JP6520321B2 - Waterproof anticorrosion structure of concrete structure and waterproof anticorrosion method of concrete structure - Google Patents
Waterproof anticorrosion structure of concrete structure and waterproof anticorrosion method of concrete structure Download PDFInfo
- Publication number
- JP6520321B2 JP6520321B2 JP2015076623A JP2015076623A JP6520321B2 JP 6520321 B2 JP6520321 B2 JP 6520321B2 JP 2015076623 A JP2015076623 A JP 2015076623A JP 2015076623 A JP2015076623 A JP 2015076623A JP 6520321 B2 JP6520321 B2 JP 6520321B2
- Authority
- JP
- Japan
- Prior art keywords
- waterproof
- concrete
- rubber sheet
- anticorrosion
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、コンクリート構造物の防水防食構造およびコンクリート構造物の防水防食工法に関する。 The present invention relates to a waterproof anticorrosion structure for a concrete structure and a waterproof anticorrosion method for a concrete structure.
コンクリート構造物の防水防食構造およびコンクリート構造物の防水防食工法としては、例えば、セメント構造物の表面に結晶増殖剤層を形成した上に、アクリル樹脂系、エポキシ樹脂系の防水・防食性樹脂を塗布して防水防食性樹脂層を形成するコンクリートの防水防食構造とその製造方法が知られている(例えば、特許文献１参照)。 For example, as a waterproof anticorrosion structure for a concrete structure and a waterproof anticorrosion method for a concrete structure, a crystal growth agent layer is formed on the surface of a cement structure, and an acrylic resin epoxy resin epoxy resin waterproof / anticorrosion resin is used. DESCRIPTION OF RELATED ART The waterproofing anticorrosion structure of concrete which apply | coats and forms a waterproof anticorrosion resin layer and its manufacturing method are known (for example, refer patent document 1).
上記のようなコンクリートの防水防食構造では、コンクリート構造物上に形成される結晶増殖剤層及び防水防食性樹脂層は、下地コンクリートに対する変形追従性が極めて乏しいため、下地コンクリートにクラックが生じた場合には、結晶増殖剤層および防水防食性樹脂層にクラックが生じてしまう虞がある。結晶増殖剤層および防水防食性樹脂層にクラックが生じると、クラックから下地コンクリート側に硫酸や有機酸が浸入して下地コンクリートを腐食させる、或いは、防水防食性樹脂層の接着性を低下せしめ防水防食性樹脂層の剥がれや膨れを助長する虞があるという課題がある。 In the above waterproof and anticorrosion structure of concrete, since the crystal growth agent layer and the waterproof and anticorrosion resin layer formed on the concrete structure are extremely poor in deformation followability to the base concrete, when the base concrete is cracked There is a risk that the crystal growth agent layer and the waterproof and corrosion-resistant resin layer may be cracked. When a crack is generated in the crystal growth agent layer and the waterproof and corrosion-resistant resin layer, sulfuric acid and an organic acid infiltrate into the substrate concrete side from the crack to corrode the substrate concrete, or the adhesiveness of the waterproof and corrosion-resistant resin layer is reduced to waterproof There is a problem that there is a risk of promoting peeling and swelling of the anticorrosive resin layer.
本発明はかかる従来の課題に鑑みてなされたものであり、その目的とするところは、下地コンクリートにクラックが生じても高い防水防食性が維持されるコンクリート構造物の防水防食構造およびコンクリート構造物の防水防食工法を提供することにある。 The present invention has been made in view of such conventional problems, and the object of the present invention is to provide a waterproof anticorrosion structure and concrete structure of a concrete structure in which high waterproof anticorrosion properties are maintained even if cracks occur in the base concrete. To provide a waterproof anticorrosion method.
かかる目的を達成するために本発明のコンクリート構造物の防水防食構造は、下地コンクリートと前記下地コンクリート上に設けられるエポキシ樹脂系防食材との間にゴムシートが設けられており、前記ゴムシートは、前記エポキシ樹脂系防食材側に不織布または繊維質シートを備えていることを特徴とするコンクリート構造物の防水防食構造である。 In order to achieve the above object, in the waterproof and anticorrosion structure of the concrete structure of the present invention, a rubber sheet is provided between the base concrete and the epoxy resin based anticorrosion material provided on the base concrete, and the rubber sheet is A waterproof and anticorrosion structure for a concrete structure, comprising a non-woven fabric or a fibrous sheet on the side of the epoxy resin based anticorrosion material.
