JP6274574B2 - Laminated glass, glass with heating mechanism and vehicle - Google Patents

Description

  The present invention relates to a laminated glass having a mesh sheet, a glass with a heating mechanism having a laminated glass, and a vehicle having the laminated glass.

  2. Description of the Related Art Conventionally, as a defroster device used for a window glass such as a front window or a rear window of a vehicle, an apparatus in which a heating wire made of tungsten wire or the like is arranged on the entire window glass is known (for example, Patent Document 1 and Patent Document 2). reference). In this prior art, a heating wire arranged on the entire window glass is energized, and the window glass is heated by resistance heating to remove fogging of the window glass or to melt snow and ice attached to the window glass. The occupant's field of view can be secured.

JP 2013-173402 A JP-A-8-72674

  In a conventional defroster device, a bonding layer and a heating wire are sandwiched between a pair of glass plates and thermocompression bonded to form a laminated glass. Moreover, as a heating wire, what consists of the tungsten wire etc. which were manufactured at another process was used. However, in the method of arranging heating wires manufactured in a separate process, the arrangement pattern of heating wires is limited to simple shapes such as straight lines and wavy lines, and it is difficult to arrange them in a complicated shape. In addition, it is difficult to properly arrange heating wires having a rectangular cross-sectional shape on the glass plate or the resin layer in the same direction. Therefore, the heating wire has only to have a circular cross-sectional shape.

  On the other hand, as a wiring forming method, a method of forming a conductive wiring on a base substrate by patterning using a photolithography technique is known. In this method, first, a conductive metal layer is formed on a flat base substrate by attaching a metal foil such as a copper foil, plating, sputtering, or the like. Next, a resist pattern is formed on the conductive metal layer using a photolithography technique. Then, the conductive metal layer is etched using this resist pattern as a mask. By this etching, the conductive metal layer is patterned into a pattern substantially the same as the resist pattern. This method has an advantage that even a conductive wiring having a complicated arrangement pattern or cross-sectional shape can be easily formed.

  By the way, many window glasses such as a front window and a rear window of a vehicle are curved in order to reduce air resistance and improve design. And when providing the defroster apparatus provided with the heating wire in this curved window glass, it is necessary to insert | stack a heating wire between a pair of curved glass plates to make a laminated glass.

  However, if a flat plate member is sandwiched between a pair of curved glass plates, there is a problem that the flat plate member cannot follow the curve of the glass plate and wrinkles occur in the flat plate member. Therefore, when the heating wire is formed in the laminated glass provided with the defroster device, it has not been possible to employ the above-described technology for forming the conductive wiring on the base substrate by patterning using the photolithography technology.

  The present invention has been made in consideration of the above points, and when a mesh sheet in which a conductive mesh is formed on a substrate is sandwiched between a pair of curved glass plates, wrinkles are generated on the mesh sheet. It aims at suppressing appropriately.

The laminated glass according to the present invention is
A pair of curved glasses;
A mesh sheet disposed between the pair of curved glasses;
A bonding layer disposed between each glass and the mesh sheet and bonding the glass and the mesh sheet;
The mesh sheet has an unstretched resin base material and a conductive mesh formed on the unstretched resin base material.

  In the laminated glass according to the present invention, the conductive mesh is formed using a conductive fine wire, and the width of the conductive fine wire changes so as to become narrower as the distance from the unstretched resin base material increases along the normal direction of the mesh sheet. May be.

  In the laminated glass according to the present invention, the conductive mesh is formed using a conductive fine wire, and the conductive fine wire may include a conductive metal layer and a dark color layer covering at least a part of the surface of the conductive metal layer. Good.

  The glass with a heating mechanism according to the present invention includes the laminated glass described above and a power source connected to the conductive mesh of the laminated glass.

  A vehicle according to the present invention includes the laminated glass described above.

  ADVANTAGE OF THE INVENTION According to this invention, when the sheet | seat which formed the heating wire on the base base material is pinched | interposed between a pair of curved glass plates, generation | occurrence | production of a wrinkle in a sheet | seat can be suppressed appropriately.

