JPH0421437A - Laminated sheet for electrical use - Google Patents
Laminated sheet for electrical useInfo
- Publication number
- JPH0421437A JPH0421437A JP12784190A JP12784190A JPH0421437A JP H0421437 A JPH0421437 A JP H0421437A JP 12784190 A JP12784190 A JP 12784190A JP 12784190 A JP12784190 A JP 12784190A JP H0421437 A JPH0421437 A JP H0421437A
- Authority
- JP
- Japan
- Prior art keywords
- metal foil
- film
- necessary
- electrical
- pressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は電子機器、電気機器、コンピューター、通信機
器等に用いられる電気用積層板に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to an electrical laminate used in electronic equipment, electrical equipment, computers, communication equipment, etc.
従来の弗素樹脂からなる電気用積層板は、弗素樹脂エマ
ルジョンを基材に含浸、乾燥することを反復して所要樹
脂量を基材に付着させて得られるものであるが、基材へ
の樹脂含浸性が悪く電気性能のバラツキ、反りが大きく
なる問題があった。Conventional electrical laminates made of fluororesin are obtained by repeatedly impregnating and drying a base material with a fluororesin emulsion to adhere the required amount of resin to the base material. There were problems with poor impregnating properties, variations in electrical performance, and increased warping.
〔発明が解決しようとする問題点]
従来の技術で述べたように弗素樹脂エマルジョンを基材
に含浸、乾燥してなるプリプレグを用いた電気用積層板
は電気性能のバラツキ、反りが太き(なる問題点がある
。本発明は実施例の技術における上述の問題点に鑑みて
なされたもので、その目的とするところは電気性能のバ
ラツキ及び反りの少ない電気用積層板を提供することに
ある。[Problems to be Solved by the Invention] As described in the prior art, electrical laminates using prepreg made by impregnating and drying a fluororesin emulsion into a base material have variations in electrical performance and large warpage ( The present invention has been made in view of the above-mentioned problems in the technology of the embodiments, and its purpose is to provide an electrical laminate with less variation in electrical performance and less warpage. .
本発明は所要枚数の基材の各上面及び又は下面に弗素樹
脂フィルムを配し、更に必要に応じて最外層に金属箔を
配設した積層体を一体化してなることを特徴とする電気
用積層板のため、基材に溶融樹脂が圧入されるので基材
への樹脂の含浸が均一となり電気性能のバラツキ、反り
を少なくすることができたもので、以下本発明の詳細な
説明する。The present invention is an electrical product characterized by integrating a laminate in which a required number of base materials are each provided with a fluororesin film on the upper and/or lower surfaces, and if necessary, a metal foil is provided on the outermost layer. Because it is a laminate, the molten resin is press-fitted into the base material, so that the base material is uniformly impregnated with the resin, reducing variations in electrical performance and warping.The present invention will be described in detail below.
本発明に用いる基材としてはガラス、アスベスト等の無
機繊維やポリエステル、ポリアクリル、ポリビニルアル
コール、ポリアミド、ポリイミド、ポリフェニレンサル
ファイド、ポリウレタン等の有機合成繊維や木綿等の天
然繊維からなる織布、不織布、77)或いは祇又はこれ
等の組合せ基材で基材は予じめカンプリング剤等で処理
しておくこともできる。弗素樹脂フィルムとしては、四
弗化エチレン樹脂、四弗化エチレンパーフルオロビニル
エーテル共重合体、四弗化エチレン六弗化プロピレン共
重合体、四弗化エチレンエチレン共重合体、三弗化塩化
エチレン樹脂等のように弗素樹脂全般のフィルムを用い
ることができる。フィルムの厚みはO,OO5〜0.5
mmが好ましく、必要に応じて弗素樹脂には水酸化ア
ルミニウム、タルク、シリカ、アルミナ、炭酸カルシウ
ム、炭酸マグネシウム等の無機充填剤やガラス繊維チッ
プ、アスベスト、木粉、パルプ、綿粉等の繊維質充填剤
を添加することもできる。金属箔としては銅、アルミニ
ウム、鉄、ニンケル、亜鉛等の単独、合金、複合箔が用
いられ、必要に応じて金属箔の片面に接着剤層を設けて
おき、より接着性を向上させることもできる。一体止手
段としてはプレス、多段プレス、マルチロール等が用い
