JPH0478105B2 - - Google Patents
Info
- Publication number
- JPH0478105B2 JPH0478105B2 JP10574887A JP10574887A JPH0478105B2 JP H0478105 B2 JPH0478105 B2 JP H0478105B2 JP 10574887 A JP10574887 A JP 10574887A JP 10574887 A JP10574887 A JP 10574887A JP H0478105 B2 JPH0478105 B2 JP H0478105B2
- Authority
- JP
- Japan
- Prior art keywords
- protection sheet
- surface protection
- water
- synthetic resin
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
産業上の利用分野
本発明は、アクリル板をはじめとする合成樹脂
板の表面に貼着してその表面保護を図るための表
面保護用シートに関するものである。
従来の技術
アクリル板、塩化ビニル板、ポリカーボネート
板、ポリスチレン板、ABS板などの合成樹脂板
は、その表面が平滑で美麗であることが製品価値
上重要である。
合成樹脂板の保管中、輸送中あるいは切削加工
時にその表面が傷つけられることを防止するため
に、合成樹脂板の片面または両面に表面保護用シ
ートを貼着することが行われており、従来この目
的のための表面保護用シートの一つとして、紙基
材の片面にポリビニルアセテート部分鹸化物の水
溶液からなる水性糊剤を塗布、成層したものが用
いられている。
水性糊剤を塗布した表面保護用シートを合成樹
脂板に貼着するには、この水性糊剤は再湿活性型
であるので、表面保護用シートの水性糊剤塗布層
側に高温の水蒸気を吹付けて活性化し、ゴムロー
ルで合成樹脂板表面に押圧圧着する方法が一般的
にとられている。
上記表面保護用シートを貼着した合成樹脂板
は、検査のためにその表面保護用シートを部分的
に剥離し再貼着することがある。この場合、水性
糊剤としてポリビニルアセテート部分鹸化物のみ
の水溶液を用いると再貼着性が不足するため、ポ
リビニルアセテート部分鹸化物に多価アルコール
や水性のアクリル系粘着剤を添加して剥離性およ
び再貼着性を向上させることが行われている。
また、アクリル板等の合成樹脂板は、所定の寸
法にするためにトリミングを行うが、製造収率向
上のためにトリミングした残りの部分を再使用す
ること、つまり、トリミング残を粉砕し、該粉砕
物を単独であるいは新しい樹脂に混合して成形に
供することが一般的に行われている。
発明が解決しようとする問題点
しかしながら、紙基材の片面に上述の水性糊剤
（ポリビニルアセテート部分鹸化物に多価アルコ
ールや水性のアクリル系粘着剤を添加した水性糊
剤）を塗布、成層した保護用シートを貼着した合
成樹脂板にあつては、トリミング残を再使用する
と、合成樹脂板表面にわずかに残存した水性糊剤
のために、再生した合成樹脂板が黄色ないし褐色
に変色するという問題点があつた。
この変色の原因は、表面保護用シートの水性糊
剤塗布層側に高温の水蒸気を吹付けて活性化し、
ゴムロールで合成樹脂板表面に押圧圧着する際、
水性糊剤の表面に残存している余分の水分が押圧
されるに従い水性糊剤を溶解しながら紙基材の両
側縁部を通つて合成樹脂板端面に流出して該合成
樹脂板を汚染し、その結果、トリミング残に糊剤
がわずかに残存することになるためであると考え
られる。
本発明は、トリミング残を再使用したとき、再
生した合成樹脂板に変色が生じないようにした表
面保護用シートを提供することを目的になされた
ものである。
問題点を解決するための手段
本発明は、「紙基材１の片面に水性糊剤の塗布
層２を形成した表面保護用シートにおいて、前記
紙基材１の両側縁部に水性糊剤の未塗布ゾーン
３，３を設けたことを特徴とする合成樹脂板の表
面を保護するための表面保護用シート。」をその
要旨とするものである。
以下本発明を詳細に説明する。
本発明における合成樹脂板としては、アクリル
板、塩化ビニル板、ポリカーボネート板、ポリス
チレン板、ABS板など押出成形や注型成形によ
つて製造される各種の合成樹脂板があげられる。
これらの中では、押出成形法によるアクリル板
（つまりポリメチルメタクリレー板）が、再生さ
れた場合変色が顕著であるため、特に重要であ
る。
このような合成樹脂板の片面または両面に貼着
する表面保護用シートとしては、紙基材１の片面
に水性糊剤の塗布層２を形成した表面保護用シー
トが用いられる。
表面保護用シートを構成する紙基材１として
は、両更クラフト紙、片艶クラフト紙、上質紙な
どが用いられるが、平滑性の良い片艶クラフト紙
が特に重要である。
紙基材１の重量は、20〜80g/m2程度が適当で
ある。
紙基材（殊に片艶クラフト紙）１は、JIS−Ｐ
−8112に規定する紙のステキヒト・サイズ度試験
方法による測定で２〜15秒のサイズ度を有するも
のであることが望ましい。サイズ度がこの範囲か
らはずれると、水分の吸収速度が過度に速くなつ
たり遅くなつたりするため、表面保護用シートを
製造する際に水性糊剤が浸透して紙基材の表面に
所定量の糊剤を確保できなかつたり、押圧圧着操
作時に未塗布ゾーン３による余分の水分の吸収が
円滑に行われなくなつたりする。
水性糊剤としては、ポリビニルアセテート部分
鹸化物系、澱粉系または水溶性セルロースエーテ
ル系の高分子を接着成分とする水性糊剤が適当で
あり、そのほかカゼインをはじめ種々の水溶性ま
たは水分散性の高分子が用いられる。
