JPH02251589A - 二液型水系接着剤 - Google Patents
二液型水系接着剤Info
- Publication number
- JPH02251589A JPH02251589A JP7239889A JP7239889A JPH02251589A JP H02251589 A JPH02251589 A JP H02251589A JP 7239889 A JP7239889 A JP 7239889A JP 7239889 A JP7239889 A JP 7239889A JP H02251589 A JPH02251589 A JP H02251589A
- Authority
- JP
- Japan
- Prior art keywords
- parts
- adhesive
- essentially composed
- water
- cross
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
く技術分野〉
本発明は、常温硬化型で二液性の水系接着剤に関する、
〈従来技術〉
従来より、アクリル系共重合体などに各種官能基を付与
した粘着剤や接着剤に、架橋剤を添加して凝集力を強め
て、耐熱性や耐水性を向上させる方法がとられている。
した粘着剤や接着剤に、架橋剤を添加して凝集力を強め
て、耐熱性や耐水性を向上させる方法がとられている。
例えば、水酸基やカルボキシル基の官能基を有するアク
リル系共重合体やクロロブレン系重合体に、架橋剤とし
てエポキシ化合物やイソシアネート化合物を添加した場
合には、経時増粘が大きく、塗布作業性を悪＜ １．た
。また、架橋剤として酸化亜鉛などの金属酸化物を添加
した場合には、粘着性が低下して初期接着力を悪くした
。
リル系共重合体やクロロブレン系重合体に、架橋剤とし
てエポキシ化合物やイソシアネート化合物を添加した場
合には、経時増粘が大きく、塗布作業性を悪＜ １．た
。また、架橋剤として酸化亜鉛などの金属酸化物を添加
した場合には、粘着性が低下して初期接着力を悪くした
。
〈発明の目的〉
本発明の目的は、架橋剤を添加しても経時増粘が少なく
、かつ粘着力の低下をもたらさ々い二液型の水系接着剤
−である。
、かつ粘着力の低下をもたらさ々い二液型の水系接着剤
−である。
〈発明の開示〉
本発明は、分子内にカルボキシル基または水酸基を有す
る水分散型の芳香族系ないしは脂環族系共重合体を主成
分とする主剤と、アセチルアセトン金属塩を主成分とす
る架橋剤とから々る二液型水系接着剤である。
る水分散型の芳香族系ないしは脂環族系共重合体を主成
分とする主剤と、アセチルアセトン金属塩を主成分とす
る架橋剤とから々る二液型水系接着剤である。
本発明で用いられる分子内にカルボキシル基を有する芳
香族系ないしは脂環族系共重合体は、１種または２種以
上の不飽和カルボン酸で変性されたエマルジ四ンであり
、不飽和カルボン酸の使用量は全単量体に対して０．５
〜３０係（重ｆ）が適当である。ここで芳香族ないしは
脂環族系と［７ては、スチレン、ロジン、テルペン、シ
クロペンタジェン、Ｃ９系石油樹脂、フェノール樹脂、
キシレン樹脂、クマロン−インデン樹脂、ビニルトルエ
ン、α−メチルスチレン等があり、アクリル酸エステル
、酢酸ビニル、ブタジェン、イソブチレン、ビニルブチ
ラール、ビニルエーテル、塩化ビニル、イソプレン、ク
ロロプレンなどのエチレン系やジエン系化合物で変性す
ること本できる。不飽和カルボン酸としては、アクリル
酸、メタクリル酸、クロトン酸、イタコン酸、無水マレ
イン酸などがあげられる。次に、アセチルアセトン金属
