JPH03120040A - Decoration metal plate - Google Patents
Decoration metal plateInfo
- Publication number
- JPH03120040A JPH03120040A JP25957689A JP25957689A JPH03120040A JP H03120040 A JPH03120040 A JP H03120040A JP 25957689 A JP25957689 A JP 25957689A JP 25957689 A JP25957689 A JP 25957689A JP H03120040 A JPH03120040 A JP H03120040A
- Authority
- JP
- Japan
- Prior art keywords
- pattern
- metal plate
- stereoscopic
- decorative
- coating film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
［産業上の利用分野〕
本発明は建築、構築物の内、外壁材の表面材として有用
な金属薄板の化粧面に、隆起印刷により任意模様を形成
し、この表面全面を化粧塗膜で被覆することにより立体
的な意匠性と耐候性とを付加した化粧金属板に関するも
のである。[Detailed Description of the Invention] [Industrial Application Field] The present invention involves forming an arbitrary pattern by raised printing on the decorative surface of a thin metal plate useful as a surface material for exterior wall materials in buildings and structures, and applying the pattern to the entire surface. The present invention relates to a decorative metal plate that is coated with a decorative coating film to provide three-dimensional design and weather resistance.
（従来の技術］
一般に、建築、構築物の内、外壁の表面材としては金属
））■仮、例えばカラー鋼板、角波、プリント鋼板、サ
ンドイッチ構造のサイデイング材、サンドイッチパネル
等が使用されている。(Prior Art) In general, metals are used as surface materials for internal and external walls of buildings and structures, such as colored steel plates, square corrugations, printed steel plates, sandwich structure siding materials, and sandwich panels.
しかしながら、この種建材は、化粧面がフラットで、か
つ立体感に欠は美観に劣る欠点があった。However, this type of building material has the disadvantage that the decorative surface is flat, lacks a three-dimensional effect, and is poor in aesthetic appearance.
また、プリント鋼板は印刷により模様が施されているが
、化粧面はフラットであり、上記欠点を幾分、近視距離
から見た際に改善したにすぎず、さらに、立体感を付与
した例としてはエンボス加工を施した化粧金属板が知ら
れている。しかしながら、このエンボス加工はエンボス
ロール、金属薄板の材質の関係で板材が歪んだり、捻し
れたりする変形のため模様の形状が大幅に制限されると
共に、エンボス深さもあまり深く形成できず、立体感に
欠ける不利があった。In addition, printed steel plates have patterns printed on them, but the decorative surface is flat, which only improves the above-mentioned drawbacks when viewed from a near-sighted distance. is known for its embossed decorative metal plates. However, with this embossing process, the shape of the pattern is greatly limited due to the deformation of the plate material such as distortion or twisting due to the material of the embossing roll and the thin metal plate, and the depth of the embossing cannot be formed very deep, resulting in a three-dimensional effect. There was a disadvantage that it lacked.
〔課題を解決するための手段］
本発明はこのような欠点を除去するため、金属薄板から
なる基板の少なくとも一表面に隆起印刷による模様を施
し、この表面全面を上記模様の隆起を損ねることなしに
化粧塗膜で被覆し、立体感があり、かつ模様に限定され
ない任意模様が形成でき、その上化粧面の耐候性、耐食
性および加工性を大幅に改善した化粧金属板を提供する
。[Means for Solving the Problems] In order to eliminate such drawbacks, the present invention applies a pattern by ridge printing on at least one surface of a substrate made of a thin metal plate, and prints a pattern on the entire surface without impairing the ridges of the pattern. To provide a decorative metal plate which is coated with a decorative coating film, has a three-dimensional effect, can form any pattern not limited to patterns, and has greatly improved weather resistance, corrosion resistance and workability of the decorative surface.