このようなコンクリート構造物の防水防食構造によれば、下地コンクリートとエポキシ樹脂系防食材との間にゴムシートが設けられているので、たとえ下地コンクリートにクラックを伴う変形や変位が生じたとしても、エポキシ樹脂系防食材との間に設けられたゴムシートが緩衝材となりエポキシ樹脂系防食材にクラックが生じることを防止することが可能である。また、ゴムシートが備える不織布または繊維質シートにより、エポキシ樹脂系防食材とゴムシートとをより確実に接合することが可能である。このため、下地コンクリートにクラックが生じても高い防水防食性が維持されるコンクリート構造物の防水防食構造を提供することが可能である。 According to such a waterproof and anticorrosion structure of a concrete structure, since a rubber sheet is provided between the base concrete and the epoxy resin based anticorrosion material, even if deformation or displacement accompanied by a crack occurs in the base concrete. The rubber sheet provided between the epoxy resin-based anticorrosion material serves as a buffer material, and it is possible to prevent the occurrence of cracks in the epoxy resin-based corrosion protection material. Moreover, it is possible to join an epoxy resin system anticorrosion material and a rubber sheet more certainly by a nonwoven fabric or a fibrous sheet which a rubber sheet is provided. For this reason, it is possible to provide a waterproof and corrosion prevention structure of a concrete structure in which high waterproof and corrosion resistance is maintained even if a crack occurs in the base concrete.
かかるコンクリート構造物の防水防食構造であって、前記下地コンクリートと前記ゴムシートとの間にプライマーが介在されていることが望ましい。 In such a waterproof and anticorrosion structure for a concrete structure, it is preferable that a primer be interposed between the base concrete and the rubber sheet .
このようなコンクリート構造物の防水防食構造によれば、下地コンクリートとゴムシートとの間にプライマーが介在されているので、下地コンクリートとゴムシートとの付着性が向上し、下地コンクリートにゴムシートをより確実に付着させることが可能である。 According to the waterproof anticorrosion structure of such concrete structures, since a primer between the underlying concrete and the rubber sheet is interposed, improved adhesion to the underlying concrete and rubber sheet, the rubber sheet to the underlying concrete It is possible to adhere more reliably.
かかるコンクリート構造物の防水防食構造であって、前記下地コンクリートと前記ゴムシートとの間にケイ酸質系塗布防水材が介在されていることが望ましい。 It is desirable that it is a waterproof and anticorrosion structure of such a concrete structure, and a siliceous coating waterproof material is interposed between the base concrete and the rubber sheet .
このようなコンクリート構造物の防水防食構造によれば、下地コンクリートとゴムシートとの間にケイ酸質系塗布防水材が介在されているので、下地コンクリートとゴムシートとの界面に発生する背面水によるエポキシ樹脂系防食材の膨れや剥離などに伴う損傷を抑えることが可能である。 According to the waterproof anticorrosion structure of such concrete structures, since siliceous based coating waterproof material is interposed between the lower ground concrete and rubber sheet, generated at the interface between the underlying concrete and rubber sheet rear It is possible to suppress the damage caused by the swelling and peeling of the epoxy resin based anticorrosive material by water.
かかるコンクリート構造物の防水防食構造であって、前記ゴムシート上に素地調整材としてポリマーセメントモルタルが塗布され、該ポリマーセメントモルタルの表面にプライマーが塗布され、該プライマーの表面に前記エポキシ樹脂系防食材が塗布されていることが望ましい。 In the waterproof and anticorrosion structure of such a concrete structure, a polymer cement mortar is applied on the rubber sheet as a substrate adjusting material, a primer is applied on the surface of the polymer cement mortar, and the epoxy resin based protection is applied on the surface of the primer. It is desirable that food is applied .
かかるコンクリート構造物の防水防食構造であって、前記ゴムシート上に素地調整材として樹脂パテが塗布され、 該樹脂パテの表面に前記エポキシ樹脂系防食材が塗布されていることが望ましい。
このようなコンクリート構造物の防水防食構造によれば、素地調整材の表面にプライマーを塗布する工程が省略され、コンクリート構造物の防水防食構造をより簡便に実現することができる。
It is desirable that in the waterproof and anticorrosion structure of such a concrete structure, a resin putty be applied on the rubber sheet as a base adjustment material, and the epoxy resin based anticorrosion material be applied on the surface of the resin putty .
According to such a waterproof and anticorrosion structure of a concrete structure, the step of applying a primer to the surface of the base material adjusting material can be omitted, and the waterproof and anticorrosion structure of the concrete structure can be realized more simply.
