JP6269122B2 - Lubricating grease composition - Google Patents
Lubricating grease composition Download PDFInfo
- Publication number
- JP6269122B2 JP6269122B2 JP2014021344A JP2014021344A JP6269122B2 JP 6269122 B2 JP6269122 B2 JP 6269122B2 JP 2014021344 A JP2014021344 A JP 2014021344A JP 2014021344 A JP2014021344 A JP 2014021344A JP 6269122 B2 JP6269122 B2 JP 6269122B2
- Authority
- JP
- Japan
- Prior art keywords
- oxazoline
- lubricating grease
- grease composition
- dimethanol
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は潤滑グリース組成物に関し、詳しくは、防錆性に優れる潤滑グリース組成物に関する。 The present invention relates to a lubricating grease composition, and more particularly to a lubricating grease composition having excellent rust prevention properties.
近年、ロシアやブラジル、東南アジア等の新興市場における鉄鋼、自動車、一般機械、精密機器等さまざまな産業分野において潤滑グリースが使用されている。世界さまざまな地域における低温から高温多湿環境下での使用に対応するため、耐低温性や耐熱性を維持した状態での防錆性向上への要求が大きくなっている。 In recent years, lubricating grease has been used in various industrial fields such as steel, automobiles, general machinery and precision equipment in emerging markets such as Russia, Brazil and Southeast Asia. In order to support the use in low temperature to high temperature and humidity environment in various regions of the world, there is an increasing demand for improvement in rust resistance while maintaining low temperature resistance and heat resistance.
特許文献１には、グリース組成物において、ナフテン酸亜鉛やコハク酸誘導体が防錆添加剤として有効である旨が開示されている。 Patent Document 1 discloses that zinc naphthenate and succinic acid derivatives are effective as anticorrosive additives in grease compositions.
特許文献２には、中性金属スルホネート、過塩基性スルホネート及びアスパラ銀酸誘導体を用いることで、摩耗特性、耐摩耗性及び防錆性を付与した潤滑剤が開示されている。 Patent Document 2 discloses a lubricant imparted with wear characteristics, wear resistance, and rust resistance by using a neutral metal sulfonate, an overbased sulfonate, and an aspartic acid derivative.
特許文献３には、防錆添加剤として、非イオン性界面活性剤、２−エチルヘキンサン酸亜鉛を用いることで、良好な音響特性や耐漏洩性を維持しつつ、防錆性を有する潤滑剤組成物が開示されている。 Patent Document 3 discloses a lubricant composition having antirust properties while maintaining good acoustic characteristics and leakage resistance by using a nonionic surfactant and zinc 2-ethylhexanoate as anticorrosive additives. Things are disclosed.
しかし、これらの潤滑剤組成物では、現在要求されている耐低温性、耐熱性、防錆性の機能を満足することができない。 However, these lubricant compositions cannot satisfy the currently required functions of low temperature resistance, heat resistance and rust resistance.
そこで、本発明は、耐低温性や耐熱性、かつ防錆性に優れる潤滑グリース組成物を提供することを課題とする。 Then, this invention makes it a subject to provide the lubricating grease composition which is excellent in low temperature resistance, heat resistance, and rust prevention property.
また本発明の他の課題は、以下の記載により明らかとなる。 Other problems of the present invention will become apparent from the following description.
上記課題は以下の各発明によって解決される。 The above problems are solved by the following inventions.
１．
基油、増ちょう剤からなるグリース基材に、オキサゾリン化合物が配合されてなり、
オキサゾリン化合物の配合量が全グリース重量に対して０．３〜１１ｗｔ％の範囲であり、
前記オキサゾリン化合物は、２−ヘプタデセニル−２−オキサゾリン−４，４−ジメタノール、２−ヘプタデシル−２−オキサゾリン−４，４−ジメタノール、２−アルキル−２−オキサゾリン−４，４−ジメタノール、及び、２−アルケニル−２−オキサゾリン−４，４−ジメタノールから選択されることを特徴とする潤滑グリース組成物。
1.
Oxazoline compound is blended with grease base material consisting of base oil and thickener,
Range der of 0.3～11Wt% amount is the total grease weight of oxazoline compound is,
The oxazoline compound is 2-heptadecenyl-2-oxazoline-4,4-dimethanol, 2-heptadecyl-2-oxazoline-4,4-dimethanol, 2-alkyl-2-oxazoline-4,4-dimethanol, And a lubricating grease composition selected from 2-alkenyl-2-oxazoline-4,4-dimethanol .
２．前記基油が、鉱油、合成炭化水素油、エステル系合成油、エーテル系合成油、又はグリコール系合成油から選ばれる少なくとも１種を含有することを特徴とする前記１記載の潤滑グリース組成物。 2. 2. The lubricating grease composition according to 1 above, wherein the base oil contains at least one selected from mineral oil, synthetic hydrocarbon oil, ester synthetic oil, ether synthetic oil, or glycol synthetic oil.
３．前記増ちょう剤が、金属石けん系、複合金属石けん系、又はウレア系化合物から選ばれる少なくとも１種を含有することを特徴とする前記１又は２記載の潤滑グリース組成物。 3. 3. The lubricating grease composition as described in 1 or 2 above, wherein the thickener contains at least one selected from metal soaps, composite metal soaps, and urea compounds.