〔実施例］
以下に、図面を用いて本発明に係る化粧金属板の一実施
例について詳細に説明する。すなわち、本発明に係る化
粧金属板上は第１図（ａ）、（ｂ）に拡大して示すよう
に基板２の少なくとも一表面２ａに隆起印刷等により立
体模様３を形成し、この立体模様３を含む表面に化粧塗
膜６を設け、この化粧塗膜６が立体模様３を埋設しない
厚さで被覆するものである。さらに説明すると、基板２
は平板状の亜鉛鉄板、カラー鋼板、ガルファン、ガルバ
リウム鋼板、アルミ・亜鉛メツキ鋼板、ステンレス板、
アルミニウム板、銅板の１種からなり、その厚さは０．
２７〜１．６ｍｍ位である。勿論、基板２は所用断面形
状にロール成形、プレスにより形成されるものである。[Example] Hereinafter, an example of the decorative metal plate according to the present invention will be described in detail with reference to the drawings. That is, on the decorative metal plate according to the present invention, as shown enlarged in FIGS. 1(a) and 1(b), a three-dimensional pattern 3 is formed on at least one surface 2a of the substrate 2 by raised printing or the like. A decorative coating film 6 is provided on the surface including the three-dimensional pattern 3, and this decorative coating film 6 covers the three-dimensional pattern 3 with a thickness that does not embed it. To explain further, substrate 2
flat galvanized iron plates, colored steel plates, galvanized steel plates, galvanized steel plates, aluminum/galvanized steel plates, stainless steel plates,
It is made of one type of aluminum plate or copper plate, and its thickness is 0.
It is about 27 to 1.6 mm. Of course, the substrate 2 is formed into the desired cross-sectional shape by roll forming or pressing.
立体模様３は塗料４ａをインクジェット方式で形成した
もの、あるいはインク５の上に合成樹脂パウダー４（以
下、単にパウダーという）を塗布し、これを溶融し、焼
成したもの等であり、膜厚は１００〜１０００ミクロン
位で、立体感を出すものである。この立体模様３は任意
模様を印刷等により形成する。なお、前記塗料４ａ、パ
ウダー４はポリエステル樹脂、アクリル樹脂、ポリエチ
レン樹脂、シリコンポリエステル樹脂、フッソ樹脂、Ｐ
ＶＡ、ナイロン１２、フェノール樹脂、ウレタン樹脂等
のように一般に塗膜のビヒクルとなるものであればよい
。化粧塗膜６は上記した塗料の他、エポキシ樹脂、ポリ
スチレン、酢酸ビニル樹脂等の１種以上からなる。勿論
、透明塗料、着色塗料のいずれをも使用できる。The three-dimensional pattern 3 is formed by forming a paint 4a using an inkjet method, or by applying synthetic resin powder 4 (hereinafter simply referred to as powder) on top of the ink 5, melting it, and baking it, etc., and the film thickness is as follows: It is about 100 to 1000 microns and gives a three-dimensional effect. This three-dimensional pattern 3 is formed by printing an arbitrary pattern. The paint 4a and powder 4 are polyester resin, acrylic resin, polyethylene resin, silicone polyester resin, fluorine resin, P
Any material that generally serves as a vehicle for the coating film may be used, such as VA, nylon 12, phenol resin, urethane resin, etc. The decorative coating film 6 is made of one or more of epoxy resin, polystyrene, vinyl acetate resin, etc. in addition to the above-mentioned paints. Of course, either transparent paint or colored paint can be used.