また、下地コンクリート上に、前記下地コンクリートと反対側に不織布または繊維質シートを備えた複数のゴムシートを、隣り合う前記ゴムシートの端部同士を重ねて貼り付けるゴムシート貼付ステップと、貼り付けた前記ゴムシート上に素地調整材を塗布するとともに重なり合う前記ゴムシートによる段差を均す素地調整材塗布ステップと、前記素地調整材上にエポキシ樹脂系防食材を塗布する防食材塗布ステップと、を有することを特徴とするコンクリート構造物の防水防食工法である。 In addition, a rubber sheet attaching step of laminating a plurality of rubber sheets provided with a non-woven fabric or a fibrous sheet on the side opposite to the base concrete on the base concrete, overlapping the end portions of the adjacent rubber sheets , said surface preparation material applying step to smooth the step caused by the rubber sheet overlapping with applying a surface preparation material to the rubber sheet was a sacrificial material coating step of applying the epoxy resin anticorrosion material on the surface preparation materials, a It is a waterproof anticorrosion method of a concrete structure characterized by having.
このようなコンクリート構造物の防水防食工法によれば、隣り合うゴムシートの端部同士を重ね合わせて貼り付けた複数のゴムシート上に素地調整材を塗布してエポキシ樹脂系防食材を塗布することにより、たとえ下地コンクリートにクラックを伴う変形や変位が生じたとしてもエポキシ樹脂系防食材にはクラックが生じ難い防水防食構造を容易に実現することが可能である。また、ゴムシート上に塗布する素地調整材により、ゴムシートを重ね合わせたときに生じる段差をならすので、ゴムシートとエポキシ樹脂系防食材との間に隙間が生じにくい。このため、より損傷しにくい防水防食層を形成することが可能である。 According to such a waterproof anticorrosion method of a concrete structure, a base adjusting material is applied on a plurality of rubber sheets on which end portions of adjacent rubber sheets are overlapped and attached, and an epoxy resin anticorrosion material is applied. Thus, even if deformation or displacement accompanied by a crack occurs in the base concrete, it is possible to easily realize a waterproof and corrosion resistant structure in which a crack is less likely to occur in the epoxy resin-based corrosion-resistant material. In addition, since the base adjustment material applied on the rubber sheet smoothes the step that is generated when the rubber sheets are stacked, a gap does not easily occur between the rubber sheet and the epoxy resin-based anticorrosion material. For this reason, it is possible to form a waterproof and anticorrosion layer which is less likely to be damaged.
また、不織布または繊維質シートを備えたゴムシートを用いることにより、エポキシ樹脂系防食材をより確実にゴムシートに接合することが可能である。すなわち、下地コンクリートにクラックが生じても高い防水防食性が維持されるコンクリート構造物の防水防食工法を提供することが可能である。 In addition, by using a rubber sheet provided with a non-woven fabric or a fibrous sheet, it is possible to more reliably bond the epoxy resin based anticorrosion material to the rubber sheet . That is, it is possible to provide a waterproof and anticorrosion method for a concrete structure in which high waterproof and anticorrosion properties are maintained even if cracks occur in the base concrete.
本発明によれば、下地コンクリートにクラックが生じても高い防水防食性が維持されるコンクリート構造物の防水防食構造およびコンクリート構造物の防水防食工法を提供することが可能である。 According to the present invention, it is possible to provide a waterproof anticorrosion structure for a concrete structure and a waterproof anticorrosion method for a concrete structure, in which high waterproof anticorrosion properties are maintained even if cracks occur in the base concrete.
以下、本発明に係る一実施形態について図面を参照しつつ詳細に説明する。 Hereinafter, an embodiment according to the present invention will be described in detail with reference to the drawings.
本実施形態では、本発明のコンクリート構造物の防水防食構造を、例えば、鉄筋コンクリート造の地下ピットの底をなす下地コンクリート１に適用した例について説明する。 In this embodiment, an example in which the waterproof and corrosion prevention structure of the concrete structure of the present invention is applied to, for example, a foundation concrete 1 which forms the bottom of a reinforced concrete underground pit will be described.
本実施形態のコンクリート構造物の防水防食構造は、図１に示すように、下地コンクリート１の表面にプライマー２を介して弾性シートとしてのゴムシート３が設けられ、ゴムシート３の上に素地調整材４が設けられ、素地調整材４の表面にプライマー５を介して硫酸や有機酸等に抵抗性を有するエポキシ樹脂系防食材６が設けられている。 In the waterproof and anticorrosion structure of a concrete structure according to the present embodiment, as shown in FIG. 1, a rubber sheet 3 as an elastic sheet is provided on the surface of a base concrete 1 via a primer 2. A material 4 is provided, and an epoxy resin-based anticorrosion material 6 having resistance to sulfuric acid, organic acid or the like is provided on the surface of the base material adjustment material 4 via a primer 5.