られる。The base materials used in the present invention include woven fabrics, non-woven fabrics made of inorganic fibers such as glass and asbestos, organic synthetic fibers such as polyester, polyacrylic, polyvinyl alcohol, polyamide, polyimide, polyphenylene sulfide, and polyurethane, and natural fibers such as cotton; 77) Alternatively, the base material may be treated with a compulsing agent or the like in advance using a base material made of Mizuki or a combination thereof. Examples of fluororesin films include tetrafluoroethylene resin, tetrafluoroethylene perfluorovinyl ether copolymer, tetrafluoroethylene hexafluoropropylene copolymer, tetrafluoroethylene ethylene copolymer, and trifluorochloride ethylene resin. Any film made of fluororesin can be used, such as the following. The thickness of the film is O, OO5~0.5
mm is preferable, and if necessary, the fluororesin may contain inorganic fillers such as aluminum hydroxide, talc, silica, alumina, calcium carbonate, magnesium carbonate, etc., and fibrous materials such as glass fiber chips, asbestos, wood powder, pulp, and cotton powder. Fillers can also be added. As the metal foil, single, alloy, or composite foils of copper, aluminum, iron, nickel, zinc, etc. are used, and if necessary, an adhesive layer can be provided on one side of the metal foil to further improve adhesiveness. can. As the unitary fixing means, a press, a multi-stage press, a multi-roll, etc. are used.
以下本発明を実施例にもとづいて説明する。The present invention will be explained below based on examples.
〔実施例1〕
厚さ0.15mmのガラス布7枚の各層間及び最外層に
厚さ0.1mmの四弗化エチレン六弗化プロピレン共重
合体フィルム(ダイキン工業株式会社製、ネオフロンフ
ィルム)を配し、更に最外層に厚さ0.035mmの接
着剤付銅箔の接着剤側をフィルムと対向させて夫々配設
した積層体を成形圧力2゜kg/cd、280℃で60
分間プレスで積層成形して厚さ1.2閣の電気用積層板
を得た。[Example 1] A 0.1 mm thick tetrafluoroethylene hexafluoropropylene copolymer film (manufactured by Daikin Industries, Ltd., Neoflon Film ), and the outermost layer was a 0.035 mm thick adhesive-coated copper foil with the adhesive side facing the film.
An electrical laminate with a thickness of 1.2 mm was obtained by lamination molding using a minute press.
実施例と同じ四弗化エチレン六弗化プロピレン共重合体
エマルジョンを樹脂量が30重量%になるように厚さ0
.15mのガラス布に含浸、乾燥したプリプレグ7枚を
重ね、更にその最外層に実施例と同じF4箔を夫々配設
した積層体を実施例と同様に処理して厚さ1.2mmの
電気用積層板を得た。The same tetrafluoroethylene hexafluoropropylene copolymer emulsion as in the example was prepared to a thickness of 0 so that the resin amount was 30% by weight.
.. A laminate in which 7 sheets of impregnated and dried prepreg were stacked on a 15 m long glass cloth, and the same F4 foil as in the example was placed on each of the outermost layers was treated in the same manner as in the example to produce a 1.2 mm thick electrical grade. A laminate was obtained.
実施例及び比較例の電気用積層板の性能は第1表のよう
である。The performance of the electrical laminates of Examples and Comparative Examples is shown in Table 1.
第
表
〔発明の効果〕
本発明は上述した如く構成されている。特許請求の範囲
に記載した構成を有する電気用積層板においては電気性
能のバラツキ、反りが少なくなる効果がある。Table 1 [Effects of the Invention] The present invention is constructed as described above. The electrical laminate having the structure described in the claims has the effect of reducing variations in electrical performance and warping.
Claims (1)
脂フイルムを配し、更に必要に応じて最外層に金属箔を
配設した積層体を一体化してなることを特徴とする電気
用積層板。(1) An electrical device characterized by being formed by integrating a laminate in which a fluororesin film is arranged on the upper and/or lower surfaces of each of the required number of base materials, and if necessary, a metal foil is arranged on the outermost layer. laminate board.