次に製造法につき簡単に説明する。いま、第２図に示す
ように基板２の一表面２ａに、例えばアルファベット文
字Ａ、Ｂ、Ｃ・・・等を隆起印刷により立体模様３を形
成すると仮定する。そこで、−表面２ａにインク５を介
してアルファベットを印刷し、その上にナイロン１２よ
りなるパウダー４を塗布し、余分なパウダー４は回収す
る。次にインク５とパウダー４はヒータにより３００〜
４００’Ｃの炉内にて焼成され、高さ５００ミクロンの
立体模様３を形成する。次にポリエステル樹脂をビヒク
ルとした塗料よりなる化粧塗膜６を表面にウェットで３
０ミクロン塗布し、２００〜３００℃の炉内に送給し、
焼成して完了する。Next, the manufacturing method will be briefly explained. Now, it is assumed that a three-dimensional pattern 3 is formed on one surface 2a of the substrate 2 by, for example, alphabetical letters A, B, C, etc. by raised printing, as shown in FIG. Therefore, an alphabet is printed on the surface 2a using ink 5, and powder 4 made of nylon 12 is applied thereon, and the excess powder 4 is collected. Next, ink 5 and powder 4 are heated to 300~
It is fired in a furnace at 400'C to form a three-dimensional pattern 3 with a height of 500 microns. Next, a decorative coating film 6 made of a paint containing polyester resin as a vehicle is wet applied to the surface.
0 micron coating, fed into a furnace at 200-300℃,
Finish by baking.
上記化粧金属板上はフラット板に印刷した従来のプリン
ト鋼板に比べ立体感に冨み、かつ耐候性もすぐれていた
。特に、カラー鋼板上に、さらに立体模様３を形成した
際には、耐候性は抜群である。しかも、模様は印刷と同
様に微細な点まで形成でき、模様に制限を受けることが
なかった。The above-mentioned decorative metal plate had a richer three-dimensional effect and better weather resistance than conventional printed steel plates printed on flat plates. In particular, when the three-dimensional pattern 3 is further formed on the colored steel plate, the weather resistance is excellent. Moreover, the pattern can be formed down to the minute dots in the same way as with printing, and there are no restrictions on the pattern.
〔発明の効果］
上述したように本発明に係る化粧金属板によれば、■立
体ｖＡ様は印刷のため形状に制限がな（、任意模様を形
成できる。■立体模様と基板と化粧塗膜の一体化が確実
に図れ、塗膜が剥落したり、ツクしたり、クラックが入
ったりすることがなく、耐候性、耐水性にすぐれる。■
立体模様はエンボス加工、フラット板と異なる立体感が
あり、希有な外観を呈する。■低コストで、かつ容易に
製造できる。等の特徴がある。[Effects of the Invention] As described above, according to the decorative metal plate of the present invention, there is no restriction on the shape of the three-dimensional vA because it is printed (and any pattern can be formed). ■ The three-dimensional pattern, the substrate, and the decorative coating film The coating is reliably integrated, the paint film does not peel off, tack, or crack, and it has excellent weather and water resistance.■
The three-dimensional pattern has a three-dimensional effect that is different from embossed or flat plates, giving it a rare appearance. ■Low cost and easy to manufacture. It has the following characteristics.
第１図（ａ）、（ｂ）は本発明に係る化粧金属板の一部
を拡大して示す断面図、第２図は上記化粧金属板の一例
を示す斜視図である。
上・・・化粧金属板、２・・・′基板、３・・・立体模
様、６・・・化粧塗膜。FIGS. 1(a) and 1(b) are enlarged sectional views showing a part of the decorative metal plate according to the present invention, and FIG. 2 is a perspective view showing an example of the decorative metal plate. Top... Decorative metal plate, 2...' substrate, 3... Three-dimensional pattern, 6... Decorative coating film.
Claims (1)
ウダ状の合成樹脂とから厚さ１００〜１０００ミクロン
程度の隆起印刷により立体模様を形成し、該模様を含む
表面を化粧塗膜で上記立体模様に対応して被覆したこと
を特徴とする化粧金属板。(1) A three-dimensional pattern is formed on one surface of a thin metal plate substrate using ink and a powdered synthetic resin by printing raised bumps with a thickness of approximately 100 to 1000 microns, and the surface containing the pattern is coated with a decorative coating. A decorative metal plate characterized by being coated in accordance with the three-dimensional pattern.