ゴムシート３は、例えばブチルゴム製のシートであり、下地コンクリート１側に貼り付けられるように下面に粘着層３ａが設けられており、上面には、不織布３ｂや繊維質シートが一体に設けられている。 The rubber sheet 3 is, for example, a butyl rubber sheet, and the adhesive layer 3a is provided on the lower surface so as to be attached to the base concrete 1 side, and the nonwoven fabric 3b and the fibrous sheet are integrally provided on the upper surface There is.
１枚のゴムシート３の面積は、地下ピットの床の面積より十分に小さいので、地下ピットの床を施工する場合には、複数枚のゴムシート３を用い、互いに隣り合うゴムシート３の端部同士が重なり合うように各ゴムシート３を配置して隙間が生じないように設けられている。
素地調整材４は、例えば、ポリマーセメントモルタルや樹脂パテであって、ゴムシート３の表面に塗布するとともにゴムシート３を重ね合わせることにより生じた段差をならすように塗布されている。
Since the area of one rubber sheet 3 is sufficiently smaller than the area of the floor of the underground pit, when constructing the floor of the underground pit, using a plurality of rubber sheets 3, the ends of the rubber sheets 3 adjacent to each other are used Each rubber sheet 3 is disposed so that the parts overlap with each other so that no gap is generated.
The base adjusting material 4 is, for example, a polymer cement mortar or a resin putty, and is applied to the surface of the rubber sheet 3 so as to smooth the step caused by overlapping the rubber sheet 3.
エポキシ樹脂系防食材６は、素地調整材４との間にプライマー５を介して４層重ねて塗布されている。 The epoxy resin-based anticorrosion material 6 is applied to the base material adjustment material 4 in four layers with the primer 5 interposed therebetween.
本実施形態のコンクリート構造体の防水防食構造を地下ピットの床に施工する防水防食工法は、例えば図２に示すように、まず、床をなす下地コンクリート１の表面を清掃しジャンカ処理を行い（表面前処理ステップＳ１）、その後下地コンクリート１の表面にプライマー２をローラーばけ等により均一に塗布する（プライマー塗布ステップＳ２）。 For example, as shown in FIG. 2, the waterproofing and corrosion preventing method of constructing the waterproofing and corrosion preventing structure of the concrete structure of the present embodiment on the floor of the underground pit first cleans the surface of the foundation concrete 1 forming the floor and performs the junker treatment In the surface pretreatment step S1), after that, the primer 2 is uniformly applied to the surface of the base concrete 1 by a roller brush or the like (primer application step S2).
次に、ゴムシート３の剥離紙を剥がして粘着層を露出し、互いに隣り合うゴムシート３の端部同士が重なり合うように複数枚のゴムシート３をプライマー２が塗布された下地コンクリート１上に貼り付けて床全面に敷き詰める（弾性シート貼付ステップＳ３）。敷き詰めたゴムシート３はハンドローラー等により十分に圧着する。 Next, the release paper of the rubber sheet 3 is peeled off to expose the adhesive layer, and a plurality of rubber sheets 3 are coated on the base concrete 1 to which the primer 2 is applied so that the end portions of the adjacent rubber sheets 3 overlap. It sticks and it spreads on the whole floor (elastic sheet sticking step S3). The spread rubber sheet 3 is sufficiently crimped by a hand roller or the like.
次に、敷き詰められたゴムシート３上に素地調整材４を塗布する（素地調整材塗布ステップＳ４）。素地調整材４は、ゴムシート３が重ね合わされて生じた段差をならすとともに、その他のゴムシート３の表面にはほぼ均一に塗布する。このとき、素地調整材４としてポリマーセメントモルタルを用いた場合には、その表面にプライマー５を塗布する。一方、樹脂パテを用いた場合には、プライマー５は塗布しない。 Next, the substrate adjusting material 4 is applied onto the spread-laid rubber sheet 3 (substrate adjusting material applying step S4). The base adjusting material 4 flattens the level difference generated by the overlapping of the rubber sheets 3 and applies the surface substantially uniformly to the surfaces of the other rubber sheets 3. At this time, when a polymer cement mortar is used as the substrate adjusting material 4, the primer 5 is applied to the surface thereof. On the other hand, when the resin putty is used, the primer 5 is not applied.