FIG. 1 is a diagram for explaining an embodiment according to the present invention, and is a perspective view schematically showing a vehicle provided with a laminated glass. In particular, FIG. 1 schematically shows an automobile with laminated glass as an example of a vehicle. FIG. 2 is a view of the laminated glass as viewed from the normal direction of the plate surface. FIG. 3 is a cross-sectional view of the laminated glass of FIG. FIG. 4 is a view showing a state before lamination of each member constituting the laminated glass of FIG. FIG. 5 is a plan view of the mesh sheet as seen from the normal direction of the sheet surface, and is a plan view showing an example of a conductive mesh pattern. FIG. 6 is a cross-sectional view corresponding to the line AA in FIG. 5, and is a diagram illustrating an example of a cross-sectional shape of the conductive thin wire. FIG. 7 is a cross-sectional view corresponding to the line AA in FIG. 5 and is a diagram illustrating another example of the cross-sectional shape of the conductive thin wire. FIG. 8 is a diagram for explaining an example of a method for producing laminated glass. FIG. 9 is a diagram for explaining an example of a method for producing laminated glass. FIG. 10 is a diagram for explaining an example of a method for producing laminated glass. FIG. 11 is a diagram for explaining an example of a method for producing laminated glass. FIG. 12 is a diagram for explaining an example of a method for producing laminated glass. FIG. 13 is a diagram for explaining an example of a method for producing laminated glass. FIG. 14 is a diagram for explaining an example of a method for producing laminated glass. FIG. 15 is a diagram for explaining an example of a method for manufacturing a laminated glass.

  Hereinafter, an embodiment of the present invention will be described with reference to the drawings. In the drawings attached to the present specification, for the sake of illustration and ease of understanding, the scale, the vertical / horizontal dimension ratio, and the like are appropriately changed and exaggerated from those of the actual product.

  In the present specification, the terms “plate”, “sheet”, and “film” are not distinguished from each other only based on the difference in names. For example, “mesh sheet” is a concept that includes a member that can be called a plate or a film. Therefore, “mesh sheet” is a member called “mesh plate (substrate)” or “mesh film”. It cannot be distinguished only by the difference.

  In addition, “sheet surface (plate surface, film surface)” means a target sheet-like member (plate-like) when the target sheet-like (plate-like, film-like) member is viewed as a whole and globally. It refers to the surface that coincides with the plane direction of the member or film-like member.

  Furthermore, as used in this specification, the shape and geometric conditions and the degree thereof are specified. For example, terms such as “parallel”, “orthogonal”, “identical”, length and angle values, etc. Without being bound by meaning, it should be interpreted including the extent to which similar functions can be expected.

  1 to 15 are diagrams for explaining an embodiment according to the present invention. Among these, FIG. 1 is a diagram schematically showing an automobile equipped with a laminated glass, FIG. 2 is a diagram of the laminated glass viewed from the normal direction of the plate surface, and FIG. 3 is a diagram of FIG. FIG. 4 is a cross-sectional view of the glass, and FIG. 4 is a diagram showing a state before lamination of each member constituting the laminated glass of FIG.

  As shown in FIG. 1, an automobile 1 as an example of a vehicle has window glasses such as a front window, a rear window, and a side window. Here, an example in which the front window 5 is formed of a laminated glass 10 will be described. The automobile 1 has a power source 7 such as a battery.

  FIG. 2 shows the laminated glass 10 viewed from the normal direction of the plate surface. Moreover, the cross-sectional view corresponding to the III-III line of the laminated glass 10 of FIG. 2 is shown in FIG. The laminated glass 10 includes a pair of curved glass plates 11 and 12, a mesh sheet 20 disposed between the pair of curved glass plates 11 and 12, and a joint that joins the glass plates 11 and 12 and the mesh sheet 20. Layers 13 and 14.

  The mesh sheet 20 connects the base material 30, the conductive mesh 40 formed on the base material 30, the wiring part 15 for energizing the conductive mesh 40, and the conductive mesh 40 and the wiring part 15. And a connecting portion 16.

