JP7137112B2 - 射出成形体およびその製造方法 - Google Patents
射出成形体およびその製造方法 Download PDFInfo
- Publication number
- JP7137112B2 JP7137112B2 JP2022012586A JP2022012586A JP7137112B2 JP 7137112 B2 JP7137112 B2 JP 7137112B2 JP 2022012586 A JP2022012586 A JP 2022012586A JP 2022012586 A JP2022012586 A JP 2022012586A JP 7137112 B2 JP7137112 B2 JP 7137112B2
- Authority
- JP
- Japan
- Prior art keywords
- copolymer
- molded article
- injection
- injection molded
- units
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本開示の射出成形体において、前記射出成形体からの50質量%フッ化水素酸への金属溶出量が、200μg/m2以下であることが好ましい。
本開示の射出成形体において、前記共重合体の前記フルオロ(アルキルビニルエーテル)単位が、パーフルオロ(プロピルビニルエーテル)単位であることが好ましい。
本開示の射出成形体において、前記共重合体のフルオロ(アルキルビニルエーテル)単位の含有量が、全単量体単位に対して、4.1~4.5質量%であることが好ましい。
本開示の射出成形体において、前記共重合体の372℃におけるメルトフローレートが、12.0~17.6g/10分であることが好ましい。
本開示の射出成形体において、前記共重合体の官能基数が、主鎖炭素数106個あたり、20個以下であることが好ましい。
本開示の射出成形体は、雌型継手であることが好ましい。
本開示の製造方法において、前記シリンダとして、Niメッキが施されたシリンダ、または、Ni基合金により形成されたシリンダを用い、前記スクリュとして、Ni基合金により形成され、先端にスミアヘッドが設けられたスクリュを用いることが好ましい。
CF2=CFO(CF2CFY1O)p-(CF2CF2CF2O)q-Rf (1)
(式中、Y1はFまたはCF3を表し、Rfは炭素数1~5のパーフルオロアルキル基を表す。pは0~5の整数を表し、qは0~5の整数を表す。)で表される単量体、および、一般式(2):
CFX=CXOCF2OR1 (2)
(式中、Xは、同一または異なり、H、FまたはCF3を表し、R1は、直鎖または分岐した、H、Cl、BrおよびIからなる群より選択される少なくとも1種の原子を1~2個含んでいてもよい炭素数が1~6のフルオロアルキル基、若しくは、H、Cl、BrおよびIからなる群より選択される少なくとも1種の原子を1~2個含んでいてもよい炭素数が5または6の環状フルオロアルキル基を表す。)で表される単量体からなる群より選択される少なくとも1種を挙げることができる。
I:吸光度
K:補正係数
t:フィルムの厚さ(mm)
ジノルマルプロピルパーオキシジカーボネート、ジイソプロピルパーオキシジカーボネート、ジsec-ブチルパーオキシジカーボネート、ジ-2-エトキシエチルパーオキシジカーボネートなどのジアルキルパーオキシカーボネート類;
t-ブチルパーオキシイソブチレート、t-ブチルパーオキシピバレートなどのパーオキシエステル類;
ジt-ブチルパーオキサイドなどのジアルキルパーオキサイド類;
ジ[フルオロ(またはフルオロクロロ)アシル]パーオキサイド類;
などが代表的なものとしてあげられる。
各単量体単位の含有量は、NMR分析装置(たとえば、ブルカーバイオスピン社製、AVANCE300 高温プローブ)により測定した。
ASTM D1238に従って、メルトインデクサーG-01(東洋精機製作所社製)を用いて、372℃、5kg荷重下で内径2.1mm、長さ8mmのノズルから10分間あたりに流出するポリマーの質量(g/10分)を求めた。
示差走査熱量計(商品名:X-DSC7000、日立ハイテクサイエンス社製)を用いて、昇温速度10℃/分で200℃から350℃までの1度目の昇温を行い、続けて、冷却速度10℃/分で350℃から200℃まで冷却し、再度、昇温速度10℃/分で200℃から350℃までの2度目の昇温を行い、2度目の昇温過程で生ずる溶融曲線ピークから融点を求めた。
