JPH0881661A - Kraft adhesive tape - Google Patents
Kraft adhesive tapeInfo
- Publication number
- JPH0881661A JPH0881661A JP21911494A JP21911494A JPH0881661A JP H0881661 A JPH0881661 A JP H0881661A JP 21911494 A JP21911494 A JP 21911494A JP 21911494 A JP21911494 A JP 21911494A JP H0881661 A JPH0881661 A JP H0881661A
- Authority
- JP
- Japan
- Prior art keywords
- water
- soluble
- kraft
- base material
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は段ボ−ルの封緘に使用す
るクラフト粘着テ−プに関し、特に使用済段ボ−ルを再
生する際、段ボ−ルと共に溶解しうるクラフト粘着テ−
プに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a kraft adhesive tape used for sealing a corrugated ball, and more particularly, a kraft adhesive tape which can be dissolved together with the corrugated ball when reclaiming a used corrugated ball.
Regarding
【０００２】[0002]
【従来の技術】クラフト粘着テ−プは段ボ−ル封緘用と
して多量に使用されている。そして、使用済段ボ−ルは
回収され、再生利用するため再生工程において水に溶解
され、再度抄紙される。封緘用として使用されたクラフ
ト粘着テ−プは段ボ−ルに貼り付けられたまま再生工程
に送られる。しかし、一般にクラフト粘着テ−プは裏打
ち層としてポリエチレンがラミネ−トされていたり、或
いは水不溶性粘着剤が使用されている場合が多く、再生
工程において、これらはパルパ−で水中に分散・解離さ
れ、不純物として再生工程のスクリ−ン等に残留した
り、或はスクリ−ンを通り抜け再生紙の中に不純物とし
て混入し、ライントラブル及び製品の不純物の混入等の
悪影響を及ぼすことがあった。これを防止するため、段
ボ−ルの再生工程に先立って貼着されている粘着テ−プ
を取り去ることが考えられるが、極めて手間がかかり、
またコストがかさむので、再生工程前に粘着テ−プを取
り去ることは問題がある。BACKGROUND OF THE INVENTION Kraft adhesive tape is widely used for sealing corrugated balls. Then, the used stage ball is recovered, dissolved in water in the recycling step for recycling, and paper-made again. The kraft adhesive tape used for sealing is sent to the recycling process while being attached to the corrugated ball. However, in general, Kraft adhesive tapes often have polyethylene laminated as a backing layer, or a water-insoluble adhesive is used, and these are dispersed / dissociated in water by a pulper in the regeneration process. However, it may remain as an impurity in the screen or the like in the recycling process, or may pass through the screen and be mixed as an impurity in the recycled paper, which may have adverse effects such as line troubles and mixing of impurities in the product. In order to prevent this, it is conceivable to remove the adhesive tape that has been attached prior to the step of recycling the corrugated ball, but it is extremely time-consuming and
Also, removing the adhesive tape before the recycling process is problematic because it is costly.
【０００３】これらの問題点を解決するために、アルカ
リ離解可能なクラフトテ−プや水離解可能なクラフト粘
着テ−プやクレ−コ−ト加工したクラフト紙の片面に水
溶性粘着剤を塗工したクラフト粘着テ−プが発表されて
いるが（例えば実開平５−２２５３９号、実開平５−４
５０４７号、特開平５−１８６７５０号参照）、実際の
パルパ−離解においてはアルカリを添加しない場合が多
く、そのため離解が不充分である場合が生じたり、ま
た、前記公報記載の紙粘着テ−プでは基材上に目止め処
理を施し、その上に剥離処理を施しているため工程が増
え製造上面倒、かつコストアップという問題があった。In order to solve these problems, a water-soluble adhesive is applied to one side of an alkali disintegratable craft tape, a water disintegratable craft adhesive tape, or a kraft-coated kraft paper. Although the craft adhesive tape has been announced (for example, No. 5-22539, No. 5-4
No. 5047 and JP-A-5-186750), alkali is often not added in actual pulper disintegration, which may result in insufficient disintegration and the paper adhesive tape described in the above publication. However, since the sealing treatment is performed on the base material and the peeling treatment is performed thereon, there is a problem that the number of processes is increased and the manufacturing top is upset and the cost is increased.
