JP6610308B2 - Decorative sheet and decorative board - Google Patents

Decorative sheet and decorative board Download PDF

Info

Publication number
JP6610308B2
JP6610308B2 JP2016019264A JP2016019264A JP6610308B2 JP 6610308 B2 JP6610308 B2 JP 6610308B2 JP 2016019264 A JP2016019264 A JP 2016019264A JP 2016019264 A JP2016019264 A JP 2016019264A JP 6610308 B2 JP6610308 B2 JP 6610308B2
Authority
JP
Japan
Prior art keywords
pearl
layer
pattern layer
mass
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2016019264A
Other languages
Japanese (ja)
Other versions
JP2017136751A (en
Inventor
彩 明石
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toppan Inc
Original Assignee
Toppan Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Inc filed Critical Toppan Inc
Priority to JP2016019264A priority Critical patent/JP6610308B2/en
Publication of JP2017136751A publication Critical patent/JP2017136751A/en
Application granted granted Critical
Publication of JP6610308B2 publication Critical patent/JP6610308B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、化粧シート及び化粧板に関する。   The present invention relates to a decorative sheet and a decorative board.

従来、化粧シートとしては、例えば、特許文献１に記載の技術がある。この特許文献１１に記載の技術では、見る角度や光の加減によって見た目の変化が生じる意匠性を付与するため、化粧シートに対し、パール顔料を使用したパール柄層を設けている。ここで、パール顔料を複数種類使用することで、さらに意匠性を向上させることも考えられる。
しかしながら、単純にパール柄層を構成するインキ（メジウム）に複数種類のパール顔料を添加すると、複数種類のパール顔料の混ざり具合等によっては、密着強度が低下する可能性がある。そのため、パール柄層で構成される柄等が制約される可能性がある。 Conventionally, as a decorative sheet, there exists a technique of patent document 1, for example. In the technique described in Patent Document 11, a pearl pattern layer using a pearl pigment is provided on a decorative sheet in order to impart a design property in which an appearance changes depending on a viewing angle or light. Here, it is conceivable to further improve the design by using a plurality of kinds of pearl pigments.
However, when a plurality of types of pearl pigments are simply added to the ink (medium) constituting the pearl pattern layer, the adhesion strength may be lowered depending on the mixing condition of the plurality of types of pearl pigments. Therefore, there is a possibility that the pattern composed of the pearl pattern layer is restricted.

特開２０１４−１４８０５８号公報JP 2014-148058 A

本発明は、上記の点に着目したもので、密着強度の低下を抑制しつつ、パール柄層による意匠性の向上効果を増大可能な化粧シート及び化粧板を提供することを目的とする。   This invention pays attention to said point, and it aims at providing the decorative sheet and decorative board which can increase the improvement effect of the design property by a pearl pattern layer, suppressing the fall of adhesive strength.

上記課題を解決するために、本発明の一態様は、基材層の上に、複数種類のパール顔料を使用したパール柄層、透明樹脂層、及び表面保護層がこの順に積層されている化粧シートであって、パール柄層は、マイカ、酸化チタン及び酸化スズを含む第１パール顔料とメジウムとを含む第１パール柄層と、マイカ、酸化チタン及び酸化鉄を含む第２パール顔料とメジウムとを含む第２パール柄層とが積層されてなり、第１パール柄層は、メジウム１００質量部に対して、第１パール顔料を０質量部より大きく２３質量部以下含んでおり、第２パール柄層は、メジウム１００質量部に対して、第２パール顔料を０質量部より大きく１０質量部以下含んでいることを特徴とする。   In order to solve the above problems, one embodiment of the present invention is a makeup in which a pearl pattern layer, a transparent resin layer, and a surface protective layer using a plurality of types of pearl pigments are laminated in this order on a base material layer. The pearl pattern layer includes a first pearl pattern layer including a first pearl pigment containing mica, titanium oxide and tin oxide and a medium, a second pearl pigment including mica, titanium oxide and iron oxide, and a medium. The first pearl pattern layer contains the first pearl pigment more than 0 parts by mass and less than 23 parts by mass with respect to 100 parts by mass of the medium. The pearl pattern layer contains the second pearl pigment in an amount of more than 0 parts by mass and 10 parts by mass or less with respect to 100 parts by mass of the medium.

本発明の一態様によれば、第１パール柄層のパール顔料の含有量と第２パール柄層のパール顔料の含有量とを調整したため、第１パール柄層や第２パール柄層の凝集破壊を抑制でき、密着強度の低下を抑制できる。また、第１パール柄層と第２パール柄層とを積層したため、パール柄層による意匠性の向上効果を増大できる。   According to one aspect of the present invention, since the content of the pearl pigment in the first pearl pattern layer and the content of the pearl pigment in the second pearl pattern layer are adjusted, the first pearl pattern layer and the second pearl pattern layer are aggregated. Breakage can be suppressed and a decrease in adhesion strength can be suppressed. Moreover, since the 1st pearl pattern layer and the 2nd pearl pattern layer were laminated | stacked, the improvement effect of the design property by a pearl pattern layer can be increased.

