JP6946395B2 - Conductive adhesives, adhesive structures and electronic components using them - Google Patents

Conductive adhesives, adhesive structures and electronic components using them Download PDF

Info

Publication number
JP6946395B2
JP6946395B2 JP2019194347A JP2019194347A JP6946395B2 JP 6946395 B2 JP6946395 B2 JP 6946395B2 JP 2019194347 A JP2019194347 A JP 2019194347A JP 2019194347 A JP2019194347 A JP 2019194347A JP 6946395 B2 JP6946395 B2 JP 6946395B2
Authority
JP
Japan
Prior art keywords
meth
acrylate
conductive adhesive
conductive
phosphate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2019194347A
Other languages
Japanese (ja)
Other versions
JP2021066833A (en
Inventor
茉里 徳武
茉里 徳武
阿部　真二
真二 阿部
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Chemical Industrial Co Ltd
Original Assignee
Nippon Chemical Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Chemical Industrial Co Ltd filed Critical Nippon Chemical Industrial Co Ltd
Priority to JP2019194347A priority Critical patent/JP6946395B2/en
Priority to CN202080074013.7A priority patent/CN114585704B/en
Priority to DE112020005164.1T priority patent/DE112020005164T5/en
Priority to PCT/JP2020/039297 priority patent/WO2021079852A1/en
Publication of JP2021066833A publication Critical patent/JP2021066833A/en
Application granted granted Critical
Publication of JP6946395B2 publication Critical patent/JP6946395B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、紫外線硬化型の導電性接着剤、それを用いた接着構造体及び電子部品に関するものである。 The present invention relates to an ultraviolet curable conductive adhesive, an adhesive structure using the same, and an electronic component.

半導体や発光ダイオード等の電子部品をフィルムや紙等の基板上に形成された電極に導電性接着剤や異方導電性接着剤を用いて接着する方法として、フェイスダウン方式により電子部品を熱圧着させる方法（熱圧着法）が広く一般的に用いられている（例えば、特許文献１）。具体的には、基板上に形成された電極の上に異方導電性接着剤を塗布し、突起状電極と呼ばれるバンプを有する半導体を当該バンプが電極上に位置するように載置し、約１８０℃に加熱された上部ヒートツール及び下部ヒートツールで、半導体が載置された基板を挟み込むことにより異方導電性接着剤を硬化させ、半導体を電極に電気的に接続させると同時に基板上に半導体を実装させている。 As a method of bonding electronic components such as semiconductors and light emitting diodes to electrodes formed on a substrate such as film or paper using a conductive adhesive or an anisotropic conductive adhesive, the electronic components are thermocompression bonded by a face-down method. The method of making the material (thermocompression bonding method) is widely and generally used (for example, Patent Document 1). Specifically, an anisotropic conductive adhesive is applied onto the electrodes formed on the substrate, and a semiconductor having bumps called protruding electrodes is placed so that the bumps are located on the electrodes. The anisotropic conductive adhesive is cured by sandwiching the substrate on which the semiconductor is placed between the upper heat tool and the lower heat tool heated to 180 ° C., and the semiconductor is electrically connected to the electrodes and at the same time on the substrate. A semiconductor is mounted.

しかし、熱圧着法により半導体を基板に実装した場合、ヒートツールの熱により、半導体周辺の基板にゆがみが生じてしまう。このようなゆがみを防ぐための対策として、ヒートツールの温度を下げてゆがみを軽減させる方法も提案されているが、実装時間が延びてしまうため実用的ではない。また、低温硬化接着剤も開発されているが、それでも１３０℃以上に加熱する必要があるため、基板のゆがみを完全に防止することはできない。 However, when a semiconductor is mounted on a substrate by the thermocompression bonding method, the substrate around the semiconductor is distorted due to the heat of the heat tool. As a measure to prevent such distortion, a method of lowering the temperature of the heat tool to reduce the distortion has been proposed, but it is not practical because the mounting time is extended. Further, although a low-temperature curing adhesive has been developed, it is still necessary to heat it to 130 ° C. or higher, so that it is not possible to completely prevent the distortion of the substrate.

半導体を基板に実装する際に加熱を必要としない方法としては、紫外線硬化型樹脂を含む接着剤を用いる方法が知られている（例えば、特許文献２）。 As a method that does not require heating when mounting a semiconductor on a substrate, a method using an adhesive containing an ultraviolet curable resin is known (for example, Patent Document 2).

しかしながら、紫外線硬化型樹脂を含む接着剤には密着性が低いという問題があり、これを改善するためにリン酸基含有モノマーを含有させる方法が提案されている（例えば、特許文献３及び非特許文献１）。しかし、このようなリン酸基含有モノマーを含む紫外線硬化型樹脂を用いた導電性接着剤は、金属を含むと貯蔵安定性（ポットライフ）が短くなるという問題があり、密着性及び貯蔵安定性に優れた、紫外線硬化型樹脂を用いた導電性接着剤の開発が要望されている。 However, the adhesive containing the ultraviolet curable resin has a problem of low adhesion, and in order to improve this, a method of containing a phosphoric acid group-containing monomer has been proposed (for example, Patent Document 3 and non-patent). Document 1). However, a conductive adhesive using an ultraviolet curable resin containing such a phosphoric acid group-containing monomer has a problem that storage stability (pot life) is shortened when it contains a metal, and has adhesion and storage stability. There is a demand for the development of a conductive adhesive using an ultraviolet curable resin, which is excellent in terms of quality.

特開２００３−３０４００３号公報Japanese Unexamined Patent Publication No. 2003-304003 特開２０１５−０５３３１６号公報Japanese Unexamined Patent Publication No. 2015-0533316 特開平０９−２６３７４４号公報Japanese Unexamined Patent Publication No. 09-263744

東亜合成グループ研究年報、第９号、１９〜２４頁、２００６年Toagosei Group Annual Research Report, No. 9, pp. 19-24, 2006

したがって、本発明の目的は、密着性に優れ、更に貯蔵安定性にも優れた、紫外線硬化型樹脂を用いた導電性接着剤、並びに該導電性接着剤を用いた接着構造体及び電子部品を提供することにある。 Therefore, an object of the present invention is to provide a conductive adhesive using an ultraviolet curable resin, which has excellent adhesion and storage stability, and an adhesive structure and electronic components using the conductive adhesive. To provide.

本発明者らは、上記課題に鑑み鋭意研究を重ねた結果、リン酸基含有モノマーを含む紫外線硬化型樹脂を用いた導電性接着剤において、リン酸基含有モノマーに由来する遊離リン酸イオンが貯蔵安定性に影響すること、また、特定のリン酸イオン不活性化剤を含有させることにより、紫外線硬化型樹脂を用いた導電性接着剤の貯蔵安定性が向上することを見出し、本発明を完成するに到った。 As a result of diligent research in view of the above problems, the present inventors have found free phosphate ions derived from the phosphate group-containing monomer in a conductive adhesive using an ultraviolet curable resin containing a phosphate group-containing monomer. We have found that the storage stability of a conductive adhesive using an ultraviolet curable resin is improved by affecting the storage stability and by containing a specific phosphate ion inactivating agent, and the present invention has been made. It has come to be completed.

すなわち、本発明が提供する第１の発明は、（メタ）アクリレート（Ａ）、光重合開始剤（Ｂ）、リン酸基含有モノマー（Ｃ）、リン酸イオン不活性化剤（Ｄ）及び導電性粒子（Ｅ）を含有する導電性接着剤である。 That is, the first invention provided by the present invention includes (meth) acrylate (A), photopolymerization initiator (B), phosphate group-containing monomer (C), phosphate ion inactivating agent (D) and conductivity. It is a conductive adhesive containing the sex particles (E).

また、本発明が提供しようとする第２の発明は、前記第１の発明の導電性接着剤を介して被接着部材同士が接着されている接着構造体である。 Further, the second invention to be provided by the present invention is an adhesive structure in which members to be adhered to each other are adhered to each other via the conductive adhesive of the first invention.

本発明によれば、密着性に優れ、更に貯蔵安定性にも優れた、紫外線硬化型樹脂を用いた導電性接着剤を提供することができる。 According to the present invention, it is possible to provide a conductive adhesive using an ultraviolet curable resin, which has excellent adhesion and storage stability.

本発明の導電性接着剤を用いた電子部品の実装方法によって、基板に実装された電子部品の構成を示す断面図である。It is sectional drawing which shows the structure of the electronic component mounted on the substrate by the mounting method of the electronic component using the conductive adhesive of this invention. 本発明の導電性接着剤を用いた電子部品の実装方法に用いる装置の構成の一例を示す模式図である。It is a schematic diagram which shows an example of the structure of the apparatus used in the mounting method of the electronic component using the conductive adhesive of this invention. 本発明の導電性接着剤を用いた電子部品の実装方法に用いる装置の照射部材の底面図である。It is a bottom view of the irradiation member of the apparatus used in the method of mounting an electronic component using the conductive adhesive of this invention. 本発明の導電性接着剤を用いた電子部品の実装方法によって、基板に実装された電子部品の構成を示す平面図である。It is a top view which shows the structure of the electronic component mounted on the substrate by the method of mounting an electronic component using the conductive adhesive of this invention. 本発明の導電性接着剤を用いた電子部品の実装方法によって基板に電子部品を実装する際に、紫外可視光が直接照射されない非照射領域を説明するための断面図である。It is sectional drawing for demonstrating the non-irradiation region which is not directly irradiated with ultraviolet visible light at the time of mounting an electronic component on a substrate by the method of mounting an electronic component using the conductive adhesive of this invention. 本発明の導電性接着剤を用いた電子部品の実装方法によって基板に別の電子部品を実装する際に、紫外可視光が直接照射されない非照射領域を説明するための断面図である。It is sectional drawing for demonstrating the non-irradiation region which is not directly irradiated with ultraviolet visible light when another electronic component is mounted on a substrate by the method of mounting an electronic component using the conductive adhesive of this invention.

以下、本発明を好ましい実施形態に基づいて説明する。
本発明の導電性接着剤は、（メタ）アクリレート（Ａ）、光重合開始剤（Ｂ）、リン酸基含有モノマー（Ｃ）、リン酸イオン不活性化剤（Ｄ）及び導電性粒子（Ｅ）を含有することを特徴とするものである。換言すれば、（メタ）アクリレート（Ａ）、光重合開始剤（Ｂ）及びリン酸基含有モノマー（Ｃ）からなる紫外線硬化型樹脂（以下、単に「紫外線硬化型樹脂」という場合がある。）と、リン酸イオン不活性化剤（Ｄ）と、導電性粒子（Ｅ）とを含有する導電性接着剤である。 Hereinafter, the present invention will be described based on preferred embodiments.
The conductive adhesive of the present invention includes (meth) acrylate (A), photopolymerization initiator (B), phosphate group-containing monomer (C), phosphate ion inactivating agent (D) and conductive particles (E). ) Is contained. In other words, an ultraviolet curable resin composed of (meth) acrylate (A), a photopolymerization initiator (B) and a phosphoric acid group-containing monomer (C) (hereinafter, may be simply referred to as "ultracurable resin"). A conductive adhesive containing a phosphate ion inactivating agent (D) and conductive particles (E).

