JPH1053679A - Styrene polymer composition - Google Patents

Styrene polymer composition

Info

Publication number
JPH1053679A
JPH1053679A JP21083196A JP21083196A JPH1053679A JP H1053679 A JPH1053679 A JP H1053679A JP 21083196 A JP21083196 A JP 21083196A JP 21083196 A JP21083196 A JP 21083196A JP H1053679 A JPH1053679 A JP H1053679A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
acid
polymer
styrene
higher
pts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP21083196A
Other languages
Japanese (ja)
Inventor
Masahiko Itakura
Heihachiro Tada
Takao Yugawa
平八郎 多田
雅彦 板倉
隆生 湯川
Original Assignee
Daicel Chem Ind Ltd
ダイセル化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To obtain a styrene polymer composition capable of exhibiting excellent strength, moldability and heat-resistance in balanced state without deteriorating the transparency and useful in the field of food container, light electric appliance, etc., by compounding a styrene polymer with a specific lubricant and an inorganic filler having a specific particle diameter. SOLUTION: This composition is produced by compounding (A) 100 pts.wt. of a styrene polymer with (B) 0.001-3 pts.wt. of an inorganic filler having an average particle diameter of 0.001-10μ (e.g. barium sulfate or calcium carbonate) and (C) 0.001-3 pts.wt. of a lubricant consisting of a higher fatty acid (e.g. stearic acid or behenic acid), a higher fatty acid salt (e.g. zinc stearate or sodium stearate) or a higher fatty acid amide (e.g. stearylamide or ethylenebisstearylamide).

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、透明性、成形性、 The present invention relates to the transparency, moldability,
実用強度及びコストパフォーマンスに優れたスチレン重合体組成物に関する。 Styrene polymer composition excellent in practical strength and cost performance related.

【0002】 [0002]

【従来の技術】スチレン重合体は、透明性、成形性に優れかつ安価であり食品容器や弱電機器等幅広い分野で使用されている。 BACKGROUND ART Styrene polymers, transparency, have been used with excellent and inexpensive food containers and light electrical appliances such as a wide range of fields in moldability. しかしながら、スチレン重合体は他の透明樹脂(特に、スチレン−アクリロニトリル共重合体、 However, styrene polymers other transparent resin (in particular, styrene - acrylonitrile copolymer,
スチレン−メチルメタクリレート共重合体等のスチレン系重合体)と比べると実用強度に劣るという問題点がある。 Styrene - there is a problem of poor practical strength as compared with the styrene-based polymer) such as methyl methacrylate copolymer. 特に深底の箱状の成形品の場合、しばしば射出成形の金型からの離型時に成形品が割れるという問題が起こる。 In a particularly deep box-shaped molded article, often a problem that the molded article is broken when the release from the mold of the injection molding takes place.

【0003】一般にスチレン重合体の実用強度を上げるためには、重合体の分子量を高くしている。 In order to increase the practical strength of generally styrene polymer has a higher molecular weight of the polymer. しかしながら、分子量を高くすると流動性が悪くなるため、流動性の改良を目的としてミネラルオイル等の可塑剤が一般的に添加されている。 However, the fluidity and increase the molecular weight is deteriorated, plasticizers such as mineral oil is generally added for the purpose of flowability improvement. 可塑剤を添加すると、流動性は向上するが耐熱性が低下する。 The addition of plasticizer, fluidity is improved to decrease the heat resistance. このように、実用強度、成形性、耐熱性のバランスを考えると現状のスチレン重合体は、充分満足できるものではなかった。 Thus, practical strength, formability, given the balance between heat resistance current styrene polymers, was not fully satisfactory.

【0004】 [0004]

【発明が解決しようとする課題】従って、本発明の目的は、強度、成形性、耐熱性のバランスの優れたスチレン重合体組成物、特に実用強度に優れたスチレン重合体組成物を提供することにある。 OBJECTS OF THE INVENTION It is therefore an object of the present invention is to provide strength, moldability, excellent styrene polymer composition of the balance of heat resistance, the styrene polymer composition particularly excellent in practical strength It is in.