【０００４】[0004]
【発明が解決しようとする課題】本発明者は上記の問題
点を解決すべく種々検討した結果、水離解性の良好なク
ラフト紙に一方の面に水溶性樹脂とシリコ−ンエマルジ
ョンの混合液からなる剥離剤を、他方の面に水溶性粘着
剤を、それぞれ塗布することにより、上記課題を解決で
き本発明を完成したもので、本発明は段ボ−ルに貼着し
たまま何らの残渣を残すことなく再生できるクラフト粘
着テ−プを提供することを目的とする。As a result of various studies to solve the above problems, the present inventor has found that kraft paper having good water disintegration has a mixed solution of a water-soluble resin and a silicone emulsion on one side. The above-mentioned problems can be solved and the present invention has been completed by applying a water-soluble pressure-sensitive adhesive to the other surface, respectively, and the present invention can be applied to a corrugated ball without any residue. It is an object of the present invention to provide a kraft adhesive tape that can be recycled without leaving.
【０００５】[0005]
【課題を解決するための手段】本願発明の要旨はクラフ
ト紙を基材とし、その一方の面に水溶性樹脂とシリコ−
ンエマルジョンの混合物からなる剥離層を設け、他方の
面に水溶性粘着剤層を設けたことを特徴とするクラフト
粘着テ−プであり、場合によっては基材と水溶性粘着剤
層との間に水溶性目止め剤層を介在させてもよい。SUMMARY OF THE INVENTION The gist of the present invention is to use kraft paper as a base material, on one surface of which a water-soluble resin and a silicone are used.
A Kraft pressure-sensitive adhesive tape, comprising a release layer made of a mixture of emulsions and a water-soluble pressure-sensitive adhesive layer on the other surface. You may interpose a water-soluble sealing agent layer in.
【０００６】以下、本発明について詳細に述べる。本発
明における基材としては、水離解性の良好なクラフトパ
ルプを原料として抄紙された末晒、クラフト半晒クラフ
ト、晒クラフト紙等のクラフト紙が挙げられ、この水離
解性の良好なクラフトパルプとはＪＩＳ Ｐ８１２２規
定によるサイズ度が１０ｓｅｃ未満のものである。従
来、クラフト粘着テ−プに使用されているクラフト紙の
サイズ度は、１０以上２５ｓｅｃ程度であり、本発明で
使用するものは、従来のものよりサイズ度は小さく、水
浸透性が速い。The present invention will be described in detail below. Examples of the substrate in the present invention include unbleached kraft papers made from kraft pulp having good water disintegration, kraft papers such as semi-bleached kraft, and bleached kraft paper. Means that the size degree according to JIS P8122 standard is less than 10 sec. Conventionally, the sizing degree of the kraft paper used for the kraft adhesive tape is about 10 to 25 seconds, and the stencil used in the present invention has a smaller sizing degree and a faster water permeability than the conventional ones.