４．
基油、増ちょう剤からなる潤滑グリース組成物に含まれる、２−ヘプタデセニル−２−オキサゾリン−４，４−ジメタノール、２−ヘプタデシル−２−オキサゾリン−４，４−ジメタノール、２−アルキル−２−オキサゾリン−４，４−ジメタノール、及び、２−アルケニル−２−オキサゾリン−４，４−ジメタノールから選択されるオキサゾリン化合物の、防錆剤としての使用。
4).
2-heptadecenyl-2-oxazoline-4,4-dimethanol, 2-heptadecyl-2-oxazoline-4,4-dimethanol, 2-alkyl- , contained in a lubricating grease composition comprising a base oil and a thickener Use of an oxazoline compound selected from 2-oxazoline-4,4-dimethanol and 2-alkenyl-2-oxazoline-4,4-dimethanol as a rust inhibitor.
本発明によれば、耐低温性や耐熱性、かつ防錆性に優れる潤滑グリース組成物を提供することができる。 According to the present invention, a lubricating grease composition excellent in low temperature resistance, heat resistance and rust prevention can be provided.
以下、本発明の実施の形態を説明する。 Embodiments of the present invention will be described below.
本発明の潤滑グリース組成物は、基油と増ちょう剤とからなるグリース基材に、少なくともオキサゾリン化合物が配合されてなる。 The lubricating grease composition of the present invention is formed by blending at least an oxazoline compound with a grease base material composed of a base oil and a thickener.
防錆剤としてオキサゾリン化合物を配合することにより、耐低温性や耐熱性を損なわず防錆性に優れる潤滑グリース組成物を提供することができる。 By blending an oxazoline compound as a rust inhibitor, it is possible to provide a lubricating grease composition that is excellent in rust resistance without impairing low temperature resistance and heat resistance.
＜基油＞
基油としては、鉱油、合成炭化水素油、エステル系合成油、エーテル系合成油、グリコール系合成油から選ばれる少なくとも１種の基油を用いることが好ましい。
<Base oil>
As the base oil, it is preferable to use at least one base oil selected from mineral oil, synthetic hydrocarbon oil, ester synthetic oil, ether synthetic oil, and glycol synthetic oil.
これらの基油の１種を選択使用してもよいし、２種以上の基油を併用してもよい。 One of these base oils may be selectively used, or two or more base oils may be used in combination.
鉱油としては、例えば、パラフィン系、ナフテン系が挙げられる。 Examples of the mineral oil include paraffinic and naphthenic oils.
合成炭化水素としては、例えば、ポリαオレフィン、エチレンαオレフィンオリゴマー、ポリブテンが挙げられる。 Examples of the synthetic hydrocarbon include poly α olefin, ethylene α olefin oligomer, and polybutene.
エステル系合成油としては、例えば、ジエステルやポリオールエステル、芳香族エステル等のエステル油が挙げられる。エーテル系合成油としては、アルキルジフェニルエーテルが挙げられる。 Examples of the ester-based synthetic oil include ester oils such as diesters, polyol esters, and aromatic esters. Examples of the ether synthetic oil include alkyl diphenyl ether.
グリコール系合成油としては、ポリエチレングリコール、ポリプロピレングリコールが挙げられる。 Examples of the glycol-based synthetic oil include polyethylene glycol and polypropylene glycol.
樹脂、ゴムに対する影響を考慮した場合、合成炭化水素油を使用することが好ましいが、本発明においては特に限定されない。 In consideration of the influence on the resin and rubber, it is preferable to use a synthetic hydrocarbon oil, but it is not particularly limited in the present invention.
＜増ちょう剤＞
増ちょう剤としては、金属石けん系、複合金属石けん系、またはウレア系化合物から選ばれる少なくとも１種を使用できる。
<Thickener>
As the thickener, at least one selected from metal soaps, composite metal soaps, and urea compounds can be used.
金属石けん系としては、Ｌｉ石けん、Ｃａ石けん、アルミニウム石けんなどが挙げられ、その中でも、Ｌｉ石けんを好ましく用いることができる。 Examples of the metal soap system include Li soap, Ca soap, aluminum soap, and among them, Li soap can be preferably used.
Ｌｉ石けんとしては、炭素数１２〜２４の脂肪族モノカルボン酸および／または少くとも１個のヒドロキシル基を含む炭素数１２〜２４の脂肪族モノカルボン酸のリチウム塩などが挙げられ、１２−ヒドロキシステアリン酸リチウム塩やステアリン酸リチウム塩を好ましく用いることができる。 Examples of Li soaps include aliphatic monocarboxylic acids having 12 to 24 carbon atoms and / or lithium salts of aliphatic monocarboxylic acids having 12 to 24 carbon atoms containing at least one hydroxyl group. A lithium stearate salt or a lithium stearate salt can be preferably used.
Ｌｉ石けんを調製する方法としては、例えば、以下の方法が挙げられる。
基油と、１２−ヒドロキシステアリン酸と水酸化リチウムを所定量配合し、混合撹拌釜にて約８０〜１３０℃で加熱撹拌しけん化反応を行い、溶融温度まで加熱撹拌した後、冷却することで、基油とＬｉ石けんが混合したゲル状物質を作成する。
その後、各種添加剤を加え撹拌した後、ロールミルもしくは高圧ホモジナイザーに通し潤滑グリース組成物を調製することができる。
Examples of the method for preparing Li soap include the following methods.
By mixing a predetermined amount of base oil, 12-hydroxystearic acid and lithium hydroxide, performing a saponification reaction by heating and stirring at about 80 to 130 ° C. in a mixing and stirring vessel, heating and stirring to the melting temperature, and then cooling. Then, a gel material mixed with base oil and Li soap is prepared.
Then, after adding various additives and stirring, a lubricating grease composition can be prepared through a roll mill or a high-pressure homogenizer.
複合金属石けん系としては、例えば、Ｌｉ複合石けん、Ｃａ複合石けん、Ｂａ複合石けんなどが挙げられ、その中でも、Ｌｉ複合石けん、Ｂａ複合石けんを好ましく用いることができる。 Examples of the composite metal soap system include Li composite soap, Ca composite soap, Ba composite soap, etc. Among them, Li composite soap and Ba composite soap can be preferably used.
Ｌｉ複合石けんとしては、(ａ)成分脂肪族モノカルボン酸２種以上のリチウム系複合石けんまたは（ａ）成分脂肪族モノカルボン酸と（ｂ）炭素数２〜１２の脂肪族ジカルボン酸またはそのジエステルおよび炭素数７〜２４の芳香族モノカルボン酸またはそのエステルの少なくとも１種とのリチウム系複合石けんが挙げられる。 Examples of the Li composite soap include (a) two or more types of lithium-based composite soaps, or (a) component aliphatic monocarboxylic acids and (b) aliphatic dicarboxylic acids having 2 to 12 carbon atoms or diesters thereof. And lithium-based composite soaps with at least one of C7-24 aromatic monocarboxylic acids or esters thereof.
Ｌｉ複合石けんを調製する方法としては、例えば、以下の方法が挙げられる。
基油と１２ヒドロキシステアリン酸と水酸化リチウムを混合撹拌釜に所定量配合し、約８０〜１３０℃で加熱撹拌しけん化反応を行ない、さらにアゼライン酸を所定量配合し、約８０〜２００℃で加熱撹拌し、そこに水酸化リチウムを加え、冷却することで、基油とＬｉ複合石けんが混合したゲル状物質を作成する。
その後、各種添加剤を加え撹拌した後、ロールミルもしくは高圧ホモジナイザーに通し潤滑グリース組成物を調製することができる。
Examples of the method for preparing the Li composite soap include the following methods.
A base oil, 12 hydroxystearic acid and lithium hydroxide are mixed in a predetermined amount in a mixing and stirring vessel, heated and stirred at about 80 to 130 ° C. to carry out a saponification reaction, and further azelaic acid is mixed in a predetermined amount at about 80 to 200 ° C. The mixture is heated and stirred, lithium hydroxide is added thereto, and the mixture is cooled to produce a gel substance in which the base oil and the Li composite soap are mixed.
Then, after adding various additives and stirring, a lubricating grease composition can be prepared through a roll mill or a high-pressure homogenizer.
Ｂａ複合石けんとしては、脂肪族ジカルボン酸とモノアミドカルボン酸との複合石けんが挙げられる。 Examples of the Ba complex soap include complex soaps of aliphatic dicarboxylic acid and monoamide carboxylic acid.
Ｂａ複合石けんを調製する方法としては、例えば、以下の方法が挙げられる。
基油とセバシン酸およびカルボン酸モノステアリルアミドを混合撹拌釜に所定量配合し、約８０〜２００℃で加熱撹拌し、そこに水酸化バリウムを加えて、冷却することで、基油とＢａ複合石けんが混合したゲル状物質を作成する。
その後、各種添加剤を加え撹拌した後、ロールミルもしくは高圧ホモジナイザーに通し潤滑グリース組成物を調製することができる。
Examples of the method for preparing the Ba composite soap include the following methods.
Base oil, sebacic acid and carboxylic acid monostearylamide are mixed in a predetermined amount in a mixing and stirring kettle, heated and stirred at about 80 to 200 ° C., barium hydroxide is added thereto, and cooled, so that the base oil and Ba composite are mixed. Create a gel-like substance mixed with soap.
Then, after adding various additives and stirring, a lubricating grease composition can be prepared through a roll mill or a high-pressure homogenizer.
ウレア系化合物としては、ジウレア化合物、トリウレア化合物、テトラウレア化合物、ポリウレア化合物等が挙げられ、好ましくはジウレア化合物が用いられる。 Examples of the urea compound include diurea compounds, triurea compounds, tetraurea compounds, polyurea compounds, and the like, and diurea compounds are preferably used.
ウレア系化合物としては、具体的には下記一般式で表されるものなどが挙げられる。
一般式 Ｒ′(ＮＨＣＯＮＨＲ)ｎＮＨＣＯＮＨＲ″
式中、Ｒは２価の芳香族炭化水素基を表す。Ｒ′、Ｒ″は１価のＣ６〜Ｃ２４脂肪族飽和または不飽和炭化水素基、脂環状炭化水素基または芳香族炭化水素基を表わす。ｎは整数であり、ｎ＝１はジウレア化合物であり、ｎ＝２はトリウレア化合物であり、ｎ＝３はテトラウレア化合物であり、ｎ＝４以上はポリウレア化合物である。
Specific examples of urea compounds include those represented by the following general formula.
Formula R ′ (NHCONHR) nNHCONHR ″
In the formula, R represents a divalent aromatic hydrocarbon group. R ′ and R ″ each represent a monovalent C6-C24 aliphatic saturated or unsaturated hydrocarbon group, alicyclic hydrocarbon group or aromatic hydrocarbon group. N is an integer and n = 1 is a diurea compound. , N = 2 is a triurea compound, n = 3 is a tetraurea compound, and n = 4 or more is a polyurea compound.
ウレア系化合物を調製する方法としては、例えば、以下の方法が挙げられる。
基油とジフェニルメタンジイソシアネートとオクチルアミンとを７０〜１８０℃で加熱撹拌し反応を行い、昇温、冷却することで、基油とウレア系化合物が混合したゲル状物質を作成する。
その後、各種添加剤を加え撹拌した後、ロールミルもしくは高圧ホモジナイザーに通し潤滑グリース組成物を調製することができる。
Examples of the method for preparing the urea compound include the following methods.
A base oil, diphenylmethane diisocyanate, and octylamine are heated and stirred at 70 to 180 ° C. to react, and the temperature is raised and cooled to create a gel-like substance in which the base oil and the urea compound are mixed.
Then, after adding various additives and stirring, a lubricating grease composition can be prepared through a roll mill or a high-pressure homogenizer.
＜オキサゾリン化合物＞
オキサゾリン化合物としては、２−ヘプタデセニル−２−オキサゾリン−４，４−ジメ
タノール、２−ヘプタデシル−２−オキサゾリン−４，４−ジメタノール、２−アルキル
−２−オキサゾリン−４，４−ジメタノール、２−アルケニル−２−オキサゾリン−４，
４−ジメタノールなどが挙げられ、その中でも特に２−ヘプタデセニル−２−オキサゾリ
ン−４，４−ジメタノールを好ましく用いることができる。
<Oxazoline compound>
The oxazoline compound, 2-heptadecyl cell-2- oxazoline-4,4-dimethanol, 2-heptadecyl-2-oxazoline-4,4-dimethanol, 2-alkyl-2-oxazoline-4,4-di Methanol, 2-alkenyl-2-oxazoline-4,
And 4-dimethanol and the like, can be preferably used especially 2-heptadecyl cell-2- oxazoline-4,4-dimethanol among them.
オキサゾリン化合物は市販品を使用することができ、ＡＮＧＵＳ Ｃｈｅｍｉｃａｌ Ｃｏｍｐａｎｙ社製「ＡＬＫＡＴＥＲＧＥ−Ｔ」等が挙げられる。 A commercially available product can be used as the oxazoline compound, and examples thereof include “ALKATERGE-T” manufactured by ANGUS Chemical Company.
オキサゾリン化合物の配合量は、全グリース重量に対して、０．３〜１１ｗｔ％の範囲であることが好ましく、さらに好ましくは０．３〜１０ｗｔ％であり、またさらに好ましくは０．５〜３ｗｔ％である。 The blending amount of the oxazoline compound is preferably in the range of 0.3 to 11 wt%, more preferably 0.3 to 10 wt%, and still more preferably 0.5 to 3 wt% with respect to the total grease weight. It is.
オキサゾリン化合物の配合量が全グリース重量に対して０．２５ｗｔ％未満であると、最適な防錆性に欠け、１１．００ｗｔ％を超えると、耐熱性、耐低温性に欠けるため好ましくない。 If the blending amount of the oxazoline compound is less than 0.25 wt% with respect to the total grease weight, the optimum rust prevention property is lacking, and if it exceeds 11.00 wt%, the heat resistance and low temperature resistance are lacking.
＜その他＞
本発明の潤滑グリース組成物には、その効果に影響を与えない範囲で他の物質も添加することができる。例えば、公知の酸化防止剤や極圧剤、油性剤、粘度指数向上剤等を適宜選択して添加することができる。
<Others>
Other substances may be added to the lubricating grease composition of the present invention as long as the effect thereof is not affected. For example, known antioxidants, extreme pressure agents, oiliness agents, viscosity index improvers and the like can be appropriately selected and added.
酸化防止剤としては、例えば２，６−ジ−ｔ−ブチル−４−メチルフェノール、４，４’−メチレンビス（２，６−ジ−ｔ−ブチルフェノール）等のフェノール系酸化防止剤、アルキルジフェニルアミン、トリフェニルアミン、フェニル−α−ナフチルアミン、フェノチアジン、アルキル化−α−ナフチルアミン、アルキル化フェノチアジン等が挙げられる。 Examples of the antioxidant include phenolic antioxidants such as 2,6-di-tert-butyl-4-methylphenol and 4,4′-methylenebis (2,6-di-tert-butylphenol), alkyldiphenylamine, Examples include triphenylamine, phenyl-α-naphthylamine, phenothiazine, alkylated-α-naphthylamine, and alkylated phenothiazine.
極圧剤としては、例えばリン酸エステル、亜リン酸エステル、リン酸エステルアミン塩等のリン系化合物、スルフィド類、ジスルフィド類等の硫黄化合物、ジアルキルジチオリン酸塩、ジアルキルジチオカルバミン酸金属塩等が挙げられる。 Examples of extreme pressure agents include phosphorous compounds such as phosphate esters, phosphite esters, phosphate ester amine salts, sulfur compounds such as sulfides and disulfides, dialkyldithiophosphates, metal salts of dialkyldithiocarbamic acid, and the like. It is done.
油性剤としては、例えば脂肪酸またはそのエステル、高級アルコールや多価アルコールまたはそのエステル、脂肪族アミン、脂肪族モノグリセライド等が挙げられる。 Examples of the oily agent include fatty acids or esters thereof, higher alcohols and polyhydric alcohols or esters thereof, aliphatic amines, and aliphatic monoglycerides.
粘度指数向上剤としては、例えば、ポリメタクリレート、エチレン−プロピレン共重合体、ポリイソブチレン、ポリアルキルスチレン、スチレン-イソプレン共重合体水素化物などが挙げられる。 Examples of the viscosity index improver include polymethacrylate, ethylene-propylene copolymer, polyisobutylene, polyalkylstyrene, styrene-isoprene copolymer hydride, and the like.
本発明の実施例について説明する。かかる実施例によって本発明が限定されるものではない。 Examples of the present invention will be described. The present invention is not limited to the embodiments.
１．各潤滑グリース組成物の調製方法
＜Ｌｉ石けん系潤滑グリース組成物の調製＞
表に示される基油と、１２−ヒドロキシステアリン酸と水酸化リチウムを、表に示す量配合し、混合撹拌釜にて約８０〜１３０℃で加熱撹拌しけん化反応を行い、溶融温度まで加熱撹拌した後、冷却した。生成したゲル状物質に酸化防止剤１ｗｔ％、防錆剤として表に示す化合物を表に示す量配合加え撹拌した後、ロールミルもしくは高圧ホモジナイザーに通し潤滑グリース組成物を調整した。
1. Preparation method of each lubricating grease composition <Preparation of Li soap-based lubricating grease composition>
The base oil shown in the table, 12-hydroxystearic acid and lithium hydroxide are blended in the amounts shown in the table, and the mixture is stirred and heated at about 80 to 130 ° C. in a mixing and stirring vessel, and stirred to the melting temperature. And then cooled. The resulting gel-like substance was mixed with the antioxidant 1 wt% and the compound shown in the table as a rust inhibitor in the amount shown in the table and stirred, and then passed through a roll mill or a high-pressure homogenizer to prepare a lubricating grease composition.
＜Ｂａ複合石けん系潤滑グリース組成物の調製＞
表に示される基油と、セバシン酸およびカルボン酸モノステアリルアミドを混合撹拌釜に配合し、約８０〜２００度で加熱撹拌し、そこに水酸化バリウムを加えて、冷却した。バリウム複合石けんの総量としては、表に示される量配合された。生成したゲル状物質に酸化防止剤１ｗｔ％、防錆剤として表に示す化合物を表に示す量配合加え撹拌した後、ロールミルもしくは高圧ホモジナイザーに通し潤滑グリース組成物を調製した。
<Preparation of Ba complex soap-based lubricating grease composition>
The base oil shown in the table, sebacic acid and carboxylic acid monostearylamide were mixed in a mixing and stirring vessel, heated and stirred at about 80 to 200 degrees, barium hydroxide was added thereto, and the mixture was cooled. The total amount of barium composite soap was blended as shown in the table. The resulting gel material was mixed with 1 wt% of an antioxidant and the compounds shown in the table as a rust inhibitor and stirred, and then passed through a roll mill or a high-pressure homogenizer to prepare a lubricating grease composition.
＜Ｌｉ複合石けん系潤滑グリース組成物の調製＞
表に示される基油と、１２−ヒドロキシステアリン酸と水酸化リチウムを混合撹拌釜に所定量配合し、約８０〜１３０℃で加熱撹拌しけん化反応を行ない、さらにアゼライン酸を所定量配合し、約８０〜２００℃で加熱撹拌し、そこに水酸化リチウムを加え、冷却した。リチウム複合石けんの総量としては、表に示される量配合された。生成したゲル状物質に酸化防止剤１ｗｔ％、防錆剤として表に示す化合物を表に示す量配合加え撹拌した後、ロールミルもしくは高圧ホモジナイザーに通し潤滑グリース組成物を調製した。
<Preparation of Li composite soap-based lubricating grease composition>
The base oil shown in the table, 12-hydroxystearic acid and lithium hydroxide are blended in a predetermined amount in a mixing and stirring kettle, heated and stirred at about 80 to 130 ° C. for saponification reaction, and further azelaic acid is blended in a predetermined amount, The mixture was heated and stirred at about 80 to 200 ° C., lithium hydroxide was added thereto, and the mixture was cooled. The total amount of lithium composite soap was blended in the amounts shown in the table. The resulting gel material was mixed with 1 wt% of an antioxidant and the compounds shown in the table as a rust inhibitor and stirred, and then passed through a roll mill or a high-pressure homogenizer to prepare a lubricating grease composition.
＜ウレア系化合物グリースの調製＞
表に示される基油と、ジフェニルメタンジイソシアネートとオクチルアミンとを表に示す量配合し、７０〜１８０℃で加熱撹拌し反応を行い、昇温、冷却を行なった。ウレア系化合物の総量としては、表に示される量配合された。生成したゲル状物質に酸化防止剤１ｗｔ％、防錆剤として表に示す化合物を表に示す量配合加え撹拌した後、ロールミルもしくは高圧ホモジナイザーに通し潤滑グリース組成物を調製した。
<Preparation of urea compound grease>
The base oil shown in the table, diphenylmethane diisocyanate and octylamine were blended in the amounts shown in the table, and the reaction was conducted by heating and stirring at 70 to 180 ° C., and the temperature was raised and cooled. The total amount of urea compounds was blended in the amounts shown in the table. The resulting gel material was mixed with 1 wt% of an antioxidant and the compounds shown in the table as a rust inhibitor and stirred, and then passed through a roll mill or a high-pressure homogenizer to prepare a lubricating grease composition.