これらの中では、取扱い性や性能の点から、ポ
リビニルアセテート部分鹸化物、特に鹸化度が86
〜89.5モル％程度、重合度が400〜2500程度のも
のが実用上最も適している。なお、このポリビニ
ルアセテート部分鹸化物は、通常の製法によれば
少量の酢酸ナトリウムを含むが、メタノールなど
で抽出処理することにより、酢酸ナトリウム含有
量をさらに低減することもできる。
上述の高分子（殊にポリビニルアセテート部分
鹸化物）には、剥離性および再貼着性を向上させ
るために、多価アルコール（グリセリンなど）や
水性のアクリル系粘着剤を配合することが好まし
い。これらの配合は、均一接着性（貼着操作時の
非接着部発生の防止）の点でも有利である。多価
アルコールの配合割合は、ポリビニルアセテート
部分鹸化物100重量部に対し10〜150重量部程度、
水性のアクリル系粘着剤の配合割合は、ポリビニ
ルアセテート部分鹸化物100重量部に対し10〜400
重量部程度とすることが多い。
水性糊剤は、必要に応じ帯電防止剤、紫外線防
止剤、老化防止剤、防カビ剤、界面活性剤、充填
剤、着色剤などを含んでいてもよい。
紙基材１への水性糊剤の塗布量は、固形分で２
〜25g/m2、特に〜20g/m2の範囲に設定すること
が多いが、必ずしもこの範囲に限られるものでは
ない。
そして本発明においては、水性糊剤を紙基材１
の片面に塗布して塗布層２を形成させるに際し、
前記紙基材１の両側縁部に水性糊剤の未塗布ゾー
ン３，３を設ける。
未塗布ゾーン３の巾は、３〜15mmの範囲に設定
することが特に望ましい。この巾が３mm未満で
は、水性糊剤を再湿活性化し、ゴムロールで合成
樹脂板表面に押圧する際、押圧されるに従つて側
縁部に向けて流出される水性糊剤を溶解した余分
の水分の未塗布ゾーン３においての吸収が充分に
は行われなくなる。一方未塗布ゾーン３の巾が15
mmを越えると、表面保護用シートを合成樹脂板の
貼着する操作が困難になつたり、合成樹脂板へ貼
着後剥離現象を生ずることがある。
作 用
上記のようにして得られた表面保護用シートを
合成樹脂板に貼着するには、水性糊剤の塗布層２
が再湿活性を有するものであるため、保護用シー
トの塗布層２形成面側から加湿し、ついで保護用
シートを合成樹脂板に当てがつてゴムロールで圧
着する方法が採用される。加湿は高温の水蒸気の
吹付けによつて行うが、場合により、冷水の塗
布、温水の塗布によつて行うこともある。
水性糊剤の塗布層２の加湿を高温の水蒸気の吹
付けにより行い、ゴムロールによる押圧圧着時に
水性糊剤の表面に残存している余分の水分が合成
樹脂板の側縁部に向けて流出するようなことがあ
つても、その流出分は未塗布ゾーン３で紙基材１
に吸収されて合成樹脂板端面までには到達せず、
従つて合成樹脂板を汚染することがない。
合成樹脂板のトリミング残の再使用に際して
は、表面保護用シートがまだ貼着しているときは
これを剥離除去した後粉砕し、該粉砕物を単独で
あるいは新しい樹脂に混合して成形に供する。
この再使用品は通常であれば黄色ないし褐色に
変色するが、本発明の表面保護用シートを用いた
場合はほとんど変色を生じない。
実施例
次に実施例をあげて本発明をさらに説明する。
実施例
第１図は、本発明の表面保護用シートを合成樹
脂板の表面に貼着したときの一例を示した断面図
である。
図中、１は紙基材、２は水性糊剤の塗布層、３
は未塗布ゾーンであり、４は合成樹脂板である。
鹸化度88モル％、重合度1700のポリビニルアセ
テート部分鹸化物100重量部、グリセリン40重量
部および固形分45重量％ののアクリル系エマルジ
ヨン80重量部を適量の水に溶解して水性糊剤を調
製した。
紙基材１として、目付け49g/m2、JIS−Ｐ−
8112に規定する紙のステキヒト・サイズ度試験方
法によるサイズ度が５秒の巾1090mmの片艶クラフ
ト紙を用い、この片艶クラフト紙に上記の水性糊
剤を塗布し、熱風乾燥した。この際、片艶クラフ
ト紙の両側縁部の０mm（全面塗布）、２mm、３mm、
８mm、12mmまたは18mmの巾の部分は水性糊剤を塗
布しない未塗布ゾーン３とし、また塗布層２にお
ける水性糊剤の塗布量は固形分で８g/m2とした。
併せて、サイズ度がほぼ０秒およびサイズ度が
20秒の片艶クラフト紙についても、その両側縁部
の５mmの巾の部分を残して上記と同様に水性糊剤
の塗布を行つた。
合成樹脂板４の一例としての厚さ３mmのアクリ
ル板（ポリメチルメタクリレート板）を押出成形
しながら、その両面に上記で得た表面保護用シー
トを貼着していつた。貼着操作は、表面保護用シ
ートの水性糊剤塗布層２側に高温の水蒸気を吹付
けながら、ゴムロールで押圧圧着することにより
行つた。
次に、貼着後のアクリル板４の両側縁を化粧断
のためにトリミングし、該トリミング残を回収し
て粉砕し、押出機により再溶融して再生アクリル
板を成形した。
上記貼着時の状況および再生アクリル板の変色
の度合を目視観察した。
結果を第１表に示す。
第１表から、No.３、４、５および８の場合に、
最も良好な結果が得られることがわかる。
