JPH0288659A - Colored thermoplastic resin composition and production thereof - Google Patents
Colored thermoplastic resin composition and production thereofInfo
- Publication number
- JPH0288659A JPH0288659A JP23898088A JP23898088A JPH0288659A JP H0288659 A JPH0288659 A JP H0288659A JP 23898088 A JP23898088 A JP 23898088A JP 23898088 A JP23898088 A JP 23898088A JP H0288659 A JPH0288659 A JP H0288659A
- Authority
- JP
- Japan
- Prior art keywords
- bis
- pts
- fatty acid
- acid amide
- alkylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
(産業上の利用分野)
本発明は、便座等の衛生機器、電話機、家電製品のハウ
ジング等の各種成形品の製造用材料として有用な着色し
たスチレン系樹脂の組成物及びその製造方法に関する。Detailed Description of the Invention (Field of Industrial Application) The present invention relates to a colored styrene resin composition useful as a material for manufacturing various molded products such as sanitary appliances such as toilet seats, telephones, and housings for home appliances. and its manufacturing method.
(従来の技術)
ABS樹脂に代表されるゴム含有スチレン系樹脂は機械
的性質の均衡に優れているので、各種製品の成形材料と
して広く使用されているが、その場合特に色外観が重要
視されることが多い。(Prior art) Rubber-containing styrenic resins, typified by ABS resins, have excellent balance of mechanical properties and are therefore widely used as molding materials for various products, but in this case color appearance is particularly important. Often.
そして、ABS樹脂を製造する場合、加工性や流動性を
向上させるため滑剤のアルキレン−ビス脂肪酸アミドを
樹脂中に添加することが多い。When producing ABS resin, alkylene-bis fatty acid amide as a lubricant is often added to the resin in order to improve processability and fluidity.
このようなアルキレン−ビス−脂肪酸アミドを含有する
ABS樹脂を着色する場合、通常酸化チタンをベースと
した各棟梁、顔料着色剤が用いられ、この際酸化チタン
等染、顔料を樹脂中に均一に分散させるために脂肪酸金
属塩等の分散剤が使用れる。When coloring ABS resin containing such alkylene-bis-fatty acid amide, a pigment coloring agent based on titanium oxide is usually used. A dispersant such as a fatty acid metal salt is used for dispersion.
ところが、着色剤として酸化チタンを含有し、そして脂
肪酸金属塩等の分散剤を含有する着色ABS樹脂を射出
成形機にて成形すると、なぜか成品に黒いすしが発生す
る場合がしばしばある。この外観不良現象を黒条と称し
ている。However, when a colored ABS resin containing titanium oxide as a colorant and a dispersant such as a fatty acid metal salt is molded using an injection molding machine, black stains often appear on the product for some reason. This phenomenon of poor appearance is called black streaks.
(発明が解決しようとする課B)
本発明は、ABS樹脂に代表されるスチレン系樹脂の着
色した成形品に観察される黒条発生の不良現象を解決す
ることを目的としている。(Problem B to be Solved by the Invention) The present invention aims to solve the defective phenomenon of black streaks observed in colored molded products of styrenic resins, typified by ABS resins.
(課題を解決するための手段)
本発明は、
(1)アルキレン−ビス−脂肪酸アミドを含有するスチ
レン系樹脂を、酸化アルミニウムで表面処理された酸化
チタンを必須成分とする着色剤で着色した樹脂組成物に
おいて、着色剤の分散剤としてアルキレン−ビス−脂肪
酸アミド及び/又は脂肪酸亜鉛を使用して着色したこと
を特徴とした着色樹脂組成物、及び
(2) アルキレン−ビス−脂肪酸アミドを含有する
スチレン系樹脂に、酸化アルミニウムで表面処理された
酸化チタンを必須成分とする着色剤と、′た樹脂組成物
の製造方法
に関するものである。(Means for Solving the Problems) The present invention provides: (1) A resin in which a styrene resin containing an alkylene-bis-fatty acid amide is colored with a coloring agent whose essential component is titanium oxide that has been surface-treated with aluminum oxide. A colored resin composition characterized in that the composition is colored using an alkylene-bis-fatty acid amide and/or a fatty acid zinc as a dispersant for a colorant, and (2) containing an alkylene-bis-fatty acid amide. The present invention relates to a method for producing a resin composition containing a styrene resin and a coloring agent containing titanium oxide surface-treated with aluminum oxide as an essential component.
本発明に用いるスチレン系樹脂は特に制限はなく、具体
例を示すなら、アクリロニトリループクジエン−スチレ
ン共重合体、アクリロニトリルブタジェン−α−メチル
−スチレン共重合体、ポリスチレン、アクリロニトリル
−スチレン共重合体、及びこれらのブレンド物等があげ
られる。The styrenic resin used in the present invention is not particularly limited, and specific examples include acrylonitrile-butadiene-styrene copolymer, acrylonitrile-butadiene-α-methyl-styrene copolymer, polystyrene, and acrylonitrile-styrene copolymer. , and blends thereof.