【0005】 [0005]

【課題を解決するための手段】本発明者等は、鋭意検討の結果、スチレン重合体に特定の無機充填剤と特定の滑剤を特定量加えることによって、特にスチレン重合体の持つ透明性を損なわず実用強度に優れたスチレン重合体組成物を完成するに至った。 The present inventors have SUMMARY OF THE INVENTION The result of intensive studies, by adding a specific amount of a specific lubricant and specific inorganic filler to a styrene polymer, in particular to impair the transparency possessed by the styrene polymer not have completed the excellent styrene polymer composition practical strength.

【0006】すなわち、本発明は、スチレン重合体 100 Namely, the present invention is a styrene polymer 100
重量部に対して、平均粒子径が 0.001〜10ミクロンである無機充填剤 0.001〜3重量部と、高級脂肪酸、高級脂肪酸塩及び高級脂肪酸アミドからなる群より選ばれる少なくとも1種の滑剤 0.001〜3重量部とを含有することを特徴とするスチレン重合体組成物に関する。 Relative to the weight part, and the inorganic filler 0.001 parts by weight average particle diameter of 0.001 to 10 microns, higher fatty acid, at least one lubricant selected from the group consisting of higher fatty acid salts and higher fatty acid amides 0.001 about styrene polymer composition characterized by containing a part by weight.

【0007】本発明は、スチレン重合体に細かい粒子径を有する無機充填剤と特定の滑剤を少量添加することにより、透明性をそれほど損なうことなく、樹脂の実用強度を改良するというものである。 [0007] The present invention, by adding a small amount of a specific lubricant and the inorganic filler having a fine particle size styrene polymer without impairing significantly the transparency, is that to improve the practical strength of the resin. 例えば、高強度タイプのスチレン重合体に細かい無機充填剤と特定の滑剤とを少量添加することにより、高強度タイプのスチレン重合体より更に実用強度の優れた、AS樹脂(スチレン−アクリロニトリル共重合体)に近い実用強度を有するスチレン重合体樹脂組成物を製造することができるというものである。 For example, high strength type of styrene polymer fine inorganic filler and by adding a small amount of a specific lubricant, high strength even more types of styrene polymer excellent in practical strength, AS resin (styrene - acrylonitrile copolymer it is that it is possible to produce a styrene polymer resin composition having a close practical strength in).

【0008】 [0008]

【発明の実施の形態】本発明で用いるスチレン重合体は、重量平均分子量が10万から50万の範囲の一般に成形加工されているポリスチレン(GPPS)である。 Styrene polymer used in DETAILED DESCRIPTION OF THE INVENTION The present invention is a polystyrene having a weight average molecular weight is formed into a generally ranging from 100,000 500,000 (GPPS).

【0009】スチレン重合体を構成する単量体であるスチレン化合物としては、スチレン、α−メチルスチレンなどのα−置換アルキルスチレン、p−メチルスチレンなどの核置換アルキルスチレンなどが挙げられる。 [0009] As the styrene compound is a monomer constituting the styrene polymer include styrene, alpha-methylstyrene such as alpha-substituted alkyl styrene, nuclear substituted alkyl styrene such as p- methyl styrene. スチレン重合体の重合方法としてはバッチ式の懸濁重合法または連続塊状重合法を用いることができ、熱重合または開始剤による重合などのラジカル重合法のいずれでも使用できる。 The polymerization method of the styrenic polymers can be used suspension polymerization or continuous bulk polymerization batch can be used in either a radical polymerization method such as polymerization by thermal or initiator.

【0010】本発明で用いる無機充填剤とは、炭酸カルシウム、タルク、水酸化マグネシウム、クレー、シリカ、硫酸バリウム、酸化チタン、酸化亜鉛、酸化マグネシウム、マイカ、ヨウ化カリウム、水酸化リチウム、硫酸アルミニウムナトリウム、硫酸鉄、ヘキサフルオロリン酸カリウム、トリポリリン酸ナトリウム等が挙げられる。 [0010] The inorganic filler used in the present invention include calcium carbonate, talc, magnesium hydroxide, clay, silica, barium sulfate, titanium oxide, zinc oxide, magnesium oxide, mica, potassium iodide, lithium hydroxide, aluminum sulfate sodium, iron sulfate, potassium hexafluorophosphate, sodium tripolyphosphate. これらの中でも硫酸バリウム及び/又は炭酸カルシウムが好ましい。 Barium and / or calcium carbonate sulfate Among these, preferred.