最後に、エポキシ樹脂系防食材６を塗布する（防食材塗布ステップＳ５）。エポキシ樹脂系防食材６は、ローラーばけ等により３〜４層重ねて塗布する。 Finally, the epoxy resin based anticorrosive material 6 is applied (anticorrosive material applying step S5). The epoxy resin based anticorrosion material 6 is applied by overlapping three to four layers by roller brushing or the like.
本コンクリート構造物の防水防食構造によるクラック発生防止の効果として、ひび割れ追従性試験の結果を示す。図３にひび割れ追従性試験に用いた試験片を示し、図４にひび割れ追従性試験の結果を示す。 As an effect of the crack generation prevention by the waterproof and corrosion prevention structure of this concrete structure, the result of a crack followability test is shown. The test piece used for the crack followability test is shown in FIG. 3, and the result of the crack followability test is shown in FIG.
ひび割れ追従性試験では、長方形状のフレキシブル基板７の長手方向におけるほぼ中央に、長手方向と直交する方向に沿って、一方の面側のみ切り込み７ａを設け、他方の面に切り込み７ａの両側に亘るように防食材塗膜８を形成した試験片９を用意する。試験片９に形成する防食材塗膜８は、（１）エポキシ樹脂系防食材６のみ塗布したもの（２）エポキシ樹脂系防食材６とフレキシブル基板７との間にポリマーセメント防水材を設けたもの（３）エポキシ樹脂系防食材６とフレキシブル基板７との間にゴムシート３を設けたもの、の３種類とし、各々４つの試験片９を用意した。ここで、いずれの試験片９もエポキシ樹脂系防食材６を４層設けている。 In the crack followability test, the notch 7a is provided only at one surface side along the direction orthogonal to the longitudinal direction at substantially the center of the rectangular flexible substrate 7 in the longitudinal direction, and the other surface extends over both sides of the notch 7a. Thus, the test piece 9 which formed the anticorrosive coating film 8 is prepared. The anticorrosive coating 8 formed on the test piece 9 is (1) coated with only the epoxy resin based anticorrosive 6 (2) a polymer cement waterproofing material provided between the epoxy resin based anticorrosive 6 and the flexible substrate 7 Three (3) types were used, in which the rubber sheet 3 was provided between the epoxy resin-based anticorrosive material 6 and the flexible substrate 7, and four test pieces 9 were prepared. Here, each test piece 9 is provided with four layers of the epoxy resin based anticorrosive material 6.
ひび割れ追従性試験では、防食材塗膜８を形成した試験片９に、フレキシブル基板７の切り込み７ａにクリップゲージ（不図示）を備え、防食材塗膜８の表面には、切り込み７ａの両側に亘るように歪みゲージ（不図示）を貼り付け、クリップゲージ及び歪みゲージが備えられた試験片９の、フレキシブル基板７の長手方向における両端部を引張試験機にて引張する。このとき、フレキシブル基板７が切り込み７ａにて破断した部位をひび割れとみなし、その後の防食材塗膜８の追従性及びひび割れの発生状況を確認している。 In the crack followability test, the test piece 9 on which the anticorrosive coating 8 is formed is provided with a clip gauge (not shown) in the notch 7a of the flexible substrate 7 and on the surface of the anticorrosive coating 8 on both sides of the notch 7a. A strain gauge (not shown) is attached across the entire surface, and both ends of the test piece 9 provided with the clip gauge and the strain gauge in the longitudinal direction of the flexible substrate 7 are pulled with a tensile tester. At this time, a portion where the flexible substrate 7 is broken at the notch 7a is regarded as a crack, and the followability of the anticorrosive coating film 8 and the occurrence of the crack thereafter are confirmed.