  In the example shown in FIGS. 2 and 3, the conductive mesh 40 is energized from the power source 7 such as a battery through the wiring portion 15 and the connection portion 16, and the conductive mesh 40 is heated by resistance heating. The heat generated in the conductive mesh 40 is transmitted to the glass plates 11 and 12 through the bonding layers 13 and 14, and the glass plates 11 and 12 are warmed. Thereby, the cloudiness by the dew condensation adhering to the glass plates 11 and 12 can be removed. Moreover, when snow and ice adhere to the glass plates 11 and 12, this snow and ice can be melted. Therefore, a passenger | crew's visual field is ensured favorable.

  In order to produce this laminated glass 10, as shown in FIG. 4, the curved glass plate 11, the bonding layer 13, the mesh sheet 20, the bonding layer 14, and the curved glass plate 12 are superposed in this order, and heated and pressurized. Thus, the curved glass plate 11, the mesh sheet 20, and the curved glass plate 12 are bonded by the bonding layers 13 and 14.

  At this time, the flat mesh sheet 20 is sandwiched between the curved glass plates 11 and 12, but by using the unstretched resin base material 30 as the base material 30 of the mesh sheet 20, wrinkles to the mesh sheet 20 are achieved. Can be appropriately suppressed. Details of the substrate 30 will be described later.

  In particular, when the glass plates 11 and 12 are used for a front window, it is preferable to use a glass plate having a high visible light transmittance so as not to obstruct the occupant's field of view. Examples of the material of the glass plates 11 and 12 include soda lime glass and blue plate glass. The glass plates 11 and 12 preferably have a transmittance in the visible light region of 90% or more. Here, the visible light transmittance of the glass plates 11 and 12 is measured within a measurement wavelength range of 380 nm to 780 nm using a spectrophotometer (“UV-3100PC” manufactured by Shimadzu Corporation, JISK0115 compliant product). Of the transmittance at each wavelength. The visible light transmittance may be lowered by coloring a part or the whole of the glass plates 11 and 12. In this case, it is possible to block direct sunlight and to make it difficult to visually recognize the inside of the vehicle from outside the vehicle.

  Moreover, it is preferable that the glass plates 11 and 12 have a thickness of 1 mm or more and 5 mm or less. With such a thickness, the glass plates 11 and 12 excellent in strength and optical characteristics can be obtained.

  The glass plates 11 and 12 and the mesh sheet 20 are bonded via bonding layers 13 and 14, respectively. As the bonding layers 13 and 14, layers made of materials having various adhesiveness or tackiness can be used. The bonding layers 13 and 14 preferably have a high visible light transmittance. As a typical joining layer, the layer which consists of polyvinyl butyral (PVB) can be illustrated. The thickness of the bonding layers 13 and 14 is preferably 0.15 mm or more and 0.7 mm or less, respectively.

  The laminated glass 10 is not limited to the illustrated example, and may be provided with other functional layers expected to exhibit a specific function. Moreover, you may make it one functional layer exhibit two or more functions, for example, the glass plates 11 and 12 of the laminated glass 10, the joining layers 13 and 14, and the base material 30 of the mesh sheet 20 mentioned later You may make it provide a function to at least one. Examples of functions that can be imparted to the laminated glass 10 include antireflection (AR) function, hard coat (HC) function having scratch resistance, infrared shielding (reflection) function, ultraviolet shielding (reflection) function, and polarization function. An antifouling function and the like can be exemplified.

  Next, the mesh sheet 20 will be described. The mesh sheet 20 connects the base material 30, the conductive mesh 40 provided on the base material 30, the wiring part 15 for energizing the conductive mesh 40, and the conductive mesh 40 and the wiring part 15. And a connecting portion 16. The mesh sheet 20 has substantially the same plane dimensions as the glass plates 11 and 12, and may be disposed over the entire laminated glass 10, or only on a part of the laminated glass 10 such as a front portion of a driver's seat. May be.

  The base material 30 functions as a base material that supports the conductive mesh 40. The base material 30 is a transparent and electrically insulating substrate that generally transmits a wavelength in the visible light wavelength band (380 nm to 780 nm), and is not substantially stretched in its manufacturing process. It is a stretched resin substrate.