２．実施例に用いた基油、防錆剤、酸化防止剤の詳細
＜基油＞
・ポリ−α−オレフィンＡ：４０℃粘度１８ｍｍ２/ｓ（イネオスオリゴマーズジャパン社製「ＤＵＲＡＳＹＮ１６４」）
・ポリ−α−オレフィンＢ：４０℃粘度６８ｍｍ２/ｓ（イネオスオリゴマーズジャパン社製「ＤＵＲＡＳＹＮ１７０」）
・パラフィン系鉱油Ａ：４０℃粘度２２ｍｍ２/ｓ（ＪＸ日鉱日石エネルギー社製「スーパーオイルＮ２２」）
・パラフィン系鉱油Ｂ：４０℃粘度１４１ｍｍ２/ｓ（ＪＸ日鉱日石エネルギー社製「スーパーオイルＮ１５０」）
・ポリオールエステル：４０℃粘度２９ｍｍ２/ｓ（日本油脂社製「ユニスター Ｈ−３３４Ｒ」）
・ジフェニルエーテル：４０℃粘度１００ｍｍ２/ｓ（ＭＯＲＥＳＣＯ社製「モレスコハイルーブＬＢ−１００」）
2. Details of base oil, rust inhibitor and antioxidant used in Examples <Base oil>
Poly-α-olefin A: 40 ° C. viscosity 18 mm 2 / s (“DURASYN164” manufactured by Ineos Oligomers Japan)
Poly-α-olefin B: 40 ° C. viscosity 68 mm 2 / s (“DURASYN170” manufactured by Ineos Oligomers Japan)
Paraffin-based mineral oil A: 40 ° C. viscosity 22 mm 2 / s (“Super Oil N22” manufactured by JX Nippon Oil & Energy Corporation)
Paraffinic mineral oil B: viscosity at 40 ° C. of 141 mm 2 / s (“Super Oil N150” manufactured by JX Nippon Oil & Energy Corporation)
Polyol ester: 40 ° C. viscosity 29 mm 2 / s (“Unistar H-334R” manufactured by NOF Corporation)
Diphenyl ether: 40 ° C. viscosity 100 mm 2 / s (MORESCO “MORESCO HILUB LB-100”)
＜防錆剤＞
・オキサゾリン（２−ヘプタデセニル−２−オキサゾリン−４，４−ジメタノール）：Ａ
ＮＧＵＳ Ｃｈｅｍｉｃａｌ Ｃｏｍｐａｎｙ社製「ＡＬＫＡＴＥＲＧＥ−Ｔ」
・中性カルシウムスルホネート：ＫＩＮＧ社製「ＮＡ−ＳＵＬ ＣＡ−１０８９」
・過塩基性カルシウムスルホネート：ルブリゾール社製「ＬＺ５３４７」
・ソルビタンモノオレエート：三洋化成工業社製「イオネットＳ−８０Ｓ」
・アルケニルコハク酸：三洋化成工業社製「サンヒビター１０２」
・バリウムスルホネート：ＫＩＮＧ社製「ＮＡ−ＳＵＬ ＢＳＮ」
・亜鉛スルホネート：ＫＩＮＧ社製「ＮＡ−ＳＵＬ ＺＳ」
・アスパラギン酸誘導体：ＫＩＮＧ社製「Ｋ−ＣＯＲＲ １００Ａ２」
・２−エチルヘキサン酸亜鉛：ナカライテスク社製
・酸化パラフィン金属塩：日本精蝋社製「ＯＸ−０８５１」
・サルコシン誘導体：ＢＡＳＦ社製「ＳＡＲＫＯＳＹＬ Ｏ」
<Rust preventive>
Oxazoline (2-heptadecyl Se-2- oxazoline-4,4-dimethanol): A
“ALKATERGE-T” manufactured by NGUS Chemical Company
-Neutral calcium sulfonate: "NA-SUL CA-1089" manufactured by KING
・ Overbased calcium sulfonate: “LZ5347” manufactured by Lubrizol
・ Sorbitan monooleate: “Ionet S-80S” manufactured by Sanyo Chemical Industries
・ Alkenyl succinic acid: "Sunhibitor 102" manufactured by Sanyo Chemical Industries
Barium sulfonate: “NA-SUL BSN” manufactured by KING
・ Zinc sulfonate: “NA-SUL ZS” manufactured by KING
Aspartic acid derivative: “K-CORR 100A2” manufactured by KING
・ Zinc 2-ethylhexanoate: Nacalai Tesque ・ Oxidized paraffin metal salt: “OX-0851” manufactured by Nippon Seiwa Co., Ltd.
・ Sarcosine derivative: “SARKOSYL O” manufactured by BASF
＜酸化防止剤＞
実施例では酸化防止剤として、フェニル−α−ナフチルアミン（三洋化成工業社製ＶＡＮＬＵＢＥ８１）を用いた。
<Antioxidant>
In the examples, phenyl-α-naphthylamine (VANLUBE81 manufactured by Sanyo Chemical Industries) was used as an antioxidant.