ひび割れ追従性試験の結果は、（１）エポキシ樹脂系防食材６のみ塗布した防食材塗膜８を備えた試験片９は、図４（ａ）に示すようにフレキシブル基板７の破断後、防食材塗膜８は０．０１ｍｍまで追従して破断した。（２）エポキシ樹脂系防食材６とフレキシブル基板７との間にポリマーセメント防水材を設けた防食材塗膜８を備えた試験片９は、図４（ｂ）に示すようにフレキシブル基板７の破断後、防食材塗膜８は０．９ｍｍまで追従して破断した。（３）エポキシ樹脂系防食材６とフレキシブル基板７との間にゴムシート３を設けた防食材塗膜８を備えた試験片９は、図４（ｃ）に示すようにフレキシブル基板７の破断後、防食材塗膜８は５ｍｍ以上破断することなく追従した。 The results of the crack followability test were as follows: (1) The test piece 9 provided with the anticorrosive coating 8 coated with only the epoxy resin based anticorrosive 6 was protected after breakage of the flexible substrate 7 as shown in FIG. The food coating 8 was broken following to 0.01 mm. (2) The test piece 9 provided with the anticorrosive coating film 8 provided with a polymer cement waterproofing material between the epoxy resin based anticorrosive material 6 and the flexible substrate 7 is a flexible substrate 7 as shown in FIG. After breakage, the anticorrosive coating 8 fractured following up to 0.9 mm. (3) The test piece 9 provided with the anticorrosive coating film 8 provided with the rubber sheet 3 between the epoxy resin based anticorrosive material 6 and the flexible substrate 7 is a fracture of the flexible substrate 7 as shown in FIG. After that, the anticorrosive coating 8 was followed without breaking for 5 mm or more.
このように本実施形態のコンクリート構造物の防水防食構造によれば、下地コンクリート１とエポキシ樹脂系防食材６との間にゴムシート３が設けられているので、たとえ下地コンクリート１にクラックを伴う変形や変位が生じたとしても、エポキシ樹脂系防食材６との間に設けられたゴムシート３が緩衝材となりエポキシ樹脂系防食材６にクラックが生じることを防止することが可能である。すなわち、下地コンクリート１にクラックが生じても高い防水防食性が維持されるコンクリート構造物の防水防食構造を提供することが可能である。 As described above, according to the waterproof and corrosion preventing structure of the concrete structure of the present embodiment, since the rubber sheet 3 is provided between the base concrete 1 and the epoxy resin based anticorrosion material 6, the base concrete 1 is accompanied by a crack. Even if deformation or displacement occurs, the rubber sheet 3 provided between the epoxy resin-based anticorrosive material 6 serves as a buffer material, and it is possible to prevent the epoxy resin-based anticorrosive material 6 from being cracked. That is, it is possible to provide a waterproof and corrosion resistant structure of a concrete structure in which high waterproof and corrosion resistance is maintained even if a crack occurs in the base concrete 1.
また、下地コンクリート１とゴムシート３との間にプライマー２が介在されているので、下地コンクリート１とゴムシート３との付着性が向上し、下地コンクリート１にゴムシート３をより確実に付着させることが可能である。 Further, since the primer 2 is interposed between the base concrete 1 and the rubber sheet 3, the adhesion between the base concrete 1 and the rubber sheet 3 is improved, and the rubber sheet 3 is more reliably adhered to the base concrete 1. It is possible.
また、防水性を備えたゴムシート３により、下地コンクリート１から浸透してくる背面水の発生を抑えることが可能である。このため、背面水によるエポキシ樹脂系防食材６の膨れや剥離の発生を抑え、損傷を防止することが可能である。 Moreover, it is possible to suppress generation | occurrence | production of the back surface water which permeates from the base concrete 1 by the rubber sheet 3 provided with waterproofness. For this reason, it is possible to suppress generation | occurrence | production of swelling and peeling of the epoxy resin-type anticorrosive material 6 by back surface water, and to prevent damage.
また、ゴムシート３が粘着層３ａを備えているので、ゴムシート３を下地コンクリート１により確実に貼り付けることが可能である。 Moreover, since the rubber sheet 3 is provided with the adhesive layer 3a, the rubber sheet 3 can be reliably attached to the base concrete 1.
また、ゴムシート３が不織布３ｂまたは繊維質シートを備えているので、ゴムシート３にエポキシ樹脂系防食材６をより確実に接合することが可能である。 Further, since the rubber sheet 3 is provided with the non-woven fabric 3b or the fibrous sheet, it is possible to more reliably bond the epoxy resin based anticorrosion material 6 to the rubber sheet 3.
また、隣り合うゴムシート３の端部同士を重ね合わせて貼り付けた複数のゴムシート３上に素地調整材４を塗布してエポキシ樹脂系防食材６を塗布することにより、例え下地コンクリート１にクラックを伴う変形や変位が生じたとしてもエポキシ樹脂系防食材６にはクラックが生じ難い防水防食構造を容易に実現することが可能である。 In addition, the base adjusting material 4 is applied on a plurality of rubber sheets 3 on which the end portions of adjacent rubber sheets 3 are overlapped and attached, and the epoxy resin based anticorrosion material 6 is applied. Even if deformation or displacement accompanied by a crack occurs, it is possible to easily realize a waterproof and corrosion-resistant structure in which a crack is less likely to occur in the epoxy resin based corrosion resistant material 6.