共重合体のペレットを、コールドプレスにより成形して、厚さ0.25~0.30mmのフィルムを作製した。このフィルムをフーリエ変換赤外分光分析装置〔FT-IR(Spectrum One、パーキンエルマー社製)〕により40回スキャンし、分析して赤外吸収スペクトルを得、完全にフッ素化されて官能基が存在しないベーススペクトルとの差スペクトルを得た。この差スペクトルに現れる特定の官能基の吸収ピークから、下記式(A)に従って試料における炭素原子1×106個あたりの官能基数Nを算出した。
N=I×K/t (A)
I:吸光度
K:補正係数
t:フィルムの厚さ(mm)
参考までに、本開示における官能基について、吸収周波数、モル吸光係数および補正係数を表2に示す。モル吸光係数は低分子モデル化合物のFT-IR測定データから決定したものである。
純水を51.8L、パーフルオロシクロブタンを40.9kg、パーフルオロ(プロピルビニルエーテル)(PPVE)を1.57kg、メタノールを1.03kg、テトラフルオロエチレン(TFE)を0.64MPaまで圧入、ジ-sec-ブチルパーオキシジカーボネートの代わりにジ-n-プロピルパーオキシジカーボネートの50%メタノール溶液0.103kg、PPVEをTFEの供給1kg毎に0.038kg追加、TFEの追加投入量が40.9kgに達したところで重合を終了させることに変更し、乾燥粉末を42.4kg得た以外は、特開2020-97750号の実施例1に記載の方法と同様にして、ペレットを得た。得られたペレットを用いて上記した方法によりPPVE含有量を測定した。結果を表3に示す。
純水を51.8L、パーフルオロシクロブタンを40.9kg、パーフルオロ(プロピルビニルエーテル)(PPVE)を2.69kg、メタノールを2.48kg、テトラフルオロエチレン(TFE)を0.64MPaまで圧入、ジ-sec-ブチルパーオキシジカーボネートの代わりにジ-n-プロピルパーオキシジカーボネートの50%メタノール溶液0.051kg、PPVEをTFEの供給1kg毎に0.057kg追加、TFEの追加投入量が40.9kgに達したところで重合を終了させることに変更し、乾燥粉末を43.2kg得た以外は、特開2020-97750号の実施例1に記載の方法と同様にして、ペレットを得た。得られたペレットを用いて上記した方法によりPPVE含有量を測定した。結果を表3に示す。
純水を51.8L、パーフルオロシクロブタンを40.9kg、パーフルオロ(プロピルビニルエーテル)(PPVE)を1.92kg、メタノールを3.09kg、テトラフルオロエチレン(TFE)を0.64MPaまで圧入、ジ-sec-ブチルパーオキシジカーボネートの代わりにジ-n-プロピルパーオキシジカーボネートの50%メタノール溶液0.051kg、PPVEをTFEの供給1kg毎に0.044kg追加、TFEの追加投入量が40.9kgに達したところで重合を終了させることに変更し、乾燥粉末を42.7kg得た以外は、特開2020-97750号の実施例1に記載の方法と同様にして、ペレットを得た。得られたペレットを用いて上記した方法によりPPVE含有量を測定した。結果を表3に示す。
純水を51.8L、パーフルオロシクロブタンを40.9kg、パーフルオロ(プロピルビニルエーテル)(PPVE)を2.05kg、メタノールを4.13kg、テトラフルオロエチレン(TFE)を0.64MPaまで圧入、ジ-sec-ブチルパーオキシジカーボネートの代わりにジ-n-プロピルパーオキシジカーボネートの50%メタノール溶液0.051kg、PPVEをTFEの供給1kg毎に0.046kg追加、TFEの追加投入量が40.9kgに達したところで重合を終了させることに変更し、乾燥粉末を42.8kg得た以外は、特開2020-97750号の実施例1に記載の方法と同様にして、ペレットを得た。得られたペレットを用いて上記した方法によりPPVE含有量を測定した。結果を表3に示す。
純水を51.8L、パーフルオロシクロブタンを40.9kg、パーフルオロ(プロピルビニルエーテル)(PPVE)を1.85kg、メタノールを4.00kg、テトラフルオロエチレン(TFE)を0.64MPaまで圧入、ジ-sec-ブチルパーオキシジカーボネートの代わりにジ-n-プロピルパーオキシジカーボネートの50%メタノール溶液0.051kg、PPVEをTFEの供給1kg毎に0.043kg追加、TFEの追加投入量が40.9kgに達したところで重合を終了させることに変更し、乾燥粉末を42.6kg得た以外は、特開2020-97750号の実施例1に記載の方法と同様にして、ペレットを得た。得られたペレットを用いて上記した方法によりPPVE含有量を測定した。結果を表3に示す。