［（メタ）アクリレート（Ａ）］
本発明の導電性接着剤に係る（メタ）アクリレート（Ａ）は、紫外可視光が照射されることにより硬化し、上記紫外線硬化型樹脂の主剤となるものであり、（メタ）アクロイル基を少なくとも１つ有する化合物である。（メタ）アクリレート（Ａ）はモノマーであってもオリゴマーであってもよいが、モノマーであることが好ましい。
なお、本発明において、「（メタ）アクリレート」とは、アクリレート及びメタクリレート、すなわちアクリル酸エステル及びメタクリル酸エステルを包含する概念である。 [(Meta) Acrylate (A)]
The (meth) acrylate (A) according to the conductive adhesive of the present invention is cured by being irradiated with ultraviolet-visible light and becomes the main agent of the ultraviolet curable resin, and has at least a (meth) acroyl group. It is a compound having one. The (meth) acrylate (A) may be a monomer or an oligomer, but is preferably a monomer.
In the present invention, "(meth) acrylate" is a concept including acrylate and methacrylate, that is, acrylic acid ester and methacrylic acid ester.

（メタ）アクリレートモノマーとしては、１つの（メタ）アクリロイル基を有する化合物（以下、「単官能(メタ）アクリル系モノマー」ということがある)、及び２つ以上の（メタ）アクリロイル基を有する化合物（以下、「多官能(メタ）アクリル系モノマー」ということがある)挙げられる。本発明においては、公知の（メタ）アクリレートを特に制限なく用いることができる。 As the (meth) acrylate monomer, a compound having one (meth) acryloyl group (hereinafter, may be referred to as “monofunctional (meth) acrylic monomer”), and a compound having two or more (meth) acryloyl groups. (Hereinafter, it may be referred to as "polyfunctional (meth) acrylic monomer"). In the present invention, known (meth) acrylates can be used without particular limitation.

単官能（メタ）アクリル系モノマーとしては、例えば、アルキル（メタ）アクリレート、アルコキシアルキル（メタ）アクリレート、アミノ基を有する（メタ）アクリレート、脂肪族環、芳香族環及び複素環等の環構造を有する（メタ）アクリレート、水酸基を有する（メタ）アクリレート等が挙げられる。 Examples of the monofunctional (meth) acrylic monomer include a ring structure such as an alkyl (meth) acrylate, an alkoxyalkyl (meth) acrylate, a (meth) acrylate having an amino group, an aliphatic ring, an aromatic ring, and a heterocyclic ring. Examples thereof include (meth) acrylate having (meth) acrylate and (meth) acrylate having a hydroxyl group.

アルキル（メタ）アクリレートとしては、例えば、メチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクリレート、イソプロピル（メタ）アクリレート、ブチル（メタ）アクリレート、アミル（メタ）アクリレート、イソブチル（メタ）アクリレート、ｔ−ブチル（メタ）アクリレート、ペンチル（メタ）アクリレート、イソアミル（メタ）アクリレート、ヘキシル（メタ）アクリレート、ヘプチル（メタ）アクリレート、オクチル（メタ）アクリレート、イソオクチル（メタ）アクリレート、２−エチルヘキシル（メタ）アクリレート、ノニル（メタ）アクリレート、デシル（メタ）アクリレート、イソデシル（メタ）アクリレート、ウンデシル（メタ）アクリレート、ドデシル（メタ）アクリレート、ラウリル（メタ）アクリレート、トリデシル（メタ）アクリレート、セチル（メタ）アクリレート、ステアリル（メタ）アクリレート、イソステアリル（メタ）アクリレート、イソミリスチル（メタ）アクリレート等が挙げられる。 Examples of the alkyl (meth) acrylate include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, isopropyl (meth) acrylate, butyl (meth) acrylate, amyl (meth) acrylate, and isobutyl (meth) acrylate. Acrylate, t-butyl (meth) acrylate, pentyl (meth) acrylate, isoamyl (meth) acrylate, hexyl (meth) acrylate, heptyl (meth) acrylate, octyl (meth) acrylate, isooctyl (meth) acrylate, 2-ethylhexyl ( Meta) acrylate, nonyl (meth) acrylate, decyl (meth) acrylate, isodecyl (meth) acrylate, undecyl (meth) acrylate, dodecyl (meth) acrylate, lauryl (meth) acrylate, tridecyl (meth) acrylate, cetyl (meth) Examples thereof include acrylate, stearyl (meth) acrylate, isostearyl (meth) acrylate, and isomyristyl (meth) acrylate.

アルコキシアルキル（メタ）アクリレートとしては、例えば、メトキシエチル（メタ）アクリレート、３−メトキシブチル（メタ）アクリレート、エチルカルビトール（メタ）アクリレート、２−エチルヘキシルカルビトール（メタ）アクリレート、エトキシエトキシエチル（メタ）アクリレート、ブトキシエチル（メタ）アクリレート、メトキシエチレングリコール（メタ）アクリレート、エトキシジエチレングリコール（メタ）アクリレート、エトキシエチル（メタ）アクリレート、メトキシトリエチレングリコール（メタ）アクリレート、メトキシポリエチレングリコール（メタ）アクリレート、メトキシポリプロピレングリコール（メタ）アクリレート等が挙げられる。 Examples of the alkoxyalkyl (meth) acrylate include methoxyethyl (meth) acrylate, 3-methoxybutyl (meth) acrylate, ethyl carbitol (meth) acrylate, 2-ethylhexyl carbitol (meth) acrylate, and ethoxyethoxyethyl (meth) acrylate. ) Acrylate, butoxyethyl (meth) acrylate, methoxyethylene glycol (meth) acrylate, ethoxydiethylene glycol (meth) acrylate, ethoxyethyl (meth) acrylate, methoxytriethylene glycol (meth) acrylate, methoxypolyethylene glycol (meth) acrylate, methoxy Polypropylene glycol (meth) acrylate and the like can be mentioned.

アミノ基を有する（メタ）アクリレートとしては、例えば、ジメチルアミノエチル（メタ）アクリレート、ジエチルアミノエチル（メタ）アクリレート、７−アミノ−３，７−ジメチルオクチル（メタ）アクリレート、ジメチルアクリルアミド、ジエチルアクリルアミド、ヒドロキシエチルアクリルアミド、アクリロイルモルホリン、イソプロピルアクリルアミド、ジメチルアミノプロリルアクリルアミド等が挙げられる。 Examples of the (meth) acrylate having an amino group include dimethylaminoethyl (meth) acrylate, diethylaminoethyl (meth) acrylate, 7-amino-3,7-dimethyloctyl (meth) acrylate, dimethylacrylamide, diethylacrylamide, and hydroxy. Examples thereof include ethyl acrylamide, acryloyl morpholine, isopropyl acrylamide, dimethylaminoprolyl acrylamide and the like.

脂肪族環、芳香族環及び複素環等の環構造を有する（メタ）アクリレートとしては、例えば、トリシクロデカン（メタ）アクリレート、ジシクロペンテニル（メタ）アクリレート、イソボロニル（メタ）アクリレート、アダマンチル（メタ）アクリレート、フェニル（メタ）アクリレート、ベンジル（メタ）アクリレート、テトラヒドロフルフリル（メタ）アクリレート、モルフォリンアクリレート、フェニルグリシジル（メタ）アクリレート、アクリロイルオキシエチルヘキサヒドロフタルイミド、（２−メチル−２−エチル−１，３−ジオキソラン−４−イル）メチルアクリレート、テトラヒドロフルフリルアクリレート等が挙げられる。
また、これら（メタ）アクリレートのアルキレンオキサイド変性物も使用することもできる。 Examples of the (meth) acrylate having a ring structure such as an aliphatic ring, an aromatic ring and a heterocyclic ring include tricyclodecane (meth) acrylate, dicyclopentenyl (meth) acrylate, isobolonyl (meth) acrylate, and adamantyl (meth). ) Acrylate, phenyl (meth) acrylate, benzyl (meth) acrylate, tetrahydrofurfuryl (meth) acrylate, morpholine acrylate, phenylglycidyl (meth) acrylate, acryloyloxyethyl hexahydrophthalimide, (2-methyl-2-ethyl-) 1,3-Dioxolan-4-yl) methyl acrylate, tetrahydrofurfuryl acrylate and the like can be mentioned.
In addition, alkylene oxide-modified products of these (meth) acrylates can also be used.

水酸基を有する（メタ）アクリレートとしては、例えば、炭素数が２〜９の脂肪族基に水酸基の結合した（メタ）アクリレート等が挙げられる。該（メタ）アクリレートにはフェノキシ基のような置換基が結合していてもよい。上記（メタ）アクリレートとしては、例えば２−ヒドロキシエチル（メタ）アクリレート、３−ヒドロキシプロピル（メタ）アクリレート、４−ヒドロキシブチル（メタ）アクリレート及び２−ヒドロキシ−３−フェノキシプロピル（メタ）アクリレート等が挙げられる。 Examples of the (meth) acrylate having a hydroxyl group include (meth) acrylate in which a hydroxyl group is bonded to an aliphatic group having 2 to 9 carbon atoms. Substituents such as phenoxy groups may be attached to the (meth) acrylate. Examples of the (meth) acrylate include 2-hydroxyethyl (meth) acrylate, 3-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, and 2-hydroxy-3-phenoxypropyl (meth) acrylate. Can be mentioned.

多官能（メタ）アクリル系モノマーには、２官能（メタ）アクリル系モノマーと３官能以上の（メタ）アクリル系モノマーが含まれる。２官能（メタ）アクリル系モノマーとしては、例えば、炭素数が４〜９の脂肪族ジオールの（メタ）アクリレート化合物、アルキレンオキサイド型（メタ）アクリレート化合物及び環構造を有する（メタ）アクリレート化合物等が挙げられる。 The polyfunctional (meth) acrylic monomer includes a bifunctional (meth) acrylic monomer and a trifunctional or higher functional (meth) acrylic monomer. Examples of the bifunctional (meth) acrylic monomer include (meth) acrylate compounds of aliphatic diols having 4 to 9 carbon atoms, alkylene oxide type (meth) acrylate compounds, and (meth) acrylate compounds having a ring structure. Can be mentioned.

炭素数が４〜９の脂肪族ジオールのアクリレート化合物としては、例えば、ネオペンチルグリコールジ（メタ）アクリレート及び１，６−ヘキサンジオールジ（メタ）アクリレート等が挙げられる。これら脂肪族ジオールの（メタ）アクリレートは、脂肪族エステルやアルキレンオキサイドによって変性されていてもよい。脂肪族エステル変性（メタ）アクリレート化合物としては、例えば、ネオペンチルグリコールヒドロキシピバリン酸ジ（メタ）アクリレート及びカプロラクトン変性ネオペンチルグリコールヒドロキシピバリン酸ジ（メタ）アクリレート等が挙げられる。アルキレンオキサイド変性（メタ）アクリレート化合物としては、例えば、ジエチレンオキサイド変性ネオペンチルグリコールジ（メタ）アクリレート、ジプロピレンオキサイド変性ネオペンチルグリコールジ（メタ）アクリレート、ジエチレンオキサイド変性１，６−ヘキサンジオールジ（メタ）アクリレート及びジプロピレンオキサイド変性１，６−ヘキサンジオールジ（メタ）アクリレート等が挙げられる。 Examples of the acrylate compound of the aliphatic diol having 4 to 9 carbon atoms include neopentyl glycol di (meth) acrylate and 1,6-hexanediol di (meth) acrylate. The (meth) acrylate of these aliphatic diols may be modified with an aliphatic ester or an alkylene oxide. Examples of the aliphatic ester-modified (meth) acrylate compound include neopentyl glycol hydroxypivalate di (meth) acrylate and caprolactone-modified neopentyl glycol hydroxypivalate di (meth) acrylate. Examples of the alkylene oxide-modified (meth) acrylate compound include diethylene oxide-modified neopentyl glycol di (meth) acrylate, dipropylene oxide-modified neopentyl glycol di (meth) acrylate, and diethylene oxide-modified 1,6-hexanediol di (meth). ) Acrylate and dipropylene oxide-modified 1,6-hexanediol di (meth) acrylate and the like can be mentioned.