また、下地コンクリート１とエポキシ樹脂系防食材６との緩衝層として備える部材が、厚みを管理して製造されるゴムシート３なので、貼り付けるだけで均一な厚みの緩衝層を容易に形成することが可能である。このため、緩衝層の厚み管理をすることなく容易に施工することが可能である。
また、ゴムシート３上に塗布する素地調整材４により、ゴムシート３を重ね合わせたときに生じる段差をならすので、ゴムシート３とエポキシ樹脂系防食材６との間に隙間が生じにくい。このため、より損傷しにくい防水防食層を形成することが可能である。すなわち、下地コンクリート１にクラックが生じても高い防水防食性が維持されるコンクリート構造物の防水防食構造を容易に実現することが可能なコンクリート構造物の防水防食工法を提供することが可能である。
Moreover, since the member provided as a buffer layer of the base concrete 1 and the epoxy resin-based anticorrosion material 6 is a rubber sheet 3 manufactured by controlling the thickness, it is possible to easily form a buffer layer having a uniform thickness simply by pasting. Is possible. For this reason, it is possible to apply easily, without managing the thickness of a buffer layer.
In addition, the base adjusting material 4 applied on the rubber sheet 3 smoothes the difference in level when the rubber sheet 3 is superposed, so that a gap is not easily generated between the rubber sheet 3 and the epoxy resin based anticorrosion material 6. For this reason, it is possible to form a waterproof and anticorrosion layer which is less likely to be damaged. That is, it is possible to provide a waterproof and corrosion protection method of a concrete structure capable of easily realizing a waterproof and corrosion protection structure of a concrete structure in which high waterproof and corrosion resistance is maintained even if a crack occurs in the base concrete 1 .
上記実施形態においては、地下ピットの床をなす下地コンクリート１の表面にプライマー２を塗布した例について説明したが、例えば下地コンクリート１が湿潤状態にある場合や、水槽をなし隣接するピットとの間を仕切るコンクリート壁を防水防食処理する場合には、図５に示すように、下地コンクリート１とゴムシートとの間にケイ酸質系塗布防水材１０を設けることが望ましい。すなわち図２におけるプライマー塗布ステップＳ２において、下地コンクリート１の表面にプライマー２に替えてケイ酸質系塗布防水材１０を塗布することが望ましい。この場合には、ケイ酸質系塗布防水材１０によっても下地コンクリート１から浸透してくる背面水の発生が抑えられ、更に下地コンクリート１の表面を硬く緻密に改善することが可能である。このため、下地コンクリート１が湿潤状態にある場合等であっても、背面水によるエポキシ樹脂系防食材６の膨れや剥離の発生を抑えより確実に損傷を防止することが可能である。 In the above embodiment, although the example in which the primer 2 is applied to the surface of the foundation concrete 1 forming the floor of the underground pit has been described, for example, when the foundation concrete 1 is in a wet state or without a water tank, between the adjacent pits. When waterproofing and treating the concrete wall which partitions off, as shown in FIG. 5, it is desirable to provide the siliceous coating waterproofing material 10 between the base concrete 1 and the rubber sheet. That is, in the primer application step S2 in FIG. 2, it is desirable to apply the siliceous-based application waterproofing material 10 to the surface of the base concrete 1 instead of the primer 2. In this case, the generation of back surface water permeating from the base concrete 1 is suppressed also by the siliceous coating waterproof material 10, and it is possible to make the surface of the base concrete 1 hard and dense. For this reason, even when the base concrete 1 is in a wet state or the like, it is possible to prevent the occurrence of swelling and peeling of the epoxy resin-based anticorrosion material 6 due to the back water more reliably prevent damage.
上記実施形態においては、弾性シートとしてブチルゴム製のシートを用いた例について説明したが、これに限るものではない。例えば、エチレンプロピレンゴム、エチレン酢酸ビニルシート、塩化ビニル樹脂系シートなどの合成高分子系シートや改質アスファルトシートなど、下地コンクリート１のひび割れや膨れ等により下地コンクリート１とエポキシ樹脂系防食材６との間に生じる変位を吸収できる程度の弾性を備えたシートであれば構わない。 In the said embodiment, although the example using the sheet | seat made from butyl rubber as an elastic sheet was demonstrated, it does not restrict to this. For example, base concrete 1 and epoxy resin based anticorrosion material 6 by cracking or swelling of base concrete 1 such as synthetic polymer sheet such as ethylene propylene rubber, ethylene vinyl acetate sheet, vinyl chloride resin sheet and modified asphalt sheet The sheet may be any sheet as long as it has an elasticity enough to absorb the displacement occurring between the two.