塩は、結晶性の粉末で、金属イオンとその価数の相違に
よっているいろな色観をもつ、分子内錯塩型キレート化
合物で、分子式Ｍ （ＣＨｓ Ｃｏ ＣＨＣｏ ＣＨａ
）ｎ で示され、Ｍ ＝Ａｌｌ 、Ｃｒ ｓ Ｚｎ
＊ Ｃｕ 、Ｎｉ ＊ Ｃｏ ＊ Ｆ ｅ ｓＭｇ 、
Ｍｎ々どで、ｎ＝＝２〜４である。これらのうちでも
アセチルアセトンアルミニウム塩が作業性、接着性能の
点で最適で、その添加量は０．５〜２０ＰＨＲが適当で
ある。
香族系ないしは脂環族系共重合体は、１種または２種以
上の不飽和カルボン酸で変性されたエマルジ四ンであり
、不飽和カルボン酸の使用量は全単量体に対して０．５
〜３０係（重ｆ）が適当である。ここで芳香族ないしは
脂環族系と［７ては、スチレン、ロジン、テルペン、シ
クロペンタジェン、Ｃ９系石油樹脂、フェノール樹脂、
キシレン樹脂、クマロン−インデン樹脂、ビニルトルエ
ン、α−メチルスチレン等があり、アクリル酸エステル
、酢酸ビニル、ブタジェン、イソブチレン、ビニルブチ
ラール、ビニルエーテル、塩化ビニル、イソプレン、ク
ロロプレンなどのエチレン系やジエン系化合物で変性す
ること本できる。不飽和カルボン酸としては、アクリル
酸、メタクリル酸、クロトン酸、イタコン酸、無水マレ
イン酸などがあげられる。次に、アセチルアセトン金属
塩は、結晶性の粉末で、金属イオンとその価数の相違に
よっているいろな色観をもつ、分子内錯塩型キレート化
合物で、分子式Ｍ （ＣＨｓ Ｃｏ ＣＨＣｏ ＣＨａ
）ｎ で示され、Ｍ ＝Ａｌｌ 、Ｃｒ ｓ Ｚｎ
＊ Ｃｕ 、Ｎｉ ＊ Ｃｏ ＊ Ｆ ｅ ｓＭｇ 、
Ｍｎ々どで、ｎ＝＝２〜４である。これらのうちでも
アセチルアセトンアルミニウム塩が作業性、接着性能の
点で最適で、その添加量は０．５〜２０ＰＨＲが適当で
ある。
〈発明の作用拳効果〉
本発明では、分子内のカルボキシル基または水酸基の７
セチルアセトン金属塩による架橋が次式の如く室温でゆ
るやかに進行するので、経時増粘が少なく、かつ粘着力
の低下をもたらさない。また、接着完了後の長期養生に
て、高強度化が可能である。
セチルアセトン金属塩による架橋が次式の如く室温でゆ
るやかに進行するので、経時増粘が少なく、かつ粘着力
の低下をもたらさない。また、接着完了後の長期養生に
て、高強度化が可能である。
なお、−りニーツー一は芳香族ないしは脂環族系共重合
を示し、Ｍは前記の如き金属類を示す。
を示し、Ｍは前記の如き金属類を示す。
以上の如く、金属架橋により分子量が増大して凝集力が
強くなり、耐熱性や耐水性が向上する。
強くなり、耐熱性や耐水性が向上する。
次に、実施例と比較例によシ説明する。
実施例１及び比較例１．２．３
フラスコ内に乳化剤のノニルフェノールポリエーテル硫
酸アンモニウム２部と水１００部を８０°Ｃに保ちなが
ら攪拌して、２−エチルへキシルアクリレート８０部と
スチレンモノマー２０部とアクリル酸モノマー２部に予
め軟化点８０℃のロジンエステル１００部を溶解したも
のを、触媒１０係過硫酸アンモニウム水溶液２部と共に
３時間要して滴下して乳化重合して主剤とした。次にこ
の主剤１００部に対して、架橋剤としてアセチルアセト
ンアルミニウム塩２部を添加撹拌して実施例１の接着剤
とした。また、水溶性エポキシ化合物２部を添加攪拌し
て比較例１の接着剤とし、同様にイソシアネート化合物
２部のものを比較例２．５０４酸化亜鉛分散液２部のも
のを比較例３の接着剤とした。
酸アンモニウム２部と水１００部を８０°Ｃに保ちなが
ら攪拌して、２−エチルへキシルアクリレート８０部と
スチレンモノマー２０部とアクリル酸モノマー２部に予
め軟化点８０℃のロジンエステル１００部を溶解したも
のを、触媒１０係過硫酸アンモニウム水溶液２部と共に
３時間要して滴下して乳化重合して主剤とした。次にこ
の主剤１００部に対して、架橋剤としてアセチルアセト
ンアルミニウム塩２部を添加撹拌して実施例１の接着剤
とした。また、水溶性エポキシ化合物２部を添加攪拌し
て比較例１の接着剤とし、同様にイソシアネート化合物
２部のものを比較例２．５０４酸化亜鉛分散液２部のも
のを比較例３の接着剤とした。
これらの２０℃における初期粘度を１００として、８時
間後及び２４時間後の経時粘度変化塞、及びＪＩＳ Ｚ
０２３７ ｒ粘着テープ・粘着シート試験方法」に
単拠した粘着力（１８０度引きはがし法、ｋｇｆ／ ２
５ ｇ巾）、タック（゛球転法、３０度傾斜板、Ｎｏ、
）の測定値を第１表に示す。
間後及び２４時間後の経時粘度変化塞、及びＪＩＳ Ｚ
０２３７ ｒ粘着テープ・粘着シート試験方法」に
単拠した粘着力（１８０度引きはがし法、ｋｇｆ／ ２
５ ｇ巾）、タック（゛球転法、３０度傾斜板、Ｎｏ、
）の測定値を第１表に示す。
第１表
実施例２、比較例４．５．６
フラスコ内に乳化剤のノニルフェノールポリエーテル硫
酸アンモニウム２部と水１００部を８０℃に保ちながら
攪拌して、エチルアクリレートモノマー８０部とスチレ
ンモノマー２０部とアクリル酸モノマー２部に予めＣ９
系石油樹脂１２０部を溶解したもめを、触媒の１０１過
硫酸アンモニウム水溶液２部と共に、３時間要して乳化
重合して主剤とした。次に、この主剤１００部に対して
、架橋剤としてアセチルアセトンアルミニウム塩２部を
添加攪拌して実施例２の接着剤とした。また、水溶性エ
ポキシ化合物２部を添加攪拌して比較例４の接着剤とし
、同様にイソシアネート化合物２部のものを比較例５と
し、５０係酸化亜鉛分散液２部のものを比較例６の接着
剤とした。
酸アンモニウム２部と水１００部を８０℃に保ちながら
攪拌して、エチルアクリレートモノマー８０部とスチレ
ンモノマー２０部とアクリル酸モノマー２部に予めＣ９
系石油樹脂１２０部を溶解したもめを、触媒の１０１過
硫酸アンモニウム水溶液２部と共に、３時間要して乳化
重合して主剤とした。次に、この主剤１００部に対して
、架橋剤としてアセチルアセトンアルミニウム塩２部を
添加攪拌して実施例２の接着剤とした。また、水溶性エ
ポキシ化合物２部を添加攪拌して比較例４の接着剤とし
、同様にイソシアネート化合物２部のものを比較例５と
し、５０係酸化亜鉛分散液２部のものを比較例６の接着
剤とした。
これらの２０℃における初期粘度を１００として、８時
間後及び２４時間後の経時粘度変化基、及び次の接着条
件下でのコンタクト接着性（有、無）と接着力（引張剪
断強度；ｋｇ／ｄ１１８０度剥離強度：に９／２５５ｗ
幅）の測定値を第２表に示す。
間後及び２４時間後の経時粘度変化基、及び次の接着条
件下でのコンタクト接着性（有、無）と接着力（引張剪
断強度；ｋｇ／ｄ１１８０度剥離強度：に９／２５５ｗ
幅）の測定値を第２表に示す。
接着条件
塗布量
被着体
１２０ ｔ／イ（片面当り）、両面塗布引張剪断強度；
合板×鋼板 １８０度剥離；９号キャンパスＸアルミ板８０℃、３分
間 ａｋｙ／ｄ、ｓ秒間 ７日間、室温 ２０℃、６０°Ｃ 乾 燥 圧 締 養 生 測定温度
合板×鋼板 １８０度剥離；９号キャンパスＸアルミ板８０℃、３分
間 ａｋｙ／ｄ、ｓ秒間 ７日間、室温 ２０℃、６０°Ｃ 乾 燥 圧 締 養 生 測定温度
Claims (1)
- 分子内にカルボキシル基または水酸基を有する水分散型
の芳香族系ないしは脂環族系共重合体を主成分とする主
剤と、アセチルアセトン金属塩を主成分とする架橋剤と
からなることを特徴とする二液型水系接着剤