【０００７】剥離層としては水溶性樹脂、シリコ−ンエ
マルジョンの混合物からなる剥離処理剤を使用する。剥
離処理剤には、場合により防滑剤、顔料等を添加しても
良い。この剥離処理剤は塗工に適した粘度に水で調整す
る。剥離処理剤に使用する水溶性樹脂としては、カルボ
キシメチルセルロ−ス（ＣＭＣ）、ポリビニルアルコ−
ル（ＰＶＡ）、水溶性アクリル樹脂及びその誘導体等が
使用できる。又、防滑剤としては、二酸化ケイ素、炭酸
マグネシウム、炭酸カルシウム、硬質樹脂等が使用可能
である。好適な剥離処理剤として、例えば重合度２００
〜３０００、ケン化度７０〜１００％のＰＶＡ１００部
に対し、シリコ−ンエマルジョン６〜３００部、シリコ
−ンエマルジョン用架橋剤０．５〜３０部を混合した混
合液をあげることが出来る。As the release layer, a release treatment agent composed of a mixture of a water-soluble resin and a silicone emulsion is used. An antislip agent, a pigment and the like may be added to the release treatment agent depending on the case. This release treating agent is adjusted with water to a viscosity suitable for coating. Examples of the water-soluble resin used for the release treatment agent include carboxymethyl cellulose (CMC) and polyvinyl alcohol.
(PVA), water-soluble acrylic resin and its derivatives, etc. can be used. Further, as the anti-slip agent, silicon dioxide, magnesium carbonate, calcium carbonate, hard resin and the like can be used. As a suitable release treatment agent, for example, a polymerization degree of 200
˜3000, saponification degree 70˜100% PVA100 parts, and silicone emulsion 6˜300 parts, silicone emulsion crosslinking agent 0.5˜30 parts are mixed.
【０００８】本発明においては、必要に応じて、目止め
層を設けることができる。目止め層は、基材と粘着剤の
間に塗布し、粘着剤の基材へのしみ込みを防止する目的
で使用しする。使用できる目止め剤としては、剥離剤と
同様の水溶性樹脂である。粘着剤層は、剥離層とは反対
面の基材上、または目止め層の上に水溶性粘着剤を塗工
することによって設ける。水溶性の粘着剤としては、例
えば（メタ）アクリル酸や無水マレイン酸などのカルボ
ン酸含有モノマ−と（メタ）アクリル酸エステルとの共
重合体や、それらのナトリウム塩、カリウム塩、アンモ
ニウム塩、ジメチルアミン塩、トリメチルアミン塩、ヒ
ドラジン塩等の中和物などがあり、その他アクリル酸の
誘導体として水酸基を有する（メタ）アクリル酸２−ヒ
ドロキシエチルや（メタ）アクリル酸２−ヒドロキシプ
ロピル、或いはアクリルアミドのようなアミド化合物、
アクリル酸ジメチルアミノエチルのようなアミノ基を有
する化合物など、親水性基を持ち、かつ水に溶けるもの
をベ−スポリマ−の全てまたは一部に使用している粘着
剤が使用できる。また、アクリル系以外でも、メチルセ
ルロ−ス、エチルセルロ−ス、カルボキシメチルセルロ
−ス等のセルロ−ル系、ポリビニルアルコ−ル、ポリビ
ニルピロリドン等のビニル系ポリマ−、或いはグア−ル
ガム、ロ−カストビ−ンガム等の糖類誘導体なども水溶
性粘着剤としては使用できる。本発明のクラフト粘着テ
−プの層構成を図示すると、図１又は図２の通りであ
る。図において、クラフト紙よりなる基材１の一方の面
には、剥離層２が構成されており、他方の面には水溶性
粘着層３が構成されている。また、場合によっては基材
１と水溶性粘着層３との間に水溶性目止め層４を設け
る。In the present invention, a sealing layer can be provided if necessary. The sealing layer is applied between the base material and the pressure-sensitive adhesive, and is used for the purpose of preventing the pressure-sensitive adhesive from soaking into the base material. As a filling agent that can be used, a water-soluble resin similar to the release agent is used. The pressure-sensitive adhesive layer is provided by applying a water-soluble pressure-sensitive adhesive on the base material opposite to the release layer or on the sealing layer. Examples of the water-soluble adhesive include copolymers of carboxylic acid-containing monomers such as (meth) acrylic acid and maleic anhydride and (meth) acrylic acid esters, sodium salts, potassium salts, and ammonium salts thereof, There are neutralized products such as dimethylamine salt, trimethylamine salt, hydrazine salt, and the like, and 2-hydroxyethyl (meth) acrylate and 2-hydroxypropyl (meth) acrylate, which have a hydroxyl group as a derivative of acrylic acid. An amide compound,
An adhesive having a hydrophilic group and being soluble in water, such as a compound having an amino group such as dimethylaminoethyl acrylate, may be used for all or part of the base polymer. Further, other than acrylic type, methyl type cellulose, ethyl type cellulose, carboxymethyl type cellulose and other vinyl type polymers, polyvinyl alcohol, polyvinyl pyrrolidone and other vinyl type polymers, or guar gum, locust beer. A sugar derivative such as lingua can also be used as the water-soluble adhesive. The layer structure of the kraft pressure-sensitive adhesive tape of the present invention is illustrated in FIG. 1 or 2. In the figure, a release layer 2 is formed on one surface of a base material 1 made of kraft paper, and a water-soluble adhesive layer 3 is formed on the other surface. In some cases, a water-soluble filling layer 4 is provided between the base material 1 and the water-soluble adhesive layer 3.
【０００９】[0009]
【実施例及び比較例】以下、実施例をもって本発明を詳
細に説明する。 実施例１ 本発明の実施例として使用した剥離処理剤の混合液の一
例を表１に示す。EXAMPLES AND COMPARATIVE EXAMPLES The present invention will be described in detail below with reference to Examples. Example 1 Table 1 shows an example of a mixed solution of the release treatment agent used as an example of the present invention.
【００１０】[0010]
【表１】 ここで使用したポリビニルアルコ−ルの重合度は５５０
で、そのけん化度は９９％である。またシリコ−ンエマ
ルジョンのシリコ−ン含有量は２０％であった。[Table 1] The degree of polymerization of the polyvinyl alcohol used here is 550.
The saponification degree is 99%. The silicone content of the silicone emulsion was 20%.
【００１１】実施例２ 坪量７３ｇ／ｍ2（サイズ度０ｓｅｃ）の末晒クラフト
クルパック紙に実施例１の剥離処理剤を片面に固形分３
ｇ／ｍ2となるように直接基材上に塗布し、１５０℃６
０秒で乾燥キュア−し、続いて他の片面に変性ポリアク
リル酸を主成分とした水溶性粘着剤を糊厚３０μｍとな
るように塗布し、１１０℃−２分乾燥させてテ−プを得
た。Example 2 An unbleached kraft klep pack paper having a basis weight of 73 g / m 2 (size degree 0 sec) was coated with the release treating agent of Example 1 on one side to give a solid content of 3
It was coated directly on the substrate so that it would be g / m 2, and 150 ° C 6
It is dried and cured for 0 seconds, and then a water-soluble pressure-sensitive adhesive containing modified polyacrylic acid as a main component is applied to the other surface to a paste thickness of 30 μm and dried at 110 ° C. for 2 minutes to form a tape. Obtained.
【００１２】実施例３ 坪量７３ｇ／ｍ2（サイズ度０ｓｅｃ）の末晒クラフト
クルパック紙の片面に実施例１の剥離剤を固形分３ｇ／
ｍ2となるように直接基材上に塗布し、１５０℃−６０
秒で乾燥キュアし、続いて他方の面にポリビニルアルコ
−ル（ＰＶＡ）を固形分１ｇ／ｍ2となるように塗布乾
燥して目止め剤層を形成し、その上に変性ポリアクリル
酸を主成分とした水溶性粘着剤を糊厚３０μｍとなるよ
うに塗布し１１０℃−２分乾燥させてテ−プを得た。Example 3 The release agent of Example 1 was applied to one side of an unbleached kraft-curl pack paper having a basis weight of 73 g / m 2 (size degree of 0 sec) at a solid content of 3 g /
Direct so that the m 2 was coated onto a substrate, 0.99 ° C. -60
It is dried and cured for 2 seconds, and then polyvinyl alcohol (PVA) is applied to the other surface so as to have a solid content of 1 g / m 2 and dried to form a sealing agent layer, and the modified polyacrylic acid is coated thereon. A water-soluble pressure-sensitive adhesive as a main component was applied so as to have a paste thickness of 30 μm and dried at 110 ° C. for 2 minutes to obtain a tape.