上記実施形態は、本発明の理解を容易にするためのものであり、本発明を限定して解釈するためのものではない。本発明は、その趣旨を逸脱することなく、変更、改良され得ると共に、本発明にはその等価物が含まれることはいうまでもない。 The above embodiments are for the purpose of facilitating the understanding of the present invention, and are not for the purpose of limiting the present invention. It goes without saying that the present invention can be modified and improved without departing from the gist thereof, and that the present invention includes the equivalents thereof.
１ 下地コンクリート
２ プライマー
３ ゴムシート
３ａ 粘着層
３ｂ 不織布
４ 素地調整材
５ プライマー
６ エポキシ樹脂系防食材
７ フレキシブル基板
７ａ 切り込み
８ 防食材塗膜
９ 試験片
１０ ケイ酸質系塗布防水材
DESCRIPTION OF SYMBOLS 1 base concrete 2 primer 3 rubber sheet 3a adhesive layer 3b non-woven fabric 4 base material adjustment material 5 primer 6 epoxy resin based anticorrosion material 7 flexible substrate 7 a notch 8 anticorrosive material coating 9 test piece 10 siliceous coating waterproof material
Claims (6)
前記ゴムシートは、前記エポキシ樹脂系防食材側に不織布または繊維質シートを備えていることを特徴とするコンクリート構造物の防水防食構造。 A rubber sheet is provided between the base concrete and the epoxy resin based anticorrosive material provided on the base concrete,
The waterproof and anticorrosion structure of a concrete structure, wherein the rubber sheet is provided with a non-woven fabric or a fibrous sheet on the side of the epoxy resin based anticorrosion material.
前記下地コンクリートと前記ゴムシートとの間にプライマーが介在されていることを特徴とするコンクリート構造物の防水防食構造。 A waterproof and corrosion resistant structure for a concrete structure according to claim 1,
A waterproof and corrosion preventing structure for a concrete structure, wherein a primer is interposed between the base concrete and the rubber sheet .
前記下地コンクリートと前記ゴムシートとの間にケイ酸質系塗布防水材が介在されていることを特徴とするコンクリート構造物の防水防食構造。 A waterproof and corrosion resistant structure for a concrete structure according to claim 1,
A waterproof and anticorrosion structure for a concrete structure, wherein a siliceous coating waterproof material is interposed between the base concrete and the rubber sheet .
前記ゴムシート上に素地調整材としてポリマーセメントモルタルが塗布され、
該ポリマーセメントモルタルの表面にプライマーが塗布され、
該プライマーの表面に前記エポキシ樹脂系防食材が塗布されていることを特徴とするコンクリート構造物の防水防食構造。 A waterproof and corrosion resistant structure for a concrete structure according to any one of claims 1 to 3, which is:
A polymer cement mortar is applied on the rubber sheet as a substrate adjusting material,
A primer is applied to the surface of the polymer cement mortar;
A waterproof and corrosion resistant structure for a concrete structure , wherein the epoxy resin based corrosion resistant material is applied to the surface of the primer .
前記ゴムシート上に素地調整材として樹脂パテが塗布され、
該樹脂パテの表面に前記エポキシ樹脂系防食材が塗布されていることを特徴とするコンクリート構造物の防水防食構造。 A waterproof and corrosion resistant structure for a concrete structure according to any one of claims 1 to 3, which is:
A resin putty is applied on the rubber sheet as a substrate adjustment material,
A waterproof and corrosion resistant structure of a concrete structure , wherein the epoxy resin based corrosion inhibitor is applied to the surface of the resin putty .
貼り付けた前記ゴムシート上に素地調整材を塗布するとともに重なり合う前記ゴムシートによる段差を均す素地調整材塗布ステップと、
前記素地調整材上にエポキシ樹脂系防食材を塗布する防食材塗布ステップと、
を有することを特徴とするコンクリート構造物の防水防食工法。 A rubber sheet attaching step of attaching a plurality of rubber sheets provided with a non-woven fabric or a fibrous sheet on the side opposite to the base concrete on the base concrete, overlapping end portions of the adjacent rubber sheets ;
Applying a substrate adjusting material onto the stuck rubber sheet and applying a substrate adjusting material applying step to level the level difference caused by the overlapping rubber sheets ;
An anticorrosive material application step of applying an epoxy resin anticorrosion material on the base material adjustment material;
A waterproof and anticorrosion method for a concrete structure characterized by having: