JP6258605B2 - Flooring - Google Patents

Description

  The present invention relates to a composite plywood formed by laminating a decorative layer on the surface of a wooden substrate.

For example, composite plywood formed by laminating a decorative layer on the surface of a wood substrate made of softwood plywood is used as a building board material such as a floor board. In such a composite plywood, it is necessary to prevent irregularities on the surface of the wooden substrate from appearing on the design surface via the decorative layer. That is, unevenness may appear on the surface of the wooden substrate due to, for example, nodes existing on the plywood of the conifer. Although it is difficult to eliminate the unevenness on the surface itself, when the unevenness appears on the design surface through the decorative layer, the design properties of the composite plywood are degraded.
Therefore, it has been proposed to prevent irregularities from appearing on the surface (design surface) of the composite plywood by sticking a wood fiber board to the surface of the wood substrate (Patent Document 1).

JP-A-5-57841

  However, among wooden fiberboards, for example, even when MDF (Medium Density Fiberboard) is interposed between the wooden substrate and the decorative layer, the unevenness caused by the knots and cracks of the wooden substrate is sufficient. It is difficult to absorb. As a result, there is a problem that irregularities appear on the design surface of the composite plywood, and the design properties thereof deteriorate. In addition, even if the unevenness of the wooden substrate can be absorbed on one surface of the wooden fiberboard, if the surface on the decorative layer side of the wooden substrate is too soft, a smooth design surface cannot be obtained, which is a factor that deteriorates the design There is a risk of becoming.

This invention is made | formed in view of this background, and intends to provide the flooring material excellent in the designability which can prevent the unevenness | corrugation of a wooden board | substrate from appearing in a design surface.

One aspect of the present invention is a flooring as a building board made of composite plywood,
The composite plywood is
A wooden substrate,
A wet hardboard laminated on the surface of the wooden substrate;
The wet hardboard is formed by bonding together the decorative layer laminated on the surface opposite to the wood substrate,
The wet hardboard includes a hard surface on one main surface, a soft surface softer than the hard surface on the other main surface, the hard surface facing the decorative layer side, and the soft surface facing the wood In the state facing the substrate side, it is interposed between the wooden substrate and the decorative layer,
The wet hardboard may have a embossed layer formed by forming irregularities on the soft surface,
The hard surface has a pencil hardness of H to 4H,
The decorative layer is a flooring material comprising a veneer veneer (claim 1).

In the flooring , the wet hardboard is interposed between the wooden substrate and the decorative layer with the hard surface facing the decorative layer and the soft surface facing the wooden substrate. Thereby, the floor material excellent in the designability which can prevent the unevenness | corrugation of a wooden board | substrate from appearing in a design surface can be obtained.

  That is, by directing the soft surface of the wet hardboard toward the wooden substrate, irregularities caused by nodes, cracks, etc. in the wooden substrate can be absorbed in the soft surface. That is, the soft surface can be flexibly deformed along the unevenness of the wooden substrate, and the deformation can be prevented from being transmitted to the opposite side surface (hard surface) of the wet hardboard.

  On the other hand, by making the hard surface of the wet hardboard face the decorative layer side, it is possible to prevent the surface on which the decorative layer is attached from being deformed. As a result, for example, the surface on which the decorative layer is attached can be a smooth surface, and the decorative layer can be formed in a desired state to improve the design.

As described above, according to the present invention, it is possible to provide a flooring material that can prevent the unevenness of the wooden substrate from appearing on the design surface and has excellent design properties.

Sectional explanatory drawing of the composite plywood in Example 1. FIG. Sectional explanatory drawing of the wet hard board of the state before lamination | stacking in Example 1. FIG. FIG. 3 is a partially enlarged cross-sectional explanatory view of a composite plywood for explaining the function and effect in Example 1.

The wet hard board, that have a embossed layer formed by forming irregularities on the soft surface. Thereby , the soft surface can be made sufficiently soft. Moreover, the softness | flexibility of a soft surface can be adjusted appropriately by designing the thickness of an embossing layer and the shape (mesh size etc.) of an embossing layer appropriately.

The wooden substrate may be made of a coniferous board. In this case, the design of the flooring can be effectively improved. In other words, coniferous boards generally have many nodes and are relatively prone to cracking. When such a coniferous board is used for a wooden substrate, there is a concern that unevenness of the wooden substrate may appear on the design surface. In such a case, by arranging the wet hardboard as described above, it is possible to effectively absorb the irregularities of the wooden substrate and to effectively improve the design of the design surface.