アルキレンオキサイド型（メタ）アクリレート化合物としては、例えば、ネオペンチルグリコール変性トリメチロールプロパンジ（メタ）アクリレート、ポリエチレングリコールジ（メタ）アクリレート及びポリプロピレングリコールジ（メタ）アクリレート等が挙げられる。 Examples of the alkylene oxide type (meth) acrylate compound include neopentyl glycol-modified trimethylolpropane di (meth) acrylate, polyethylene glycol di (meth) acrylate, and polypropylene glycol di (meth) acrylate.

環構造を有する（メタ）アクリレート化合物としては、例えば、トリシクロデカンジメチロールジ（メタ）アクリレート及びジシクロペンタニルジ（メタ）アクリレート等が挙げられる。 Examples of the (meth) acrylate compound having a ring structure include tricyclodecanedimethyloldi (meth) acrylate and dicyclopentanyldi (meth) acrylate.

３官能以上の（メタ）アクリル系モノマーとしては、例えば、トリメチロールプロパントリ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、炭素数２〜５の脂肪族変性ジペンタエリスリトールペンタ（メタ）アクリレート、炭素数２〜５の脂肪族変性ジペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールペンタ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、カプロラクトン変性ジペンタエリスリトールヘキサ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、トリス〔（メタ）アクリロキシエチル〕イソシアヌレート、カプロラクトン変性トリス〔（メタ）アクリロキシエチル〕イソシアヌレート及びジトリメチロールプロパンテトラ（メタ）アクリレート、エトキシ化トリメチロールプロハントリアクリレート、トリメチロールプロパンプロピレンオキサイド変性トリアクリレート、エトキシ化グリセリントリアクリレート、並びにイソシアヌル酸エチレンオキサイド変性ジ及びトリアクリレート等が挙げられる。 Examples of the trifunctional or higher functional (meth) acrylic monomer include trimethylpropantri (meth) acrylate, pentaerythritol tri (meth) acrylate, and aliphatic modified dipentaerythritol penta (meth) acrylate having 2 to 5 carbon atoms. Aliphatic-modified dipentaerythritol tetra (meth) acrylate having 2 to 5 carbon atoms, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, caprolactone-modified dipentaerythritol hexa (meth) acrylate, pentaerythritol tetra (Meta) Acrylate, Tris [(Meta) Acryloxyethyl] Isocyanurate, Caprolactone Modified Tris [(Meta) Acryloxyethyl] Isocyanurate and Ditrimethylol Propantetra (Meta) Acrylate, Trimethylol Prohantriacrylate, Trimethylol Examples thereof include propanepropylene oxide-modified triacrylate, ethoxylated glycerin triacrylate, and isocyanurate ethylene oxide-modified di and triacrylate.

本発明においては、単官能（メタ）アクリル系モノマーと多官能（メタ）アクリル系モノマーとを併用することが、硬化物の硬度、耐熱性及び収縮性の観点から好ましい。この場合の多官能（メタ）アクリル系モノマーの配合割合は、単官能（メタ）アクリル系モノマー１００質量部に対して５〜８０質量部が好ましく、１０〜６０質量部とすることが、柔軟性と収縮性のバランスの観点から、より好ましい。 In the present invention, it is preferable to use a monofunctional (meth) acrylic monomer and a polyfunctional (meth) acrylic monomer in combination from the viewpoint of hardness, heat resistance and shrinkage of the cured product. In this case, the blending ratio of the polyfunctional (meth) acrylic monomer is preferably 5 to 80 parts by mass with respect to 100 parts by mass of the monofunctional (meth) acrylic monomer, and the flexibility is preferably 10 to 60 parts by mass. It is more preferable from the viewpoint of the balance between shrinkage and shrinkage.

本発明においては、（メタ）アクリレート（Ａ）として、基材に対する密着性を向上させるため、上記（メタ）アクリレートモノマーと（メタ）アクリレートオリゴマーを併用することができる。 In the present invention, the (meth) acrylate monomer and the (meth) acrylate oligomer can be used in combination as the (meth) acrylate (A) in order to improve the adhesion to the substrate.

本発明で用いる（メタ）アクリレートオリゴマーは、上記（メタ）アクリレートモノマーに溶解するものが好ましく、このようなオリゴマーとしては、例えば、エポキシ（メタ）アクリレート、ポリエステル（メタ）アクリレート及びウレタン（メタ）アクリレート等が挙げられる。なお、本発明においてオリゴマーとは、分子量５００以上のものをいう。 The (meth) acrylate oligomer used in the present invention is preferably one that dissolves in the above (meth) acrylate monomer, and examples of such oligomers include epoxy (meth) acrylate, polyester (meth) acrylate and urethane (meth) acrylate. And so on. In the present invention, the oligomer means an oligomer having a molecular weight of 500 or more.

エポキシ（メタ）アクリレートは、エポキシ樹脂と（メタ）アクリル酸との反応によって得られるものである。エポキシ樹脂としては、例えばビスフェノールＡ型エポキシ樹脂及びビスフェノールＦ型エポキシ樹脂等のビスフェノール型エポキシ樹脂、並びにノボラック型エポキシ樹脂等が挙げられる。 Epoxy (meth) acrylate is obtained by reacting an epoxy resin with (meth) acrylic acid. Examples of the epoxy resin include bisphenol type epoxy resins such as bisphenol A type epoxy resin and bisphenol F type epoxy resin, and novolak type epoxy resins.

ポリエステル（メタ）アクリレートは、ポリエステルポリオールと（メタ）アクリル酸との反応によって得られるものである。ポリエステルポリオールは、多価アルコールと多塩基酸との反応によって得られるものである。多価アルコールとしては、例えば、ネオペンチルグリコール、エチレングリコール、プロピレングリコール、１，６−ヘキサンジオール、トリメチロールプロパン、ペンタエリスリトール、トリシクロデカンジメチロール及びビス（ヒドロキシメチル）シクロヘキサン等が挙げられる。多塩基酸としては、例えば、コハク酸、フタル酸、ヘキサヒドロ無水フタル酸、テレフタル酸、アジピン酸、アゼライン酸及びテトラヒドロ無水フタル酸等が挙げられる。 The polyester (meth) acrylate is obtained by reacting a polyester polyol with (meth) acrylic acid. The polyester polyol is obtained by reacting a polyhydric alcohol with a polybasic acid. Examples of the polyhydric alcohol include neopentyl glycol, ethylene glycol, propylene glycol, 1,6-hexanediol, trimethylolpropane, pentaerythritol, tricyclodecanedimethylol and bis (hydroxymethyl) cyclohexane. Examples of the polybasic acid include succinic acid, phthalic acid, hexahydrophthalic anhydride, terephthalic acid, adipic acid, azelaic acid, tetrahydrophthalic anhydride and the like.

ウレタン（メタ）アクリレートは、ポリオールと有機ポリイソシアネートとヒドロキシ（メタ）アクリレート化合物との３成分の反応、又はポリオールを使用せずに有機ポリイソシアネートとヒドロキシ（メタ）アクリレート化合物との２成分の反応によって得られるものである。ポリオールとしては、ポリプロピレングリコール、ポリテトラメチレングリコール等のポリエーテルポリオール、前記多価アルコールと前記多塩基酸との反応によって得られるポリエステルポリオール、前記多価アルコールと前記多塩基酸とε−カプロラクトンとの反応によって得られるカプロラクトンポリオール、及びポリカーボネートポリオール（例えば、１，６−ヘキサンジオールとジフェニルカーボネートとの反応によって得られるポリカーボネートポリオール）等が挙げられる。有機ポリイソシアネートとしては、例えばイソホロンジイソシアネート、ヘキサメチレンジイソシアネート、トリレンジイソシアネート、キシレンジイソシアネート、ジフェニルメタン−４，４’−ジイソシアネート及びジシクロペンタニルジイソシアネート等が挙げられる。 Urethane (meth) acrylate is produced by a three-component reaction of a polyol, an organic polyisocyanate, and a hydroxy (meth) acrylate compound, or a two-component reaction of an organic polyisocyanate and a hydroxy (meth) acrylate compound without using a polyol. It is what you get. Examples of the polyol include polyether polyols such as polypropylene glycol and polytetramethylene glycol, polyester polyols obtained by reacting the polyhydric alcohol with the polybasic acid, and the polyhydric alcohol, the polybasic acid, and ε-caprolactone. Examples thereof include caprolactone polyol obtained by the reaction and polycarbonate polyol (for example, polycarbonate polyol obtained by the reaction of 1,6-hexanediol and diphenyl carbonate). Examples of the organic polyisocyanate include isophorone diisocyanate, hexamethylene diisocyanate, tolylene diisocyanate, xylene diisocyanate, diphenylmethane-4,4'-diisocyanate and dicyclopentanyl diisocyanate.

これらの（メタ）アクリレートモノマー及び（メタ）アクリレートオリゴマーは、１種のみを使用してもよく、２種以上を任意の割合で混合して使用することもできる。 As these (meth) acrylate monomers and (meth) acrylate oligomers, only one kind may be used, or two or more kinds may be mixed and used at an arbitrary ratio.

また、本発明においては、これらの（メタ）アクリレートモノマー及び（メタ）アクリレートオリゴマーと、アミノ基を有する（メタ）アクリレート、Ｎ−アクリロイルオキシエチルヘキサヒドロフタルイミド、イソシアヌル酸エチレンオキサイド変性ジ及びトリアクリレート、ウレタン（メタ）アクリレート等の窒素原子を含む（メタ）アクリル系モノマー及び／又は（メタ）アクリレートオリゴマーとを併用することが、更に密着性、耐熱性及び硬度を向上させる観点から好ましい。窒素原子を含む（メタ）アクリル系モノマー及び／又は（メタ）アクリレートオリゴマーを併用する場合、窒素原子を含む（メタ）アクリル系モノマーの配合割合は、（メタ）アクリレート（Ａ）中、１５質量％〜９５質量％であることが好ましく、２０〜８０質量％とすることが、密着性をいっそう向上させる観点から好ましい。 Further, in the present invention, these (meth) acrylate monomers and (meth) acrylate oligomers, (meth) acrylate having an amino group, N-acryloyloxyethyl hexahydrophthalimide, isocyanurate ethylene oxide-modified di and triacrylate, It is preferable to use a (meth) acrylic monomer containing a nitrogen atom such as urethane (meth) acrylate and / or a (meth) acrylate oligomer in combination from the viewpoint of further improving adhesion, heat resistance and hardness. When a (meth) acrylic monomer containing a nitrogen atom and / or a (meth) acrylate oligomer is used in combination, the blending ratio of the (meth) acrylic monomer containing a nitrogen atom is 15% by mass in the (meth) acrylate (A). It is preferably ~ 95% by mass, and preferably 20 to 80% by mass from the viewpoint of further improving the adhesion.

（メタ）アクリレート（Ａ）の導電性接着剤中の配合量は１５〜９５質量％が好ましく、３０〜９０質量％とすることが、硬化性及び密着性の観点から、より好ましい。 The blending amount of the (meth) acrylate (A) in the conductive adhesive is preferably 15 to 95% by mass, more preferably 30 to 90% by mass from the viewpoint of curability and adhesion.

