JPH0515858B2 - - Google Patents
Info
- Publication number
- JPH0515858B2 JPH0515858B2 JP58132097A JP13209783A JPH0515858B2 JP H0515858 B2 JPH0515858 B2 JP H0515858B2 JP 58132097 A JP58132097 A JP 58132097A JP 13209783 A JP13209783 A JP 13209783A JP H0515858 B2 JPH0515858 B2 JP H0515858B2
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- fiber
- reinforced
- outer mold
- aerated concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は、表面の外型が繊維補強コンクリー
トからなり内部に気泡コンクリートが充填された
繊維補強気泡コンクリートパネルの製造方法に関
する。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to a method for producing a fiber-reinforced cellular concrete panel whose outer surface is made of fiber-reinforced concrete and whose interior is filled with cellular concrete.
最近の建物には、普通コンクリート、軽量コン
クリートあるいは気泡コンクリート等で成形され
たPCパネルが広く使用されているが、普通コン
クリートからなるPCパネルは強度が大きい反面、
重量が極めて重く取扱いが極めて面倒であつた。
PC panels made of ordinary concrete, lightweight concrete, or aerated concrete are widely used in modern buildings, but while PC panels made of ordinary concrete have high strength,
It was extremely heavy and difficult to handle.
一方、軽量コンクリートや気泡コンクリートか
らなるPCパネルは、軽い反面、強度が極めて弱
いだけでなく、比較的脆いため取扱い中に縁部が
欠けることがよくあつた。 On the other hand, although PC panels made of lightweight concrete or aerated concrete are light, they not only have extremely low strength, but also are relatively brittle, so their edges often break during handling.
そこで、特開昭54−7723号公報には、一端、芯
材となるコンクリート板を製造した後、このコン
クリート板の周囲に繊維補強モルタルを塗り付け
て、該表面層を乾燥させて繊維補強気泡コンクリ
ートパネルを製造する方法が提案されている。 Therefore, Japanese Patent Application Laid-Open No. 54-7723 discloses that after a concrete plate serving as a core material is manufactured, a fiber-reinforced mortar is applied around the concrete plate, the surface layer is dried, and fiber-reinforced foam is formed. A method of manufacturing concrete panels is proposed.
又、特開昭54−31434号公報には、型枠内に収
納しても変形しないように予め上方開口の箱型の
外殻繊維補強モルタル層を硬化養生させ、その
後、該箱型の外殻内に気泡コンクリートを注入す
る方法が提案されている。 Furthermore, in Japanese Patent Application Laid-Open No. 54-31434, a fiber-reinforced mortar layer for an upper-opening box-shaped outer shell is hardened and cured in advance so that it does not deform even when stored in a formwork, and then the outer shell of the box-shaped outer shell is cured. A method of injecting aerated concrete into the shell has been proposed.
しかし、特開昭54−7723号公報に示された方法
では、予め芯材となるコンクリート板を硬化養生
させておく必要があり、その後、該芯材の回りに
表面材となる繊維補強モルタルを塗り付けて、該
表面層を乾燥させて製造する必要があるので、表
面の外型が繊維補強コンクリートからなり内部に
気泡コンクリートが充填された繊維補強気泡コン
クリートパネルとするためには長い時間を必要と
するという欠点があつた。
However, in the method disclosed in JP-A-54-7723, it is necessary to harden and cure the concrete plate that will serve as the core material in advance, and then apply fiber-reinforced mortar that will serve as the surface material around the core material. Because it is necessary to apply the material and dry the surface layer, it takes a long time to produce a fiber-reinforced cellular concrete panel whose outer surface is made of fiber-reinforced concrete and whose interior is filled with cellular concrete. There was a drawback that it was.
また、特開昭54−31434号公報に示された方法
では、逆に上方開口の箱型の外殻繊維補強モルタ
ル層を予め硬化養生させておく必要があり、その
後、該箱型の外殻内に気泡コンクリートを注入し
て硬化養生させる必要があり、やはり、表面の外
型が繊維補強コンクリートからなり内部に気泡コ
ンクリートが充填された繊維補強気泡コンクリー
トパネルとするためには長い時間を必要とすると
いう欠点があつた。 In addition, in the method disclosed in JP-A-54-31434, on the contrary, it is necessary to harden and cure the upper opening box-shaped outer shell fiber-reinforced mortar layer in advance, and then the box-shaped outer shell It is necessary to pour aerated concrete inside the panel and allow it to harden, and it takes a long time to create a fiber-reinforced aerated concrete panel in which the outer surface is made of fiber-reinforced concrete and the inside is filled with aerated concrete. There was a drawback of doing so.