  The base material 30 can be produced by a known method that does not include a stretching step, such as an extrusion method, a calendar method, or a casting method. Here, in the winding process after the manufacturing process or after the manufacturing process of the sheet as the base material, the sheet is pulled and may be slightly stretched in some cases, but this is not included in “stretching”. In other words, even if unavoidable stretching occurs in order to properly wind the sheet, the sheet produced in that process is included in the “unstretched” sheet unless it includes a substantial stretching process.

  The resin contained in the base material 30 may be any resin as long as it transmits visible light, but a thermoplastic resin can be preferably used. Examples of the thermoplastic resin include acrylic resins such as polymethyl methacrylate, polyester resins such as polyvinyl chloride, polyethylene terephthalate, and amorphous polyethylene terephthalate (A-PET), polyolefin resins such as polyethylene resin and polypropylene, triacetyl cellulose ( Cellulose resins such as cellulose triacetate), polystyrene, polycarbonate resin, AS resin, and the like. In particular, acrylic resin and polyvinyl chloride are preferable because they are excellent in etching resistance, weather resistance, and light resistance.

  Moreover, it is preferable that the base material 30 has a thickness of 0.03 mm or more and 0.15 mm or less in consideration of retainability of the conductive mesh 40, light transmittance, and the like.

  The conductive mesh 40 will be described with reference to FIGS. FIG. 5 is a plan view of the mesh sheet 20 as viewed from the normal direction of the sheet surface, and is a diagram illustrating an example of an arrangement pattern of the conductive mesh 40.

  The conductive mesh 40 is energized from the power source 7 such as a battery through the wiring portion 15 and the connection portion 16 and generates heat by resistance heating. And when this heat | fever is transmitted to the glass plates 11 and 12 through the joining layers 13 and 14, the glass plates 11 and 12 are warmed.

  As shown in FIG. 5, the conductive mesh 40 is a mesh member that defines a large number of openings 43. The conductive mesh 40 includes a plurality of conductive thin wires 41 extending between the two branch points 42 and defining the openings 43. That is, the conductive mesh 40 is configured as a collection of a large number of thin conductive wires 41 that form branch points 42 at both ends. In particular, in the illustrated example, at the branch point 42, three conductive thin wires 41 are connected at an equal angle, so that a large number of honeycomb-shaped openings 43 of the same shape surrounded by the six conductive thin wires 41 are defined. Yes.

  In the illustrated example, the conductive mesh 40 has a mesh pattern in which honeycomb-shaped openings 43 having the same shape are regularly arranged. However, the conductive mesh 40 is not limited to such a mesh pattern, and may be a triangle, a rectangle, or the like. Mesh pattern in which irregularly shaped openings 43 are irregularly arranged, such as a mesh pattern in which openings 43 of the same shape are regularly arranged, a mesh pattern in which irregularly shaped openings 43 are regularly arranged, and a Voronoi mesh Various mesh patterns such as patterns can be used.

  Examples of the material for forming the conductive mesh 40 include one or more of gold, silver, copper, platinum, aluminum, chromium, molybdenum, nickel, titanium, palladium, indium, tungsten, and alloys thereof. Can be illustrated.

  FIG. 6 is a cross-sectional view corresponding to the line AA in FIG. 5, and is a diagram illustrating an example of a cross-sectional shape of the conductive thin wire. A plurality of thin conductive wires 41 forming the conductive mesh 40 are formed on the base material 30. In the illustrated example, the conductive thin wire 41 has a surface 41 a on the base material 30 side, a surface 41 b on the opposite side of the base material 30, and side surfaces 41 c and 41 d, and has a substantially rectangular cross section as a whole. The width W of the thin conductive wire 41, that is, the width W along the sheet surface of the substrate 30 is 2 μm or more and 20 μm or less, and the height (thickness) H, that is, along the normal direction to the sheet surface of the substrate 30. The height (thickness) H is preferably 1 μm or more and 60 μm or less. According to the conductive thin wire 41 having such a dimension, since the conductive thin wire 41 is sufficiently thinned, the conductive mesh 40 can be effectively invisible.

  The conductive thin wire 41 is provided on the first dark color layer 46 provided on the base material 30, the conductive metal layer 45 provided on the first dark color layer 46, and the conductive metal layer 45. The second dark color layer 47 is included. In other words, the surface on the base material 30 side of the surface of the conductive metal layer 45 is covered with the first dark color layer 46, and the surface on the opposite side of the base material 30 among the surface of the conductive metal layer 45 and The second dark color layer 47 covers both side surfaces.

  The conductive metal layer 45 made of a metal material exhibits a relatively high reflectance. When the light is reflected by the conductive metal layer 45 that forms the conductive thin wires 41 of the conductive mesh 40, the reflected light is visually recognized and may hinder the occupant's field of view. Further, when the conductive metal layer 45 is visually recognized from the outside, the designability may be deteriorated. Therefore, the dark color layers 46 and 47 are disposed on at least a part of the surface of the conductive metal layer 45. The dark color layers 46 and 47 may be layers having a visible light reflectance lower than that of the conductive metal layer 45, and are dark color layers such as black. The dark color layers 46 and 47 make it difficult for the conductive metal layer 45 to be visually recognized, so that the occupant's field of view can be favorably secured. Moreover, the fall of the designability when seen from the outside can be prevented.

  FIG. 7 is a cross-sectional view corresponding to the line AA in FIG. 5 and is a diagram illustrating another example of the cross-sectional shape of the conductive thin wire. In the illustrated example, the conductive thin wire 41 has a surface 41a on the base material 30 side, a surface 41b on the opposite side of the base material 30, and side surfaces 41c and 41d. The surface 41a on the substrate 30 side and the surface 41b on the opposite side of the substrate 30 are parallel. The side surface 41 c has a tapered surface that approaches the side surface 41 d as the distance from the base material 30 increases along the normal direction of the sheet surface of the mesh sheet 20. The side surface 41d also has a tapered surface that approaches the side surface 41c as the distance from the base material 30 increases along the normal direction of the sheet surface of the mesh sheet 20. The thin conductive wire 41 has a substantially trapezoidal cross section as a whole. That is, the width of the thin conductive wire 41 changes so as to become narrower as the distance from the base material 30 increases along the normal direction of the mesh sheet 20. Similarly to the example shown in FIG. 6, the first dark color layer 46 covers the surface on the base material 30 side of the surface of the conductive metal layer 45. A second dark color layer 47 covers the surface opposite to the material 30 and both side surfaces.

  In FIG. 7, the conductive thin wire 41 has a substantially trapezoidal cross section as a whole, and the width of the conductive thin wire 41 becomes narrower as it is separated from the base material 30 along the normal direction of the mesh sheet 20. Although what is changing was shown, it is not restricted to this, The side surfaces 41c and 41d may be comprised by the curve, or may be multistage shape. Further, there may be a portion where the width of the conductive thin wire 41 is partially increased as the distance from the base material 30 is increased along the normal direction of the mesh sheet 20. That is, when the cross section of the thin conductive wire 41 is viewed as a whole and globally, the width of the thin conductive wire 41 changes so as to become narrower as it is separated from the base material 30 along the normal direction of the mesh sheet 20. If it is,

  In the example illustrated in FIG. 7, the width of the conductive thin wire 41 is configured to change so as to become narrower as it is separated from the base material 30 along the normal line direction of the mesh sheet 20. 12. When laminating the bonding layers 13 and 14 and the mesh sheet 20, the conductive mesh 40 can be reliably embedded in the bonding layer 13, and bubbles remain at the interface between the conductive mesh 40 and the bonding layer 13. Can be suppressed.

  Next, an example of a method for manufacturing the mesh sheet 20 will be described with reference to FIGS. 8-15 is sectional drawing which shows an example of the manufacturing method of the mesh sheet 20 in order.

  First, as shown in FIG. 8, a base material 30 is prepared. The base material 30 is a transparent, electrically insulating, unstretched resin base material that is generally transparent and transmits a wavelength in the visible light wavelength band (380 nm to 780 nm).

  Next, as shown in FIG. 9, a first dark color layer 46 is provided on the substrate 30. For example, the first dark color layer 46 is formed on the substrate 30 by a plating method including electroplating and electroless plating, a sputtering method, a CVD method, a PVD method, an ion plating method, or a combination of these two or more. Can be provided. Various known materials can be used as the material for the first dark color layer 46. For example, copper nitride, copper oxide, nickel nitride and the like can be exemplified.