純水を51.8L、パーフルオロシクロブタンを40.9kg、パーフルオロ(プロピルビニルエーテル)(PPVE)を1.92kg、メタノールを4.17kg、テトラフルオロエチレン(TFE)を0.64MPaまで圧入、ジ-sec-ブチルパーオキシジカーボネートの代わりにジ-n-プロピルパーオキシジカーボネートの50%メタノール溶液0.051kg、PPVEをTFEの供給1kg毎に0.044kg追加、TFEの追加投入量が40.9kgに達したところで重合を終了させることに変更し、乾燥粉末を42.7kg得た以外は、特開2020-97750号の実施例1に記載の方法と同様にして、ペレットを得た。得られたペレットを用いて上記した方法によりPPVE含有量を測定した。結果を表3に示す。
純水を51.8L、パーフルオロシクロブタンを40.9kg、パーフルオロ(プロピルビニルエーテル)(PPVE)を1.98kg、メタノールを4.37kg、テトラフルオロエチレン(TFE)を0.64MPaまで圧入、ジ-sec-ブチルパーオキシジカーボネートの代わりにジ-n-プロピルパーオキシジカーボネートの50%メタノール溶液0.051kg、PPVEをTFEの供給1kg毎に0.045kg追加、TFEの追加投入量が40.9kgに達したところで重合を終了させることに変更し、乾燥粉末を42.7kg得た以外は、特開2020-97750号の実施例1に記載の方法と同様にして、ペレットを得た。得られたペレットを用いて上記した方法によりPPVE含有量を測定した。結果を表3に示す。
純水を51.8L、パーフルオロシクロブタンを40.9kg、パーフルオロ(プロピルビニルエーテル)(PPVE)を2.11kg、メタノールを0.16kg、テトラフルオロエチレン(TFE)を0.64MPaまで圧入、ジ-sec-ブチルパーオキシジカーボネートの代わりにジ-n-プロピルパーオキシジカーボネートの50%メタノール溶液0.103kg、PPVEをTFEの供給1kg毎に0.047kg追加、TFEの追加投入量が40.9kgに達したところで重合を終了させることに変更し、乾燥粉末を42.8kg得た以外は、特開2020-97750号の実施例1に記載の方法と同様にして、ペレットを得た。得られたペレットを用いて上記した方法によりPPVE含有量を測定した。結果を表3に示す。
純水を51.8L、パーフルオロシクロブタンを40.9kg、パーフルオロ(プロピルビニルエーテル)(PPVE)を2.11kg、メタノールを1.12kg、テトラフルオロエチレン(TFE)を0.64MPaまで圧入、ジ-sec-ブチルパーオキシジカーボネートの代わりにジ-n-プロピルパーオキシジカーボネートの50%メタノール溶液0.103kg、PPVEをTFEの供給1kg毎に0.047kg追加、TFEの追加投入量が40.9kgに達したところで重合を終了させることに変更し、乾燥粉末を42.8kg得た以外は、特開2020-97750号の実施例1に記載の方法と同様にして、ペレットを得た。得られたペレットを用いて上記した方法によりPPVE含有量を測定した。結果を表3に示す。
射出成形機(住友重機械工業社製、SE50EV-A)を使用し、クラス10000のクリーンルーム内で成形を行った。射出成形機のスクリュとして、スクリュヘッドにスミアヘッドが設けられたスクリュを用い、射出成形機のスクリュおよびシリンダの材質はNi基合金であった。射出成形機のシリンダの最高温度を表4に記載のとおりとし、金型温度を200℃とし、射出速度を20mm/sとして、共重合体を射出成形し、シート状射出成形体(40mm×40mm×0.5mmt)を作製した。金型として、HPM38にNiめっきを施した金型(40mm×40mm×0.5mmt、4個取り、サイドゲート)を用いた。
射出成形機(住友重機械工業社製、SE50EV-A)を使用して成形を行った。射出成形機のスクリュとして、スクリュヘッド、逆止リングおよびシールリング(スクリュ3点セット)により構成されるスクリュ先端が設けられたスクリュを用い、射出成形機のスクリュおよびシリンダの材質はステンレスであり、表面にCrメッキが施されていた。射出成形機のシリンダの最高温度を表4に記載のとおりとし、金型温度を200℃とし、射出速度を20mm/sとして、共重合体を射出成形し、シート状射出成形体(40mm×40mm×0.5mmt)を作製した。金型として、HPM38製の金型(40mm×40mm×0.5mmt、4個取り、サイドゲート)を用いた。