この発明の目的は、可及的短時間に表面の外型
が繊維補強コンクリートからなり内部に気泡コン
クリートが充填された繊維補強気泡コンクリート
パネルとする製造方法を提供することである。 An object of the present invention is to provide a method for manufacturing a fiber-reinforced cellular concrete panel whose outer surface is made of fiber-reinforced concrete and whose interior is filled with cellular concrete in the shortest possible time.
このようにこの発明の目的は、極めて軽い上に
強度が極めて大きい製品が、簡単な製造工程によ
り生産時間が短く、量産による製造コストの大幅
な逓減が図れる製造方法を提供することである。 As described above, an object of the present invention is to provide a manufacturing method that allows a product to be extremely light and extremely strong to be produced in a short production time through a simple manufacturing process, and to significantly reduce manufacturing costs through mass production.
この発明の表面の外型が繊維補強コンクリート
からなり内部に気泡コンクリートが充填された繊
維補強気泡コンクリートパネルとする製造方法
は、繊維補強コンクリートからなる中空状の外型
を所定の断面形状に押出し成形し、次いで前記の
押出された外型内に気泡コンクリートを充填し
て、さらに、充填されたことによる変形を無くす
ために前記外型をプレスした後、前記外型をオー
トクレーブ養生することを特徴とする表面が繊維
補強コンクリートで補強された気泡コンクリート
パネルの製造方法である。
The method of manufacturing a fiber-reinforced aerated concrete panel in which the surface outer mold is made of fiber-reinforced concrete and the inside is filled with aerated concrete includes extruding a hollow outer mold made of fiber-reinforced concrete into a predetermined cross-sectional shape. Then, the extruded outer mold is filled with aerated concrete, and after the outer mold is pressed to eliminate deformation caused by the filling, the outer mold is cured in an autoclave. This is a method for manufacturing aerated concrete panels whose surfaces are reinforced with fiber-reinforced concrete.
この発明に外型として使用される繊維補強コン
クリートは、ガラス繊維、カーボン繊維、スチー
ル繊維、石綿繊維、ナイロン繊維、ポリプロピレ
ン繊維、ポリスチレン繊維等の各種補強繊維を混
入した繊維補強コンクリートより形成されたもの
であり、このようなコンクリートを所定の中空状
の断面形状に押出し、それを外型とし、その中に
気泡コンクリートを充填し、続いて気泡コンクリ
ートを充填した状態の外型をオーとクレーブ養生
して充分に硬化させるのである。 The fiber-reinforced concrete used as the outer mold in this invention is formed from fiber-reinforced concrete mixed with various reinforcing fibers such as glass fiber, carbon fiber, steel fiber, asbestos fiber, nylon fiber, polypropylene fiber, and polystyrene fiber. This type of concrete is extruded into a predetermined hollow cross-sectional shape, used as an outer mold, filled with aerated concrete, and then the outer mold filled with aerated concrete is cured in an oven. The material is then cured sufficiently.
そして上記のように押し出された状態の外型に
気泡コンクリートを充填するのであるから、この
充填により外型が変形するので、オートクレーブ
養生する前に、気泡コンクリートを充填した外型
の上下面をプレスして変形を整形するのである。 Then, as the extruded outer mold is filled with aerated concrete as described above, this filling deforms the outer mold, so before curing in an autoclave, press the top and bottom surfaces of the outer mold filled with aerated concrete. Then, the deformation is corrected.
以下、この発明を図示する一実施例によつて説
明する。
Hereinafter, the present invention will be explained by way of an illustrative embodiment.
第１図乃至第４図に示したこの発明に従つて製
造される表面が繊維補強コンクリートで補強され
た気泡コンクリートパネル１は、外型２内に気泡
コンクリート３が充填され、必要に応じて補強鉄
筋４が配筋されていたり、複数個の貫通孔５がパ
ネルの長手方向に連続して形成された製品であ
る。 The aerated concrete panel 1 whose surface is reinforced with fiber-reinforced concrete and which is manufactured according to the present invention as shown in FIGS. This is a product in which reinforcing bars 4 are arranged and a plurality of through holes 5 are formed continuously in the longitudinal direction of the panel.
そして外型２は、ガラス繊維、カーボン繊維、
スチール繊維、石綿繊維、ナイロン繊維、ポリプ
ロピレン繊維、ポリエチレン繊維等の各種補強繊
維を混入した繊維補強コンクリートを素材として
断面略矩形の筒状に押出し成形されている。 The outer mold 2 is made of glass fiber, carbon fiber,
It is made of fiber-reinforced concrete mixed with various reinforcing fibers such as steel fibers, asbestos fibers, nylon fibers, polypropylene fibers, and polyethylene fibers, and is extruded into a cylindrical shape with a substantially rectangular cross section.