  Next, as shown in FIG. 10, a conductive metal layer 45 is provided on the first dark color layer 46. As described above, the conductive metal layer 45 is a layer made of one or more of gold, silver, copper, platinum, aluminum, chromium, molybdenum, nickel, titanium, palladium, indium, tungsten, and alloys thereof. The conductive metal layer 45 can be formed by a known method. For example, a method of attaching a metal foil such as copper foil using a weather resistant adhesive, a plating method including electroplating and electroless plating, a sputtering method, a CVD method, a PVD method, an ion plating method, or these A method of combining two or more can be employed.

  Next, as shown in FIG. 11, a resist layer 48 is provided on the conductive metal layer 45. The resist layer 48 is a resin layer having photosensitivity to, for example, light in a specific wavelength range, for example, ultraviolet rays. This resin layer may be formed by sticking a resin film, or may be formed by coating a fluid resin. The specific photosensitive characteristics of the resist layer 48 are not particularly limited. For example, as the resist layer 48, a photocurable photosensitive material may be used, or a photodissolvable photosensitive material may be used.

  Thereafter, as shown in FIG. 12, the resist layer 48 is patterned to form a resist pattern 49. As a method of patterning the resist layer 48, various known methods can be employed. In this example, a resin layer having photosensitivity to light in a specific wavelength region, for example, ultraviolet rays, is used as the resist layer 48. Patterning is performed using a known photolithography technique. First, a mask in which a portion to be patterned is opened or a mask in which a portion to be patterned is shielded is disposed on the resist layer 48, and the resist layer 48 is irradiated with ultraviolet rays through this mask. Thereafter, the portion where the ultraviolet rays are shielded by the mask or the portion irradiated with the ultraviolet rays is removed by means such as development. Thereby, the patterned resist pattern 49 can be formed.

  Next, as shown in FIG. 13, the conductive metal layer 45 and the first dark color layer 46 are etched using the resist pattern 49 as a mask. By this etching, the conductive metal layer 45 and the first dark color layer 46 are patterned into a pattern substantially the same as the resist pattern 49. The etching method is not particularly limited, and a known method can be employed. Known methods include, for example, wet etching using an etchant, plasma etching, and the like. Thereafter, as shown in FIG. 14, the resist pattern 49 is removed.

  Finally, the second dark color layer 47 is formed on the surface 41b and the side surfaces 41c and 41d on the opposite side of the base material 30 of the conductive metal layer 45. For example, the second dark color layer 47 is subjected to a darkening process (blackening process) on a part of the material forming the conductive metal layer 45, and the metal oxide or metal sulfide is formed from a part of the conductive metal layer 45. A second dark color layer 47 made of a material can be formed. Alternatively, the second dark color layer 47 may be provided on the surface of the conductive metal layer 45, such as a coating film of dark color material or a plating layer of nickel or chromium. Alternatively, the second dark color layer 47 may be provided by roughening the surface of the conductive metal layer 45.

  In this example, the second dark color layer 47 is formed on the surface 41b and the side surfaces 41c and 41d opposite to the base material 30 of the conductive metal layer 45. However, the present invention is not limited to this, and the base material 30 of the conductive metal layer 45 is not limited thereto. The second dark color layer 47 may be formed only on the opposite surface 41 b or only on the side surfaces 41 c and 41 d of the conductive metal layer 45.

  In the case where the second dark color layer 47 is formed only on the surface 41b on the opposite side of the base material 30 of the conductive metal layer 45, for example, the second metal layer 45 is formed on the conductive metal layer 45 after the step shown in FIG. A dark color layer 47 and a resist layer 48 are provided in this order, and the resist layer 48 is patterned to form a resist pattern 49. Thereafter, the second dark color layer 47, the conductive metal layer 45, and the first dark color layer 46 may be etched using the resist pattern 49 as a mask.

  When the second dark color layer 47 is formed only on the side surfaces 41c and 41d of the conductive metal layer 45, for example, the second dark color layer without removing the resist pattern 49 after the step shown in FIG. 47 is formed, and then the resist pattern 49 is removed.

  If the first dark color layer 46 is not necessary, the step of providing the first dark color layer 46 on the substrate 30 shown in FIG. 9 may be omitted.

  As described above, the laminated glass 10 in the present embodiment includes the pair of curved glass plates 11 and 12, the mesh sheet 20 disposed between the pair of curved glass plates 11 and 12, and each glass plate 11. , 12 and the mesh sheet 20 and bonding layers 13 and 14 for bonding the glass plates 11 and 12 and the mesh sheet 20 to each other. The mesh sheet 20 includes a base material 30 and a conductive mesh 40 formed on the base material 30. As in the patterning method described above, the conductive mesh 40 can be produced on the base material 30 using various materials and various methods, and a desired pattern can be imparted with high accuracy. Therefore, for example, the laminated glass 10 having excellent optical characteristics can be produced.

  On the other hand, this laminated glass can be manufactured by heating and pressurizing a mesh sheet between glass plates via a bonding layer. However, the present inventors have found that in the laminated glass in a cooled state after heating and pressurization, there may be a problem that wrinkles are generated on the base material. Generation | occurrence | production of the wrinkle to a base material has generate | occur | produced in the curved location of a laminated glass, and the grade of a wrinkle changes according to the grade of the curvature of a laminated glass.

  In general, in a sheet stretched in the production process (stretched sheet), a residual stress is generated in the sheet in the stretching process, and when the sheet is heated to the vicinity of the melting point or the glass transition point, the sheet is largely contracted by the residual stress. On the other hand, in a sheet that has not been stretched in the manufacturing process (non-stretched sheet), the residual stress due to the stretching process does not occur, and thus the shrinkage of the sheet when the sheet is heated can be suppressed. Therefore, by using an unstretched resin base material as the base material 30 of the mesh sheet 20, the generation of wrinkles on the mesh sheet 20 can be effectively prevented as compared with the case where a base material stretched as the base material 30 is used. Is done.

The degree of shrinkage of the sheet can be evaluated by the absolute value of the heat shrinkage rate. The heat shrinkage rate is a dimensional change rate defined in JIS C 2151, and is defined as a dimensional change rate after a test piece having a predetermined size is heated at 100 ° C. for 15 minutes and cooled to room temperature. If the dimension before heating is L ₀ and the dimension after heating / cooling is L, the heat shrinkage S (%) is
S = (L ₀ −L) / L ₀ × 100
It can be expressed as

  The absolute value of the heat shrinkage rate of the non-stretched sheet that has not been stretched in the manufacturing process is smaller than the absolute value of the heat shrinkage rate of the stretched sheet that has been stretched in the manufacturing process. Typically, the maximum absolute value of the heat shrinkage rate in each direction in the plane of the unstretched sheet is 10% or less, and 5% or less from the viewpoint of reliably suppressing the occurrence of wrinkles. preferable.

  Note that various modifications can be made to the above-described embodiment.

  For example, the conductive mesh 40 of the mesh sheet 20 may be provided not on the glass plate 11 side surface of the substrate 30 but on the glass plate 12 side surface. Moreover, you may provide in the both surfaces of the glass plate 11 side and the glass plate 12 side of the base material 30. FIG.

  The laminated glass 10 may be used for a rear window, a side window, or a sunroof of the automobile 1. Moreover, you may use for windows of vehicles other than a motor vehicle, such as a railway, an aircraft, a ship, and a spacecraft.

  Furthermore, the laminated glass 10 can also be used in places other than the vehicle, in particular, in places that divide the room from the outdoors, such as buildings, stores, and house windows.

  In addition, although the some modification with respect to embodiment mentioned above was demonstrated above, naturally, it is also possible to apply combining several modifications suitably.

  EXAMPLES Hereinafter, although this invention is demonstrated in detail using an Example, this invention is not limited to this Example.

  The laminated glass which concerns on Examples 1-3 and the comparative example demonstrated below was produced actually, and generation | occurrence | production of wrinkles was confirmed. The laminated glass is composed of the first glass plate, the first bonding layer, the mesh sheet, the second bonding layer, and the second glass plate in this order in the same manner as the laminated glass described in the above embodiment. I included it. In each laminated glass, the same thing was employ | adopted for the 1st and 2nd glass plate and the 1st and 2nd joining layer. Specifically, curved blue plate glass plates having a length of 100 mm, a width of 100 mm, and a thickness of 2 mm were used as the first and second glass plates. As the first and second bonding layers, layers made of polyvinyl butyral (PVB) having a length of 100 mm, a width of 100 mm, and a thickness of 0.4 mm were used.