【0011】本発明において、無機充填剤の平均粒子径は 0.001〜10ミクロン、好ましくは0.005〜5ミクロンである。 [0011] In the present invention, the average particle size of 0.001 to 10 microns of the inorganic filler is preferably 0.005 to 5 microns. 平均粒子径が 0.001ミクロン未満であると、分散性が非常に悪く樹脂中に均一に分散させることができない。 When the average particle size is less than 0.001 microns, can not be uniformly dispersed in the dispersion is very poor resin. また無機充填剤の平均粒子径が10ミクロンを超えると、実用強度の改良が認められない。 Also the average particle size of the inorganic filler exceeds 10 microns, the improvement of practical strength is not observed. また平均粒子径が10ミクロンを超えると無機充填剤の添加量が極少量でもスチレン重合体成形品のヘーズ値が大きくなり好ましくない。 The average particle diameter haze value of the additive amount of more than 10 microns inorganic filler very small amount even styrene polymer molded article is increased undesirably. このように実用強度と透明性のバランスを考えると、無機充填剤の平均粒子径は 0.001〜10ミクロン、 Thus think the balance of practical strength and transparency, the average particle size of 0.001 to 10 microns of the inorganic filler,
好ましくは 0.005〜5ミクロンである。 Preferably from 0.005 to 5 microns.

【0012】本発明において、無機充填剤の添加量はスチレン重合体 100重量部に対して、0.001〜3重量部、 [0012] In the present invention, the addition amount of the inorganic filler with respect to the styrene polymer 100 parts by weight, 0.001 parts by weight,
好ましくは 0.001〜1重量部である。 Preferably from 0.001 parts by weight. 添加量が 0.001重量部未満であると実用強度の改良効果が得られない。 Amount can not be obtained the effect of improving the practical strength is less than 0.001 part by weight. また、3重量部を超えるとスチレン重合体成形品のヘーズ値が大きくなり好ましくない。 Further, 3 parts by weight by weight, the styrene polymer moldings haze value increases undesirably.

【0013】また、本発明のスチレン重合体組成物は、 Further, the styrene polymer composition of the present invention,
実質的には強度の改良されたGPPSであり、透明性が重要である。 Virtually an improved GPPS strength, transparency is important. 3mm肉厚プレートでのヘーズ値(ASTM The haze value of a 3mm thick plate (ASTM
D1003)が 5.0以下であることが好ましい。 It is preferred D1003) is 5.0 or less. ヘーズ値は、無機充填剤の添加量、平均粒子径や無機充填剤の種類の違い等に大きく影響を受ける。 Haze value, the added amount of the inorganic filler, greatly affected by the average type of differences in particle size and an inorganic filler, and the like. 例えば、2〜3 For example, 2-3
ミクロンの粒子径の硫酸バリウムであれば、添加量としては、スチレン重合体100重量部に対して 0.001〜0.05 If barium sulfate having a particle size of microns, the addition amount, relative to the styrene polymer 100 parts by weight of 0.001 to 0.05
重量部が好ましい。 Parts by weight preferred. また、0.02〜0.03ミクロンの粒子径の硫酸バリウムであれば、添加量としては、スチレン重合体 100重量部に対して0.01〜1.0 重量部が好ましい。 Further, if the barium sulfate particle size of 0.02 to 0.03 microns, the addition amount, 0.01 to 1.0 parts by weight based on the styrene polymer 100 parts by weight is preferred.
すなわち最適添加量は、無機充填剤の添加量、粒子径や無機充填剤の種類の違いに影響を受ける。 That the optimum amount of addition, the addition amount of the inorganic filler, the effect on the difference in the type of particle size and inorganic filler subjected.