３．実施例、比較例
＜実施例１〜７、比較例１〜１１＞
上記＜Ｌｉ石けん系潤滑グリース組成物の調整＞の通り、表に示す配合材料を、表に示す量配合させて、潤滑グリース組成物を得た。
3. Examples, Comparative Examples <Examples 1-7, Comparative Examples 1-11>
As described in <Preparation of Li soap-based lubricating grease composition>, the blending materials shown in the table were blended in the amounts shown in the table to obtain a lubricating grease composition.
＜実施例８〜１０、比較例１２、１５、１６＞
上記＜Ｂａ複合石けん系潤滑グリース組成物の調整＞の通り、表に示す配合材料を、表に示す量配合させて、潤滑グリース組成物を得た。
<Examples 8 to 10, Comparative Examples 12, 15, and 16>
As described above <Preparation of Ba complex soap-based lubricating grease composition>, the blending materials shown in the table were blended in the amounts shown in the table to obtain a lubricating grease composition.
＜実施例１１〜１３、比較例１３、１７＞
上記＜Ｌｉ複合石けん系潤滑グリース組成物の調整＞の通り、表に示す配合材料を、表に示す量配合させて、潤滑グリース組成物を得た。
<Examples 11 to 13, Comparative Examples 13 and 17>
As described in <Preparation of Li composite soap-based lubricating grease composition>, the blending materials shown in the table were blended in the amounts shown in the table to obtain a lubricating grease composition.
＜実施例１４、１５、比較例１４＞
上記＜ウレアグリースの調整＞の通り、表に示す配合材料を、表に示す量配合させて、潤滑グリース組成物を得た。
<Examples 14 and 15, Comparative Example 14>
As described in <Preparation of urea grease>, the blending materials shown in the table were blended in the amounts shown in the table to obtain a lubricating grease composition.
４．評価方法
得られた潤滑グリース組成物について、下記の項目について評価を行ない、結果を表１〜表４に示した。
4). Evaluation Method The obtained lubricating grease composition was evaluated for the following items, and the results are shown in Tables 1 to 4.
＜混和ちょう度評価＞
得られた潤滑グリース組成物について、ＪＩＳ Ｋ２２２０．７：２０１３に準拠し、混和ちょう度試験を行った。２５０〜３２０の範囲内であると、潤滑グリースに好適なちょう度であると評価できる。
<Evaluation of blending consistency>
The resulting lubricating grease composition was subjected to a blending consistency test in accordance with JIS K2220.7: 2013. It can be evaluated that it is the consistency suitable for lubricating grease as it exists in the range of 250-320.
＜耐低温性評価＞
得られた潤滑グリース組成物について、ＪＩＳ Ｋ２２２０．１８：２０１３に準拠し、低温トルク試験を行った。
試験温度：−３０℃
防錆剤未配合のグリース組成物の起動トルク（Ｎ・ｃｍ）に対して、防錆剤配合グリースの起動トルク（Ｎ・ｃｍ）がどれだけ増加したかで評価を行なった。
本発明においては、増加量が１０未満であれば、耐低温性が良好に保たれていると評価できる。
<Low temperature resistance evaluation>
The obtained lubricating grease composition was subjected to a low temperature torque test in accordance with JIS K2220.18: 2013.
Test temperature: -30 ° C
Evaluation was made as to how much the starting torque (N · cm) of the anti-rust agent-containing grease increased relative to the starting torque (N · cm) of the grease composition not containing the anti-rust agent.
In the present invention, if the amount of increase is less than 10, it can be evaluated that the low temperature resistance is kept good.
＜耐熱性評価＞
得られた潤滑グリース組成物について、ＪＩＳ Ｋ２２２０．１１：２０１３に準拠し、離油度試験を行った。
試験温度：１００℃
防錆剤未配合のグリース組成物の離油度（ｗｔ％）に対して、防錆剤配合グリースの離油度（ｗｔ％）がどれだけ増加したかで評価を行なった。
本発明においては、増加量が５未満であれば、耐熱性が良好に保たれていると評価できる。
<Heat resistance evaluation>
The obtained lubricating grease composition was subjected to an oil separation test in accordance with JIS K2220.11: 2013.
Test temperature: 100 ° C
Evaluation was made as to how much the oil separation degree (wt%) of the grease containing a rust inhibitor increased with respect to the oil separation degree (wt%) of the grease composition containing no rust inhibitor.
In the present invention, if the increase amount is less than 5, it can be evaluated that the heat resistance is kept good.
＜防錆性評価＞
得られた潤滑グリース組成物について、ＤＩＮ５１８０２（ＥＭＣＯＲ試験）に準拠し、以下のとおり防錆試験を行った。
規定の自動調心玉軸受（１３０６Ｋ）に潤滑グリース組成物１０ｇを充填し、エムコ試験機に取り付け、試験機に７％食塩水を３０ｍｌ入れた後、室温にて、８０ｒｐｍで８時間回転、１６時間停止を２回繰り返した。その後さらに８時間運転後、１０８時間放置し、軸受外輪軌道面の発錆状態を、以下記載の基準に従って、６段階に評価した。
０：発錆なし
１：非常に弱い発錆（発錆が３点以内）
２：弱い発錆（発錆部分が表面の１％未満）
３：発錆（発錆部分が表面の１％以上５％未満）
４：強い発錆（発錆が表面の５％以上１０％未満）
５：非常に強い発錆（発錆が表面の１０％以上）
<Rust prevention evaluation>
About the obtained lubricating grease composition, the rust prevention test was done as follows based on DIN51802 (EMCOR test).