INDUSTRIAL APPLICATION FIELD The present invention relates to a surface protection sheet for attaching to the surface of a synthetic resin board such as an acrylic board to protect the surface. Prior Art For synthetic resin boards such as acrylic boards, vinyl chloride boards, polycarbonate boards, polystyrene boards, and ABS boards, it is important for the product value that the surfaces be smooth and beautiful. In order to prevent the surface of a synthetic resin board from being damaged during storage, transportation, or cutting, a surface protection sheet is pasted on one or both sides of the synthetic resin board. As one type of surface protection sheet for this purpose, one in which an aqueous sizing agent made of an aqueous solution of a partially saponified polyvinyl acetate is coated and layered on one side of a paper base material is used. In order to attach a surface protection sheet coated with a water-based glue to a synthetic resin board, high-temperature water vapor is applied to the water-based glue coating layer of the surface protection sheet, since this water-based glue is rewetting active. A commonly used method is to activate the resin by spraying it and press it onto the surface of a synthetic resin plate using a rubber roll. For inspection, the synthetic resin plate to which the surface protection sheet is attached may be partially peeled off and reattached. In this case, if an aqueous solution of only partially saponified polyvinyl acetate is used as an aqueous adhesive, re-adhesiveness will be insufficient, so polyhydric alcohol or water-based acrylic adhesive is added to the partially saponified polyvinyl acetate to improve releasability and Efforts are being made to improve re-adhesiveness. In addition, synthetic resin plates such as acrylic plates are trimmed to the specified dimensions, but in order to improve manufacturing yield, it is necessary to reuse the trimmed portion, in other words, crush the trimming residue and remove the trimmed parts. It is common practice to mold the pulverized product alone or by mixing it with new resin. Problems to be Solved by the Invention However, the above-mentioned aqueous sizing agent (an aqueous sizing agent made by adding polyhydric alcohol or water-based acrylic adhesive to partially saponified polyvinyl acetate) is applied and layered on one side of a paper base material. If a synthetic resin board with a protective sheet pasted is reused after trimming, the recycled synthetic resin board will turn yellow or brown due to the slight amount of water-based glue remaining on the surface of the synthetic resin board. There was a problem. The cause of this discoloration is that the surface protection sheet is activated by spraying high-temperature water vapor on the water-based adhesive layer side.