  The mesh sheet had a base material and a honeycomb-like conductive mesh formed on the base material. The conductive mesh was produced by patterning a copper foil by the photolithography technique described above. The conductive fine wire of the conductive mesh had a width of 10 μm and a height (thickness) of 10 μm. The opening ratio of the conductive mesh was 80%. The conductive mesh of the mesh sheet was common among the laminated glasses. On the other hand, as the base material of the mesh sheet, different resin films were used between the laminated glasses as follows.

Example 1
In Example 1, an unstretched acrylic resin film having a length of 110 mm, a width of 110 mm, and a thickness of 0.1 mm was used as the base material of the mesh sheet. The maximum absolute value of the heat shrinkage rate in each direction in the plane was 5%.

(Example 2)
In Example 2, unstretched amorphous polyethylene terephthalate having a length of 110 mm, a width of 110 mm, and a thickness of 0.1 mm was used as the base material of the mesh sheet. The maximum absolute value of the heat shrinkage rate in each direction in the plane was 5%.

(Example 3)
In Example 3, unstretched polyvinyl chloride having a length of 110 mm, a width of 110 mm, and a thickness of 0.1 mm was used as the base material of the mesh sheet. The maximum absolute value of the heat shrinkage rate in each direction in the plane was 8%.

(Comparative example)
In the comparative example, a uniaxially stretched polyethylene terephthalate film having a length of 110 mm, a width of 110 mm, and a thickness of 0.025 mm was used as the base material of the mesh sheet. The maximum absolute value of the heat shrinkage rate in each direction in the plane was 20%.

  Each laminated glass was produced by the following common method. The first glass plate, the first bonding layer, the mesh sheet, the second bonding layer, and the second glass plate described above were stacked in this order in the atmospheric pressure and carried into the autoclave apparatus. Next, after reducing the pressure inside the autoclave, it was heated and pressurized at 150 ° C. and 10 atm for 60 minutes. Then, it took out in atmospheric pressure, cooled to room temperature, and produced the laminated glass.

  About the laminated glass which concerns on the produced Examples 1-3 and the laminated glass which concerns on a comparative example, the presence or absence of wrinkles was determined visually. Even when carefully observing the laminated glasses according to Examples 1 to 3, the presence of wrinkles could not be confirmed. On the other hand, the laminated glass according to the comparative example had many wrinkles that could be visually confirmed.

DESCRIPTION OF SYMBOLS 1 Car 5 Front window 7 Power supply 10 Laminated glass 11 Glass plate 12 Glass plate 13 Joining layer 14 Joining layer 15 Connection part 16 Wiring part 20 Mesh sheet 30 Base material (non-stretched resin base material)
40 conductive mesh 41 conductive thin wire 42 branch point 43 opening 45 conductive metal layer 46 first dark color layer 47 second dark color layer 48 resist layer 49 resist pattern

Claims (5)

A pair of curved glass plates;
A mesh sheet disposed between the pair of curved glass plates;
A bonding layer disposed between each glass plate and the mesh sheet and bonding the glass plate and the mesh sheet; and
The mesh sheet is a laminated glass having an unstretched resin substrate and a conductive mesh formed on the unstretched resin substrate. The conductive mesh is formed using a thin conductive wire,
2. The laminated glass according to claim 1, wherein a width of the conductive thin wire changes so as to become narrower as it is separated from the unstretched resin base material along a normal direction of the mesh sheet. The conductive mesh is formed using a thin conductive wire,
The laminated glass according to claim 1 or 2, wherein the thin conductive wire has a conductive metal layer and a dark color layer covering at least a part of the surface of the metal layer. Laminated glass according to any one of claims 1 to 3,
And a power source connected to the conductive mesh of the laminated glass.   The vehicle provided with the laminated glass as described in any one of Claims 1-3, or the glass with a heating mechanism of Claim 4.