本発明の実施形態の化粧シート及び化粧板を表す模式的断面図である。It is typical sectional drawing showing the decorative sheet and decorative board of embodiment of this invention. 変形例に係る化粧シート及び化粧板を表す模式的断面図である。It is typical sectional drawing showing the decorative sheet and decorative plate which concern on a modification.

次に、本発明の実施形態について図面を参照しつつ説明する。
ここで、図面は模式的なものであり、厚みと平面寸法との関係、各層の厚みの比率等は現実のものとは異なる。また、以下に示す実施形態は、本発明の技術的思想を具体化するための構成を例示するものであって、本発明の技術的思想は、構成部品の材質、形状、構造等が下記のものに特定するものでない。本発明の技術的思想は、特許請求の範囲に記載された請求項が規定する技術的範囲内において、種々の変更を加えることができる。 Next, embodiments of the present invention will be described with reference to the drawings.
Here, the drawings are schematic, and the relationship between the thickness and the planar dimensions, the ratio of the thickness of each layer, and the like are different from the actual ones. Further, the embodiment described below exemplifies a configuration for embodying the technical idea of the present invention, and the technical idea of the present invention is that the material, shape, structure, etc. of the component parts are as follows. It is not something specific. The technical idea of the present invention can be variously modified within the technical scope defined by the claims described in the claims.

本実施形態の化粧シート１００は、図１に示すように、基材層１の一方の面に、ベタ層２、パール柄層３、アンカーコート層４、透明樹脂層６、及び表面保護層７，８，９がこの順に積層され、また基材層１の他方の面に裏面プライマー層１０が形成されている。また、化粧シート１００の裏面プライマー層１０側の面には、接着剤層２１を介して基材２０の一方の面に貼り付けられる（形成される）ことで、化粧板１１０が構成される。   As shown in FIG. 1, the decorative sheet 100 of the present embodiment has a solid layer 2, a pearl pattern layer 3, an anchor coat layer 4, a transparent resin layer 6, and a surface protective layer 7 on one surface of the base material layer 1. , 8 and 9 are laminated in this order, and the back surface primer layer 10 is formed on the other surface of the base material layer 1. Further, the decorative sheet 110 is configured by being attached (formed) to one surface of the base material 20 via the adhesive layer 21 on the surface of the decorative sheet 100 on the back surface primer layer 10 side.

＜基材層１＞
基材層１は、樹脂フィルムから構成される。樹脂フィルムとしては、例えば、着色ポリプロピレン樹脂を使用できる。基材層１の厚さは、例えば、３０〜２００μｍとする。
＜ベタ層２＞
ベタ層２は、基材層１とパール柄層３との接着性を向上するための層である。ベタ層２としては、例えば、二液ウレタン樹脂と塩酢ビ樹脂とを混合した樹脂を使用できる。樹脂には、着色のために有機顔料が添加されている。ベタ層２は、例えば、基材層１の上にベタ層２構成用の樹脂を塗工して形成する。乾燥後の塗布量は、例えば、２ｇ/ｍ2とする。 <Base material layer 1>
The base material layer 1 is composed of a resin film. For example, a colored polypropylene resin can be used as the resin film. The thickness of the base material layer 1 is, for example, 30 to 200 μm.
<Solid layer 2>
The solid layer 2 is a layer for improving the adhesion between the base material layer 1 and the pearl pattern layer 3. As the solid layer 2, for example, a resin in which a two-component urethane resin and a vinyl acetate resin are mixed can be used. An organic pigment is added to the resin for coloring. The solid layer 2 is formed, for example, by applying a resin for forming the solid layer 2 on the base material layer 1. The coating amount after drying is, for example, 2 g / m 2 .

＜パール柄層３＞
パール柄層３は、複数種類のパール顔料を用いて形成される。具体的には、パール柄層３は、第１パール顔料とメジウムとを含む第１パール柄層３Ａと、第２パール顔料とメジウムとを含む第２パール柄層３Ｂとが積層されている。第１パール顔料は、マイカ、酸化チタン及び酸化スズを含む銀色のパール顔料である。マイカ：酸化チタン：酸化スズの比率は、例えば、６０．０〜６２．０：３７．５〜３９．５：０．５〜２．０とする。 <Pearl pattern layer 3>
The pearl pattern layer 3 is formed using a plurality of types of pearl pigments. Specifically, the pearl pattern layer 3 includes a first pearl pattern layer 3A including a first pearl pigment and a medium, and a second pearl pattern layer 3B including a second pearl pigment and a medium. The first pearl pigment is a silver pearl pigment containing mica, titanium oxide and tin oxide. The ratio of mica: titanium oxide: tin oxide is, for example, 60.0 to 62.0: 37.5 to 39.5: 0.5 to 2.0.

また、第２パール顔料は、マイカ、酸化チタン及び酸化鉄を含む金色のパール顔料である。マイカ：酸化チタン：酸化鉄の比率は、例えば、４４．０〜４６．０：４６〜４７．０：９．０〜９．５とする。これにより、第１パール柄層３Ａで構成される柄、つまり銀色のパール顔料の柄と、第２パール柄層３Ｂで構成される柄、つまり金色のパール顔料の柄とを合成でき、パール柄層３による意匠性の向上効果を増大することができる。本実施形態では、第１パール柄層３Ａがベタ層２側に位置し、第２パール柄層３Ｂがアンカーコート層４側に位置している。第２パール柄層３Ｂと第１パール柄層３Ａとのそれぞれは、メジウムにパール顔料を含有してなる塗工液（インキ）を印刷で塗工して形成される。   The second pearl pigment is a golden pearl pigment containing mica, titanium oxide and iron oxide. The ratio of mica: titanium oxide: iron oxide is, for example, 44.0-46.0: 46-47.0: 9.0-9.5. Thereby, the pattern composed of the first pearl pattern layer 3A, that is, the pattern of the silver pearl pigment, and the pattern composed of the second pearl pattern layer 3B, that is, the pattern of the golden pearl pigment can be synthesized. The improvement effect of the design property by the layer 3 can be increased. In the present embodiment, the first pearl pattern layer 3A is located on the solid layer 2 side, and the second pearl pattern layer 3B is located on the anchor coat layer 4 side. Each of the second pearl pattern layer 3B and the first pearl pattern layer 3A is formed by applying a coating liquid (ink) containing a pearl pigment in a medium by printing.

また、第１パール柄層３Ａ及び第２パール柄層３Ｂのパール顔料の粒径は、１μｍ以上１００μｍ以下、好ましくは５μｍ以上５０μｍ以下の範囲に設定する。第１パール柄層３Ａ及び第２パール柄層３Ｂそれぞれの厚さは、例えば、５μｍ〜５０μｍとする。
また、メジウムとしては、例えば、アクリル樹脂、ウレタン樹脂、ポリアミド樹脂、アクリルポリオール樹脂等を使用できる。また、必要に応じて、イソシアネート系の硬化剤、シリコンオイル等の滑剤やワックス等の耐摩強化剤を１〜５％添加してもよい。 The particle size of the pearl pigment of the first pearl pattern layer 3A and the second pearl pattern layer 3B is set in the range of 1 μm to 100 μm, preferably 5 μm to 50 μm. The thickness of each of the first pearl pattern layer 3A and the second pearl pattern layer 3B is, for example, 5 μm to 50 μm.
Moreover, as a medium, an acrylic resin, a urethane resin, a polyamide resin, an acrylic polyol resin etc. can be used, for example. Moreover, you may add 1-5% of anti-wear strengthening agents, such as lubricants, such as isocyanate hardening | curing agent and silicone oil, and wax, as needed.

ここで、第１パール柄層３Ａは、メジウム１００質量部に対して、第１パール顔料を０質量部より大きく２３質量部以下含み、第２パール柄層３Ｂは、メジウム１００質量部に対して、第２パール顔料を０質量部より大きく１０質量部以下含むようにする。または、第１パール柄層３Ａは、メジウム１００質量部に対して、第１パール顔料を０質量部より大きく１７質量部以下含み、第２パール柄層３Ｂは、メジウム１００質量部に対して、第２パール顔料を１０質量部より大きく３３質量部以下含むようにする。これにより、第１パール柄層３Ａや第２パール柄層３Ｂの凝集破壊を抑制でき、密着強度を向上できる。   Here, the first pearl pattern layer 3A includes the first pearl pigment larger than 0 parts by mass and 23 parts by mass or less with respect to 100 parts by mass of the medium, and the second pearl pattern layer 3B includes 100 parts by mass of the medium. The second pearl pigment is contained in an amount larger than 0 parts by mass and 10 parts by mass or less. Alternatively, the first pearl pattern layer 3A contains the first pearl pigment larger than 0 parts by mass and 17 parts by mass or less with respect to 100 parts by mass of the medium, and the second pearl pattern layer 3B contains 100 parts by mass of the medium. The second pearl pigment is contained in an amount of more than 10 parts by mass and not more than 33 parts by mass. Thereby, the cohesive failure of the 1st pearl pattern layer 3A and the 2nd pearl pattern layer 3B can be suppressed, and adhesive strength can be improved.

＜アンカーコート層４＞
アンカーコート層４は、パール柄層３と透明樹脂層６との接着性を向上させるための層である。アンカーコート層４としては、例えば、二液ウレタン樹脂を使用できる。アンカーコート層４は、例えば、パール柄層３（第２パール柄層３Ｂ）の上にアンカーコート層４用の二液ウレタン樹脂を塗工して形成する。乾燥後の塗布量は１．２ｇ/ｍ2とする。 <Anchor coat layer 4>
The anchor coat layer 4 is a layer for improving the adhesion between the pearl pattern layer 3 and the transparent resin layer 6. As the anchor coat layer 4, for example, a two-component urethane resin can be used. The anchor coat layer 4 is formed, for example, by applying a two-component urethane resin for the anchor coat layer 4 on the pearl pattern layer 3 (second pearl pattern layer 3B). The coating amount after drying is 1.2 g / m 2 .

＜接着剤層５＞
接着剤層５は、透明な接着剤からなる層である。透明な接着剤としては、例えば、酸変性ポリプロピレン樹脂を使用できる。接着剤層５の厚さは、例えば、１２μｍとする。
＜透明樹脂層６＞
透明樹脂層６は、パール柄層３で構成される柄が透けて見える、透明な樹脂からなる層である。透明な樹脂としては、例えば、熱可塑性樹脂を使用できる。例えば、ポリオレフィン（ＰＰ）樹脂がある。透明樹脂層６の厚さは、例えば、６８μｍとする。 <Adhesive layer 5>
The adhesive layer 5 is a layer made of a transparent adhesive. For example, an acid-modified polypropylene resin can be used as the transparent adhesive. The thickness of the adhesive layer 5 is 12 μm, for example.
<Transparent resin layer 6>
The transparent resin layer 6 is a layer made of a transparent resin through which the pattern formed by the pearl pattern layer 3 can be seen. As the transparent resin, for example, a thermoplastic resin can be used. For example, there is a polyolefin (PP) resin. The thickness of the transparent resin layer 6 is 68 μm, for example.

＜表面保護層７，８，９＞
表面保護層７，８，９は、透明樹脂層６やパール柄層３等を保護するために化粧シート１００の表層に設けられる透明な樹脂層である。表面保護層７（以下、「第１表面保護層７」とも呼ぶ）は、透明樹脂層６側に位置し、表面保護層９（以下、「第３表面保護層９」とも呼ぶ）は、表層側に位置し、表面保護層８（以下、「第２表面保護層８」とも呼ぶ）は、第１表面保護層７と第３表面保護層９との間に位置している。ここで、第１表面保護層７はアンカー層として機能し、第２表面保護層８はプライマー層として機能する。
第１表面保護層７と第２表面保護層８とのそれぞれは、例えば、二液ウレタン樹脂を使用できる。乾燥後の塗布量は、３ｇ/ｍ2とする。また、第３表面保護層９としては、例えば、紫外線硬化型樹脂を使用できる。乾燥後の塗布量は、例えば、６ｇ/ｍ2とする。 <Surface protective layers 7, 8, 9>
The surface protective layers 7, 8, 9 are transparent resin layers provided on the surface layer of the decorative sheet 100 in order to protect the transparent resin layer 6, the pearl pattern layer 3, and the like. The surface protective layer 7 (hereinafter also referred to as “first surface protective layer 7”) is located on the transparent resin layer 6 side, and the surface protective layer 9 (hereinafter also referred to as “third surface protective layer 9”) is a surface layer. The surface protective layer 8 (hereinafter also referred to as “second surface protective layer 8”) is positioned between the first surface protective layer 7 and the third surface protective layer 9. Here, the first surface protective layer 7 functions as an anchor layer, and the second surface protective layer 8 functions as a primer layer.
For example, a two-component urethane resin can be used for each of the first surface protective layer 7 and the second surface protective layer 8. The coating amount after drying is 3 g / m 2 . As the third surface protective layer 9, for example, an ultraviolet curable resin can be used. The coating amount after drying is, for example, 6 g / m 2 .

＜裏面プライマー層１０＞
裏面プライマー層１０は、基材層１と基材２０との接着性を向上させるためのアンカー層である。裏面プライマー層１０としては、例えば、二液ウレタン樹脂を使用できる。
＜接着剤層２１＞
接着剤層２１は、接着剤からなる層である。接着剤としては、例えば、水性ビニルウレタン樹脂を使用できる。乾燥後の塗布量は、例えば、６ｇ/ｍ2とする。
＜基材２０＞
基材２０としては、例えば、合板、ＭＤＦ層中密度繊維版、パーティクルボード層、金属板、無機質系基材を使用できる。基材２０の厚さは、例えば、５ｍｍとする。 <Backside primer layer 10>
The back primer layer 10 is an anchor layer for improving the adhesion between the base material layer 1 and the base material 20. As the back surface primer layer 10, for example, a two-component urethane resin can be used.
<Adhesive layer 21>
The adhesive layer 21 is a layer made of an adhesive. As the adhesive, for example, an aqueous vinyl urethane resin can be used. The coating amount after drying is, for example, 6 g / m 2 .
<Substrate 20>
As the base material 20, for example, a plywood, an MDF layer medium density fiber plate, a particle board layer, a metal plate, or an inorganic base material can be used. The thickness of the base material 20 is 5 mm, for example.

＜本実施形態の効果＞
本実施形態に係る発明は、以下の効果を奏する。
（１）本実施形態に係る化粧シート１００は、基材層１の上に、複数種類のパール顔料を使用したパール柄層３、透明樹脂層６及び表面保護層７，８，９がこの順に積層されている。そして、パール柄層３は、マイカ、酸化チタン及び酸化スズを含む第１パール顔料とメジウムとを含む第１パール柄層３Ａと、マイカ、酸化チタン及び酸化鉄を含む第２パール顔料とメジウムとを含む第２パール柄層３Ｂとが積層されている。また、第１パール柄層３Ａは、メジウム１００質量部に対して、第１パール顔料を０質量部より大きく２３質量部以下含んでおり、第２パール柄層３Ｂは、メジウム１００質量部に対して、第２パール顔料を０質量部より大きく１０質量部以下含んでいる。 <Effect of this embodiment>
The invention according to this embodiment has the following effects.
(1) The decorative sheet 100 according to the present embodiment has a pearl pattern layer 3, a transparent resin layer 6, and surface protective layers 7, 8, and 9 using a plurality of kinds of pearl pigments in this order on the base layer 1. Are stacked. The pearl pattern layer 3 includes a first pearl pattern layer 3A including a first pearl pigment and medium containing mica, titanium oxide and tin oxide, and a second pearl pigment and medium including mica, titanium oxide and iron oxide. The 2nd pearl pattern layer 3B containing is laminated | stacked. Further, the first pearl pattern layer 3A contains the first pearl pigment in an amount of more than 0 parts by mass and not more than 23 parts by mass with respect to 100 parts by mass of the medium, and the second pearl pattern layer 3B has an amount of 100 parts by mass of the medium. In addition, the second pearl pigment is contained in an amount larger than 0 parts by mass and 10 parts by mass or less.

このような構成により、第１パール柄層３Ａのパール顔料の含有量と第２パール柄層３Ｂのパール顔料の含有量とを調整したため、第１パール柄層３Ａや第２パール柄層３Ｂの凝集破壊を抑制でき、密着強度の低下を抑制できる。また、第１パール柄層３Ａと第２パール柄層３Ｂとを積層したため、パール柄層３による意匠性の向上効果を増大できる。   With such a configuration, the content of the pearl pigment in the first pearl pattern layer 3A and the content of the pearl pigment in the second pearl pattern layer 3B are adjusted, so that the first pearl pattern layer 3A and the second pearl pattern layer 3B Cohesive fracture can be suppressed, and a decrease in adhesion strength can be suppressed. Moreover, since the 1st pearl pattern layer 3A and the 2nd pearl pattern layer 3B were laminated | stacked, the improvement effect of the design property by the pearl pattern layer 3 can be increased.

（２）本実施形態に係る化粧シート１００は、基材層１の上に、複数種類のパール顔料を使用したパール柄層３、透明樹脂層６及び表面保護層７，８，９がこの順に積層されている。そして、パール柄層３は、マイカ、酸化チタン及び酸化スズを含む第１パール顔料とメジウムとを含む第１パール柄層３Ａと、マイカ、酸化チタン及び酸化鉄を含む第２パール顔料とメジウムとを含む第２パール柄層３Ｂとが積層されている。また、第１パール柄層３Ａは、メジウム１００質量部に対して、第１パール顔料を０質量部より大きく１７質量部以下含んでおり、第２パール柄層３Ｂは、メジウム１００質量部に対して、第２パール顔料を１０質量部より大きく３３質量部以下含んでいる。 (2) The decorative sheet 100 according to this embodiment includes a pearl pattern layer 3, a transparent resin layer 6, and surface protective layers 7, 8, and 9 using a plurality of kinds of pearl pigments in this order on the base material layer 1. Are stacked. The pearl pattern layer 3 includes a first pearl pattern layer 3A including a first pearl pigment and medium containing mica, titanium oxide and tin oxide, and a second pearl pigment and medium including mica, titanium oxide and iron oxide. The 2nd pearl pattern layer 3B containing is laminated | stacked. In addition, the first pearl pattern layer 3A contains the first pearl pigment larger than 0 parts by mass and 17 parts by mass or less with respect to 100 parts by mass of the medium, and the second pearl pattern layer 3B includes 100 parts by mass of the medium. The second pearl pigment is contained in an amount of more than 10 parts by mass and not more than 33 parts by mass.

このような構成により、第１パール柄層３Ａのパール顔料の含有量と第２パール柄層３Ｂのパール顔料の含有量とを調整したため、第１パール柄層３Ａや第２パール柄層３Ｂの凝集破壊を抑制でき、密着強度の低下を抑制できる。また、第１パール柄層３Ａと第２パール柄層３Ｂとを積層したため、パール柄層３による意匠性の向上効果を増大できる。
（３）本実施形態に係る化粧板１１０は、基材２０と、その基材２０の一方の面に形成された化粧シート１００とを有する。
これにより、意匠性が高く、密着強度が高い化粧板１１０を提供できる。 With such a configuration, the content of the pearl pigment in the first pearl pattern layer 3A and the content of the pearl pigment in the second pearl pattern layer 3B are adjusted, so that the first pearl pattern layer 3A and the second pearl pattern layer 3B Cohesive fracture can be suppressed, and a decrease in adhesion strength can be suppressed. Moreover, since the 1st pearl pattern layer 3A and the 2nd pearl pattern layer 3B were laminated | stacked, the improvement effect of the design property by the pearl pattern layer 3 can be increased.
(3) The decorative board 110 according to the present embodiment includes a base material 20 and a decorative sheet 100 formed on one surface of the base material 20.
Thereby, the decorative board 110 with high designability and high adhesion strength can be provided.