When press-bonding the surface of a synthetic resin board with a rubber roll,
As the excess moisture remaining on the surface of the water-based glue is pressed, it dissolves the water-based glue and flows out through both side edges of the paper base material to the end surface of the synthetic resin board, contaminating the synthetic resin board. This is thought to be because, as a result, a small amount of glue remains on the trimming residue. An object of the present invention is to provide a surface protection sheet that prevents discoloration of a recycled synthetic resin board when the trimming residue is reused. Means for Solving the Problems The present invention provides a surface protection sheet in which a coating layer 2 of an aqueous sizing agent is formed on one side of a paper base material 1, in which a water-based sizing agent is applied to both side edges of the paper base material 1. A surface protection sheet for protecting the surface of a synthetic resin board, characterized in that uncoated zones 3, 3 are provided.'' The present invention will be explained in detail below. Examples of the synthetic resin board in the present invention include various synthetic resin boards manufactured by extrusion molding or cast molding, such as an acrylic board, a vinyl chloride board, a polycarbonate board, a polystyrene board, and an ABS board.
Among these, extrusion molded acrylic plates (ie, polymethyl methacrylate plates) are particularly important because they undergo significant discoloration when recycled. As a surface protection sheet to be attached to one or both sides of such a synthetic resin board, a surface protection sheet in which a coating layer 2 of an aqueous glue is formed on one side of a paper base material 1 is used. As the paper base material 1 constituting the surface protection sheet, double-sided kraft paper, single-sided kraft paper, high-quality paper, etc. are used, but single-sided kraft paper with good smoothness is particularly important. The appropriate weight of the paper base material 1 is about 20 to 80 g/m 2 . Paper base material (especially single gloss kraft paper) 1 is JIS-P
It is desirable that the paper has a sizing degree of 2 to 15 seconds as measured by the Steckigt sizing test method for paper as specified in -8112. If the size is out of this range, the water absorption rate will be too fast or too slow, so when manufacturing surface protection sheets, the water-based glue will penetrate and deposit a predetermined amount on the surface of the paper base material. It may not be possible to secure the adhesive, or the uncoated zone 3 may not be able to absorb excess water smoothly during the pressure bonding operation. Suitable water-based glues include water-based glues containing partially saponified polyvinyl acetate, starch, or water-soluble cellulose ether-based polymers as adhesive components, as well as casein and other water-soluble or water-dispersible glues. Polymers are used. Among these, polyvinyl acetate partially saponified products, especially those with a saponification degree of 86, are preferred from the viewpoint of handling and performance.
~89.5 mol % and a polymerization degree of approximately 400 to 2,500 are most suitable for practical use. Although this partially saponified polyvinyl acetate product contains a small amount of sodium acetate according to a normal production method, the sodium acetate content can be further reduced by extraction treatment with methanol or the like. It is preferable to blend a polyhydric alcohol (such as glycerin) or a water-based acrylic adhesive into the above-mentioned polymer (especially partially saponified polyvinyl acetate) in order to improve removability and reattachability. These formulations are also advantageous in terms of uniform adhesion (prevention of non-adhesive areas during pasting operations). The blending ratio of polyhydric alcohol is approximately 10 to 150 parts by weight per 100 parts by weight of partially saponified polyvinyl acetate.
The mixing ratio of water-based acrylic adhesive is 10 to 400 parts by weight per 100 parts by weight of partially saponified polyvinyl acetate.
It is often about parts by weight. The aqueous sizing agent may contain an antistatic agent, an ultraviolet ray inhibitor, an antiaging agent, a fungicide, a surfactant, a filler, a coloring agent, and the like, as required. The amount of water-based sizing agent applied to paper base material 1 is 2 in terms of solid content.
Although it is often set in the range of ~25 g/m 2 , particularly ~20 g/m 2 , it is not necessarily limited to this range. In the present invention, the water-based sizing agent is applied to the paper base material 1.
When forming coating layer 2 by coating on one side of
Zones 3, 3 where no aqueous sizing agent is applied are provided on both side edges of the paper base material 1. It is particularly desirable that the width of the uncoated zone 3 is set in a range of 3 to 15 mm. If this width is less than 3 mm, when the aqueous sizing agent is re-wetted and activated and pressed onto the surface of the synthetic resin board with a rubber roll, the excess water-based sizing agent that dissolves and flows out toward the side edges as it is pressed is removed. Water is not absorbed sufficiently in the uncoated zone 3. On the other hand, the width of uncoated zone 3 is 15
If it exceeds mm, it may become difficult to attach the surface protection sheet to the synthetic resin plate, or the surface protection sheet may peel off after being attached to the synthetic resin plate. Function In order to adhere the surface protection sheet obtained as described above to a synthetic resin board, a coating layer of water-based glue 2.
Since it has rewetting activity, a method is adopted in which the protective sheet is humidified from the side on which the coating layer 2 is formed, and then the protective sheet is applied to a synthetic resin plate and pressed with a rubber roll. Humidification is performed by spraying high-temperature water vapor, but depending on the case, it may also be performed by applying cold water or hot water. The coating layer 2 of the water-based glue is humidified by spraying high-temperature steam, and the excess water remaining on the surface of the water-based glue flows out toward the side edges of the synthetic resin board during pressure bonding with a rubber roll. Even if something like this happens, the spilled water will be transferred to the paper substrate 1 in the uncoated zone 3.
is absorbed and does not reach the end surface of the synthetic resin plate,
Therefore, the synthetic resin plate is not contaminated. When reusing the trimming residue of a synthetic resin board, if the surface protection sheet is still attached, remove it and crush it, and use the crushed material alone or mixed with new resin for molding. . Normally, this reused product would discolor to yellow or brown, but when the surface protection sheet of the present invention is used, almost no discoloration occurs. Examples Next, the present invention will be further explained with reference to Examples. Example FIG. 1 is a sectional view showing an example of a surface protection sheet of the present invention adhered to the surface of a synthetic resin plate. In the figure, 1 is a paper base material, 2 is an aqueous glue coating layer, and 3 is a paper base material.
is an uncoated zone, and 4 is a synthetic resin plate. An aqueous sizing agent was prepared by dissolving 100 parts by weight of a partially saponified polyvinyl acetate with a degree of saponification of 88 mol% and a degree of polymerization of 1700, 40 parts by weight of glycerin, and 80 parts by weight of an acrylic emulsion with a solid content of 45% by weight in an appropriate amount of water. did. As paper base material 1, basis weight 49g/m 2 , JIS-P-
A single gloss kraft paper with a width of 1090 mm and a sizing degree of 5 seconds according to the Stekicht sizing test method specified in 8112 was used. The above water-based sizing agent was applied to the single gloss kraft paper and dried with hot air. At this time, 0mm (full coating), 2mm, 3mm,
A portion with a width of 8 mm, 12 mm or 18 mm was an uncoated zone 3 in which no aqueous adhesive was applied, and the amount of the aqueous adhesive applied in the coating layer 2 was 8 g/m 2 in terms of solid content. In addition, the size degree is almost 0 seconds and the size degree is
The water-based glue was applied to the 20-second single-gloss kraft paper in the same manner as above, leaving 5 mm wide portions on both sides of the paper. While extruding an acrylic plate (polymethyl methacrylate plate) having a thickness of 3 mm as an example of the synthetic resin plate 4, the surface protection sheet obtained above was adhered to both sides of the plate. The adhering operation was carried out by pressing and bonding with a rubber roll while spraying high-temperature steam onto the aqueous adhesive layer 2 side of the surface protection sheet. Next, both side edges of the acrylic board 4 after adhesion were trimmed for decorative cutting, and the trimming residue was collected, crushed, and remelted using an extruder to form a recycled acrylic board. The conditions at the time of attachment and the degree of discoloration of the recycled acrylic board were visually observed. The results are shown in Table 1. From Table 1, in the case of No. 3, 4, 5 and 8,
It can be seen that the best results can be obtained.