また外型２の長手方向に連続して形成され、こ
の発明に従つて製造された表面が繊維補強コンク
リートで補強された気泡コンクリートパネル１を
壁材として並べて設置した際、隣り合うパネル
１，１の凸部６と凹部７とが係合するようになつ
ている。 Furthermore, when the aerated concrete panels 1 formed continuously in the longitudinal direction of the outer mold 2 and whose surfaces are reinforced with fiber-reinforced concrete manufactured according to the present invention are installed side by side as wall materials, the adjacent panels 1, 1 The convex portion 6 and the concave portion 7 are adapted to engage with each other.
そこで、この発明の表面が繊維補強コンクリー
トで補強された気泡コンクリートパネル１の製造
方法の実施例を説明する。 Therefore, an embodiment of the method of manufacturing a cellular concrete panel 1 whose surface is reinforced with fiber-reinforced concrete according to the present invention will be described.
まず、外型２を所定断面の筒状に押出成形す
る。続いて、押出された外型２の両端を塞いで外
に注入する気泡コンクリートが漏れないようにし
て、外型２内に気泡コンクリート３を充填し発泡
させる。 First, the outer mold 2 is extruded into a cylindrical shape with a predetermined cross section. Next, both ends of the extruded outer mold 2 are closed to prevent the aerated concrete poured outside from leaking, and the outer mold 2 is filled with aerated concrete 3 and foamed.
次に、気泡コンクリート３を充填した外型２を
上下よりプレスして気泡コンクリート３を発泡さ
せたことによつてできた外型２の変形をなくし、
製品の寸法精度を高める。 Next, the outer mold 2 filled with aerated concrete 3 is pressed from above and below to eliminate deformation of the outer mold 2 caused by foaming the aerated concrete 3,
Improve the dimensional accuracy of products.
続いて、これをオートクレーブ養生して充分に
硬化させて製品とする。 Subsequently, this is cured in an autoclave to be sufficiently cured to form a product.
なお、補強鉄筋４を入れる場合は、気泡コンク
リート３を充填する前に、外型２内に配筋する。 In addition, when reinforcing reinforcing bars 4 are inserted, they are arranged inside the outer mold 2 before filling with the aerated concrete 3.
また、連通孔５は、例えば、気泡コンクリート
３の中に予め芯材を配置しておき、プレスし、養
生した後、前記芯材を引き抜く等の方法によつて
形成する。 The communicating holes 5 are formed by, for example, placing a core material in the aerated concrete 3 in advance, pressing it, curing it, and then pulling out the core material.
本発明の表面が繊維補強コンクリートで補強さ
れた気泡コンクリートパネルは、外型と気泡コン
クリートを同時に硬化養生するので従来の方法に
比べ遥に短時間で製造できる。しかも、極めて軽
い上に、強度が極めて大きく量産による製造コス
トの大幅な低廉化を図ることができる。
The aerated concrete panel of the present invention whose surface is reinforced with fiber-reinforced concrete can be manufactured in a much shorter time than conventional methods because the outer mold and the aerated concrete are hardened and cured at the same time. Moreover, it is extremely light, has extremely high strength, and can be mass-produced to significantly reduce manufacturing costs.
また、実施例に示したように気泡コンクリート
内に貫通孔を設けた後、オートクレーブ養生すれ
ば、オートクレーブに要する時間をさらに短縮す
ることができ、製造工程全体に要する時間の更な
る短縮が図れる。 Further, as shown in the example, if the aerated concrete is cured in an autoclave after forming through holes, the time required for autoclaving can be further shortened, and the time required for the entire manufacturing process can be further shortened.
第１図、第２図および第３図はこの発明に従つ
て製造されたパネルの断面図、第４図は第１図の
斜視図である。
１……本発明により製造されたパネル、２……
外型、３……気泡コンクリート、４……補強鉄
筋、５……貫通孔、６……凸部、７……凹部。
1, 2 and 3 are cross-sectional views of panels manufactured according to the invention, and FIG. 4 is a perspective view of FIG. 1. 1... Panel manufactured according to the present invention, 2...
Outer mold, 3...Aerated concrete, 4...Reinforcement reinforcing bars, 5...Through hole, 6...Protrusion, 7...Recess.
Claims (1)
を所定の断面形状に押出し成形し、次いで前記の
押出された外型内に気泡コンクリートを充填し
て、さらに、充填されたことによる変形を無くす
ために前記外型をプレスした後、前記外型をオー
トクレーブ養生することを特徴とする表面が繊維
補強コンクリートで補強された気泡コンクリート
パネルの製造方法。1. A hollow outer mold made of fiber-reinforced concrete is extruded into a predetermined cross-sectional shape, and then the extruded outer mold is filled with aerated concrete, and further, in order to eliminate deformation due to filling. A method for producing an aerated concrete panel whose surface is reinforced with fiber-reinforced concrete, which comprises pressing the outer mold and then curing the outer mold in an autoclave.