Moreover, the said wooden board | substrate shall consist of a plywood formed by laminating | stacking a single board. In this case, deformation such as warpage hardly occurs and an inexpensive flooring can be obtained.

In addition, the decorative layer, ing from veneer. Thereby , the flooring material with the high design property which made the design surface express the grain can be obtained. In particular, since the floor material has a decorative layer laminated on the hard surface of the wet hardboard, a design surface with particularly excellent design properties can be obtained.

In addition, the composite plywood, Ru architectural plate der. Thereby , the board | plate material for construction excellent in the designability can be obtained.

Further, the composite plywood, Ru flooring der. Thereby , the flooring excellent in the designability can be provided. In particular, flooring is a product in which the design of the design surface (floor surface) is important. If the unevenness of the wooden substrate appears on the design surface, the commercial value tends to be greatly reduced. Therefore, in the composite plywood as a flooring material, it is important to prevent the unevenness of the wooden substrate from appearing on the design surface.

Example 1
Examples of the flooring will be described with reference to FIGS.
As shown in FIG. 1 , the composite plywood 1 as a flooring material of this example includes a wood substrate 2, a wet hard board 3 laminated on the surface of the wood substrate 2, and a wet hard board 3 on the opposite side to the wood substrate 2. The decorative layer 4 laminated on the surface is joined to each other.
The wet hardboard 3 includes a hard surface 31 on one main surface and a soft surface 32 that is softer than the hard surface 31 on the other main surface. The wet hardboard 3 is interposed between the wooden substrate 2 and the decorative layer 4 with the hard surface 31 facing the decorative layer 4 and the soft surface 32 facing the wooden substrate 2.

The wooden board | substrate 2 consists of a softwood board | plate material, and consists of a plywood formed by laminating | stacking a single board. That is, the wooden board | substrate 2 is a plywood formed by laminating | stacking the single board obtained by cutting the timber of a conifer. Examples of conifers include cedar and cypress.
In this example, the decorative layer 4 is a veneer. For example, hardwood such as hippopotamus, oak, chestnut, walnut, tammo and wild cherry can be used for the veneer (veneer) constituting the decorative layer 4.

The wet hardboard 3 is a hardboard (hard fiberboard) defined as one having a density of 0.80 g / cm ³ or more among fiberboards defined in JIS A 5905: 2003, and is obtained by a wet method. It is a wet hard fiberboard.
The wet hard board 3 is manufactured as follows, for example. That is, first, wood fibers obtained by grinding wood chips into fibers are mixed with a large amount of water. Here, you may add some (for example, 0.5 mass%) resin adhesive. The slurry in which the wood fibers are dispersed in water in this way is placed on a wire mesh to form a mat. And it shape | molds and spin-dry | dehydrates with a hot press from the top of a mat-like slurry. For example, it compresses with a press (hot plate), applying heat at about 200 degreeC for several minutes. Thus, the wet hard board 3 can be obtained.

  As shown in FIG. 2, the wet hardboard 3 obtained in this way has a mesh pattern of a wire mesh formed on one surface. That is, in the above-described manufacturing method, the recesses 321 are formed in a mesh shape on the lower surface of the mat placed on the wire mesh. Thereby, the embossed layer 320 is formed in the wet hard board 3 on the one surface side. The side on which the embossed layer 320 is formed becomes the soft surface 32. The thickness of the embossed layer 320 corresponds to the depth of the recess 321 formed on the soft surface 32.

  The wet hard board 3 has a hard surface 31 on the opposite side of the soft surface 32. That is, the wet hard board 3 obtained by the wet manufacturing method as described above can form a thick region close to the surface pressed by a high-temperature press die (hot plate) with high density. As a result, the hard surface 32 of the wet hardboard 3 can have a pencil hardness of H to 4H. On the other hand, the soft surface 32 is so soft that the pencil hardness cannot be measured. The hardness of the soft surface 32 is, for example, about the same as that of a soft fiberboard.

Moreover, the density of the wet hardboard 3 gradually decreases from the hard surface 31 side to the soft surface 32 side. That is, the hard layer with high density and the soft layer with low density are not separated by a clear boundary. However, a predetermined thickness from the hard surface 31 side is a rock layer 310 having a particularly high density.
Incidentally, the composite plywood 1 of this example, use Irare as architectural plate, in particular, need use as flooring.

Next, the function and effect of this example will be described.
In the composite plywood 1, the wet hardboard 3 is interposed between the wooden substrate 2 and the decorative layer 4 with the hard surface 31 facing the decorative layer 4 and the soft surface 32 facing the wooden substrate 2. Yes. Thereby, the composite plywood 1 excellent in design property which can prevent the unevenness | corrugation of the wooden substrate 2 from appearing in the design surface 11 can be obtained.

