness of 25 μm. The evaluation results are shown in Table 2.
【００１７】［比較例１］実施例１で使用したクラフト
原紙に、クレーコートする代わりに、厚さ２０μｍのポ
リエチレンをラミネートし、更に水溶性粘着剤に代わり
にスチレンイソプレンブロック共重合体系のホットメル
ト粘着剤を４０μｍの厚みで塗工した。評価結果を表２
に示す。Comparative Example 1 Instead of clay coating, the kraft base paper used in Example 1 was laminated with polyethylene having a thickness of 20 μm, and the water-soluble adhesive was replaced with a styrene-isoprene block copolymer hot melt. The adhesive was applied in a thickness of 40 μm. Table 2 shows the evaluation results
Shown in.
【００１８】[0018]
【表２】 [Table 2]
【００１９】（脚注） （１）高湿下経時品：４０℃×９０％ＲＨ×３日 （２）水溶性：段ボールに粘着テープを貼付したものを
水中に浸漬し、２０分攪拌した後の状態を評価した。(Footnote) (1) Aged product under high humidity: 40 ° C. × 90% RH × 3 days (2) Water solubility: Corrugated cardboard with adhesive tape attached is immersed in water and stirred for 20 minutes. The condition was evaluated.
【００２０】表２から明らかなように、本発明のクラフ
ト粘着テープは、段ボールに対する粘着性能に優れてい
ると共に、水中で攪拌すると容易に粘着剤層が水に溶け
て剥離する。これに対して、比較例の粘着テープは、水
中で攪拌しても段ボールから剥離しない。As is clear from Table 2, the kraft pressure-sensitive adhesive tape of the present invention has excellent adhesiveness to corrugated cardboard, and when stirred in water, the pressure-sensitive adhesive layer is easily dissolved in water and peeled off. On the other hand, the pressure-sensitive adhesive tape of the comparative example does not peel off from the corrugated cardboard even when stirred in water.
【００２１】[0021]
【発明の効果】本発明によれば、基材及び粘着剤ともに
水に分散・溶解するため、テープを貼り付けた状態のま
まで段ボールをリサイクルにかけることができるクラフ
ト粘着テープが提供される。According to the present invention, since the base material and the pressure sensitive adhesive are both dispersed and dissolved in water, there is provided a kraft pressure sensitive adhesive tape which allows the corrugated board to be recycled while the tape is still attached.
【図１】本発明のクラフト粘着テープの積層構成を示す
図である。FIG. 1 is a diagram showing a laminated structure of a kraft pressure-sensitive adhesive tape of the present invention.
１ 離型部 ２ クレーコート紙 ３ クラフト原紙 ４ 水溶性粘着剤層 1 Release part 2 Clay coated paper 3 Kraft base paper 4 Water-soluble adhesive layer
Claims (1)
に、水溶性の粘着剤を塗工して成ることを特徴とするク
ラフト粘着テープ。1. A kraft pressure-sensitive adhesive tape comprising a clay-coated kraft paper coated on one side with a water-soluble pressure-sensitive adhesive.