【００１３】比較例１ 坪量７５ｇ／ｍ2（サイズ度２１ｓｅｃ）の末晒クラフ
トクルパック紙の片面に実施例１の剥離剤を固形分３ｇ
／ｍ2となるように塗布し、１５０℃−６０秒で乾燥キ
ュア−し、他面に天然ゴムを主成分とするゴム系粘着剤
を糊厚４０μｍとなるように塗布し１１０℃−１分乾燥
させてテ−プを得た。Comparative Example 1 3 g of the solid content of the release agent of Example 1 was applied to one side of unbleached kraft-curl pack paper having a basis weight of 75 g / m 2 (size degree 21 sec).
/ M 2 and dried and cured at 150 ° C. for 60 seconds, and a rubber adhesive mainly composed of natural rubber is applied on the other surface so that the adhesive thickness becomes 40 μm and 110 ° C. for 1 minute. It was dried to obtain a tape.
【００１４】比較例２ 坪量７３ｇ／ｍ2（サイズ度１３ｓｅｃ）の末晒クラフ
トクルパック紙の片面にポリエチレンラミネ−トを１５
μｍラミネ−トし、その上にシリコ−ン剥離剤（溶剤
系）を固形分０．５ｇ／ｍ2となるように塗布し、１５
０℃−６０秒で乾燥キュア−し、もう片面に天然ゴムを
主成分とするゴム系粘着剤を糊厚３５μｍとなるように
塗布し１１０℃−１分乾燥させてテ−プを得た。Comparative Example 2 15 g of polyethylene laminate was applied to one side of unbleached kraft-curl pack paper having a basis weight of 73 g / m 2 (size degree 13 sec).
μm laminating - collected by, on the silicone that - applying down stripping agent (solvent-based) to have a solid content 0.5 g / m 2, 15
It was dried and cured at 0 ° C. for 60 seconds, a rubber-based pressure-sensitive adhesive containing natural rubber as a main component was applied to the other surface so as to have a paste thickness of 35 μm, and dried at 110 ° C. for 1 minute to obtain a tape.
【００１５】このようにして得られた各粘着テ−プの特
性を表２及び表３に示す。なお、表２及び３における特
性の測定方法及び評価は次の通りである。 粘着力 ＪＩＳ Ｚ０２３７−８ ボ−ルタッフ ＪＩＳ Ｚ０２３７ ＳＰ保持力 ＪＩＳ Ｚ０２３７−１１ クラフト紙保持力 サンプル試験面積 １０×２０ｍｍ 圧着 １ｋｇ×１往復 懸垂加重 １ｋｇ 被着体 クラフト紙 高速巻き戻し速度 １０Ｍ／ｍｉｎ 段ボ−ル実用試験 被着体段ボ−ル Ｋ７Ｗ テ−プサンプル ５０ｍｍ幅、Ｉ貼り、 Ｎ数、１０個 圧着後常温では４８時間、４０℃−６５％ＲＨでは６時
間後に３以上８ｍｍ未満ずれたものを「ずれ」、８ｍｍ
以上ずれたものを「剥がれ」とし、サンプル１０個中の
「剥がれ」、「ずれ」の個数を測定した。 水溶性試験 ボ−ル紙（坪量４００ｇ／ｍ2）１ｍ2上に
テ−プ１０ｇを張る代りに０．０８ｍ2上にテ−プ０．
８ｇを張った。これを３×３ｃｍ程にカットし、ＮａＯ
Ｈ、ＨＣｌでＰＨ３〜１２に調整した水１０００ｃｃ
（２０℃）と共に標準離解機（ＪＩＳ８２０９）にて５
分間離解して評価した。The characteristics of each adhesive tape thus obtained are shown in Tables 2 and 3. The measuring methods and evaluations of the characteristics in Tables 2 and 3 are as follows. Adhesive force JIS Z0237-8 Ball-tuff JIS Z0237 SP retention force JIS Z0237-11 Kraft paper retention force Sample test area 10 x 20 mm Crimping 1 kg x 1 reciprocating suspended load 1 kg Adherent kraft paper High speed rewinding speed 10 M / min − Practical test Adherent stage ball K7W tape sample 50 mm width, I pasted, N number, 10 pieces After pressure bonding, at room temperature for 48 hours, and at 40 ° C.-65% RH for 6 hours, shifted by 3 mm or more and less than 8 mm. "Displacement" of objects, 8 mm
The above-mentioned deviation was defined as “peeling”, and the number of “peeling” and “deviation” in 10 samples were measured. Soluble test ball - roll paper (basis weight 400 g / m 2) Te on 1 m 2 - Te on 0.08 m 2 instead of tensioning the flop 10 g - flop 0.