The specified self-aligning ball bearing (1306K) is filled with 10 g of the lubricating grease composition, attached to the Emco testing machine, and 30 ml of 7% saline is added to the testing machine, and then rotated at 80 rpm for 8 hours at room temperature. The time stop was repeated twice. Thereafter, after further operation for 8 hours, the system was left for 108 hours, and the rusting state of the bearing outer ring raceway surface was evaluated in 6 stages according to the criteria described below.
0: No rusting 1: Very weak rusting (rusting within 3 points)
2: Weak rusting (rusting part is less than 1% of the surface)
3: Rusting (rusting part is 1% or more and less than 5% of the surface)
4: Strong rusting (rusting is 5% or more and less than 10% of the surface)
5: Very strong rusting (rusting is 10% or more of the surface)
５．評価
実施例と比較例３〜１１、１６、１７によると、防錆剤としてオキサゾリンを配合することにより、防錆性に優れ、且つ耐熱性、耐低温性に優れた潤滑グリース組成物が得られることが確認できた。
5). Evaluation According to Examples and Comparative Examples 3 to 11, 16, and 17, a lubricating grease composition excellent in rust prevention, heat resistance, and low temperature resistance can be obtained by blending oxazoline as a rust inhibitor. I was able to confirm.
また、比較例１、１５によると、オキサゾリン配合量が全グリース重量に対して０．２５ｗｔ％未満であると、防錆性に劣ることが確認できる。 Further, according to Comparative Examples 1 and 15, it can be confirmed that the oxazoline content is less than 0.25 wt% with respect to the total grease weight, and the rust prevention property is poor.
一方、比較例２、１２〜１４によると、オキサゾリン配合量が全グリース重量に対して１１．００ｗｔ％を超える範囲で配合された場合は、耐熱性、耐低温性に劣ることが確認できる。 On the other hand, according to Comparative Examples 2 and 12 to 14, when the amount of oxazoline is blended in a range exceeding 11.00 wt% with respect to the total grease weight, it can be confirmed that the heat resistance and low temperature resistance are poor.
本発明の潤滑グリース組成物は、防錆性を必要とする軸受、ギヤ部、ゴムシール部などに好適に使用することができ、具体的には、電動ラジエータファンモータ、ファンカップリング、電制ＥＧＲ、電子制御スロットバルブ、オルタネータ、アイドラプーリ、電動ブレーキ、ハブユニット、ウォーターポンプ、パワーウィンドウ、スライドドア、ワイパ、電動パワーステアリング等の自動車補機の転がり軸受、すべり軸受またはギア部、ゴムシール部、工作機械、製紙機械用軸受などに使用することができる。 The lubricating grease composition of the present invention can be suitably used for bearings, gears, rubber seals and the like that require rust prevention, and specifically, electric radiator fan motors, fan couplings, electric control EGRs. , Electronic control slot valves, alternators, idler pulleys, electric brakes, hub units, water pumps, power windows, sliding doors, wipers, electric power steering, etc., rolling bearings, plain bearings or gears, rubber seals It can be used for bearings for machines and paper machines.
また、その他、防錆性が必要となる自動変速機用コントロールスイッチ、レバーコントロールスイッチ、プッシュスイッチ等の防錆性、潤滑性が要求される電気接点部分、ビスカスカップリングのＸリング部分、排気ブレーキのＯリング等、ゴムシール部分、ヘッドライト、シート、ＡＢＳ、ドアロック、ドアヒンジ、クラッチブースタ、２分割フライホイール、ウィンドレギュレータ、ボールジョイント、クラッチブースター等のギヤ、摺動部、釣具用や自動車用の転がり軸受、ギヤ部等にも適用可能である。 In addition, control switches for automatic transmissions that require rust prevention, lever control switches, push switches and other electrical contact parts that require rust prevention and lubrication, the X-ring part of viscous couplings, and exhaust brakes O-rings, rubber seals, headlights, seats, ABS, door locks, door hinges, clutch boosters, 2-split flywheels, window regulators, ball joints, clutch boosters, etc. Gears, sliding parts, fishing gears and automobiles It can also be applied to rolling bearings, gear parts, and the like.
Claims (4)
オキサゾリン化合物の配合量が全グリース重量に対して０．３〜１１ｗｔ％の範囲であり、
前記オキサゾリン化合物は、２−ヘプタデセニル−２−オキサゾリン−４，４−ジメタノール、２−ヘプタデシル−２−オキサゾリン−４，４−ジメタノール、２−アルキル−２−オキサゾリン−４，４−ジメタノール、及び、２−アルケニル−２−オキサゾリン−４，４−ジメタノールから選択されることを特徴とする潤滑グリース組成物。 Oxazoline compound is blended with grease base material consisting of base oil and thickener,
Range der of 0.3～11Wt% amount is the total grease weight of oxazoline compound is,
The oxazoline compound is 2-heptadecenyl-2-oxazoline-4,4-dimethanol, 2-heptadecyl-2-oxazoline-4,4-dimethanol, 2-alkyl-2-oxazoline-4,4-dimethanol, And a lubricating grease composition selected from 2-alkenyl-2-oxazoline-4,4-dimethanol .