【0014】また、無機充填剤を良好に分散させかつ成形時の金型と樹脂との良好な離型性を得ることを目的として、高級脂肪酸、高級脂肪酸塩及び高級脂肪酸アミドからなる群より選ばれる少なくとも1つの滑剤を添加する。 Further, for the purpose of obtaining a good releasing property between to good dispersion of the inorganic filler and the mold and the resin during molding, selected from the group consisting of higher fatty acids, higher fatty acid salts and higher fatty acid amides adding at least one lubricant is. その添加量は、スチレン重合体 100重量部に対して The addition amount thereof, with respect to styrene polymer 100 parts by weight
0.001〜3重量部であり、好ましくは0.01〜1重量部である。 0.001 parts by weight, preferably 0.01 to 1 part by weight. 添加量が 0.001重量部未満であると、実質的な効果は得られない。 If the amount is less than 0.001 part by weight, a substantial effect can not be obtained. 添加量が3重量部を超えると耐熱性が低くなり過ぎたり、透明性が悪くなったり、金型汚れがひどくなるなどし、好ましくない。 Or the amount becomes too low heat resistance exceeds 3 parts by weight added, may become poor transparency, and the like mold contamination is worse, undesirable. これら滑剤を構成する脂肪酸は、1分子あたりの炭素数が10〜25個の範囲で選ばれ、好ましくは12〜22個のものである。 Fatty acids constituting these lubricants, carbon atoms per molecule is selected in the 10 to 25 range, preferably of 12-22. 炭素原子数が10個未満であると金型汚れがひどく、または25個より多いと透明性が悪くなるので好ましくない。 Mold contamination and the number of carbon atoms is less than 10 badly, or undesirably deteriorates more transparency than 25. 高級脂肪酸、高級脂肪酸塩の代表例としては、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、オレイン酸、 Higher fatty acids, as a representative example of the higher fatty acid salt, lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid,
ベヘニン酸など、及びこれらの、周期律表第I族、第II Such as behenic acid, and of these, Group I of the periodic table, II,
族、第III 族、第IV族に属する金属の塩が挙げられる。 Group, Group III, metal salts belonging to Group IV, and the like.
これらの中でも、ステアリン酸、ベヘニン酸、ステアリン酸亜鉛、ステアリン酸カルシウム、ステアリン酸ナトリウムが好適である。 Among these, stearic acid, behenic acid, zinc stearate, calcium stearate, sodium stearate are preferred. 高級脂肪酸アミドの代表例としては、ステアリン酸アミド、オレイン酸アミド、エチレンビスステアリルアミド等が挙げられる。 Representative examples of the higher fatty acid amide, stearic acid amide, oleic acid amide, ethylene bis-stearyl amide.

【0015】本発明のスチレン重合体組成物の製造方法は、スチレン重合体の重合時に無機充填剤及び/又は滑剤を添加してもよいし、スチレン重合体ペレット或いはパウダーと無機充填剤及び/又は滑剤とを押出機等の成形加工機によって溶融混練することにより製造することもできる。 Method for producing a [0015] styrene polymer composition of the present invention, an inorganic filler at the time of polymerization of the styrene polymer and / or to a lubricant may be added, styrene polymer pellets or powder and inorganic filler and / or It can also be produced by melt-kneading the lubricant by molding machine such as an extruder. また、スチレン重合体ペレット表面に無機充填剤と滑剤とを均一に付着させた状態や、無機充填剤を練り込まれたスチレン重合体ペレットの表面に滑剤を均一に付着させた状態でそのまま直接成形品の成形に供することもできる。 Moreover, as it directly molded styrene polymer pellet surface condition and adhered with an inorganic filler and a lubricant uniformly, in a state of uniformly deposited was a lubricant to the surface of the styrene polymer pellets kneaded with inorganic filler It can also be subjected to a molding of goods.

【0016】本発明のスチレン重合体組成物には必要に応じて、熱、光、酸素に対する安定剤(例えば、フェノール系化合物、リン系化合物などの酸化防止剤;ベンゾトリアゾール系化合物、ベンゾフェノン系化合物、サリチル酸フェニル化合物などの紫外線吸収剤;ヒンダードアミン系安定剤)や、流動パラフィン等の可塑剤、帯電防止剤、着色剤などの添加剤を添加してもよい。 [0016] If necessary, the styrene polymer composition of the present invention, heat, light, stabilizers against oxygen (e.g., phenol compounds, antioxidants such as phosphorus compounds; benzotriazole compounds, benzophenone compounds ultraviolet absorbents such as phenyl salicylate compound; hindered amine stabilizer), and a plasticizer such as liquid paraffin, antistatic agents, may be added additives such as coloring agents. これら添加剤の他、HIPSやSBSエラストマーを必要に応じて少量添加してもよい。 Besides these additives, it may be added in small quantities as needed HIPS and SBS elastomer. しかし、あくまで最終スチレン重合体樹脂組成物の3mm肉厚プレートでのヘーズ値(ASTM D1003)が 5.0以下となる範囲内においてであることが好ましい。 However, it is preferred only at the extent that the haze value of a 3mm thick plate of the final styrene polymer resin composition (ASTM D1003) is 5.0 or less.

【0017】 [0017]

【実施例】以下実施例によって本発明を更に詳しく説明するが、本発明はこれらの実施例によって何ら制限されるものでない。 BRIEF DESCRIPTION following examples the invention in more detail, but the present invention is not intended to be these Examples in any way limiting.

【0018】実施例1〜5、比較例1〜4 表1に示した配合処方で配合し、2軸押出機で 220℃で溶融混練し、その混合物を 220℃で射出成形を行うことにより、テストピースを作成し、物性測定を行った。 [0018] Examples 1-5, were blended in the formulations shown in Comparative Examples 1-4 in Table 1, kneaded at 220 ° C. in a twin screw extruder, by carrying out injection molding the mixture at 220 ° C., create a test piece was subjected to measurement of physical properties. その結果を表1に記す。 The results are shown in Table 1. 尚、各物性の測定方法は以下の通りである。 The measurement method of each physical property is as follows.

【0019】(1)ヘーズ値:ASTM D1003に準じて測定した。 [0019] (1) haze value was measured according to ASTM D1003. テストピース厚みは3mmとした。 Test piece thickness was 3mm. (2)アイゾット衝撃強度:JIS K6871に準じて測定した。 (2) Izod impact strength was measured in accordance with JIS K6871. (3)落球衝撃試験:カラープレート成形品(幅 100mm (3) Falling ball impact test: collar plate molded article (width 100mm
×長さ350mm ×厚み3mm)を成形し、凹部が形成された台上に載置し、前記凹部に向かって50gの鋼球を落下させ、成形品の破壊の有無を目視で観察した。 × molding a 350 mm × thickness 3mm) long, it was placed on the platform with a recess formed, toward the recess by dropping a steel ball of 50 g, was observed whether the destruction of the molded article was visually. 成形品の破壊の確率が50%となる落下の高さから、エネルギー基準に換算し、50%破壊エネルギーとして表示した。 From a height of fall of the probability of destruction of the molded article is 50% in terms of energy criteria, were expressed as 50% breaking energy. (4)外観:成形品を目視で観察し、キラキラしたものがほとんど目立って見えないものを「良」とし、キラキラしたものがかなり目立って見えるものを「悪」とした。 (4) Appearance: was visually observed a molded article, the ones that can not be seen by most noticeable thing was sparkling as "good", it was what those sparkling looks quite conspicuous as "evil".

【0020】 [0020]

【表1】 [Table 1]

【0021】尚、表1中の略語は以下の通りである。 [0021] In addition, the abbreviations in Table 1 are as follows. GPPS−1;高強度タイプGPPS(重量平均分子量 GPPS-1; high strength type GPPS (weight average molecular weight
35万) GPPS−2;高強度タイプGPPS(重量平均分子量 350,000) GPPS-2; high strength type GPPS (weight average molecular weight
32万) AS樹脂 ;セビアンN050( ダイセル化学工業(株) 製) BF−20 ;硫酸バリウム(堺化学工業(株)製)、 320,000) AS resin; CEVIAN N050 (manufactured by Daicel Chemical Industries, Ltd.) BF-20; Barium sulfate (Sakai Chemical Industry Co., Ltd.),
平均粒子径0.03μm BMH ;硫酸バリウム(堺化学工業(株)製)、 The average particle diameter of 0.03 .mu.m BMH; barium sulfate (manufactured by Sakai Chemical Industry Co.),
平均粒子径 2.5μm。 The average particle diameter of 2.5μm.

【0022】実施例6 実施例1と同じ配合処方でスチレン樹脂と無機充填剤を2軸押出機で 220℃で溶融混練し、無機充填剤入りペレットを得た。 The kneaded at 220 ° C. styrene resin and an inorganic filler in a twin-screw extruder in the same formulation as Example 6 Example 1 to obtain a mineral-filled pellet. このペレットに実施例1と同じ量の滑剤を添加し、タンブラーで良く混合し、ペレット表面に滑剤を付着させた。 The pellet was added the same amount of lubricant as in Example 1, were thoroughly mixed in a tumbler was deposited lubricant to pellet surface. 得られたペレットは実施例1で得られたペレットよりもペレットの流動性は良かった。 The resulting pellets was good fluidity of the pellets than pellets obtained in Example 1. また、このペレットを 220℃で射出成形を行い、テストピースを作成し、物性測定を行ったところ、実施例1と同じ値が得られた。 Further, the pellet was subjected to injection molding at 220 ° C., to create a test piece was subjected to physical property measurements were obtained the same value as in Example 1.

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl. 6識別記号 庁内整理番号 FI 技術表示箇所 C08K 5/20 KFZ C08K 5/20 KFZ ────────────────────────────────────────────────── ─── front page continued (51) Int.Cl. 6 identification symbol Agency in Docket No. FI art display portion C08K 5/20 KFZ C08K 5/20 KFZ

Claims (6)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 スチレン重合体 100重量部に対して、平均粒子径が 0.001〜10ミクロンである無機充填剤 0.001 Respect 1. A styrene polymer 100 parts by weight, the inorganic filler 0.001 average particle size of 0.001 to 10 microns
    〜3重量部と、高級脂肪酸、高級脂肪酸塩及び高級脂肪酸アミドからなる群より選ばれる少なくとも1種の滑剤 At least one lubricant selected from the group consisting of a 3 weight parts, higher fatty acids, higher fatty acid salts and higher fatty acid amides
    0.001〜3重量部とを含有することを特徴とするスチレン重合体組成物。 Styrene polymer composition characterized by containing a 0.001 parts by weight.
  2. 【請求項2】 無機充填剤の平均粒子径が 0.005〜5ミクロンである請求項1記載のスチレン重合体組成物。 Wherein the average particle diameter of the inorganic filler is a styrene polymer composition according to claim 1, wherein 0.005 to 5 microns.
  3. 【請求項3】 無機充填剤が、硫酸バリウム及び/又は炭酸カルシウムである請求項1又は2記載のスチレン重合体組成物。 Wherein the inorganic filler, according to claim 1 or 2 styrene polymer composition, wherein the barium sulfate and / or calcium carbonate.
  4. 【請求項4】 3mm肉厚プレートでのヘーズ値(AST 4. A haze value of at 3mm thick plate (AST
    M D1003)が5.0以下である請求項1〜3の何れか1項に記載のスチレン重合体組成物。 M D1003) styrene polymer composition according to any one of claims 1 to 3 is 5.0 or less.
  5. 【請求項5】 スチレン重合体 100重量部に対して、平均粒子径が 0.001〜10ミクロンである無機充填剤 0.001 Relative 5. A styrene polymer 100 parts by weight, the inorganic filler 0.001 average particle size of 0.001 to 10 microns
    〜3重量部を溶融混練したスチレン重合体ペレット表面に、高級脂肪酸、高級脂肪酸塩及び高級脂肪酸アミドからなる群より選ばれる少なくとも1種の滑剤 0.001〜3 To 3 weight parts to melt-kneading the styrene polymer pellet surface, higher fatty acid, at least one lubricant selected from the group consisting of higher fatty acid salts and higher fatty acid amides 0.001
    重量部を均一に付着させたスチレン重合体組成物。 Styrene polymer composition uniformly deposited so by weight.
  6. 【請求項6】 スチレン重合体 100重量部に対して、平均粒子径が 0.001〜10ミクロンである無機充填剤 0.001 Against 6. Styrene 100 parts by weight of the polymer, the inorganic filler 0.001 average particle size of 0.001 to 10 microns
    〜3重量部を溶融混練したスチレン重合体ペレット表面に、高級脂肪酸、高級脂肪酸塩及び高級脂肪酸アミドからなる群より選ばれる少なくとも1種の滑剤 0.001〜3 To 3 weight parts to melt-kneading the styrene polymer pellet surface, higher fatty acid, at least one lubricant selected from the group consisting of higher fatty acid salts and higher fatty acid amides 0.001
    重量部を均一に付着させた状態でそのまま直接成形品の成形に供することを特徴とするスチレン重合体組成物の成形方法。 Method of molding the styrene polymer composition, characterized in that directly subjected to direct molded article molded in a state of uniformly deposited so by weight.
JP21083196A 1996-08-09 1996-08-09 Styrene polymer composition Pending JPH1053679A (en)