【表】
(1)のサイズ度。
実施例 ２〜３
水性糊剤として澱粉を接着成分とする水性糊剤
（実施例２）、水溶性セルロースエーテルを接着成
分とする水性糊剤（実施例３）を用いたほかは実
施例１と同様の実験を行つた結果、実施例１に準
ずる効果が得られた。
発明の効果
本発明の表面保護用シートを合成樹脂板に貼着
すると、合成樹脂板への押圧操作時に余分の水分
が水性糊剤を溶解しながら紙基材の両側縁部を通
つて合成樹脂板端面に流出して該合成樹脂板を汚
染することが確実に防止される。
そのため、トリミング残を単独であるいは新し
い樹脂に混合して再使用に供しても、再使用品の
黄変はほとんど認められず、製品価値の高いもの
となる。
従つて、従来であれば黄変のため再使用できな
かつたトリミング残の再使用が可能になり、ある
いは従来であれば新しい樹脂に混合するときの混
合比率がごく少量に制限されていたものがその混
合比率を上げることができるので、合成樹脂板の
製造コストが著しく低減する。
よつて本発明の表面保護用シートは、各種の合
成樹脂板、殊にアクリル板の表面保護の目的に好
適である。[Table] Size degree of (1).
Examples 2 to 3 Same as Example 1 except that a water-based glue containing starch as an adhesive component (Example 2) and a water-based glue containing water-soluble cellulose ether as an adhesive component (Example 3) were used as the water-based glue. As a result of conducting a similar experiment, effects similar to those of Example 1 were obtained. Effects of the Invention When the surface protection sheet of the present invention is adhered to a synthetic resin board, when the sheet is pressed onto the synthetic resin board, excess moisture dissolves the water-based glue and passes through both side edges of the paper base material to the synthetic resin. It is reliably prevented that the synthetic resin plate will be contaminated by flowing out to the end face of the plate. Therefore, even if the trimming residue is reused alone or mixed with new resin, yellowing of the reused product is hardly observed and the product value is high. Therefore, it is now possible to reuse trimming residue that could not be reused due to yellowing, or the mixing ratio of new resin, which was previously limited to a very small amount, can now be reused. Since the mixing ratio can be increased, the manufacturing cost of the synthetic resin board can be significantly reduced. Therefore, the surface protection sheet of the present invention is suitable for the purpose of protecting the surface of various synthetic resin boards, especially acrylic boards.
第１図は、本発明の表面保護用シートを合成樹
脂板の表面に貼着したときの一例を示した断面図
である。
１…紙基材、２…水性糊剤の塗布層、３…未塗
布ゾーン、４…合成樹脂板。
FIG. 1 is a sectional view showing an example of a surface protection sheet of the present invention adhered to the surface of a synthetic resin plate. DESCRIPTION OF SYMBOLS 1...Paper base material, 2...Coating layer of water-based glue, 3...Uncoated zone, 4...Synthetic resin board.
Claims (1)
した表面保護用シートにおいて、前記紙基材１の
両側縁部に水性糊剤の未塗布ゾーン３，３を設け
たことを特徴とする合成樹脂板の表面を保護する
ための表面保護用シート。 ２ 紙基材１の側縁部に設けた未塗布ゾーン３の
巾が３〜15mmである特許請求の範囲第１項記載の
表面保護用シート。 ３ 紙基材１が、JIS−Ｐ−8112に規定する紙の
ステキヒト・サイズ度試験方法による測定で２〜
15秒のサイズ度を有するものである特許請求の範
囲第１項記載の表面保護用シート。 ４ 紙基材１が、片艶クラフト紙である特許請求
の範囲第１項記載の表面保護用シート。 ５ 水性糊剤が、ポリビニルアセテート部分鹸化
物系、澱粉系または水溶性セルロースエーテル系
の高分子を接着成分とする水性糊剤である特許請
求の範囲第１項記載の表面保護用シート。[Scope of Claims] 1. In a surface protection sheet in which a coating layer 2 of an aqueous sizing agent is formed on one side of a paper base 1, zones 3, 3 where no aqueous sizing agent is applied are formed on both side edges of the paper substrate 1. A surface protection sheet for protecting the surface of a synthetic resin board, characterized in that it is provided with. 2. The surface protection sheet according to claim 1, wherein the width of the uncoated zone 3 provided on the side edge of the paper base material 1 is 3 to 15 mm. 3 Paper base material 1 has a rating of 2 to 2 as measured by the Steckigt sizing test method for paper specified in JIS-P-8112.
The surface protection sheet according to claim 1, which has a size degree of 15 seconds. 4. The surface protection sheet according to claim 1, wherein the paper base material 1 is single-gloss kraft paper. 5. The surface protection sheet according to claim 1, wherein the aqueous sizing agent is an aqueous sizing agent whose adhesive component is a partially saponified polyvinyl acetate-based, starch-based, or water-soluble cellulose ether-based polymer.