フッ素イオン溶出量の測定には、199回目の射出成形により得られた射出成形体を用いた。セラミック製のはさみを用いて、得られた射出成形体のランナーから4個のシート状射出成形体(40mm×40mm×0.5mmt)を切り離した。4個のシート状射出成形体の全てを純水14gに浸漬させ、滅菌機で121℃、1時間加熱した後、得られた水から射出成形体を取り出し、残った水のフッ素イオン濃度をフッ素イオンメーターにて測定した。得られた測定値から、下記式にしたがって、射出成形体の表面積当たりのフッ素イオン溶出量を算出した。
フッ素イオン溶出量(μg/m2)=測定値(μg/g)×純水量(g)/4個の射出成形体の合計表面積(m2)
フッ素イオン溶出量の測定には、200回目の射出成形により得られた射出成形体を用いた。また、測定に用いる容器として、50質量%フッ化水素酸に7日間、25℃に浸漬後、超純水洗浄したPFA製容器を用いた。
金属溶出量(μg/m2)=[測定用溶液中の金属濃度(ng/g)-参照用溶液中の金属濃度(ng/g)]×50質量%フッ化水素酸量(g)×0.001(μg/ng)/4個の射出成形体の合計表面積(m2)
射出成形機(住友重機械工業社製、SE50EV-A)を使用し、クラス10000のクリーンルーム内で成形を行った。射出成形機のスクリュとして、スクリュヘッドにスミアヘッドが設けられたスクリュを用い、射出成形機のスクリュおよびシリンダの材質はNi基合金であった。射出成形機のシリンダの最高温度を390℃、金型温度を200℃、射出速度10mm/sとして、共重合体を射出成形し、シート状射出成形体(100cm×100cm×2mmt)を作製した。金型として、HPM38にNiメッキを施した金型(100cm×100cm×2mmt、サイドゲート)を用いた。
得られた射出成形体を観察し、以下の基準により評価した。表面の荒れの有無は、射出成形体の表面を触ることにより、確認した。
・評価(目視)
2:表面全体が平滑であり、成形体全体にフローマークも観られない
1:金型のゲートが位置していた箇所から1cmの範囲内の表面に荒れが確認され、または、金型のゲートが位置していた箇所から1cmの範囲内にフローマークが観られるが、それ以外の範囲は、表面全体が平滑であり、フローマークも観られない
0:金型のゲートが位置していた箇所から4cmの範囲内の表面に荒れが確認され、または、金型のゲートが位置していた箇所から4cmの範囲内にフローマークが観られる
オゾン発生装置(商品名:SGX-A11MN(改)、住友精機工業社製)で発生させたオゾンガス(オゾン/酸素=10/90容量%)をイオン交換水が入ったPFA製の容器に接続し、イオン交換水中にバブリングしてオゾンガスに水蒸気を添加した後、シート状射出成形体が入ったPFA製のセルに0.7リットル/分で室温にて通して試料を湿潤オゾンガスに曝露した。曝露を開始してから90日後に試料を取り出し、表面をイオン交換水で軽くすすいだ後、透過型光学顕微鏡を用いて倍率100倍で試料表面から深さ5~200μmの部分を観察し、標準スケールとともに撮影し、試料表面1mm2あたりの長さ10μm以上のクラックの数を測定し、以下の基準により評価した。
○:クラック数10個以下
△:クラック数10個超50個以下
×:クラック数50個超
シート状射出成形体を60℃で24時間おいた後で、ヘイズメーター(商品名:NDH7000SP、日本電色工業株式会社製)を用いて、JIS K 7136に準じて、純水を入れた石英セルにシートを浸し、ヘイズ値を測定した。
シート状射出成形体を60℃で24時間おいた後で、射出成形体から80mm×10mmの試験片を切り出し、電気炉にて100℃で20時間加熱した。得られた試験片を用いた以外は、JIS K-K 7191-1に記載の方法に準じて、ヒートディストーションテスター(安田精機製作所社製)にて、試験温度30~150℃、昇温速度120℃/時間、曲げ応力1.8MPa、フラットワイズ法の条件にて試験を行った。次式により荷重たわみ率を求めた。80℃での荷重たわみ率が小さいシートは、熱時剛性に優れている。