又、本発明に用いる酸化チタンの粒径には制限はなく、
普通粒子(0,2〜0.3μm)から微粒子(0,01
〜0.02μm)まであらゆる大きさのものを使用でき
る。通常用いる酸化チタンの表面処理剤量は、酸化チタ
ン100重量部に対し酸化アルミニウム0.1〜7重量
部である。Furthermore, there is no limit to the particle size of titanium oxide used in the present invention,
From ordinary particles (0.2 to 0.3 μm) to fine particles (0.01
Any size can be used, up to 0.02 μm). The amount of the titanium oxide surface treatment agent usually used is 0.1 to 7 parts by weight of aluminum oxide per 100 parts by weight of titanium oxide.
このような酸化チタンをスチレン系樹脂に添加する際に
は分散剤を使用するが、使用する分散剤はアルキレン−
ビス−脂肪酸アミド及び/又は脂肪酸亜鉛であれば特に
問題はなく、具体例を示すなら、前者はメチレン−ビス
−ステアリルアミド、エチレン−ビス−ステアリルアミ
ド等が使用され、かつこれらは樹脂の滑剤としても作用
する。後者はステアリン酸亜鉛、ラウリン酸亜鉛、リシ
ノール酸亜鉛、2−エチル−ヘキソイン酸亜鉛等が使用
される。又、必要に応じて、酸化チタン以外の着色剤、
耐候(光)剤、酸化防止剤、可塑剤、湿潤剤、分散樹脂
等の添加物を加えることもできる。A dispersant is used when adding titanium oxide to styrenic resin, but the dispersant used is alkylene-based.
There is no particular problem as long as it is a bis-fatty acid amide and/or a fatty acid zinc.To give a specific example, methylene-bis-stearylamide, ethylene-bis-stearylamide, etc. are used for the former, and these are used as a lubricant for the resin. also works. As the latter, zinc stearate, zinc laurate, zinc ricinoleate, zinc 2-ethyl-hexoate, etc. are used. Also, if necessary, colorants other than titanium oxide,
Additives such as weathering (light) agents, antioxidants, plasticizers, wetting agents, and dispersion resins can also be added.
例えば、耐候(光)剤としては特に制限はなく、具体例
を示すなら、ヒンダードアミン系、ベンゾフェノン系、
ベンゾトリアゾール系等が使用される。又、酸化防止材
としては特に制限はな(、具体例を示すなら、フェノー
ル系、ヒンダードフェノール系等が使用される。For example, there are no particular restrictions on weathering (light) agents; specific examples include hindered amine, benzophenone,
Benzotriazole and the like are used. Further, there are no particular restrictions on the antioxidant (specific examples include phenol type, hindered phenol type, etc.).
酸化チタンの樹脂への添加量については、樹脂100重
量部に対し0.1〜10重量部が好ましく、更に好まし
くは0.5〜5.0重量部であるが、0.1重量部より
少ないと着色が不十分であり、10重量部を超えると樹
脂の強度低下を引き起こす。The amount of titanium oxide added to the resin is preferably 0.1 to 10 parts by weight, more preferably 0.5 to 5.0 parts by weight, but less than 0.1 parts by weight. If the amount exceeds 10 parts by weight, the strength of the resin will decrease.
又、アルキレン−ビス−脂肪酸アミドの樹脂への添加量
については、樹脂100重量部に対し0、1〜2重量部
が好ましいが、0.1重量部より少ないと着色剤の分散
が不十分であり、2重量部を超えると押出機にてペレッ
ト化が困難となる不具合が生じる。The amount of alkylene-bis-fatty acid amide added to the resin is preferably 0.1 to 2 parts by weight per 100 parts by weight of the resin, but if it is less than 0.1 part by weight, the colorant will not be sufficiently dispersed. However, if it exceeds 2 parts by weight, it becomes difficult to pelletize using an extruder.
又、脂肪酸亜鉛の樹脂への添加量については、樹脂10
0重量部に対し0.1〜2重量部が好ましいが、0.1
重量部より少ないと着色剤の分散が不十分であり、2重
量部を超えると押出機にてペレット化が困難となる不具
合が生じる。In addition, regarding the amount of fatty acid zinc added to the resin, resin 10
0.1 to 2 parts by weight is preferred, but 0.1 parts by weight
If it is less than 2 parts by weight, the colorant will not be sufficiently dispersed, and if it exceeds 2 parts by weight, it will be difficult to pelletize in an extruder.
(実施例)
以下、実施例及び比較例によって本発明を更に詳しく説
明する。実施例及び比較例中に記載される部はすべて重
晋基準で示した。(Examples) Hereinafter, the present invention will be explained in more detail with reference to Examples and Comparative Examples. All parts described in Examples and Comparative Examples are based on Chongjin standards.
実施例1〜11
ABS樹脂(滑剤を含まないABS樹脂100部にアル
キレン−ビス−ステアリルアミド(EBS)を1.0部
添加した)100部と、表−1に示した酸化チタン、分
散剤、分散樹脂及び補色剤を、押出機に供給し、シリン
ダー設定温度220〜230℃にて混練し、9種の着色
ベレット(樹脂組成物)を得た。Examples 1 to 11 100 parts of ABS resin (1.0 part of alkylene-bis-stearylamide (EBS) was added to 100 parts of ABS resin that does not contain a lubricant), titanium oxide shown in Table 1, a dispersant, The dispersion resin and complementary coloring agent were supplied to an extruder and kneaded at a cylinder temperature of 220 to 230°C to obtain nine types of colored pellets (resin compositions).
このペレットを東芝機械側製lS−80CNV射出成形
機により成形し、100mmX 100mmX2mmの
平板状成形品を50枚作製した。The pellets were molded using an IS-80CNV injection molding machine manufactured by Toshiba Machine Co., Ltd. to produce 50 flat molded products measuring 100 mm x 100 mm x 2 mm.
この時の成形条件を次に示す。The molding conditions at this time are shown below.
(1) シリンダー設定温度=220“C(2)
F CV : 40mm/5ec(3)スクリュー回転
数:60r、10m。(1) Cylinder set temperature = 220"C (2)
F CV: 40mm/5ec (3) Screw rotation speed: 60r, 10m.
(4)耐圧: 60〜70 kg/cJ(5) 背圧
:Qkg/c己
(6) 計量ストローク:60〜70mm(7)金型
温度:50°C
得られた成形品の黒条発生状態を観察し、黒条の発生し
た成形品の枚数を調べた。結果を表−1に示す。(4) Pressure resistance: 60-70 kg/cJ (5) Back pressure: Qkg/cJ (6) Metering stroke: 60-70 mm (7) Mold temperature: 50°C Condition of black streaks in the obtained molded product The number of molded products with black streaks was determined. The results are shown in Table-1.
比較例1〜11
ABS樹脂(滑剤を含まないABS樹脂100ト(樹脂
組成物)を得た。Comparative Examples 1 to 11 100 ABS resins (resin compositions) containing no lubricant were obtained.
以下、実施例と同様にして平板状成形品を作製し、黒条
発生状態を観察した。結果を表−2に示す。Hereinafter, flat molded products were produced in the same manner as in the examples, and the state of black streak formation was observed. The results are shown in Table-2.
但し、表中のZn−3tはステアリン酸亜鉛、EB−3
はエチレン−ビス−ステアリルアミド、Mg−3tはス
テアリン酸マグネシウムを意味する。又、PSは低分子
量ポリスチレン、ASはアクリロニトリル−スチレン共
重合体を意味する。However, Zn-3t in the table is zinc stearate, EB-3
means ethylene-bis-stearylamide, and Mg-3t means magnesium stearate. Further, PS means low molecular weight polystyrene, and AS means acrylonitrile-styrene copolymer.
補色剤を押出機に供給し、シリンダー設定温度220〜
230“Cにて混練し、9種の着色ペレソ(発明の効果
)
本発明の着色されたスチレン系樹脂組成物は、成形時に
観察される黒条発生が解消された非常に有用なものであ
る。Supply the complementary color agent to the extruder and set the cylinder temperature to 220~
The colored styrenic resin composition of the present invention was kneaded at 230"C and colored in 9 types (effects of the invention). The colored styrenic resin composition of the present invention is very useful because it eliminates the appearance of black streaks observed during molding. .
Claims (2)
レン系樹脂を、酸化アルミニウムで表面処理された酸化
チタンを必須成分とする着色剤で着色した樹脂組成物に
おいて、着色剤の分散剤としてアルキレン−ビス−脂肪
酸アミド及び/又は脂肪酸亜鉛を使用して着色したこと
を特徴とした着色樹脂組成物。(1) In a resin composition in which a styrene resin containing an alkylene-bis-fatty acid amide is colored with a coloring agent whose essential component is titanium oxide surface-treated with aluminum oxide, the alkylene-bis-fatty acid amide is used as a dispersant for the colorant. - A colored resin composition characterized in that it is colored using fatty acid amide and/or fatty acid zinc.
レン系樹脂に、酸化アルミニウムで表面処理された酸化
チタンを必須成分とする着色剤と、アルキレン−ビス−
脂肪酸アミド及び/又は脂肪酸亜鉛を添加することを特
徴とする着色した樹脂組成物の製造方法。(2) A styrene resin containing alkylene-bis-fatty acid amide, a coloring agent whose essential component is titanium oxide surface-treated with aluminum oxide, and alkylene-bis-fatty acid amide.
A method for producing a colored resin composition, which comprises adding fatty acid amide and/or fatty acid zinc.