  That is, by directing the soft surface 32 of the wet hardboard 3 toward the wooden substrate 2, the unevenness 29 caused by the nodes and cracks in the wooden substrate 2 can be absorbed by the soft surface 32 as shown in FIG. 3. . That is, the wood substrate 2 often has nodes, cracks, and the like, and as a result, the unevenness 29 may appear on the surface of the decorative board 4 (wet hardboard 3). However, in the composite plywood 1 of this example, the soft surface 32 is flexibly deformed along the unevenness 29 of the wooden substrate 2 so that the deformation is not transmitted to the opposite side surface (hard surface 31) of the wet hardboard 3. can do.

  On the other hand, by directing the hard surface 31 of the wet hardboard 3 toward the decorative layer 4, the surface on which the decorative layer 4 is adhered can be prevented from being deformed. As a result, for example, the surface on which the decorative layer 4 is adhered can be a smooth surface, and the decorative layer 4 can be formed in a desired state to improve the design.

  Moreover, since the wet hard board 3 has the embossed layer 320 on the soft surface 32 side, the soft surface 32 can be made sufficiently soft. Moreover, the hardness of the soft surface 32 can be adjusted appropriately by designing the thickness of the embossed layer 320 and the shape (mesh shape) of the embossed layer 320 appropriately.

  The wooden substrate 2 is made of a coniferous board. Therefore, the design properties of the composite plywood 1 can be improved effectively. In other words, coniferous boards generally have many nodes and are relatively prone to cracking. When such a coniferous board is used for the wooden substrate 2, there is a concern that the unevenness 29 of the wooden substrate 2 appears on the design surface 11. In such a case, by disposing the wet hardboard 3 as described above, the unevenness 29 of the wooden substrate 2 can be effectively absorbed and the designability of the design surface 11 can be effectively improved.

Moreover, since the wooden board | substrate 2 consists of a plywood formed by laminating | stacking a single board, it is hard to produce deformation | transformation, such as curvature, and can obtain the cheap composite plywood 1. FIG.
Moreover, since the decorative layer 4 consists of a veneer board, the composite plywood 1 with the high design property which made the design surface 11 express the wood grain can be obtained. In particular, since the composite plywood 1 has the decorative layer 4 laminated on the hard surface 31 of the wet hardboard 3, it is possible to obtain a design surface 11 that is particularly excellent in design.

Moreover, the board | plate material for construction excellent in the designability can be obtained by making the composite plywood 1 into the board | plate material for construction.
In particular, by applying the composite plywood 1 to a flooring material, a flooring material excellent in design can be obtained. That is, in particular, the flooring is a product in which the designability of the design surface 11 (floor surface) is important. If the unevenness 29 of the wooden substrate 2 appears on the design surface 11, the commercial value is likely to be greatly reduced. Therefore, it is important to prevent the unevenness 29 of the wooden substrate 2 from appearing on the design surface 11 in the floor material, and the composite plywood 1 of this example effectively realizes this.

As described above, according to this example, it is possible to provide a flooring material excellent in design properties that can prevent the unevenness of the wooden substrate from appearing on the design surface.

As the woody substrate, addition of plywood, for example solid plate, LVL: may (Laminated Veneer Lumber laminated veneer) or the like.

DESCRIPTION OF SYMBOLS 1 Composite plywood 2 Wood board 3 Wet hard board 31 Hard surface 32 Soft surface 4 Makeup layer

Claims (3)

It is a flooring as a building board made of composite plywood,
The composite plywood is
A wooden substrate,
A wet hardboard laminated on the surface of the wooden substrate;
The wet hardboard is formed by bonding together the decorative layer laminated on the surface opposite to the wood substrate,
The wet hardboard includes a hard surface on one main surface, a soft surface softer than the hard surface on the other main surface, the hard surface facing the decorative layer side, and the soft surface facing the wood In the state facing the substrate side, it is interposed between the wooden substrate and the decorative layer,
The wet hardboard may have a embossed layer formed by forming irregularities on the soft surface,
The hard surface has a pencil hardness of H to 4H,
The flooring material , wherein the decorative layer comprises a hardwood veneer . The flooring material according to claim 1, wherein the wooden substrate is made of a coniferous board. The flooring according to claim 1 or 2, wherein the wooden substrate is made of plywood formed by laminating a single plate.

Images