（変形例）
（１）なお、本実施形態では、パール柄層３において、第１パール柄層３Ａがベタ層２側に位置し、第２パール柄層３Ｂがアンカーコート層４側に位置する例を示したが、他の構成を採用することもできる。例えば、第２パール柄層３Ｂがベタ層２側に位置し、第１パール柄層３Ａがアンカーコート層４側に位置する構成としてもよい。
（２）また、本実施形態では、ベタ層２上にパール柄層３を形成する例を示したが、他の構成を採用することもできる。例えば、図２に示すように、ベタ層２を省略してもよい。 (Modification)
(1) In the present embodiment, in the pearl pattern layer 3, the first pearl pattern layer 3A is located on the solid layer 2 side, and the second pearl pattern layer 3B is located on the anchor coat layer 4 side. However, other configurations can be employed. For example, the second pearl pattern layer 3B may be positioned on the solid layer 2 side, and the first pearl pattern layer 3A may be positioned on the anchor coat layer 4 side.
(2) Moreover, although the example which forms the pearl pattern layer 3 on the solid layer 2 was shown in this embodiment, another structure is also employable. For example, as shown in FIG. 2, the solid layer 2 may be omitted.

（実施例１）
実施例１では、着色ポリプロピレン樹脂を用いて基材層１を形成した。基材層１の厚さは７０μｍとした。続いて、基材層１の一方の面に、二液ウレタン樹脂と塩酢ビ樹脂とを混合した樹脂に有機顔料を添加した塗工液を塗工してベタ層２を形成した。乾燥後の塗布量は２ｇ/ｍ2とした。続いて、ベタ層２上に、メジウムを主成分とする透明な樹脂に、マイカ、酸化チタン及び酸化スズを含む第１パール顔料を含む塗工液を塗工して第１パール柄層３Ａを形成した。第１パール顔料としては、日本光研工業（株）のＭＦ１００ＲＮを使用した。第１パール顔料の粒径は、５〜３０μｍとした。続いて、第１パール柄層３Ａ上に、メジウムを主成分とする透明な樹脂に、マイカ、酸化チタン及び酸化鉄を含む第２パール顔料を含む塗工液を塗工して第２パール柄層３Ｂを形成した。第２パール顔料としては、日本光研工業（株）のＭＣ３０２を使用した。第２パール顔料の粒径は、５〜３０μｍとした。これにより、パール柄層３を形成した。 Example 1
In Example 1, the base material layer 1 was formed using a colored polypropylene resin. The thickness of the base material layer 1 was 70 μm. Subsequently, a solid layer 2 was formed on one surface of the base material layer 1 by applying a coating liquid obtained by adding an organic pigment to a resin obtained by mixing a two-component urethane resin and a vinyl chloride resin. The coating amount after drying was 2 g / m 2 . Subsequently, a coating liquid containing a first pearl pigment containing mica, titanium oxide and tin oxide is applied onto the solid layer 2 on a transparent resin mainly composed of medium to form the first pearl pattern layer 3A. Formed. As the first pearl pigment, MF100RN manufactured by Nippon Koken Kogyo Co., Ltd. was used. The particle size of the first pearl pigment was 5 to 30 μm. Subsequently, a coating liquid containing a second pearl pigment containing mica, titanium oxide, and iron oxide is applied onto the first pearl pattern layer 3A on a transparent resin mainly composed of medium. Layer 3B was formed. MC302 manufactured by Nippon Koken Kogyo Co., Ltd. was used as the second pearl pigment. The particle size of the second pearl pigment was 5 to 30 μm. Thereby, the pearl pattern layer 3 was formed.

続いて、パール柄層３上に、二液ウレタン樹脂を塗工してアンカーコート層４を形成した。乾燥後の塗布量は１．２ｇ/ｍ2とした。続いて、アンカーコート層４上に、酸変性ポリプリピレン樹脂を用いて接着剤層５を形成した。接着剤層５の厚さは、１２μｍとした。続いて、接着剤層５上に、ポリオレフィン（ＰＰ）樹脂を用いて透明樹脂層６を形成した。透明樹脂層６の厚さは、６８μｍとした。続いて、透明樹脂層６の上に、二液ウレタン樹脂を塗工して第１表面保護層７を形成した。乾燥後の塗布量は、３ｇ/ｍ2とした。続いて、第１表面保護層７の上に、二液ウレタン樹脂を塗工して第２表面保護層８を形成した。乾燥後の塗布量は、３ｇ/ｍ2とした。続いて、第２表面保護層８の上に、紫外線硬化型樹脂を塗工して第３表面保護層９を形成した。乾燥後の塗布量は、６ｇ/ｍ2とした。 Subsequently, a two-component urethane resin was applied on the pearl pattern layer 3 to form an anchor coat layer 4. The coating amount after drying was 1.2 g / m 2 . Subsequently, an adhesive layer 5 was formed on the anchor coat layer 4 using an acid-modified polypropylene resin. The thickness of the adhesive layer 5 was 12 μm. Subsequently, a transparent resin layer 6 was formed on the adhesive layer 5 using a polyolefin (PP) resin. The thickness of the transparent resin layer 6 was 68 μm. Subsequently, a two-component urethane resin was applied on the transparent resin layer 6 to form a first surface protective layer 7. The coating amount after drying was 3 g / m 2 . Subsequently, a two-component urethane resin was applied on the first surface protective layer 7 to form a second surface protective layer 8. The coating amount after drying was 3 g / m 2 . Subsequently, an ultraviolet curable resin was applied on the second surface protective layer 8 to form a third surface protective layer 9. The coating amount after drying was 6 g / m 2 .

また、基材層１の他方の面、つまり、ベタ層２と反対側の面に、二液ポリエステルポリオールとセルロース樹脂とを配合した塗工液を塗工して裏面プライマー層１０を形成した。乾燥後の塗布量は、１．２ｇ/ｍ2とした。これにより、化粧シート１００を形成した。
続いて、裏面プライマー層１０の上に、水性ビニルウレタン樹脂を塗工して接着剤層２１を形成した。乾燥後の塗布量は、６ｇ/ｍ2とした。続いて、接着剤層２１を介して、化粧シート１００に基材２０を貼り付けた。これにより、化粧板１１０を形成した。 Further, a back primer layer 10 was formed by applying a coating liquid containing a two-component polyester polyol and a cellulose resin to the other surface of the base material layer 1, that is, the surface opposite to the solid layer 2. The coating amount after drying was 1.2 g / m 2 . Thereby, the decorative sheet 100 was formed.
Subsequently, an aqueous vinyl urethane resin was applied on the back primer layer 10 to form an adhesive layer 21. The coating amount after drying was 6 g / m 2 . Subsequently, the base material 20 was attached to the decorative sheet 100 via the adhesive layer 21. Thereby, the decorative board 110 was formed.

（実施例２）
実施例２では、ベタ層２を省略した。それ以外は実施例１と同様の構成とした。
（評価判定）
以上の実施例１，２の化粧板１１０について、次の評価を実施した。
（密着強度）
化粧シート１００の端部を１インチ巾で人為的に基材２０から剥離し、常温で引張試験機により引張荷重を加えて、剥離時の荷重を測定した。引張速度は５０ｍｍ/分とした。そして、剥離時の荷重が１９．６Ｎ/インチ以上のものを、合格「○」とした。
評価結果を表1に示す。 (Example 2)
In Example 2, the solid layer 2 was omitted. Otherwise, the configuration was the same as in Example 1.
(Evaluation judgment)
The following evaluation was implemented about the decorative board 110 of the above Examples 1 and 2.
(Adhesion strength)
The edge of the decorative sheet 100 was artificially peeled from the substrate 20 with a width of 1 inch, and a tensile load was applied by a tensile tester at room temperature, and the load at the time of peeling was measured. The tensile speed was 50 mm / min. And the thing of the load at the time of peeling 19.6 N / inch or more was set as the pass "(circle)".
The evaluation results are shown in Table 1.

Figure 0006610308
Figure 0006610308

表１から、実施例１（ベタ層２あり）、実施例２（ベタ層２なし）のいずれも、第１パール柄層３Ａが、メジウム１００質量部に対して、第１パール顔料を０質量部より大きく２３質量部以下含んでおり、第２パール柄層３Ｂが、メジウム１００質量部に対して、第２パール顔料を０質量部より大きく１０質量部以下含んでいる化粧シート１００では、剥離時の荷重が１９．６Ｎ/インチとなり、密着強度（剥離強度）が合格「○」となった。   From Table 1, in Example 1 (with a solid layer 2) and Example 2 (without a solid layer 2), the first pearl pattern layer 3A is 0 mass of the first pearl pigment with respect to 100 mass parts of the medium. In the decorative sheet 100, the second pearl pattern layer 3B contains a second pearl pigment larger than 0 parts by mass and 10 parts by mass or less with respect to 100 parts by mass of the medium. The load at the time was 19.6 N / inch, and the adhesion strength (peeling strength) was a pass “◯”.