［光重合開始剤（Ｂ）］
本発明の導電性接着剤に係る光重合開始剤（Ｂ）は、上記紫外線硬化型樹脂を効率的に光硬化させる成分である。本発明で用いることができる光重合開始剤（Ｂ）は特に制限されないが、例えば、２−ベンジル−２−ジメチルアミノ−１−（４−モルホリノフェニル）−１−ブタノン、２−（ジメチルアミノ）−２−［（４−メチルフェニル）メチル］−［４−（４−モルホリニル）フェニル］−１−ブタノン、２−メチル−１−［４−（メチルチオ）フェニル］−２−モルホリノプロパン−１−オン、ベンゾフェノン、メチルベンゾフェノン、ｏ−ベンゾイル安息香酸、ベンゾイルエチルエーテル、２，２−ジエトキシアセトフェノン、２，４−ジエチルチオキサントン、ジフェニル−（２，４，６−トリメチルベンゾイル）ホスフィンオキシド、エチル−（２，４，６−トリメチルベンゾイル）フェニルホスフィネート、４，４’−ビス（ジエチルアミノ）ベンゾフェノン、１−ヒドロキシシクロヘキシル−フェニルケトン、２，２−ジメトキシ−１，２−ジフェニルエタン−１−オン、１−［４−（２−ヒドロキシエトキシ）−フェニル］−２−ヒドロキシ−２−メチル−１−プロパン−１−オン、２,２−ジメトキシ−２−フェニルアセトフェノール及び１−［４−（２−ヒドロキシエトキシ）−フェニル］−２−ヒドロキシ−２−メチル−１−プロパン−１−オン等のアルキルフェノン系光重合開始剤、ビス（２，４，６−トリメチルベンゾイル）−フェニルホスフィンオキサイド及びジフェニル（２，４，６−トリメチルベンゾイル）ホスフィンオキシド等のアシルフォスフィンオキサイド系光重合開始剤、１，２−オクタンジオン，１−［４−（フェニルチオ）−２−（Ｏ−ベンゾイルオキシム）］等のオキシムエステル系光重合開始剤、並びにスルホニウム塩系光重合開始剤等が挙げられる。これらの光重合開始剤は、１種のみを使用してもよく、２種以上を任意の割合で混合して使用することもできる。 [Photopolymerization Initiator (B)]
The photopolymerization initiator (B) according to the conductive adhesive of the present invention is a component that efficiently photocures the ultraviolet curable resin. The photopolymerization initiator (B) that can be used in the present invention is not particularly limited, and is, for example, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -1-butanone, 2- (dimethylamino). -2-[(4-Methylphenyl) methyl]-[4- (4-morpholinyl) phenyl] -1-butanone, 2-methyl-1- [4- (methylthio) phenyl] -2-morpholinopropane-1- On, benzophenone, methylbenzophenone, o-benzoylbenzoic acid, benzoylethyl ether, 2,2-diethoxyacetophenone, 2,4-diethylthioxanthone, diphenyl- (2,4,6-trimethylbenzoyl) phosphenyl oxide, ethyl-( 2,4,6-trimethylbenzoyl) phenylphosphinate, 4,4'-bis (diethylamino) benzophenone, 1-hydroxycyclohexyl-phenylketone, 2,2-dimethoxy-1,2-diphenylethane-1-one, 1, -[4- (2-Hydroxyethoxy) -phenyl] -2-hydroxy-2-methyl-1-propane-1-one, 2,2-dimethoxy-2-phenylacetophenol and 1- [4- (2-) Hydroxyethoxy) -phenyl] -2-hydroxy-2-methyl-1-propane-1-one and other alkylphenone-based photopolymerization initiators, bis (2,4,6-trimethylbenzoyl) -phenylphosphine oxide and diphenyl (2,4,6-trimethylbenzoyl) Acylphosphine oxide-based photopolymerization initiators such as 2,4,6-trimethylbenzoyl) phosphine oxide, 1,2-octanedione, 1- [4- (phenylthio) -2- (O-benzoyloxime)], etc. Examples thereof include an oxime ester-based photopolymerization initiator and a sulfonium salt-based photopolymerization initiator. Only one of these photopolymerization initiators may be used, or two or more of these photopolymerization initiators may be mixed and used at an arbitrary ratio.

本発明においては、光重合開始剤（Ｂ）としてアルキルフェノン系光重合開始剤を使用することが、硬化性の観点から好ましく、特に１−ヒドロキシシクロヘキシル−フェニルケトンを使用することが好ましい。 In the present invention, it is preferable to use an alkylphenone-based photopolymerization initiator as the photopolymerization initiator (B) from the viewpoint of curability, and it is particularly preferable to use 1-hydroxycyclohexyl-phenylketone.

前記光重合開始剤（Ｂ）の使用量は、（メタ）アクリレート（Ａ）１００質量部に対して０．５〜１５質量部が好ましく、１〜１２質量部とすることが、硬化性の観点から、より好ましい。 The amount of the photopolymerization initiator (B) used is preferably 0.5 to 15 parts by mass, preferably 1 to 12 parts by mass with respect to 100 parts by mass of the (meth) acrylate (A), from the viewpoint of curability. Therefore, it is more preferable.

［リン酸基含有モノマー（Ｃ）］
本発明の導電性接着剤に係るリン酸基含有モノマー（Ｃ）は、上記紫外線硬化型樹脂の密着性向上に寄与する成分である。本発明で用いることができるリン酸基含有モノマー（Ｃ）は、特に制限されず、重合性の官能基を有し、かつリン酸基を有するモノマーであればよい。 [Phosphate group-containing monomer (C)]
The phosphoric acid group-containing monomer (C) according to the conductive adhesive of the present invention is a component that contributes to improving the adhesion of the ultraviolet curable resin. The phosphoric acid group-containing monomer (C) that can be used in the present invention is not particularly limited as long as it is a monomer having a polymerizable functional group and having a phosphoric acid group.

リン酸基含有モノマー（Ｃ）としては、例えば、２-メタクリロイロキシエチルアシッドホスフェート、ジ−２−メタクリロイロキシエチルアシッドホスフェート、３−メタクリロイロキシプロピルアシッドホスフェート、ジ−３−メタクリロイロキシプロピルアシッドホスフェート、エチレンオキサイド変性リン酸ジメタクリレート、リン酸含有エポキシメタクリレート等のリン酸（メタ）アクリレート類、ビニルホスホン酸などのリン酸ビニル化合物等が挙げられる。 Examples of the phosphate group-containing monomer (C) include 2-methacryloyloxyethyl acid phosphate, di-2-methacryloyloxyethyl acid phosphate, 3-methacryloyloxypropyl acid phosphate, and di-3-methacryloyloxypropyl. Examples thereof include acid phosphate, ethylene oxide-modified dimethacrylate phosphate, phosphate (meth) acrylates such as phosphoric acid-containing epoxy methacrylate, and vinyl phosphate compounds such as vinylphosphonic acid.

リン酸基含有モノマー（Ｃ）としては、下記一般式（１）又は（２）で表されるリン酸（メタ）アクリレートが好ましい。 As the phosphoric acid group-containing monomer (C), a phosphoric acid (meth) acrylate represented by the following general formula (1) or (2) is preferable.

Figure 0006946395
（式中、Ｒ１は水素原子又はメチル基を示す。Ａは炭素数１〜４の直鎖状又は分岐状のアルキレン基を示す。ｍは１〜４、好ましくは１〜２の整数を示す。）
Figure 0006946395
 (In the formula, R 1 represents a hydrogen atom or a methyl group. A represents a linear or branched alkylene group having 1 to 4 carbon atoms. M represents an integer of 1 to 4, preferably 1 to 2. .)

これらのリン酸基含有モノマーは、１種のみを使用してもよく、２種以上を任意の割合で混合して使用することもできる。 Only one kind of these phosphoric acid group-containing monomers may be used, or two or more kinds may be mixed and used at an arbitrary ratio.

リン酸基含有モノマー（Ｃ）の配合量は、（メタ）アクリレート（Ａ）１００質量部に対して０．５〜５０質量部が好ましく、３〜３０質量部とすることが、密着性を向上させる観点から、より好ましい。 The blending amount of the phosphoric acid group-containing monomer (C) is preferably 0.5 to 50 parts by mass with respect to 100 parts by mass of the (meth) acrylate (A), and 3 to 30 parts by mass improves the adhesion. It is more preferable from the viewpoint of making it.

［リン酸イオン不活性化剤（Ｄ）］
本発明の導電性接着剤に係るリン酸イオン不活性化剤（Ｄ）は、上記紫外線硬化型樹脂と導電性粒子とを含む導電性接着剤に貯蔵安定性を付与する成分であり、具体的には、リン酸基含有モノマー（Ｃ）に由来する遊離リン酸イオンを不活性化して、他の成分との反応を抑制することにより貯蔵安定性を付与する成分である。本発明で用いることができるリン酸イオン不活性化剤（Ｄ）は、遊離リン酸イオンを不活性化できるものであればよく、リン酸イオンを吸着して不活性化する化合物及びリン酸イオンと反応して不活性化する化合物等が挙げられる。 [Phosphate ion inactivating agent (D)]
The phosphate ion inactivating agent (D) according to the conductive adhesive of the present invention is a component that imparts storage stability to the conductive adhesive containing the ultraviolet curable resin and conductive particles, and is specific. Is a component that imparts storage stability by inactivating free phosphate ions derived from the phosphate group-containing monomer (C) and suppressing the reaction with other components. The phosphate ion inactivating agent (D) that can be used in the present invention may be any as long as it can inactivate free phosphate ions, and is a compound that adsorbs and inactivates phosphate ions and phosphate ions. Examples thereof include compounds that react with and inactivate.

リン酸イオンを吸着して不活性化する化合物としては、活性アルミナ、シリカゲル、ゼオライト、粘度鉱物、活性炭、活性白土、珪藻土及びセライト等が挙げられる。これらのＢＥＴ比表面積は５０〜７００ｍ２／ｇであることが好ましく、１００〜５００ｍ２／ｇであることが、遊離リン酸イオンの吸着性の観点から、より好ましい。 Examples of the compound that adsorbs and inactivates phosphate ions include activated alumina, silica gel, zeolite, viscous mineral, activated charcoal, activated clay, diatomaceous earth, and celite. Preferably these BET specific surface area is 50~700m 2 / g, it is, from the viewpoint of adsorption of free phosphate ions, more preferably from 100 to 500 m 2 / g.

リン酸イオンと反応して不活性化する化合物としては、例えば、Ｚｎ、Ａｌ、Ｂａ、Ｃａ、Ｍｇ、Ｚｒ、Ｔｉ、Ｓｎ、Ｓｉ、Ｉｎ、Ｃｅ、Ａｇ及びＹｂから選ばれる金属元素を１種又は２種以上含有する無機金属化合物が挙げられる。前記無機金属化合物としては、前記金属元素の酸化物、水酸化物、炭酸塩、硝酸塩、硫酸塩、珪酸塩等が挙げられ、また、金属元素を２種以上含む複合塩であってよく、無水物であっても含水物であってもよい。更に前記無機金属化合物は多孔質のものであってもよい。これらの無機金属化合物は、２種以上を併用することもできる。無機金属化合物の物性は、特に制限されるものではないが、導電性接着剤中に均一分散させ、リン酸イオンを効率的に粒子表面に固定化させる観点から、ＢＥＴ比表面積が０．１ｍ２／ｇ以上であることが好ましく、０．１〜２００ｍ２／ｇであることがより好ましく、０．３〜１００ｍ２／ｇであることが特に好ましい。 As the compound that reacts with the phosphate ion and inactivates, for example, one kind of metal element selected from Zn, Al, Ba, Ca, Mg, Zr, Ti, Sn, Si, In, Ce, Ag and Yb. Alternatively, an inorganic metal compound containing two or more kinds can be mentioned. Examples of the inorganic metal compound include oxides, hydroxides, carbonates, nitrates, sulfates, silicates and the like of the metal element, and may be a composite salt containing two or more kinds of metal elements, and are anhydrous. It may be a substance or a hydrous substance. Further, the inorganic metal compound may be porous. Two or more of these inorganic metal compounds can be used in combination. The physical properties of the inorganic metal compound are not particularly limited, but the BET specific surface area is 0.1 m 2 from the viewpoint of uniformly dispersing the inorganic metal compound in the conductive adhesive and efficiently immobilizing the phosphate ions on the particle surface. / preferably g or more, more preferably 0.1～200M 2 / g, particularly preferably 0.3~100m 2 / g.

リン酸イオン不活性化剤（Ｄ）は、導電性接着剤中に均一に分散させ、紫外可視光を内部まで到達させる観点から、レーザー回析・散乱式粒度分布測定法により求められる平均粒子径が１００μｍ以下であることが好ましく、０．０１〜６０μｍであることがより好ましい。 The phosphate ion inactivating agent (D) is uniformly dispersed in the conductive adhesive, and the average particle size obtained by the laser diffraction / scattering particle size distribution measurement method from the viewpoint of allowing ultraviolet visible light to reach the inside. Is preferably 100 μm or less, and more preferably 0.01 to 60 μm.

本発明においては、リン酸イオン不活性化剤（Ｄ）として、活性アルミナが、リン酸イオンを吸着して固定化する能力に優れているため好ましい。また、酸化亜鉛などの亜鉛化合物が、リン酸イオンとの反応性に優れ、粒子表面にリン酸イオンを固定化する能力にも優れているため好ましい。 In the present invention, activated alumina is preferable as the phosphate ion inactivating agent (D) because it has an excellent ability to adsorb and immobilize phosphate ions. Further, a zinc compound such as zinc oxide is preferable because it has excellent reactivity with phosphate ions and also has an excellent ability to immobilize phosphate ions on the particle surface.

リン酸イオン不活性化剤（Ｄ）の配合量は、リン酸基含有モノマー（Ｃ）１００質量部に対して０．５〜２０質量部が好ましく、１〜１０質量部とすることが、貯蔵安定性及び密着性の観点から、より好ましい。 The amount of the phosphate ion inactivating agent (D) to be blended is preferably 0.5 to 20 parts by mass with respect to 100 parts by mass of the phosphate group-containing monomer (C), and is preferably 1 to 10 parts by mass. More preferable from the viewpoint of stability and adhesion.

［導電性粒子（Ｅ）］
本発明の導電性接着剤に係る導電性粒子（Ｅ）は、導電性を付与する成分である。本発明においては、導電性粒子（Ｅ）として、導電性接着剤、異方性導電膜、異方導電性接着剤に使用されている公知のものを用いることができる。導電性粒子（Ｅ）としては、例えば、金、銀、銅、ニッケル、パラジウム、ハンダ等の金属粒子、カーボン粒子のようなそれ自体で導電性を有するもの、芯材粒子の表面を導電性金属で被覆処理した導電性粒子等が挙げられる。 [Conductive particles (E)]
The conductive particles (E) according to the conductive adhesive of the present invention are components that impart conductivity. In the present invention, as the conductive particles (E), known particles used in a conductive adhesive, an anisotropic conductive film, and an anisotropic conductive adhesive can be used. Examples of the conductive particles (E) include metal particles such as gold, silver, copper, nickel, palladium, and solder, those having conductivity by themselves such as carbon particles, and conductive metals on the surface of the core material particles. Examples thereof include conductive particles coated with.

導電性粒子の大きさは、本発明の導電性接着剤の具体的な用途に応じて適切に選択すればよいが、電子回路接続用の導電材料として用いる場合には、粒径が小さすぎると対向電極間での導通ができなくなり、一方、大きすぎると隣接電極間の短絡が発生する。そのため、導電性粒子の平均粒子径は、電気抵抗法を用いて測定された値で０．１〜１０００μｍが好ましく、０．５〜１００μｍが特に好ましい。 The size of the conductive particles may be appropriately selected according to the specific use of the conductive adhesive of the present invention, but when used as a conductive material for connecting an electronic circuit, the particle size is too small. Conduction between the counter electrodes becomes impossible, while if it is too large, a short circuit occurs between the adjacent electrodes. Therefore, the average particle size of the conductive particles is preferably 0.1 to 1000 μm, particularly preferably 0.5 to 100 μm, as a value measured by the electric resistance method.

導電性粒子の形状は、特に制限はないが、一般に粉粒状であり、それ以外の形状、例えば繊維状、中空状、板状、針状であってもよく、粒子表面に多数の突起を有するものや不定形のものであってもよい。分散性の観点からは、導電性粒子の形状は球状であることが好ましい。 The shape of the conductive particles is not particularly limited, but is generally powdery and granular, and may have other shapes such as fibrous, hollow, plate-like, and needle-like, and has a large number of protrusions on the particle surface. It may be a thing or an irregular shape. From the viewpoint of dispersibility, the shape of the conductive particles is preferably spherical.

本発明の導電性接着剤を、異方導電性接着剤として使用する場合、導電性粒子（Ｅ）は、芯材粒子の表面を導電性金属で被覆処理した金属被覆粒子であることが好ましい。 When the conductive adhesive of the present invention is used as an anisotropic conductive adhesive, the conductive particles (E) are preferably metal-coated particles in which the surface of the core material particles is coated with a conductive metal.

芯材粒子としては、無機物であっても有機物であっても特に制限なく用いることができる。無機物の芯材粒子としては、金、銀、銅、ニッケル、パラジウム、ハンダ等の金属粒子、合金、ガラス、セラミックス、シリカ、金属又は非金属の酸化物（含水物も含む）、アルミノ珪酸塩を含む金属珪酸塩、金属炭化物、金属窒化物、金属炭酸塩、金属硫酸塩、金属リン酸塩、金属硫化物、金属酸塩、金属ハロゲン化物及び炭素等が挙げられる。有機物の芯材粒子としては、例えば、天然繊維、天然樹脂、ポリエチレン、ポリプロピレン、ポリ塩化ビニル、ポリスチレン、ポリブテン、ポリアミド、ポリアクリル酸エステル、ポリアクリルニトリル、ポリアセタール、アイオノマー、ポリエステルなどの熱可塑性樹脂、アルキッド樹脂、フェノール樹脂、尿素樹脂、ベンゾグアナミン樹脂、メラミン樹脂、キシレン樹脂、シリコーン樹脂、エポキシ樹脂及びジアリルフタレート樹脂等が挙げられる。芯材粒子として樹脂を用いると、金属被覆粒子の比重が軽くなるために沈降しにくく、分散安定性が良好となり、また、樹脂の弾性による電気接続の維持が可能とため好ましい。 The core material particles may be inorganic or organic without particular limitation. Examples of the inorganic core particles include metal particles such as gold, silver, copper, nickel, palladium, and solder, alloys, glass, ceramics, silica, metal or non-metal oxides (including hydrous substances), and aluminosilicates. Examples thereof include metal silicates, metal carbides, metal nitrides, metal carbonates, metal sulfates, metal phosphates, metal sulfides, metal acid salts, metal halides and carbons. Examples of the organic core particles include thermoplastic resins such as natural fibers, natural resins, polyethylene, polypropylene, polyvinyl chloride, polystyrene, polybutene, polyamide, polyacrylic acid ester, polyacrylic nitrile, polyacetal, ionomer, and polyester. Examples thereof include alkyd resin, phenol resin, urea resin, benzoguanamine resin, melamine resin, xylene resin, silicone resin, epoxy resin and diallyl phthalate resin. It is preferable to use a resin as the core material particles because the specific gravity of the metal-coated particles becomes lighter, so that they are less likely to settle, the dispersion stability is improved, and the electrical connection can be maintained by the elasticity of the resin.

芯材粒子の形状は、特に制限はないが、一般に粉粒状であり、それ以外の形状、例えば繊維状、中空状、板状、針状であってもよく、粒子表面に多数の突起を有するものや不定形のものであってもよい。分散性の観点からは、導電性粒子の形状は球状であることが好ましい。 The shape of the core material particles is not particularly limited, but is generally powdery and granular, and may have other shapes such as fibrous, hollow, plate-like, and needle-like, and has a large number of protrusions on the particle surface. It may be a thing or an irregular shape. From the viewpoint of dispersibility, the shape of the conductive particles is preferably spherical.

芯材粒子の大きさは、電気抵抗法を用いて測定された値で０．１〜１０００μｍが好ましく、０．５〜１００μｍが特に好ましい。粒径が小さすぎると対向電極間での導通ができなくなり、一方、大きすぎると隣接電極間の短絡が発生する。 The size of the core material particles is preferably 0.1 to 1000 μm, particularly preferably 0.5 to 100 μm, as measured by the electric resistance method. If the particle size is too small, conduction between the counter electrodes will not be possible, while if it is too large, a short circuit will occur between the adjacent electrodes.

芯材粒子の表面を導電性金属で被覆処理する方法としては、蒸着法、スパッタ法、メカノケミカル法、ハイブリダイゼーション処理を利用する等の乾式法、電解めっき法、無電解めっき法等の湿式法、あるいはこれらを組み合わせた方法を用いることができる。 As a method for coating the surface of the core material particles with a conductive metal, a dry method such as a vapor deposition method, a sputtering method, a mechanochemical method, or a hybridization treatment, an electrolytic plating method, a wet method such as an electroless plating method, etc. , Or a method combining these can be used.

前記金属被覆粒子は、金、銀、銅、ニッケル、パラジウム及びハンダ等から選ばれる１種又は２種以上の導電性金属で被覆処理されていることが好ましく、特に芯材粒子の表面に無電解めっきにより金属皮膜を形成した金属めっき粒子が、粒子表面を均一かつ濃密に被覆できる点で好ましく、とりわけ該金属皮膜が金又はパラジウムであるものが導電性を高くすることができる点で好ましい。なお、前記金属皮膜は合金（例えばニッケル−リン合金やニッケル−ホウ素合金）であってもよい。 The metal-coated particles are preferably coated with one or more conductive metals selected from gold, silver, copper, nickel, palladium, solder and the like, and in particular, the surface of the core material particles is electroless. Metal-plated particles having a metal film formed by plating are preferable in that the surface of the particles can be uniformly and densely coated, and those in which the metal film is gold or palladium are particularly preferable in that the conductivity can be increased. The metal film may be an alloy (for example, a nickel-phosphorus alloy or a nickel-boron alloy).

導電性粒子（Ｅ）の配合量は、（メタ）アクリレート（Ａ）１００質量部に対して２〜４０質量部が好ましく、３〜２５質量部がより好ましく、５〜２０質量部が更に好ましい。導電性粒子（Ｅ）の使用量が上記範囲内にあることにより、接続抵抗が高くなることが抑制されて接続信頼性が向上する。 The blending amount of the conductive particles (E) is preferably 2 to 40 parts by mass, more preferably 3 to 25 parts by mass, and even more preferably 5 to 20 parts by mass with respect to 100 parts by mass of the (meth) acrylate (A). When the amount of the conductive particles (E) used is within the above range, the connection resistance is suppressed from being increased and the connection reliability is improved.

本発明に係る導電性接着剤には、その他に、当該技術分野において、公知の添加剤を使用でき、その添加量も紫外可視光が内部まで到達できる範囲の量で含有させることができる。他の添加剤としては、例えば、光増感剤、脱泡剤、チキソ性付与剤、粘度調整剤、レベリング散剤、シランカップリング剤、安定剤、イオン交換体などを例示することができる。また、必要により溶剤を含有させることができる。 In addition, an additive known in the art can be used in the conductive adhesive according to the present invention, and the amount of the additive can be contained in an amount within a range in which ultraviolet visible light can reach the inside. Examples of other additives include a photosensitizer, a defoaming agent, a thixotropic agent, a viscosity modifier, a leveling powder, a silane coupling agent, a stabilizer, an ion exchanger and the like. In addition, a solvent can be contained if necessary.

本発明の導電性接着剤は、紫外可視光を照射することにより硬化させることができる。紫外可視光の波長の範囲は、１００〜７００ｎｍが好ましく、１５０〜５００ｎｍがより好ましく、１８０〜４００ｎｍが更に好ましい。 The conductive adhesive of the present invention can be cured by irradiating with ultraviolet-visible light. The wavelength range of ultraviolet-visible light is preferably 100 to 700 nm, more preferably 150 to 500 nm, and even more preferably 180 to 400 nm.

本発明の導電性接着剤を用いて電子部品を接着する方法としては、公知の方法を用いることができ、例えば、電極が形成された透明な基板の表面に、本発明の導電性接着剤を、スリットコーター、ロールコーター、スピンコーター、スクリーン印刷法、メタルマスク印刷法、ディスペンサー、ジェットディスペンサー等の塗工装置を用いて、膜厚が０．１〜１００μｍとなるように塗布し、電子部品の一部が前記電極の上方に位置するように前記電子部品を前記基板上に載置して前記透明基板側から紫外可視光を照射することにより、電子部品を接着することができる。 As a method for adhering electronic components using the conductive adhesive of the present invention, a known method can be used. For example, the conductive adhesive of the present invention is applied to the surface of a transparent substrate on which an electrode is formed. , Slit coater, roll coater, spin coater, screen printing method, metal mask printing method, dispenser, jet dispenser, etc. The electronic component can be adhered by placing the electronic component on the substrate so that a part of the electronic component is located above the electrode and irradiating the transparent substrate side with ultraviolet visible light.

紫外可視光の照射量は、５０〜２０，０００ｍＪ／ｃｍ２が好ましく、特に好ましくは、３００〜１０，０００ｍＪ／ｃｍ２である。紫外可視光の光線照射による硬化においては、紫外〜近紫外の光線を照射するランプであれば光源は問わない。光源としては、例えば、低圧、高圧若しくは超高圧水銀灯、メタルハライドランプ、（パルス）キセノンランプ、無電極ランプ及びＬＥＤ等が挙げられる。 The irradiation amount of ultraviolet-visible light is preferably 50 to 20,000 mJ / cm 2 , and particularly preferably 300 to 10,000 mJ / cm 2 . In the curing by irradiation with ultraviolet visible light, the light source does not matter as long as it is a lamp that irradiates ultraviolet to near-ultraviolet rays. Examples of the light source include low-pressure, high-pressure or ultra-high-pressure mercury lamps, metal halide lamps, (pulse) xenon lamps, electrodeless lamps, LEDs and the like.

本発明に係る導電性接着剤は、異方導電性接着剤として用いることができ、微細化するＩＣチップ、発光ダイオード等の電子部品や回路基板の電極接続に対して信頼性の高い接続ができる。 The conductive adhesive according to the present invention can be used as an anisotropic conductive adhesive, and can be connected with high reliability to the electrode connection of electronic parts such as IC chips and light emitting diodes to be miniaturized and circuit boards. ..

本発明の導電性接着剤を介して被接着部材同士が接着されている接着構造体としては、例えば、電極を有する基板にＩＣチップを接着した、ＩＣカードやＩＣタグなどのＲＦＩＤ関連製品や、電極を有する基板に発光ダイオードを接着した発光電子部品等が挙げられる。 Examples of the adhesive structure in which the members to be adhered are bonded to each other via the conductive adhesive of the present invention include RFID-related products such as IC cards and IC tags in which an IC chip is bonded to a substrate having an electrode. Examples thereof include light emitting electronic components in which a light emitting diode is adhered to a substrate having an electrode.

本発明に係る接着構造体としては、例えば、図１に示す、基板に実装された電子部品を例示することができる。
フィルムや紙のような基板１の一方の面である表面１ａ上に、電極であるアルミアンテナ２が形成されている。表面１ａには、少なくともアルミアンテナ２の全体を含む範囲に、本発明の導電性接着剤３が塗布され紫外可視光により硬化されている。基板１には、表面１ａ上に、金属電極５を有する電子部品、すなわち半導体であるＩＣチップ４が、金属電極５がアルミアンテナ２の上方に位置するように載置されている。ＩＣチップ４は、本発明の導電性接着剤３（導電性粒子６を含む）によって基板１の表面１ａ側に接着されている。なお、アルミアンテナ２と、金属電極５すなわちＩＣチップ４とは、導電性粒子６を介して通電するように構成されている。 As the adhesive structure according to the present invention, for example, the electronic component mounted on the substrate shown in FIG. 1 can be exemplified.
An aluminum antenna 2 as an electrode is formed on a surface 1a which is one surface of a substrate 1 such as a film or paper. The conductive adhesive 3 of the present invention is applied to the surface 1a so as to include at least the entire aluminum antenna 2, and the surface 1a is cured by ultraviolet-visible light. On the substrate 1, an electronic component having a metal electrode 5, that is, an IC chip 4, which is a semiconductor, is placed on the surface 1a so that the metal electrode 5 is located above the aluminum antenna 2. The IC chip 4 is adhered to the surface 1a side of the substrate 1 by the conductive adhesive 3 (including the conductive particles 6) of the present invention. The aluminum antenna 2 and the metal electrode 5, that is, the IC chip 4 are configured to be energized via the conductive particles 6.

本発明の導電性接着剤を用いて電子部品を実装する方法の中で、特に好ましい方法として、電極が形成された基板の表面に、紫外可視光が照射されることにより硬化する樹脂を含む接着剤を塗布するステップと、電子部品の一部が前記電極の上方に位置するように前記電子部品を前記基板上に載置するステップと、前記基板に対して垂直に紫外可視光を照射するステップとを含む、電子部品の実装方法において、前記基板の前記表面側には、前記紫外可視光を透過させない非透過部分が存在し、該非透過部分の外接矩形の短辺の長さが２ｍｍ以下とし、前記紫外可視光を照射するステップの前、又はそのステップと同時に、前記紫外可視光が透過可能な透明又は半透明の平坦な板部材で前記基板を加圧する方法が挙げられる（特開２０１５−５３３１６号公報参照）。 Among the methods for mounting electronic components using the conductive adhesive of the present invention, as a particularly preferable method, adhesion containing a resin that is cured by irradiating the surface of the substrate on which the electrodes are formed with ultraviolet visible light. A step of applying the agent, a step of placing the electronic component on the substrate so that a part of the electronic component is located above the electrode, and a step of irradiating the substrate with ultraviolet visible light perpendicularly. In the method for mounting an electronic component including , Before the step of irradiating the ultraviolet visible light, or at the same time as the step, a method of pressurizing the substrate with a transparent or translucent flat plate member capable of transmitting the ultraviolet visible light can be mentioned (Japanese Patent Laid-Open No. 2015-). 53316 (see).

本発明の導電性接着剤を用いて、電子部品を実装する装置の一例を図２に示す。
図２の電子部品を実装する装置３０は、基板１を載置すると共に基板１を加熱する加熱部材であるヒートテーブル３１と、紫外可視光を照射する照射部材３２と、照射部材３２をヒートテーブル３１に向かってあるいはヒートテーブル３１から離れるように移動させる駆動装置３３と、制御部３４とを備えている。制御部３４は、ヒートテーブル３１と、照射部材３２と、駆動装置３３とのそれぞれに電気的に接続されている。 FIG. 2 shows an example of an apparatus for mounting an electronic component using the conductive adhesive of the present invention.
The device 30 for mounting the electronic component of FIG. 2 has a heat table 31 which is a heating member for mounting the substrate 1 and heating the substrate 1, an irradiation member 32 for irradiating ultraviolet visible light, and a heat table for the irradiation member 32. It includes a drive device 33 that moves toward or away from the heat table 31, and a control unit 34. The control unit 34 is electrically connected to the heat table 31, the irradiation member 32, and the drive device 33, respectively.

図３に、照射部材３２が基板１（図２参照）に接触する接触面３５の構成を示す。接触面３５は、紫外可視光が透過可能な透明又は半透明の平坦な板部材３６から構成されており、板部材３６を通して、照射部材３２の内部に設けられた紫外可視光の光源３７が見えるようになっている。光源３７は、制御部３４（図２参照）からの給電によって、紫外可視光を照射するようになっている。なお、光源３７としては、ＬＥＤ、メタハライドランプ、キセノンランプ、加圧水銀ランプ、高圧水銀ランプ、超高圧水銀ランプ、カーボンアーク灯、その他波長１００〜７００ｎｍに発光分布を有する光を発するものを用いることができる。 FIG. 3 shows the configuration of the contact surface 35 in which the irradiation member 32 contacts the substrate 1 (see FIG. 2). The contact surface 35 is composed of a transparent or translucent flat plate member 36 capable of transmitting ultraviolet visible light, and the light source 37 of ultraviolet visible light provided inside the irradiation member 32 can be seen through the plate member 36. It has become like. The light source 37 is adapted to irradiate ultraviolet-visible light by supplying power from the control unit 34 (see FIG. 2). As the light source 37, an LED, a metahalide lamp, a xenon lamp, a pressurized mercury lamp, a high-pressure mercury lamp, an ultra-high pressure mercury lamp, a carbon arc lamp, or any other lamp that emits light having a light emission distribution at a wavelength of 100 to 700 nm is used. Can be done.

次に、上記した電子部品を実装する装置３０を用いた実装方法について説明する。
ＩＣチップ４の平面形状は任意の形状でよいが、ここでは、図４に示されるような楕円形状を有するものとして説明する。なお、基板１に実装されたＩＣチップ４は、ＩＣカードやＩＣタグなどのＲＦＩＤ関連製品に用いられる。また、基板１に実装された発光ダイオード１４は、発光電子部品に用いられる。 Next, a mounting method using the device 30 for mounting the above-mentioned electronic components will be described.
The planar shape of the IC chip 4 may be any shape, but here, it will be described as having an elliptical shape as shown in FIG. The IC chip 4 mounted on the substrate 1 is used for RFID-related products such as IC cards and IC tags. Further, the light emitting diode 14 mounted on the substrate 1 is used for a light emitting electronic component.