荷重たわみ率(%)=a2/a1×100
a1:試験前の試験片厚み(mm)
a2:80℃でのたわみ量(mm)
日立ハイテクサイエンス社製TMA-7100を用いて引張クリープ歪を測定した。シート状射出成形体(40mm×40mm×0.5mmt)から幅2mm、長さ22mmのサンプルを作製した。サンプルを治具間距離10mmで測定治具に装着した。サンプルに対して、断面荷重が3.32N/mm2になるように荷重を負荷し、200℃に放置し、試験開始後70分の時点から試験開始後1320分の時点までのサンプルの長さの変位(mm)を測定し、初期のサンプル長(10mm)に対する長さの変位(mm)の割合(引張クリープ歪(%))を算出した。200℃、1320分間の条件で測定する引張クリープ歪(%)が小さいシートは、高温の環境中で引張荷重が長時間負荷されても伸びにくく、長時間引張クリープ特性に優れている。
シート状射出成形体を60℃で24時間おいた後で、射出成形体から試験片を作製した。試験カップ(透過面積7.065cm2)内にジメチルカーボネート(DMC)を5.5g入れ、シート状試験片で覆い、PTFEガスケットを挟んで締め付け、密閉した。シート状試験片とDMCが接するようにして、温度60℃で60日間保持した後取出し、室温で1時間放置後に質量減少量を測定した。次式により、電解液透過度(g/m2)を求めた。
電解液透過度(g/m2)=質量減少量(g)/透過面積(m2)
シート状射出成形体を60℃で24時間おいた後で、射出成形体からシート状試験片を作製した。試験カップ(透過面積12.56cm2)内にMEKを10g入れ、シート状試験片で覆い、PTFEガスケットを挟んで締め付け、密閉した。シート状試験片とMEKが接するようにして、温度60℃で60日間保持した後取出し、室温で1時間放置後に質量減少量を測定した。次式により、MEK透過度(g/m2)を求めた。
MEK透過度(g/m2)=質量減少量(g)/透過面積(m2)
シート状射出成形体を60℃で24時間おいた後で試験片として使用した。テーバー摩耗試験機(No.101 特型テーバー式アブレーションテスター、安田精機製作所社製)の試験台に試験片を固定し、試験片表面温度150℃、荷重500g、摩耗輪CS-10(研磨紙#240で20回転研磨したもの)、回転速度60rpmの条件で、テーバー摩耗試験機を用いて摩耗試験を行った。1000回転後の試験片重量を計量し、同じ試験片でさらに8000回転試験後に試験片重量を計量した。次式により、摩耗量を求めた。
摩耗量(mg)=M1-M2
M1:1000回転後の試験片重量(mg)
M2:8000回転後の試験片重量(mg)
島津製作所社製疲労試験機MMT-250NV-10を用いて6万回引張強度維持率を測定した。シート状射出成形体およびASTM D1708マイクロダンベル用いて、ダンベル形状(厚み2.4mm、幅5.0mm、測定部長さ22mm)のサンプルを作製した。サンプルを測定治具に装着し、サンプルを装着した状態で測定治具を150℃の恒温槽中に設置した。ストローク0.2mm、周波数100Hzで、一軸方向への引張りを繰り返し、引張り毎の引張強度(ストロークが+0.2mmの時の引張強度)を測定した。以下の式に従って測定値から6万回引張強度維持率を算出した。
6万回引張強度維持率(%)=引張強度(6万回)(mN)/引張強度(5千回)(mN)×100
13.5mm×38mmの長方形ダンベルを用いて、シート状射出成形体を打ち抜くことにより、3個の試験片を得た。得られた各試験片の長辺の中心に、ASTM D1693に準じて、19mm×0.45mmの刃でノッチを入れた。100mlポータブルリアクタ(TVS1型、耐圧ガラス工業社製)に、ノッチ試験片3個とN-メチルピロリドン(NMP)25gを入れ、電気炉にて150℃で20時間加熱後、ノッチ試験片を取り出した。得られたノッチ試験片3個をASTM D1693に準じた応力亀裂試験治具に取り付け、電気炉にて200℃で24時間加熱した後、ノッチおよびその周辺を目視で観察し、亀裂の数を数えた。亀裂が生じないシートは、薬液に浸漬された後でも耐熱変形性が優れている。
○:亀裂の数が0個である
×:亀裂の数が1個以上である
(T型継手の作製)
シリンダの最高温度を390℃、金型温度を160℃、射出速度8mm/sに変更し、金型を変更した以外は実験例1と同様にして、合成例1~9の共重合体を射出成形することにより、図1に示す形状のT型継手を作製した。金型として、HPM38にNiめっきを施した金型(T型継手、外径20mm、内径16mm、厚み2mm、全長60mm、全高35mm、分岐部サイドゲート)を用いた。
オゾン発生装置(商品名:SGX-A11MN(改)、住友精機工業社製)で発生させたオゾンガス(オゾン/酸素=10/90容量%)をイオン交換水が入ったPFA製の容器に接続し、イオン交換水中にバブリングしてオゾンガスに水蒸気を添加した後、T型継手が入ったPFA製のセルに0.7リットル/分で室温にて通して試料を湿潤オゾンガスに曝露した。曝露を開始してから90日後に試料を取り出し、表面をイオン交換水で軽くすすいだ後、透過型光学顕微鏡を用いて倍率100倍で試料表面から深さ5~200μmの部分を観察し、標準スケールとともに撮影し、試料表面1mm2あたりの長さ10μm以上のクラックの数を測定し、以下の基準により評価した。
○:クラック数10個以下
△:クラック数10個超50個以下
×:クラック数50個超
T型継手をジメチルカーボネート(DMC)に80℃で30日間浸漬し、室温まで冷却してからT型継手を取り出して、エアガンで成形体表面を濡らしているDMCを飛ばしてから、T型継手の重量を測定した。浸漬前の重量に対する、浸漬後の重量の変化率(質量ppm)を算出した。
1.ゲ-ト付近中空部の内部表面荒れ
金型のゲート部に対応する継手の位置(図1に示す位置A)の周辺の内壁の荒れを目視で確認し、以下の基準により評価した。
○:表面荒れあり
×:表面荒れなし
ゲート正面の接続部の内径の真円度を測定した。金型のゲート部に対応する継手の位置(図1に示す位置A)の正面に位置する接続部(図1に示す接続部B)の内径をT字の横棒と並行方向を起点として、45°ごとに4点測定して、最大内径Dmaxおよび最小内径Dminを測定した。得られた測定値から、真円度=(Dmax-Dmin)/2の式に従って真円度を算出し、以下の基準で評価した。
○:真円度0.05未満
×:真円度0.05以上
T型継手の作製のための射出成形を繰り返し、100回連続成形した際の、外観に糸引き起因となる繊維状の筋の有無を観察した。
○:繊維状の筋の外観不良ゼロ
×:繊維状の筋の外観不良1個以上
Claims (9)
- テトラフルオロエチレン単位およびフルオロ(アルキルビニルエーテル)単位を含有する共重合体を含有する射出成形体であって、
前記共重合体のフルオロ(アルキルビニルエーテル)単位の含有量が、全単量体単位に対して、3.9~4.8質量%であり、
共重合体のテトラフルオロエチレン単位の含有量が、全単量体単位に対して、95.2~96.1質量%であり、
前記共重合体の372℃におけるメルトフローレートが、11.0~19.0g/10分であり、
前記共重合体の融点が、296~305℃であり、
前記射出成形体からの水へのフッ素イオン溶出量が、5500μg/m 2 以下であり、
前記射出成形体からの50質量%フッ化水素酸への金属溶出量が、200μg/m 2 以下である射出成形体。 - 前記共重合体の前記フルオロ(アルキルビニルエーテル)単位が、パーフルオロ(プロピルビニルエーテル)単位である請求項1に記載の射出成形体。
- 前記共重合体の前記フルオロ(アルキルビニルエーテル)単位の含有量が、全単量体単位に対して、4.1~4.5質量%である請求項1または2に記載の射出成形体。
- 前記共重合体の372℃におけるメルトフローレートが、12.0~17.6g/10分である請求項1~3のいずれかに記載の射出成形体。
- 前記共重合体の-CF=CF 2 、-CF 2 H、-COF、-COOH、-COOCH 3 、-CONH 2 および-CH 2 OHの官能基数が、主鎖炭素数106個あたり、20個以下である請求項1~4のいずれかに記載の射出成形体。
- 雌型継手である請求項1~5のいずれかに記載の射出成形体。
- 請求項1~6のいずれかに記載の射出成形体の製造方法であって、シリンダ、および、前記シリンダ内に収容されたスクリュを備える射出成形機を用いて、前記共重合体を射出成形することにより前記射出成形体を得る製造方法。
- 前記シリンダ内の前記共重合体の温度を、385~395℃に調整する請求項7に記載の製造方法。
- 前記シリンダとして、Niメッキが施されたシリンダ、または、Ni基合金により形成されたシリンダを用い、前記スクリュとして、Ni基合金により形成され、先端にスミアヘッドが設けられたスクリュを用いる請求項7または8に記載の製造方法。