8g was stretched. Cut this into 3 x 3 cm pieces and use NaO
1000 cc of water adjusted to pH 3-12 with H and HCl
5 with standard disintegrator (JIS8209) together with (20 ° C)
It disaggregated for a minute and evaluated.
【００１６】[0016]
【表２】 [Table 2]
【００１７】[0017]
【表３】 なお表３は表２で評価したテ−プを６５℃、８０％Ｒ
Ｈ、７２時間エ−ジング後の結果を示す。[Table 3] Table 3 shows the tape evaluated in Table 2 at 65 ° C and 80% R.
The results after H and 72 hours aging are shown.
【００１８】[0018]
【発明の効果】以上述べたように本発明にかかるクラフ
ト粘着テ−プは水溶性が良好なため段ボ−ルに貼着した
ままで再生工程に付しても段ボ−ルと共に完全に溶解
し、パルパ−内に何らの残渣が残らず、ライントラブル
が発生しなかった。As described above, since the kraft adhesive tape according to the present invention has good water solubility, it can be completely attached together with the corrugated ball even when it is subjected to the regenerating process while being attached to the corrugated ball. It was dissolved and no residue remained in the pulper, and no line trouble occurred.
【図１】本発明にかかるクラフト粘着テ−プの層構成を
示した図。FIG. 1 is a view showing a layer structure of a kraft pressure-sensitive adhesive tape according to the present invention.
【図２】本発明にかかる他のクラフト粘着テ−プの層構
成を示した図。FIG. 2 is a view showing a layer structure of another kraft pressure-sensitive adhesive tape according to the present invention.
１ クラフト紙よりなる基材 ２ 剥離層 ３ 水溶性粘着層 ４ 水溶性目止め層 1 Base Material Made of Kraft Paper 2 Release Layer 3 Water-Soluble Adhesive Layer 4 Water-Soluble Filling Layer
Claims (3)
水溶性樹脂とシリコ−ンエマルジョンの混合物からなる
剥離層を設け、他方の面に水溶性粘着剤層を設けたこと
を特徴とするクラフト粘着テ−プ。1. A kraft paper base material, a release layer comprising a mixture of a water-soluble resin and a silicone emulsion is provided on one surface thereof, and a water-soluble adhesive layer is provided on the other surface thereof. Craft adhesive tape.
未満の水離解性に優れたクラフト紙である請求項１記載
のクラフト粘着テ−プ。2. The tape has a size of 10 sec.
The kraft adhesive tape according to claim 1, which is a kraft paper excellent in water disintegration property.
に水溶性目止め剤層を介在させた請求項１及び請求項２
記載のクラフト粘着テ−プ。3. The water-soluble sealing agent layer is interposed between the base material of the tape and the water-soluble pressure-sensitive adhesive.
Kraft adhesive tape as described.