ＩＣチップ４を基板１に対して垂直な方向から見たときに、ＩＣチップ４が外接する外接矩形２０を想定する。この外接矩形２０は、２つの互いに平行な長辺２１と、２つの互いに平行な短辺２２とを有しているが、短辺２２の長さは２ｍｍ以下、好ましくは１．５ｍｍ以下である。なお、外接矩形が正方形の場合は、長辺及び短辺のそれぞれの長さは等しいので、一辺の長さが２ｍｍ以下、好ましくは１．５ｍｍ以下であればよい。ＩＣチップ４は紫外可視光を透過させないので、図５に示されるように、基板１に対して垂直な方向にＩＣチップ４を投影した領域（斜線部分の領域）は、紫外可視光を基板１に対して垂直に照射した場合に、紫外可視光が導電性接着剤３（図５に非図示）に直接には照射されない領域、すなわち非照射領域２３となる。ＩＣチップ４の外接矩形２０の短辺２２（図４参照）が２ｍｍ以下、好ましくは１．５ｍｍ以下であるので、短辺２２に平行な方向の非透過部分の幅Ｗは、ＩＣチップ４全体にわたって２ｍｍ以下、好ましくは１．５ｍｍ以下となる。 It is assumed that the circumscribed rectangle 20 is circumscribed by the IC chip 4 when the IC chip 4 is viewed from a direction perpendicular to the substrate 1. The circumscribed rectangle 20 has two long sides 21 parallel to each other and two short sides 22 parallel to each other, and the length of the short sides 22 is 2 mm or less, preferably 1.5 mm or less. .. When the circumscribed rectangle is a square, the lengths of the long side and the short side are the same, so that the length of one side may be 2 mm or less, preferably 1.5 mm or less. Since the IC chip 4 does not transmit ultraviolet visible light, as shown in FIG. 5, the region where the IC chip 4 is projected in the direction perpendicular to the substrate 1 (the shaded area) is the region where the ultraviolet visible light is transmitted to the substrate 1. When irradiated perpendicular to the above, the ultraviolet-visible light is not directly irradiated to the conductive adhesive 3 (not shown in FIG. 5), that is, the non-irradiated region 23. Since the short side 22 (see FIG. 4) of the circumscribing rectangle 20 of the IC chip 4 is 2 mm or less, preferably 1.5 mm or less, the width W of the non-transparent portion in the direction parallel to the short side 22 is the entire IC chip 4. It is 2 mm or less, preferably 1.5 mm or less.

一方、図６に示されるように、電子部品として、透明な材料からなる発光ダイオード１４を基板１に実装する場合、基板１に対して垂直に照射された紫外可視光は、発光ダイオード１４を透過して導電性接着剤３（図６に非図示）に照射される。ただし、発光ダイオード１４が透明であっても金属電極５は透明ではなく、紫外可視光は金属電極５を透過しないので、金属電極５が非透過部分となり、基板１に対して垂直な方向に金属電極５を投影した領域（斜線部分の領域）が非照射領域２３となる。この場合、金属電極５の外接矩形の短辺の長さが２ｍｍ以下、好ましくは１．５ｍｍ以下であれば、金属電極５の外接矩形の短辺に平行な方向の非透過部分の幅Ｗ’は、金属電極５全体にわたって２ｍｍ以下、好ましくは１．５ｍｍ以下となる。すなわち、図５に示されるように、ＩＣチップ４のような紫外可視光を透過させない電子部品を基板１に実装する場合には、ＩＣチップ４が、紫外可視光を透過させない非透過部分となり、図６に示されるように、発光ダイオード１４のような紫外可視光を透過させる電子部品を基板１に実装する場合には、発光ダイオード１４の金属電極５が、紫外可視光を透過させない非透過部分となる。 On the other hand, as shown in FIG. 6, when the light emitting diode 14 made of a transparent material is mounted on the substrate 1 as an electronic component, the ultraviolet visible light emitted perpendicularly to the substrate 1 is transmitted through the light emitting diode 14. Then, the conductive adhesive 3 (not shown in FIG. 6) is irradiated with the conductive adhesive 3. However, even if the light emitting diode 14 is transparent, the metal electrode 5 is not transparent, and ultraviolet visible light does not pass through the metal electrode 5, so that the metal electrode 5 becomes a non-transmissive portion and the metal is formed in a direction perpendicular to the substrate 1. The region on which the electrode 5 is projected (the shaded area) is the non-irradiated region 23. In this case, if the length of the short side of the circumscribing rectangle of the metal electrode 5 is 2 mm or less, preferably 1.5 mm or less, the width W'of the non-transmissive portion in the direction parallel to the short side of the circumscribing rectangle of the metal electrode 5. Is 2 mm or less, preferably 1.5 mm or less over the entire metal electrode 5. That is, as shown in FIG. 5, when an electronic component such as the IC chip 4 that does not transmit ultraviolet visible light is mounted on the substrate 1, the IC chip 4 becomes a non-transmissive portion that does not transmit ultraviolet visible light. As shown in FIG. 6, when an electronic component that transmits ultraviolet visible light such as a light emitting diode 14 is mounted on the substrate 1, the metal electrode 5 of the light emitting diode 14 is a non-transmissive portion that does not transmit ultraviolet visible light. It becomes.

図２に示されるように、ヒートテーブル３１の上に基板１を載置する。基板１には既に、表面１ａにアルミアンテナ２が形成され、少なくともアルミアンテナ２の全体を含む範囲に導電性接着剤３が塗布され、金属電極５がアルミアンテナ２の上方に位置するようにＩＣチップ４が載置されている。ヒートテーブル３１の上に基板１を載置する前に、制御部３４は予めヒートテーブル３１を１５〜１００℃の範囲の適切な温度に加熱しておいてもよい。ヒートテーブル３１の上に基板１を載置後、制御部３４は、駆動装置３３を起動することにより、照射部材３２をヒートテーブル３１に向かって移動させ、基板１をヒートテーブル３１と照射部材３２とによって挟む。更に制御部３４は、照射部材３２から紫外可視光を照射させ、基板１をヒートテーブル３１と照射部材３２とによって加圧する。この際に加える圧力は、０．０１〜５００Ｎ／ｍｍ２の範囲で、より好ましくは０．０３〜３００Ｎ／ｍｍ２の範囲で適宜設定される。この加圧の間に、導電性接着剤３に紫外可視光が照射されることにより導電性接着剤３が硬化する。導電性接着剤３が完全に硬化するのに十分な時間だけ加圧及び加熱した後、制御部３４は、駆動装置３３によって照射部材３２をヒートテーブル３１から離れるように移動させ、ヒートテーブル３１による加熱及び照射部材３２からの紫外可視光の照射を終了することにより、基板１へのＩＣチップ４の実装が完了する。 As shown in FIG. 2, the substrate 1 is placed on the heat table 31. An aluminum antenna 2 is already formed on the surface 1a of the substrate 1, a conductive adhesive 3 is applied to a range including at least the entire aluminum antenna 2, and an IC is provided so that the metal electrode 5 is located above the aluminum antenna 2. The chip 4 is placed. Before placing the substrate 1 on the heat table 31, the control unit 34 may preheat the heat table 31 to an appropriate temperature in the range of 15 to 100 ° C. After placing the substrate 1 on the heat table 31, the control unit 34 activates the drive device 33 to move the irradiation member 32 toward the heat table 31, and moves the substrate 1 to the heat table 31 and the irradiation member 32. Sandwiched by. Further, the control unit 34 irradiates the irradiation member 32 with ultraviolet visible light, and pressurizes the substrate 1 by the heat table 31 and the irradiation member 32. Pressure applied to this case, the range of 0.01~500N / mm 2, more preferably is appropriately set in the range of 0.03~300N / mm 2. During this pressurization, the conductive adhesive 3 is cured by irradiating the conductive adhesive 3 with ultraviolet visible light. After pressurizing and heating the conductive adhesive 3 for a time sufficient to completely cure, the control unit 34 moves the irradiation member 32 away from the heat table 31 by the driving device 33, and uses the heat table 31. By completing the heating and irradiation of ultraviolet visible light from the irradiation member 32, the mounting of the IC chip 4 on the substrate 1 is completed.

この実施の形態では、電子部品としてＩＣチップ４及び発光ダイオード１４を例にして説明したが、これらに限定するものではない。紫外可視光が照射されることによって硬化する接着剤によって接着される電子部品であれば任意のものであってもよい。 In this embodiment, the IC chip 4 and the light emitting diode 14 have been described as examples of electronic components, but the present invention is not limited thereto. Any electronic component that is adhered by an adhesive that cures when irradiated with ultraviolet-visible light may be used.

この実施の形態では、制御部３４が照射部材３２をヒートテーブル３１に向かって移動させていたが、この形態に限定するものではない。照射部材３２を固定しておき、ヒートテーブル３１を照射部材３２に向かって移動させてもよいし、両者を互いに向かって同時に又は交互に移動させてもよい。 In this embodiment, the control unit 34 moves the irradiation member 32 toward the heat table 31, but the present invention is not limited to this embodiment. The irradiation member 32 may be fixed and the heat table 31 may be moved toward the irradiation member 32, or both may be moved simultaneously or alternately toward each other.

この実施の形態では、導電性接着剤３に紫外可視光を照射させるときに、ヒートテーブル３１によって加熱も一緒に行っていたが、この形態に限定するものではない。この加熱は、導電性接着剤３の硬化反応を促進するために行うものであるので、ヒートテーブル３１の代わりに、加熱を行わない単なる固定台を用いて、紫外可視光の照射のみを行ってもよい。 In this embodiment, when the conductive adhesive 3 is irradiated with ultraviolet-visible light, it is also heated by the heat table 31, but the present invention is not limited to this embodiment. Since this heating is performed to accelerate the curing reaction of the conductive adhesive 3, instead of the heat table 31, a simple fixing table that does not heat is used to irradiate only ultraviolet visible light. May be good.

この実施の形態では、ヒートテーブル３１の上に基板１を載置していたが、この形態に限定するものではない。接触面３５が上方に向くように照射部材３２を配置し、基板１を接触面３５上に載置する形態であってもよい。この場合、照射部材３２の上方にヒートテーブル３１が配置され、ヒートテーブル３１を照射部材３２に向かって移動させてもよいし、照射部材３２をヒートテーブル３１に向かって移動させてもよいし、両者を互いに向かって同時に又は交互に移動させてもよい。 In this embodiment, the substrate 1 is placed on the heat table 31, but the present invention is not limited to this embodiment. The irradiation member 32 may be arranged so that the contact surface 35 faces upward, and the substrate 1 may be placed on the contact surface 35. In this case, the heat table 31 may be arranged above the irradiation member 32, and the heat table 31 may be moved toward the irradiation member 32, or the irradiation member 32 may be moved toward the heat table 31. Both may be moved towards each other simultaneously or alternately.

以下、本発明を実施例により説明するが、本発明はこれらの実施例に限定されるわけではない。 Hereinafter, the present invention will be described with reference to Examples, but the present invention is not limited to these Examples.

［（メタ）アクリレート（Ａ）］
（メタ）アクリレート（Ａ）は、下記の市販のものを使用した。 [(Meta) Acrylate (A)]
As the (meth) acrylate (A), the following commercially available one was used.

Figure 0006946395
Figure 0006946395

［光重合開始剤（Ｂ）］
光重合開始剤（Ｂ）は、下記の市販のものを使用した。 [Photopolymerization Initiator (B)]
The following commercially available photopolymerization initiator (B) was used.

Figure 0006946395
Figure 0006946395

［リン酸基含有モノマー（Ｃ）］
リン酸基含有モノマー（Ｃ）は、下記の市販のものを使用した。 [Phosphate group-containing monomer (C)]
As the phosphoric acid group-containing monomer (C), the following commercially available one was used.

Figure 0006946395
Figure 0006946395

［リン酸イオン不活性化剤（Ｄ）］
リン酸イオン不活性化剤（Ｄ）は、下記の市販のものを使用した。 [Phosphate ion inactivating agent (D)]
As the phosphate ion inactivating agent (D), the following commercially available one was used.

Figure 0006946395
Figure 0006946395

［導電性粒子（Ｅ）］
導電性粒子は、球状の樹脂粒子の表面に金−ニッケルの導電層を有する平均粒子径が３．０μｍである金めっき粒子（日本化学工業製）を用いた。 [Conductive particles (E)]
As the conductive particles, gold-plated particles (manufactured by Nippon Kagaku Kogyo Co., Ltd.) having a gold-nickel conductive layer on the surface of spherical resin particles and having an average particle diameter of 3.0 μm were used.

｛実施例１〜８及び比較例１〜２｝
表５に示す組成で、（メタ）アクリレート（Ａ）、光重合開始剤（Ｂ）、リン酸基含有モノマー（Ｃ）、リン酸イオン不活性化剤（Ｄ）及び添加剤としてアエロジルＲＸ２００（チキソ性付与剤：日本アエロジル製）を、自転・公転式真空ミキサーを用いて２５℃で１時間混合し、実施例１〜８及び比較例１〜２の導電性接着剤を調製した。 {Examples 1 to 8 and Comparative Examples 1 to 2}
The composition shown in Table 5 includes (meth) acrylate (A), photopolymerization initiator (B), phosphate group-containing monomer (C), phosphate ion inactivating agent (D), and Aerosil RX200 (Chixo) as an additive. The sex-imparting agent (manufactured by Nippon Aerosil) was mixed at 25 ° C. for 1 hour using a rotating / revolving vacuum mixer to prepare conductive adhesives of Examples 1 to 8 and Comparative Examples 1 and 2.

＜貯蔵安定性（ポットライフ）の評価＞
導電性接着剤５ｇを容器に入れ、その容器を３０℃に保ち、１日後及び３日後の状態を目視で観察し、その状態を評価した。結果を表５に併記した。
なお、表中の貯蔵安定性の評価結果は下記のことを示す。
×：１日後には硬化している。
〇：１日後は状態に変化なし、３日後にはゲルが観察される。
◎：１日後及び３日後も状態に変化なし。 <Evaluation of storage stability (pot life)>
5 g of the conductive adhesive was placed in a container, the container was kept at 30 ° C., and the state after 1 day and 3 days was visually observed and the state was evaluated. The results are also shown in Table 5.
The evaluation results of storage stability in the table are as follows.
X: Hardened after 1 day.
〇: No change in state after 1 day, gel is observed after 3 days.
⊚: No change in condition after 1 day and 3 days.

＜密着性の評価＞
ＰＥＴフィルム上にアルミニウム配線が形成された基板（サイズ：縦２．５ｃｍ、横８ｃｍ）上のアルミ配線の全体を含む範囲に、実施例及び比較例で調製した導電性接着剤を、硬化後の厚さが５０μｍとなるようにディスペンス法で塗布し、金パンプを有するＩＣを載置した。温度２５℃、１Ｎ／ｍｍ２の加圧下で、紫外可視光（波長３６５ｎｍ、照度５，０００ｍＷ／ｃｍ２）を２秒間照射して導電性接着剤を硬化させることにより、評価用の接着構造体を作製した。なお、用いた導電性接着剤は調製して２時間以内のものを使用した。
作製した接着構造体について、導電性接着剤のダイシェア強度を測定した。ダイシェア強度は、基板からＩＣチップを剥離する際の強度（Ｎ／ｍｍ２）を、デジタルフォースゲージを用いて測定した。結果を表５に併記した。なお、表中のダイシェア強度結果は下記のことを示す。
○：２０Ｎ／ｍｍ２以上
×：２０Ｎ／ｍｍ２未満 <Evaluation of adhesion>
After curing, the conductive adhesives prepared in Examples and Comparative Examples were applied to a range including the entire aluminum wiring on a substrate (size: length 2.5 cm, width 8 cm) in which aluminum wiring was formed on a PET film. It was applied by the dispense method so as to have a thickness of 50 μm, and an IC having a gold pump was placed. An adhesive structure for evaluation is obtained by irradiating ultraviolet visible light (wavelength 365 nm, illuminance 5,000 mW / cm 2 ) for 2 seconds under a pressure of 25 ° C. and 1 N / mm 2 to cure the conductive adhesive. Was produced. The conductive adhesive used was prepared and used within 2 hours.
The die shear strength of the conductive adhesive was measured for the produced adhesive structure. The die shear strength was measured by using a digital force gauge to measure the strength (N / mm 2 ) when the IC chip was peeled off from the substrate. The results are also shown in Table 5. The die-share strength results in the table show the following.
◯: 20 N / mm 2 or more ×: 20 N / mm less than 2

Figure 0006946395
Figure 0006946395

リン酸基含有モノマー（Ｃ）及びリン酸イオン不活性化剤（Ｄ）を使用した実施例１〜８の導電性接着剤は、接着構造体の密着性に優れており、ポットライフが良好であった。リン酸基含有モノマー（Ｃ）使用し、リン酸イオン不活性化剤（Ｄ）を使用しない比較例１の導電性接着剤は、接着構造体の密着性に優れているが、ポットライフに問題があった。リン酸基含有モノマー（Ｃ）使用しない比較例２の導電性接着剤は、ポットライフは概ね良好であるが、接着構造体の密着性に劣っていた。 The conductive adhesives of Examples 1 to 8 using the phosphate group-containing monomer (C) and the phosphate ion inactivating agent (D) have excellent adhesion of the adhesive structure and have a good pot life. there were. The conductive adhesive of Comparative Example 1 using the phosphate group-containing monomer (C) and not the phosphate ion inactivating agent (D) has excellent adhesion of the adhesive structure, but has a problem in pot life. was there. The conductive adhesive of Comparative Example 2 in which the phosphoric acid group-containing monomer (C) was not used had generally good pot life, but was inferior in adhesion of the adhesive structure.

１ 基板
１ａ （基板の）表面
１ｂ （基板の）底面
２ アルミアンテナ（電極）
３ 導電性接着剤
４ ＩＣチップ（半導体、電子部品）
５ 金属電極
６ 導電性粒子
１４ 発光ダイオード（電子部品）
２０ 外接矩形
２１ （外接矩形の）長辺
２２ （外接矩形の）短辺
２３ 非照射領域
３０ 装置
３１ ヒートテーブル（加熱部材）
３２ 照射部材
３３ 駆動装置
３４ 制御部
３５ 接触面
３６ 板部材
３７ 光源
1 Substrate 1a (of the substrate) Surface 1b (of the substrate) Bottom surface 2 Aluminum antenna (electrode)
3 Conductive adhesive 4 IC chip (semiconductor, electronic component)
5 Metal electrode 6 Conductive particles 14 Light emitting diode (electronic component)
20 Circumscribed rectangle 21 Long side (of circumscribed rectangle) 22 Short side of (circumscribed rectangle) 23 Non-irradiated area 30 Device 31 Heat table (heating member)
32 Irradiation member 33 Drive device 34 Control unit 35 Contact surface 36 Plate member 37 Light source

Claims (12)

（メタ）アクリレート（Ａ）、光重合開始剤（Ｂ）、リン酸基含有モノマー（Ｃ）、リン酸イオン不活性化剤（Ｄ）及び導電性粒子（Ｅ）を含有する導電性接着剤。 A conductive adhesive containing (meth) acrylate (A), photopolymerization initiator (B), phosphate group-containing monomer (C), phosphate ion inactivating agent (D) and conductive particles (E). リン酸基含有モノマー（Ｃ）が、リン酸基含有（メタ）アクリレートである請求項１に記載の導電性接着剤。 The conductive adhesive according to claim 1, wherein the phosphoric acid group-containing monomer (C) is a phosphoric acid group-containing (meth) acrylate. リン酸基含有モノマー（Ｃ）の含有量が、（メタ）アクリレート（Ａ）１００重量部に対して１〜５０質量部である請求項１に記載の導電性接着剤。 The conductive adhesive according to claim 1, wherein the content of the phosphoric acid group-containing monomer (C) is 1 to 50 parts by mass with respect to 100 parts by weight of the (meth) acrylate (A). リン酸イオン不活性化剤（Ｄ）が、リン酸イオンを吸着して不活性化する化合物及び／又はリン酸イオンと反応して不活性化する化合物からなる請求項１に記載の導電性接着剤。 The conductive adhesion according to claim 1, wherein the phosphate ion inactivating agent (D) comprises a compound that adsorbs and inactivates phosphate ions and / or a compound that reacts with phosphate ions to inactivate. Agent. リン酸イオンを吸着して不活性化する化合物が、活性アルミナ、シリカゲル、ゼオライト、粘度鉱物、活性炭、活性白土、珪藻土及びセライトからなる群より選ばれる請求項４に記載の導電性接着剤。 The conductive adhesive according to claim 4, wherein the compound that adsorbs and inactivates phosphate ions is selected from the group consisting of activated alumina, silica gel, zeolite, viscous minerals, activated charcoal, activated clay, diatomaceous earth, and cellite. リン酸イオンと反応して不活性化する化合物が、Ｚｎ、Ａｌ、Ｂａ、Ｃａ、Ｍｇ、Ｚｒ、Ｔｉ、Ｓｎ、Ｓｉ、Ｉｎ、Ｃｅ、Ａｇ及びＹｂから選ばれる金属元素を１種又は２種以上含有する無機金属化合物である請求項４に記載の導電性接着剤。 The compound that reacts with the phosphate ion to inactivate is one or two metal elements selected from Zn, Al, Ba, Ca, Mg, Zr, Ti, Sn, Si, In, Ce, Ag and Yb. The conductive adhesive according to claim 4, which is an inorganic metal compound contained as described above. リン酸イオン不活性化剤（Ｄ）の配合量が、リン酸基含有モノマー（Ｃ）１００質量部に対して０．５〜３０質量部である請求項１に記載の導電性接着剤。 The conductive adhesive according to claim 1, wherein the amount of the phosphate ion inactivating agent (D) is 0.5 to 30 parts by mass with respect to 100 parts by mass of the phosphate group-containing monomer (C). 導電性粒子（Ｅ）が、芯材粒子の表面を導電性金属で被覆した導電性粒子である請求項１に記載の導電性接着剤。 The conductive adhesive according to claim 1, wherein the conductive particles (E) are conductive particles in which the surface of the core material particles is coated with a conductive metal. 異方導電性接着剤である請求項８に記載の導電性接着剤。 The conductive adhesive according to claim 8, which is an anisotropic conductive adhesive. 請求項１〜９のいずれか１項に記載の導電性接着剤を介して被接着部材同士が接着されている接着構造体。 An adhesive structure in which members to be adhered to each other are adhered to each other via the conductive adhesive according to any one of claims 1 to 9. 請求項１〜９のいずれか１項に記載の導電性接着剤を用いた電子部品。 An electronic component using the conductive adhesive according to any one of claims 1 to 9. 電子部品が、ＩＣカード、ＩＣタグ及び発光電子部品から選ばれる請求項１１に記載の電子部品。



The electronic component according to claim 11, wherein the electronic component is selected from an IC card, an IC tag, and a light emitting electronic component.
JP2019194347A 2019-10-25 2019-10-25 Conductive adhesives, adhesive structures and electronic components using them Active JP6946395B2 (en)