また、第１パール柄層３Ａが、メジウム１００質量部に対して、第１パール顔料を０質量部より大きく１７質量部以下含んでおり、第２パール柄層３Ｂが、メジウム１００質量部に対して、第２パール顔料を１０質量部より大きく３３質量部以下含んでいる化粧シート１００でも、剥離時の荷重が１９．６Ｎ/インチとなり、密着強度が合格「○」となった。それゆえ、適切な密着強度（剥離強度）を有する化粧シート１００を提供できることがわかった。また、上記実施例１、２に記載の化粧シート１００の他にも、上記実施形態に記載の材料等を有する種々の化粧シート１００についても同様の効果を確認できた。   In addition, the first pearl pattern layer 3A contains the first pearl pigment larger than 0 parts by mass and 17 parts by mass or less with respect to 100 parts by mass of the medium, and the second pearl pattern layer 3B contains 100 parts by mass of the medium. Even in the decorative sheet 100 containing the second pearl pigment larger than 10 parts by mass and not more than 33 parts by mass, the load at the time of peeling was 19.6 N / inch, and the adhesion strength was “good”. Therefore, it was found that the decorative sheet 100 having an appropriate adhesion strength (peel strength) can be provided. In addition to the decorative sheets 100 described in Examples 1 and 2, the same effects could be confirmed for various decorative sheets 100 having the materials described in the above embodiment.

１００ 化粧シート
１１０ 化粧板
１ 基材層
２ ベタ層
３ パール柄層
３Ａ 第１パール柄層
３Ｂ 第２パール柄層
４ アンカーコート層
５ 接着剤層
６ 透明樹脂層
７，８，９ 表面保護層
１０ 裏面プライマー層
２０ 基材
２１ 接着剤層 DESCRIPTION OF SYMBOLS 100 Decorative sheet 110 Decorative plate 1 Base material layer 2 Solid layer 3 Pearl pattern layer 3A First pearl pattern layer 3B Second pearl pattern layer 4 Anchor coat layer 5 Adhesive layer 6 Transparent resin layers 7, 8, 9 Surface protective layer 10 Back primer layer 20 Base material 21 Adhesive layer

Claims (3)

基材層の上に、複数種類のパール顔料を使用したパール柄層、透明樹脂層、及び表面保護層がこの順に積層されている化粧シートであって、
前記パール柄層は、マイカ、酸化チタン及び酸化スズを含む第１パール顔料とメジウムとを含む第１パール柄層と、マイカ、酸化チタン及び酸化鉄を含む第２パール顔料とメジウムとを含む第２パール柄層とが積層されてなり、
前記第１パール柄層は、メジウム１００質量部に対して、前記第１パール顔料を０質量部より大きく２３質量部以下含んでおり、前記第２パール柄層は、メジウム１００質量部に対して、前記第２パール顔料を０質量部より大きく１０質量部以下含んでいることを特徴とする化粧シート。 On the base material layer, a decorative sheet in which a pearl pattern layer using a plurality of kinds of pearl pigments, a transparent resin layer, and a surface protective layer are laminated in this order,
The pearl pattern layer includes a first pearl pattern layer including a first pearl pigment containing mica, titanium oxide and tin oxide and a medium, a second pearl pigment including mica, titanium oxide and iron oxide, and a medium. 2 pearl pattern layers are laminated,
The first pearl pattern layer includes the first pearl pigment in an amount of more than 0 parts by mass and not more than 23 parts by mass with respect to 100 parts by mass of the medium, and the second pearl pattern layer includes 100 parts by mass of the medium. A decorative sheet comprising the second pearl pigment in an amount of more than 0 parts by mass and 10 parts by mass or less. 基材層の上に、複数種類のパール顔料を使用したパール柄層、透明樹脂層、及び表面保護層がこの順に積層されている化粧シートであって、
前記パール柄層は、マイカ、酸化チタン及び酸化スズを含む第１パール顔料とメジウムとを含む第１パール柄層と、マイカ、酸化チタン及び酸化鉄を含む第２パール顔料とメジウムとを含む第２パール柄層とが積層されてなり、
前記第１パール柄層は、メジウム１００質量部に対して、前記第１パール顔料を０質量部より大きく１７質量部以下含んでおり、前記第２パール柄層は、メジウム１００質量部に対して、前記第２パール顔料を１０質量部より大きく３３質量部以下含んでいることを特徴とする化粧シート。 On the base material layer, a decorative sheet in which a pearl pattern layer using a plurality of kinds of pearl pigments, a transparent resin layer, and a surface protective layer are laminated in this order,
The pearl pattern layer includes a first pearl pattern layer including a first pearl pigment containing mica, titanium oxide and tin oxide and a medium, a second pearl pigment including mica, titanium oxide and iron oxide, and a medium. 2 pearl pattern layers are laminated,
The first pearl pattern layer includes the first pearl pigment in an amount of more than 0 parts by mass and not more than 17 parts by mass with respect to 100 parts by mass of the medium, and the second pearl pattern layer includes 100 parts by mass of the medium. A decorative sheet comprising the second pearl pigment in an amount of more than 10 parts by mass and not more than 33 parts by mass. 基材と、その基材の一方の面に形成された請求項１または２に記載した化粧シートとを有することを特徴とする化粧板。   A decorative board comprising a base material and the decorative sheet according to claim 1 or 2 formed on one surface of the base material.
JP2016019264A 2016-02-03 2016-02-03 Decorative sheet and decorative board Active JP6610308B2 (en)